By Charles Fulton

The study of the condensation of zinc from its vapor was undertaken to shed light on certain problems encountered in large-scale electric zinc-furnace work recently conducted. It is a matter of common knowledge that one of the disadvantages of the arc type, electric zinc furnace, is the production of a large amount of blue powder and proportionately little liquid spelter, for, as stated by Stansfield,1 "A notable defect in the electric smelting of zinc ores is the difficulty experienced in obtaining the distilled zinc in the liquid state; when zinc ores are smelted electrically, very little liquid metal is commonly obtained, nearly all of the zinc being in the state of powder."

Jan 8, 1918

By Ursula E. Wolff

The precipitation of carbides from an alloy containing 33 pct Ni, 21 pct Cr, balance iron, was investigated electron microscopically by means of extraction replicas and thinned metal foils. Annealing temperatures ranged from 565°to 870°C and up to several thousand hours. M23C6 precipitated in pain boundaries, incoherent and coherent twin boundaries in that sequence. The orientation relationship between carbides and austenite matrix was determined and correlated with the morphology of the carbides and with the type of boundary in which precipitation occurred. In large-angle grain boundaries, as well as in coherent twin boundaries, the carbides had the same orientation as one of the adjacent pains. These carbides formed sheets of individual flakes with shapes related to the orientation of the boundary. In incoherent twin boundaries carbides precipitated in ribbons composed of pavallel rods. An unidentified subcarbide was found to precede precipitation of M23C6 in these boundaries. The M 23 C6 rods had a kind of fiber texture with (110) parallel to the long dimension of the rods and ribbon, and with orientations of both of the adjacent twin-related austenite crystals Predominant in the texture of the carbide. A hard sphere crystal model has been used to discuss orientation and morphology of the carbides in terms of free volume and vacancies available in the boundaries. A number of papers have dealt with the morphology of chromium carbide (M23 C6) precipitated in austenitic stainless steels.1"7 In all these investigations, the carbides were examined in the electron microscope by means of extraction replicas. With this technique, the carbides retain the spatial distribution they had in the bulk sample. However, since the matrix is dissolved in the process, the particles can turn in an unpredictable way; and the orientation relationship between matrix and carbides cannot be established. In this paper the results of studies on extraction replicas and on thinned metal foils are reported. These studies were undertaken to determine the matrix-to-car bide orientation relationship, and to correlate the orientation of the carbides with their morphology. PROCEDURE The material used was an austenitic alloy with 33 pct Ni, 21 pct Cr, balance iron, containing approximately 0.05 pct C. Coupons of 1.25-mm sheet were first solution-annealed at 1050°C for 15 min and air-cooled. Then, to precipitate the carbides, samples were isothermally annealed in the range from 565" to 870°C for times up to several thousand hours. All further specimen-preparation procedures were carried out after the final anneal. Carbon extraction replicas from polished and etched surfaces were made with 10 pct bromine in methyl alcohol.' Thin foils were prepared from punched-out 3-mm-diam disksg which fit into the electron-microscope holder. The disks were prethinned by grinding to approximately 0.5 mm thickness, and then electro-polished in a polytetrafluoroethylene holder1' with a solution containing 5 pct perchloric acid in acetic acid to which 10 g per 1 Cro3 and 5 g per 1 nickel chloride were added (etchant modified from that of Briers et al."). This solution dissolves neither the carbides nor the austenite around the carbides preferentially. By using extraction replicas, electron micrographs and selected-area electron-diffraction patterns were taken from the same carbide arrays. By using thin foils, electron micrographs were made from a grain boundary area containing carbides. Electron-diffraction patterns were then taken from the same area and from each of the adjacent grains separately. In this manner, the orientation of each grain could be determined without interference by the carbide pattern. A peculiarity of extraction replicas should be pointed out. After the matrix is etched away, the carbide arrays float freely in the etching and washing solutions, and are held in place only at the anchoring points in the carbon replica. When the replica is picked up with a screen the carbide arrays tend to flip to one side. Thus, while the surface features are preserved, the original arrangement of the carbides may severely and unpredictably be disturbed whenever the specimen contains large amounts of interconnected carbides. Nevertheless, it is possible to correlate the different morphologies of the carbides with the type of boundary in which they have precipitated. RESULTS 1) Extraction Replicas. Fig. 1 shows that the grain boundaries usually are curved, multicornered surfaces of random orientation. The coherent twin boundaries (which are (111) planes) cut a grain into parallel slices. Incoherent twin boundaries occur at the ends and on the steps of twins and are often narrow, parallel-sided strips which are much longer than they are wide. Different morphologies can clearly be distinguished for the M23Ce carbides precipitated in each of these types of boundaries, and agree well with those observed by kinzel.2 The kinetics of this precipitation has been investigated." The first carbides precipitate in junctions of three grain boundaries and fan out from there into the adjoining boundary surfaces, Fig. 2(a). These carbides are oriented randomly, Fig. 2(b), and become coarser and thicker as annealing time increases. The large-angle grain boundaries are next to fill

