By Kenneth A. Moon

Kenneth A. Moon (U.S. Army Materials Research Agency)—The authors are to be congratulated for a very interesting and valuable paper. Their discussion of the structural implications of the results shown in their Fig. 5, however, requires a small correction. The model of Speiser and Spretnak with 0 = 1 and z' = 2 is perfectly reasonable for the Ti-O a phase, but Eq. [3] is valid only for solutions sufficiently dilute that the number of empty sites excluded by more than one filled site is negligible. The composition at which intrinsic saturation occurs therefore cannot be deduced from Eq. [3], but but must be decided by consideration of the structural details of the phase in question. In this case, intrinsic saturation is expected not at the composition Ti3O but at Ti2O, because Ti2O has the anti-Cd structurel4 for which each filled octahedral site has two nearby empty sites, one in the hexagonal plane immediately above it, and one in the similar plane below it. The other two models, with ?=1/3 and 1/2, imply a distinction between octahedral sites in pure titanium which is not easy to justify. The problem of extending Speiser's and Spretnak's treatment in a general way to more concentrated solutions will be the subject of a forthcoming publication by the writer. M. T. Hepworth and R. Schuhmann, Jr. (authors' reply)—The authors wish to thank Dr. Moon for calling to their attention the paper by Holmberg which presents the results of X-ray studies of Ti-O solutions ranging from 0 to 33 at. pct 0 and quenched from various annealing temperatures between 400" and 1800°C. Within these ranges, Holmberg found three types of phases: 1) At high oxygen contents (above 25 at. pct) and low annealing temperatures, he found the anti-Cd(OH)2 structure referred to by Dr. Moon. In this structure each titanium atom is in contact with 3 oxygens and each oxygen is in contact with 6 titaniums, the "available" oxygen sites corresponding to every other layer of octahedral sites in the titanium matrix. The limiting composition is Ti2O. However, this anti-Cd(OH)2 structure was not observed for samples containing 25 at. pct 0 or less. 2) For the specimen containing 25 at. pct 0 annealed at 400°C an ordered Ti3O structure was observed. This structure is related to the anti-Cd(OH)2 structure but differs from it by providing only two oxygens adjacent to each titanium atom and thus is consistent with the model represented by Eq. [5] in our paper, with 6 = 1/3, z' = 0. 3) For dilute solutions and for more concentrated solutions annealed at higher temperatures, the structure corresponds to that of the metal with random distribution of oxygens among all the octahedral sites. Thus, it is interesting to observe that the thermo-dynamic indications of ordering in the vicinity of Ti3O can now be supported qualitatively at least by Holmberg's X-ray evidence of the existence of an ordered phase of the composition Ti3O. That is, for solutions with oxygen contents close to that of Ti3O, both the thermodynamic data and the X-ray data are more consistent with models based on the ordered structure of Ti3O than they are with the model which Dr. Moon suggests corresponding to "intrinsic saturation" at Ti2O.

Jan 1, 1963

By Archer E., Wheeler

Producing copper companies were active during 1941 owing to the national defense program the United States and the requirements of the friendly belligerent nation. This activity extended to the American owned properties in South America, the major part of whose product was taken by the Metals Reserve Co., a U.S. Government agency. Anaconda Copper Mining Co. is building a new converter plant at Anaconda, with four units of the Peirce-Smith type. The addition is being built adjacent to the reverberatory plant so as to avoid the necessity of hauling matte and slag. It is expected to be completed this year.

Jan 1, 1942

By J. M. Dupouy, R. A. Rawe, M. B. Bever

The aging characteristics of a titanium alloy containing 13 pct V, I1 pct Cr, and 4 pct A1 have been investigated by hardness measurements, X-ray diffraction, and metallography. The P phase decomposes into 0 + a, and 0 + a, + TiCr, above about 1050°F; below this temperature a transition phase, believed to be w, precipitates first, followed by a, and TiCr,. The observed hardening is attributed to these reactions. Cold working of solution-treated specimens accelerates hardening and raises the hardness level attained. A TTT diagram is proposed. NEW titanium-base alloys, designated as "all-beta," have recently been developed. These alloys contain large amounts of P-stabilizing elements such as molybdenum, chromium, or vanadium. When cooled from the solution temperature, they consist only of P; in particular, the martensitic a,' phase does not form.

