By Jilai Xue

Experiments with various industrial cathodes ranging from 35 wt.% to 100 wt.% graphitic and fully graphitized carbons were carried out in a laboratory aluminum electrolysis cell. Sodium and cryolite bath penetration into the cathode samples was measured by XRD and SEM-EDS analysis. For a higher cryolite ratio in the bath, the cathodes with lower graphitic carbons exhibited more sodium penetration than the fully graphitized. The increased graphitization in the cathode materials can reduce Na, NaF and Na3AlF6 penetration. SEM-EDS inspection reveals that the sodium and fluorides penetration within the cathode samples has different patterns for varying graphitization of the carbon materials. XRD quantitative analysis indicates that there is a large percentage of Na3AlF6 in the penetrated bath. The results can provide useful information for quality evaluation of the industrial cathode products.

Jan 1, 2010

By Shengfan Zhou, XUEWEN WANG, Bianfang Chen, Mingyu Wang

Vanadium was leached from roasted stone coal by NaOH solution, and the effect of leaching temperature, leaching time, addition of NaOH, liquid to solid ratio, the grinding fineness of stone coal, and stirring speed on the vanadium leaching rate was studied. The kinetics analysis for the process is presented by the shrinking core model. The results show that the vanadium leaching ratio of roasted stone coal can be beyond 75% at the 6% NaOH addition, leaching temperature of 95°C, leaching time of 7h, liquid to solid ratio of 1.2mL/g, and grinding fineness of 0.111mm. The leaching process is controlled by interfacial reaction kinetics and the apparent activation energy was 59.36kJ/mol.

Jan 1, 2016

By Sumantra Mandal

The hot deformed microstructure of the 15Cr-15Ni-2.2Mo-Ti modified austenitic stainless steel (commonly known as alloy D9) was investigated employing electron backscatter diffraction (EBSD). Hot compression tests were conducted in a Gleeble thermo-mechanical simulator at temperatures of 1173K-1373K (in steps of 100K) with a strain rate of 10 and 100 s-1 to different strains. Various kinds of deformation patterns were observed inside the deformed grains. These were inferred as the development of geometrically necessary boundaries or formation of parallel set of micro-bands. Recrystallized grains were partitioned from the deformed grains employing grain orientation spread approach. Extent of dynamic recrystallization (DRX) was found to be minimal at 1173K. DRX was predominantly found to happen at and above 1273K which increases with increase in strain. DRX nucleation and development mechanisms were discussed with respect to bulging of the parent grains and sub-grain rotation. Special emphasize is given on the role of annealing twins on DRX nucleation and subsequent expansion.

Jan 1, 2009

By Guomin Jiang

Potassium ferrate is an excellent multifunctional reagent for wastewater treatment, but its preparation is crucial. The improved hypochlorite oxidation method was used to prepare potassium ferrate in this study. Iron nitrate, the preferred iron source, was added into hypochlorite solution and then the stabilization agent was added during the purification process of product. The influence of available chlorine content, iron molecular proportion, reaction temperature and reaction time on potassium ferrate preparation was investigated. The optimal condition for potassium ferrate preparation is 15% of available chlorine content , 0.6 of iron molecular proportion , 30i of reaction temperature , 45min of reaction time. The yield of potassium ferrate is about 67% with high purity (> 99%). The structure and performances of the product was characterized by XRD, EDX, SEM, TG and IR and the results show that the prepared product is consistent with the properties of potassium ferrate(VI).

Jan 1, 2010

By Jian Yang

The mechanism of resulfurization in the desulfurization process with magnesium vapor produced in situ by aluminothermic reduction of magnesium oxide was clarified in the present work. The influences of various operating parameters on the resulfurization were studied and the methods that could prevent resulfurization were proposed. There are two kinds of mechanisms of resulfurization in the desulfurization process with magnesium. One is decomposition of the desulfurization product of MgS under the inert atmosphere. The other is oxidation of MgS under the oxidative atmosphere. Under the present experimental conditions, lowering operating temperature and oxygen partial pressure in the atmosphere could effectively prevent the resulfurization. Adding CaO onto the melt surface was an effective method for preventing the resulfurization due to transformation of the desulfurization product of MgS into the more stable compound of CaS. Since addition of the activated charcoal powders greatly decreased the transfer rate of oxygen in the atmosphere to the melt surface, it also reduced the resulfurization remarkably.

