By J. Sjöblom

New copper and nickel processes, flash converting and DON, direct high-grade nickel matte smelting, have been developed in order to replace the conventional and not so environmentally friendly PS-converting process. With a laboratory scale laminar-flow furnace the combustion reactions of sulfidic feed particles can be investigated under simulated flash smelting conditions. In the present study, finely ground and screened feed fractions of a copper matte and a nickel matte were flash oxidized in a laminar-flow furnace. The experiments were carried out using 20, 21 vol% and 75 vol% O2 in nitrogen, at temperatures 1100 and 1300 °C and reaction zone length of 7.5-16 cm. The samples were quenched in a water film after a specified reaction time. The matte particle reactions were stopped after short residence time intervals in order to obtain a better understanding of the reaction mechanisms. Chemical analysis was used to determine oxidation degree, and optical and scanning electron microscope combined with energy dispersive analysis was used for characterization of the reacted particles. On the basis of the experimental results the reactivity of the mattes is discussed and possible reaction and dust formation mechanisms are considered.

Jan 1, 1999

By A. Patti, S. Reutzel, D. M. Herlach, L. Ratke, I. Egry

Cu-Co shows a metastable miscibility gap in the region of the undercooled melt. Undercooling of the melt below the binodal leads to separation of the melt into a Co-rich LI-phase and a Curich L2-phase. Experimentally, undercooling into the metastable miscibility gap is realised by means of electromagnetic levitation (EML), processing in drop tube (DT) and by melt flux embedding. As undercooling is large in these experiments, the velocity of the solidification front is high and the microstructure is frozen in instantaneously. Samples have been undercooled and solidified in the TEMPUS-facility (container less electromagnetic processing under weightlessness) during parabolic flight under reduced gravity conditions. Microstructures of solidified samples have been analysed and compared to those processed under gravitational conditions. The influence of convection on phase growth is much lower in reduced gravity. The microstructure shows spherical droplets of the minority phase, statistically dispersed in the majority phase.

Jan 1, 2004

By A. E. Wraith

The tuyère flow rates of Peirce-Smith converters and bath smelting reactors are rendered particularly sensitive to accretion formation, bath depth variations and the general aerodynamic design of the blast delivery system by the limited pressure-flow properties of the conventional single stage centrifugal blower. This sensitivity is examined in terms of tuyère practice, vessel management and fixed engineering parameters for Peirce-Smith converters and the Noranda Reactor by use of the flow resistance factor, R*. New understanding of the effect of accretion growth on the flow behaviour of individual tuyères shows that blowing rates and hence throughputs could be optimised by careful attention to operating detail even within present plant constraints. The concept of the resistance vector is introduced to elucidate comparisons between different practices and to provide reference standards for optimisation. On this basis, the benefits of introducing quite moderate changes in the pressure-flow properties of the blast delivery system are considered. In view of recent developments in the flexible use of converters as hybrid bath smelting vessels for matte production, the foundation is now laid for a searching consideration of relationships between vessel volume and shape, blowing requirements, tuyère performance and production rates, the detail of which will be examined more appropriately in a forthcoming paper.

Jan 1, 1999

By S. S. Babu, T. Hong, T. DebRoy, S. A. David

"Oxide inclusions form in welds because of deoxidation reactions in the weld pool. These inclusions control the weld microstructure development. Thermodynamic and kinetic calculation of oxidation reaction can describe inclusion characteristics such as number density, size, and composition. Experimental work has shown that fluid-flow velocity gradients in the weld pool can accelerate inclusion growth by collision and coalescence. Moreover, fluid flow in welds can transport inclusions to different temperature regions that may lead to repeated dissolution and growth of inclusions. These phenomena are being studied with the help of computational coupled heat transfer, fluid-flow, thermodynamic, and kinetic models. The results show that the inclusion formation in steel welds can be described as a function of the welding processes, process parameters, and steel composition.IntroductionThe relationship between inclusions and formation of a high-toughness phase, namely acicular ferrite in low-alloy steel welds, is well known (1-4). Past research has focused on maximizing acicular ferrite amount in welds by controlling welding processes, process variables, and welding consumable parameters. Research has shown that there is a complex interaction between inclusion characteristics, prior austenite grain size, and weld metal hardenability. In a low-alloy steel weld, the small addition of titanium lead to a change in the inclusion composition and resulted in a transition in the microstructure from bainitic to acicular ferrite [see Fig. I]. This in turn lead to the best combination of strength and toughness. This paper describes the inclusion formation in low-alloy steel welds."

