By P. J. Spencer, J. N. Pratt

The vapor pressure of manganese over liquid Mn-Sn alloys has been determined by a high-temperature torsion-effusion technique. Alloys containing from 8 to 100 at. pct Mn were investigated in the temperature range jrom 1280" to 1580" and the measured pressure values were used to calculate the partial and integral thermodynamic properties of the liquid alloys. The activities show small negative departures from ideality while the integral heats and excess entropies of mixing are asymmetric inform, changing from positive to negative with increasing manganese content. The possible contribution of various factors to the observed thermodynamic properties is discussed. COMPARATIVELY few thermodynamic data are available for manganese alloy systems.' Therefore, as part of a continuing program of studies of the thermodynamic properties of transition metal alloys, measurements have been made on various binary alloys involving this element. In recent publications,2~3 investigations of liquid Mn-Cu alloys and of the Mn-Au system in both solid and liquid states have been reported. For the first-mentioned system the work suggested that magnetic interactions may be responsible for the observed form of the thermodynamic properties, while in the second the influence of the electrochemical factor appears to be dominant. The present paper describes a similar study of liquid Mn-Sn alloys. Again the thermodynamic properties have been obtained from vapor pressure measurements made by use of a high-temperature torsion-effusion technique.4 A detailed description of the apparatus and of the experimental procedures used in alloy preparation and pressure measurement may be found elsewhere.2'4 EXPERIMENTAL RESULTS Sixteen alloys, ranging in composition from 8 to 100 at. pct Mn, were prepared from spectroscopically standardized manganese of 99.99 pct purity and tin of 99.999 pct purity, both supplied by Johnson-Matthey and Co., Ltd. One-gram samples of the alloys were obtained by carefully weighing appropriate amounts of the pure components into an effusion cell; this was then suspended in the apparatus and the metals melted together in situ by heating under vacuum to approximately 1550°K. After allowing sufficient time for a homogeneous liquid alloy to be formed, vapor pressure measurements were commenced. These were determined as rapidly as possible at a series of steady temperatures within the range of interest. The duration of experimental runs on individual samples was kept sufficiently short to ensure insignificant varia- tion of alloy composition during investigation. After completing pressure measurements, the alloys were rapidly cooled and their compositions checked by weighing or chemical analysis. All experiments were conducted using effusion cells machined entirely from boron nitride. Measurements were made using a variety of cells with orifice areas ranging from 0.0032 to 0.0075 sq cm and lengths of the order of 0.04 cm; the usual effusion correction factors for orifice geometry and molecular distribution were calculated using Freeman and Searcy's equation5 and had values between 0.6 and 0.75 for the orifices employed here. The vapor pressures of manganese over the alloys were measured at approximately 20°K intervals in the temperature range 1280" to 1580°K. In view of the close approximation of the measured pressures to Clausius-Clapeyron behavior in the experimental temperature range, the data for each alloy have been expressed by equations of the form: logp(atm) =-A/T + B A least-squares computer treatment was applied to the vapor pressure values in order to obtain the coefficients A and B with their associated error. The resulting equations are listed in Table I, together with the equation for pure solid manganese obtained from a previous study.4 To minimize the effect of possible apparatus calibration errors, the activities and partial free energies of manganese in the alloys were calculated by initial reference to the latter equation, obtained from identical torsion-effusion measurements. The immediately resulting thermodynamic quantities, based on a solid manganese reference state, were then converted to refer to the more appropriate supercooled pure liquid manganese standard; tabulated values of the free energies of solid and liquid manganese from Hultgren et al.' were used for this purpose. Partial entropies of solution of manganese were calculated from the temperature coefficients of the free energies and partial heats from the Gibbs-Helmholtz relationship.

Jan 1, 1969

By C. Law McCabe, R. G. Hudson

The Knudsen cell has been employed to determine the free energy of formation of Mn7Cs in the temperature range 800" to 950°C. A value of 66,440 cal was found for hH°o for a-manganese. Measurements of the pressure of manganese over a mixed carbide, (Fe,Mn),C, points to a power relationship between aun7cs and N.4,. RECENTLY Kuo and Perssonl have reported that the carbide of manganese which is in equilibrium with graphite at temperatures up to 1100° C is Mn7Ca. There are no published data on the thermo-dynamic properties of this compound. In order to determine the stability of Mn7Ca, it appeared that, by obtaining the pressure of manganese above 8-manganese and also above Mn,C, in equilibrium with graphite, the free energy of formation of Mn7Ca from 8-manganese and graphite could be obtained. In addition, the vapor pressure of manganese, reported by Kelley From data of Bauer and Brunner,' is subject to some uncertainty and further determinations of the vapor pressure of manganese seemed warranted. In this investigation of the pressure of manganese vapor above pure manganese and also above the carbide of manganese in equilibrium with graphite the apparatus used is the Knudsen orifice cell. The same apparatus, experimental procedure, and method of calculating the pressure was used in this investigation as in one previously reported.~ Care was taken to insure that the cells were at constant weight before using them in a run. The manganese charged in the cell was CP grade powder, carbon free, obtained from the Fisher Scientific Co. A spectroscopic analysis of the manganese after appreciable amounts of it had vaporized from the Knudsen cell showed that no element was present in sufficient quantities to contribute to a weighable weight loss or to decrease the vapor pressure of manganese to any appreciable extent. The spectro-graphic analysis was 0.002 pct Cu, 0.05 pct Fe, 0.002 pct Pb, and 0.002 pct Ni. 8-manganesea is the allo-tropic form of manganese which was present in the cell at temperatures used in this investigation. The manganese carbide, Mn,Ca, was made in the following way: In a closed graphite cell manganese powder was added to graphite powder, which was made from graphite rods for spectrographic use. The manganese powder was the same as that described previously; 5 pct excess graphite was added over that required for the formation of Mn7C,. The mixture was heated in a closed graphite cell for approximately 20 hr at 1350°K under vacuum. X-ray analysis revealed that there was no manganese present after this treatment, but that the lines due to Mn,C, were present. In order to prove that there was no volatile carbide of manganese which was effusing out of the cell, the following experiment was performed: A graphite effusion cell containing graphite power, in excess of that to form Mn,C, of a desired amount, was brought to constant weight on heating at 1228°K. The required amount of manganese was accurately weighed and then added to the graphite effusion cell. The cell was placed in a vacuum at 1228°K for one week, which was the time calculated for the manganese to have effused completely, assuming instantaneous formation of Mn,C8. The cell was then weighed again. This experiment was carried out on two different occasions and both times the weight loss of the cell came within 1 pct of the weight of manganese originally charged minus the weight of manganese left in the cell, as determined by chemical analysis. These data are summarized in Table I. This agreement is considered to be within experimental error and is taken as proof that no carbide of manganese is volatile in this temperature range. It was established, by X-ray analysis, that Mn,C, formed before appreciable amounts of manganese vaporized from the metal powder which was charged. The identification of the carbide of manganese which was present in the Knudsen cell in equilibrium with graphite and manganese vapor was carried out by Kehsin Kuo at the University of Uppsala. He established that the authors' sample, which was submitted to him for analysis, contained the phase

