By W. Hodge, A. F. Haskins, R. M. Evans

Refractory boron compounds are shown to resist corrosion by molten zinc. Coatings were made from ferroboron and manganese boron by several methods: welding, hard facing, and pack diffusion; and techniques of coatings are very important. Mechanical failure of the diffusion coatings can be partially eliminated by applying them to type 416 chromium steels rather than carbon steels. Welded coatings made with a tungsten arc are better than those made by other welding methods. Sintered compacts of mixtures of iron and chromium borides developed strengths of about 30,000 psi. They resisted corrosion of zinc at 600°C and oxidation at higher temperatures. MOLTEN zinc rapidly attacks common metals of construction. The rate of attack is greatly amplified at temperatures over 500°C. However, there are many applications where it is necessary, or at least advantageous, to use metal construction, such as for galvanizing pots and zinc smelter equipment. Condensers and agitator linings used in continuous zinc smelting processes are eroded and corroded by violently agitated molten zinc. Pumps, tubing, and other parts to permit transfer of molten zinc would be desirable in many zinc handling operations. The development of metallic materials which are resistant to molten zinc also might permit its use as a heat-transfer medium in modern high efficiency power plants. In reviewing previous work on zinc-resistant metals, it was evident that most of the available data refer to corrosion at temperatures just above the melting point. Tungsten and high Mo-Fe alloys containing more than 80 pct Mo resist corrosion by molten zinc.', ' Imhoff states that because chromium is not attacked by zinc, chromium plating improves galvanizing pot life." Nitrided cast iron has been used in die-casting machines' where the molten alloy is 96 pct Zn and 4 pct Al. Other metals that have been suggested as of possible value for zinc resistance are columbium, tantalum, and titanium.V he corrosion of steel by zinc has been discussed by many authors,z, "2 None of these materials resisted corrosion by molten zinc at the temperatures used in this investigation, i.e., 600" to 700°C. I. Exploratory and Resistant-Coating Tests To make a study of zinc-resistant metals, exploratory tests were conducted to sort out roughly those materials which seemed most worthy of further development. This preliminary study included both solid metals and surface coatings. Exploratory Corrosion Tests in Molten Zinc—In initiating a study of this problem, numerous samples of metals and alloys were evaluated by dynamic corrosion tests made at 440 °C. Each metal was tested in its most readily available form, which, because of shape and size, was often unsuited for standard corrosion testing. The equipment used for dynamic corrosion testing of all materials, except in a few initial experiments, is shown in Fig. 1. Samples were tied to tungsten rods with tungsten wire, immersed in the zinc, and revolved at 12 rpm about the circumference of a 4 in. diam circle. Speed of travel was about 12.5 fpm. The molten zinc was protected from oxidation by an atmosphere of carbon monoxide, or, at a later period in the program, by a 9:1 mixture of nitrogen and hydrogen. When the effect of both molten metal and atmosphere was desired, the zinc level was lowered. Special high grade zinc was used in all of the corrosion tests. Corrosion losses for materials tested are shown in Tables I and 11. Whenever the materials were available in suitable form, the losses are reported in mils per year. It was recognized that weight losses on irregularly shaped specimens did not show the corrosion rate but the important consideration—poor resistance to corrosion—could be determined readily.

Jan 1, 1956

By W. C. Elli, M. E. Fine

YOUNG'S modulus of elasticity in metals ordinarily decreases with rising temperature. The range of the thermoelastic coefficient at room tem- 1/E dE/dT perature (temperature coefficient of modulus, is illustrated1 by the values for tungsten and hard-drawn aluminum, —95 and —1220x10-6 eg C-1. However, a nearly zero thermoelastic coefficient is observed in some ferromagnetic alloys over a limited temperature range. In these alloys, as the temperature is raised, an increase in modulus arising from loss of ferromagnetism compensates the normal decrease. Iron-nickel alloys containing 36 to 52 pct Ni behave in this manner. In the present investiga- tion, the dependence of the modulus and thermo-elastic coefficient on cold working and annealing were studied in iron-nickel alloys in this range of nickel. Although these alloys, when fully annealed, have a coefficient near zero over a very small temperature interval, the temperature range of low coefficient can be extended greatly by straining and then stress-relief annealing. The modulus of face-centered cubic iron-nickel alloys annealed at 1000°C does not vary linearly with composition at room temperature but, as shown by the solid line of fig. 1, from Koster,' is minimum at 40 pct Ni and maximum at 87 pct Ni. The modulus increases with applied magnetic field but retains the minimum near 40 pct Ni. Schematic change of modulus with temperature for three compositions is shown in fig. 2.'. ' With increasing temperature, the slope becomes less negative, goes through zero (temperature of minimum modulus for the alloy), becomes positive, and resumes its normal negative value above the Curie