Jan 1, 1961

By I. R. Kramer, H. Shen, S. E. Podlaseck

The tensile and creep properties of aluminum in vacuum have been investigated. It was found that the general effect of a vacuum environment was to reduce the rate of work hardening. Results obtained from creep tests showed that lowering the test pressure from 2 x 10-4 to 10-7 torr produced a decrease in the activation energy as much as 500 cal per mole. An attempt is made to explain these effects in terms of how the surface-stress field of a specimen may be affected by a vacuum environment during plastic deformation. In a previous paper,' the results were reported of some of our early work on the effect of vacuum environment on the stress-strain curve of aluminum single crystals. This effort has been extended to the studies of the tensile and creep properties in vacuum as a function of various metallurgical parameters. Some of the recent surface-effect studies2'3 have revealed that a region of high dislocation density, the so-called "debris" layer, is formed near the surface of the specimen as a result of plastic deformation. This layer acts as a surface barrier to oppose dislocation movement. The strength of this barrier depends on the surface condition such as oxidation or surface removal. Experimental results obtained from surface-removal work2, 3 indicate that such a surface barrier, which may be characterized by a stress field, affects the applied stress and the rate of work hardening. In the case of aluminum, this stress field was found to be directly proportional to the strain and the strain rate; however, the slope of this curve is independent of orientation of the crystal and may be altered by using different surface treatment. Since the escape of dislocations may be retarded by the presence of an oxide on the surface of a specimen, it is expected that a change in the rate of oxidation in vacuum will affect the process of dislocation accumulation in the debris layer. Consequently, it also affects the plastic behavior of a metal. This paper reports the changes in some of the creep and tensile properties of aluminum in vacuum and discussions of the observed effects in terms of the concept of the "debris" layer. EXPERIMENTAL PROCEDURE Tensile Tests. A sketch of the tensile apparatus is given in Fig. 1. This apparatus was contained in a bell jar (14 in. diam by 24 in. high) connected to a 10-in. vacuum system. The load was applied to the specimen by means of a gear train which was driven by a magnetic clutch located outside the vacuum chamber. The specimen, held by a pair of square shoulder grips, was attached to the load cell at the top and the drive gear at the bottom. A displacement transducer was placed between the two grips as shown in the figure to measure the elongation. Signals of elongation and load were amplified and recorded on an X-Y recorder. The system was capable of detecting loads as small as 0.025 lb and displacements of 0.0002 in. Shoulder-grip specimens of aluminum single crystals, having a nominal square cross section of 1/8 by 1/8 in. and a 3-1/2-in, gage length, were grown by the Bridgeman techniques. The original purity was 99.997 pet. The orientations of the crystals investigated are shown in Fig. 4(a). The crystals were annealed at 600°C for 2-1/2 hr, electropolished, and placed in the vacuum test chamber without any delay. All the crystals were deformed at a strain rate of 4 x 10-5 sec-1 at 24o ± 3°C. A study was made to find whether a chemically passive surface film would give the same effect as a vacuum environment. Specimens of aluminum 1100 (0.187 in. diam with a grain size of 0.1 mm)

Jan 1, 1965

By John L. Walter

A sintered compact of iron containing 0.007 vol fraction of glass , prepared 6). powder rnetullurgtcal lechniques, was rolled lo foil, 0.001 in. /hick. The foil sullrples were anneuled a1 650° to 850°C in hydrogen. Pri,narj recryslullization prodtnced large grains which Lc3ere highly elongnled in the rolling direclion und which had an unusual prgferred orientation. The glass parlicles assumed a stringerlike dispersiorz on working; llie slrinyers were parallel lo the rolling direction and to the long axis of the grains. The same unusual grain structure, preferred orientation, and stringerlike dispersion of purticles are found in heal-ily rolled and annealed foil of tungsten which has heen doped wilh small amounts of aluminum, silicon, and polassiutvt. Both the proper dispersion of the particles and severe working (reductions in excess of 98 pct) are necessary to produce the elongzcted grain structure. RECENTLY, the author reported on the origin of the elongated or "nonsag" grain structure in tungsten foil which was doped with aluminum, silicon, and potassium.' It was observed that particles, identified as mullite (Al6Si2Ol3), were present in the doped ingot (as sintered) and at all stages of processing from ingot to sheet or wire. It was shown that the particles, being plastic at tungsten working temperatures (up to 1550"C), underwent a "stringing out" parallel to the working di-direction. It was concluded that these strings of particles were responsible for the formation of the highly elongated interlocking grains observed in doped tungsten wire or sheet. To give further credence to this explanation of a long-observed but not understood phenomenon, it was decided to design a new system, one which was analogous to the doped-tungsten system. Thus, a bcc metal, iron, was chosen to be doped with glass which would be plastic at reasonable working temperatures for iron. The glass chosen was a #0080 Corning lime glass which melts at about 810°C. This is approximately the same fraction of the melting point of iron (0.6) as the melting temperature of mullite is of tungsten. It will be shown that all the observed unusual features of the doped tungsten are duplicated in the glass. doped iron, even to the preferred orientation of the grains in the recrystallized sheet. In the tungsten sheet the preferred orientation consists of two components, (1i3)(691) and (013)(362), neither of which has been observed as a component in textures of primary recrystallized bcc metals. EXPERIMENTAL PROCEDURE The glass, in the form of fine powder, was added to high-purity electrolytic iron powder and mixed dry. The particular composition chosen was 0.007 vol fraction of glass. After mixing, the powder was mechanically pressed to a disk 0.5 in. diam and 0.15 in. thick at a pressure of 5000 psi. The pellet was sintered, in pure dry hydrogen, for 2 hr at 8 50°C. The sintered pellet was then heated to 750°C and rolled to 50 pct reduction of thickness in two passes, with reheating between passes. The rolling temperature was then reduced to 600°C and the slab was rolled to a thickness of 0.050 in. Rolling to 0.010 in. was accomplished in several passes at 300°C. Final reductions to 0.003 and 0.001 in. were taken at room temperature. This rolling temperature schedule was similar, in terms of the fraction of the melting point, to that used in the rolling of the doped tungsten. The total reduction of thickness was in excess of 99 pct. Samples of the rolled foil were lightly electro-polished and annealed for 1 to 6 hr at temperatures of 650" to 85O°C in hydrogen. Samples for transmission electron microscopy were thinned on a Disa Electropol using AC-1 electrolyte.