Jan 1, 1967

By C. H. Li, J. Washburn, E. R. Parker

Yield stress in single crystals of zinc was shown to be dependent on prior annealing temperature and rate of cooling after annealing. Rate of strain hardening beyond the yield was not sensitive to annealing procedure. A tentative mechanism for the effect was discussed. COMPARATIVE mechanical tests of metal single crystals generally show a large scatter of results. Many factors may contribute to this variation. The present investigation was undertaken to evaluate the influence of two factors not ordinarily considered of major importance—annealing temperature and cooling rate after annealing. Since plastic properties of crystals are thought to depend on the presence of lattice imperfections, it follows that a variation in properties should result from differences in the distribution and density of these imperfections. Furthermore, in the light of current theories of interaction between edge dislocations and lattice vacancies,' it seems possible that annealing temperature and subsequent rate of cooling might play a part in this distribution. Analysis of the effect of these variables on plastic properties may lead to a better understanding of the annealed state. Single crystals of zinc which have been strained in simple shear undergo complete recovery of mechanical properties upon subsequent annealing. This behavior is useful because a single specimen can be used repeatedly, thus eliminating the uncontrollable variables introduced by the use of many crystals. The test section of the crystals used for these experiments was a cylinder 1/8 in. thick with a cross-sectional area of about 1/3 sq in. The specimens were acid-machined from spherical single crystals 1 in. in diameter in such a way that the slip plane (0001) was at right angles to the axis of the cylinder. In testing, a shear stress was applied along one of the slip directions, [2110] in the (0001) plane.' All crystals, unless otherwise noted, were grown in a helium atmosphere from molten 99.99 pct pure Horse Head Special Zinc. Fig. 1 is a family of curves obtained from one crystal. Each curve was obtained by deforming the crystal to 10 pct strain at a rate of 3 pct per min, following an anneal of 1 hr at 260°C. The strain direction was reversed every other time so that no progressive change in shape of the specimen took place during the series of tests. Since the stress-strain curve was reproducible within a fairly narrow range under the same conditions of annealing, it was then possible to determine the effect of changes in annealing conditions. A crystal was tested repeatedly as previously described but the annealing temperature and rate of cooling preceding each test were varied (Fig. 2). Two cooling rates were used, approximately 30°C per min and 3°C per min. Annealing was conducted at three temperatures, 200°, 300°, and 400°C. For a given annealing time and rate of cooling the room temperature flow stress was higher the higher the annealing temperature. The increase in flow stress was small as the annealing temperature was increased from 200° to 300°C but rose rapidly when the annealing temperature was raised from 300" to 400°C. Faster cooling from the high temperature produced an even greater strengthening of the crystal. The curves were obtained in the order indicated by the numbers. The stress level associated with a certain annealing treatment was, within the limits of scatter, always the same regardless of the

Jan 1, 1954

By C. A. Allen

FOR over three years we have been endeavoring to reduce the number of fatalities and minor accidents in Utah. The physical condition of the o? Represents the average of 4 States mentioned excluding the catastrophes indicated. FIG. 1.-NUMBER KILLED PER MILLION SHORT TONS OF COAL PRODUCED IN COLO¬RADO, NEW MEXICO, UTAH, WYOMING, AND BITUMINOUS MINES OF THE UNITED STATES, 1914 TO 1920. mines, concentrators, and smelters is good, yet the number of accidents,

Jan 5, 1922

By Orville R. Lyons

THE Russellton preparation plant of Republic Steel Corp., located north of Pittsburgh, Pa., prepares 395x0-in. Thick-Freeport coal by means of a 13-ft 6-in. diam Chance cone and 16 No. 7 Deister tables. The plant feed ranges between 370 and 410 tons per hr, of which approximately 31 pct is 1/4xO-in. size, and the plant reject ranges between 14 and 16 pct of the feed.

