By J. F. Enrietto

Internal friction measurements were used to determine the effect of manganese on the solubility and precipitation kinetics of nitrogen. Manganese, in concentrations up to 0.75 pct, has little effect on the solubility at temperatures above 250°C. On the other hand, at Concentrations as low as 0.15 pct, manganese inhibits the formation of iron nitrides, especially Fe4N, even though it may not form a precipitnte itself. The precipitation and solubility of carbides and nitrides have been extensively investigated in the pure Fe-C and Fe-N systems.1-3 In recent years, some effort has been ispent in studying the influence of substitutional alloying elements on the behavior of carbon and nitrogen in ferrite.4 -7 In particular Fast, Dijkstra, and Sladek have investigated the effect of 0.5 pct Mn on the internal friction and hardness during the quench aging of Fe-Mn-N alloys.', ' They found that at low temperatures (below 200°C) the presence of 0.5 pct Mn greatly retarded quench aging. For example, after 66 hr at 200°C very little precipitation had taken place in the iron alloyed with manganese, whereas precipitation was complete after a few minutes in a pure Fe-N alloy. The effect of varying the manganese content and the details of the precipitation process were not mentioned in these papers. Fast' postulated that manganese causes a local lowering of the free energy of the lattice with a resulting segregation of nitrogen atoms to these low energy sites. The segregated nitrogen atoms are bound so tightly to the manganese atoms that they cannot form a precipitate. The internal friction measurements of Dijkstra and Sladek tended to confirm the concept of segregation of nitrogen around manganese atoms, and the increase in free energy on transferring a mole of nitrogen atoms from a segregated to a "normal" lattice site was computed to be - 2800 cal. Dijkstra and Sladek9 distinguished between two types of precipitates: ortho, a nitride of appreciably different manganese content than that of the matrix, and para, a nitride with a manganese content essentially that of the matrix. With each type of precipitate a solubility, again designated ortho or para, can be associated. Since the internal friction maximum in alloys which were aged several hours at 600" C dropped almost to zero, Dijkstra and Sladek9 concluded that the ortho solubility must be very low. The effect of temperature on the ortho and para solubilities has no1: been investigated. There are obviously several gaps in our knowledge concerning the influence of manganese on the behavior of nitrogen in a-iron. It was the purpose of the experiments described in this paper to determine the following: 1) The ortho and para solubilities of nitrogen as a function of temperature. 2) The details of the precipitation process at elevated temperatures. 3) The effect of varying the manganese concentration on the above phenomena. EXPERIMENTAL PROCEDURE Internal friction is conveniently employed in studying the precipitation of nitrides and/or carbides from a -iron because it is one of the few parameters, perhaps the only one, which is not affected by the presence of the precipitate itself. For this reason, internal friction techniques were heavily relied upon in the present experiment. A) Preparat of -. All specimens were prepared from electrolytic iron and electrolytic manganese. Alloys containing 0.15, 0.33, 0.65, and 0.75 wt pct Mn were vacuum melted and cast into 25 lb ingots. After being hot rolled to 3/4 in. bars, the ingots were swaged and drawn to 0.030 in. wires. The wires wen? decarburized and denitrided by annealing at 750° C for 17 hr in flowing hydrogen saturated with warer vapor. To obtain a medium grain size, - 0.1 mm, the wires were then heated to 945oC, allowed to soak for 1 hr, furnace cooled to 750°C, and water quenched. Subsequent internal friction measurements showed that this procedure reduced the nitrogen and carbon concentrations of the alloys to less than 0.001 wt pct. The wires were nitrided by sealing them in pyrex capsules containing anhydrous ammonia and annealing them for 24 hr at 580°C, the nitrogen being retained in solid solution by quenching the capsule into water. Immediately after quenching, the wires were stored in liquid nitrogen to prevent any precipitation of nitrides. By varying the pressure of ammonia in the capsule, it was possible to produce any desired nitrogen concentration. B) Internal Friction. The internal Friction measurements were made on a torsional pendulum of the Ke type,'' a frequency OF 1. or 2 cps being used. For

Jan 1, 1962

By P. C. Claspy, P. H. Smakula

The electro-optic coefficients of LiNbO, and KTao.,5Nboe3,O3 (KTN) have been experimentally determined at the HeNe laser wavelengths of 0.6328, 1.15, and 3.39 µ. The coefficients were calculated fronz the retardation induced by an applied electric field. The retardations were measured by observing one or move transmission maxima and minima as a function of the applied field, and by measuring the retardation directly with a Babinet-Soleil compensator. The values obtained agree quite well with those previo~lsly reported by others. Extinction ratios as high as 3000:l have been observed. Resistivities and Curie temperatures have also been measured. Light-induced optical inhornogeneities in LiNbO, repovted by others have been observed. CONSIDERABLE interest has recently been shown in the electro-optic properties of LiNb03 (Refs. 1 and 2) and KTN.3, 4 These crystals have a number of advantages over such well-known materials as KDP. These advantages include: 1) the infrared transmission of KTN and LiNb03 extends to 5 p whereas that of KDP cuts off at 1.5 p ; 2) driving voltages required for modulators using these materials are considerably lower than those required for KDP. After first discussing some theoretical considerations of the electro-optic effect, we will report the results of measurements of the dc electro-optic coefficients of these materials at wavelengths of 0.6328, 1.15, and 3.39 p. THEORY The generalized equation for the electro-optic effect can be written: Although lattice polarization is the fundamental variable, rather than the applied electric field, we follow the convention of expressing the linear electro-optic effect in terms of the applied field. For LiNbO the quadratic terms are negligible. Since KTN has a center of symmetry the rijk tensor is 0. After applying the usual symmetry considerations and index contractions,* the rijk and gijkl tensors can be expressed as follows: LiNbOaT If field directions are now chosen, the change in refractive index and the angle between the induced optic axes and the crystallographic axes can be found. The induced rotations of the principal axes of the index ellipsoid for fields in principal crystallographic directions are given in Table I. Since KTN is initially isotropic, the principal axes in the zero-field condition are parallel to the crystallographic axes. The induced retardations are given in Table 11. EXPERIMENTAL We obtained the various electro-optic coefficients by measuring the induced retardation as a function of