Jan 1, 1999

By Nobumasa Kemori

Six kinds of copper '90ncentrates. were treated individually in a ,pilot scale. Outokumpu flsah smelting furnace ~n order to study their ?flash smelting behavior with respect to oxygen efficiency and dust generation. The copper concentrates tested were selected from the more than twenty sources which are treated at the Sumitomo Toyo copper smelter, so as to provide a wide range of chemical composition in terms .of Cu, S,Fe, Pb + Zn + As, and Si~ content. Oxygen efficiency 'and dust generation rates obtained in 'the experiments ranged from 80% ,to 108% and 11% to 20%, respectively. Relationships between these results and experhnental conditions such as chemical and mineral composition of the copper concentrates, flux ratio, fuel consumption and so on are also discussed quantitatively in this paper.

Jan 1, 1998

By Takamitsu Nakasuga, Haiping Sun, Kyushu University, Katsumi Mori

"The kinetic behavior of reduction of chromite ore by liquid iron containing carbon and silicon has been investigated under various experimental conditions to clarify the reduction mechanism. It was found that the reduction rate of chromium ore by liquid Fe-C alloy was very slow. In addition, when carbon and silicon coexisted in the iron melt, silicon was found to preferentially oxidized to form silica, which favored for the fonnation of liquid slag and the rate of reduction was considerably accelerated. The similar effect was obtained by the addition of some fluxes, such as SiO2, Na2B407, CaO-SiO2, which also promoted the formation of a liquid slag and thus the reduction rate in the early stage also increased.IntroductionThe reduction of Cr2O3 is a basic reaction for production of ferro-chromium from chromite ore and for chromium recovery from the slag fonned during the decarburization period of a stainless steel-making process. The reduction of chromite ore consumes much energy and its reaction rate is not so high. Thus, in order to increase the reduction efficiency, it is strongly desired to clarify its reduction mechanism from the practical and the theoretical points of view."

Jan 1, 2000

By Yasuo Ojima

The mainstream of copper smelting processes in the world today is a combination of Outokumpu type Flash smelting and PS (Pierse Smith) converting process. Presently it can be estimated that about 50% of the worldwide copper production is produced by the Flash smelting process and 80% by the PS converting process. PS converting process due to its operational flexibility and despite its batch character of operation has been widely used in many smelters for more than 100 years. However, an environmental issue has been pointed out related to this process because of the difficulty of handling the fugitive gases. Recently several copper smelters in the world have been newly constructed and others have executed major modification and modernization, The continuous converting process has been applied in many of them instead of PS converting process. This paper compares PS to the emerging continuous converting process and makes a prospect of the future of the copper converting process.

Jan 1, 2003

By D. J. Chaiko

Certain radionuclide ions (e.g., TcO4) exhibit unusually strong Affinities toward the polymer-rich phase in aqueous biphase systems generated by combinations of salt solutions with polymers such as poly(ethylene glycol) (PEG) and poly(propylene glycol) (PPG). Thus, aqueous. polymer ,phases could potentially be used to selectively extract these ions during pretreatment of radioactive tank wastes at Hanford. To help develop a fundamental understanding of the interactions between various ions and polymers in aqueous solution, interaction enthalpies between sodium -perrhenate and a random copolymer of PEG and PPG (UCON-50) were measured by microcalorimetric titration. An entropy compensation effect was observed in this system in which changes in enthalpic interactions were balanced by entropy changes such that the interaction free energy remained constant and approximately equal to zero.