Jan 1, 1951

By Edwin B. Wilson, Charles F. Cockrell

The application of evolutionary operation is proposed for the cleaning of coal by the heavy media process. Analysis of the data given suggests some benefits that may not be immediately appreciated unless evolutionary operation is applied. For example, while it may seem obvious to increase specific gravity when the ash and sulfur content of the clean coal is lower than that allowed, evolutionary operation may show that an increase in feed rate or an increase in both feed rate and specific gravity would be a more profitable alternative. In addition, by using evolutionary operation, up-to-date knowledge of the effect of change of feed rate or specific gravity on yield and product quality is available. This information facilitates confidence about decisions made in regard to the day-to-day operation of these units. A number of other applications in the minerals industry are proposed. An application of evolutionary operation in a related field is also given where a large number of variables were required to be optimized.

Jan 1, 1969

By J. L. Gillson

The big mass of anorthosite in the Lake Sanford district and the bodies of titaniferous magnetite that occur in a small area near the south margin of the mass have been described repeatedly, and the puzzling problems of the genesis of the rocks and ores have stimulated the deductive reasoning of geologists for a hundred years. Some of these men have taken a leading part in describing the anorthosite rock and forming hypotheses concerning its origin; some have contributed most to the study of the ore deposits; and some have made classical Studies introducing a basic approach to the problems of the anorthosite rock and genesis of the titaniferous magnetites. Much of the writing on the problems of rock and ore genesis has been based on physical-chemical reasoning rather than on field and microscope observations of the rocks and ores. Most of these geologists conclude that the anorthosite was formed by true magmatic crystallization, involving previous settling or squeezing out of ferromagnesian minerals from the parent magma. The associated gabbro is a separate segregation or later intrusion, and the lighter colored and finer grained facies of the anorthosite is either a chilled border zone of the anorthosite or the result of granulation by crushing of the coarse, dark blue rock of the main mass. This blue rock, called the Marcy type, is named after the highest peak in the range. The finer grained and lighter colored rock is called the Whiteface, after another mountain appropriately named for a cliff colored by this facies of the anorthosite.

Mar 1, 1956

By O. D. Gaither

This paper is an analytical study of the flow of fluids through small vertical conduits. Small conduits are defined as 11/4-in. nominal diameter tubing size and smaller, and approximately twice this area for annular conduits (i.e., 1- X 21/2-in. annulus and smaller). Experimental data are presented for the 1-X2-in. and 11/4- X 2%-in. annuli, and the I-in. and 11/4-in. tubing, since these represent the small conduit sizes and configurations generally encountered in oilfield applications. Data have been gathered for these conduits for single-phase water, single-phase gas and two-phase water-gas mixtures, with particular emphasis on high gas-liquid ratios. Water rates in excess of 2,000 BID and gas rates in excess of 2.5 MMcf/D, and two-phase flow ratios in between these two, represent the scope of the data gathered. Existing equations have been applied to predict flowing pressures and compared with experimental data. New correlations have been developed. INTRODUCTION The increased economic pressure on the domestic oil industry in the United States has constantly required the use of new techniques and equipment designed to reduce the cost of finding and producing oil and gas. Since tangible items are most readily apparent in economic analysis, the advent of lower-cost well completions was inevitable. One of the methods used to reduce costs which has received widespread attention is the slim-hole completion technique where tubing is used as the well casing and in which small conduits are used for tubing if necessary. Small conduits, defined by Kirkpatrick1 as "11/4-in. diameter nominal tubing and smaller for tubing flow and less than twice the 11/4-in. diameter nominal tubing internal flow area for annulus flow", have also found widespread usage as siphon strings for de-watering gas wells and as "kill" strings in deep high-pressure oil and gas wells. The growing use of small-diameter tubing has resulted in an increased need for development of improved methods to measure or predict flowing bottom-hole pressures since the physical dimensions generally preclude the use of subsurface-recording pressure gauges. Even in the cases where small bombs are available, the relatively high velocities encountered at nominal flow rates make it necessary to use excessive weight bars or special hold-down devices. Attempts to use recognized correlations to accurately predict flowing or gas-lift performance in wells equipped with small conduits have been generally unsuccessful. Insufficient field data were available to allow the development of a correlation on this basis, and an experimental approach was applied in an attempt to obtain a workable relation. The experimental approach used to obtain the data presented in this paper was actually a compromise between a field installation and a laboratory study. A test well 1,000 ft in length was used to obtain flow data on single-phase liquid, single-phase gas and two-phase water-gas flowing mixtures. Liquid rates up to 2,200 B/D and gas rates up to 3 MMcf/D were used in the single-phase flow studies. Two-phase flow rates from 100 to 600 B/D with gas-liquid ratios from 500 to 8,000 cu ft/bbl were recorded. Experimental data were obtained for single- and two-phase flow through 1-in and 11/4-in. nominal tubing, and through the annuli between 1- and 2-in. and 11/4- and 2%-in. nominal tubing strings. Experimental results for the two-phase flow are compared to the Poettmann-Carpenter correlation2 which is widely used as a comparative standard for development of multiphase flow predictions in flowing and gas-lift wells. Correlations developed by Tek,3 Baxendell and Thomas" were also investigated. The experimental data recorded herein fell in between the two flow regimes as defined by Ros," and this correlation also failed to yield satisfactory results. The fact that existing correlations failed to confirm the experimental data led to the need for development of a new correlation. Although a two-phase flow study was the primary objective of this investigation, data were also recorded for single-phase flow of water and gas, and constants were developed relating to pipe roughness and equivalent diameters for annular flow. These single-phase studies assisted materially in the development of certain of the two-phase flow results. Considerable previous work has been published which presented relationship of surface measurements to bottom-hole condition. The works of Buthod and Whiteley,6 Jones,' Poettmannb and the Texas Railroad Commission" are classic examples of the successful use of mathematical relationships which allow acceptable predictions of subsurface pressures, when gas is the flowing fluid. Darcy and others have derived relationships which may be used with minor modifications to predict subsurface flowing conditions in injection and water-supply wells. As previously stated, the application of the single-phase flow relationships