Jan 1, 1968

By A. J. Williams

THE province of Saskatchewan, situated in the center of the Great Plains region of Canada, has, like most prairie areas, an essentially agricultural economy. Most of its population of about 860,000 is located in the southern half of the province in the farming and ranching areas. To the north of the prairie is a broad forested belt supporting a considerable timbering industry, and the northern one third of the province is glaciated pre-Cambrian rock formation. This latter area is relatively barren of vegetation, but the presence within it of a considerable variety of radioactive, noble and base metals, and industrial minerals has been shown by prospecting in recent years.' Glacial Geology The Keewatin ice sheet, considered to have accumulated in the country to the west of Hudson Bay in Pleistocene time, covered at its maximum advancement almost all of Saskatchewan and extended south of the international boundary. Only in the Cypress Hills in the southwest and around Wood Mountain in the south central portion of the province did the preglacial formations escape the action for this glacial period. The bedrock of the plains and forest areas therefore is overlain by moraines and modified glacial drift, which vary in thickness from a few feet to 400 or 500 ft.' Glacial action in the pre-Cambrian area of the province was largely erosional, most of the more recent formations and some of the pre-Cambrian rock being transported out of the area to the south and west. It has been estimated that about 13 pct of this area is composed of lakes and rivers not too adaptable to rail or water transportation, so that until the use of aviation for exploration purposes became general, development of the area was slow. To the south, the heavy mantle of glacial drift has to some extent deterred the discovery of industrial minerals in the bedrock underlying the forest and prairie regions3 At the same time, this drift contains numerous deposits of those most elementary and necessary industrial minerals, sand and gravel. Sedimentary Basin The major feature of the sedimentary deposits underlying the plains regions is the basinal structure known as the Moose Jaw syncline, which runs from the southeast corner of the province in a northwesterly direction. To the west of this syncline the formations curve upward, then have been faulted and further upthrust to appear at the surface in the foothills of the Rockies in Alberta; to the east and north they curve upward into Manitoba and northern Saskatchewan, but the surface contacts are covered mostly with glacial drift.238 The axis of the syncline dips to the southeast, so that there is also an upward trend of the formations along the axis to the northwest. In illustration of the regional structure underlying the province, the pre-Cambrian basement has been logged in drillholes at the following depths in several locations: Ogema (south central), 9390 ft; Gronlid (northeast), 2599 ft; Vera (northwest), 4422 ft; Big River (north northwest), 2348 ft. Fig. 1 indicates the general surface geology of the province, ignoring such glacial overburden as may overlie many of the bedrock formations. Also indicated is the approximate location of the axis of the Moose Jaw syncline.' Industrial Minerals Clays: The province is fortunate in possessing a widespread distribution of clays of ceramic value, ranging from those used for heavy structural products to the high grade pottery and china clays. Shales suitable for brick and tile production are found in the Upper Cretaceous and Tertiary formations across the south of the province where the glacial drift is thin or nonexistent. Many deposits of glacial lake clays suitable for such wares are found scattered over the rest of the province south of the pre-Cambrian area. The Whitemud formation of the Upper Cretaceous is a narrow sedimentary band of secondary clays found intermittently at points across the south of the province where glacial action did not disturb or remove them.' In the southwest corner of the province, around Eastend in the Frenchman River valley, the refractory clays of this formation are contaminated somewhat with iron compounds or other alteration products of basaltic rocks. This eliminates the use of those clays in true whitewares, as they fire to creamy buff shades at the lower temperatures and to a blue-specked grey at cone 8 to 12, (2280°F to 2390°F), the range commonly used in firing whiteware. However, for use in the production of colored artware, caneware, stoneware or crockery, and sewerpipe, this type of clay makes an excellent body that requires little or no addition of flint, feldspar, or other fluxing materials such as are required in the higher class of ware.' It is not a grade of clay that can be shipped great distances to the manufacturing centers, but a market for considerable tonnages has developed at nearby Medicine Hat, where cheap natural gas is available for the firing of the ware. Farther east in the south central portion of the province, the clays of the Whitemud formation are generally more refractory and white burning. The formation is divided into three zones, consisting of white clays, brown shale, and white sandy clays.