Jan 1, 1999

By S. N. Monteiro, C. M. F. Vieira, A. P. N. M. de Sa, J. P. D. Vitorino

"This work has as its objective to characterize an ash waste and to evaluate its incorporation into a clay to produce bricks and roofing tiles. The waste is a type of fly-ash resulting from the incineration of a selected part of urban garbage, which is basically constituted of organic matter and plastics. The waste was submitted to mineralogical and chemical characterization. Compositions were prepared with incorporation of the waste in amounts of up to 20wt.% into athe clay. Rectangular specimens were prepared by extrusion and fired in a laboratory furnace at 900°C. The physical and mechanical properties evaluated were: linear shrinkage, water absorption and flexural rupture strength. The results showed that the waste is predominantly composed of quartz and calcium compounds. The incorporation of the ash was deleterious to the evaluated properties of the clay. It is suggested that the incorporation should be made in amounts below 5wt. % to avoid deleterious effect in the mechanical strength and water absorption of the clayey ceramic.IntroductionThe world attention has turned to a subject of great concern today, the production and disposal of large amounts of industrial wastes as well as wastes of various sources. When deposed in an unsuitable place, these wastes can cause considerable harm to human health and to the environment. Our planet suffers with air pollution, groundwater and soil contamination as well as silting of rivers and lakes with the growing amounts of our society wastes.The recycling of waste materials is of great interest to the industries, mainly due to the environmental agencies legislation. One of the practices for correct disposal of these wastes being investigated is to incorporate into red ceramics, such as bricks and roofing tiles. The natural variability of the characteristics of the clays associated with the relatively simple processing techniques and also the low performance required for the products allow the presence of relatively high levels of impurities in clayey ceramics."

Jan 1, 2011

By T. Ranki-Kilpinen

In the flash smelting technique, developed by Outokumpu Oyj, off-gases with dust load are directed into the heat recovery boiler (HRB). As the temperature decreases, metallic sulphates become thermodynamically stable. Sulphation of oxidic particles initiates. The release of heat causes an increase in particle temperatures, and soft sulphated particles can stick to the heat transfer surfaces. Dust accretion may form and cause operational problems. The objectives of the project are to study sulphation reaction mechanisms and kinetics of flue- dust particles under HRB conditions, and get more information for the flue-dust treatment possibilities. The sulphation behaviour of synthetic Cu2O particles (37-53 pm) was studied using a fluid-bed reactor of laboratory scale. The experimental parameters in the latest campaign were oxygen and sulphur dioxide contents of 2.5-10 vol-% 02 and 40-60 vol-% SO2 respectively and temperatures of 600-660°C. Samples were examined microscopically (SEM+EDS) and chemical analysis were conducted. The sulphation rate was found to have a maximum at the certain temperature, which was dependent on the gas SO2 content. Regardless of the level of SO2, a rise in oxygen content promoted sulphate formation.

Jan 1, 2002

By Shunsuke Yagi

A surface alloying technique was investigated using alternating pulsed electrolysis in an aqueous solution containing a single metal component for the formation of an Fe-Cr layer on an iron substrate. In the process, the iron substrate was dissolved during each anodic polarization of the pulsed electrolysis, providing iron ions in the vicinity of the substrate, while the Fe-Cr alloy was electrodeposited during subsequent cathodic polarizations. A bright, flat, and crack-free Fe-Cr layer with a composition gradient was obtained using a solution containing a trivalent chromium component and a complex forming agent together with some supporting or buffering salts.

Jan 1, 2006

By J. G. Reid

Nickel is second only to aluminium, of all non-ferrous metals, in energy required to convert the ore to metal. Nickel Laterite ores, which constitute the feed source for approximately 40% of world nickel production, are at a particular disadvantage because of the absence of sulphur, as an energy source, in the ore and because lateritic ores general 1 y are not amenable to beneficiation. The dramatic escalation of oil prices which commenced in 1973 and continued for a decade meant that Nickel Laterite refineries using oil as a primary energy source were placed at a distinct disadvantage relative to refineries utilizing nickel sulphide concentrate feeds. By the late 1970's the continuing large difference in oil and coal prices caused Greenvale to consider converting certain high oil consuming areas of the refinery to coal. These investigations confirmed that the areas of ore drying and power generation, which together consumed 50% of total Plant oil requirements, could be economically converted from oil to coal firing. Construction of the coal conversion facilities commenced in October 1980 and the first ore drying air heater came on line in August 1981. Construction was completed with the commissioning of the coal fired boiler in June 1982. This paper outlines the additions required to receive and utilize coal in ore drying and power generation and how the changeover was completed with minimal process disruption.