By R. F. Pilgrim

A digital computer program to mathematically simulate the effect of limited changes in feed rate in the range of 80 to 95 tph on a plant-scale wet grinding circuit has been developed and tested. The circuit studied included an 8-ft-diam X 12-ft rod mill operating in open circuit and feeding two parallel 12-ft-diam x 10-ft pebble mills, each one operating in closed circuit with an 8 X 32-ft rake classifier. The simulation is an empirical one based on two sets of data collected manually from the operating circuit under what was said to be steady-state feed rates of 80 and 95 tph with all other operating variables also at steady state. The procedure is a combination of several published approaches to the modeling of grinding mills and classifiers and it is applicable to a wide range of circuits. The program permits the computing of the size distributions of all feeds and discharges of all grinding units and classifiers in the circuit for a specified feed rate. The data used in this report for demonstrating the program are unsatisfactory since the circuit was not operating under steady-state conditions when it was sampled. Consequently the circuit model parameters could not be accurately estimated. The predictive power would be greatly improved if new data were obtained under true steady-state conditions.

Jan 1, 1973

By G. D. Cremer, J. J. Cordiano

Aluminum powder is a well-known article of commerce and in various forms has been marketed widely for use in paint, for pyrotechnic purposes and for exothermic mixtures. For a number of reasons, however, aluminum powder has not been employed extensively in powder metallurgy, although a great many proposals along this line have been offered. Aluminum and alumiuum-alloy powders oxidize readily upon exposure to air and the thin film of oxide (or hydroxide) thus formed is highly refractory, in that ordinary gaseous reducing agents such as hydrogen or carbon monoxide do not reduce the oxide to metal at temperatures below the melting point of aluminum. It has been thought that the presence of these films of oxide on aluminum particles would interfere markedly in powder metallurgical work and a number of suggestions have been made, either for preventing the formation of the film through the production of the powders in inert or reducing atmospheres, or for the removal of the oxide by means of powerful reducing agents, including "nascent" or atomic hydrogen released from metal hydrides. A second and more serious difficulty in the use of aluminum and aluminum-alloy powders in powder metallurgy resides in the fact that during compression such powders tend to adhere or cold-weld to the die walls, thus interfering with the formation and ejection of a compact. A third difficulty, which has been encountered only with aluminum-alloy powders, is their hardness when compared with elemental aluminum. Certain of these powders are susceptible to age-hardening, which further hinders the formation of strong green compacts. These conditions are particularly true of atomized aluminum-alloy powders. Even in the annealed condition, plastic deformation of alloy powders under pressure is low when compared with unalloyed powders. This fact, coupled with the lower corrosion resistance of the alloy powders. is probably the significant factor in our failure to obtain strong sintered pieces. Methods of Puoducing the Powder Many methods have been proposed for manufacture of aluminum powder, only a few of which are used commercially. Several of the more important processes include: (I) atomization of the molten metal; (2) mechanical pulverization and other types of comminution; and (3) graining, in which molten aluminum is stirred during freezing. For pigment and certain pyrotechnic uses aluminum flake powder is desirable, because of its greater proportion of surface to volume; and large quantities of such material are made by a procedure that involves stamping or ball milling. In making flake intended for use as pigment,

