By J. L. Tokich, A. R. Troiano

INTRODUCTION SINCE 1921, when Hull' discovered that cobalt can exist in the face-centered cubic and hexagonal close-packed modifications, the transitions that occur in cobalt have been extensively studied. It is generally agreed that on heating the hexagonal lattice changes to the cubic structure at temperatures ranging from 400 to 500°C although considerable doubt exists as to the exact temperature. Data concerning the temperature of the transformation on cooling are much less concordant and their interpretation has not been satisfactory. The study is further complicated by the fact that many investigators have reported the existence of a high temperature allotropic change in the range 850 to 1020°C, at which the cubic lattice reverts to the hexagonal modification. The transition on cooling, which has been reported as occurring at various temperatures from approximately 400 to 100°C, is of particular interest. Troiano and Greninger2 have recently suggested and considered the possibility of allotropic transformations occurring in pure metals by a shear-type, diffusionless (martensite) transformation. The case of cobalt was specifically discussed and certain observations of previous investigators evaluated in terms of this type of transformation. Table 1 briefly outlines the methods and results of previous investigators of the transformation temperatures of cobalt. MATERIALS AND METHODS The major portion of this investigation was performed with cobalt sheet containing a total of 0.2 pct impurities with carbon present to the extent of 0.1 pct. After melting in an induction furnace under an atmosphere of hydrogen, the carbon content analyzed 0.03 pct. Some observations were repeated with hydrogen reduced cobalt compresses analyzing 99.9 pct pure. No significant variations in results were observed employing the as-received sheet, the remelted stock, or the cobalt compresses. Filings for X ray diffraction analysis were sealed in evacuated glass ampoules. Pyrex glass tubing was used for temperatures below 600°C and for higher temperatures clear fused quartz was satisfactory. After appropriate heat treatment at various temperatures, the specimen ampoules were furnace cooled, air cooled or quenched by crushing under distilled water. This allowed a range of cooling velocities from less than one degree C per sec to greater than 1,000°C per sec. X ray diffraction patterns were taken with a Debye camera and filtered characteristic cobalt K-alpha radiation. The proportion of the existing phases was roughly approximated by visual examina-

Jan 1, 1948

By Richard P. Rothwell

A REFERENCE to the geological map of Alabama shows the coal- measures of that State to form three distinct fields. The Coosu, or most easterly, contains about one hundred square miles ; the Cahaba, or middle field, which is also the most southern true coal in the United States, contains about 230 square miles ; and the Warrior field, which contains in the State of Alabama some 5000 square miles, is the southern extremity of the great carboniferous deposit, which extends through Pennsylvania, West Virginia, Kentucky, Tennessee, and Georgia. But very little has yet been done towards developing those coal- fields, partly owing to the absence of all commercial manufacturing enterprise in the South under slavery, and partly owing to the want of capital and the disturbed condition of the South since the war. During the past three or four years I have devoted a large part of my time to the examination of the coal and iron ores of this range,

Jan 1, 1874

By Don M. Jackson

The techniques for the growth and controlled, graded doping of silicon epitaxial overgrowth layers were established. Grading of- impurities such as arsenic or boron in arbitrarily chosen profiles oiler four orders of magnitude (from I X 10Lg to 1 X 10L5 cm) was accomplished. The graded structures were grown in a stepwise manner where in the profiles were approximated by growing many separate layers with small doping-level changes between layers. Masked-area growth of silicon through windows in a SiO2 masking film was acconiplished through the simultaneous injection of HCl gas 102th Sic14 in the epitaxial reactor. The HCl served to inhihit the growth of silicon on the Sz02 surface, and also to control the cross-sectional profile of the silicon mesas. silicon from the substrate was etched out through the windows, and then epitaxial material was used to fill the holes hack in to form planar diodes. Simullaneous HCl injection was adapted to control the cross-section profile of the hack-filled regions. Arsenic-huried regions beneath in te- In recent months, the epitaxial growth process in semiconductor materials technology has evolved into a complex system directed at both material improvement for better monolithic integrated-circuit characteristics and the development of new silicon structures for future integrated-circuit needs. The advent of high-temperature HC1 gas etching1 grated-circuit transistors reduced V(SAT) by slightly more than one third, bringing this parame-ter to that of an isolated component transistor. When arsenic was diffused into the starting sub-stvate, it was necessary to remove any excess arsenic in order to avoid excessive audodoping of the subsequent epitaxial layer. Oxide isolation of single-crystal regions in a substrate provided complete electrical isolation of integrated-circuit components, thereby eliminating parasitic capacitance which is inherent in standard integrated-circuit processing. The process involved the etching of deep mesas on silicon Wafers, the formation of an oxide over the mesa surface, and then the deposition of several mils of polycrystalline silicon over the oxide. The original substrate was lapped and polished allay until the mesas were left isolated in the polycrys-talline matrix. The Final components were fabri-cated in the single-crystal islands. Speed and power-handling capabilities of standard circuits were improved through the process. wherein work-damaged material is removed from the surface of the silicon wafer just prior to the silicon deposition step has made it possible to grow silicon films with structural quality that approaches that of the substrate. HBr used in the same volume ratio as HC1 etches silicon at the same rate and with the same results as HC1. Recent developments in epitaxial materials technology have occurred in the areas of precise doping control, buried prediffused regions between over-