Jan 1, 1958

By E. S. Machlin

The wzodel of Blandin and Diplunt;, generalized to include a phase factor, is applied to the carbon-carbon interaction in iron. Darken&apos;s "energetic" model is generalized to include not only first neighbor interactions but further neighbor interactions as well. On the bases of these generalized models relations are derived for the activity of carbon in both austenite and ferrite in terms of the carbon-carbon Pair interaction energies. A single function then yields the pair interaction energies consistent with the experimental activities of carbon in both ferrite and austenite. Thus, a simple explanation is given for the observation that the nearest-neighbor interaction between carbon is repulsive in austenite and attractive in ferrite. Certain consequences of this approach are explored. OnE object of the present paper is to attempt to take into account the consequences of electrostatic contributions to the carbon-carbon pair interaction energy for carbon as a solute in iron. Friedel&apos; has shown that oscillations in electrostatic potential are to be expected about a solute atom in a metallic solution. Blandin and 6lant6&apos; have shown that such oscillations yield an interaction energy between pairs of solute atoms that obeys the relation: W{ = A cos(2ftFri + 4>)/(kFri)3 [l] where kF = Fermi wave vector, ri = distance between solute atoms comprising the pair7 <p = phase factor dependent only on electronic nature of solute and solvent, A = coefficient dependent only on electronic nature of solute and solvent. Machlin3 found that Eq. [I] accurately described the pair interaction energy derived from short-range order measurements based on field ion microscope observations of dilute alloys of platinum. He also found that the value of the phase factor $ derived from residual resistivity measurements agreed well with that obtained from the analysis of the short-range order data. Harrison and paskin4 were able to predict the long-range ordering energy of 0 brass using Relation [I] and residual resistivity values to predict the value of the phase factor $. Machlin5 has repeated their analysis and applied it to the prediction of the long-range ordering energy in AgZn and AgCd with excellent agreement between prediction and experiment. Both A and $ are independent of the crystal structure. The Fermi wave vector depends uniquely upon the conduction electron concentration per unit volume in the spherical approximation of the Fermi surface. Thus, Eq. [I] is expected to apply to both fer- rite and austenite with only one set of values of A and $. Mossbauer studies6 yield the result that iron has one 4s electron. We shall make an assumption found to hold previously for platinum3&apos;7 and nikel, which is that only the s electrons are involved in shielding the perturbing potential of carbon. With this assumption, kF = 1.35 A-l. Although A and $ may be obtained from certain mdels&apos;&apos;&apos; we shall take A and $ to be empirical constants in the spirit of Kohn and osko.&apos; Thus, Eq. [I] involves two adjustible parameters. Consequently, two independent relations in A and $I are required in order to evaluate them for carbon as a solute in iron. We may use a recent analysis of Aaronson, Domain, and poundg who showed that Darken&apos;s energetic model,1° as well as others, can be used to describe the activity-temperature data for carbon in iron in both the aus-tenitic and ferritic phases. Darken&apos;s model takes into account only first neighbor pair interactions. For our needs, all neighbor pairs need to be taken into account. It is convenient to generalize Darken&apos;s model. The result for the partition function for austenite is: over the temperature range 800" to 1200°C and where the uncertainty corresponds to one standard deviation. Eq. [4] effectively yields only one relation. Another relation is required to obtain unique values for A and $. One property of Eq. [4] is that it is independent of crystal structure. Hence, data for a iron can be used to obtain another relation. To arrive at this relation we must generalize Eqs. [2] and [3] so that they may be applied to the bcc a iron. The result is that:

Jan 1, 1969

By J. L. Taylor, Pol Duwez

THE present knowledge of the Ti-Al system is limited to the portion of the diagram extending from pure aluminum to the intermetallic compound TiAl3&apos; A preliminary investigation of the titanium-rich Ti-A1 alloys revealed that the solubility of aluminum in titanium is quite extensive and that the transformation temperature of titanium is raised by alloying with aluminum. From an X-ray diffraction study of alloys containing up to 75 atomic pct Al (TiAl3), the phase boundaries at 750°C were located as follows: the a titanium solid solution extends from 0 to about 36 atomic pct Al, a two-phase region exists from 36 to 46 atomic pct Al, and an intermediate phase of varying concentration extends from 46 to 62 atomic pct Al. The purpose of the present paper is to describe the crystal structure of this new phase. The alloys were prepared by melting in a helium arc furnace on a water-cooled copper plate, using a furnace essentially the same as that described in ref. 2. The titanium metal was of the iodide type furnished by the New Jersey Zinc Co., and a piece of pure aluminum (99.99 pct) was obtained through the courtesy of the Aluminum Co. of America. After melting, the samples, weighing approximately 5 g, were sealed in evacuated fused silica tubes and homogenized for 4 hr at 1000°C. The specimens were then held for 10 days at 750°C and rapidly cooled to room temperature. Filings were then taken from each sample, sealed in evacuated vials, annealed at 750°C for 4 hr, and rapidly cooled to room temperature by quenching the vials in water. Powder diffraction patterns were obtained with a 14.32 cm diam camera, using K copper radiation filtered through a nickel foil. Structure Determination The X-ray diffraction patterns of the alloys containing 46, 50, 55. 60, and 62 atomic pct Al were identical, except for a slight shift in the positions of the reflections. The alloy containing 55 atomic pct Al was chosen far structure determination. The powder pattern contained 37 reflections and the a, doublets were well resolved in the back-reflection range. The relatively small number of reflections and the sharpness of the pattern were considered as an indication of a simple atomic arrangement in a relatively small unit cell of high symmetry, and an attempt was therefore made to solve the structure without single crystal work. A satisfactory fit was found on a large scale Hull-Davey tetragonal chart for an axial ratio of approximately 1.45. All the reflections were readily indexed and the tentative unit cell dimensions were computed to be a - 2.81 kX, c - 4.07 kX, and c/a = 1.448. The indices (hkl) and the values of d and sin2 A are given in Table I. The agreement between observed and computed sin2 is quite satisfactory. Once the unit cell was known, the details of the structure were readily found. First, it is obvious that the number of atoms per unit cell cannot exceed two, since more than two atoms would lead to a density greater than that of pure titanium. The next logical step is to assume that the two atoms occupy the corner and center of the cell. If this assumption is correct, the structure may be described as follows: space group D1, - P 4/mmm; one titanium atom in a: 000; one aluminum atom in d: 1/2 1/2 1/2: and no extinctions. Assuming this structure to be the correct one. intensities were computed by means of the usual equation: sin2 0 cos 0 where F is the structure factor; 8, the Bragg angle. and p, the multiplicity factor. The calculated values of intensities are compared in Table I with the visually estimated intensities. The agreement is quite satisfactory and the structure is therefore confirmed. The crystal structure of TiAl just described is the same as that of AuCu ordered. The AuCu ordered

Jan 1, 1953

By F. Garofalo

It has been shown by various investigators that during constant stress creep the dependence of minimum creep rate, 6,, on stress, o, is given by em = A onat low stress levels, md by 6, = A&apos; exp [ß s] at high stress levels. In these relations A, n, A&apos;, and ß are constant at constant temperature. A single relation has been found which satisfies conditions for both high and low stresses and agrees well with experimental results. This relation is 2, = AN (sinh a s)n, where A" is a constant at constunt temperature and a = p/n. This relation also satisfies the linear relation, 6, = k s, found at temperatures near the melting point at low stresses. EXPERIMENTAL creep results have led to a number of empirical relationships between minimum creep rate, 6,, and the applied stress, s. Under conditions of constant stress it is generally found that at low-stress levels,&apos;-&apos; the dependence of minimum creep rate is given by 6, = Asn. At high-stress levels&apos;74 the experimental results fit the relation, 6, = A&apos; exp [po l. In these relations A, n, A&apos; and ß are constant at constant temperature. A model based on climb-of-edge dislocations from a pile-up array leads to a relation similar to that found experimentally at low stresses.&apos; On the other hand. theories based on chemical-reaction rate,5 nonconservatively moving dislocation jogs, and jog migration and climb-of-edge dislocations4 lead to a relation similar to that found experimentally at high stresses. No difference in mechanism between low and high stress levels has been clearly defined; it is questionable whether such a difference really exists. In any event, the major argument usually given in substantiation of a change in mechanism from low to high stresses is that no single relation exists for defining the stress dependence of the creep rate over wide ranges in stress. However, such a relation has been found and is of the form, dm = A" (sinh a s)n, where A" is a constant at con- stant temperature and a = ß/n. This relation agrees well with experimental results over wide ranges in stress and temperature for copper, aluminum, an A1-3.1 pct Mg alloy, and an austenitic stainless steel. STRESS DEPENDENCE OF MINIMUM CREEP RATE At low stress levels the minimum creep rate, gm, depends on the stress, 0, under conditions of constant stress creep through the relation em=Aon [1] The quantities A and n have been defined previously. In the range in which this relation applies, a linear dependence is found in a log em,-log o plot. Above the stress range of application of relation [I], the minimum creep rate increases much mar; rapidly than predicted by relation [I]. This behavior is shown in Fig. 1 for a series of creep tests on copper4 at various temperatures ranging from 673 o to 973°K. Relation [I] is satisfied at the lower stresses, although the results at 973°K are quite limited. In all cases the transition beyond the applicable range of relation [I] is a gradual one indicating no abrupt change in mechanism. For all test temperatures, values of n have been determined from the results in Fig. 1. These are reported in Table I under Alog tm/hlog o. At high stress levels the stress dependence of minimum creep rate under conditions of constant stress is given by im = A&apos; exp [ß a] 2] All factors have been defined previously. In a log em-0 plot, relation [2] predicts a linear function. Experimentally, a pronounced deviation from the prediction of relation [2] is found at lower stresses. As the stress is lowered, the minimum creep rate decreases more rapidly than predicted by relation [2]. This shown for copper in Fig. 2. Again it is found that the transition from high to low stresses is gradual and no really sharp change is found. Values of p determined from the high stress results are given in Table I. The dependence of minimum creep rate on stress at constant temperature for all ranges in stress