Jan 1, 1943

By G. D. Cremer, J. J. Cordiano

Aluminum powder is a well-known article of commerce and in various forms has been marketed widely for use in paint, for pyrotechnic purposes and for exothermic mixtures. For a number of reasons, however, aluminum powder has not been employed extensively in powder metallurgy, although a great many proposals along this line have been offered. Aluminum and alumiuum-alloy powders oxidize readily upon exposure to air and the thin film of oxide (or hydroxide) thus formed is highly refractory, in that ordinary gaseous reducing agents such as hydrogen or carbon monoxide do not reduce the oxide to metal at temperatures below the melting point of aluminum. It has been thought that the presence of these films of oxide on aluminum particles would interfere markedly in powder metallurgical work and a number of suggestions have been made, either for preventing the formation of the film through the production of the powders in inert or reducing atmospheres, or for the removal of the oxide by means of powerful reducing agents, including "nascent" or atomic hydrogen released from metal hydrides. A second and more serious difficulty in the use of aluminum and aluminum-alloy powders in powder metallurgy resides in the fact that during compression such powders tend to adhere or cold-weld to the die walls, thus interfering with the formation and ejection of a compact. A third difficulty, which has been encountered only with aluminum-alloy powders, is their hardness when compared with elemental aluminum. Certain of these powders are susceptible to age-hardening, which further hinders the formation of strong green compacts. These conditions are particularly true of atomized aluminum-alloy powders. Even in the annealed condition, plastic deformation of alloy powders under pressure is low when compared with unalloyed powders. This fact, coupled with the lower corrosion resistance of the alloy powders. is probably the significant factor in our failure to obtain strong sintered pieces. Methods of Puoducing the Powder Many methods have been proposed for manufacture of aluminum powder, only a few of which are used commercially. Several of the more important processes include: (I) atomization of the molten metal; (2) mechanical pulverization and other types of comminution; and (3) graining, in which molten aluminum is stirred during freezing. For pigment and certain pyrotechnic uses aluminum flake powder is desirable, because of its greater proportion of surface to volume; and large quantities of such material are made by a procedure that involves stamping or ball milling. In making flake intended for use as pigment,

Jan 1, 1943

By C. H. Mathewson

CHARACTER OF THE WORK IN HAND IN planning the present experiments, we have made a particular effort to secure that adjustment of working conditions which would render the forthcoming tests most serviceable by way of indicating the comparative properties of the three different commercial grades of copper used. More specifically, we have endeavored to obtain certain definite information with respect to the relative behavior under test of ordinary electrolytic copper and furnace-refined lake copper containing (a) a moderate percentage of arsenic and (b) a rather large percentage of arsenic, in addition to the usual content of silver and other impurities. These comparisons were made systematic and comprehensive by testing throughout a series of (eight) reductions running from 0 to 70 per cent. in the case of cold-rolled metal, and throughout a series of (15) temperatures running from 100° C. to 1,000° C. in the case of annealed metal. In other words, a survey of properties similar to that made by Grard,1 in the case of electrolytic copper, was here repeated (with modifications) and extended to two other commercial varieties of copper.