Jan 1, 1965

By D. E. Trout, W. R. Hibbard

Previous investigations have shown that the cold rolling textures1n2 and the drawn wire textures3 of copper change their secondary components after the addition of about 1 pct aluminum and 5 pct zinc, but do not change after the addition of as much as 30 pct nickel. However, few data are available on compression textures. Barrett4 reports from unpublished work with E. L. Layland that compression rolled copper develops a texture which is predominately (110) in the compression plane with a secondary spread to (113) and weaker spread to (100) as shown in Fig 1. However, 70-30 alpha brass similarly treated develops a texture again predominately (110) in the compression plane and with a weak secondary spread to {113} but with moderate (111) secondary intensities illustrated in Fig 2. Experimental Procedure Specimens of the compositions shown in Table 1 remaining from a previous investigation3 were annealed to a grain size of 0.090 mm average diam and machined to cylinders 0.20 in. diam and 0.20 in. high. Cylinders were compressed 90 pct reduction in height between lubricated steel blocks in a tensile machine. Glancing X ray photo-grams using copper K-alpha radiation were taken at an angle of 0 degrees to the compression surface. (111), (002) and (220) rings were analyzed to define the textures shown in Table 1. The results are in agreement with Barrett4 as to types of textures and are essentially in agreement with previous work1,2,3 as to the effects of composition. In the wire study3 it was reported that the 4.99 pct zinc alloy had a brass-type texture, while the data in Table 1 indicate a copper-type texture for compression. The wire specimen of the 4.99 pct zinc alloy was re-examined by X rays and it was established that the [loo] component still exists in the wire axis. Therefore, Table 2 of Ref. 3 is in error and should indicate a double [ill], [loo] copper-type texture for this alloy. This correction results in complete consistency with regard to compositional effects, namely that copper and its alloys containing up to approximately 1 pet aluminum, 5 pct zinc and at least 30 pct nickels develop a copper-type texture and more concentrated copper-aluminum and copper-zinc solid solution alloys will form a brass-type texture. Summary Compression textures developed in copper and its alpha solid solution alloys of aluminum, nickel and zinc are essentially the same types as those re- ported by Barrett4 with compositional effects occurring at approximately the same percent additions as previously reported for rolled sheet182 and drawn wire.3 The Scovill Manufacturing Co., Waterbury, Conn., furnished the copper and brass alloys, performed certain chemical analyses and supplied laboratory facilities where needed. References 1. Brick, Martin and Angier: Tram. A.S.M. (1943) 31, 675. 2. Dahl and Pawlek: Zlsch. Melall. (1936) 28, 266. 3. Hibbard and Yen: Trans. AIME 175, 126. Melals Tech.. Feb. 1948, TP 2334. 4. Barrett: Structure of Metals, mc- Graw-Hill (19421, 386.

Jan 1, 1950

By R. W. Raymond

In my paper on " End-Lines and Side-Lines in the Mining Law," read at the New York meeting of February, 1889 (Trans., xvii., 787), I discussed certain points involving the rights of a locator, B, who had located and surveyed a piece of ground, X + Y, of which only Y was properly subject to location, X being already held by another claimant, and had applied for and received a patent, granting X + Y, " excepting and excluding X." The paper concluded with the following questions : " Is there any difference in effect between the grant to him of Y simply and the grant of X + Y, ' excepting and excluding X' ? Why should any mining locator stake out his boundaries upon another location, and thus appear to assert a claim which he immediately withdraws? What is the legal force of such boundaries, established upon the land of another?" After calling attention to the fact that the entrance upon another's land for such a purpose is a trespass, and the principle that no trespasser can create by his trespass any right which he would not have without it, I reserved to another occasion a review of the history of the absurd practice of imaginary boundaries for mining claims, and a discussion of their legal effect. This practice is founded, of course, in the regulations and decisions of the United States General Land Office. There is nothing in the Revised Statutes which hints at it. On the contrary, the terms of Section 2322, giving to a locator " the exclusive right of possession and enjoyment" of the surface of his claim, seems clearly to forbid the use of that surface for the boundary-stakes of another locator. But the Act of 1866, though it provided for the issue of patents upon payment to the Government of so much per acre, and really by implication (as I have always believed) involved the absolute grant of the surface, was not so construed by the courts generally, or by the Land Office. Surveys were laid one over another in inextricable confusion, and the United States sold at $5 per acre the

Jan 1, 1890

By D. A. Elgillani, M. C. Fuerstenau

With either sulfonate or oleate as collector, quartz responds to flotation with moderate additions of calcium only at moderately high pH, where some portion of the activator has hydrolyzed to caOH+ . Calculations of the concentrations of various ionic and precipitated species of calcium and collectors suggest that the products of [(CaOH+) (RSO3)] and [(CaOH+)(01-)] determine whether flotation is obtained under specific conditions. Ion products on the order of 10-12 were calculated for both the sulfonate and oleate systems. The activating effect of calcium ion in nonmetallic flotation systems is of considerable interest because of the normal presence of calcium in natural water. As a result, this phenomenon has received quite some attention in the past. Kraeber and Boppel1 showed that quartz could be activated by calcium above pH 10 with sulfonate as collector. The feasibility of selectively separating quartz from hematite with calcium activation at relatively high pH was demonstrated by Clemmer, Clemmons, Rampacek, Williams, and stacy.2 Cooke and Digre3 showed with a bubble pick-up method that the minimum quantity of calcium ion required as activator for complete pick-up of particles occurs at pH 11.5 for an addition of 20 mg per liter sodium oleate. They also showed that larger additions of calcium (10-fold increase per unit decrease of pH) must be added for complete bubble pick-up as the pH is reduced. Schuhmann and Prakash,4 using a vacuum flotation technique, found that quartz could be floated with moderate additions of calcium chloride and oleic acid at neutral pH, providing the metal ion was present in stoichiometric excess over the quantity needed to form the normal soap with oleic acid. They also reported that calcium will function as an activator only in basic media. More recently, Eigeles and volova5 have shown that essentially complete flotation of quartz is obtained with 6 x 10-4 mole per liter calcium chloride and 1.7 x 10-5 mole per liter sodium oleate at pH 11.6. while no flotation is obtained at about pH 10.9 and below. The importance of adsorption of activator and collector at the air-liquid interface is also demonstrated in these systems. The important role that metal ion hydrolysis assumes in quartz activation systems was also demonstrated recently.6-8 A detailed investigation of metal activation in sulfonate flotation of quartz was undertaken in one system7 and yielded a number of interesting and important observations. Quantification of the data of this system7 to the extent desired was not possible, though, because certain species could neither be ignored nor accounted for accurately. These difficulties can be circumvented when calcium is involved as activator. This detailed analysis was undertaken to obtain a more quantitative explanation of calcium and metal ion activation in quartz flotation. EXPERIMENTAL MATERIALS AND METHODS Sodium alkyl aryl sulfonate9 mol wt 450, and pure potassium oleate were used as collectors. All other reagents used were reagent grade in quality, i.e., n-amyl alcohol as frother, KOH for pH adjustment, and calcium chloride. Conductivity water, made by passing distilled water through an ion exchange column, was used in the investigation. Quartz was prepared by leaching the sized sample (48 x 150 mesh) with HC1 until no iron could be detected in the leach liquor. The experimental equipment and procedure were the same as that described previously.6,10 EXPERIMENTAL RESULTS As the presence of precipitates was noted in all of the systems to which ca++ and collector were added, experiments were undertaken to determine the solubility products of calcium sulfonate and calcium oleate using a nephelometer. With this technique, collector is titrated into a known solution, which in this case was 5 x 10-5 mole per liter CaCl2 at pH 5.5. Upon precipitation of the calcium-col lector salt, e.g., calcium oleate, light is scattered and detected