Jan 1, 1963

By M. J. Marcinkowski, Gordon E. Lakso

An extensive investigation has been made of the deformation behavior associated with the Fe3Si super-lattice using transmission electron microscopy techniques. Above 243°K the stress-strain curve exhibits three stages. Stage I occurs at a very low stress level and is related to the generation of perfect superlat-tice dislocations. Stage II is characterized by an extremely rapid rate of work hardening and is associated with the Taylor type locking of these superlattice dislocations. Finally Stage III is related to dynamic recovery processes since the work hardening rate is very small. Below 243ºK, only Stage I is observed, but it occurs at a much higher stress level. This latter observation is related to the generation of imperfect dislocations in Stage I with the consequent production of second nearest neighbor antiphase boundaries. The reason for this is that insufficient thermal energy is available at these low temperatures to generate the complete and perfect superlattice dislocations. It has been shown that the fully ordered FeCo alloys, i.e., those possessing the B2 type structure, exhibit three distinct stages of work hardening whereas the corresponding disordered alloys show only one.&apos;" This difference in behavior between the disordered and ordered alloys has been attributed to the fact that dislocations in the former case travel only as ordinary 1/2ao(111) types whereas in the latter case the move through the lattice as coupled 1/2a0(111) dislocations separated by an antiphase boundary (APB), i.e., the so-called superlattice dislocation. Although some preliminary work has been carried out concerning plastic deformation in ordered alloys possessing the DO3 type superlattice,3 no detailed analysis similar to that described in Refs. 1 and 2 has been attempted. Specifically, it has been suggested that the superlattice dislocation in this particular type structure should consist of four ordinary 1/2ao<111> types bound together by first and second nearest-neighbor APB&apos;s. Fe3A1 and Fe3Si are the two classic alloys possessing the DO3 type lattice; however, because of the somewhat higher ordering energies associated with the FesSi alloy, which in turn assures that dislocations will travel through the lattice as perfect superlattice dislocations under at least some conditions, it was chosen for the present investigation. Because of the extreme brittleness of Fe3Si, all deformation was done in compression. Stress-strain curves were obtained using both polycrystalline samples as well as single crystals. In the latter case the crystals were oriented so that deformation could be controlled either by single or double slip. They were then wafered parallel to and at various angles to the operative slip planes. These wafers were in turn examined by transmission electron microscopy (TEM) techniques in order to determine the extent of the interaction from the dislocation configuration contained therein. EXPERIMENTAL PROCEDURE The alloys used in this investigation were arc melted under helium from electrolytic iron of greater than 99.90 wt pct purity and transistor grade silicon of 99.99 wt pct purity. A typical analysis of interstitial impurities showed 120 ppm 0, 15 ppm N, and 65 ppm C Because of the extremely low ductility of the Fe3Si alloys, it was necessary to spark cut 0.230-in. diam polycrystalline cylinders 0.400 in. long from arc-melted fingers using a thin-walled brass tube as a cutting tool. The polycrystalline alloys could not be recrystallized since very little strain was induced in preparation. However they were annealed at 1273°C for 15 min in evacuated vycor capsules to relieve any cooling stresses that may have developed during solidification and then air cooled. The resulting grain size of the alloy was 0.50 mm. According to warlimont4 1273ºC is just within the single phase field where FesSi possesses the DO3 type lattice. In addition because of this high critical ordering tem-ature, air cooling from this temperature was believed sufficient to fully order all of the Fe3Si samples used in the present investigation. For the same reason, no attempt was made to achieve any degree of disorder by quenching. In fact, rapid quenching from 1123°K caused cracking. Such cracking was first suggested by sato5 with respect to the experimental observations of Glaser and Ivanick.6 Single crystal compression specimens were spark cut from single crystal ingots grown in a Bridgman type furnace. The iron and silicon for the crystals was prealloyed by arc-melting two 130-g buttons which were cut into small pieces before remelting in the furnace. This procedure resulted in a long-range inhomogeneity of 0.5 at. pct Si between the top and bottom of the 2-in.-long single crystal ingot, which was assumed to be negligible in the present investigation. The single crystals, after orienting and spark-cutting, were about 0.37 in. by 0.37 in. in cross section and about 0.5 in. long. True stress-strain curves were obtained using an Instron Tensile Testing machine in conjunction with techniques described previously. 1,7 The strain rate was 0.05 in. per in. per min. Prior to testing, the ends of all the compression cylinders were hand polished using a special jig to insure parallelism after which the sides of the samples were electrochemically polished to eliminate stress risers and to facilitate slip line observations. Test temperatures between 77" and 823°K were obtained using various cooling and heating media as described in Ref. 7 while at the upper end of this temperature range, a mixture of equal

Jan 1, 1970

By H. H. Podgurski, J. C. M. Li, Y. T. Chou, F. N. Davis, R. A. Oriani

When an Fe-2 pct A1 alloy is nitrogemted at 500ºC with a gus tnixture (NH3-H2) in which the nitrogen activity has been kept Lou] enough to avoid the formation of iron nitride, a two-phase alloy is generuled which consists of AlN particles and a ferrite phase cotaining a heavy network of dislocations. The amount of nitrogen contained in such an alloy, when equilibrated with the nitrogenating atmosphere, far exceeds both that needed to satisfy the normal solution requirements of a Fe and that needed to convert all of the aluninuwi to AlN. This excess nitrogen is accounted for as being trapped on dislocations, adsorbed at the ferrite -AlN interface, and as an en-Iuznced lattice solubility in strained ferrite. This excessive uptake of nitrogen had previously been attribuled by other investigators to the formation of a nonstoichiornetric aluminum nitride. Isotope exchange experiments revealed various amomts of exchargeable N14 present in the originally nitrided samples that could not be removed by reduction with HS at 500ºC. This exchangeable nitrogen has been identified us that bound to the AlN -ferrite interface. Estimates of inter facial areas in alloys containing -3 pct by weight of A1N are as high as 10 sq m per g of alloy. ThE first1 of this series of papers described the experiments forming the basis for the elucidation of the mechanism of the formation of aluminum nitride particles within an Fe-A1 alloy. It was found that not only are dislocations necessary for the nucleation of the AlN particles but also the nitriding reaction in turn produces a dense network of dislocations in the ferrite matrix. It was also observed that nitrogen in excess of that needed for the formation of stoichiometric AIN is taken up by the alloy without the formation of an iron nitride. The present paper is an analysis of the excess nitrogen sorbed by the nitrided Fe-A1 alloy which considers the structure generated by the formation of the aluminum nitride particles. Because of the high density of dislocations, this system has proved to be quite useful in studying nitrogen-dislocation interactions. Wriedt and Darken2 have already reported such studies in a cold-worked ferritic steel. EXPERIMENTAL Nitrogen Sorption. The specimens of this alloy were cold worked (50 pct reduction) to 0.011 in. thickness and chemically cleaned in a 2:1 concentrated phosphoric acid-50 pct hydrogen peroxide solution before nitrogenation. The flowing nitrogenating atmosphere (11 pct NH3-89 pct H2) was established before the ni- trogenating temperature was reached. The same gravimetric and gas-flow equipment described in an earlier paper1 was also used in this investigation. Changes in nitrogen concentration were followed gravimetrically when establishing the isotherms. In the isotope exchange experiments, concentration changes were followed volumetrically. In some instances chemical analyses (Kjeldahl method) were used to check for material balances in both the gravimetric and volumetric procedures. Our objective was to obtain reversible nitrogen sorption isotherms for alloys equilibrated with NH3-H2 gas mixtures over a large range of nitrogen activity* and temperature. The *Defined as equal to PN H /P3/2 ,where P corresponds to partial pressure in atmospheres. Actually the nitrogen activity, aN, in the alloy equals K PNH3 /p3/2H2, where K is the equilibrium constant for the reaction NH3 = N + 3/2H2. upper limit for nitrogen activity was below that which would produce iron nitride; for reasons which will become apparent later, most of the sorption studies were made in the temperature range between 400" and 500&apos;C. The alloy sample studied most extensively in this investigation was given a series of successive reductions (100 pct H2) and nitrogenating treatments at 500°C to attain a stabilized structure. Presumably some dislocations were lost during these treatments. Throughout most of the sorption studies, temperature was held at ± 1°C and the gas-phase composition was held to k0.2 pet NH3. Based upon the results of numerous diffusion experiments with this alloy* the &apos;Results to be published in a third paper of this series. times chosen for equilibration were considered more than adequate, Nitrogen Isotope Exchange. The first exchange experiments were carried out by circulating a measured quantity of H2 and NH3* (with a predetermined isotopic *The NH3 was synthesized over a synthetic ammonia iron catalyst using H2, and N2, enriched with N15. AS the NH3 was formed it was removed continuously from the gas phase by circulating the mixture through a refrigerated (78ºK) trap. When most of the nitrogen had been converted to NH3, it was distilled from the trap into a glass storage vessel. composition, N15/N14) over a nitrided specimen at 450°C in a closed glass system. Attempts to reach the exchange limit isothermally, i.e., an isotopic ratio (N15/N14) in the gas phase identical with the extractable nitrogen in the nitrided alloy, were futile. The exchange rate between the gas phase and the alloy was too slow, involving many days. To circumvent the slow exchange with the gas phase, measured amounts of N15 and N14 were introduced into the alloy by nitrogenating with an NH3-H2, mixture at 500°C containing an N15/N14 ratio of 7.76; the charged specimens were then sealed by allowing an oxide film to form over them in air, and in this final condition the specimens were subjected to 500°C in vacuum for various times during which isotope exchange was allowed to proceed within the specimen. It was estab-

