Search Documents

By Sijun Li, Bingyu Zhang, Haitao Zhou, Zhendong Zhang, Guofei Si, Xianghua Liu

"Hot compression test of Nb microalloyed coiled tubing steel is performed on Gleeble3500 at 1123K—1373K and strain rate from 0.001 to 5s-1. It is found that flow softening occurs and the flow curves exhibit a peak with a characteristic of dynamic recrystallization (DRX) and change with temperature and strain rate significantly. The peak stress and peak strain are dependent on the Zener-Hollomon relationship with activation energy of 390 KJ/mol. On the basis of Avrami equation and the Zener-Hollomon parameter, it is obtained that the dynamic recrystallization kinetics equation with which the calculated and measured recrystallization fraction is very close. On the results of hot compression test, the Nb microalloyed coiled tubing steel is rolled by Thermo-Mechanical-Control-Processing (TMCP), and it is obtained that the yield strength and tensile strength of Nb microalloyed coiled tubing steel are 565MPa and 685MPa respectively, and the elongation percentage is 30.1%.IntroductionCoiled tubing is widely used in oil field for well logging, well completion, drilling, work over and other operation in various fields to solve a number of conventional operating techniques problem which are difficult resolved, and it plays a more and more important part in exploration and production at oil field. [1] It will improve the efficiency of exploration and exploitation, studying, developing and using coiled tubing technology. Therefore, the development of domestic coiled tubing materials and manufacturing technology are great significance. It is well known that Coiled tubing has relatively poor working conditions and complex force state. So, the coiled tubing needs satisfier a kind of high strength, high plasticity, and corrosion resistant under complex oil gas condition. As the coiled tubing technology developed, the level of the coiled tubing steel is from CT55 originally to CT90 and CT100, and the corresponding tensile strength is 483MPa-758MPa. [2, 3]"

Jan 1, 2012

By Jiang Diao, Xuan Liu, Tao Zhang, Bing Xie

In the present study, the oxidation process of vanadium and chromium bearing hot metal was investigated by using CaO-FetO-SiO2 slags at 1653K in MoSi2 furnace. The results indicated that both the vanadium distribution LV and chromium distribution LCr were of the orders of 2.2~2.4 with the basicity range of 1.32~1.78 and FeO weight percent range of 28%~45%. Both LV and LCr decreased with increasing basicity and decreasing FeO weight percent. The phosphorus distribution LP was of the order of 1.34~1.56. However, LP increased with increasing basicity and decreasing FeO weight percent. The oxidation ratio values of V and Cr in hot metal were above 84% and the values of P were nearly 50%. In other words, it means the addition of CaO in vanadium slag provided a certain ability of dephosphorization along with keeping high oxidation ratios of V and Cr.

Jan 1, 2015

By Jr. Foot

The Bureau of Mines, U.S. Department of the Interior, investigated flotation methods for recovering fluorite and byproduct beryllium from the Fish Creek deposit of Nevada. The preferred method includes (l) fluorite rougher and cleaner flotation, (2) de sliming at 20 micrometers, (3) muscovite flotation, (4) silicate flotation, (5) hypochlorite wash of silicate concentrate, and (6) beryllium rougher and cleaner flotation from the silicate concentrate, Laboratory results showed that over 94 pct of. the fluorite was recovered in a concentrate containing 96 pct CaFz. Beryllium flotation produced .concentrates .containing in excess of 5 pct BeO with recoveries over 70 pct. A 1.00-lb/h continuous flotation unit was constructed to demonstrate this procedure,