Jan 1, 1967

By C. G. Dunn, P. K. Koh

THE primary recrystallization texture in cold-rolled silicon iron, which is the matrix texture for developing the Goss texture or the cube-on-edge texture by secondary recrystallization at temperatures near 900°C,1-5,21 has not been adequately described. Thus from the present available information, it is not possible to explain satisfactorily both the grain-growth selectivity of the matrix and the often observed magnetic torque curve, which itself provides some information on the texture. Also lacking is information on the special annealing texture that develops in this material when the annealing temperature is 1200°C or higher and the rate of rise to temperature is extremely rapid. From the work of May and Turnbull5 and from unpublished work, it was known that isothermal annealing near 1200°C tends to reduce the extent of secondary recrystallization and that a much weaker cube-on-edge texture results if appreciable normal grain growth replaces secondary recrystallization. Koh and Dunn6,7 have obtained additional information on complex primary recrystallization textures from further studies made after normal grain growth. In these instances the initial textures were retained during normal grain growth. A similar result reasonably could be expected in the present study except for the presence of a grain growth ihibitor1-5,8,9.21 and its tendency to allow only a few grains to grow. However, any information on the orientations of grains in the special annealing texture, even if far from representative of the initial matrix texture, would provide useful information on the nature of the matrix texture. In the present texture study the method of Newkirk and Bruce,10 which is based on the methods of Geisler" and Schwartz, 12 is used to obtain a complete (110) pole figure of the primary recrystallization texture. The high-temperature annealing texture is determined simply from the orientations of a large number of selected grains. The kinetic nature of the process that produces the annealing texture is treated elsewhere13 and it is shown that a form of secondary recrystallization with a very high rate of nucleation occurs during rapid annealing at high temperatures. EXPERIMENTAL PROCEDURE Commercial 0.014-in. cold-rolled silicon iron strip (3.16 wt pct Si), prepared by two stages of cold rolling with an intermediate short anneal, was given a decarburizing 3-min anneal at 800°C. Me-tallographic studies indicated complete recrystallization. Short-time anneals at 900° C and at higher temperatures proved that secondary recrystallization had not begun at 800°C, in fact, the short additional anneals were still in the induction period of secondary recrystallization. A rapid rise to an annealing temperature of 1260°C (2300°F) was obtained in a BaC12and NaCl fused salt bath. The structures that resulted from anneals in the range 12- to 1000-sec duration were relatively finegrained, even though the growth was a form of exaggerated grain growth13 or secondary recrystallization with a high nucleation frequency.= Many of the grains were large enough for an X-ray study using a 5-mil X-ray beam. A transmission Laue Camera and an optical-mechanical stage for moving the grains into the X-ray beam were used. A total of 325 grains were X-rayed in this manner and the grain orientations determined. Complete (110) pole figures were obtained for the primary recrystallization texture using CoKa radiation at 30 kv in the back-reflection range, such as (220) for (110) poles, as described recently by Newkirk and Bruce.10 The low voltage serves to reduce the spurious white radiation to a minimum. A filter of 0.001-inch iron foil was located in front of the detector slit for transmission and in front of the beam slit for back reflection. A new and improved specimen holder extended the useful tilting angle range for transmission to 70 deg instead of 60 deg as previously reported.' A torque magnetometer was used to obtain the magnetic torque curves for a number of l-in. diam disk specimens. RESULTS The (110) pole figure of the material after recrystallization at 800°C is shown in Fig. 1. The positions of the pole concentrations are found to be

Jan 1, 1961

By D. Cox, M. J. Duggin, L. Zwell

The carbides of approximate composition and Mn have been studied using X-ray diffraction techniques. Those carbides of the type (Fe,Aln)zC ave isostructural with cementite. The cell pararmeters a and c have minimum values at approximately 10 at. pd substitution of manganese for iron; no satisfactory explanation has yet been found for this phenomenon. The carbide fFeMn4)C has a monoclinic unit cell whose dimensions are close to those of ,11,15Cz A neu-troip-dij~ractiot~ study of (F'eAlrz4)C~ reveals that, like MnsCZ, it is isostructural with Pd5Bz. The iron and manganese atoms occupy the palladium atom sites, while the carbon atoms were found to have the same atomic coordinates as the hovon atoms. A neutrorr-diffraction study of indicates that the carbon-atom positions are very close to those occupied in (Fez.,ll/lr~,.3)C. In both carbides studied, tlre iron and manganese atomzs were found to be essentially randomly distributed, although, in the case of (Fe,.811fn1.2)C, it is possible that there may be a slight preference of manganese atoms for- the general (d) positions and a corresponding slight preference of iron atoms for the special (c) positions. It has been found that a complete range of solid solution exists between Fe3C and Mn3C at 1050°C,I although Mn3C becomes unstable when the temperature is reduced to 95O0C,' and can only be retained by rapid quenching. It is also known that a complete range of solid solution exists from Fe5Cz to M~SC~,~ although the stability range of carbides of the type (Fe,Mn)sCz as a function of the relative proportions of iron and manganese is not known. X-ray examinations of Oh-man's carbide3 and Spiegeleisenkristall,~ which have the approximate compositions (Fe3.67Mnl.33)C2 and (Fe3-,Mn,)C, where x lies between 0.4 and 1, respectively, have been made. The following carbides have also been studied: ] The lattice parameters determined during these investigations are listed in Table I. It is seen that carbides of the type (Fe,Mn)sCz have a monoclinic unit cell while carbides of the type (Fe,Mn)3C have an orthorhombic unit cell. It is evident that the variation of lattice parameters with manganese content is not linear for carbides of the type (Fe,Mn)3C. The coordinates of the atoms in (Fe2.7Mno.3)C have recently been determined by single-crystal analysis., The fractional atomic coordinates have been shown by Fasiska and jeffrey to be in good agreement withj those deduced from an earlier analysis of Fe3C by Lipson and etch.' However, it was impossible to determine whether iron and manganese atoms occupied ordered positions because of the small difference between the atomic scattering factors of iron and manganese. The atomic positions in Mn5Cz (Refs. 8 and 9) and Fe5C2 (Refs. 7 and 8) have been obtained only by comparisons made with the isostructural compounds P~SB~.' Since X-ray diffraction techniques were used in these investigations, accurate positioning of the carbon atoms, which have a low atomic scattering factor, was difficult. No attempt has been made to determine the atomic positions in the other carbides previously studied. It was felt that an investigation of the lattice parameters of a number of intermediate carbides of the types (Fe,Mn)sCZ and (Fe,Mn)& would be of interest. It seemed likely that a neutron-diffract ion study of such carbides would indicate whether ordering occurred between the iron and manganese atoms because of the large difference between the neutron-scattering cross sections of iron and manganese. It also seemed probable that such an investigation would provide a determination of the atomic coordinates of the carbon atoms. I) EXPERIMENTAL DETAILS Specimens, each weighing approximately 20 g, were carefully prepared according to the following proportions: The components were 500-mesh powders of 99.995 pct purity iron and spectroscopically pure carbon and a 200-mesh powder of 99.995 pct purity manganese. The component powders were intimately mixed by prolonged shaking, then each specimen was inserted into a spot-welded cylindrical container of tantalum foil, whose end was closed but not sealed. Each specimen in its envelope was then sintered at 1050° C for 24 hr in a thin-walled evacuated quartz capsule, such a time having been previously found sufficient for equilibrium to be attained.' Each specimen was then quenched in order to attempt to retain the high-temperature phase, as the literature indicates that transformations may occur on cooling. Debye-Scherrer X-ray photographs were taken of each specimen using a 114.6-mm-diam camera, Fig. 1, patterns 2 to 6. The exposure time was 6 hr using filtered iron radiation at a tube voltage of 40 kv and a tube current of 12 ma.

