Hot Deformation Behavior of Nb Microalloyed Coiled Tubing Steel

"Hot compression test of Nb microalloyed coiled tubing steel is performed on Gleeble3500 at 1123K—1373K and strain rate from 0.001 to 5s-1. It is found that flow softening occurs and the flow curves exhibit a peak with a characteristic of dynamic recrystallization (DRX) and change with temperature and strain rate significantly. The peak stress and peak strain are dependent on the Zener-Hollomon relationship with activation energy of 390 KJ/mol. On the basis of Avrami equation and the Zener-Hollomon parameter, it is obtained that the dynamic recrystallization kinetics equation with which the calculated and measured recrystallization fraction is very close. On the results of hot compression test, the Nb microalloyed coiled tubing steel is rolled by Thermo-Mechanical-Control-Processing (TMCP), and it is obtained that the yield strength and tensile strength of Nb microalloyed coiled tubing steel are 565MPa and 685MPa respectively, and the elongation percentage is 30.1%.IntroductionCoiled tubing is widely used in oil field for well logging, well completion, drilling, work over and other operation in various fields to solve a number of conventional operating techniques problem which are difficult resolved, and it plays a more and more important part in exploration and production at oil field. [1] It will improve the efficiency of exploration and exploitation, studying, developing and using coiled tubing technology. Therefore, the development of domestic coiled tubing materials and manufacturing technology are great significance. It is well known that Coiled tubing has relatively poor working conditions and complex force state. So, the coiled tubing needs satisfier a kind of high strength, high plasticity, and corrosion resistant under complex oil gas condition. As the coiled tubing technology developed, the level of the coiled tubing steel is from CT55 originally to CT90 and CT100, and the corresponding tensile strength is 483MPa-758MPa. [2, 3]"