Jan 1, 2006

By Dong-Wei Li, Tao Zhang, Diao Jiang, Zhou Wang

The feasibility of simultaneous vanadium extraction and phosphorus removal from vanadium-containing hot metal was demonstrated with laboratory experimental investigation.The effect of CaO addition on the distribution behavior of vanadium, phosphorus between basic vanadium slag and semi-steel as well as the influence of basicity on the leaching behavior of vanadium, phosphorus was particularly studied. Results show that vanadium oxidation ratio slightly decreases with the increase of basicity, but phosphorus oxidation ratio rapidly increases with the increase of basicity. The leaching of roasted vanadium slag with various CaO contents indicated that the optimal slag basicity for extracting vanadium was 1.5. The maximum leaching efficiency of vanadium could reach 84.02% and the sequence of vanadium leaching efficiency by using different leaching reagents was: 160 g/L Na2CO3 > 100 g/L NaHCO3 > 400 g/L (NH4)2CO3 > 5% H2SO4.

Mar 1, 2017

By Biswadeep Saha, Meenakshisundaram Ramanathan, Chai Ren, Sivaraman Guruswamy

"Fe-Ga alloys have a large low-field magnetostriction and these alloys are attractive candidates in energy conversion and harvesting applications. Small additions of W also increase the magnetostriction of Fe. In this paper changes in magnetostriction by W substitution for Ga in various Fe-x at.% Ga alloys are presented. Fe-Ga-W single crystals were grown using vertical Bridgman Growth technique. [001]-orientated single crystal samples were prepared with faces within 1 degree off <100> orientation. The samples were annealed at 1150 °C in the alpha-phase region and water quenched. The magnetostriction coefficient (3/2)A-100 measurements were made on these Fe-Ga-W single crystals. The result on the effects of W substitution and annealing on the magnetostrictive behavior of these alloys are discussed.*Support of this work by NSF-DMR under the award DMR-0854166 is gratefully acknowledged.IntroductionMagnetostrictive materials changes their dimension exhibit reversible strains and changes in elastic properties in the presence of an applied magnetic field or the reciprocal effect of changes in the magnetic properties with the application of stress [IJ and are very important in sensor, actuator device, linear motor, magnetomechanical devices, microelectro- mechanical devices, active vibration dampening devices application areas. The discovery of an order of magnitude enhancement in the magnetostriction of Fe with Ga addition coupled with low saturation magnetic fields, and excellent mechanical properties opened up the possibility of obtaining larger magnetostriction values in other low-cost ductile a-Fe phase based alloys with alloying additives that are less expensive than rareearths such as Tb and Dy [2·4l_ The magnetostriction values observed in Fe-Ga single crystals are sensitive to thermal history and composition. The formation of second short range ordering phases and local defects inside crystal structure can also cause a dramatic change to this alloy's magnetostriction behavior [5-9l_"

Jan 1, 2012

By W. M. Cross

Bubble attachment time measurements for the rare-earth phosphate minerals monazite and xenotime were made as a function of oleate concentration, sodium fluoride addition, and temperature. Results indicate that the rare-earth phosphates behave similarly to other phosphate minerals, notably collophanlte and fluorapatite, which have been studied previously. The addition of sodium fluoride yielded a modest decrease in bubble attachment time with fluoride additions below the apparent fluoride surface precipitation point, while at fluoride additions greater than the apparent precipitation point a significant decrease in attachment time occurs. Increasing the temperature or the system gave a slight decrease in bubble attachment time in the absence or sodium fluoride. With sodium fluoride addition and below the apparent fluoride surface precipitation point, an increase in temperature actually increased the attachment time. For sodium fluoride additions above the apparent fluoride surface precipitation point, a temperature increase significantly decreased the attachment time.