Jan 1, 1968

By Shiro Ban-ya, John Chipman

Using the same experimental method previously described, the activity of sulfur in a number of quaternary and more complex liquid iron alloys at 1550oC is determined. A "cross-product term zj.zk is determined for each of the quaternary alloys to take account of the mutual effects of the combinalion on the indi-vidual contributions to In 5 The interactiotl coefjicienls delermined for ternary solutions and cross-pvoducl coefficierlts from the quaternary systems are used to estimate the activity coefficient of sulfur in more complex alloys. OUR recent papers 1,2 have described new determinations of the activity of sulfur in Fe-S binary and Fe-S-j ternary solutions, but the practical applications of these data require the estimation of activity of sulfur in more complex systems. Previously, Sherman and chipman3 devised an approximate method for calculating the activity of sulfur in complex systems by summing the contributions to the logarithm of the activity coefficient of each element in the alloy. This procedure is more successful, as one of us has pointed out,4 when the concentration variable is taken as zs = ns/(nFe — nS t CLJ~ nj) rather than the conventional atom fraction x~ = nS/(nF, + nS + Enj). In the former definition, which is based on analogy to interstitial solutions, the value assigned to uj is normally +1 for metallic and -1 for nonmetallic elements." In addition, however, the effects of mutual interaction between alloying elements must be considered for the accurate estimation of the activity of sulfur in more complex systems. The purpose of this investigation has been to devise a more reliable method for estimating the activity coefficient of sulfur in nmIticomponent iron alloys. The measurements were carried out on some quaternary systems Fe-S-j-k for combinations of silicon, chromium, nickel, cobalt, molybdenum, and tungsten. Manganese was not included since the experimental method has been found unsatisfactory for volatile, sulfide-forming elements. The experimental method was the same in every detail as described previously. 1,2 The concentrations of sulfur, silicon, chromium, and copper in the quenched metals were determined by chemical analysis but those of nickel, cobalt, molybdenum, and tungsten were calculated from charged amounts. Iron sulfide was included in the charges in amounts estimated to furnish approximately the final sulfur content. CALCULATION W2 have shown2 that when zs and zj are the concentration variables in a ternary Fe-S-j solution the logarithm of the activity coefficient S = a~/zg is a linear function of the variables as and aj defined as follows:

Jan 1, 1970

By W. R. McMillan, E. A. Gulbransen, K. F. Andrew

Annealed and electrolytically polished pure iron was oxidized between 650° and 850°C at oxygen pressures of 0.1 to 2 microns Hg. Electron optical studies showed that oxidation occurs discontinuously over the surface and orients crystallographically with the substructure of the metal grains. IN previous papers', " the authors described the formation of oxide films on high purity iron at norrnal pressures and at temperatures below 300°C. Electron optical studies showed that the oxide film consisted of many individual oxide crystallites having nearly random orientation on each metal grain. The size of the oxide crystallites depended upon the temperature and upon the extent of oxidation. In these studies the crystallite size varied from 250 to 1800Å. Recently, Bardolle and Benard3 studied the crystal habit of the oxide crystallites formed on Armco iron between 650" and 850°C in what might be defined as a "poor vacuum" atmosphere in which the pressure could be varied between 10-1 to 10-3 mm of Hg. Their results showed that, at 850°C and a vacuum of l0-2 to 10-3 mm of Hg, a few well oriented nuclei of oxide were formed on the metal grains. At pressures between l0-1 to 10-2 mm of Hg, many oriented nuclei of oxide were formed. At 750°C the metal surface was bright although an oxide was present. Unfortunately, the extent of oxidation, the oxygen pressure, and the influence of carbon in the metal were not determined, and it was, therefore, impossible to give a theoretical interpretation to the very beautiful light micrographs. Bardolle and Benard used the light microscope to determine the crystal habit of the oxide and X-ray diffraction to determine the orientation relationships. It was believed that the use of controlled amounts of oxidation at high temperature is an important method for the study of the initial stages of oxidation of metals at high temperatures. This paper presents the first results of an electron optical study of this problem for iron. Since the electron microscope and electron-diffraction methods using stripped oxide films and surface replicas yielded finer details of the crystal habit and structure of oxide film, these methods were used in this study. Two types of iron having different carbon contents were used: Puron and Armco* iron. A com- parison of the results for these materials made possible a study of the influence of the surface oxide-carbon reaction on the initial stages of oxidation. Before discussing the experimental results, the thermodynamic equilibria of 1—the oxidation reaction, 2—the surface oxide-carbon reaction, and 3—the solubility of oxygen in iron, will be considered. In addition, it is important to consider the kinetic-theory predictions on the rate of collision of oxygen with the iron surface. Thermodynamic and Kinetic-Theory Calculations Only one type of reaction is usually considered in the oxidation of iron at normal pressures at high temperatures: Fe(a) + 1/2O2(g) = FeO(s) 3Fe(a) + 2O2(g) = Fe3O4(s) 2Fe(a) +3/2O2(g) = a-Fe2O3(s). [11 However, two other reactions may occur: FeO(s) + C (solid solution in Fe) + Fe(a) + CO(g) [2] and Fe(a) + O2(g) e Fe(a) (solid solution of 0,). [ 3 ] In addition, iron will react with the higher oxide at certain temperatures to form FeO. For a complete interpretation of the oxidation of iron at low pres-

Jan 1, 1955

By K. H. Hiller

A rotational viscometer has been designed which perrnits the measurement of the rheological properties of drilling muds and other non-Newtonian fluids under conditions equivalent to those in a deep borehole (350F, 10,000 psi). The important mechanical features of this instrument are described, and its design criteria are discussed. The flow equations for the novel configuration of the viscometer are derived and the calibration procedures are described. The data and their interpretation, resulting from measurement of the flow properties and static gel strengths of homoionic montmorillonite suspensiom at high temperatures and pressures, are presented. Data are also presented for the flow behavier of typical drilling fluids at high temperatures and pressures. The pressure losses in the drill pipe and the annulus depend critically upon the flow parameters of the drilling fluid. This work demonstrates the need to measure these parameters under bottom-hole conditions in order to obtain a reliable estimate of the pressure losses in the mud system. INTRODUCTION The rheological properties of drilling fluids are affected by temperature and pressure, but the extent of these effects on the dynamic flow properties is not well known. Measurements of changes of the flow properties of clay-water drilling muds with temperature have been reported by Srini-Vasan and Gatlin.1 The temperatures reported did not exceed 200F, a limitation imposed by the apparatus used by these authors. The rheological properties of clay suspensions were measured at temperatures up to 100C by Gurdzhinian.' Neither the nature of the exchange ions in the clay suspensions nor the degree of purity were defined in his work, nor were the measurements extended to currently used drilling fluids. The lack of systematic measurements of dynamic flow properties at high temperatures and pressures seems the more surprising since during the last decade the importance of the control of the hydraulic properties of drilling fluids has come to be widely recognized. Very good mathematical treatments of the friction losses in drill pipe and annulus have been developed.3 4 These treatments are based on the assumption that drilling fluids behave as Bingham plastic fluids. Quite often this assumption is justified, while in other cases a power law equation pro- duces better fit than the Bingham model does. For convenience in applying viscometer data to pressure-drop calculations, the Bingham plastic flow equation is preferable and, therefore, has been applied to the data reported in this paper, although other equations may fit these data more accurately. In a Bingham plastic fluid the relationship between the shearing stress 7 and the rate of shear D is given by the following equation: where is the plastic viscosity and 4 the yield point. If 4 = 0, the equation for simple Newtonian flow, 7 = pD, is obtained. Two empirical constants are required for the description of laminar flow of a Bingham plastic fluid, and calculations of the flow behavior at high temperatures and pressures cannot be better than is permitted by the accuracy with which these constants are known. For this reason a high-pressure, high-temperature rhe-ometer has been designed to measure the plastic viscosity the yield point +, and the static gel strength S, at pressures up to 10,000 psi and temperatures up to 350F. The important features of its design will be described. The results of measurements on homoionic clay slurries will be discussed insofar as they are relevant to an understanding of the general flow behavior of clay-water drilling fluids. The results of measurements on some typical drilling fluids will be presented also, and their practical implications will be briefly discussed. DESCRIPTION OF EQUIPMENT MECHANICAL FEATURES A viscometer designed to measure the plastic viscosity, yield point and gel strength of non-Newtonian fluids must permit the measurement of the shearing stress t at any given rate of shear D. This is possible only if t and D are approximately uniform throughout the entire sheared sample. A Couette apparatus is the most convenient method of realizing this condition, as has been pointed out by Grodde." The "high-pressure, high-temperature rheometer" described in this paper is basically a rotational Couette viscometer that is immersed in a cell in which pressure and temperature can be controlled over the range of interest. Fig. 1 shows schematically the important features of the pressure cell and associated equipment. The heart of the instrument is the rotating cup. It is shown more clearly in Fie. 2. which revresents the lower one-third of the pressure cell (below the input drive shaft shown in Fig. 1), and it is shown in detail in Fig. 3. For measurements of dynamic flow properties, the rotating cup is driven by a 1/2-hp electric motor, which operates through a Vickers

