By Wei Luo, Yuanbo Zhang, Zhixiong You, Zijian Su, Guanghui Li, Tao Jiang

"In this study, the appropriate sintering process parameters for low-grade ferromanganese ores were investigated. The results showed that, under the condition of natural basicity (R=0.03), the optimal parameters were obtained as follows: moisture of mixture 9 .1 %, coke powder 9 .9% and sintering negative pressure 7 KPa. And the corresponding yield, ISO tumbling index and utilization coefficient reached at 80.18%, 61.27% and 1.515t·m-2·h-1, respectively. Under the optimal parameters, the emission of harmful gases, such as S02 and NOx, were reduced evidently with 30% of coke powder replaced by biomass charcoal. Moreover, it was found that the basicity had obvious effects on the quality of the sinters when it changed between 0.03 and 2.4. The ISO tumbling index gradually decreased from 61.27% to 55.47% with the basicity increasing from 0.03 to 1.2, then, it began to increase after the basicity further increased to 2.4.IntroductionManganese is mainly consumed by steel and battery industries, particularly in the steel plants and ferroalloy units. The consumption of metal manganese in the ferroalloy industry accounts for 85%-90% of the total Mn [1-2]. Therefore, ensuring sufficient manganese alloys is essential to meet the rapid development of steel industry. Recently, rich-manganese slag containing high grade Mn (>40%), low Fe (1%) and P (<0.03%) is considered as superior raw materials for manganese alloys. While the sinters made from manganese ores are major raw materials for producing rich-manganese slag with the increasing exhaustion of natural rich manganese lump ores [3-5]."

Jan 1, 2013

By P. A. Rusin

Many manganiferous silver deposits remain undeveloped because standard chemical extraction methods yield poor recoveries or are &apos; environmentally unacceptable. Biotreatment of such ore deposits in our laboratory resulted in manganese and silver recoveries of greater than 90%. Ore and sediment samples were collected from mining sites in Colorado and Arizona. Portions of samples were incubated in a semi-solid mineral salts medium amended with 20 mM glucose mid manganese dioxide (Mn medium). The cultures were incubated at 3(fC until manganese reduction was detected by a .color change fr:om .black to clear. Bacteria from these cultures were purified on Tryptic Soy Agar and individual isolates were retested for Mn reduction by an agar overlay method. Bacteria were identified according to Bergefs Manual ?of Systematic . Bacteriology. Most of the Mn-reducing bacteria are Bacillus species. Bacterial manganese reduction kinetic experiments were performed in 52 ml mineral salts broth supplemented with manganiferous silver ore instead of manganese dioiide. These cultures were incubated with agitation for 16 d. Aliquots were removed periodically and analyzed for solubilized manganese by atoniic absorption (AA). Cyanide (1,0 M) Vias added to the remaining ore-medium mixture for a 24 h bottle roll. The supernatant was analyzed for soluble silver by AA. Similar experiments were conducted on a larger scale using 15% pulp density. After bfotreatment of the ore, standard bottle rolls were performed. The pregnant solutions and the residues were analyzed for manganese and silver?using AA or fire assay as appropriate. In sterile. controls-which received no biotreatment, manganese and silver recoveries were 0.3% and 10% respectively; During biotreatment, total manganese solubilizatiori was as high as 99.8%. The reduced manganese could . be stripped from ?the growth medium using hydrometallurgical techniques. Silver recovery vaned from 70% to 92.5%. Microbial treatment of refractory mangairlferous ores can result in high recoveries of manganese and silver. Retention time varies depending upon the relative concentrations of manganese, silver, and other metals in the ore with only two days required in some cases, The biotreatment of ore is environmentally&apos; acceptable while the use. of chemicals such as sulfur dioxide is less so.

Jan 1, 1991

By Xiaobing Yang, Animesh Jha, Greg Doughty

"Successful use of inert anodes should reduce the CO2 footprint in aluminum production. The search for a “holy grail” inert anode for metal electro-winning from constituent oxides using molten salt bath as an electrolytic medium is continuing. In this article we demonstrate the engineering approaches for the fabrication of intermetallic anodes, based on a quaternary Al-Ti-Cu-M (M:Ni, Fe) system for primary aluminium production. In particular, we examine the microstructural and electrochemical properties of alloys, based on the quaternary compositions. We explain the aspects of phase stability under anodic potential, which leads to the loss of anodic materials in the temperature range of 850-1050oC. The results are analysed in the context of oxidation reaction and formation of oxide layers which readily dissolve in the cryolite melt and prevent passivation. The paper also describes the conditions under which the reduction of aluminium at the graphite cathode occurs which also strongly depends on the molten salt chemistry for the nucleation of molten aluminium at the cathode.1. IntroductionOxygen-evolving inert anodes are an alternative to the conventional consumable carbon anodes for the production of primary aluminium. In this paper the materials selection criteria chosen for the engineering of anode is based on the understanding of the thermodynamic stabilities of aluminide intermetallic phases, some of which are formed and remained stable in fluoride melts. For example, the formation Al3Ti dispersed in aluminium metal via molten-fluoride flux reaction is well known in the context of aluminium casting and grain refining [1-3]. It is for this reason in our research we concentrated on the engineering of stable intermetallic phase mixture in the Al-Ti-Cu ternary system, shown in Figure 1 [4]. In this figure two compositions in the Al3-0.5zTi1-0.5zCuz family are shown with the substitution of 7 atomic % and 11 atomic % copper. However initial investigations showed that these two compositions were unsuitable due to the formation of low-temperature liquid (~540oC) and intermetallic phase, Al2Cu along the Al-Cu binary edge during solidification. The Al2Cu phase segregated along the boundaries of Al3Ti and Al5Ti2Cu, and dissolved away when electrolysis was carried out using these anodes above 800oC. The presence of consequential porosity in the anode material increased the corrosion of the alloy through local heating due to high current density at 0.8 A cm-2. The early tests were carried out with cryolite melts, shown in Figure 2, having 3 weight percent of Al2O3 in the bath at 850oC."