Jan 6, 1953

By C. A. Siebert, S. H. Bush

Isothermal temper-embrittlement studies were conducted on a 5140 steel at various temperatures for times as long as 3000 hr. Specimens from the embrittled steel were subjected to impact tests, metallographic examination, microhardness, and lattice-parameter measurements. SEVERAL of the steels in the low alloy group are subject to a pronounced decrease in impact energy if held within, or cooled slowly through, a range of temperatures below the lower critical. This phenomenon, known as temper embrittlement, is quite pronounced in the chromium steels of which AISI 5140 is typical. This study considered the response of one heat of 5140 steel when embrittled isothermally at various temperatures for times as long as 3000 hr. Excellent reviews of the work done in the field of temper embrittlement have been written by Hollomonl and Woodfine.' Both authors list the various theories which have been advanced to explain temper embrittlement. Some of the mechanisms considered were: 1—a transformation below 700°C; 2—an allotropic modification of iron; 3—precipitation from the ferrite of such compounds as carbides, nitrides, phosphides, or chromium oxides; 4—decomposition of retained austenite; 5—modification of special carbides; 6—grain-boundary segregation; and 7—selective distribution of carbides. The present study investigated the changes in hardness, Meyer's number, impact properties, micro-structure, and lattice parameter which occurred on embrittlement. Previous studies considered the influence of microstructure and of prior austenitic grain size3 on the response of 5140 steel to temper embrittlement. Equipment and Procedure All samples were taken from one heat of 5140 steel; the chemical composition of this steel was: 0.43 pct C, 0.86 pct Mn, 0.020 pct P, 0.019 pct S, 0.27 pct Si, 0.84 pct Cr, 0.10 pct Ni, 0.06 pct Mo, 0.10 pct Cu, and the remainder Fe. The material was received as % in. rounds. This stock was cut down to blanks measuring approximately 0.425~0.425~2.196 in. Heat Treatment: The rough blanks were normalized at 1600°F (870°C) for 1 hr, then austenitized at 1600°F (870°C) for 1 1/2 hr, and quenched into an agitated oil bath. The specimens were tempered at 1275°F (690°C) for 5 hr and water quenched. These tempered specimens were designated as the toughened state. Embrittling Treatments: The tempered bars were divided into sets and subjected to the various embrittling treatments listed in Table I. Temperatures from 750" to 1050°F were investigated for times of 1 to 3000 hr. Special tests to determine the effect of heating a short time at a higher temperature after long-time embrittlement at some lower temperature were also conducted. All specimens were water quenched at the end of the embrittling cycle, then ground and notched to obtain standard Charpy V-notch specimens. Impact Tests: The bars were fractured in a 260 ft-lb Charpy impact unit; specimens were fractured at temperatures ranging from —315°F to room temperature. Fixed temperatures used consisted of —315°F with liquid nitrogen, —115°F with dry ice and acetone, and 32°F with ice and water. Intermediate temperatures were obtained by suspending the bars in a jig over the liquid nitrogen, dry ice and acetone, or ice and water.

Jan 1, 1955

By John J. Sense

The Mission unit of the American Smelting and Refining Co., located 20 miles south of Tucson, Ariz., is a high-volume, 15,000 tpd operation which utilizes a relatively light equipment fleet. As such, management is very conscious of the mechanical and operational availability of the equipment in use. One of the key items in attaining this efficiency is a complete and reliable record of mechanical and operational machine availability which is an invaluable guide for: 1) Estimating future equipment and personnel requirements of an operating property. 2) Planning an expansion program of an operating property. 3) Estimating equipment and personnel requirements of a new property. 4) Selection of replacement equipment. 5) Comparison of separate operating properties.

Jan 3, 1964

By Lawrence H. Van Vlack

The energy of the y-iron grain boundary was determined to be 850 ergs per cm2 at 1105°C. The a/a and the a/y boundaries possess somewhat less energy. The microstructures of several iron alloys are discussed in terms of the interfacial energy relationships. THE dependence of the shape of liquid interfaces upon their energies has been studied for some time.1"3 Recently, Smith' concluded that many of the microstructures observed in metals may be attributed to the energies of the interfaces between the grains and phases. While the energies of liquid surfaces have been measured by numerous different methods: only two attempts have been made to determine experimentally the energy of surfaces involving crystalline solids. Udin, Shaler, and Wulff8 used a procedure introduced by Berggren7 to measure the surface tension of solid copper. It consisted of determining the load required on a thin copper wire so that the surface tension was counteracted, and no net strain resulted. Bailey and Watkins8 sed a different technique and were able to determine both the surface tension of copper and the tension of the copper grain boundary. They measured the contact angle which liquid lead makes against a copper surface. They then calculated the above energies from the surface energy of liquid lead by using the Pb vs. Cu/CuY dihedral angle and the surface groove angle formed during thermal etching. They obtained a value of 1800 dynes per cm for the surface tension of clean copper and approximately 640 dynes per cm for the tension of copper grain boundaries. The former value was somewhat higher than Udin's value of 1500 dynes per cm. This paper includes a determination of the energy of the y-iron grain boundary. In addition, the micro-structural relationships of several other metallic and nonmetallic phases with iron were examined and an attempt was made to interpret the observed structures in terms of interfacial energy relationships. Theoretical Considerations In a three-phase material containing a solid and two liquids, there may be two solid/liquid interfaces, one liquid/liquid interface and one inter- granular interface. Liquid/liquid interfacial energies can be measured directly. Therefore, by determining the energy of such an interface and by measuring the required interfacial angles: the energies of the interfaces involving solids may be obtained.10 They may be shown schematically as in Fig. 1. The above procedure requires the following assumptions: 1—The interfacial energies are, in general, unaffected by boundary orientation, and 2— the shapes of the interfaces are unaltered between annealing and sectioning for microscopic examination. The first assumption is good to a first approximation as shown by Dunn and Lionetti11 except for a few critically orientated boundaries. Two conditions may alter the shape of a boundary upon cooling: 1—Precipitation of dissolved material upon one side of the interface, and 2—a change in volume during the transition from one phase modification to another. The former must be detected by microscopic observation. The latter may become appreciable in systems containing an interface between two liquids which solidify after annealing. However, possible movement of the two-liquid interface may be checked in the system diagrammed in Fig. 1 by measuring 8, for example, and comparing it with its value as calculated from the other interfacial angles by: tan8, C11 05 COS- o- + cos 8, cos- The choice of a suitable pair of liquids is limited by several factors. The relative values of the several