Jan 7, 1916

By P. R. Sahm, T. V. Pruss

Mixtures of fine GaSb and Gds as well as preal-loyed GaSbl,As, powders were hot-pressed at 690°C and 25,000 psi. Dense alloys with compositional gradients of less than 5 pct were obtained from mixtures containing about 20 mol pct GaAs. For x < 0.2, there were increasing compositional gradients, and for x > 0.2 a GaAs-rich second phase appeared in the microstructure. Densification as well as alloying wlechanisms were enhanced by dissociation and, possibly, oxidation reactions of the powders. Densification of coarse prealloyed material, however, primarily depended on plastic flow phenomena and required temperatures just below solidus and pressures of 50,000 psi Thermal and electrical properties were measured. Although in no case was the figure of merit of melt growth materials approached closer than to within 25 pct, the better overall thermoelectric properties were found in coarse-grained, prealloyed materzals which had been compacted to near theoretical density and where grain regrowth had been induced. Similar results are believed to hold in other binary 111-V compound systems if processed under similar conditions. The densification of unalloyed GaSb powders during pressure sintering (= hot pressing) was shown to depend strongly on powder particle size.&apos; Fine powders displayed a "liquid skin effect" that enhanced compaction through the presence of liquid gallium, whereas coarse powders compacted predominantly by plastic flow. The liquid skin effect, in particular, appeared attractive for alloying GaSb with other, higher-melting, III-V compounds, and to densify these in a one-step operation. This is of special interest in the case of III-V compound alloys as the conventional techniques of melt growth or long-time annealing of powders2 is very time-consuming, especially in cases where a large separation of liquidus and solidus can be expected, such as in GaSbl alloys.2 It was felt that experimentation with this system, a particularly unfavorable example, would allow us to extrapolate to several other, more favorable, cases. Uses of Ill-V alloys are most evident in thermoelectric energy conversion devices.&apos; For this reason certain thermal and electrical properties were measured and compared to those of melt-grown material and to hot-pressed prealloyed powders. EXPERIMENTAL PROCEDURE The pressure-sintering apparatus has been previously described.&apos; Using this equipment, both powder mixtures of GaSb with GaAs and prealloyed GaSbl-,As, powders were hot-pressed. The mixtures were pre- pared from cast GaSb and melt-grown GaAs. The prealloyed material was obtained from stoichiometric melts, initially heated to 1200°C in an evacuated quartz ampoule, and then annealed in the solidus-liquidus interval. A typical annealing cycle consisted of a heating to 850°C (1 hr), extended successive annealing at 750°C (65 hr), and slow stepwise cooling (25 hr) to below solidus. The GaSb, GaAs, and GaSbl-,As, materials were ground in a vibrational mill to particle sizes below 500 . A jet mill reduced these further where necessary. Fine powders were analyzed by Coulter counting for their size distribution. Average sizes by volume were calculated from the data. Mixing of the powders, where necessary, was carried out through rapid vibrational motion. The hot-pressing operation consisted of a degassing period of 15 hr, in most cases at 690°C, followed by several hours of compression, normally 25,000 psi at 690°C for powder mixtures and 50,000 psi at 710°C for prealloyed powders. The chemical compositions were confirmed by X-ray fluorescence analysis. To estimate the degree of solid solution achieved, lattice parameters were determined and interpreted according to Vegard&apos;s rule. In addition, optical microscopy helped to correlate the relative amounts of the phases present as well as the degree of porosity to the measured density. To reveal grain boundaries, polished surfaces were etched4 with H 2 O:H 2 O:HCl = 2:l:l. In several cases microscopic concentration gradients were monitored by electron-probe analysis-. RESULTS AND DISCUSSION Alloying and Densification of GaSn-GaAs Powder Mixtures. After preliminary experiments showed that no appreciable alloying took place in mixtures of coarse GaSb (22.5 p) and fine GaAs (2.5 p) powders, hot pressing of mixtures was confined to fine powders only (3.1 and 2.4 p, respectively). Alloying and densification apparently occurred simultaneously with a grain regrowth mechanism which depended on the presence of a liquid phase.&apos; The liquid phase was provided by the dissociation of GasbS particles into liquid gallium and antimony above 555°C. This not only enhanced grain regrowth and densification, as in unalloyed GaSb,&apos; but took on additional importance here for the alloying process. Alloying was speeded up by the resulting liquid-solid interaction as compared to the very slow solid-state diffusion process normally expected at these temperatures.&apos; The results obtained with a series of powder mixtures have been compiled in Table I. It is seen that for mixtures with less than 20 mol pct GaAs, x < 0.2, the compositional ranges increased and for x > 0.2 a GaAs-rich phase and free antimony appeared in the microstructure in sizable amounts.

Jan 1, 1968

By J. J. Calaman, D. H. Fleming

DURING 1950 the jet-piercing process was used commercially in the piercing of primary blast-holes in magnetic taconite at the preliminary taconite plant of .the Erie Mining Co., Aurora, Minn. The Erie Mining Co. purchased a jet-piercing machine and associated equipment in 1949, and the machine has been in operation since its installation in the summer of that year. An overall view of the pit with the JPM-1 jet-piercing machine in operation is shown in Fig. 1. During three months of 1949 and continuously since February 1950, production piercing took place under all pit conditions. By the end of October 1950, a total of 15,000 linear ft of hole had been pierced in an open pit handling an average of 1200 to 1800 tons of crude a day in one 8-hr shift. While it is recognized that this output does not approach the millions of tons a year planned for the developing Minnesota taconite projects, the machine as a unit has been operating under conditions probably more adverse than those that eventually will be encountered in the large operations. This pilot operation has permitted evaluation of the piercing problem in the full-scale taconite plant. This paper describes jet-piercing process funda- mentals, important features of the latest jet-piercing burners and machine, actual piercing results obtained, and new developments that give promise of materially increasing overall process efficiency. To produce the blasthole, jet-piercing utilizes thermal energy, as contrasted with the application of mechanical energy in churn drills and jackham-mers. The heart of the process may be termed a tailored flame produced by a rocket-type burner, thermodynamically similar in every respect to that of the giant rockets being developed for military purposes. The heat release in the combustion chamber of the burner is about 50x10&apos; Btu per cu ft per hr as compared with 5x10&apos; for most modern steam generators.* Combustion of liquid petroleum fuels (kerosine, diesel oil, or No. 2 fuel oil) with gaseous oxygen in the burner chamber at pressures of 100 to 200 psi results in temperatures of about 4300°F. Expansion of the hot combustion gases through divergent nozzles produces high-temperature supersonic jets having measured velocities of about 6000 fps. Impinging the flame jets on rock causes a thin surface layer to expand and break away from the base as a result of the thermally induced stresses. This spalling action is aided further in chert and quartzite by the 0.82 pct volume change resulting from the 6 to p quartz inversion at 1066"F.t The dynamic action of the jets whisks the spalled rock