Jan 1, 1985

By Ko-ichiro Ohno

It is recently recognized that the iron reduction and melting as well as the slag separation of a composite of granular iron ore and coal are completed in a very short period of about 10 minutes when the composite is rapidly heated up to approximately 1673K. These phenomena are expected to be applied to a new iron-making process. The mechanism of iron ore reduction and iron-slag separation during rapid heating has not yet been revealed and the fundamental research has just started. Carburization of the reduced iron is regarded as one of the most important steps in this process. In the present work, the composite was prepared from four kinds of coal or graphite as a carbon source and electrolytic iron powder as a completely reduced iron ore. The temperature at which the liquid formation and iron carburization occurred was monitored. Direct observation of smelting reduction behavior was made by a confocal laser-scanning microscope combined with the infrared image-heating furnace to clarify the effect of molten ash on iron carburization. It was found that the meltdown temperature of composite became lower as the melting temperature of coal ash decreased. From the observed result, it was presumed that the liquid slag would act as an important media for the carbon transfer from coal to iron. The carburization mechanism during the smelting reduction was estimated as follows. When slag containing iron oxide melted down and contacted carbon, iron oxide in the slag was reduced and the formation of the metallic iron particle as well as the its carburization occurred simultaneously at the slag-carbon interface. Carburized iron particle was carried from slag-carbon to slag-iron interfaces due to the slag convection flow caused by the difference of the interfacial tension between the carbon-slag and iron-slag interfaces. Carburization of reduced iron could proceed with a repeat of the above-mentioned process.

Jan 1, 2003

By J. R. Goode

Up to one half of neodymium and praseodymium production, key ingredients in permanent magnets, is produced illegally. About 60% of cobalt production, critical in lithium-ion batteries and other applications, comes from central African states, and much of it is produced illegally. Tantalum, important in modern electronics, is also primarily sourced from central Africa and, again, much of it illegally. Illegal mineral production, as exemplified here, is often used to fund armed conflict. Furthermore, it is typically conducted with scant regard for human rights and environmental protection. It also leads to depressed prices which in turn limits the possibility of legitimate producers entering the market. Systems of traceability and provenance, along with cooperative supply chain participants can limit the production of illegitimate material and thereby improve conditions in the countries of origin and reduce downward pressure on prices.

By Julien Favre, Akihiko Chiba, Damien Fabregue, Yuichiro Koizumi, Eric Maire

"The mechanical behavior of Co-20Cr-15W-10Ni alloy is studied by compression tests at high temperature. Microstructures after deformation are evaluated using SEM-EBSD. Significant grain refinement occurs by dynamic recrystallization for high temperature and low strain rate (T>1100°C, <0.1s-1), and at high strain rate (~10s-1). Dynamic recrystallization is discontinuous and occurs by grain boundaries nucleation, leading to a necklace structure. The nucleation mechanism is most likely to be bulging of grain boundaries. However, recrystallization occurs also by rotation of annealing twins which can bulge as well. The modeling of mechanical behavior gives a fair quantification of flow softening due to dynamic recrystallization, indicating the progress of dynamic recrystallization with deformation.IntroductionCobalt-chromium alloys are used in biomedical applications for the elaboration of implants due to their outstanding mechanical properties and their high resistance to corrosion. For stent application a large ductile behavior is required in addition to the high mechanical strength. Indeed stents have to undergo a deformation until e˜40% during their expansion [1]. Conventional Co-Cr-Mo (CCM) alloys exhibit limited ductility (maximal deformation about e˜30%) [2]. Co-Cr-W-Ni (L-605) alloy is a better candidate for stent elaboration since its fracture strain can exceed 40% (comparable to nickel superalloys (Figure 1), while it keeps high mechanical strength. In spite of the presence of nickel element in this alloy, biocompatibility is sufficient for vascular implants, therefore L-605 alloy is extensively used for heart valves and stent elaboration [3]."