Jan 1, 1988

By Yanping Xiao

In submerged-arc furnace (SAF) for smelting chromite ores into ferrochrome, there exist large temperature gradients and wide distributions of mineralogy and compositions in the furnace, due to the complexity of feed structure and electrical-thermal-chemical interactions. This leads to various zones in the furnace and thus different reaction mechanisms. In the present paper, the behaviour of chromium in the submerged arc furnace is discussed in various reaction zones, including solid state chromite reduction in the packed bed zone, chromite dissolution and reactions in the smelting and coke bed zone, and recovering chromium from slag to metal. In the gas-solid reaction zone, the reaction mechanism is discussed based on the experimental observations and analysis. In the smelting zone, the behaviour of partially reduced chromite and slag formation are analyzed based on the information in literature. The slag in FeCr process contains mainly Al2O3, MgO, SiO2, CaO and CrOx, featured by chromium with both divalent and trivalent oxidation state, which plays an important role for chromium recovery into metal. The factors influencing the slag and metal interfacial reactions and the chromium recovery are addressed.

Jan 1, 2006

Halide media are considered as suitable alternatives to cyanide for extracting gold and have received much attention lately. The extraction of gold by iodide-iodine mixture has been patented and briefly studied without much attention given to the fundamental aspects of this process. This paper reports recent studies on the kinetics of gold extraction in iodide media, using hypochlorite, iodine and hydrogen peroxide oxidants. The kinetics of dissolution was found to be dependent on the solution pH, reagent concentration and most importantly the iodide- oxidant molar ratio. Without proper control, the gold surface can be passivated due to the formation of solid products. Thermodynamic modelling was carried out to determine the equilibria governing the dissolution process. The formation of AuI solid was also identified as a possible product during the dissolution.

Jan 1, 1992

By Scott Samson, Weidong Wang, Shekhar Bhansali, Vandana Upadhyay

"We present an improved design for the two-arm polysilicon thermal actuator. The classic thermal actuator design produces a localized hot spot at approximately the center of the thin actuator arm. This phenomenon limits the actuator efficiency, lifetime, and reliability. Since the actuator deflection is based on thermal expansion of the material, advantage may be gained by making the temperature profile more uniform along the hot-arm length. In our design, the geometry of the thin arm is modified by forming a nonlinear structure near the approximate location of the original hot spot. Electromechanical simulations of this design show an increase in deflection, due to a flattening of the temperature profile along the hot arm. The solid model generation, finite element analysis and simulations are carried out using PEA software. Experimental devices are in the process of being fabricated by using a polysilicon rnicromachining process.1. IntroductionMost active MEMS devices employ some kind of actuating mechanism to increase functionality. Various actuating mechanisms like magnetic, electrostatic, thermal, magnetostatic and piezoelectric have been investigated and incorporated for actuating microstructures. The primary features required from many on-chip actuating mechanisms are large deflection (>10 µm), low actuation voltage, low power.consumption, reliability, fast response, ease of design and fabrication, and small size. Thermal actuation is an attractive mechanism for rnicromechanical devices requiring high actuation forces, large deflections, good linearity and low actuation voltage. Thermal actuators, also known as ""electrothermal actuators"", ""heatuators"" or ""U-shaped thermal actuators"", have been largely used in MEMS based devices to provide both in-plane and out-of-plane actuation [l] .Thermal actuators are also easily compatible with standard CMOS circuitry due to their low driving voltage. However, high power consumption remains a major drawback of the thermal actuation mechanism."

Jan 1, 2004

By Linfeng Zhou, Rong Sun, Guanghui Li, Zhiwei Peng, Tao Jiang

The effects of microwave roasting on separation of rhenium (Re) and molybdenum (Mo) from a molybdenite concentrate have been investigated based on evaluation of the heating characteristics of the concentrate in the microwave field. The results show that a variety of operating variables, namely microwave power, sample weight, sample geometry, roasting temperature, roasting time and atmosphere significantly impact on the volatilization rates of Re and Mo. The optimum conditions for Re-Mo separation are microwave power 1300 W, sample weight 20 g, sample geometry pellets, temperature 600 oC, time 1.5 h, and atmosphere 20%O2. Under these experimental conditions, the volatilization rate of Re reaches 88.12%, while that of Mo is just 5.15%. Microwave-assisted roasting provides an alternative route to separating Re and Mo from molybdenite concentrate.