Jan 1, 1952

By Edmund Davenport

Tier; production of thorium of high purity by the Ca-CaCl2 reduction has been described by Marden and Rentschler,1 who also reported some of the properties of the coherent, ductile metal obtained from this pure thorium powder. The present paper describes the properties of thorium produced by the Ca-CaCl2 process modified in some details to meet commercial conditions. The principal effect of these changes in process has been an unavoidable increase in the oxide content of the thorium.

Jan 1, 1929

By S. Andrew Kulin, L. Kaufman

A general treatment of the broadening of X-ray double-crystal spectrometer rocking curves due to distributions of tilts and strains has been carried out. The results of this treatment have been applied to the case where dislocations in a crystal give rise to both tilts and strains. On this basis it is found that the rocking-curve halfwidth due to imperfections in the crystal, ßC , increases with increasing Bragg angle, 8. These considerations predict linear relationships between & and tan2 , and ßCand tan 8, for Gaussian and Cauchy distributions of dislocations, respectively. The zero intercept of the ßC us 8 curve, which is a measure of the degree of imperfection of the crystal, is found to depend directly on the distribution rather than the number of dislocations. In addition, the slope-intercept ratio for the ßc - ? curve has been calculated for both the Gaussian and Cauchy distributions. Experimental determination of the - 8 curves for a series of copper single crystals prepared by the Bridgeman and Czochralski methods yields results in agreement with the calculated slope-intercept ratio for a Cauchy distribution of dislocations. CERTAIN X-ray techniques have been used to study the perfection of single crystals. Gay, Hirsch, and Kelly have considered the spreading of spots into arcs on Debye-Sherrer rings due to imperfections. The Double-Crystal Spectrometer has also been applied to this problem.2 The characteristics of Double-Crystal Spectrometer Rocking Curves have been described in the literature by various workers.2-4 By assuming a random spacing of dislocations which give rise to a Gaussian distribution of misorientations relative to some mean orientation in a crystal Gay, et al.,1 arrive at the conclu- sion that the most probable misorientation is given by where h is the spacing between dislocations, and 8 and are the relative misorientations of neighboring regions. If ßC is the halfwidth of the rocking curve (the width at one-half the peak intensity) due to dislocations in the crystal then5

Jan 1, 1960

By Robert Maes, Robert de Strycker

The solidifzcation reactions in the Cu-Sn-As system were determined by microscopic examination, thermal analysis, and X-ray diffraction. The system presents no ternary compound. There is a quasi-binary section, of a simple eutectic type, between the compounds Cu5As2 and SnAs; the system presents, in addition, one ternary eutectic reaction, one ternary peritectic reaction, and seven transitional reactions. The temp-peratures corresponding to each of these reactions were determined, most of them with an accuracy of *lLC. The isothermal lines of the liquidus surface were also established for almost the entire diagram. NO reference was found in the literature relative to the Cu-Sn-As phase diagram and this is believed to be the first study on this subject. The Cu-Sn diagram was taken from Hansen and Anderko;&apos; it is represented by Fig. 1, with the phase designation which will be used in the remainder of this work. For the Cu-As diagram, the solution proposed by Hansen and ~nderko&apos; must be modified to take account of recent data, principally from Heyding and Despault~ and from Hume-Rothery and Burns; this yields the diagram represented by Fig. 2. As for the Sn-As diagram, it is not established with certainty, particularly so far as concerns the solid solubility of tin in arsenic and the solidification reactions near the compound SnsAsz. For this last point, Hansen and Anderko propose two solutions: congruent melting of Sn3Asz with a eutectic SnsAsZ + SnAs or incongruent melting implying a peri-tectic reaction L + SnAs = Sn3As2. Microscopic examination of the few binary alloys prepared in this composition range made us prefer the second of these solutions, which gives the diagram shown by Fig. 3. EXPERIMENTAL METHODS The experimental techniques used in this work were microscopic observation and thermal analysis; a few X-ray diffraction patterns were taken to verify the