Jan 1, 2012

By J. J. Talja

An investigation of oxidation of various nickel concentrates was carried out using differential scanning calorimetry (DSC). The aim of this study was to determine the ignition temperature and investigate other oxidation behavior of various sulfide-based nickel concentrates. Variables in the experiments were mineralogy, particle size and partial pressure of oxygen with temperature increasing linearly at 25 K/min from 323 to 1023 K (50-750 °C). The igni¬tion temperature was determined to represent the starting point of rapid oxidation. The reac¬tion enthalpies of the concentrates were determined and the amount of heat generated up to various time were used to calculate the extent of reaction. Mineralogical changes at various stages of oxidation were also investigated. For this purpose a second set of DSC-experiments were carried out in which each experiment was interrupted at a desired temperature between 673-873 K. From these tests the weight loss of samples were determined and changes in the individual constituent of sulfide minerals were analyzed. For pentlandite-based Ni-concentrates the ignition temperature was 705-710 K (approximately 435 °C). Pyrite was the first sulfide to oxidize. Reactivity of the violarite-based concentrate was greater than those of the pentlandite-based concentrates. The stoi-chiometry of pentlandite changed before ignition because of preferential oxidation of iron. Rapid oxidation of the pentlandite mineral occurred at about 823 K (550 °C). By 900 K about 90 % of the iron in pentlandite was converted to hematite, and NiS containing some iron was formed.

Jan 1, 1994

By Luciano B. Oliveira, Luis G. C. Marques, Sergio N. Monteiro, Marcos V. M. Fagundes

"Biodiesel production is normally associated with large plantations of oily vegetables such as soybean and colza, in large rural areas. However, in the municipal limits of the city of Rio de Janeiro, southeast of Brazil, biodiesel is being produced from wastes commonly generated by typical urban activities such as sewage sludge, discarded fat from meat markets and post-used cooking oils. In the present work, the experience of producing biodiesel from urban wastes in Rio de Janeiro is assessed. The type of precursor materials, equipments and logistics are presented. The environmental and economical advantages as well as the drawbacks are discussed.IntroductionThe interest for a liquid fuel that could substitute those obtained from petroleum started more than one hundred years ago when Rudolph Diesel tested his no-spark internal combustion engine, impelled by compression, with peanut oil. By that time, petroleum was beginning to be extracted in large scale and no one was concerned with the future environmental problems and its eventual depletion. In the last century, the successful association of petroleum based fuels with the automotive industry was an almost insurmountable obstacle to any attempt to use nonmineral oils [1]. In addition to the greater efficiency and, by then, lower price of the diesel from petroleum, the use of plain vegetable oils introduced undesirable carbon deposits and reduced the engine lifetime. Today, the situation is reverse. The continuous increase in the price of petroleum and, above all, its contribution to climate changes are strongly motivating the use of biofuels to replace those obtained from fossil fuels such as petroleum, natural gas and coal [2].In the case of the common petroleum derived diesel, many countries are now engaged in large scale substitution programs. The USA should produce more than 700 million litters of biodiesel, while the European Community is expected too produce around 6.5 billion litters in 2008. In Brazil, the federal biodiesel program imposed a minimum of 2% addition to the common diesel. This would demand a production of 800 million litters in 2008 [3]. The Brazilian biodiesel is made from a diversified source of vegetables mainly castor bean, African palm and soybean. The main producers are agrobusiness firms located in large rural areas of the Brazilian hinterland [4]."

Jan 1, 2008

By Heng Yi

The salt lake brines that lithium is extracted from have high chloride levels making the brine very corrosive to stainless steel extraction column internals. This is a significant problem in column scale-up to industrial production. Two types of corrosion-resistant ceramic internals, the hybrid ceramic internal and ceramic plate, were designed and tested under pilot conditions for future industrial application in this field. The hydrodynamic results (Yi et al. Ind Eng Chem Res 56 (4):999–1007 (2016), [1]) show that holdup of hybrid ceramic internal is higher than that of ceramic plate by around 50%, while Sauter mean diameter when using the hybrid ceramic internal is smaller than when using the ceramic plate by around 30%. This results in a larger mass transfer area, hence better mass transfer efficiency for the hybrid ceramic internal. Axial dispersion and mass transfer parameters are also examined (Yi et al. Ind Eng Chem Res 56(11):2049–3058 (2017), [2]). The results show that the column with hybrid ceramic internals has 50% lower axial dispersion coefficient and 50% higher mass transfer coefficient, leading to higher mass transfer efficiency. The transfer unit height of the column using hybrid ceramic internals can be as low as 0.2 m, showing very good efficiency. This is promising for near-future applications. Two-phase computational fluid dynamics (CFD) models have been developed for the two columns with ANSYS FLUENT commercial software. CFD successfully predicts the higher holdup and lower axial dispersion coefficients for the hybrid sieve plate pulsed column as measured in the experiments, and the cause for the difference in performance has been explained with information from CFD.