Jan 1, 1989

By Zhongning Shi, Ramana G. Reddy, Min Li, Zhaowen Wang

Electrodeposition of cobalt from cobalt tetrafluoroborate (Co(BF4)2) was investigated using 1- butyl-3-methylimidazolium tetrafluoroborate (BMIMBF4) ionic liquid. The experiments were conducted at 353 K. Chronoamperometry experiments confirm that the electrodeposition of cobalt on tungsten electrode proceeds via three-dimensional instantaneous nucleation with diffusion-controlled growth process. The average diffusion coefficient of Co(II) was found to be 7.5 × 10-8 cm2s-1 at 353 K, which is in good agreement with the estimated value from cyclic voltammetry. The electrochemical deposit was characterized using SEM-EDS and XRD methods. The SEM image shows formation of a dense and compact deposit at - 0.75 V. The EDS and XRD analysis confirm that the obtained deposit is pure cobalt metal.

Jan 1, 2015

By M. F. Hochella

Transmission electron microscopy (TEM) and energy dispersive X-ray (EDX) analysis have been used to study the mode of occurrence and mineral associations of gold in partially oxidized high grade gold ore from the Carlin sediment-hosted deposit. Rounded.gold particles have been observed that range in size from 0.03 to 0.1 p.m (300 to 1000 A) in diameter. The gold is associated with maghemite h-Fep3l and a K-Al-Si-bearing phase that is suspected to be illite. Detailed descriptions of gold and its mineral associations in &apos;Carlin-type&apos; gold deposits are critical not only to understanding the mechanism of fluid transport and precipitation of gold, but also to developing improved metallurgical techniques for the recovery of gold from refractory ore. Direct observation of gold in unoxidized ore is rare due to its relatively high degree of dissemination and low average bulk concentration which averages 9 ppm according to Radtke (1). Hausen and Kerr (2) observed 1 to 5 p.m grains of gold directly in oxidized ore but these microscopically visible particles account for only a small percentage of gold present in the ore. The samples used in this study were selected from individual beds of high grade, partially oxidized ore (4.55 oz/ton or 156 ppm gold) that were collected in the Main pit of the Carlin mine. The samples were collected from several thinly laminated carbonate micrite beds within the top 50 meters of the Roberts Mountains Formation. The carbonate micrite has been altered by hydrothermal fluids to a calcite-absent, moderately silicified rock referred to as alteration zone #3 by Bakken and Einaudi (3). Based on petrographic and SEM studies, the samples contain carbonaceous matter, and both pyrite and iron oxide pseudomorphs after pyrite. The oxidation of pyrite may be a pro-duct of deep weathering, in which case limited remobilization of gold may have occurred. TEM sections of the rock were prepared by first embedding small chips in low viscosity epoxy. The epoxy blocks were cut with a Reichert Ultracut E ultramicrotome, producing thin sections less than 0.1 p.m thick. The sections were examined with a Phil-lips 400ST TEM at 120 keV in both imaging and selected area diffraction modes. Native golci*was easily detected in TEM bright field images due to the large electron density contrast between gold and all other phases that are present (Figs. 1 and 2), Gold was positively identified with high spatial resolution EDX analysis in the transmission electron microscope, although selected area diffraction of individual grains was not successful EDX analyses of the platy and massive minerals immediately surrounding the gold particles typically indicate the presence of Si, AI, K, and Fe, However, the d-spacings derived from selected area diffraction of these polycrystalline masses (as, for example, in Fig. 2) give an exact match for maghemite. As a result, there is no diffraction information to identify the K-AI-Si-bearing phase(s). The lack of a diffraction pattern could be due to either electron beam damage or to a poorly crystalline phase(s).