Jan 1, 1953

By R. W. Winson

Asbestos is the generic name given to a group of fibrous mineral silicates found in nature. They are all incombustible and can be separated by mechanical means into fibers of various lengths and cross sections, but each differs in chemical composition from the others. The commercial grades of asbestos consist of a spectrum of lengths and sizes and are not definitive as are most organic fibers. It is generally recognized that there are two main groups of asbestos. The first only contains the fibrous serpentine called chrysotile and comprises about 94% of the world production of asbestos. The second group contains five minerals in the amphibole series+rocidolite, amosite, anthophyllite, tremolite, and actinolite. The latter two have no commercial importance. Properties Physical The structures of asbestos fibers have been studied intensively over a number of years. X-ray diffraction patterns have been used as a means of identification and classification. Low angle X-ray scattering techniques have shown that chrysotile fibers are "hexagonally close packed" and parallel to each other, having cross-sectional diameters varying from 18014 to 300A units, while the amphibole fibers are many times larger in cross section. Electron micrographs of the more common types of as- bestos are shown in [Figs. 1-4]. [Fig. 1] illustrates the softness and flexibility of chrysotile which make it suitable for textile-type products. For a number of years there was considerable controversy over the exact nature of chrysotile fiber, but the photographic evidence in [Figs. 5-7] clearly show that it is tubular in structure. The curvature is the result of the mismatch in the dimensions of the silica [Si,O,l and brucite [Mg(OH),] layers which are on the inside and outside, respectively, of a double sheet. This curvature had been predicted by Pauling (1930) years ago based on the molecular dimensions of the two component structures.

Jan 1, 1975

By William L. Fink, L. A. Willey

Since so many different curves have been published for the solid solubility of zinc in aluminum, it seems desirable to definitely establish the correct curve by two or more independent methods. The curve published in part I1t was based entirely upon X-ray measurements because the other methods employed at that time were not satisfactory. The present paper (the seventeenth of this series on high-purity aluminum alloys) describes the determination of the solid solubility of zinc in aluminum by the measurement of electrical resistivity at temperature and by microscopic examination. Since the publication of our part I in 1932, an investigation of the solubility relations in the aluminum-zinc system has been reported by Schmid and Wassermann2, who obtained their solubility results from lattice-parameter measurements on heat-treated and quenched specimens. The diagram that they published is shown in Fig. 1. In this investigation they also found by X-ray measurements that the parameter of the gamma phase changed continuously with zinc content and at such a rate that it would be identical with that of the beta phase at 60 atomic per cent zinc. It was concluded therefore that the beta and gamma phases, from the point of view of structural relationship, are one single phase. They also suggested a gap of immiscibility between 270" and 350" C. The complete boundary in this region could not be determined satisfactorily by the method employed and therefore was not shown in their diagram. Aluminum-zinc Alloys Materials Used.—Electrolytically refined aluminum3 was used in preparing the alloys for the work reported in this paper. Chemical analysis showed the following impurities: 0.004 to 0.005 per cent silicon, 0.006 to 0.008 per cent iron and 0.005 to 0.006 per cent copper. Also,

Jan 1, 1936

By M. Kaufman, A. E. Palty

THE mechanical properties of an alloy under given test conditions are in the main determined by the grain size and the phases present, their distribution and temperature-time dependence. Alloys intended for use at elevated temperatures, especially multiphase alloys depending upon precipitation reactions for strengthening, are particularly susceptible to changes in the phases present. Unfortunately, for modern superalloys, very little published information exists which relates the mechanical properties to the basic structural variables. The present work is an effort to do this for an alloy widely used in aircraft gas turbines and related applications, Udimet 500.* The mechanical properties inves- two heats is within the normal specifications for the alloy. However, the elements which most strongly influence the phase reactions, C, Ti, Al, and Mo, are comparable in the two heats. There was no intentional addition of boron, but normal pickup is about 0.002 pct. The vacuum-melted material was received in the form of centerless ground wrought bar stock % in. diam. PHASE STUDIES A) Methods—Two methods were used to determine the phases present: X-ray diffraction measurements on electrolytically digested residues, and microscopic examination. No single commonly used electrolyte will reveal all the phases that may be present; therefore, two complementary acids were selected: HCl and H3PO4. The necessity for this will be shown below in the results. The acid concentrations used were 10 pct HC1 in alcohol and 10 pct H3 PO4 in water. The current density was maintained below 0.1 amp per sq in. Residues were rinsed and separated by centrifuga-tion. X-ray diffraction patterns were obtained in a 114 mm Debye-Scherrer type camera using cobalt radiation. A temperature of 2250°F was selected to obtain as complete solutioning of phases as possible without encountering incipient melting. Specimens were