By Sharif Jahanshahi

Calcium ferrite slags are often associated with Professor Yazawa due to his pioneering work on the thermodynamics of this type of melts. Over the past years CSIRO has invested some effort in studying physico-chemical properties of such melts to fill in some gaps in our knowledge and explore opportunities for application of the understanding developed. These investigations cover thermodynamics, transport properties of calcium ferrite based slags, as well as the kinetics of reactions of such slags with refractories. The present paper provides an overview of some of these studies and highlights some of the interesting behavior of such melts. The oxidation state of copper and arsenic in calcium ferrite based slags are predominantly Cu+ and As3+, respectively, at oxygen potentials below 10.1 atm. The concentration ofCu2+ in such slags becomes significant at oxygen potentials of greater than 10&apos;1 atm at 1300 ?C. The activities of CuOo.s and AsOl.S in calcium ferrite slags show strong deviations from the Raoultian Law, while that of CoO is very close to ideal behaviour with respect to pure solid CoO. Addition of Si02 to calcium ferrite slags can have significant effects on the activities of FeO and Fe2O3 and hence the stability of magnetite phase. Transfer of oxygen in calcium ferrite slags is fast with diffusivity of 2xlO?3 cm2/s at 1350 °C and activation energy of 16 kcal/mol Presence of solid phases, such as magnetite, has pronounced effect on the viscosity of calcium ferrite slags. The observed dependence on solid loading and shear rate indicates deviation from Newtonian behaviour. The interfacial tension between copper mattes and calcium ferrite slags is strongly dependent on the matte grade, with the determined values being much lower than the corresponding ones for interfacial tension between similar mattes and iron silicate slags. MgO, Cr2O3 and MgCr2O4 have low solubility in calcium ferrite slags and their solubility increases with increasing copper oxide content of the slag at 1300 °c. The oxidation state of the slag has strong effects on phase transformation, dissolution rate and disintegration of refractories in calcium ferrite slags. Other key factors with major impact on slag-refractory interactions include viscosity and surface tension of slags as well as the contact angle between slag and refractory material.

Jan 1, 2003

By A. E. M. Warner

Inco Limited has long and extensive experience in converting nickel-copper primary smelting mattes over a broad range of nickel/copper weight ratios and combined nickel-copper-cobalt contents. At the Copper Cliff Smelter, the composition of the converter product matte has to meet the requirements of the matte separation process; at the Thompson Smelter, converter matte of a different composition is cast into anodes for nickel electrorefining; and in Soroako, Indonesia, a very low copper product matte is granulated for the Japanese market. Recently, Inco has conducted pilot plant testing of three possible nickel-copper matte continuous converting routes, namely flash converting, oxygen top blowing-nitrogen bottom stirring, and tuyere blowing. This test work has generated substantial new information on nickel-copper matte converting chemistry. This overview paper reviews the metallurgy of nickel-copper matte converting, in particular the behaviour of cobalt and the operating conditions required to meet the iron and sulfur specifications of the product matte. The relevant thermodynamic information is used to discuss the industrial data.