Jan 1, 1987

By D. Gu, R. G. Anthony, C. V. Philip, M. E. Huckman

"In this paper, we review the equations needed to construct an ion exchange column model. These models contain three major components: 1) a differential material balance around the column, 2) a differential material balance around an ion exchange particle, and 3) a constitutive equation for diffusive flux. We then examine the ability of a fairly simple mathematical model to predict ion exchange column experimental data. This model contains the traditional absorption theory equations and is used to predict the behavior of a column filled with a hydrous crystalline silico-titanate and which is removing trace amounts of Cs+ from a high pH, complex electrolyte solution. Finally, we propose replacing Fick's law with the Nemst-Planck equation as the constitutive equation for diffusive flux. We use a NemstPlanck type model to predict batch experimental data, then evaluate it by comparing it's ability to predict experimental data to that of a more traditional Fick's law type model. The data from this comparison suggests that the Nemst-Planck type model yields better results.IntroductionMillions of gallons of strongly basic, radioactive waste are currently stored in underground storage tanks at Hanford and Savannah River and several locations within the United States. Due to the limited life expectancy of the tanks, there is a pressing need to remediate these wastes. This need has prompted the recent development of new ion-exchange materials for removing radioactive elements from aqueous solutions. A novel material called TAM-5 has been developed jointly by Texas A&M University and Sandia National Laboratories. TAM- 5, a crystalline silico-titanate, is highly selective for Cs + in the complex electrolytic solutions typical of these wastes. It is stable in very basic solutions and in radioactive environments [1, 2 ,3]. In laboratory testing to determine the selectivity of various materials, TAM-5 was superior to other candidate ion exchangers [4, 5]. The selectivities were determined by measuring a distribution coefficient, Kd, which is defined as the concentration, gig or mmols/g of Cs in the solid phase divided by the concentration, mg/L or mmols/mL, of Cs in the liquid phase. The units of Kd are ml/g or L/kg. Table 1 shows Kd values for TAM-5 compared to 9 other candidate materials in a typical waste solution [6]."

Jan 1, 1996

By Dong Joon Min, Joo Hyun Park, Mi Sun Choi, Jae Hong Shin

Sublimation of ZrCl4 is important for the production of nuclear grade metallic Zr in Kroll’s process. The sublimation kinetics of ZrCl4 was investigated by TGA under both isothermal and non-isothermal conditions. The sublimation rate of ZrCl4 increased with increasing temperature under isothermal conditions. ZrCl4 sublimation was confirmed to be a zero-order process under isothermal conditions, whereas it was first-order kinetics under non-isothermal conditions. The activation energy of ZrCl4 sublimation under isothermal conditions was 21.7 kJ/mol. The activation energy for non-isothermal sublimation was 101.4 kJ/mol and 108.1 kJ/mol with the Kissinger method and Flynn- Wall-Ozawa method, respectively. These non-isothermal activation energies were very close to the heat of sublimation (103.3 kJ/mol). Sublimation occurs by two elementary steps: surface reaction and desorption. Therefore, the overall activation energy of ZrCl4 sublimation is 104.8(±3.4) kJ/mol. The activation energy of the surface reaction and desorption steps are proposed to be 83.1 kJ/mol and 21.7 kJ/mol, respectively.

Jan 1, 2014

By H. Ipek

In this study the effects of interstitial ratios on k-feldspar samples were investigated. The k-feldspar samples were taken from Egypt using dry batch grinding conditions and a kinetic model. Three different mono size fractions (-3350+2360, -850+600 and -300+212 µm) were ground separately for 0.5, 1, 4, and 8 minutes and at four different interstitial ratios (125%, 100%, 75% and 50%) using a Bond mill with a mixture of five ball sizes. The mill used was at a size of 30.5 cm diameters, with 30.5 cm length, providing a total mill volume of 22272 cm3. The mill has a total mass consisting of 22648 g. steel ball mixtures of 38.10, 31.75, 25.40, 19.05 and 12.70mm diameters, occupying 22% of mill volume. The mill rotates at a speed of 70 rpm. The weights of the feed charges were 3000, 2000, 1000, and 500 g for 125%, 100%, 75% and 50% filling of the interstices of the balls respectively. The specific rate of breakage (Si) was determined from the top size fractions at different grinding times that were mentioned above and the model parameters were compared for the four different powder filling ratios (U). In many investigations, it has been found that an interstitial filling ratio of U = 0.6-1.1 is a good powder ball loading ratio to give an efficient breakage in a ball mill. In this study, it was found that U=1.25 is a good ratio for K-Feldspar.