Jan 1, 1967

By Howard Scott

Invar is the preeminent low-expansion metal by virtue of the fact that it can be prepared with a zero coefficient of expansion at atmospheric temperature. This fact suggests that there is little room for improvement in the expansion properties of the low-expansion nickel steels. The inference is true, however, only so far as the expansion at and near atmospheric temperature is concerned, because the expansivity of invar starts to increase rapidly on heating above 100" C. and soon reaches the value of copper. Guillaumel met this situation by increasing the nickel content above that of invar. By that expedient, alloys having low expansivity under higher temperatures were obtained, but not without a large increase in minimum expansivity. The increase in minimum expansivity with increasing nickel content severely limits the technical applications of these alloys at high temperatures. Prospects of improving the expansion characteristics of the nickel steels is offered by alloying. Search for an advantageous alloying addition by analogy with other alloy systems, however, is not productive because the low-expansion characteristic is unique with that system. The rule of mixtures usually gives a fair value of the expansivity of other solid-solution alloys, but in the iron-nickel systems gives a value of 18 X 10-6 per deg. C. whereas the actual value is 1 X 10-6 per deg. C. Apparently suitable additions are not to be deduced from such ingenuous considerations. Recognition of the fact that the temperature range of low expansivity in nickel steels is terminated with loss of magnetism affords a more promising basis for the selection of an advantageous element. One may expect from that fact that additions of nonmagnetic elements to the iron-nickel alloys are detrimental to the low-expansion characteristic. Indeed, carbon, manganese, silicon, copper and chromium are detrimental to the expansion properties and no nonmagnetic element is reported to be beneficial. From the same viewpoint, the addition of a magnetic metal offers prospects of improvement. As two of the three ferromagnetic elements are already present in the

Jan 1, 1930

By L. S. Castleman, L. L. Seigle

THE formation and growth of intermetallic phase layers is of considerable practical importance to metallurgists interested in diffusion bonding and cementation processes and has been the subject of extensive qualitative investigation. In contrast, it is somewhat surprising that so little quantitative data have been amassed. The need for additional fundamental work was pointed out by Mehl in 1936,&apos; and persists to a large extent to the present day. The early studies have been reviewed by Rhines,2 and his conclusions have been summarized by Lustman and Mehl3 substantially as follows: 1) All phases that are stable at the temperature at which diffusion occurs will appear in the interdiffusion of two metals; however, in some cases, certain of the phases may be too thin to be observed and identified easily. 2) The isothermal growth of intermetallic phases generally obeys a simple parabolic equation of the form X2 = Kt, where x is the thickness of the alloy layer, K the temperature dependent reaction rate constant, and t the time. 3) The rate of thickening varies with temperature according to the Arrhenius equation k = Ae -Q/RT , where k is the parabolic rate constant, A, a temperature independent constant, Q the heat of activation for the process, R the gas constant, and T the absolute temperature. Subsequently, Lustman and Mehl made a quantitative study of the laws of growth in intermediate layers in a number of binary systems, in which one of the components was either zinc or cadmium, and the other component was one of the following: nickel, copper, silver, cobalt, gold, iron, or Monel metal; the interdiffusion times used were for the most part less than 24 hr. It was found that the simple parabolic law was not obeyed in general, but that a generalized parabolic law of the form xn = kt was valid, where n was a temperature dependent constant; also,

Jan 1, 1959

By Werner Langguth

The modern process and plant for the precipitation of gold from chlorine solutions, by sulphurous acid gas and hydrogen sulphide, differ materially from the older methods of precipitating with sulphate of iron. The chemical process and its applicability, as carried out in the Golden Reward chlorination-works at Deadwood, S. D., was described and discussed in the Engineering and Mining Journal, of New York, for February 14, and March 21, 1891. I purpose to give, in this paper, the details of construction from a general standpoint—the particular arrangement, most suitable to each case, depending, of course, upon local conditions. The accompanying sketch shows the arrangement. The plant consists of a wooden, lead-lined tank, in which the chlorine solution is precipitated; apparatus for the production of the precipitants, sulphurous acid and hydrogen sulphide; and a pressure-tank and filter-press for the collection and filtration of the precipitated gold-sulphides. These parts and arrangements are, in general, those which I employed in the Deadwood chlorinationworks, and which have proved practically successful, more than $100,000 worth of gold having been already precipitated by this method. In the construction of the generator and pressure-tank I have made, however, a few slight changes. 1. The Precipitating-Tank. The exact dimensions of this tank are not of much importance. A horizontal area of 10 x 12 feet and a height of 12 feet, holding about 7000 gallons of solution, is a good size. As the amount of attention and care required to precipitate the solution in a precipitatingtank is independent of the size of the vessel, there is economy in tanks of large capacity. Square tanks are more advantageous than round ones, because they need less floor-space, and at the same time are cheaper in construction. These tanks are made of common 2inch pine boards and 12 x 12-inch timber. They are well-bolted,