Jan 1, 2003

By George Grandy

Kvaerner experience is being used to develop software to design or simulate crushing and screening plants. The model techniques discussed are presently being used for open-circuit plants and are being extended to closed circuit plants. The program contains a library of routines, each representing a piece of equipment or unit operation, which are assembled into one of several open-circuit plant configurations. Routines include gyratory primary crushers; standard secondary and shorthead tertiary cone crushers; single, double or triple deck screens; and stockpiles, feed bins and belt conveyors. The program uses steady-state models to simulate the performance of crushers and screens that have small residence times and quickly reach equilibrium when operating conditions and/or parameters are changed. The dynamic aspect of the total circuit model concerns the storage units within the circuit, i.e. stockpiles and bins, and, in the closed circuit configuration, circulating loads and size distributions. In many cases, just vendor&apos;s catalog data are necessary for a pre-feasibility simulation; in other cases, actual plant test data are required to obtain more accurate simulations. The entire plant is shown in a single graphic screen so the user can see all the relevant information he might want, and soft-keys are provided for the user to make on- line parameter changes and observe the effects on storage elements, equipment feed rates and the final product size distributions. The model also reports equipment utilization in percentage, power consumption, and other related operating information, and soon, will be able to report estimated capital and operating costs.

Jan 1, 1999

By Behrouz Abedian, Livia M. Racz

"We address dynamic interactions between high-energy, reactive surfaces of polymer-matrix composites and solid surfaces. A common characteristic of these interfaces is that bonding occurs readily upon contact. In many industrial and biomedical applications, it is desirable to suppress this bonding phenomenon. This interfacial effect is discussed in light of the development of our new method of handling polymer-matrix composites in dental applications. This method involves vibration of the solid-polymer interface at different frequencies. For each material, there is a critical frequency at which the sum of the viscoelastic and inertial energies of the fluid at the surface exceeds the energy available for bonding. When the polymer is vibrated at or beyond this frequency, it does not adhere to solid surfaces. An important aspect of the developed process is that it can be used to characterize surface and interfacial properties of polymers under dynamic conditions, whereas existing techniques are restricted to the study of bulk dynamic properties.IntroductionThe purpose of this paper is to report on the development of a new method for manipulating polymer-matrix composite materials used in dental applications, and the potential of this process for use in materials characterization. The materials under discussion have polymer matrices of a combination of bisphenol A-glycidyl methacrylate (BIS-GMA) and triethylene glycol dimethacrylate (TEGDMA), and contain filler particles of silica and/or zirconia glasses. These materials are called direct aesthetic restorative materials, and are used for filling of cavities, repairing chipped teeth, and for other restorations in which appearance is of importance. They have the appearance of natural tooth material, and are therefore in great demand for use in the anterior portion of the mouth(l,2)."

Jan 1, 1998

By Husamuddin Ahmadzai

A survey of regulations and state of the art control technologies is presented relating to the smelting of primary aluminium, copper and recycling of residues. Some costs associated with the alternatives and trends for the coming decade in this. sector are identified.