Jan 1, 2006

By T. T. Chen

Copper anodes generated from copper scrap are relatively rich in Sn, Zn and Fe. Because of the presence of oxygen, only trace amounts of Sn occur in solid solution in the copper crystals. Thus, Sn occurs mainly as SnO2, Cu-Sn-Ni oxide and Sn-Ni-Zn oxide in the copper anodes, and Zn and Fe occur mainly as minor constituents in the Sn-Ni-Zn oxide and Cu-Sn-Ni oxide. During electrorefining, these oxide species are liberated from the copper anodes and report directly to the anode slimes. The trace amounts of Sn present in solid solution in the copper crystals dissolve but reprecipitate as Sn arsenate or a Sb-As-Sn-O phase. Accordingly, high Sn contents in copper anodes do not lead to elevated Sn concentrations in the electrolyte.

Jan 1, 2010

By S. Eck

In previous work the influence of the casting speed on the flow field and the shape of the solidification front in an industrial 0.82 x 0.25 x 0.8 m³ bronze caster had been investigated. Both numerical and experimental model represented 1:1 the real caster geometry. A comparison of the results of both numerical and experimental models for the flow during the casting process showed a good agreement in the qualitative velocity fields (flow direction and vortex formation). This work represents a parameter study of the numerical model with variations of the turbulence conditions at the inlet in order to clarify their influence on the flow field in the caster. In order to find the best boundary condition at the inlet, the numerical calculations for water have been compared with the measured flow fields in the water model. The new boundary conditions were then applied to the numerical model of the bronze casting process.

Jan 1, 2009

By A. Mezei

A process has been developed to recover cobalt, gold and bismuth from the NICO deposit in Canada. The process consists of a bulk rougher flotation followed by an optional separation by flotation to produce a bismuth concentrate and a cobalt concentrate, grading on average 12.8 % Bi and 1.8% Co, respectively. Cobalt is leached by pressure oxidation at 97% efficiency, producing a pregnant solution suitable for further processing. Before optimization, about 38% of the bismuth is recovered in the selective concentrate, wherefrom it is recovered by ferric chloride leaching followed by cementation, at overall efficiencies exceeding 98%. The gold is recovered from the cobalt and bismuth leach residues by cyanidation, at 95% efficiency. Previous work described the results of the leaching of the concentrates, recovery of gold (Part I) and the recovery of bismuth (Part 11). This work describes the results of the cobalt recovery testwork and the resulting conceptual flowsheet. The sulfur dioxide-oxygen system was the most efficient for the oxidationlprecipitation of iron and arsenic from cobalt bearing pregnant leach solutions, producing purified solutions assaying <1 mg/L As and <8 mg/L Fe. The efficiency of cobalt solvent extraction (from the resulting purified PLS containing about 1 g/L Co) ranged from 9 1 to 98%; the co-extractions ranged from 88 to 100% for copper, from 28 to 33% for magnesium, from 6 to 7% for calcium and from 96 to 98% for zinc. Sulphide precipitation processes (using either sulfur dioxidelelemental sulfur or sodium sulfide) produced residual copper concentrations in the cobalt strip solution ranging from 0.1 to 2 mg/L Cu. About 90% of the calcium and magnesium were separated by scrubbing the organic with cobalt sulfate, producing residual concentrations of 12 mg/L Ca and from 180 to 330 mg/L Mg in typical feed solutions directed to cobalt carbonate precipitation tests. Cobalt carbonate precipitation efficiencies ranged from 75 to 78% when calcium and magnesium co- precipitations were restricted from 8 to 17% and 0.3 to 0.4%, respectively. The limits required by most stringent specifications on commercial grade cobalt carbonate products were met or exceeded.

Jan 1, 2002

By Pengfu Tan

Xstrata Copper at Mount Isa in Australia has operated one copper Isasmelt furnace and four P-S converters. The phenomena of foaming occur in above 10% of converter operations. A thermodynamic model of copper P-S converter and a viscosity model of converter slag have been developed to simulate the slag blow and copper blow. The model predicts the chemistry and viscosity of copper skims during copper blow. The effects of oxygen potential, charge of dirty materials, slag carry-over, under-blowing, over-blowing, and temperature on the foaming and viscosity of copper skims have been discussed. Some improvements of the industrial operations have been presented.