On August 4, 1844, J. C. Fremont made the first record found of coal in Wyoming. On the North Fork of the Platte River, beyond Medicine Butte, in Carbon County, he noted: "in the precipitous bluffs were displayed a succession of strata containing fossil, vegetable remains, and several beds of coal. In some of the beds, the coal did not appear to be perfectly mineralized; and in some of the seams, it was compact and remarkably lustrous." A little later he noted, "longitude 111°, latitude 4 1/2°-Muddy R.--coal."1 In 1848, Clayton reported coal on Sulphur Creek near the site of old Bear River City, in Uinta County.2 Maj. Osborne Cross in his journal, on July 1, 1849, records seeing coal on Deer Creek and in one of the hills near Crooked Muddy Creek, in Converse County; on July 7, he records that the country from Deer Creek to the Sweetwater River abounds in coal, probably in Natrona and Carbon Counties.3 A letter from Asst. Quartermaster Van Vliet to General Jessup dated July 25, 1850, asked an appropriation for building shops at Fort Laramie for making repairs for the emigrants, and mentions "coal and timber," but undoubtedly meant charcoal, as no other mention of stone coal is made in the records of the fort.4 Stansbury, in 1852, placed on his map of this section the words: "Great Coal Basin," extending from the west bank of Bear River, near the present Evanston, to Point of Rocks in Sweetwater County. In 1859, a military coal reservation was established near here, but the coal was never worked to any great extent, although probably some was hauled to Fort Bridger for smithing purposes. When the fort was abandoned this reservation returned to the public lands .2 In the same year (1859), Hayden traced the lignite formation uninterruptedly from the upper Missouri Valley to a point on the North Platte River, about 80 miles northwest of Fort Laramie.5 On August 25, 1865,

Jan 1, 1942

By W. Bonfield

The microstrain characteristics of a polycrystal-line Cu 1.9 wt pet Be precipitation-hardening alloy have been determined for various conditions of aging. The friction stress remained constant for all the conditions investigated, whereas the microscopic yield stress (the stress to produce a plastic strain of 2 x 10-8 in. per in.) and the three-stage stress-strain curve in the microstrain region were sensitive to changes in dislocation and precipitate distribution. Correlations between the measurements of microplasticity and electron-nzicroscope observations of substructure are considered. ALTHOUGH the macroscopic mechanical properties of Cu 1.5 to 2.0 wt pet Be precipitation-harden ing alloys were established' in some detail, there has been no previous investigation of the nature of microyield-ing in these alloys. This paper describes a high-sensitivity extensometer determination of microplasticity in polycrystalline Cu 1.9 wt pet Be, in which the friction stress, the microscopic yield stress (the stress to produce a plastic strain of 2 x 10-6 in. per in.), and the rate of strain hardening in the micro-strain region were measured for various conditions of precipitation. The structural changes accompanying aging in this alloy were examined using transmission electron microscopy, a study which differed from previous investigations as, in order to minimize grain boundary precipitation effects,' the solution-treated alloy was cold-rolled to 40 pet reduction prior to aging. Hence the extent of recovery and recrystalliza-tion, as well as the variation of precipitate morphology and distribution, were assessed. From these results possible correlations between the microstrain characteristics and the observed precipitate and dislocation structure are considered. EXPERIMENTAL PROCEDURE The material investigated was a commercial copper beryllium alloy (Berylco 25), which had a com- position of 1.9 wt pet Be and 0.2 wt pet Co. The alloy was solution-treated at 800°C, quenched in water, and then cold-rolled to 40 pct reduction. Tensile specimens of gage length 1 in. and rectangular cross section of 0.18 by 0.06 in. were prepared from the solution-treated, cold-rolled material and aged for 15 min, 2, 24, and 100 hr at 315°C and 24 hr at 425°C to produce a range of precipitate structure. The hardness values associated with these conditions are listed in Table I. It can be seen that a maximum value is obtained after 2 hr at 315oC, which decreases with continued time at temperature to a minimum after 24 hr at 425°C. For comparison some as-solution-treated specimens were also aged for 2 hr at 315°C. The specimens heat-treated to a given condition were examined in two ways. First, the nature and distribution of the precipitate and dislocation structure was characterized using transmission electron microscopy. Thin foils were obtained from the specimens by electrolytic polishing in a 30 pet nitric acid-alcohol solution at -20oC, and were examined in an RCA EMU 3 electron microscope. Second, the mi-croplastic behavior of the specimens was measured with a Tuckerman strain gage, using the load-unload technique previously described2, 3 to determine the friction stress, the microscopic yield stress, and the variation of plastic microstrain with stress. RESULTS 1) Structural Changes During Aging. a) Annealing Processes. The solution-treated, cold-rolled Cu 1.9 wt pet Be had an irregular dislocation-cell structure,

Jan 1, 1968

By A. D. Rovig, T. J. Fisher

By converting its autogenous mills to steel ball mills at the C. E. Weed concentrator in Butte, Mont., The Anaconda Co. has achieved substantial increases in through- put tonnage, plus better recoveries as a result of the finer feed size to subsequent flotation operations. If steel grinding is so superior to autogenous grinding, why wasn't it chosen in the first place? Briefly, here's why:

Jan 10, 1975

By D. G. Russell

Two techniques have been developed with which the applicability of pressure build-up analyses can be extended to include pressure data which previously have been considered virtually unusable. One of the interpretation methods makes possible the analysis of pressure build-up performance during the wellbore fill-up or after production period which occurs soon after a well is closed in. The other technique is an extension of a method for analyzing pressure build-up performance during the late-time portion of the pressure build-up which occurs after boundary eflects first begin to alter the shape of a conventional pressure build-up curve. With both of these methods it is possible to obtain estitnates of the kh product, the skin factor and the reservoir pressure. In addition, with the late-time analysis technique it is possible to obtain an estimate of the contributory drainage volume of the well being tested. This means that in some cases a check on reservoir limit test and (or) material-balance calculations can now be obtained from pressure build-ups. Both methods are slightly more time-consuming than conventional pressure build-up analysis methods because trial-and-error plots of pressure data must be made. The late-time method for analysis of pressure build-ups is in principle applicable to the late-time portion of a two-rate flow test or a pressure drawdown test. The interpretation formulas and procedures for these types of tests are also outlined. In these cases, as with pressure build-ups, it is significant that an estimate of the contributory pore volume is also obtained. On the basis of limited experience with the new techniques, it appears that satisfactory estimates of the kh product, skin factor, reservoir pressure and, for late-time analysis, contributory drainage volume can be obtained. INTRODUCTION The analysis of bottom-hole pressure build-up behavior in closed-in wells has been a a subject of interest in petroleum engineering circles for many years. In fact, few other subjects have received as much attention as pressure buildup analysis methods have. The cause for this interest is essentially twofold in nature. First, the pressure behavior of a well can normally be measured with a reasonably high degree of accuracy so that good data for analysis can be obtained. Secondly, over a fairly wide range of operating conditions, valuable information as to the quality of the reservoir rock and completion efficiency of the well can be obtained at a nominal cost. In recent years, numerous papers have been prepared on the effects of various operating conditions and reservoir heterogeneities on pressure buildup behavior. Very little work has been done, however, on extension of pressure build-up analysis methods to those pressure data which are not amenable to analysis by the present methods. The theory upon which the analysis of shut-in bottom-hole pressure build-up data is based is derived from the solution of the radial flow equation for a slightly compressible fluid for constant-rate conditions. It requires that the well be closed in for a sufficient period of time to obtain a clearly defined linear portion on the plot of observed bottom-hole pressure vs log (t + ?t)/ ?t (where At is shut-in time, and t is producing time to the instant of shut-in). From the slope of the plot and other normally obtainable data, the formation permeability, the well damage or skin factor, and the reservoir pressure at infinite shut-in time (if the reservoir were infinite) can be estimated. The successful application of this procedure depends on being able to recognize the straight-line section on the basic pressure build-up plot. The presently used pressure build-up interpretation theory also assumes that a well is closed in at the sand face and that no production into the well occurs after shut-in. In practice, of course, the well is closed in at the surface, and inflow into the well continues until the well fills sufficiently to transmit the effect of closing-in to the formation. This adjustment period is commonly referred to as the "afterproduction" or "fill-up" portion of the pressure build-up. During the period that the well fill-up effect is most pronounced, the basic pressure build-up plot is nonlinear. At later shut-in times after the effects of a drainage boundary have been felt at the well, deviation from the straight-line behavior of the pressure build-up plot also results. In many cases either of these effects or a combination of both can make the straight-line portion on the pressure build-up plot difficult to recognize. Obviously, an extension of pressure build-up analysis methods to include the afterproduction period and the period in which boundary effects are being felt would be desirable and might render valuable pressure data which for years have been considered virtually unusable. The principal reference of note concerning pressure buildup analysis during the afterproduction period is a paper by Gladfelter, Tracy and Wilsey.1 In the approach of these authors it is necessary to measure the rate of influx into the well during the afterproduction period. This is done through sonic measurements or through measurement of tubing-head and casing-head pressures simultaneously with

Jan 1, 1967

By N. A. Gokcen, S. Fujishiro

THE pressures of Mn(g) in equilibrium with Mn7C3 and graphite have been measured by McCabe and Hudson' and Butler, McCabe, and paxton2 by means of graphite, zirconia, and Ta-Mo Knudsen cells. The details of corrections in their measurements were somewhat different from those of the authors;3'4 hence, further independent results at higher temperatures seemed to be warranted. The stoichiom-etry of Mn7C3 in equilibrium with graphite and its stability up to the vicinity of 1373 °K have been satisfactorily established by Kuo and persson5 (See also Hansen and Anderko).' The method of investigation has been described elsewhere in detail.3'4 The carbide was prepared in the manner described by McCabe and Hudson. In order to avoid possible reactions with refractory oxides, only graphite cells were used for the effusion experiments. The authors' results are the runs M-1, M-2 and M-3 listed in Table I, together with those of McCabe and co-workers. The heat capacity, c;, of Mn7C3 is not known; therefore McCable et al. plotted their data as log P vs 1/T and the results were only expressed first' as, and later2 as logP=- -14220+6.06 without further thermodynamic calculations. However, it is possible to estimate closely the necessary heat capacity as follows: When H; - &98 of CrC, or MnO, is plotted vs x, corresponding to various compounds, with temperature as the parameter, it is seen that the relationship is represented by a line of very small curvature. This relationship is also followed by other compounds which do not exhibit solid state phase transformations. In view of the fact that chromium and manganese have the atomic numbers of 24 and 25 respectively, it is reasonable to assume that H; - H;ae vs x for MnC, follows the same type of lines as those for CrC, for which adequate data are available.7 Similar correlations appear to be valid for oxides of two neighboring metals for which reliable data are available. The procedure is thus to move the lines for CrC, vertically (parallel to the axis of HT - H298) until they coincide with the points for MnC1/3, the only carbide of manganese whose H; - HO298 has been