Jan 1, 1970

By Peter R. Morris

The effecl of preferred orienlation on X-vay dzffvaction measurements of retained austenzte was investigated for four precipitation-hardening staznless steels in sheet form. A method is preserzted for estimating the ervor in measurement associated with a given samplirig direction. The method was used to select an "optimum" sampling direclion in order to minimize errors in measurement due to preferred orientation. hleasuremenls of retained austenite content employing lhe proposed sampling direction are conzpaved to measuretnents enzploying the more commonly used normal direclion for a series of sawzples. THE first application of X-ray diffraction to the measurement of retained austenite in steels is due to Sekito, 1 who employed a photographic technique in which the (111) reflection from a thin strip of gold affixed to a cylindrical sample was employed as a standard. Averbach 2 introduced the "direct comparison" method in which the ratios of observed to calculated random intensity are assumed proportional to the austenite and/or martensite contents. Averbach&apos;s work forms the basis of most subsequent X-ray diffraction methods for the determination of retained austenite. Subsequent improvements are due to: Averbach and Cohen,3 who employed a sodium chloride crystal to monochromate cobalt radiation; Averbach et a1.,4 who introduced a bent sodium chloride monochromator; Mager,&apos; who used a bent quartz crystal to monochromate chromium radiation ; Littmam, who first used a geiger counter diffractometer for this purpose; Beu and Beu and Koistinen, 11,12 who studied effects of absorption factor, surface preparation, sample geometry, integrated intensity vs peak height, choice of radiation, monochromator, and filter. The possibility of errors in measured values due to orientation effects was noted by Miller,13 who suggested examination of a surface other than the plane of rolling. Lopata and Kula 14 have developed an experimental technique in which the preferred orientation is measured in each sample. They illustrated the method for a sample containing 42 pct retained austenite. Application of their technique to the 1 to 15 pct range typical for the precipitation-hardening stainless steels does not appear feasible. EXPERIMENTAL PROCEDURE The nominal compositions of the precipitation-hardening stainless steels investigated are listed in Table I. Ingots were solution-treated, hot-rolled to approximately 0.2 in., and reduced to 0.050 in. by a suc- cession of cold rolling and annealing operations. After this treatment the 17-4PH sample was in the marten-sitic condition, while the 17-7PH, PH 14-8Mo, and PH 15-7Mo samples were in the austenitic condition. Samples of 17-7PH and PH 15-7Mo steels in the mar-tensitic condition were obtained by heating to 1750&apos;F for 10 min and holding at -100°F for 8 hr. A sample of PH 14-8Mo steel in the martensitic condition was obtained by heating to 1700°F for 1 hr and holding at -100°F for 8 hr, followed by aging at 950" for 1 hr. POLE FIGURE DETERMINATIONS Samples were thinned to 0.003 to 0.005 in. by etching in a solution containing 250 ml reagent-grade phosphoric acid (85 to 87 pct H3PO4), 250 ml technical-grade hydrogen peroxide (30 to 35 pct H 2 O 2), and 50 to 100 ml reagent-grade hydrochloric acid (37 to 38 pct HCl). The specimens were placed in an "integrating" sample holder which provided a 1-in. oscillation in the plane of the sample. The diffractometer was aligned to measure the intensity diffracted by planes of the particular {hkl} type being studied. The sample was Set for a given latitude angle, a, measured from the plane of the sheet, and diffracted intensity recorded as the longitude angle, 0, measured in the plane of the sheet from the rolling direction, was increased from 0 to 360 deg. After a 360-deg scan of B, a was incremented by 5 deg, and the process repeated. Random standards obtained by spraying suspensions of powdered iron (bcc structure) and nickel (fcc structure) in lacquer were used to correct observed intensities for absorption and geometrical effects. Zirconium-filtered molybdenum radiation was used to determine the transmission regions of the (111) (0to 45 deg), (200) (0 to 60 deg), and (220) (0 to 45 deg) austenite and (110) (0 to 45 deg), (200) (0 to 50 deg), and (211) (0 to 35 deg) martensite pole figures. Vanadium-filtered chromium radiation was used to

Jan 1, 1968

By M. J. Marcinkowski, D. B. Crittenden, A. S. Sastri

A study co.mbining stress-strain .measurements in conjunction with transmission electron microscoPy has been made with near equiatomic Fe-Cr alloys which were aged for various times at 500°C. Associated with this aging is a marked increase in deformation twinning. The outstanding feature of these twins is that they generate stress fields sufficiently great so as to give rise to spontaneous dislocation loop nucleation nearly normal to the propagating twin. This observation is in agreement with the theoretically predicted elongation of the stress field of a dislocation Perpendicular to its direction of motion as it moves near the speed of sound. Dislocation loop nucleation is more difficult in the longer aged alloys so that this energy absorption mechanism is not effective in hindering twin propagation. Since crack nucleation can readily occur near the tip of a twin, the aged alloys become extremely brittle when deformed in tension. Iron-chromium alloys in the vicinity of the equiatomic compositions become severely embrittled when aged at about 500°C. Fisher et 01.&apos; have shown that this embrittlement is related to the decomposition of the original random Fe-Cr solid solution into a chromium-rich and an iron-rich phase. In addition, Mar-cinkowski et a1.&apos; have shown that twinning becomes an increasingly more important mode of deformation as the aging time is increased. These results have been recently corroborated by the transmission electron microscopy study of Mima and amauchi . The Fe-Cr alloy thus seems ideal for verifying the predictions made in Parts I4 and 115 of this investigation where the behavior of large static or blocked twins and those of large dynamic or propagating twins, respectively, were investigated numerically. It was thus decided to measure the stress-strain curves generated by embrittled alloys that were aged for various times and to examine sections by transmission electron microscopy. EXPERIMENTAL PROCEDURE Electrolytic iron and electrolytic chromium were vacuum-melted and poured into ingot form. The composition of the resulting alloy was found to contain 46.0 wt pct Cr (47.8 at. pct), the remainder being iron. The resulting ingot was swaged above 850°C into 0.250-and 0.400-in.-diam rounds. Compression samples of 0.250 in. diam and 0.400 in. long were cut from the smaller-diameter rounds. These samples were then sealed in evacuated quartz tubes and annealed for 30 min at 1150°C to produce a uniform and equiaxed grain size of mean diameter equal to 1.73 mm. They in turn were rapidly quenched from 850°C so as to preserve the condition of random solid-solution characteristic of the elevated temperature. The samples were then aged for various times up to 300 hr at 500°C in a massive Pb-Bi alloy bath. The samples were next polished and tested in compression at room temperature as described in Ref. 6 using an Instron tensile testing machine. The strain rate used was 0.05 in. per in. per min. The remaining larger round was converted into compression specimens of 0.325 in. diam and 0.500 in. long. This larger diameter enabled wafers of sufficient size to be prepared for examination by trans-mission electron microscopy techniques after subjecting them to a suitable strain. Foil preparation is described in some detail in Ref. 6. All foils were examined in a type HU-11A Hitachi electron microscope operating at 100 kv. RESULTS AND DISCUSSION Fig. 1 shows the effect of aging at 500°C on the room-temperature stress-strain curves of the FeCr alloys. For greater clarity the origin of each curve has been displaced upward. The same origin has been used for both the 0 and the 0.1 curves. It is apparent that with increased aging times a sharp drop in load is observed at the yield stress which becomes more pronounced as aging proceeds. A loud sonic burst accompanies this drop and subsequent metallographic examination shows the sample to contain numerous twins. For intermediate aging times, a number of smaller twin bursts follow the initial large one. The total plastic strain associated with the twinning mode of deformation can be obtained by adding up the contributions AE~ from all i twin bursts, i.e., £,¦££,-, in the manner illustrated schematically in Fig. 2. The contraction of the specimen, as measured from the strip chart of the Instron, after suitably correcting for the elasticity of the machine, was converted into true strain using the assumption that there was no volume change and that the sample remained cylindrical. The dashed lines are all drawn parallel to the