Jan 1, 1961

By Y. C. Liu, W. R. Hibbard

An aluminum single crystal cold-rolled from (110) [1121 essentially retains its initial orientation after 99.6 pct reduction in thickness. The orientation of the recrys-tallized grains of this material can be described in terms of crystallographic rotations about principal poles of deformation texture. DURING the study of the recrystallization of a copper single crystal cold-rolled from a (110) [112] initial orientation, the orientation of the re-crystallized grains could be derived by a 30" rotation of the orientation of the cold-rolled matrix about its <111> poles.&apos; The present investigation was undertaken to extend the work done on copper&apos; to an aluminum crystal also cold-rolled from a (110) [112] initial orientation. Experimental Procedure The procedure of this experiment was similar to that reported for copper.&apos; An aluminum (99.998 pct) single crystal rod* 1 % in. in diameter was grown in back-reflection technique.&apos; The specimen (1.20x 1.004x0.6787 in. thick) was then rolled along the [112] direction. The final thickness was 0.0028 in., giving a reduction in thickness of about 99.6 pet. Specimens were cut from the rolled strip with scissors, and approximately in. of disturbed metal was removed with Tucker&apos;s reagent. The rolling edge remained intact. The specimens were sandwiched between two graphite plates and annealed in a lead or lead alloy bath which was electrically heated. Pole figures were constructed using the techniques previously described.&apos; Specimens were electrolytically polished4 and etched with 47 pct HNO8, 50 pct HC1, and 3 pct of 48 pct HF. The electrolytic polishing method and etching reagent employed for aluminum specimens were not entirely satisfactory and the microstruc-tures could not be studied in any detail. Results and Discussion The octahedral pole figure of cold-rolled aluminum strip is plotted in Fig. 1. The <111> poles spread in the transverse direction approximately 8" for the highest intensity areas. The spread in the transverse direction can be related to a rotation about two <110> directions lying in a plane containing the rolling direction and rolling plane normal. The two <110> directions and a scale of rotation for the <111> poles are shown in Fig. 2. The amount of rotation is consistent for three of the four <111> poles, about 35" to 40". The discrepancy for the fourth pole is believed to be due to limitations of the film technique. Alternate inter-

Jan 1, 1956

By Irving Cadoff, Richard Nolder

An analysis oj a series of samples of single -crystal silicon grown on sapphire shows that ,four distinct orientation relations exist. There are at least thirteen crystallographic planes which serve as substrates ,for epitaxial growth The model which assumes that silicon substitutes for aluminium and bonds with the oxygen atoms of the sapphire to form the first later for subsequent growth can account for the epitaxial geometry in all four cases. Multiplici-ties 01 specific orientations are found which are explained by the symmetry of both the sapphire and silicon crystal structures. It was reported in the previous paper&apos; that single-crystal silicon films can be deposited on single-crystal a A1,03 (sapphire) with a wide variety of orientations. The silicon films, however, were found to deposit in only four different orientation relationships with respect to the sapphire substrate. The X-ray data have been analyzed to determine the plane and direction of atomic fit and an atomic model to account for the epitaxial relationships at the silicon-sapphire interface has been developed. These results are described in the present paper. EXPERIMENTAL The Laue X-ray data described in the previous paper were reduced to stereographic projections in a standard manner. These data were supplemented with X-ray reflection data obtained with -& E and A Full-Circle Goniometer (Electronics and Alloys, Inc.) mounted on a Phillips diffractometer unit. The silicon films were thin enough to result in characteristic reflections from the substrate as well as the silicon. The superimposed stereographic projections were analyzed to determine the orientation relationships. Ambiguities were resolved by referring to constructed models of various lattice planes for both silicon and sapphire. These lattice models were also used to develop the model for atom fit at the interface. DATA AND ANALYSIS 1) Crystal Structures. The crystallography of silico-n, which is of the diamond cubic class with a. = 5.4~, is straightforward. The sapphire structure is more complex and generally difficult to represent in pictorial form. It is of the rhombohedra1 class but usually referred to hexagonal axes. The transformation of indices between these two systems can lead to ambiguities which will have bearing on the analysis presented herein. Therefore, the basis used in this paper is described in the appendix. Referred to the hexagonal system, the parameters of sapphire are co = 12.95.&, a, = 4.75~, c/a = 2.73. All parameters are for room temperature. Figs. 1 and 2 illustrate schematically the hexagonal unit cell model of sapphire used for this analysis. The oxygen atoms are assumed to occupy positions in an idealized hexagonal array on basal planes. Their actual positions are in a slightly distorted hexagonal array. The aluminum-atom positions are scaled to their actual positions in the lattice with respect to the basal layers of oxygen atoms. It was found that an idealized model where the aluminum atoms are assumed to lie exactly at the octahedral interstices of the oxygen lattice, similar to that used by ~ronberg,&apos; was not adequate for this study.