Jan 1, 1952

By C. S. Witherell

THE first feature that strikes one when considering the use of air enriched with oxygen in pyrochemical processes is the conservation of Enriched Air FIG. 1.-TEMPERATURES THEORETICALLY OBTAINABLE BY BURNING PURE AMOR¬PHOUS CARBON IN AN ATMOSPHERE COMPOSED OF AIR ENRICHED WITH OXYGEN, PRODUCING GAS CONTAINING CO. heat due to the partial elimination of the inert heat-carrier nitrogen, as set forth in the report of the committee. The second feature, which

Jan 11, 1924

By L. C. Brown, J. S. Kirkaldy

AS part of a program to investigate the diffusive properties of dilute ternary austenites, we have made a determination of the effects of cobalt on the activity of carbon in y iron. Samples of pure iron and Fe-Co alloys were equilibrated at 1000°C in controlled CO-C02 atmospheres, following the procedure of R. P. smith.' The 0.010-in.-thick samples were analyzed for carbon by microcombustion analysis2 to give a set of isoactivity curves. The latter were converted to activity-coefficient (standard state at infinite dilution) plots by combination with Smith's data' for the activity of carbon in pure iron measured in a CO-C02 mixture. Table I shows the composition of the base alloys used, while Fig. 1 shows the experimental results superimposed on a set of curves generated by the relation In the notation of Wagner,' the interaction parameter is the second coefficient on the right, Eq. [I] adequately correlates the experimental points for those alloys which were prepared from electrolytic iron by arc-melting (2,4, and 7 pct Co). The results for the 10 pct Co alloy (supplied by Crucible Steel Co.) do not correlate with the others. In fact, the experimental points for this alloy correspond to an interaction parameter of It is possible that the interaction parameter is a function of concentration for large cobalt additions, but we are inclined to attribute the discrepancy to the presence of a significant amount of aluminum added to this alloy for deoxidation purposes (Table I). Preliminary measurements for the system Fe-C-A1 have indicated an interaction parameter of Which implies that the effect of aluminum in solution on the carbon activity is sixty times greater than the effect of an equal weight percentage of cobalt. These observations cast some doubt on the precision of the results of Chandhok, Hirth, and Dulis who used this same 10 pct alloy for their experiments, obtaining an interaction parameter of E = 2.2. There is considerable doubt as to the activity of a plane Fe-C system. Using a CH4-Ha mixture, Smith obtains cg = 6.1 for the effect of carbon on the activity of carbon in austenite, rather than the value of 8.9 given in Eq. [I]. The use of CHa-Ha mixtures has recently been questioned by Kaufman, Radcliff, and cohens who state that there is some possibility that other hydrocarbons are formed. Fortunately, the determination of the interaction parameter is not sensitive to the coefficient of Nc. For example, using the CHI-H2 results we obtain a value which is almost the same as that obtained using the CO-CO, results. The authors wish to thank Mr. E. J. Dulis of the Crucible Steel Co. of America for supplying us with samples of the 10 pct Co alloy used in their original work. Financial assistance from the American Iron and Steel Institute is gratefully acknowledged.

Jan 1, 1963

By R. S. Rickard

Chemical processing of ores has gained new im¬petus in recent years. The reasons are many. They range from the need to process ores that are difficult to beneficiate to the avoidance of pollution. Although many think of chemical processing as a hydrometallurgical operation there are other techniques. An example is chlorination. Chlorination, although examined and discarded by many investigators, is again being considered as a means of extracting uranium1, treatment of silver-lead ores2, and the recovery of base metals from pyrite cinder and ores3. Segregation roasting of copper and nickel ores, a process similar to chlorination, is another chemical treatment being revived.

