Basic Research on External Desulfurization of Hot Iron by Dolomite

"This paper investigated a new desulfurizer, dolomite and ferrosilicon. Magnesium vapor produced by silicothermic reduction of dolomite and ferrosilicon in an immersion tube of molten iron was injected into the molten iron by carrier gas through the underpunch of the tube and desulfurization reaction occurred. In order to explore the desulfurization process of molten iron by the new desulfurizer, the thermodynamics, and experiments of magnesium vapor production and desulfurization have been studied. Through thermodynamic calculation, the reaction temperature of magnesium vapor production by 75ferrosilicon and light-burned dolomite is 1838K in the standard state and decreased with the decreasing partial pressure of magnesium vapor, PMg· When PMg=25kPa, the reaction happens at 1673K. From experiments of magnesium vapor production, reduction efficiency of Mg vapor is about 60 % in 15 minutes at 1673K. From hot metal experiments, the desulfurization efficiency is 89.35%, and the lowest sulfur concentration after desulfurization is 46ppm.IntroductionPretreatment desulfurization of hot metal has become a necessary step in modem optimizing steelmaking process for its cheap cost, which can not only liberate of blast furnace productivity and reduce the burden of produce steel, but also effectively improve overall economic efficiency of the iron and steel system[l-ZJ_ At present, injection magnesium particle is one of the two main methods of desulphurization in hot metal owing to its strong affinity for sulphur, low amount of slag produced, low iron loss in slag skimming and low equipment investment[3l. However, there are still some insufficiencies on the hot iron pretreatment with magnesium particles at present[4-5l"