Jan 1, 2016

By Jae-Chun Lee

One of the main advantages of the supported liquid membrane(SLM) would be that different kinds of ions can be extracted selectively or simultaneously from multi-component solutions by parallel treatments with multi-SLM units. This distinctive feature of the SLM extraction is originated from its non-dispersive contacting operation between organic and aqueous phases. In this study, simultaneous and selective extractions of zinc and copper ions from their mixed solutions have been demonstrated using two parallel modules of SLMs. PC88A and LIX84 were used as the extractants for zinc and copper, respectively, and the Hoechst Celanese hollow fiber modules(Liqui-Cel Lab Module) as the supporters. The performance of the simultaneous system was compared with those of the system in which the extraction of each component was achieved by individual runs

Jan 1, 1998

By P. M. Swash

The determination of the heavy minerals in beach sand samples is highly dependent on the preparation technique used. In this paper a simple reproducible method for the quantification of "recoverable" ilmenite, zircon, rutile and leucoxene by magnetic separation, is described. The procedure recommended yields information relevant to the metallurgical processing of the ore rather than to the total heavy minerals present in the samples. Finally the determination of mineral reserve estimations and grade assessments is greatly facilitated when this "mineral assay" method is employed. An assortment of other mineralogical methods are described including SEM, EMPA, XRD, XRF, Image analysis, Mossbauer. clerici and perm roll separations. The methods are briefly examined and the practical information that can be gained by using such techniques are reviewed. Experience has shown that an understanding of the relationship between the physical and chemical properties of the heavy minerals can contribute to the prediction of mineral particle behaviour. Such information may ultimately help reduce the prospect evaluation period and minimise expenditure on metallurgical testwork.

Jan 1, 1991

By Ana E. Bohé

Chlorination process is an attractive and efficient method for the metal recovery from complex materials. The process that is performed at high temperatures, allows converting all the metals contained in the material into their respective chlorides which are further separated in a selective way. Aluminum metal matrix composites with discontinuous ceramic reinforcement of short fibers, whiskers, and particles have been gaining wide acceptance as an important engineering material in automotive, aerospace, and electronic industries. Since the ceramic reinforcements are still quite expensive and contribute significantly to the final cost of composite materials, the feasibility of their recovery from the manufacturing scrap and further recycling is a factor of increasing economic interest. In the present work, a theoretical and experimental study is given for the recovery of Al2O3 and SiC particles and short fibers from three commercially available aluminum-matrix composites produced by molten metal mixing route. The process consists of transforming the constituents of metallic alloy matrices in gaseous chlorides that are dragged by the gaseous stream, while the ceramic reinforcement remains as a solid residue in the reaction bed.

Jan 1, 2006

By S. Viswanathan, A. S. Sabau

"Dimensional changes between a pattern die and its corresponding investment casting part occur as a result of complex phenomena such as thermal expansion/contraction and hot deformation (elastic, plastic, and creep) during the processing of the pattern material (wax), mold material (shell) and solidifying alloy. Determining the pattern tooling dimensions is crucial to the dimensional control of the investment casting process. To date, computational methodologies have not been applied to the prediction of dimensional changes in investment castings.This paper deals with the evaluation of wax pattern dimensions, which is one important factor in determining pattern tooling dimensions in investment casting. Cerita 29-51, an industrial wax, is considered in this study. The wax pattern dimensions are determined by considering its thermo physical and thermomechanical properties, restraint of geometrical features by the metal die, and process parameters such as dwell time, platen temperature, injection pressure, and injection temperature.IntroductionThe investment casting process involves making a disposable wax pattern by injecting wax into a metal mold, building a ceramic shell mold around the wax pattern by the application of a series of ceramic coatings to the wax pattern, dewaxing the ceramic shell mold, and casting the alloy into the shell mold. Dimensional changes between the pattern tooling and its corresponding cast part occur as a result of thermal expansion, shrinkage, hot deformation, and creep of the pattern .material (wax), mold material (shell), and solidifying alloy during the processing [1]."

Jan 1, 2001