Jan 1, 1970

By M. C. Fuerstenau, A. M. Gaudin

A homogeneous suspension is viewed by X-rays. The radiation density seen, affords a measure of the extra absorption due to the solids contained. This radiation density, at a predetermined depth, varies with time. The chart of this relationship gives the desired determination. s it is frequently necessary to know the distribu-rt tion of particle sizes in various products used in industrial applications, a number of means have been devised for these determinations. Some of them include direct microscopic measurement, screening of product, extraction of samples from a settling slurry, air and liquid elutriation, adsorption of gases and liquids, and light absorption. The absorption of light as a means for particle size analysis has been known and employed for some time. X-ray absorption has not received the attention that light has enjoyed primarily because of the complex and costly instrumentation involved with X-rays. In 1954, Brown and Skrebowskil suggested the use of X-rays for this type of determination but did not supplement their suggestion with experiment. In 1958, the authors conducted size analysis experiments on suspensions of quartz with the Trans-viewer: an X-ray unit specifically adapted for sedimentation research, and Rossa conducted experiments in a similar manner in 1959 with a stable gamma emitter, AmZ4l, on suspensions of uranium oxide. To illustrate the applicability of X-ray absorption for analyzing particle size distributions, an essentially mono-energetic and well collimated X-ray beam was used as a source. The beam was made mono-energetic by placing a zirconium filter before the counting window together with feeding the pulses from the proportional counter into a reverter, a device capable of discriminating against pulses of various heights. The sketch in Fig. 1 shows the collimation arrangement in more detail. As shown, the X-ray beam was collimated by inserting a 3/8-in. ID pipe into one of the ports of the X-ray tube and further by two small steel plates with slits 3/32-in. wide and 1/2-in. long placed in front of the window of the Geiger-Mueller (G-M) tube. One of the plates was located 1/2 in. and the other 2 1/2 in. from the window of the counter; both plates were contained in an aluminum holder mounted on the box containing the G-M tube. This type and degree of collimation should eliminate any intensity due to scattered radiation; the transmitted intensity would then be solely a functior. of the absorption by the suspension at that level. Experimentally, homogeneous suspensions of finely ground quartz were prepared, Daxad (a sulfo-nated compound made from wood) was added as dis-persant, and the transmitted X-ray intensity measured as a function of time at a fixed depth in the suspension. In more detail, the experimental procedure involved the following: 1) measuring the transmitted X-ray intensity through the Daxad solution at a predetermined position or settling depth in the absence of solids, 2) placing a known amount of dry solids into the vessel and agitating thoroughly, 3) measuring the transmitted X-ray intensity at time zero (i.e., immediately upon cessation of stirring), and 4) measuring the transmitted X-ray intensity as a function of time (a 10-sec counting interval being chosen and counting being started 5 sec before the desired time). Since a linear relationship exists between percentage solid in a slurry and the logarithm of transmitted intensity for a homogeneous material, the cumu-

Jan 1, 1961

By J. C. Scully, G. Sanderson

The electrolytic formation of y hydride in thin foils of Ti-5Al-Z.5Sn alloy and four Ti-A1 binary alloys has been studied by electron microscopy and electron diffraction. Two orientation relationships have been found: THE adsorption of hydrogen by titanium alloys from aqueous solutions has been widely reported. This can occur, for example, in both alkaline' and acidic2 pickling baths, in chemical polishing374 and electro-polishing Solutions,3,4 during cathodic polarization5" and under certain corrosion conditions,7,8 Etching reagents may also produce visible precipitates, sometimes after an aging period.9 During an investigation into the stress corrosion susceptibility of a titanium alloys by thin foil electron microscopy many observations have been made of hydride precipitation which has been deliberately promoted by techniques that are described below. The characteristics of hydride precipitation are reported and the observed crystallographic orientation relationships are discussed with reference to distortion in the titanium lattice created by the presence of the hydride. EXPERIMENTAL TECHNIQUE One grade of commercial titanium and five alloys were examined. Their composition and hardness values are shown in Table I. All the materials were in the form of thin sheet, 0.05 to 0.065 cm thick, which had been annealed after cold rolling. Foils suitable for transmission electron microscopy were made in two ways: a) by chemical polishing; and b) by elec-tropolishing. The solution used for chemical polishing was a mixture of 44 pct HF and 73 pct HNO3 in the volumetric ratio 2:3. During this polishing specimens were manually moved up and down in the solution. The reaction was veFy rapid, specimens thinning to foil thickness (2000A) in 5 min. Since chemical polishing solutions tend not to cause hydride contamination if they are kept cool3 no attempt was made to prevent the solution from becoming hot during the thinning operation. Electropolishing was performed at -30° C with a mixture3 composed of 295 cu cm methyl alcohol, 175 cu cm n-butyl alcohol, and 30 cu cm perchloric acid with an applied voltage of 40 v after chemically thinning specimens to approximately 0.017 cm thickness in a cool solution of 44 pct HF, 40 vol H2O2, and water in the volumetric ratio 1:6:3. EXPERIMENTAL RESULTS 1) Ti-5A1-2.5Sn Alloy. The Ti-5A1-2.5Sn alloy was severely contaminated by hydrogen during the chemical polishing. Foils obtained in this way contained large amounts of the y hydride phase. A typical micrograph is shown in Fig. l. The laths were identified as the hydride phase by selected-area diffraction of a large number of foils examined in a tilting stage that could be turned through 40 deg. Using the lattice spac-ings of the alloy obtained by X-ray diffraction as a standard the a value of the hydride was determined fromo the electron diffraction patterns to be 4.38 to 4.40A. The accuracy of this figure is only about ±2 pct. Further evidence of the identification was obtained by vacuum annealing chemically polished foils of the alloy at 500°C. This resulted in the dissociation of the hydride with the production of dislocations and possibly vacancy loops as shown in Fig. 2. The hydride