Jan 1, 1970

By Harry C. Swanson

TRANSPORTING concrete from mixer to forms has always been a problem. Twenty-five years ago this task was generally accomplished by means of wheelbarrow or concrete buggy. On large dam jobs, as the number of these projects increased, the gantry crane or highline came into use. Today several methods of handling concrete are employed on smaller surface construction jobs, for example, transit-mix trucks or dumpcrete trucks, which have crawler cranes with buckets for placing concrete into forms. In 1944, during early stages of developing Mather mine A shaft, several large underground concrete jobs were necessary. At this time the Cleveland-Cliffs Iron Co, purchased the first pump-crete machine, introduced by the Chain Belt Co. of Milwaukee. The machine was used to pour approximately 200 cu yd of concrete for a dam, or bulkhead, located 400 ft from the shaft. Concrete was mixed on surface, lowered down the shaft 1000 ft in a 2-cu yd bucket hung under one skip, spouted into the bowl of the pumpcrete machine from the bucket, and pumped directly into the forms. Since the day of the first pipeline concrete in 1944 to the present time, other equipment and other methods have been developed to permit transportation of concrete by pipeline through vertical and horizontal distances totaling 1 mile from mixer to forms. Much of the efficiency in present handling of underground concrete can be credited to the Bethlehem Cornwall mines, where concrete was transported through 6-in. pipe for great distances down an inclined shaft and along levels into forms.&apos; During initial development of Mather mine B shaft, with concrete work under way on two or more levels at one time, the pneumatic concrete placer, Fig. 1, was selected as best adapted for underground concrete transportation. The 3/4-cu yd pneumatic placer is a small machine readily moved from one location in the mine to another. It can be equipped with two sets of mine car wheels, which will permit moving on regular mine tracks. It is therefore possible to send concrete through the pipe at great velocity; the pipeline is clean after each shot except for the film of cement adhering to the inside. With the proper slump in the concrete, it is possible to shoot concrete 2000 ft with this machine, using the mine supply of compressed air at 95 psi. This equipment was first used at Mather mine B shaft to concrete slusher drifts, Figs. 2 and 3, and finger raises located about 2000 ft from the shaft. In several instances there were bends into crosscuts and up vertical distances into the forms. For the first pours two placers were used. The first was located near the shaft where the concrete could be spouted into it from a 2-cu yd concrete bucket on the cage. The second was set on the side of the drift at a point approximately 1500 ft from the shaft. The concrete was shot directly into the second placer from the first unit and from the second machine directly into the forms. After completion of several pours with the two machines, a trial pour with only one placer located at the shaft proved that the second placer could be eliminated. Since then all pours have been successfully completed with only one placer underground. As production of iron ore from the mine increased and the development program expanded, use of the cage for handling mine supplies and concrete became a major problem. This brought about the first attempt at shooting concrete vertically down the shaft for 2600 ft. A 6-in. pipeline with victaulic couplings installed during shaft sinking was used for the trial. One placer was set on surface 250 ft from the collar of the shaft so concrete could be spouted directly into it from the mixer. This machine shot the concrete 250 ft horizontally on surface to the shaft, 2600 ft vertically down the shaft, and 100 ft horizontally into the second placer located near the rib of the shaft station or plat. The second machine shot the batch into the forms, about 2000 ft. Total distance horizontally and vertically was 4800 ft. The entire time cycle for a ¾-cu yd batch of concrete from the mixer on surface to the forms underground totaled about 5 min. During the past two years the two-placer method from the mixer on surface to the forms underground has proved a very efficient means of transporting underground concrete. Advantages of using pipeline concrete are as follows: 1—Interference with normal mining operation is eliminated. When the cage, skips, mine cars, or mine openings are used for transporting concrete and materials used for making concrete, mine operation suffers in one way or another.

Jan 1, 1955

By W. W. Anderson, S. Razi

Electroluminescetrce of single crystals of terbium-(loped ZnS prepared by vapor-transport technique shows the sharp line specirum characteristic of the 4f— 4ft,ansitiotzs of the trivalent Tb3 rotz. V-I tt~easuverr~ents give evidence of space-ellarge-lirrlited curvent but the thrveshold for trap-filled law behavior is not iu agreement with Lampert&apos;s theory for. Single injection. Variations of &apos;brightness with applied voltage, the observation of double peaks its brightness because joms, and the spatial distribution oi electroLur?zir~escerrce indicate that the accelet~atiotz-collision mechanism involving the bst lattice and/ov shallow traps is most likely to be responsible fov excitation of&apos; electrolnminescence. Efficiency rtreusuver)~etits show the quantwn efficiency to be about 10 pct and powev efficiency about 0.05 pct. Effect of anr~eallng the crystal in sulfur vapor is to enluztzce llle rare-earth emission. It rs pvoposed tlzat sulfitv anr~ealing crreates acceptorr-lvpe defects with which the donor-type vare-eavtll ion can associate more readily vesulting in enhanced rare-earth emission. A&apos;o such e~zlznr~cerr~etrt is obserued when the crystal is atztrealetl in zinc vapor. Photolianinescence of ZnS doped nith a variety of rare earths also shows tile slurvp l~rze rwve-eavtlz erriission which in sorrretirr~es accompanied by broad band, stvuctureless lattice emission. Photo-atrd electrolutr~itzesce?~ce of ZIIS:Tb slw~rj do!rlit~unt rare-earth emission in the ~ticirzity of 54(3OA corre-sporrdit~g to the transition D* — Fj. Hoz~!el)er, the detailed line structuve of the luo spectvtr is cliffevet~t, irzdicutit~g that different sites are active in the two processes. Decay of rave-eartlr fluorescence in ZnS doped with any of sei!evul vuve eurtlzs car1 be described by a single exporleritial e.scepl joy ZrlS:lIo. Tl~is exceptiotr can be explaitred it~ tevrr~s of tlre closely spaced er~evgy 1e1:els Jov the HO~&apos; iorr. Decay lime measurertzekzts jov ZnS:Tb, using pulsed elect,-ical ar~d pulsed opticcll excitutiorzs, (11-e itz goor1 agrcetrier~t. LUMINESCENCE of rare-earth-doped materials has been a subject of interest for the past 20 years. Within the past few years there has been a considerable increase in rare-earth research motivated in search of new and more efficient laser materials and also due to the use of certain-rare-earth compounds in the preparation of color television screens. The purpose of this study has been to seek an understanding of some of the basic processes involved in exciting the rare-earth luminescence which is associated with transitions within the 4f shell of the trivalent rare-earth ion. Single crystals of ZnS doped with a variety of rare-earth ions have been prepared by vapor-transport technique described elsewhere.&apos; Photoluminescence was excited by a high-pressure short-arc mercury lamp together with suitable glass and chemical filters. For electroluminescence, sinusoidal and pulse excitations were used. 1) ELECTRICAL CHARACTERISTICS 1.1) V-I Measurements. Electroluminescence experiments were performed on crystals of terbium-doped ZnS. The samples were cleaned and etched and indium or In-Ga alloy contacts were alloyed on by heating in H2 atmosphere to 600°C for times ranging up to 10 min. Static voltage-current measurements were made on several samples. Fig. 1 shows the results for a typical sample. For voltage V < 20 v, the V-I relationship is linear giving a resistivity of 2.5 x 109 ohm-cm for this particular sample at room temperature. In the range of 20 to 250 v, I varies as V "3 and at still higher voltages (when electroluminescence is visible to the scotopic eye) current varies as Vs up to 600 v, all at room temperature. At 77"K, for V > 200 v, / I vge5 up to 1000 v. The V-I characteristics at room temperature follow reasonably well the behavior predicted by Lampert&apos; for one carrier space-charge-limited current in an insulator with traps although, as shown later, the expression derived by Lampert2 for the threshold for trap-filled law behavior Vtfl yields an unrealistically low value for trap density if we use the experimental value of 300 v for VtfL. Assuming the case for shallow trapping, the transition from Ohm&apos;s law behavior to space-charge-limited behavior occurs at voltage Vtr given by where no = thermally generated free carrier density, L = length of the sample, e = static dielectric constant, 6 = ratio of free to trapped electron densities, e = electron charge. For the ZnS:Tb crystal, L = 0.5 mm, E = 8.3 €0, Vtr - 20 v, and no = 5 x 10&apos; per cu cm, calculated from the ohmic behavior assuming electron mobility of 100 sq cm per v-sec. This results in 9 = 0= As more and more electrons are injected the Fermi level moves up in the forbidden gap toward the conduction band. If we assume a single-energy level for traps (which is not strictly correct, as we will show later), the current voltage characteristic is profoundly affected when the Fermi level crosses the trap level. The traps are now filled and injected carriers can no longer be immobilized in traps. Hence, current rises sharply with voltage. The transition from space-charge-limited behavior to the trap-filled behavior occurs at voltage VTFL given by