Jan 1, 1963

By T. M. Morris, W. E. Horst

W. E. Horst—In regard to the flotation rate being described as "first orcler" for flotation of quartz particles below 65 p in size (or any size studied in this work) in this paper, it appears that the authors' conception of rate equations is not in agreement with cited references. A first order rate equation has as one of its forms the following: a In.=a/a-x=kt where a = initial concentration, a—x = concentration at time t, t = time, and k = constant. The constant, k, has the dimension of reciprocal time which is similar to the specific flotation rate, Q. described by Eq. 2 in the authors' article, as has been previously discussed by Schumann (Ref. 1 of original article). The plotted data presented in Fig. 4 of the article utilizes the specific flotation rate, Q (min.'); however, there is not adequate data given to indicate the order of the rate equation which describes the flotation behavior of the quartz system studied. Results from the experimental work indicate that the relationship between rate of flotation (grams per minute) and cell concentration (provided the percent solids in the flotation cell is less than 5.2 pct and the particle size is less than 65 p) is described by an equation of the first order (R, = k c+", n being equal to 1 in this size range) and the use of the first order rate equation does not apply. Similarly the relationship for other particle size ranges studied is expressed by equations of the second or third order depending on the magnitude of n. T. M. Morris—The authors are to be commended for the experiments which they performed. As they state in their discussion the concentration of collector ion In solution did change with change in concentration of solids in the flotation cell. Since for a given slze of particle, flotation rate increases with concentration of collector until a maximum is reached, the effect of concentration of particles in their experiments was to vary the concentration of collector ions. A collector concentration which insures maximum supporting angle for all particles eliminates the unequal effect of collector concentration on various sized particles and the effect of size of particles and concentration of particles upon flotation rate could be more clearly assessed. I believe that if the authors had increased the concentration of collector to an amount sufficient to attain a maximum supporting angle for all particles they would find that the specific flotation rate of particles coarser than 65 p would be constant with change in the concentration of solids in the flotation cell, and that a first order rate would apply to the + 65 as well as to the —65 p sizes. It might also be discovered when this change in collector concentration was made that the maximum specific rate constant would be shifted toward a coarser fraction than when starvation quantities of collector are used since this practice favors the fine particles and penalizes the coarse particles. P. L. de Bruyn and H. J. Modi (authors' reply)—The authors wish to thank Professor Morris for his kind remarks and for mentioning the influence of equilibrium collector concentration on flotation rate. With a collector concentration sufficient to insure maximum supporting angle for all particles, a first order rate equation may indeed be found to be generally applicable irrespective of size. Such a concentration would, however, lead to 100 pct recovery of the fine particles and consequently defeat the essential objective of the investigation to derive the maximum information on flotation kinetics. To establish absolutely the validity of any single rate equation for a given size range, the ideal method would be to work with a feed consisting solely of particles of that size range. Use of such a closely sized feed would also eliminate the possibility of the interfering effect of different sizes upon one another. The authors do not believe that increasing the collector concentration would shift the maximum specific flotation rate (Q) towards a coarser fraction. Experimentation showed Q to be independent of solids concentration for all particles up to 65 µ in size, whereas the maximum value of Q was obtained in the range 37 to 10 p. Professor Morris contends that the addition of starvation quantities of collector favors fine particles at the expense of coarse particles, but the reason for this is not entirely clear to the authors. The comments by Mr. W. E. Horst are concerned only with the concept of the term "first order rate equation." According to the usage of this term in chemical kinetics, time is an important variable, as is shown in the equation quoted by Mr. Horst. All the experimental results reported by the authors were obtained under steady state continuous operations when the rate of flotation is independent of time. To be consistent with the common usage of the "first order rate equation," it would be more satisfactory to state that under certain conditions the experimental results show that the relation between flotation rate and pulp density is an equation of the first order.

Jan 1, 1957

By W. W. Yankie, A. T. Chatas

This paper is written as a discussion of the paper, "Buckling of Tubing in Pumping Wells, Its Effects and Means for Controlling It" by Arthur Lubinski and K. A. Blenkarn, which war published in the March, 1957, issue of Journal oP Petroleum Technology. An analogy is drawn between the buckling of tubing in pumping wells and a fiube, fitted with frictionless pistom, linked by an inelastic rod, and which is subject to an internal pressure. A simple derivation shows that the critical internal pressure exerts a hydrostatic force on the pisfon which is close to the Euler load for compression buckling of the same tube. While the results agree with those of Ref. I, the basis of calculations has been changed and clarified. The presence of internal upsets at the pistons is discussed. INTRODUCTION In the Appendix, Lubinski and Blenkarn state that a tube with ends closed by frietionless pistons connected by an inelastic rod (Fig. 1) will behave as a column loaded with a force equal to the tension force in the rod. They note that, while the fluid may not resist a shear force, the moment in every cross section is piston force multiplied by the elastic line deflection (c.f., the loaded column). Since the equations of the elastic lines are similar in the two cases, the solution is carried over from the loaded column. On the contrary it is suggested that while the method of solution remains unchanged from the column case, the actual stress distribution is different, a fact which is taken into account in this note. A simple method of approximating the buckling pressure is given, and their reasoning in our mathematical language is continued. GENERAL EQUATIONS The equation of an elastic line, initially straight in the x direction (Fig. 2), is given by In the case of a loaded column, this may be written: For the pressurized tube it was shown, by analogy with the loaded column, that tion has a solution that, for P, = EI/P, any deflection is stable (a criterion for buckling). An attempt will be made to describe more precisely, the forces acting on the tube, and to analyze the buckling condi,tions. DISCUSSION If the tube assumed a deflected position, the volume between the pistons would increase so that in deflecting, the energy of the fluid would decrease. When the increase in elastic energy of the tube (due to bending) is equal to the decrease of fluid pressure energy, buckling conditions exist. Analyzing the forces on the tube (Fig. 3), two transverse forces, T,, T,, exerted by the pistons, are balanced by a resultant of the pressure elements which are linearly dependent on the local curvature of the elastic line (Fig. 4). Unlike most buckling cases, the forces depend on the shape of the elastic line, a condition that makes a rigorous mathematical treatment difficult. Several approximations may be used to clarify the problem.

By M. E. Wadsworth, A. S. Peck

Infrared spectra disclose that oleic acid will not adsorb on the surface of pure beryl unless the mineral is first activated with HF. The adsorption of oleic acid on HF activated beryl is attributed to the hydrogen bonding of oleic acid monomers to F-surface bridging sites. These sites are formed as a result of the reaction of HF with chemisorbed water or surface hydroxyl. Characteristic infrared spectra of physically adsorbed oleic acid are correlated with flotation at different pH at temperatures of 25°C and 75°C for colloidal and -60-mesh particles. The usual mode of occurrence of the beryllium mineral beryl, Be3A12Si6O18, is in granite pegmatites as pale green, white, or yellow crystals. A dark green gem variety, emerald, may be found in the wall rock of pegmatite veins or in mica schist. The most important beryl deposits in the United States are in the Black Hills District of South Dakota, and several mountain ranges of central and west-central Utah contain potential commercial sources of this mineral. Several papers have been published concerning the flotation of beryl with different conditioning reagents. Kennedy and O'Meara1 reported on the essential use of HF in the flotation of beryl from different ores. The use of calcium hypochlorite to separate HF activated beryl from feldspar after flotation with an amine collector was made by Runke.2 A report on the activation of beryl with different cations using sodium oleate collector was presented by Viswa-nathan and co-workers.3 Flotation of beryl with sulfonate collector and different activating salts was employed by Fuerstenau and Bhappu.4 The role of the surface charge or zeta potential in the flotation of beryl with different collectors and salts was also extensively investigated.5"7 Previous infrared investigations by the authors8 disclosed that the orthosilicate beryllium mineral, phenacite, reacts with oleic acid to form a chemisorbed oleate monolayer on the mineral surface. Thus, chemisorption is the effective mode of adsorption in the phenacite-oleate acid flotation system. In contrast, neither chemisorption or physical adsorption of oleic acid occur on the surface of pure beryl as evidenced in this study. Efforts were subsequently made to determine the mechanism of activation and collector adsorption for HF pretreated beryl. EXPERIMENTAL PROCEDURES Large, white, terminated crystals of beryl were obtained from Madagascar through Ward's Co., Monterey, Calif. The crystals were broken into -60-mesh fragments in a porcelain mortar. Part of this prepared material was ground to a powder with a Fisher Grinder using an agate mortar and pestle. The powder was transferred to a graduated cylinder and mixed with 500 ml of distilled water. After 5 min, the colloidal suspension was separated from the settled particles by decantation and used as a stock for infrared test determinations. Adsorption tests were performed by first transferring 20 ml of colloidal suspension to 50 ml glass centrifuge tubes. The solids were then centrifuged out and the liquid was discarded. Then, the solids were pretreated with one molar HC1 or one molar HF. After 15 min, the solids were again centrifuged out. The mineral solids were washed free of residual acid by repeated centrifuging and water washing operations. Then, 20 ml of distilled water was added to the solids, and the resultant suspension was used for test purposes. In the preparation of mineral for flotation tests, 1.5 g of -60-mesh beryl was deslimed by removing the colloidal fraction by three successive water washes and decantations. Then, the coarse particles were pretreated with either one molar HCl or one molar HF for 15 min. The mineral was next washed free of acid with distilled water, and 20 ml of distilled water was added to the beryl prior to collector conditioning. The conditioning of mineral with collector was performed in 50 ml centrifuge tubes to which either NaOH or HC1 was added for pH modification. One drop (6.0 mg) of U.S.P. reagent grade oleic acid or 2 ml of 0.01 molar sodium oleate was added to the pulp and stirred at about 1500 rpm for 3 min at a