Jan 1, 1965

By H. V. Flagg

OPERATION of a modern steel plant presents a curious anomaly. Large-scale operations, in which large volumes or heavy weights of materials are involved, are not usually subject to close control or narrow specifications. On the other hand, operations that call for a high degree of precision are usually carried out under carefully controlled conditions with delicate, precise machinery and tools, and production is made secondary to quality. In a modern steel mill both extremes are taken as a matter of course. A strip mill making auto-body sheets must supply its customers with sheets that all come within a tolerance of plus or minus 0.003 in. in gauge at any point from side to side or end to end, and without blemishes either of color or surface. Sheets that were considered par excellence as recently as ten years ago could not even find a market today. Such exacting requirements have made necessary a nicety of control that approaches the watchmaker&apos;s art. Notwithstanding this necessity for precision, the scale of operation is stupendous.

Jan 1, 1940

By C. H. Mathewson

BERYLLIUM, magnesium, zinc and cadmium, together with mercury, constitute a coherent sub-group of the periodic system and these metals, excepting mercury; have been studied in sufficient detail by the new X-ray diffraction methods to prove their common adherence to the hexagonal close-packed type of crystal structure with a progressive increase in axial ratio as we pass through the group from beryllium to cadmium. The first four columns of Table 1 summarize the data on crystal structure of these metals reported in the International Critical Tables.1 The last two columns are based on results obtained in the present investigation. TABLE 1.-Lattice Constants and Twinning Law of the Be-Cd Group of Hexagonal Metals Dimensions of Unit Axial Cell, A Ratio Description of Twinning Element a° c° (c°/a°) Composition Axis Plane Beryllium 2.28(3) 3.60(7) 1.58 {1012} Probably 1 {1012} Magnesium 3.22 5.23 1.621 ,1 {1012} Zinc 2.65(7) 4.94(8 1.86(2) 11012 } 1 {1012) Cadmium 2.98 5.63 1.88(5) {1012} Probably 1 {1012} Twinning has often been observed in zinc and cadmium. The general aspects of this twinning are abundantly illustrated by photomicrographs, diagrams, etc., in the papers by Romig, and Mathewson and Phillips reported to this Institute in 1927.2. A determination of the composition

Jan 1, 1928

By David P. Shoemaker, Clara B. Shoemaker

It has been shown for an important class of complex transition intermetallic compounds (a, P, R, 6, and p phases) characterized by "normal" coordination [CN12 (icosahedral), CN14, CN15, CN16/ that interatomic distances nay be calculated to a good approximation as the sum of characteristic atomic radii. Two radii, one for major ligands and one for minor ligmds, are specified for each atom, except in the case of CN12 where only a miaaor-ligand radius is specified. The same appears to be true of transition-metal phases of simpler struc-ture: Laves phases (CN12, CN16), and p-tungsten phases (CN12, CN14). In the case of known examples of the more complex phases, a simple rule is given which specifies these radii. However, only a fraction of the known examples of the simpler phases obey this rule closely. To include the latter phases the rule may be modified by considering the radii as linear functions of the weighted average of the Pauling CN12 radii of the two kinds of atonzs, with the radii weighted according to the over-all chemical composition of the alloy. With very few exceptions interatomic distances for both tlze complex and the simpler transition phases can b$ predicted with this modified rule to within 0.06A. ManY intermetallic compounds are known of composition A,By, in which A is a transition element to the left of the manganese column in the periodic table and B is a transition element in or to the right of it. Frequently the coordination numbers (CN) found in these compounds are CN12 (icosahedral), CN14, CN15, and CN16 (called "normal" coordinations by Frank and Kasperl). Well-known examples are the cubic and hexagonal Laves phases which have CN12 and CN16, and the 0-tungsten (CrsO) phases which have CN12 and CN14. In the more complicated (often ternary) phases, such as the a phase,2 the Beck phases p3 and R~, the 6 phase,5 and the p p atoms occur with CN12, CN14, CN15, and (except for a) CN16; in many cases several crystallographically independent atoms of one particular CN occur in the asymmetric unit. A large number of independent interatomic distances are found in these complicated phases, varying from 20 in the a phase to 94 in the 6 phase. These distances show a large spread; they vary, for example, from 2.358 to 3.278A in the 6 phase. In our analysis of these distances we found that in each of these compounds every atomic position can be characterized by either one or two radii. The CN12 positions are characterized by a single radius, The higher coordinated positions are characterized by two radii, namely: the CN14 positions by 4 in the direction of the twelve "5-coordinated" ligands3 (called &apos;minor" by Frank and Kasperl) and by r:, in the direction of the two "6-coordi-nated" ligands (called "major" by Frank and Kasper); the CN15 positions by r15 for the twelve minor and r:, for the three major ligands; the CN16 positions by rlE for the twelve minor and r:, for the four major ligands. We have expressed the experimentally determined interatomic distances in observational equations as the sums of the appropriate pairs of these characteristic radii and the value of these radii have been determined by the method of least Squares. Despite their wide range, the interatomic distances could then be predicted by the sums of these atomic radii with an average deviation in any one compound of 0.06A or less. The results are summarized in Table I. Inspection of the radii thus obtained shows that in the structures in Table I the radii (in A) are given to a first approximation by the simple relationship: Where CN is the coordination number (12, 14, 15, or 16), and A = 1 for major ligands and = 0 for minor ligands. The interaLomic distances can be predicted within about 0.1A by sums of these atomic radii. Another phase belonging in this group with CN12, 14, 15, and 16 is the y phase & B7, in which A is molybdenum or tungsten and B is iron or cobalt. Recently the M%C phase has been refinedE and the observed distances also agree well with those calculated with Eq. [I]. (In the original determination of the structure of W6FeV7 the F$(II)-W(II1) distance was erroneously given as 2.84A, but we have recalculated it fro? the published parameters and found it to b? 2.57i4, in good agreement with the value of 2.6A predicted with Eq. [I.].) Many binary transition alloys are known to crystallize with the simpler structures having "nor-