Jan 1, 1968

By John A. S. Dow, Garry G. Lowder

Tapadaa is one of several centers of porphyry copper mineralization in northern Sulawesi. Host rocks are mainly varieties of quartz diorite porphyry. Structural control of mineralization is indicated by elongation of the sulfide system (5 x 1 km) parallel to prominent NW-trending structures, but in detail mineralization is strongly influenced by relative age and lithology. Hydrothermal alteration is characterized by widespread occurrence of advanced argillic assemblages and the presence of sodic rather than potassic alkali feldspar. Propylitic alteration surrounds the mineralized area. Phyllic and advanced argillic alteration occur in structurally controlled zones and in limited pervasive areas. Hypogene copper mineralization develops in rocks with sericite-albite alteration and comprises low total sulfide chalcopyrite-bornite or chalcopyrite-pyrite.

Jan 1, 1978

By Stephen D. Antolovich

RECENTLY, much interest has been generated in materials that undergo martensitic phase transformations on straining.')' While it is undoubtedly true that a large amount of ductility can be obtained at rather high strength levels, the question of the general way in which the phase transformation affects the plane strai fracture toughness, as measured by the parameter KIC, has yet to be answered. Let us consider a material that contains a sharp crack as shown in Fig. 1, and is subjected to a tensile stress 00. It is known that the presence of a crack tends to multiply the stress in the area of the crack according to the following equations:3

Jan 1, 1969

By C. G. Dunn, F. W. Daniels, M. J. Bolton

IN recent investigations1. a data on relative grain boundary energies in silicon iron have been obtained. The present investigation is a continuation of this work along similar lines for the purpose of obtaining additional information on boundary energies. One aim has been to extend the data for a (110) series, which was formerly studied,' to small differences in orientation, since a recent theory3,4 based on a dislocation model of grain boundaries predicts a E. ? (A-ln ? )* form of energy curve for small differences in orientation. Another aim has been to provide data for a (100) series—all grains having (100) planes parallel with the surface of sheet speci-mens—and to compare the results with the predicted form of energy curve. Finally, information on the nature of approach to equilibrium conditions was to be obtained through observations on the movements of grain boundaries. Recently published papers2,3,5 have treated the mathematical problem of expressing equilibrium conditions for grain boundaries for the general case when boundary energy depends upon boundary orientation. The equilibrium equations, which relate equilibrium angles and grain boundary -free energies, contain additional terms that express the variation of energy with boundary rotation. It has been necessary in the present investigation, however, to neglect these additional terms since no data for their evaluation were available. Dropping the additional terms leads to the following approximate equations which were used: E12/sin ?3 = E18/sin?2 =E28/sin?1 or those of the form: E28 + E13 cos ?3 + E12 cos ?2 = 0 Experimental Procedure Except for sample F1, all specimens were made from two lots of silicon iron called C and L respectively. The compositions of these are listed in table I. In the preparation of 12 three-grain specimens for the present investigation, a controlled grain growth technique, which has been described previously,' was used. After preparation, the specimens were notched at the boundaries to shorten them as a means of providing more rapid approach to equilibrium in the anneals. Initial grain boundary angles were determined from micrographs taken at X500. Seven anneals, totaling about two days at 1300°C and two to four days at 1400°C, were run in an atmosphere of pure dry argon as described in a previous paper.' Boundary changes generally could be followed without metallographic surface preparation, because thermal etching occurred during the anneals. These observations indicated angle changes of as much as 35" in some instances, with the major changes occurring during the first anneal. Annealing was discontinued when the angles reached stationary values. Fig. 1 gives a schematic diagram for purposes of defining crystallographic and boundary directions for three grains with common plane parallel with the sheet. Differences in orientations (expressed by A) are the angles between [00l] directions. They can be calculated with the aid of the ?'s. The grain boundary angles can be calculated from the w'S. Results Results are given in table 11. Types of crystal-lographic planes refer to those parallel with the sheet. Orientations are given in terms of [00l] direc-tions as shown in fig. 1. Except for grain 3 of specimen H6, which was unintentionally tilted 7" out of a (100) plane, all grains generally were within 1" or 2" of the plane specified. The directions of boundaries were measured generally to within 1" on both upper and lower surfaces, and the average direc- tions were determined for use in calculating the grain boundary angles. Variations in grain boundary directions refer to deviations from average directions. Boundaries near the junction point for all specimens generally were very close to perpendicu-