Jan 1, 1967

By A. H. Daane, A. S. Wilson

The U-Cr system is of the simple eutectic type with some solid solubility of chromium in r and ß uranium. The eutectic occurs at 20 atomic pet Cr and melts at 859°C. The maximum solubility of chromium in y uranium is 4 atomic pet at the eutectic temperature, and in ß uranium the solubility is estimated to be 1 atomic pet. y-ß and ß-a transformations were found to occur at 737°estimatedt° and 612°C respectively. DURING 1944 and 1945, the U-Cr constitution diagram was studied in this laboratory as a part of a research program on uranium metallurgy in the Manhattan Project, and the work was described in a Manhattan Project report issued in December 1945. This paper is based on that report, which has been declassified. Prior to this study, it had been shown by other Manhattan Project workers that the low Cr-U alloys could be quenched to retain the form of uranium. Experimental The uranium used in this work was massive metal prepared in this laboratory and contained less than 0.1 pct of other elements. The chromium was 200 mesh powder obtained from the A. D. McKay Co. and was found on analysis to be 99.5 pct Cr with 0.3 pct Fe the major impurity. Alloys, weighing 400 to 600 g, were prepared by induction heating the components to 1700°C in slip-cast ZrO, crucibles in a vacuum of 3x103 mm Hg. TO prevent too violent agitation of the melt by the induction field with subsequent crucible breakage and sample loss, the ZrO2 crucible was placed in a graphite crucible, which was surrounded by a layer of powdered carbon insulation 2 to 3 cm thick. Polished vertical sections of the alloys were examined microscopically to confirm their homogeneity. Heating and cooling curves were taken on the alloys by reheating them in ZrO, crucibles to 1200°C and inserting a mullite-protected chromel-alumel thermocouple into the melt by means of a slip seal in the vacuum head of the furnace. A recording potentiometer traced the curves which had a slope of from 3" to 6" per min. Samples of the alloys were prepared for metallo-graphic examination by conventional mechanical polishing techniques followed by an electrolytic polish in an ethylene glycol-phosphoric acid-ethyl alcohol bath. The structure of the alloys was brought out clearly by this procedure so that no further etching was required. Samples for chemical analysis were taken from drillings from the top, center, and bottom sections of the alloys. The uranium was determined by titra-tion with Ce(SO1)2, while the chromium was titrated with FeSO,; the uranium and chromium totaled at least 99.6 pct in all of the alloys prepared. X-ray samples were prepared by filing bulk specimens in a helium-filled glove box and annealing the resulting powder in a zirconium-gettered helium atmosphere. A 114.6 mm diam Debye-Scherrer camera and a Weyland nonsymmetrical self-focusing camera were used with filtered copper radiation to obtain the powder X-ray diffraction data. Results The data obtained in this study have been combined to construct the constitution diagram of the U-Cr system shown in Fig. 1 where the arrests observed in cooling curves are indicated by dots. The liquidus arrest was quite distinct in thermal data taken on alloys in the range 0 to 20 atomic pct Cr. The eutectic arrest was not observed in studies on the 2.5 and 4.5 pct Cr samples but appeared in the 7.5 pct samples, which suggested some solubility of chromium in y uranium. On quenching from 859 °C, the 2.5 pct sample showed but one phase while the 4.5 pct sample contained a small amount of the eutectic along the grain boundaries; see Figs. 2 and 3. From this the maximum solubility of chromium in r uranium has been set at 4 pct. X-ray studies on these samples showed that the r phase was not retained at room temperature by quenching, but in each case a pattern was observed .which has been identified with the ß phase of uranium. Thermal data show the y-ß transformation of uranium lowered to 737°C as a consequence of this solubility. On quenching from the ß range (660°C), precipitation of chromium in the primary uranium is observed in the 2.5 and 4.5 pct Cr samples (see Figs. 4 and 5),

Jan 1, 1956

Discussion of the paper of F. M. Simonds and E. Z. Burns, presented at the New York Meeting, February, 1913, and printed in Bulletin No. 75, March, 1913, pp. 369 to 402. W. L. SAUNDERS, New York,. N. Y.:-Mr. Burns in his native Colorado modesty has said that he apologizes for things left out of this paper. I am much impressed by what he has put into the paper, as of all the papers that I have read on the subject, describing, as it does, a specific piece of work that has been accomplished, I do not recall one that gives so much information in such a practical way. Mr. Burns has also said that it is very hard to get men to put things down while the work is being driven. My experience is that it is very much harder to get the men in charge of work of this kind to bring them in in the form of a report before a body of engineers after the work is done. We have a great many cases where records are kept in much detail, but they are usually kept under cover, with the mistaken idea that the information gained is private information for the benefit of those who have done the work. Messrs. Simonds and Burns have opened up this case so that we can get the benefit of that experience which they have had, and so that we can learn something for the future. The description contained in this paper, as I have said, is a very practical one. You will notice in going through it. that the authors have given in detail a record of their work from the beginning to the end, and they even go so far as to publish an exact copy of the Rawley Mining Co.'s daily report. That daily report is something which those of us who are engaged in similar work might copy to great advantage, and having it before us we can check up our men while doing work and exact from them equal conditions, if it is possible to do so.