Jan 1, 1964

By R. V. Norris

THE wage rates and working conditions in the anthracite. region of Pennsylvania have been governed for nearly 20 years by the award of the Anthracite Coal Strike Commission, appointed Oct. 16, 1902, by President Roosevelt. The report of this com-mission, made in March, 1903, was accepted and, with eight modifications made at various dates, has had .almost the force of law, and has kept this great indus-trial region free from strikes for almost a generation. In 1920, President Wilson appointed an Anthracite Coal Commission, and its report, accepted Aug. 30, 1920, governed wage conditions to April 1, 1922. Actually, the agreements have been for terms of two to four years, and lately, in 1916 and 1920, the employ-ees have continued at work pending the negotiation of new agreements which were made retroactive, and which have all been modifications of the original 1903 award. With the expiration, April 1, 1922, of the 1920 award approaching, Mr. Lewis, president, of the United Mine Workers of America, addressed a letter, on Feb. 20, to the operators, suggesting a meeting on March 15; this date was accepted by the latter, with the notation that the time was short. At the meeting, the Mine Workers presented 19 demands, and advised that if a satisfactory agreement was not reached by April 1.a suspension of mining would occur, contrary to the practice since 1916 of continuing work with a retro-active adjustment.

Jan 6, 1922

By E. T. Turkdogan, L. S. Darken, R. G. Olsson, H. A. Wriedt

Several aspects of the calcination of Michigan limestone were investigated: the rate of calcination of limestone spheres with diameters from 1.8 to 14 cm at temperatures from 800° to 1200°C by a thermogravimetric method; the temperature profile across limestone during calcination; the excess pressure developed in the interior of the stone during calcination; the pore surface area, pore volume, and effective gas diffusivity in burnt lime; and the microstructure of polished and fracture surfaces. It is found that, over a wide range of experimental conditions, the difference between the surface and center temperatures remains essentially unchanged during the latter half of calcination. From the rate of weight loss after about 50% calcination, the value 0.00126 cal per cm sec degree is found for the effective thermal conductivity of burnt lime. From the excess internal pressure measurements, i.e., 0.4 to 6 cm Hg at 800° to 1200°C, the permeability of burnt lime is estimated to be within the range 8 X 10-&apos; to 5 X 10&apos; sq cm. With increasing temperature and time of calcination, the pore structure of burnt lime coarsens as indicated by a decrease in the pore surface area, pore volume, and an increase in the average pore size. For the temperature range 600° to 835°C the ratio (effective gas diffusivity/molecular diffusivity) is about 0.18.

Jan 1, 1974

By L. K. Jetter, C. J. McHargue

DEVELOPMENT of preferred orientation in uranium is of interest because of the strongly anisotropic properties of the orthorhombic crystal structure. Harris&apos; reported inverse pole figures for rolled uranium rods which showed <010> and <410>* to be parallel to the rolling direction after On 0.19-in. spherical X-ray diffraction specimens taken from the center of the middle section of each rod, pole distribution data were obtained by the spectrometric method described previously.4 The specimen was rotated rapidly about the axis coinciding with the rod axis in order that a large number of grains could be scanned and was rotated slowly about an axis perpendicular to the rod axis. The variation in the diffracted X-ray intensity was recorded as a function of the latter motion (angle 4). Fiber-axis distribution charts (inverse pole figures) were prepared by the method described by Setter, McHargue, and Williams." After having been corrected for background radiation, the pole distribution data (I vs ?) were normalized. A normalizing factor for each plane has been shown to be Iranaom = f I sin 4 ? 4 and was obtained by graphical integration from the data for that plane plotted as I sin ? vs ?. The axis-distribution charts deduced from the normalized pole densities are shown in Figs. 1 to 3. On these charts, the contours indicate angular positions of equal normalized axis density,