Jan 1, 1968

By N. F. Dyson, T. R. Scott

The iilzfluence of catalytic agents on the oxidation of ZnS has been studied under pressure leaching conditions, using a chemically prepared sample of ZnS which was substantially unreactive on heating at 113°C with dilute sulfuric acid and 250 psi oxygen. Nurnerous prospective catalysts were added at the ratio of 0.024 mole per mole ZnS in the above reaction but pvonounced catalytic activity was confined to copper, bismuth, rutheniuwl, molybdenum, and iron in order of. decreasing effectiveness. In the absence of acid, where sulfate was the sole product of oxidation, catalysis was exhibited by copper and ruthenium only. Parameters affecting the oxidation rate were catalyst concentration, temperature, time, oxygen pressure, and a7riount of acid, the first two being most important. The main product of oxidation in the acid reaction was sulfur, with trinor amounts of sulfate. An electrochemical (galvanic) mechanism has been suggested for the sulfuv-forming reaction, whereby the relatively inert ZnS is "activated" by incorporation of catalyst ions in the lattice and the same catalysts subsequently accelerate the reduction of dissolved oxygen at cathodic sites on the ZnS surface. Insufficient data was obtained to Provide a detailed mechanism for sulfate fornzation, which is favored at low acidities and probably proceeds th&apos;rough intermediate transient species not identified in the preseni work. THE oxidation of zinc sulfide at elevated temperatures and pressures takes place according to the following simplified reactions: ZnS + io2 + H2SO4 — ZnSO4 + SG + HsO [i] ZnS + 20,-ZSO [21 In dilute acid both reactions occur but Reaction [I] is usually predominant, whereas in the absence of acid only Reaction [2] can be observed. Both proceed very slowly with chemically pure zinc sulfide but can be greatly accelerated by the addition of suitable catalysts, as suggested by jorling&apos; in 1954. Nevertheless, an initial success in the pressure leaching of zinc concentrates was achieved by Forward and veltman2 without any deliberate addition of catalytic agents and it was only later that the catalytic role of iron, present in concentrates both as (ZnFe)S and as impurities, was recognized and eventually patented.3 It is now apparent that another catalyst, uiz., copper, may have also played a part in the successful extraction of zinc, since copper sulfate is almost universally used as an activator in the flotation of sphalerite and can be adsorbed on the mineral surface in sufficient amount The importance of catalysis in oxidation-reduction reactions such as those cited above has been emphasized by various writers and Halpern4 sums up the situation when he writes that "there is good reason to believe that such ions (e.g., Cu) may exert an important catalytic influence on the various homogeneous and heterogeneous reactions which occur during leaching, particularly of sulfides, thus affecting not only the leaching rates but also the nature of the final products." Nevertheless relatively little work has appeared on this topic, one of the main reasons being that sufficiently pure samples of sulfide minerals are difficult to prepare or obtain. When it is realized that 1 part Cu in 2000 parts of ZnS is sufficient to exert a pronounced catalytic effect, the magnitude of the purity problem is evident. An incentive to undertake the present work was that an adequate supply of "pure" zinc sulfide became available. When preliminary tests established that the material, despite its large surface area, was substantially unreactive under pressure leaching conditions, the inference was made that it was sufficiently free from catalytic impurities to be suitable for studies in which known amounts of potential catalytic agents could be added. The first objective in the following work was to identify those ions or compounds which accelerate the reaction rate and, for practical reasons, to determine the effects of parameters such as amgunt of catalyst, temperature, time, acid concentration, and oxygen pressure. The second and ultimately the more important objective was to make use of the experimental results to further our knowledge of the reaction mechanisms occurring under pressure leaching conditions. The fact that catalysts can dramatically increase the reaction rate suggests that physical factors such as absorption of gaseous oxygen, transport of reactants and products, and so forth, are not of major importance under the experimental conditions employed and an opportunity is thereby provided to concentrate on the heterogeneous reaction on the surface of the sulfide particles. As will appear in the sequel, the first of these objectives has been achieved in a semiquantitative fashion but a great deal still remains to be clarified in the field of reaction mechanisms. EXPERIMENTAL a) Materials. The white zinc sulfide used was a chemically prepared "Laboratory Reagent" material (B.D.H.) and X-ray diffraction tests showed it to contain both sphalerite and wurtzite. The specific surface area, measured by argon absorption at 77"K, varied between 3.9 and 4.6 sq m per g. Analysis gave 65.0 pct Zn (67.1 pct theory) and 31.9 pct S (32.9 pct theory). Other metallic sulfides (CdS, FeS, and so forth) used in the experiments were also chemical preparations of "Laboratory Reagent" grade. Samples of mar ma-

Jan 1, 1969

By Marcus A. Grossmann

The Institute has established this lectureship to honor the memory of a great American metallurgist, one whose fame has continued long after his passing. As one scientist recently stated it, "All metallurgical texts gradually become outdated and outmoded, except those of the great Henry Marion Howe." It seems fitting, then, that, once every year, we shouId review, in his honor, some aspects of the science in which he was such a distinguished leader, and also discuss any new data that may help to clarify our concepts. It is my privilege, for which indeed I express the deepest appreciation to this Institute, to offer for consideration a few thoughts on the toughness and fracture of hardened steels. Before proceeding to the data, I wish to express my great indebtedness to many associates whose stimulating discussions, generous contributions of data and cooperation in experiments are gratefully acknowledged. (But I wish to absolve them of any blame that may arise from the way in which their discussions and data have been used!) First, Dr. Edgar C. Bain, Vice President, Carnegie-Illinois Steel Corporation, whose amiable but merciless criticisms and always constructive and thoughtful suggestions help unfailingly to guard against pitfalls. Then to associates at Gary Steel Works, especially Mr. H. B. Wishart, Mr. W. K. Smith and Mr. V. Elliott, for great assistance in securing data. Also to Col. C. H. Greenall, Director of Laboratories, Frankford Arsenal, and his metallurgical staff, including Messrs. J. K. Desmond, H. Markus, D. F. Armiento, H. Rosenthal and Henry George, for numerous data and illustrations. Further to Dr. J. R. Low and Dr. M. Asimow, for helpful discussions of effects of states of stress during deformation and rupture, to Mr. J. M. Hodge for discussions and data, to the staff of the U. S. Steel Corporation Research Laboratory for advice and data, and to the Metallurgical Staff at Duquesne Steel Works. The individual acknowledgments will also be found under illustrations. Acknowledgment is also due to Mr. S. C. Snyder for incredibly meticulous scrutiny of manuscript. To all of these, grateful thanks. Introduction The discussion to be offered here will deal with quench-hardened steels only, and may perhaps be considered under three headings: 1. It was found that, when ferrite was precipitated in the (prior austenite) grain boundaries of hardened steel, the notch-bar toughness was much less than in pieces fully hardened. The fracture took place in the ferrite, and the loss in toughness is attributed to the lower cohesive (cleavage) strength of the ferrite, as cornpared with martensite. 2. When notch-bar impact test pieces of quenched and tempered steels were examined as to their mode of fracture, it