Jan 1, 1968

By Robert A. Rapp

The standard molar free energy of formation of MOO,was determined between 750o to 1050o C in galvanic cell measurements involving the solid electrolyte Zr0.85 Ca0.15 O1.85. Use of the reference electrodes Fe + FexO and Ni + NiO Provided two independent determinations of FoMoo2. The data may be represented by the equation FMoO2 = -137,500 +40.0T(°K) which is in good agreement with previous CO/CO, gas equilibrium measurements of Gleiser and Chipman. The standard molar free energy of formation of molybdenum dioxide has recently been reported over a large range of high temperatures from the calorimetric experiments of King, Weller, and christensen.' Gleiser and chipman2 have also recently determined ?FmoO2 from 926o to 1068oC in CO/CO2 gas equilibrium measurements. Earlier gas equilibrium studies have been made and reviewed by Gokcen.' Over the temperature range studied by Gleiser and Chipman their values for ?FoMoO2 differed from the calorimetric data by about 700 cal. This investigation was undertaken to resolve this difference and thereby establish the two phase mixture of Mo + MOO, as an electrode of well-known oxygen potential for galvanic cell applications at very high temperatures. The galvanic cell technique involving the Zr,.,, Ca,0.15 01.85 solid electrolyte was introduced for the

Jan 1, 1963

By C. A. Meissner

THE following is a further discussion of the paper of James Gayley, " The Application of Dry-Air Blast to the Manufacture of Iron " (Trans., xxxv., 746), with special reference to his sup-plementary paper (Bi-Monthly Bulletin, No. 4, July, 1905, pp. 797 to 819), and. to the paper of J. E. Johnson, Jr., "Notes on the Physical Action of the Blast Furnace " (Bi-Monthly Bulletin, No. 5, September, 1905, pp. 1111 to 1146). Mr. Gayley's paper has been discussed also by E. Windsor Richards, R. W. Raymond, E. H. Saniter, W. J. Foster, H. M. Howe, V. Pendred, B. H. Thwaite, James Gayley and Alexander Pourcel (Trans., xxxv., pp. 1022 to 1042), Joseph W. Richards (Bi-Monthly Bulletin, No. 4, July, 1905, pp. 703 to 718); T. W. Robinson (Bi-Monthly Bulletin, No. 4, July, 1905, pp. 788 to 796) ; C. B. Dudley, R. W. Raymond, J. E. Johnson, Jr., W. F. Mattes, James Gayley, David Baker, John Birkinbine and F. E. Bachman (Bi-Monthly Bulletin, No. 5, September, 1905, pp. 1147 to 1152);.E. de Mille Campbell (Bi-Monthly Bulletin., No. 1, January, 1906, pp. 25 to 50) ; John Birkinbine (Bi-Monthly Bulletin, No. 1, January, 1906, pp. 137, 138). At the Washington meeting of the Institute, May, 1905, a very instructive and interesting paper was presented by Mr. J. E. Johnson, Jr., entitled " Notes on the Physical Action of the Blast Furnace,"' in which reference is made to Mr. Gayley's dry-blast process. A few of Mr. Johnson's conclusions, as summarized in the last pages of his paper, do not appear to me to be in complete accordance with the results obtained at the Isabella furnaces; and I therefore present the following notes which may throw further light on this subject: Mr. Gayley has called attention to the fact that the moisture in the air is an extremely variable and uncertain factor; and

May 1, 1906

By R. B. Moore

IN 1914 the writer and K. L. Kithil announced, through Bulletin 70 of the U. S. Bureau of Mines, that the United States possessed the largest deposits of radium-bearing ore in the world. At that time a small amount of this ore was being, mined and shipped to Europe, and one company was preparing to start the extraction and recovery of radium in this country. The importance of our carnotite deposits in Colorado and Utah up to the publication of Bulletin 70 was not, however, appreciated by anyone.. At that time the total supply of radium in the world was about 10 g., calculated as element, and when I estimated that at least 100 g. of radium element, and probably 200 g., would be produced from our carnotite deposits, there was a considerable amount of skepticism. Up to the present time almost 200 g. have come from this ore, and some writers put this figure a little higher. Uranium ore was found in the copper mines of the Union Minière du Haut-Katanga at Luiswishi in 1913. Later discoveries were made at other places in the Belgian Congo, and the Katanga ores now represent the largest supply of radium-bearing ore in the world. In fact, since 1923 very little radium has been produced from American carnotite, the Katanga ore representing practically the world's supply of. radium since that date.