Jan 1, 1951

By N. J. Grant, B. C. Giessen, M. Morris

The slvuclures of alloys in the system In-Bi have been investigated after (levy vapid queuching from the mell (splat cooling) to -190°C. Tuo-phase fields could be suppressed over most of the tota1 concentvalion range; five melastable phases a1, a2, ?, ?1. and ß exisl, of which four have simple elementtike structures. For example, ß has the A5 struclure of white till. Crystal-tographic data and coordination numbers for these phases aye given, as well as addilional information on the equilibrium diagram, where a new phase In5Bi3 teas found. THE phase diagrams of binary combinations of B elements from the groups B2, B3, B4, and B5 are usually of a simple type and show considerably fewer intermediate phases than combinations of these elements with A metals, transition metals, or the B1 noble metals. Aside from phases such as the typical B3-B5 compounds with the ZnS-B3 structure type, few stoichiometric phases are known; among them are In2Bi and 1nBi.l Nonstoichiometric phases include ß (In-Sn), a1, (In-Pb), and the tin-rich ? phases in the In-Sn, Cd-Sn, and Hg-Sn systems.' The first two phases have a close relationship to indium, while the latter group are known to be structurally related to a Sn. Thus, there are generally no immediate experimental data for the correlation of the crystal structures of B metals and B metal combinations with certain monotonously varying parameters, such as the valence electron concentration (VEC), or the average atomic size. Such parameters have been recognized as structure determining, e.g., for the transition 4 Sn — y phase,2,3 where nonintegral valence electron concentrations are encountered. It should be possible to extend such correlations to other binary systems, if nonequilibrium single-phase alloys could be produced over broad valence electron concentration ranges, and if their crystal structures could be regarded as being imposed by their electronic states. It has been shown in the case of the tin-rich 7 phases3 that alloy phases with typical crystal structures can be produced in B metal alloys rapidly quenched from the liquid to -190°C by the splat cooling technique due to Duwez,3-8 and reviewed in Refs. 5 and 6. The In-Bi system was selected because it extends over a valence electron concentration range in which several metastable, nonstoichiometrir phases could be expected to occur. Further, the low melting points of the known intermediate phases, In2Bi and InBi, Fig. 1(a), indicated low binding energies and thus possibly low driving forces for the formation Of the equilibrium structures. EXPERIMENTAL TECHNIQUES AND RESULTS The preparation of the quenched foils followed the practice described in Ref. 3. Master alloys were produced by melting of indium (99.97+) and bismuth (99.99+) in evacuated Vycor capsules or in an inert gas arc furnace; quantities of 20 mg were splat-cooled onto copper and silver substrates held at - 190°C; and crystal structures and lattice parameters were determined on a GE XRD-5 diffractometer using Cu Ka, radiation at -190°C and at room temperature. The duplication of each run with both substrates permitted the elimination of overlap of the substrate diffraction pattern and that of the investigated substance. The XRD patterns were usually taken from sin2 " = 0.03 to 0.35; the substrate was used as a means of internal calibration. The fractional accuracy of the lattice parameters of metastable phases is approximately 10-3 In the following, all percentages are in atomic percent. The stable and metastable phases found after rapid quenching to -190°C are listed in Table I, together with estimated concentration ranges and crystallographic data. The investigated alloys and phases present in them are given in Table 11. Except for the region between indium with 33 and 50 pct Bi, where a revision of the equilibrium phase diagram became necessary to include a new stoichiometric phase In5Bi3, the diffraction patterns taken after heating to room temperature agreed with those expected from the phase diagram, Fig. l(a). This suggests that the new nonstoichiometric phases are not stable at room temperature, thus following the observations made for the y phases based on tin.3 Results concerning the equilibrium phases In2Bi and In5Bi3 and the revision of the equilibrium phase diagram which is made necessary by the inclusion of In5Bi3 will be treated first. The Crystal Structure of In2Bi. Makarov7 had identified In2Bi as belonging to the AlB2-C32 type ; however, in a later paper the structure was revised.8 In2Bio was found to be of the Ni21n-B8ß type,21 with a = 5.496A, c = 6.57.9A, and N = 6 atoms per unit cell.9 This crystal structure was confirmed in the present work; definite evidence for the doubling of the c axis, as compared to the A1B2-C32 type, and for the proposed order structure, was found in the powder pattern. The observed lattice parameters agree well with those of Ref. 8; those measured at -190°C are given- in Table I. The Crystal Structure of In5Bi3. A new, equilibrium, intermediate phase was identified in slow-cooled, as-cast alloys; it was identified as In5Bi3. The structure has been worked out by Giessen and Grant;" lattice parameters at -190°C are given in Table I. This phase is probably identical with "In3Bi2", produced by vapor deposition techniques, but not recognized as an equilibrium phase by Palatnik et a1.11 After completion of the present work, the existence of In5Bi3 has also been demonstrated by superconductivity measurements on In-Bi alloys.20