Jan 1, 2006

By Jilai Xue, Jun Zhu, Yongqiang Liu

"Up-grading silicon feedstock by removing B and metal impurities can improve process efficiency and lower production cost in metallurgical processing for solar cells production. Hydrometallurgical study has been carried out in laboratory through alternative treatments of the metallurgical grade (MG) silicon (-200 mesh) by using hydrogen peroxide, hydrofluoric acid (4 mol/L) and NH4Cl-NH4 F (30:5) solution. The experiments were usually performed under mechanical agitation at 70 ? for 5 h. ICP-AES analysis showed that B content in MG silicon after the hydrometallurgical treatment has reduced by 92.4 %, and Fe, Al, and Ca contents by 98.8 %, 98.0 % and 81 %, respectively. Kinetics of these processes was also studied for better understanding of the effects of silicon powder size, acid concentration, leaching and oxidizing time on the processing chemistry.IntroductionAs one of the most clean and promising new energy, solar energy is used more and more in many countries all over the world, especially in United States, Japan and European Union. Most of industrialized states have made their national photovoltaic plans, which have stimulated further increase in use of solar energy. Photovoltaic Industry is at a high growth rate about 30 % [1-2]. For silicon solar cells to remain the mainstay for the photovoltaic industry it is necessary to develop a low-cost solar grade silicon feedstock [3]. At the same time, the availability of the currently M-G silicon from the semiconductor industries becomes limited [4]. With the advantages of low cost and low energy consumption, metallurgical routes to product solar–grade silicon get more attention [5]. These routes mainly include pickling, slagging, vacuum processing and directional solidification, etc [6]. Among them the most important processing step is the directional solidification, but it still can not satisfy the industrial demand for removing B. Removing B from Si remains as one of the most difficult and important processes in making M-G silicon [7]."

Jan 1, 2012

By A. R. Kiani-Rashid

Controlled graphitization has become known as a practical method for improvement of wear resistance and machining properties in steels. In this paper, the effect of heat treatment on microstructure of CK45 steel has been investigated. Austenitising was carried out at 920°C for 5 hours. Besides, isothermal transformation was conducted at 750°C in the time range of 1-20 hours. The microstructure of the steel considerably changes by this heat treatment process which exhibits the effects of temperature, appropriate austenitising duration and isothermal transformation. Conducted experiments show a suitable distribution of semi-spherical graphite particles especially on the surface of the steel. Also, analyses demonstrate that the amount of formed graphite in the austenitising temperature 920°C is more than graphite in single heat treatment temperature of 750°C.

Jan 1, 2010

By Wei Yu, Tiejun Chun, Jian Pan, Deqing Zhu

In this paper, improving the pelletization of Brazilian hematite by adding a boron bearing additive was carried out, and the pelletization parameters were also optimized. The mechanism of boron bearing additive was revealed in the kinetics of crystal grain growth by using LEICA microscopy and its software to measure hematite grain growth. Good qualities of green balls are manufactured with drop numbers above 5.7 times/0.5m, compressive strength higher than 13 N/pellet and thermal shock temperature over 620? under the following conditions: 1.2wt% bentonite, 0.4wt% boron bearing additive, 7wt% moisture and pelletizing in disc for 15 min. When the green balls were preheated at 1000? for 8 min and fired at 1280? for 15 min, the compressive strength of the fired pellets containing boron bearing additive is about 3096 N/pellet, which is far beyond the standard requirement for good quality pellets. Compared to the fired pellets without adding any boron bearing additives, the compressive strength of fired pellets containing boron bearing additive is increased by 1225 N/pellet. It is revealed that adding boron additive into the hematite pellets help to form more liquid phases, lower the activation energy of the hematite grain growth by 135.2 kJ/mol and increase grain growth rate by 33.6%, leading to higher strength of fired pellets due to forming more coarse and dense recrystallized hematite and energy saving by firing at lower temperatures for shorten time.

Jan 1, 2011