Jan 1, 1930

By J. O. Edstrom, G. Bitsianes

Parabolic rate constants were determined for the formation of wiistite by the solid state reaction between magnetite and iron. The reaction was diffusion controlled and inert marker studies indicated that the mass transport through the wiistite layer was accomplished by means of iron migration. Relationships between rate constants and self-diffusivities are discussed. The transport capacity for iron through dense wustite layers was found to be sufficient to carry on reduction, even in gaseous reduction processes. REDUCTION of iron oxides has been the subject of many investigations. Most of the work, however, has been done on rather crude material and there have been difficulties in correlating the data on a quantitative basis. The reverse process of the oxidation of iron has been studied more thoroughly and usually by starting from the pure metal. As a result, the mechanisms of oxidation are now fairly well known.It has generally been found that the oxidation of metals follows the so-called parabolic 1aw;Q hat is, when the oxides are formed as dense layers, their thicknesses are proportional to the square root of the reaction time. This parabolic law follows directly from Fick's first law of diffusion The flux, J, is defined as the quantity of diffusing substance passing per unit time through unit area of a plane at right angles to the direction of diffusion. This flux is proportional to the concentration gradient of the diffusing substance, and the factor D, known as the diffusion coefficient, is introduced as the proportionality factor with dimensions of (length)'/time. If the flux is measured as the increase of thickness of the oxide layer (Ax) per unit time (t) and the assumption is made that the concentrations of the reactants at the phase boundaries of the layer are independent of time, Eq. 1 reduces to Integration of this expression yields the parabolic function ax = k . t. [31 The product of the diffusion coefficient and the concentration difference across the oxide layer is included in the constant k. When iron is exposed to a highly oxidizing atmosphere, the oxide phases are formed normally in a topochemical fashion, i.e., the interfaces between the phases maintain parallel positions to the original surface of the specimen. Above 570°C, the phases are orientated usually in the order of iron, wiistite, magnetite, and hematite, a condition in conformance with the requirements of the Fe-0 system. Below 570°C, the wiistite phase is unstable and has not been found as a normal constituent in the oxidation products of iron. There is a strong probability that continuous layers of the solid oxides are formed as the specific volumes of the phases increase in direct order from iron to hematite.' , ' Regarding mass transport through dense solid oxide layers, Wagner' has postulated that diffusion in oxides generally may be interpreted as migration processes of ions and electrons. There must be normally a concentration gradient across the growing oxide layer for diffusion to occur. This condition requires that there be deviations from the ideal stoi-chiometric composition of the oxide and accordingly deviations from the strict order of an ideal lattice. Such "lattice defects" include interstitial ions, cation and anion vacancies, quasi-free electrons, and electron holes and are decisive for all migration processes.' Cations, anions, and electrons all may have some mobility in the oxides but the movement of one of the particles generally far exceeds that of the others. Previous work', 1,2,7 has shown that during the oxidation of iron the migration through the wiistite layer, and probably also the magnetite layer, is confined to the movement of iron ions. Migration through hematite, however, has been found to take place by oxide ion movement. These behaviors are in direct agreement with the type of vacancies present in the respective oxides. Reduction of Iron Oxides The gaseous reduction of iron oxides, like the oxidation of iron, takes place in a topochemical fashion at distinct interfaces between the appearing phases."-'" Porosities might be expected in these reaction products, since their specific volumes are less than that of the starting material. Frank and van Der Merwe" have shown, however, that it is theoretically possible for nonporous layers to form if the degree of misfit in specific volume is less than about 15 pct. These aspects on porosity formation

Jan 1, 1956

By Robert D. Pehlke, Robert G. Blossey

The solubility of nitrogen in liquid binary and ternary Fe-Ni-Co alloys has been measured by the Sieverts' method between 1550°and 1700°C. Solubility data and standard free energzes and enthalpies of solution for nitrogen in the alloys are presented. Interaction parameters are discussed and presented for binary and ternary alloys. MOST of the studies of nitrogen solubility in liquid metals have been directed toward the dilute alloys of iron. Several of these investigations have included measurements of the nitrogen solubility in Fe-Ni al10s'- and in Fe-Co alloys.435 There has been some work, however, that has extended across the e-i-" and F-CO" binaries. This investigation was undertaken to determine the nitrogen solubility in both binary and ternary alloys of the Fe-Ni-Co system. It was also hoped that the differences between earlier studies might be resolved. EXPERIMENTAL METHOD This investigation was made using a Sieverts' apparatus described previously." The nickel (99.85 pct) and cobalt (99.9 pct) were obtained from Sherritt-Gordon Mines, Ltd., and the iron (99.95 pct) was Fer-rovac-E obtained from Crucible Steel Co. Recrystal-lized alumina crucibles were used throughout the entire investigation with no evidence of crucible-melt reaction. Melt temperatures were measured with an optical pyrometer and the temperature scale calibrated against the melting points of the three pure metals. The emissivity of the melt was assumed to be a linear function of composition for all alloys, as has been shown for Fe-Ni alloys.lZ The emissivity of the pure metals at 1600°C were taken as 0.43 for iron, 0.44 for cobalt, and 0.45 for nickel. Using these emissivities, the trans mis sivity of the system was found to be 0.51 i 0.01. The Sieverts' method was used for this study and followed the procedures outlined previously.l' The individual metals were weighed to give about 100 g of alloy. The alloys were melted in the crucible under a partial pressure of argon. The system was evacuated, and the "hot volume" was measured with argon. To avoid the errors caused by vaporization, the melt was held under vacuum only long enough to ensure that all of the gas in the system had been removed. The influence of any small amount of vaporization on the "hot volume" was shown to be negligible by measuring the "hot volume" after a run. This measurement agreed with that made at the start of the run within the implicit error, 0.2 cc, caused by the limitations in accurately reading the buret. The solubility-pressure relationship was measured in the pure metals and in several alloy compositions throughout the ternary system. These measurements were made by admitting measured amounts of nitrogen to the system, and then determining the equilibrium nitrogen pressure above the melt. This method has the distinct advantage of higher accuracy, particularly at lower pressures, than measurements made by withdrawing gas from the system to reduce the pressure after determining the solubility at 1 atm nitrogen pressure. This latter method has a practical lower limit of about 0.4 atm where an increased error is encountered because the buret must be emptied to permit further measurements at lower pressures. By determining the relation between apparent solubility and pressure, it was possible to make a good estimate of the initial nitrogen content of the metal from the intercept of the solubility curve extrapolated to zero pressure.11 DISCUSSION The solubility data corrected to 1 atm nitrogen pressure are summarized in Table I. The reported solubility has been corrected for the initial nitrogen content of the alloys. The initial nitrogen contents fell between 0.0002 and 0.0010 wt pct, and were lower in the iron and nickel than in the cobalt. Sieverts' law was obeyed in all alloys at pressures up to 1 atm. Examples of this behavior are shown in Fig. 1. The reaction for solution of nitrogen is Taking the standard state as 1 wt pct N in the alloy and the reference state as nitrogen at infinite dilution in the alloy, and noting the adherence to Sieverts' law, K becomes the solubility of nitrogen in the alloy at 1 atm pressure. Thus the solubility data of Table I were used directly to calculate the standard free energy for the solution reaction. These results are also presented in Table I. The enthalpy of solution is also summarized in Table I as calculated from a form of the van't Hoff relation: Iron-Nickel System. The data for the solubility of nitrogen in liquid Fe-Ni binary alloys is presented in Fig. 2 along the with data of aito, Schenck et al.,' and Humbert and 1liott.l' The data for studies of nitrogen solubility in Fe-Ni alloys containing less than 20 pc t i'- are not presented in Fig. 2, although they are in good agreement with the present work. The results of this study are in good agreement with Schenck