Jan 1, 1992

By Sarah Beutner Mavrogenes

The mineralogy of three slags from a domestic secondary copper refinery were studied by applied mineralogical techniques to determine the: 1) phases present, 2) phase chemistry, 3) phase abundance, 4) associations, 5) crystalline habit, 6) grain size, 7)microtextures, and 8) causes for certain metallurgical problems, such as metal losses to the slags. The slags were produced by skimming the bath prior to melt-down to allow heat from the flame to reach the bath. The first slag is highly viscous and all three slags contain a large amount of copper. The "first slag", which is skimmed prior to treatment of the bath with fluxes, contains metallic copper, cuprite, delafossite, magnetite, Mg-hercynite, common spinel-chromite solid solution, picrochromite-chromite solid solution, common spinel-picrochromite solid soiution, gahnite, cassiterite, silica-rich glass, and corundum. Its abundant solid refractory phases make the slag difficult to skim. The "soda-rich slag", skimmed after the treatment of the bath with sodium carbonate flux, contains cuprite, delafossite, magnetite, cassiterite, Na-Al-silicate, and Na-Al-Ca-silicate. It contains less metallic copper than the first slag and lacks the refractory minerals. The "phosphorus-rich slag", skimmed after treatment of the bath with a copper phosphide flUX, contains metallic copper, cuprite, delafossite, berlinite, cassiterite, silica, apatite, Cu-Fe-rich apatite, copper phosphate, Cu-Fe-phosphate, and a Pb-phosphate. In contrast to the above three copper-rich slags, recent charges have produced a silver-copper-rich slag. The "silver-rich slag", skimmed after the treatment of the bath with a copper phosphor ide-borax flux, contains, cassiterite, delafossite, cuprite, a Na-Al-silicate, magnetite, metallic copper, MgO, common spinel-chromite solid solution, and wollastonite. Silver ranging from 0.05 to 2.02% was found by atomic absorption and inductively coupled plasma spectrometry analyses in the metallic copper phase.

Jan 1, 1989

By Denise Crocce Romano Espinosa, Andrea Moura Bemardes, Jorge Alberto Soares Tenorio, Daniella Cardoso Buzzi, Tatiana Scarazzato

"In copper plating processes, a fraction of raw materials are incorporated to the final products, while other portions are discarded as effluents. In this study, the application of electrodialysis (a membrane treatment process) was studied for treatment of wastewaters from cyanide-free strike baths, in order to reuse the components of this bath: copper and HEDP. The synthetic solutions studied consider 1 % of ion concentration of the bath used in this process, simulating the rinsing waters to be discarded. The electrodialysis allowed a percentage extraction up to 73% of copper ions and 72% of HEDP from the effluent. Complexes formation between the acid and copper indicates the possibility of recovery of components in the same compartment, obtaining a concentrated solution of these substances that can be reinserted in the process, for compensating drag-out losses. A diluted solution is also obtained, that can be reused as water in rinsing tanks.IntroductionIn metal finishing industries, contaminants in wastewater and the type of treatment required are determined according to the type of operation [l]. Generally, electroplating industries employ conventional wastewater treatments, e.g. oxidation of cyanide and chemical precipitation. This stage promotes reactions with soluble compounds to produce an insoluble precipitate, removed by physical separation. The sludge is dried by press-type filters [2].In this manufacturing sector, part of the raw materials are discarded as hazardous waste. The cost of discarded compounds and the treatment and disposal of waste may compromise profit margins. In addition, water consumption per unit of production stimulates the development of methods able to recover and reuse the largest possible amount of water [3].In some plating processes, cyanide-based substances are used as complexing agents and as raw materials in form of metal salts [4]. However, the toxicity associated with cyanide has been promoting research for the development of new raw materials in plating processes.A study conducted in Brazil [4] evaluated the modification of a commercial cyanide-free bath for processes of copper coating on Zamak. In the performed study, a new alkaline copper bath was formulated using l,hydroxyethane-1,1-diphosphonic acid (HEDP), an organic compound known for forming stable complexes with metal ions.As results of the study, the operational conditions and the formulation of a bath to obtain adherent, uniform and bright layers were established (Table I) [4]."

Jan 1, 2014

By Hongbo Zhao, Jun Wang, Wenqing Qin, Guanzhou Qiu, Xueduan Liu

Bio-hydrometallurgy technology was applied for the extraction of copper from the raw ores of Chambishi Mine in Zambia. A copper extraction of 93.29% was obtained for small scale column bioleaching within 63 days, while a copper extraction of 89.05% was achieved for large scale column bioleaching in 90 days, thus confirming the amenability of the raw ores for effective extraction via bioleaching. The bacteria were cultured in a 6-stage enlarge cultivation. The bacterial cultures with cell concentration of more than 1×108 cells/mL were added into a spray pond of sulfuric acid to be applied in the dump leaching, and a copper extraction of about 50% was achieved within 2 months. The production report revealed that the copper extraction increased by approximate 20%, and the acid consumption was reduced to around 35% as a consequence of adding the bacteria. The industrial demonstration of the bio-hydrometallurgy technique is now well established in Zambia, and further applications of bio-hydrometallurgy in both Zambia and Congo are currently in progress.