Jan 5, 1913

By J. Leja, A. Pomianowski

This paper deals with equimolar solutions of xanthate and alkyl trimethyl ammonium bromide adsorption on copper, nickel and sphalerite powders. After an exposition of the experimental methods used and the results obtained, a thorough discussion leads to the conclusion that some molecular association between xanthates and CnTAB's does take place in the bulk of the solution as well as at the air/liquid interface. A spectrophotometric study of xanthate solutions alone and their mixtures with equimolar amounts of alkyl trimethyl ammonium bromide (CnTAB) has established the additivity of ultraviolet spectra (190 to 400 mµ) for potassium ethyl xanthate (KEtX) and C12TAB. No obvious effect of C12TAB addition on the decomposition rate of KEtX was observed, the half life of which was established as 29±3 days at 22°C and pH ~ 6. In mixed solutions of longer xanthate homologues (e.g. hexyl and nonyl) and equimolar CnTAB, colloidal precipitates are gradually formed which contain primarily the corresponding xanthate molecules. The kinetics of collector abstraction by copper, nickel and sphalerite powders were studied in 10-5 to 10"3 M solutions of KEtX alone and in equimolar mixtures of KEtX and CI2TAB. Presence of C12TAB caused a two to three fold increase in the amounts of xanthate (equivalent to many monolayers) abstracted by copper and nickel powders (and in their rates of abstraction) but had no effect on the abstraction of xanthate by unactivated sphalerite (equivalent to less than a monolayer). The adsorption of C12TAB itself from the mixed solutions was very low, at most one monolayer only, and was not influenced by the nature of the solid powder used. A change in the rates of abstraction, observed with copper powder, was interpreted as a completion of a multilayer coating (completely enveloping the grains of powder) following which the rate of reaction between solution and substrate becomes controlled by diffusion through this coating. Work of Buckenham and Schulmanl on molecular associations between different collectors has shown unusual synergistic effects in flotation of individual minerals using mixtures of xanthates and alkyl trimethyl ammonium bromides. The objectives of the present work were: 1) to determine whether these molecular associations between the two types of collectors (indicated by strong surface tension lowering in Buckenham and Schulman's work) take place at the air/liquid interface only or in the bulk of solution as well 2) to establish whether different solids adsorb any species from the mixture of these amphipatic molecules preferentially or as molecular complexes 3) to establish whether there are any differences in the kinetics of adsorption. Metallic copper and sphalerite powder were chosen as adsorbents since they represent two extremes since copper readily adsorbs multilayers of xanthate (and is easily floated with ethyl xanthate) while unactivated sphalerite does not appreciably adsorb xanthate but is known to be readily floated by the amine type collectors. Metallic nickel was included because the infrared spectroscopic work2 on xanthate

Jan 1, 1964

By T. J. Koppenaal, M. E. Fine

A yield point effect attributed to short-range ordevi?g (SRO) occurs in Cu base Al. At at 296°K varies with heat treatment, decreasing as the annealing ternperature is raised .from 433Oto 598°K. Davies aid Cahn' observed a corresponding decrease in SRO. (523 °K anneal, measured at 77°K) is approximateZy proportional to the variations of A7 with strain rate and testing temperature are also Consistent with the idea that is associated with SRO. A preliminary investigation of the tensile properties of a Cu-Al single crystals showed the presence of a rather strong yield-point effect (drop in flow stress after initial yielding). The object of this research was to investigate its origin and behavior. a Cu-Al alloys are particularly interesting because diffuse X-ray scattering measurements by Davies and Cahn,' Houska and Averbach,' and Borie established the presence of short-range order. The degree of local order may be changed with heat treatment.' cottrel14 suggested that the presence of local order might result in a yield-point effect, and thus the possibility exists here for experimentally ascertaining the importance of short-range order with respect to yield points in these alloys. Since a 12 pct difference exists between the atomic sizes, elastic or Cottrell locking5 must also be considered. Further, Howie and swanne have shown that the stacking fault energy of copper is reduced by aluminum additions. The width of extended dislocations should thereby increase. hus the conditions appear attractive for Suzuki locking.' Finally, the possibility of stress-induced order at dislocations, schoeck locking,' must also be examined, EXPERIMENTAL PROCEDURE Alloys up to 14 at. pct Al were prepared by induction melting high-purity (99.999 pct) Cu and (99.996 pct) Al in a graphite boat under a dynamic vacuum of 5 X 10o mm of Hg. After homogenizing the ingots at 900°C for at least 24 hr under vacuum, they were rolled with intermediate anneals to strips 1.55 mm thick. Single crystals 10 in. long were grown by lowering strips, contained in a split graphite mold sealed in fused quartz at 5 X lo-' mm of Hg, through a single coil induction heater at a constant rate of 1/2 in. per hr. Tensile specimens 1.25 in. long were cut from the single crystal strips and reduced cross sections about 0.7 in. long and 3.0 to 3.5 mm2 in area were introduced by filing and abrading.8 To remove the worked portion about 10 pct of the cross-sectional area was removed by etching. Back-reflection Laue photographs of a filed and etched specimen were taken before and after annealing at 900°c for 24 hr. Small, well defined Laue spots were obtained with no visual difference in the two photographs. Further, specimens with and without the reduced sections began yielding at about the same stress. Hence, for our purposes, filing and abrading did not affect the structure of the specimens. Each single crystal specimen was annealed at 900° c in vacuum for at least 24 hr and furnace cooled; while cooling through the range of 250o to 200°c, the rate was about 55°C per hr. Orientations were determined by the usual back-reflection Laue

Jan 1, 1962

By R. M. Waterstrat

The phase VPt has been reported to have a crystal structure of the B19 (AuCd) type at low temperatures.''' A recent investigation3 has indicated that this phase forms by an ordering reaction from the disordered fcc Pt(V) solid solution which is stable at high temperatures. olander4 has shown that there exists a close structural relationship between the orthorhombic B19 structure and a fcc structure possessing the L1 , (CuAu) type of atomic ordering. One may derive the B19 structure by a shear-like displacement of the atoms in the (002) plane of the ordered fcc lattice along the (010) direction through a distance equal to one eighth of the unit cell dimension, see Fig. 1, followed by an orthorhombic distor; tion of the cube axes such that a = 2.693A. h = 4.413A. and c =4.767A (estimated uncertainty 0.005A). Filings of this phase were produced by grinding a VPt alloy having the B19 structure with a diamond dental grinding disc. When these filings were subjected to X-ray diffraction examination, a pattern of a severely cold-worked fcc structure was obtained. higher solution temperature used (1200 C) or to a much lower oxygen pressure than he reported, due to transfer through many bends and tubes in his complicated apparatus. An interesting observation was made when an oxygen addition was attempted in a cylindrical sample of columbium in the cold worked condition rather than in the annealed condition. The interior of the sample re-crystallized during the oxygen addition at 900°C. The periphery, however. (1 mm) did not recrystallize. A similar sample without oxygen recrystallized throughout the entire cross section. It appears that the re-crystallization is hindered by interstitial oxygen. Presumably, the interior recrystallized before appreciable oxygen could diffuse into the core. This work was supported by the United States Atomic Energy Commission. When the filings were annealed in a high vacuum furnace for 15 min at 110O0C, however. they returned to the B19 structure perhaps as a result of reordering. Subsequent less-severe cold-working of these filings by grinding in a hardened steel mortar and pestle at room temperature produced a transformation into a cold-worked L1, structure which was slightly tetragonal. Thus it appears that the degree of deformation may influence the final structure. Considerable line-broadening was observed in X-ray diffraction patterns obtained from the cold-worked filings and therefore no attempt was made to obtain accurate lattice parameters. Vacuum annealing treatments at 1100'C intended