Jan 1, 1947

By Marcus A. Grossmann

The Institute has established this lectureship to honor the memory of a great American metallurgist, one whose fame has continued long after his passing. As one scientist recently stated it, "All metallurgical texts gradually become outdated and outmoded, except those of the great Henry Marion Howe." It seems fitting, then, that, once every year, we shouId review, in his honor, some aspects of the science in which he was such a distinguished leader, and also discuss any new data that may help to clarify our concepts. It is my privilege, for which indeed I express the deepest appreciation to this Institute, to offer for consideration a few thoughts on the toughness and fracture of hardened steels. Before proceeding to the data, I wish to express my great indebtedness to many associates whose stimulating discussions, generous contributions of data and cooperation in experiments are gratefully acknowledged. (But I wish to absolve them of any blame that may arise from the way in which their discussions and data have been used!) First, Dr. Edgar C. Bain, Vice President, Carnegie-Illinois Steel Corporation, whose amiable but merciless criticisms and always constructive and thoughtful suggestions help unfailingly to guard against pitfalls. Then to associates at Gary Steel Works, especially Mr. H. B. Wishart, Mr. W. K. Smith and Mr. V. Elliott, for great assistance in securing data. Also to Col. C. H. Greenall, Director of Laboratories, Frankford Arsenal, and his metallurgical staff, including Messrs. J. K. Desmond, H. Markus, D. F. Armiento, H. Rosenthal and Henry George, for numerous data and illustrations. Further to Dr. J. R. Low and Dr. M. Asimow, for helpful discussions of effects of states of stress during deformation and rupture, to Mr. J. M. Hodge for discussions and data, to the staff of the U. S. Steel Corporation Research Laboratory for advice and data, and to the Metallurgical Staff at Duquesne Steel Works. The individual acknowledgments will also be found under illustrations. Acknowledgment is also due to Mr. S. C. Snyder for incredibly meticulous scrutiny of manuscript. To all of these, grateful thanks. Introduction The discussion to be offered here will deal with quench-hardened steels only, and may perhaps be considered under three headings: 1. It was found that, when ferrite was precipitated in the (prior austenite) grain boundaries of hardened steel, the notch-bar toughness was much less than in pieces fully hardened. The fracture took place in the ferrite, and the loss in toughness is attributed to the lower cohesive (cleavage) strength of the ferrite, as cornpared with martensite. 2. When notch-bar impact test pieces of quenched and tempered steels were examined as to their mode of fracture, it

Jan 1, 1947

LIST OF MEMBERS AND ASSOCIATES ARRANGED ACCORDING TO STATES AND TOWNS ALABAMA Aldrich, Aldrich, W F Anniston, Noble, A E, Smith, N B Aibacoche, Bradley, D II Bessemer, Fergusson, V Birmingham, Aldrich, T H, Aldrich, T H, Jr, Bowron, J, Bowron, C E, Davis, F H, Dimmick, F D, Hillman, McCarthy, M E , McCormack, McCrery, Ramsay, E, Shook, A M Bridge¬port, Wheeler, S K Ensley, McDonald, S, Shook, J W Fanbanks, Hamil¬ton, A L Helena, Squire, J Huntsville, Moss Lehigh, Toulmin Oxmoor, Green¬amyer, A G Plasma, Gage Rock Run, Garvin Sheffileld, Miller, D I Tuscaloesa, Lodge, J University, McCalley Woodward, Bukofzer, Woodward, A H ALASKA Dawson, Buck Douglas Island, Corbus, J P , Macdonald, J Hames, Le Wald, E A Jualin, Hoggatt, W B Juneau, Denby, Gaifield, Garside, Hamp¬ton, W H Rodman Bay, Phillpots Snettisham, Tisdale Sumdum, Thane Tel¬ler, Hirshberg, M R Treadwell City, Batcheller, J H , Kinzie Valdez, Esterly, G M Yukon, Dawson, Elmer, J M ARIZONA Bisbee, Clark, G C, Coombs, H L , Douglas, W, Hoatson, Parnall, S A, Pelton, R T, Ricketts, L D, Sherman, G F G, Smith, F W, Smith, H A Black Diamond, Bagge Blanchard, Cummins, Murray, J J Casa Grande, Rich¬mond, A B Clifton, Colquhoun, Grabill, Murray, H T , Plater, Smith, J D A, Veitch, Watson, W S Congress, Goodloe Crown King, Alexander, G E Douglas, Cornell, Kraemer, E L, Lee, G B, Rutherford, F Globe, Berray, Hoar, Snell Harrisburg, Smith, F C Jerome, Clark, W A, Thomas, C A Kingman, Treadwell, Wallace, J P Kirkland, Bretherton, G K Kofa, Lamp¬shire, J O , Pomeroy, H G Mayer, Haggott, E A Metca j, Blumenkranz, M , Forbes, D L H Morenca, Clark, C D, Fleming, J B, Honey man, Mills, C E, Wallace, L R Morristown, Stevens, H W Nogales, Glove, H G, Sandoval, A , Sandoval, P Octave, Rose, G W Phoenix, Armstrong, T , Butler, C E, Defty, Lindsay, L Prescott, Blauvelt, H , Bunker, C E, Claypool, W M , Drescher, F M , Fairbank, Nissen Tombstone, Gage, Poindexter, C L , Staunton, Walker, E W Troy, Cutting Tucson, Blake, W P, Burgess, De Lashmutt, I, McCleary, Mann, Prout, J W , Jr ARKANSAS Fayetteville, Purdue Fort Smith, Bache, F , Denman, H Little Rock, Fordyce, Scholz CALIFORNIA Alameda, Arents, King, L Arnador City, Downs, Tregloan Angeles Camp, Dig¬gles, R N , Kenney, C E Antioch, Belshaw Auburn, Coe, I J Ballarat, Thorns Berkeley, Abadie,, Christy, Dozier, Hall, F F , Hersam, Landfield, Lind¬say, L , Mansfield, N T, Morley, W S , Sharwood, W J Bag Oak Flat, Dron Bodae, Hamilton, W R, Hoover, T, Hoover, T J, Jackson, B L , Nutter , E, H Bullion, Power, H T Callahan, Scott, E H Campo Seco, Baird Cartero,

Jan 1, 1910

By C. J. Osborn

The temperature dependence of the free energies of formation of metallurgically important oxides, sulphides, chlorides, carbonates and sulphates is presented graphically, whereby the task of deriving practical metallurgical information is greatly simplified. The diagrams have been revised according to the latest available thermodynamic data. WHILE it is true that much careful investiga-tional work remains to be done, there are already available in the literature sufficient thermo-dynamic data to enable the metallurgist to predict with reasonable confidence the equilibrium conditions to be expected in most important, and potentially important, metallurgical reactions. In this connection, the careful, critical compilations of K. K. Kelley and his collaborators in numerous U. S. Bureau of Mines Bulletins are particularly valuable. However, the translation of reliable thermo-dynamic data into metallurgical language unfortunately involves lengthy manipulations of the cumbersome formulas which can be set up from heat of formation, entropy, and heat capacity data. Many years ago, Kelley20 predicted that thermo-dynamic calculations would be made in the future "with the aid of free energy, heat content, and entropy tables, rather than by means of the algebraic methods employed at present", and where such tables are available they greatly simplify the task of deriving practical metallurgical information. However, in addition to these tables, there are also available one or two reliable graphical presentations, particularly of free energy data, which may be used in the same way as the tables, but which have the added advantages that interpolation is never necessary, and that the behavior of different metals or compounds may be compared at a glance. Some years ago Professor Robert Lepsoe, Head of the Department of Metallurgy at Norways Institute of Technology (N.T.H.), began a compilation of curves showing the temperature dependence of the heat contents of the elements, and the heat contents and heats and free energies of formation of the common metallurgical compounds. With such a compilation, the thermal and free energy requirements of a reaction may be read from curves in a matter of seconds; and this statement applies not only to the formation of compounds from their elements, and to the reverse dissociation, but to any reaction involving substances whose thermodynamic properties are available. This follows from the fact that heats and free energies of formation are completely additive. For example, the free energy change associated with the chlorination of a metallic oxide at any temperature, T, is given by the free energy of formation of the chloride at temperature T minus that of the oxide also at T; both of these quantities may be read directly from curves of the type suggested above. Since this early, unpublished work of Lepsoe, both Ellingham7 and Richardson and Jeffes46 have