Jan 1, 1968

By H. C. Fiedler

The solubility of sulfur in Si-Fe was determined by the metallographic examination of heat-treated and quenched samples. In the absence of manganese, the solubility in 3.1 pct Si-Fe was found to be about 0.010 pct at 1000o C, 0.015 pct at 11000C, and 0.020 pct at 1150°C, which is substatntially less than hitherto reported. Increasing the silicon content was found to decrease the solubility of sulfur, which is consistent with the increase in the activity coefficient of sulfur with increasing silicon content that has been reported for Fe-Si alloys. Manganese additions were studied in alloys containing 3.1 pct Si and between 0.013 and 0.015 pct S. At low manganese levels the solubility product of manganese sulfide was found to be lower than previously reported. THE solubility of sulfur in pure polycrystalline iron has been reported by Rosenquist and Dunicz1 and by Turkdogan et al.2 Samples were equilibrated in atmospheres containing different ratios of H2S/H2. Both groups of investigators found a solubility limit in y iron of 0.013 pct at 1000oC and 0.031 pct at 1200°C. In addition, Rosenquist and Dunicz1 found a solubility limit in a iron of 0.020 pct at 900°C. Ainslie, Hoffman, and seybolt3 found significantly higher sulfur contents in polycrystalline iron samples than in single-crystal samples after heating at 890°C in a sealed tube containing a mixture of powdered iron and FeS made with s35. Whereas the single crystals contained 0.013 and 0.016 pct S (± 0.005 pct), the polycrystalline samples contained between 0.016 and 0.026 pct S. Autoradiographs suggested that the excess sulfur in the polycrystalline samples was due to the segregation of sulfur in solution at grain boundaries. Ainslie and seybolt4 have reported on the solubility of sulfur in 3 pct Si-Fe. Their samples were sealed in capsules containing hydrogen and sufficient sulfur as cobalt sulfide to saturate the sample. After heat treating, the sulfur-rich phase on the surface was removed by abrading, and the sulfur content of the sample was taken as the equilibrium value for that temperature. Before the equilibrating heat treatment, the samples were heated to 1300°C to coarsen the grains. The resulting grain size, which was about 3/18 in. in diam, was considered sufficiently large to preclude a sensible increase in sulfur solubility due to grain boundary segregation. They reported the solubility to be 0.029 pct at 900oC, 0.063 pct at 1000oC, 0.076 pct at 1100°C, 0.122 pct at 1200°C, and 0.098 pct at 1300°C.

Jan 1, 1968

RECEIPTS [Magazine Advertising $ 62,564.83 Magazine Sales 3,591.44 Totalm 66,156.27 Dues, Arrears7,032.88 Dues. Current96,839.74 Dues, New Members6,525.00 Dues, in advance 1,907.02 Initiation Fees7,584.00. Sale of Transactions3,909.03 Sale of Binding7,845.05 Sale of Special Editions 338.20 Sale of Year Book76.20 Sale of Pamphlets1,189.06 Sale of Authors' Reprints867.54 Miscellaneous Receipts62.93 Interest on Bank Balances1,712.89 Interest on General Reserve Fund337.50 Interest on Life Membership Fund557.84 Interest on James Douglas Library Fund....5,491.89 Total Receipts$208,433.04] [ ]

Jan 1, 1925

Magazine Advertising $ 62,564 83 Magazine Sales 3,591 44 Total 66,156 27 Dues, Arrears 7,032 88 Dues, Current 96,839 74 Dues, New Members 6,525 00 Dues, in advance 1,907 02 Initiation Fees 7,584 00 Sale of Transactions 3,909 03 Sale of Binding .. 7,845 05 Sale of Special Editions 338 20 Sale of Year Book 76 20 Sale of Pamphlets 1,189 06 Sale of Authors' Reprints 867 54 Miscellaneous Receipts 62 93 Interest on Bank Balances 1,712 89 Interest on General Reserve Fund 337 50 Interest on Life Membership Fund 557 84 Interest on James Douglas Library Fund 5,491 89 Total Receipts $208,433 04