Jan 1, 1970

By N. A. McKinnon, J. H. Auld, A. M. Marshall, R. A. Coyle

IN making a study of the slip deformation and strain hardening of single crystals of aluminum, it has been found that considerable information additional to that provided by the usual metal-lographic techniques can be obtained by the use of the microfocus X-ray method described by Schulz.1 This technique has been applied to crystals both in the state as-grown by the strain-anneal method and after they have been subjected to increasing amounts of plastic strain. Kelly and Wei" have recently reported the use of this method for a study of lineage structure in aluminum single crystals grown from the melt. The crystals, prepared from aluminum of 99.99 pct purity supplied by British Aluminium Co. Ltd., were grown in the form of flat tensile specimens with a gage section of 0.3 by 0.1 in. and a gage length of 2.3 in. The microfocus X-ray tube used provided a focus of approximately 50 half width. Examination of a large number of as-grown crystals showed no sign of any macroscopic defects in the majority of cases. However, occasionally crystals grown by the strain-anneal method did show defects similar in nature to those shown by Kelly and Wei to occur in crystals grown from the melt. In some other cases a more regular appearance of black and white lines, corresponding to valleys and ridges, respectively, in the lattice, was obtained, Fig. 1. This particular crystal was slightly deformed as the lines when present in the image of an as-grown crystal are only barely visible. The angle of tilt of the blocks is of the order of 3. It seems likely that these tilt boundaries arise during the growth of the crystal due to the specimen not being perfectly flat on the hearth of the furnace and straightening under its own weight at the elevated temperatures. For the deformation studies the crystals were strained in a Polanyi-type tensile machine. A typical photograph taken after 1.2 pct elongation of a single crystal oriented with its axis fairly close to the center of the stereographic triangle is given in Fig. 2. The reflection, which is from the (111) planes, is traversed by two systems of parallel lines. These have been identified as traces of the primary (111) slip plane and the (110) plane perpendicular to the primary slip direction. The latter lines correspond to kink bands which could not be detected by the ordinary techniques of

Jan 1, 1958

By L. C. Brown, J. S. Kirkaldy

Measurements have been made of carbon diffuswn in the five ternary austenites Fe-C-Si, Fe-C-Ni, Fe-C-Co, Fe-C-Mn, and Fe-C-Cr in which the carbon (component 1) diffuses through interstitial sites and the ternary addition (component 2) diffuses substitutionally. Values of the diffusion-coefficient ratio, D12/D11 were determined for each system with finite couples using the transient equilibrium method. The effect of temperature and of concentrations of both the carbon and substitutional component upon D12/D was examined and was found to agree with the theoretical predictions. It is concluded that within an experimental uncertainty of 10 to 15 pct, it is possible to calculate the ratio D12/D11 from purely thermody-namic data. Difficulties of measuring the other off-diagonal coefficient, 4,, are discussed. Any quantitative attack on the fundamentals of the hardenability problem in steel must begin with the multicomponent diffusion formalism and with the accumulation of data pertaining thereto. In a recent paper Kirkaldy and purdy 1 employed the formalism derived from irreversible thermodynamics to treat the problem of diffusion in ternary austenites. In the latter solutions, carbon diffuses through interstitial sites and the substitutional component diffuses through the lattice. Examples were given of diffusion in the systems Fe-Mn-C and Fe-Si-C. In the present paper, we present new results on and discuss their agreement with the thermody-namic theory. Since the theory has been slightly modified from the original presentation of Kirkaldy and Purdy, their results on Fe-Si-C and Fe-Mn-C have been recalculated and are presented here for completeness. The flux of the interstitial component with respect to a fixed lattice framework can be written as a linear expansion in the independent concentration gradients, where X1 and X2 are the independent thermody-namic forces in the lattice fixed frame of reference. These forces can be obtained from the general statement for forces in a volume fixed frame2 if the partial molar volume of carbon atoms is set equal to zero and that of the substitutional component 2 is set equal to unity, viz where the are the chemical potentials and the N's are mole fractions. Introducing into [3] and [4] the function If, as suggested by statistical arguments, the off-diagonal interaction L12 is sufficiently small, [6] reduces to i.e., the coefficient ratio becomes purely thermo-dynamic. The activity of components 1 and 2 in a dilute ternary system (standard state at infinite dilution) may be represented by the expansion3

Jan 1, 1964

By L. E. Tanner

A study was made of the transformation kinetics of the commercial titanium-base alloys, Ti-2.5Al-16V and Ti-4A1-3Mo-1V, using two different heat treatment cycles: 1) step-quenching to aging temperatures from a ß solution anneal and 2) water-quenching from an a+ß solution anneal followed by reheating to aging temperatures. Metallographic examination and hardness testing provided the major portion of the data, while electrical resistivity, dynamic elastic modulus, and X-ray diffraction techniques were also used to obtain critical or confirnzatory data. TTT diagrams were constructed from these results. The sheet alloys, Ti-2.5Al-16V and Ti-4Al-3Mo-lV, are of current interest to the Department of Defense. As an aid to the planning of their respective heat treatments, a program was carried out to determine the transformation kinetics of these alloys using ß and a + ß reference states. This paper presents the TTT diagrams constructed from data obtained by metallographic examination and hardness testing, as well as by X-ray diffraction, electrical resistivity, and dynamic elastic modulus determinations. EXPERIMENTAL PROCEDURE Materials—Sheets of the alloys were obtained from the producers in the "mill anneal'' condition and were tested prior to shipment to assure their meeting mill specifications. Chemical analyses were also supplied and are presented in Table I. Heat Treatment—The majority of the data presented in this study were obtained from hardness testing and metallographic examination. Sample coupons were cut from the alloy sheets and heat treated on a mass scale. The annealing cycles were operated in the following manner: 1) The ß solution anneals were carried out in a horizontal tube furnace with the bare samples protected by a dynamic helium atmosphere. Following this treatment, the samples were quickly transferred to lead, solder, or oil-bath furnaces for aging. After prescribed times at the various reaction temperatures they were water-quenched. 2) The second cycle simulated commercial practice, which requires the alloys be quenched to room temperature following the a + ß sotution anneal. This anneal was carried out in a muffle furnace with a dynamic helium atmosphere. The specimens were then reheated from room temperature to the reaction temperatures in lead, solder, or oil-bath furnaces, followed by water-quenching after prescribed times at these temperatures. Information concerning the critical temperatures of the alloys was obtained from the literature and solution treatments were based on these values. A summary of the solution annealing treatments is found in Tables II and 111. The aging temperatures for the (a - ß alloys ranged in 50°C intervals from 200°C (392oF) to approximately 50°C below the ß/a + ß transus in the first cycle and approximately 50°C below the a + ß solution temperature in the second. The transformations in these alloys were known to be rather rapid, and thus aging times started at 0.5 min and went to a maximum of 7000 min. Hardness Testing and Metallographic Preparation— Heat-treated samples were sheared and mounted in Bakelite with their cut edges exposed. After a flat surface was ground, the hardness was determined in Vpn on an Armstrong-Vickers machine utilizing a 20-kg load. Three to four impressions were made on each specimen. After this procedure, the hardness impressions were removed and the edge surfaces of the specimens were prepared for metallographic examination in the usual manner. The etchant was 20 pct HF and 20 pct HNO3 in glycerine. Electrical Resistivity—It has been shown that the isothermal reactions in titanium-base alloys can be followed by measuring the changes in e1etrical resistivity attending these transformations. As mentioned earlier, the reaction kinetics of a-ß alloys are rather rapid; thus, it would be expected that resistivity data obtained from these alloys would be more significant if measurements were made continuously at the respective aging temperatures. To accomplish this end a special apparatus, based on the current-potential principle, was assembled. Its design was derived from earlier devices constructed by Colner and zmeska1 4 and Levinson.5 The set-up provided for the heat treatment zof machined specimens (approximately 2 x l0-4in. in cross section by 3 in. in length) and the determination of their relative