Jan 1, 1951

By P. Chiotti, J. T. Mason

Metallographic, thermal, X-ray, and vapor-pressure data were employed in establishing the Ce-Zn phase diagram. Nine compounds and three eutectics were observed. The eutectic compositions in weight percent zinc and temperatures are 10 pct and 495"C, 37 pct and 795°C, and 56 pct and 810°C. Three of the compounds, CeZn, CeZnn, and CeZne.5, melt congru-ently at 825°, 87.505°, and 980°C, respectively; the other six compounds, CeZns, CeZns.67, CeZn4.5, CeZn5.25, CeZn,, and CeZnll, decompose peritectically at 820°, 840°, 870°, 885", 960°, and 795"C, respectively. The compound CeZn5.25 is an AB5 type with a small range of composition which lies on the zinc-rich side of the 1 to 5 stoichiometry. Zinc vapor-pressure data obtained by the dewpoint method were employed in calczilating the thermodynamic properties of both the liquid alloys and solid compounds. The data for the A critical review of the information available on the Ce-Zn system up to 1960 has been given by K. Gschneidner, Jr.&apos; Of particular interest is the work by J. schramm2 who investigated the region between 55 and 100 wt pct Zn and reported a CeZn,, compound which decomposes peritectically at 785"C, a CeZn, compound which melts congruently at 972"C, and five temperature horizontals at 79@, 817", 840", liquid alloys were fitted to the relation from which the relation was obtained by integration. In these relations F XS is the excess partial molal free energy, N is atom fraction, and the constants c and d have the values c = (-22,000 + 7.0T) and d = 6171,000 + 74.0T). Relations for the standard free energy of formation for the solid compounds were derived from the data. At 973°K the enthalpy in kilocalories per gram-atom z)aries from —11.3 for CeZnz to —8.21 for CeZn~l and the free energy in the same units varies from —7.1 joy CeZn, to -3.82 for CeZn11. and 942°C in the region between 55 and 75 wt pct Zn. No attempt was made to identify other features of the system. I. Johnson and R. yonko3 used a fused-salt cell to measure the electromotive force between pure cerium and an alloy consisting of zinc-rich liquid in equilibrium with CeZnll. Solubility data for cerium in zinc has been reported by J. Knighton et u1 .4 Johnson and Yonko give the following equa-. tions for the mole fraction of cerium in zinc and the standard free energy of formation of CeZnll:

Jan 1, 1965

By C. G. Dunn

IDENTIFICATION Of the kinds of orientation relationships that may exist among crystals is an important problem in the metallurgical field. As an aid to its solution standard orientations of several orders of twins would be very useful for rapid analyses to discover high-order as well as low-order twin relationships. Although data have been published that give orientations for three generations of twins, these data are not readily useful in the form presented; i.e., in a stereographic projection with one pole per orientation.1 However, accurate data based on calculations of the positions of all {100} planes for such groups would be very useful when presented in tabular form. Therefore, calculations have been made for a group of four orders of twins and the data are listed in Table 3. Illustrative applications are considered briefly, with the idea of pointing out what may be done with large groups of orientations. METHOD OF COMPUTING ORIENTATION OF A TWIN It is common practice to describe the orientation of a crystal in terms of the positions on a stereographic net of the poles of certain planes of the crystal. A single position on a net may be given it terms of two angle variables, two sets of which appear in the following equations: [Polar NetWalff Net x=rsinOocos4pyx=rcos0. y=rsinB,sin4,ny-rsin0.cos¢,, z=rcos0,,z=rsin0.sin4,,] The three numbers x, y and z determine a length r as well as a direction [(0, 0)] in an X, Y, Z coordinate system. In the present case, r will be set equal to (h2 + k2 +12)1/3, where h, k and 1 are the usual Miller indices for a crystallographic plane, a restriction that facilitates determination of the positions of poles of new planes from those of old or known ones,2 as will become evident later. Furthermore, since twinned lattices have certain planes in common, it is an easy matter to determine the orientation of a twin of a crystal if the orientation of the crystal itself is known. We start therefore with a crystal of known orientation (positions of three {100} poles given) and determine where the cube poles occur in first, second, third and fourth-order twins. Methods for identifying twinned lattices and for making the calculations to find the orientation of a twin have been published.3 4 Reference 4 will be illustrated in the calculation of the orientation of a twin, even though this method differs from the one used by the writer in obtaining the following data on four orders of twins. Consider a crystal S and its twin A1, A1 being one of the four {112} or {III}

Jan 1, 1945

By Fred C. Bond

AN improved method of measuring the surface area of a comminution product down to any desired particle size has been developed. The method is largely graphical, and requires relatively little calculation. It can be used with materials containing large amounts of clay, or excess fines of any kind. The surface area S is expressed in terms of square meters per 100 c.c. of solids. This expression is based upon volume rather than weight, and is considered to be more suitable for crushing and grinding problems, where the machines ordinarily are operated under constant volume conditions. It has the advantage that surface areas of different materials can be compared directly, even though their specific gravities may be unknown. The "specific surface" of a material, or the number of square centimeters of surface area per gram, is equal to 100S divided by the specific gravity. Particle diameters are expressed in microns, K being the diameter of the largest particle present and L the grind limit, or lower size limit of the particles formed directly by grinding. The value of K does not always coincide exactly with the diameters of the largest particles retained on the coarsest testing sieve, since the largest particles formed in crushing and grinding are often slabby, or have other irregular shapes. L has been chosen as 0.700 microns, or number 27.5 in the size number series, for reasons to be explained later. S is the total surface area of all particles larger than L microns in diameter. When a homogeneous comminution product is separated into fractions whose diameters bear a constant geometrical relationship p to each other, and the log per cent weight retained upon each size and passing the next larger size is plotted against the log diameter, a straight line results, which is called the distribution line, and which has a slope in called the distribution modulus. The distribution line can be extended to any desired limiting size, and the total surface area of all particles larger than that size can be calculated. The equation of the distributi0n line is [w = Cx" [I]] where w is the per cent weight retained on each successive sieve; x is the particle diameter; and C is the per cent weight retained on an opening of unit diameter.2 Theoretically, the distribution line can be extended to include infinitely small particles. When it is so extended, and the assumption is made that no fine particles are present other than those accounted for by the equation; the log per cent cumulative weight passing any series of sizes, plotted against the log diameter passed, will result in a straight line lying parallel to and above the plotted distribution line.

Jan 1, 1941

By P. Chiotti, G. R. Kilp

IN the study of zinc-zirconium1 and zinc-uranium2 systems, vapor-pressure measurements were made in order to establish the equilibrium phase diagrams for a pressure of 1 atm. In each of these systems, only zinc has an appreciable vapor pressure over the temperature range investigated. The zinc pressure was measured over a sufficiently wide temperature and composition range to permit calculation of the standard free energy, enthalpy, and entropy of formation for the compounds ZrZn, ZrZn2, ZrZn3, ZrZn6, ZrZn14 , and U2Zn17. In these calculations the compounds were treated as line compounds. Although the exact composition range was not determined, metallographic and thermal data indicate that the solubility range for these compounds is small. It is to be noted that the compound initially reported to correspond to the formula UZn9, 2 has been shown by the crystal structure work of Makarov and vinogradov3 to correspond to the formula U2Zn17,. The crystal structure is similar to that for the compounds Th2M17, investigated by Florio,4 et al; here M represents iron, cobalt, or nickel. Therefore, thermodynamic calculations are based on the formpla U2Zn17 EXPERIMENTAL The dew-point method employed to measure the vapor pressure of zinc over uranium-zinc alloys has been described previously.2 The same procedure and apparatus were used in measuring the zinc pressure over zinc-zirconium alloys. In the case of alloys in the two-phase region consisting of a zirconium and the compound ZrZn, the Knudsen effusion method was employed to obtain a few values in the temperature range 600" to 560°C. In most cases, tantalum crucibles were used to contain the zirconium alloys. THERMODYNAMIC PROPERTIES OFU2Zn17 A least-squares treatment of the vapor-pressure data obtained for 35 and 65 wt pct U alloys in the temperature range 650° to 940°C gave lOg10PAtm = 7,713/T + 6.33 Here, as in following equations, T represents degrees kelvin and P represents the zinc vapor pressure in atmospheres. The probable errors for the two constants were calculated to be 60.68 and 0.0563, respectively. This relation represents the equilibrium dissociation pressure for the reaction U2Zn17 (s) - 2U(s) + 17Zn(v) The solubility of zinc in solid uranium is negligible and the only additional information required to calculate the free energy of formation of U2Zn17 is the free energy of vaporization of pure zinc. K. K. Kelley5 gives the relations, AF°= 30,902 + 6.03Tlog T + 0.275 X 10-3T2 - 45.03T

Jan 1, 1961