Jan 1, 1893

By T. W. Guy

THE increased moisture due to water¬spraying for coal dust control is of interest even for mines from which the coal is to be wet-washed before screening, because in many cases wet coal dust materially decreases the loading efficiency of men an equipment at the faces. It also causes serious increase in the normal wear and deterioration of all equipment with which it comes in contact. It is important to the consumer if it increases his as-receive moisture. No attempt will be made in this paper t cover the entire subject of water-spraying of coal for dust control. It will be confine to discussion and data on (r) percentages c dust in bituminous coals, (2) moisture increases due to spraying for dust control in mines or plants by methods which have proven satisfactory for periods of one to five or more years, and (3) a few suggestions for research. SIZE AND PERCENTAGE OF COAL DUST The U. S. Bureau of Mines1 classifies a coal dust all bituminous coal passing 20-mesh sieve (0.0328 in. square opening; The percentage of such dust to be found is ROM coal, of course, varies widely wit. the characteristics of the seam, and with the methods used in the mining and in the preparation of the coal. ROM screen analyses of 12 U. S. coals selected at random from personal files given in Table I show: A few other screen analyses examined indicating 40 pct or more of 2o-mesh X o dust in 3/8 in. X o-sizes were not included because of uncertainty that they were representative. The number of results in Table I is not sufficient to give a reliable estimate of the average, or of the range to be expected, but it indicates that in every case the coal dust is a relatively large percentage of the total ROM coal, and, of course, a progressively larger percentage of resultants as the larger sizes are separated for marketing.

Jan 1, 1948

By C. E. Van Orstrand

AN intrusive body is a mass of igneous rock that has migrated upward, presumably from great depths. Great variations in form, composition and depth of burial occur. It is not proposed in this paper to go into all of the details of the problem. Instead, it will be assumed here that the intrusive has the form and characteristics represented in Fig. I. According to W. H. Emmons,1 minerals are not deposited in appreciable quantities below the "dead line." Important amounts of ores of virtually all metals may be found around summit cupolas, but only gold, copper and zinc (in limited quantities) are usually associated with trough cupolas. Most students of ore deposits agree that temperature changes are largely instrumental in precipitating many ores in the "hood" and that the difference in temperature between the intrusive and that of the country rock may be the chief factor in determining the mineralogy of a deposit. A problem then of some interest is to correlate the principal physical features of the intrusive with the phenomena of heat conduction as evidenced by the cooling curves and the isothermal surfaces. MATHEMATICAL THEORY In order to show the possible application of heat conduction to the interpretation of the processes of metalliferous deposition associated with intrusives, it will be assumed that the intrusive is a large parallelopiped of dimensions, 2l, 2m, 2n. The equation that represents the flow of heat from the parallelopiped into country rock (v = o, t = o), which has the same thermal properties as the intrusive, is2,3 [ ] In this equation, the origin, x = o, y = o, z = o, is at the center of the parallelopiped. &apos;v = temperature at point x, y, z, time t. vo = initial temperature throughout the intrusive, t = o. K = coefficient of thermal diffusivity. a, ß, ? are variables of integration. Put n = m in Eq. I, and we have [ ]

Jan 1, 1944

By J. J. Strohl, H. J. Schwellenbach

This paper relates the results obtained by decreasing the size of feed to a rod mill screen circuit. As would be expected, added production was gained and a finer grind with no tonnage loss was made possible. THE MacIntyre mill of the National Lead Co. has four parallel sections in which magnetic and gravity separations are made. Ore from a 5000-ton bin is fed by Hardinge constant weight feeders to a 6x12-ft open-end Marcy rod mill in each section. Rod mill discharge is bucket elevated to two 4x10-ft Tyrock screens whose oversize is returned to the rod mill. Screen undersize is pumped to Crockett separators for magnetite removal, and the Crockett tailings are sized and tabled to make an ilmenite concentrate. Minus 200-mesh material, overflowed by the Crockett and Dorrco sizers is thickened, de-slimed, and concentrated by flotation.&apos; By 1948, the development of a successful slime flotation process and numerous improvements in the gravity circuit of the mill had increased the capacity of the available concentrating equipment. At the same time, improvements in the operating techniques of the dry crushing plant and improved feeding of the crusher by the mining department had appreciably increased the production rate per operating hour in that plant. Therefore, it was decided to take advantage of the added crusher capacity to produce a finer rod mill feed and in that way increase grinding capacity. At approximately the same time, finer screens were installed in the rod mill circuits to give finer grind and thus improve liberation of the magnetite and ilmenite from the gangue and from one another. Prior to the first part of 1948, a 3/4-in. limiting screen was used for sizing rod mill feed. The first reduction in crushing plant screen size was to 1/2 in. With this screen, the circulating load in the tertiary crushing circuit was too high and plant capacity dropped below a practical hourly rate. A 9/16-in.-sq opening screen, installed next, proved satisfac-

Jan 1, 1951