Jan 1, 1962

By R. H. Hopkins, R. W. Kraft

X-ray and metallographic analysis reveal that the preferred cryslallograPhic relationships in direc-tionally solid~fied Pb-Sn eutectic specimens can be stated: interface growth direction, Experiments in which tin single-crystal seeds were used to nucleate the eutectic demonstrate that the normal lamellar structure observed at steady state can be forced to break down initially to a semide-generate structure when the crystallograPhic direction of the tin seed does not lie within the preferred eutectic interface plane. A normal structure eventually develops by preferred grain growth. X-ray topo-graphs and rocking curves substantiate that the perfection of eutectic samples increases as growth proceeds until steady-state conditions prevail. RECENT years have seen substantial progress made in the understanding of eutectic solidification through both intensive theoretical1'' and experimental investigations (see Ref. 7 for a review and extensive bibliography of both aspects). Several important observations concerning the nucleation and growth aspects of binary eutectic solidification have been brought to light. Briefly some of these include the nonrecipro-cal nucleation of one phase upon another,'j9 the tendency for a specific low-index direction of one or both phases of the eutectic to be aligned in the growth direction during unidirectional solidification,'0711 and the production of lamellar microstructures having a preferred interface plane between "11-13 phases. Questions quite naturally arise as to the mechanism by which preferred grain growth evolves during eutectic solidification and what relationships (if any) connect the initial nucleation of one phase upon another with the preferred growth directions and interface planes observed after a few centimeters of growth in many systems. This study was initiated in an attempt to answer these questions. An experiment was devised in which both the nucleation and growth steps in the crystallization of a binary eutectic, Pb-Sn, could be correlated with subsequently developed eutectic morphology and crystallography. This was accomplished by nucleating the eutectic upon a tin single crystal seed and then causing the eutectic to grow from the seed by directional freezing. The morphology of the structures produced in this manner was then monitored metallographically and the orientation relationships and substructural perfection determined by X-ray analysis. The information thus ob- tained was correlated to the growth history of the samples. EXPERIMENTAL DETAILS The eutectic of composition 38.1 wt pct Pb and 61.9 wt pct sn14 was prepared by accurately weighing lead and tin of 99.999+ (from ASARCO and Lytess Metals and Chemicals, respectively), melting in a clean Pyrex beaker under an argon blanket, and casting into the proper crucible for resolidification as described below. Tin seeds were grown by the method of ~halmers," saw-cut, oriented by the Laue method, and soldered to the pull rod of the Czochralski puller. All seeds were given a final electropolishing (to assure the removal of any deformed material from the cutting operation) and acetone degreasing immediately prior to the nucleation experiment in which they were to be used. Eutectic samples were unidirectionally solidified in a horizontal graphite boat1' or by pulling from the melt16 with tin (or graphite) seeds. A flowing argon atmosphere was employed in all experiments and growth rates and temperature gradients, constant for a given run, varied from 2 to 4 cm per hr and 8" to 15°C per cm over the course of all the experi-

Jan 1, 1969

By R. W. Heckel

The densification of molybdenum powder by hot pressing has been studied as a function of time (up to about 3 x 104 sec) at pressures of 5000, 15,000, and 30,000 psi in the temperature range from 3700o to 1200°C. Excluding results below 2 to 5 x 10 sec, the density (D) - pressure (P) - time (t) data followed the general form:

Jan 1, 1965

By G. M. Schwartz, D. M. Davidson

THE Duluth gabbro outcrops containing sulphides of copper, nickel, and iron are located on both sides of State Highway No. 1 an airline distance of 8.5 miles southeast of Ely in northeastern Minnesota. The region of known sulphide occurrences includes parts of sections 5, T. 61 N., R. 11 W., and parts of sections 25, 26, 32, 33, and 34, T. 62 N., R. 11 W. These sections, given in Fig. 1, are all in Lake County, Minnesota. Part of the area, which lies entirely within the Superior National Forest, is shown on the topographic map of the Ely quadrangle. The original discovery was made in 1948 when a small pit was opened in weathered gabbro rubble for use on a forest access road. A shear zone had caused unusual decomposition in this glaciated area, and the resulting copper stain was noted by Fred S. Childers, Sr., an Ely prospector, who began searching the outcrops along the base of the intrusive. He was joined in further exploration by Roger V. Whiteside of Duluth. In the summer of 1951 a small diamond drill was moved into the area and a hole 188 ft deep was drilled, passing through 11 ft of glacial drift into sulphide-bearing gabbro. This paper is a preliminary report on the geology of the newly discovered ore. The Duluth gabbro is one of the largest known basic intrusives and may be defined as a lopolith.' It extends northeastward from the city of Duluth as a great crescent-shaped mass that intersects the shore of Lake Superior again near Hovland, 130 miles to the northeast, see Fig. 2. The distance around the outside of the crescent is nearly 170 miles. The form of the intrusive is simple at Duluth where it ends abruptly north of the St. Louis River; at the east end, however, the gabbro splits into two elongated, sill-like masses separated mainly by lava flows and characterized by minor irregularities. The outcrop reaches a maximum width in the central part where it is about 30 miles across, and a maximum thickness of about 50,000 ft. It may be significant that the sulphides occur at the base of the thickest part. The lopolith has segregated into rock types ranging from peridotite to granite. The most abundant types are olivine gabbro, gabbro, troctolite, anortho-site, and granite. Of lesser importance quantitatively are peridotite, norite, pyroxenite, magnetite gabbro, and titaniferous magnetite. Grout estimates that two-thirds of the gabbro at Duluth is olivine gabbro. Variations in the percentages of plagio-clase, augite, olivine, and magnetite-ilmenite constitute the only essential differences found among the basic rock types. The predominant mineral is plagioclase, mainly labradorite. Plagioclase and olivine seem to have crystallized early, and the olivine rich rocks, usually troctolite, are found in the lower part. Segregations of titaniferous magnetite are abundant near the base of the gabbro along the eastern part and also occur far above the base. These have recently been described in detail by Grout.' Near the top, segregation has produced a gradation to granite, or "red rock," as it is known locally. This consists of quartz, red feldspar, and hornblende. The red rock forms a zone with a maximum width of nearly 5 miles but is quantitatively unimportant from Duluth northward for 35 miles. In Cook county, where the gabbro splits, each of the two sill-like masses has a red rock top somewhat thicker in proportion to the gabbro below than in the main central mass. The intrusive ranges from coarse to medium in grain size and from granitoid to diabasic in texture. Throughout much of the Duluth gabbro in Minnesota banding and foliation are well developed, as Grout has emphasized.V he bands are mainly a result of variation in the percentage of minerals, as in troctolite with alternating bands high in olivine and in plagioclase. A few bands may consist largely of one mineral, as is true of some segregations of magnetite. Many of the banded rocks show a clearly developed parallelism of platy plagioclase crystals, and both banding and foliation are believed to conform to the floor of the lopolith. Throughout its extent in Minnesota the Duluth gabbro dips east and south toward Lake Superior. It is generally believed to extend beneath Lake Superior and is found as a smaller mass exposed along the north side of the Gogebic district in Wisconsin and Michigan. The dip at and near the base ranges along most of its length from 20 to 40°, but at places the internal banding dips even more steeply. The dip of the upper part is much less, and if it is assumed that the flows along the north shore of Lake Superior are a dependable indication, it does not exceed 15". The formations shown in Table I which are intruded by the gabbro range from Keewatin to Middle Keweenawan in age. They present a significant picture. At the top, the gabbro and its accompanying

Jan 1, 1953

By G. M. Schwartz, D. M. Davidson

THE Duluth gabbro outcrops containing sulphides of copper, nickel, and iron are located on both sides of State Highway No. 1 an airline distance of 8.5 miles southeast of Ely in northeastern Minnesota. The region of known sulphide occurrences includes parts of sections 5, T. 61 N., R. 11 W., and parts of sections 25, 26, 32, 33, and 34, T. 62 N., R. 11 W. These sections, given in Fig. 1, are all in Lake County, Minnesota. Part of the area, which lies entirely within the Superior National Forest, is shown on the topographic map of the Ely quadrangle. The original discovery was made in 1948 when a small pit was opened in weathered gabbro rubble for use on a forest access road. A shear zone had caused unusual decomposition in this glaciated area, and the resulting copper stain was noted by Fred S. Childers, Sr., an Ely prospector, who began searching the outcrops along the base of the intrusive. He was joined in further exploration by Roger V. Whiteside of Duluth. In the summer of 1951 a small diamond drill was moved into the area and a hole 188 ft deep was drilled, passing through 11 ft of glacial drift into sulphide-bearing gabbro. This paper is a preliminary report on the geology of the newly discovered ore. The Duluth gabbro is one of the largest known basic intrusives and may be defined as a lopolith.' It extends northeastward from the city of Duluth as a great crescent-shaped mass that intersects the shore of Lake Superior again near Hovland, 130 miles to the northeast, see Fig. 2. The distance around the outside of the crescent is nearly 170 miles. The form of the intrusive is simple at Duluth where it ends abruptly north of the St. Louis River; at the east end, however, the gabbro splits into two elongated, sill-like masses separated mainly by lava flows and characterized by minor irregularities. The outcrop reaches a maximum width in the central part where it is about 30 miles across, and a maximum thickness of about 50,000 ft. It may be significant that the sulphides occur at the base of the thickest part. The lopolith has segregated into rock types ranging from peridotite to granite. The most abundant types are olivine gabbro, gabbro, troctolite, anortho-site, and granite. Of lesser importance quantitatively are peridotite, norite, pyroxenite, magnetite gabbro, and titaniferous magnetite. Grout estimates that two-thirds of the gabbro at Duluth is olivine gabbro. Variations in the percentages of plagio-clase, augite, olivine, and magnetite-ilmenite constitute the only essential differences found among the basic rock types. The predominant mineral is plagioclase, mainly labradorite. Plagioclase and olivine seem to have crystallized early, and the olivine rich rocks, usually troctolite, are found in the lower part. Segregations of titaniferous magnetite are abundant near the base of the gabbro along the eastern part and also occur far above the base. These have recently been described in detail by Grout.' Near the top, segregation has produced a gradation to granite, or "red rock," as it is known locally. This consists of quartz, red feldspar, and hornblende. The red rock forms a zone with a maximum width of nearly 5 miles but is quantitatively unimportant from Duluth northward for 35 miles. In Cook county, where the gabbro splits, each of the two sill-like masses has a red rock top somewhat thicker in proportion to the gabbro below than in the main central mass. The intrusive ranges from coarse to medium in grain size and from granitoid to diabasic in texture. Throughout much of the Duluth gabbro in Minnesota banding and foliation are well developed, as Grout has emphasized.V he bands are mainly a result of variation in the percentage of minerals, as in troctolite with alternating bands high in olivine and in plagioclase. A few bands may consist largely of one mineral, as is true of some segregations of magnetite. Many of the banded rocks show a clearly developed parallelism of platy plagioclase crystals, and both banding and foliation are believed to conform to the floor of the lopolith. Throughout its extent in Minnesota the Duluth gabbro dips east and south toward Lake Superior. It is generally believed to extend beneath Lake Superior and is found as a smaller mass exposed along the north side of the Gogebic district in Wisconsin and Michigan. The dip at and near the base ranges along most of its length from 20 to 40°, but at places the internal banding dips even more steeply. The dip of the upper part is much less, and if it is assumed that the flows along the north shore of Lake Superior are a dependable indication, it does not exceed 15". The formations shown in Table I which are intruded by the gabbro range from Keewatin to Middle Keweenawan in age. They present a significant picture. At the top, the gabbro and its accompanying

Jan 1, 1953