Jan 1, 1967

By K. R. Carson, J. Weertman

An attempt is made to ascertain the mechanism of tangle and cell formation and its dependence upon dislocation-interstitial carbon interactions. The strain-hardening behavior of single crystals of 3.25 pct Si-Fe was determined at 300° and 425°K and under conditions of both continuous and interrupted tensile strain. Significantly enhanced hardening was observed in crystals deformed at the elevated temperature, and it was further accentuated by interrupted straining. Transmission electron microscopy was used to study the resultant dislocation structures. Strain aging was found to aid tangle and cell formation at 425°K, but at both temperatures embryo tangles formed solely from primary glide dislocations, presumably by a process involving cross slip and "mushrooming". IN the course of plastic deformation all bcc metals and alloys develop a dislocation structure characterized by loose-knit groups of tangled dislocations. With increasing strain the tangles become more tightly knit and grow larger; finally a three-dimensional cellular substructure is formed:1 This process has been observed with the transmission electron microscope.'-l7 However, most investigations were confined to the study of nearly pure polycrystalline metals at relatively low temperatures. At intermediate temperatures, 0.17 to 0.14 Tm where T, is the melting temperature in degrees absolute, the mobility of interstitial impurities such as carbon is high enough to permit migration to nearby glide dislocations but is still low enough so that a significant drag force is exerted.18,19 it is also in this temperature range that a hump occurs in the curve of work-hardening rate vs temperature for iron. Analogous plots for tantalum" and columbiumzo show a definite upward trend in the work-hardening rate. Keh and Weissman1 have pointed out that this behavior may be explained solely on the basis of changes in the dislocation configuration: at low temperatures the dislocations tend to be relatively straight and uniformly distributed, but at intermediate temperatures tightly knit tangles and cellular substructure appear. The interference of these tangles with glide dislocations causes the observed increase in the work-hardening rate. This explanation appears reasonable, yet one might ask what factors cause tangle formation to be so favorable at intermediate temperatures. It seens likely that the strong dislocation-interstitial interactions which are known to occur in this temperature range are at least partly responsible," with the magnitude of the effect being proportional to the interstitial concentration. The purpose of the present work is to study the relationship between tangle formation and strain hardening in a bcc metal in the temperature range 0.17 to 0.4 Tm. Particular emphasis was placed upon a study of the effects of interstitial-dislocation interactions. Single crystals of 3.25 pct Si-Fe containing about 200 ppm of C in solid solution were used in the investigation for the following reasons: 1) The mobility of interstitial carbon in 3.25 pct Si-Fe is negligible at 300°K but increases rapidly at slightly elevated temperature22. Hence, differences between the flow curves and dislocation structures of crystals deformed at 300°K, 0.17 T,, and crystals deformed, say, at 425°K, 0.24 Tm, should be appreciable because of the enhanced dislocation-carbon interactions at the elevated temperature. This effect was accentuated in some samples by interrupted straining, thereby introducing a certain amount of aging. 2) Near room temperature, slip in suitably oriented 3.25 pct Si-Fe single crystals is largely confined to the (110) planes.23'24 Dislocation structures formed under conditions of single glide are the least complicated and their method of formation is the most easily discernable. 3) Dislocations in Si-Fe can be tightly locked with carbon atmospheres by a low-temperature aging treatment. The subsequent thinning of samples to foil thicbess causes little or no rearrangement in the dislocation structure.25 EXPERIMENTAL PROCEDURE Large single-crystal sheets of 3.25 pct Si-Fe were donated by Dr. C. G. Dunn of the General Electric Research Laboratory, Schenectady, N. Y. The orientations of the sheets were determined and slabs 1.0 by 0.25 by 0.05 in. were cut such that the desired tensile axis corresponded to the long dimension. The slabs were mechanically polished and subsequently decar-burized by heating at 1000°C for 3 days in a flowing wet-hydrogen atmosphere. A carbon content of about 200 ppm was introduced by heating at 805°C for 25 min in a flowing atmosphere of dry hydrogen containing heptane vapor. Shaped copper tools were then used to spark-machine at 0.125 by 0.50 in. gage length onto each slab. Vacuum annealing at 1225°C for 2 days followed by a quench into the cold end of the furnace to retain carbon in solid solution concluded the soecimen preparation. Continuous tensile flow curves for crystals of severa1 orientations Were obtained both at 300' and 425°K. A strain rate of 6.67 x 10-4 Per set was used in these and all other tests. Crystals oriented for single glide, B and D in Fig. 1, were subjected to a 3.5 pct plastic elongation to insure uniform slip along the gage length; they were then immediately subjected to interrupted strain cycling as indicated in Fig. 2(a). Each cycle consisted of unloading to 1.5 kg per sq mm, holding

Jan 1, 1969

By J. C. Fisher, J. H. Hollomon, David Turnbull

Understanding of the diffusion problem has recently been furthered by the analysis of Birchenall and Meh1.l They pursued the problem of the variation of the diffusion coefficient with composition for non-ideal solid solutions. Their analysis follows the tradition of Wagner,l Jost, Dehlinger, and Darken & who assumed the net flux of diffusing material to be proportional to the gradient of a quantity related to free energy. The basic assumption in Birchenall and Mehl's formulation of the problem is that the net flux of diffusing material is proportional to a thermodynamic activity gradient. To estimate the applicability of the derived relations, they corrected the diffusion coefficients of carbon in austenite by utilizing Smith's6 activity data for carbon, and the diffusion coefficients for zinc in copper with activity data computed from the vapor pressure measurements of Har-greaves.' The corrected coefficients for carbon were virtually independent of carbon concentration. For the diffusion of zinc in copper a moderate variation of diffusion coefficient with concentration remained after the correction. The problem of diffusion can be formulated in another way than that used by Birchenall and Mehl. The method is that of chemical rate theory and has been used by Eyring and his coworkers8,9 as well as by Eyring and Zwolinskilo in a discussion to Birchenall and Mehl's paper. As yet the method has not been applied to substitu-tional solid solutions. On the basis of their assumptions, Eyring and Zwolinski derived a relation between the diffusion coefficient and activity that is identical with that of Dehlinger and Darken but which does not correct for the variation of the diffusion coefficient with concentration as well as does the relation derived by Birchenall and Mehl. It was thought that the theory of diffusion would be more complete if the inconsistency between the two analyses could be rationalized and if diffusion in substitu-tional alloys were analyzed on the basis of the concepts of the chemical rate theory. Chemical Rate Theory According to the theory of absolute reaction ratess the reaction +..... +X, Eq I is viewed as taking place in two steps. First the reactants A1, A², . . . A; combine to form an activated complex M with which they are in equilibrium: A1 + A1+ . . . + A=M. Eq 2 Second the activated complex decomposes to give the products XI, XZ, . . . Xi: M?X, + X²+ . . . +Xi Eq g It has been showns that the number of activated complexes decomposing per unit volume per unit time is given by the expressiont kT -h CM † The transmission coefficient has been taken as unity.

Jan 1, 1949