Jan 1, 2015

By Yuri Gelfgat

"This paper presents some results of the investigation of the steady magnetic field influence on hydrodynamics and heat/mass transfer in processes of semiconductor single crystal growth (Si, Ge, InSn). The investigation employed mathematical and physical simulation techniques of relevant processes and full-scale experiments on growth facilities. A number of additional MHD phenomena have been found generated in the melt due to the rearrangement of flow pattern, the formation of specific convective cells, and the origin of MHD boundary and shift layer.IntroductionMagnetohydrodynamic (MHD) means of creating forces by contact-free methods in liquid conducting media have been widely used in the production of volume semiconducting single crystals. The goal of this method is to control convective transfer processes in the melt volume and on the crystallization front [1-3]. This is due to the sufficiently high conductivity of semiconductor melts (s = 104 /106 O1m-1 ) and an obvious relationship between the hydrodynamics in the melt and at interfaces and the conditions of formation of single crystals and their quality [ 1].All types of MHD effects rest upon the generation of volume electromagnetic forces in the melt by various means as well as on the possibility to direct them arbitrary in space and to adjust easily their absolute values. Fig. l presents different means how to implement MHD phenomena during single crystal growth. It should be emphasized that in all the modifications given in Fig. l additional energy introduced into the melt cannot influence directly the crystallization process since it is incomparable to the energy of molecular forces. Both the influence and efficiency of MHD means are determined solely by the change of motion, heat and mass transfer characteristics."

Jan 1, 1998

By Chengyi Ding, Xuewei Lv, Senwei Xuan, Chenguang Bai, Kai Tang, Gang Li, Yang Xu

Perovskite easily forms during sintering of vanadium titanium magnetite (VTM) and is unfavorable for the following blast furnace. Steelmaking can concomitantly produce a great quantity of oxidized scale composed mainly of FeO and Fe3O4. Calcium ferrite (CaOFe2O3, CF) can be formed by oxidized scale with lime in air atmosphere and then added to the VTM during sintering. X-ray diffraction (XRD) results indicated that perovskite is not generated at low temperature but only when the temperature increases to 1473 K in the CF–TiO2 system. Therefore, VTM sintering can be performed with a low-temperature process with doping of CF. Perovskite formation is mainly divided into two steps. First, CF melts and produces CaO. TiO2 and CaO then combine to produce perovskite. This paper also discussed the reaction mechanism of CaO–Fe2O3–TiO2 ternary system to compare the generation routes of perovskite.

Mar 1, 2018

By L. I. C. Fernandez, E. B. Ferreira Filho, L. G. Pedroti, L. G. Justino, W. E. H. Fernandes, R. C. S. S. Alvarenga

More and more industries have been concerned with the disposal of the wastes generated in their production processes, once this generates a positive impact, both visual and economic enterprise, no more needing to have resources for transport and final disposal of wastes. In this context, and seen the importance of the Portland cement a sa building material, which aims the creation of an ecological cement from the mix of two wastes, the grits, which is a waste generated in pulp production, and the granite beneficiation waste. It proceeded initially with the chemical and physical descriptions of the wastes. Five mixtures, varying the percentages of the wastes and the preparation method of the raw materials, were prepared. After,the blends were sintered in a muffle furnace at 1300 °C for 15 min, forming new compounds that were compared with national cements, according to the Brazilian technical standards. It was concluded that the sintering of the product obtained satisfactory results, presenting good binder characteristics, however, some parameters were outside the limits for common Portland cements such as rapid setting time, large expandability and low compressive strength.

Mar 1, 2017