Jan 1, 1958

By M. J. Salkind

In discussing the possible contribution of plastic deformation to neck growth during sintering, Wilson and Shewmon State that Lenel, Ansell, Salkind, and Early34, 35 concluded that dislocation flow is the rate-controlling process in sintering under zero external load. The experiments cited34, 35 were done with applied external loads, and the conclusions were that the same kinetics could be controlling sintering due to the force of gravity with no additional applied load. The effect of gravity on sintering behavior was previously cited.34, 31 In addition, Wilson and Shewmon argue that the conclusions of Refs. 34 and 35 are doubtful because the strain rate is proportional to stress for plastic flow. This assumption is true only for certain kinds of plastic flow such as Nabarro-Herring Microcree38 As Early, Lenel, and Ansell point out3&apos; plastic flow, based upon dislocation movement, can exhibit strain rates which exhibit a power law relationship to the applied stress.39, 40 Wilson and Shewmon also doubt the results of Refs. 34 and 35 because the stresses in the necks are too small for x/a > 0.1. This is true, and the experiments described in Refs. 34 and 35 were done for small values of %/a. The conclusion was that plastic flow by dislocation movement was important during the early stages of sintering when x/a is small.

Jan 1, 1968

By GLENVILTE A. COLLINS

(Presented at a Meeting of the Spokane Local Section of the Institute, Feb. 17, 1912, and accepted for publication in the Bulletin. ) WHILE I am not at the present time engaged in active mine-management, my duties permit of extensive study and examination of many mines, mills, and reduction-works in various places throughout the United States. Being much interested in efficiency-work in general, and an ardent reader of writings on this subject by Frederick W. Taylor and others, as applied to manufacturing-plants, and having served my apprenticeship from mucking to the engineering design of ore-dressing and underground plants, I hope that this paper will lead others to investigate the field more fully, to the improvement of general mine- and mill-operations, as well as the advancement, intellectually, physically, and financially, of the employee and his relations with the employer. If a man who is prepared to look closely and observe broadly starts in Canada and zig-zags from camp to camp to southern Mexico, taking time casually to inspect mines, mills, and smelters, he will be pitifully impressed by the great difference in customs, and the general waste of labor, time, and money throughout the country. He will so seldom observe a dollar&apos;s worth of results given in exchange for a dollar spent that he will form a poor opinion of operating-efficiency and management. This highly-scientific department, requiring an amount of skill and executive ability equaled in few, if any, of the professions, certainly falls short of the standard established in our greater manufacturing industries. It is easily said that this is due to the diversity of conditions in mining, milling, and smelting. But on second view it must be admitted that there is room for tremendous improvements in nearly every mining-organization. The proposal of such improvements is often met by the argument that any mine

Sep 1, 1912

By DOOLITTLE E. M.

(Canal Zone Meeting, November, 1910.) The following notes are contributed, not with the idea of offering a complete history of the development of this very important process as applied to the Leadville district, but with the hope that the practice, as it was carried out in the Bi-Metallic Smelter, may still be of interest to others. The Bi-Metallic Smelter, at Leadville, Colo., was the first to make a commercial success of the process described in the following pages, which consisted essentially of smelting raw silver- and copper-bearing sulphide ores in blast-furnaces to form a matte, which was generally re-smelted with siliceous ores for a second high-grade matte. Robert Sticht, in his excellent monograph on the subject,1 has outlined briefly the plant belonging to this company. He says, in effect: The Boulder, Mont., enterprise set the example for others with whom the patentee (w. L. Austin) had been negotiating, and the old La Plata lead-smelter at Leadville, Colo., was fashioned into a crude, temporary experimental plant for the Bi-Metallic Company, and the feasibility of the process demonstrated by a trial run. Subsequently, the plant was considerably improved, and, being supplied with very favorable ores, continued to run without interruption from August, 1892, to June, 1893. In September, 1893, smelting was resumed in a completely remodeled establishment, some $200,000 having been expended upon the new work. Thus, aside from the Montana experiments, which, under the direction of W. L. Austin, began as early as- 1885 2 at Toston, and continued with indifferent success for six or seven years, the Bi-Metallic plant at Leadville may be said to have * Formerly Superintendent, Bi-Metallic Smelting Co. + Formerly Chief Assayer and Chemist, Bi-Metallic Smelting Co. 1 Modern Copper Smelting, E. D. Peters, 7th ed., p. 415 (1895). 2 Trans., xvi., p. 259 (1887-88).

Dec 1, 1910