Jan 1, 2010

By Yunnen Chen

This work concerns the removal of zinc(II) and COD by means of sawdust obtained as a by-product from locally used wood. The zinc(II) and COD removal study has been carried out batchwise where the influence of physico-chemical key parameters such as tree species, pH value of solution, temperature and contacting time and dosage of adsorbent have been considered. The maximum percent removal was attained at pH 9 all for Zn(II) and COD after about 60 min. The adsorbent can be effectively desorption using 0.1 M HCl. The experimental results showed that ion exchange maybe the major adsorption mechanisms for binding the divalent metal ions to the sawdust. Sawdust was a potential adsorbent for the removal of Zn(II) from the effluent of electroplating industry.

Jan 1, 2009

By Elli Nurminen

Keywords: Thermal conductivity of sulphates, flash smelting, heat recovery boiler, flue dust Accretions and build-ups in metallurgical heat recovery boilers decrease the efficiency of the heat transfer and may cause process shut downs. Transient plane source method (Hot Disk) has been applied to measure the thermal conductivities of the Copper Flash Smelting flue dusts. Thermal conductivities of copper, iron and zinc sulphates, and process flue dusts were measured. The results indicate that all the components are effective thermal insulators, having a thermal conductivity of less than 1 W/mK. Decreasing dust layer porosity has an increasing effect on thermal conductivity. Insulating layers on the boiler walls decrease greatly the heat transfer efficiency of the boiler. The gathered information will be used in CFD-modelling of the process, and in the process control.

Jan 1, 2005

By Yuzhe Zhang, Matthew Andriese, Jiann-Yang Hwang, Guanghui Li, Zhiwei Peng, Tao Jiang

The microwave power absorption characteristics of iron oxides, including Fe2O3, Fe3O4 and Fe0.925O, have been studied by determining dielectric loss and magnetic loss distributions in 0.05-m-thick oxide slabs irradiated with 1.2-kW, 2.45-GHz microwaves. The results reveal that the dielectric loss is the main factor contributing to microwave absorption in Fe2O3 and Fe0.925O, while the magnetic loss dominates the power absorption in Fe3O4 below its Curie point. Uneven power distributions are observed in the slabs and this phenomenon becomes even worse at high temperatures at which the permittivity increases significantly. Quantification of power absorption in the oxides is of great importance for efficient and uniform microwave heating

Jan 1, 2015

By Chuanfu Zhang

Based on Thermogravimetric and Differential thermal analysis (TGA-DTA), porous copper powder is prepared by thermal decomposition of complicated copper oxalate. The effects of various conditions on the morphology, crystalline grain size and specific surface area of copper powder were investigated, including temperature, duration, mixing ratio of nitrogen and hydrogen. Furthermore, composition and morphologies of the products were characterized by X-ray diffraction (XRD), Scanning electron microscope (SEM) and BET adsorption isotherm. It is found that porous copper powder was produced under optimum conditions. The specific surface area is over 6.74 m2?g-1, and average pore size in particles is about 30.3 nm. After comparison of SEM images, the final product Cu well inherits the morphology of the precursor, thus a mechanism of in-situ decomposition is proposed.

Jan 1, 2009

By Kevin L. Purdy

The Process Technology Center of Phelps Dodge Mining Company (PDMC) .operates several test facilities in support of PDMC&apos;s hydrometallurgical operations. Installations for small leach columns, 15 cm. to 60 cm. (6 in. to 24 in.) in diameter, and large leach columns, 1.8 m. (6 ft.) in diameter, are complemented by a test facility for SX/EW operations. The history of and reasons for the development of these facilities: are described and original standard equipment is discussed. A primary goal in constructing these facilities was achieving a high degree of flexibility to allow for testing of new equipment and new leaching and SX/EW technologies as they are developed. Along with this challenge, construction of a filly integrated SX/EW test facility on a small scale brought its own set of challenges.

Jan 1, 1999

By K. Potluri, S. Akella, S. Bhansali

"This paper presents the design and angular strength analysis of microneedles for use as a transdermal interface for drug delivery, fluid analysis and sampling etc. Microneedles of different dimensions were designed and fabricated using various materials viz. Si02, OxideNitride- Oxide (O-N-0). The design, modeling and analysis was done using the Finite Element Analysis (FEA) software ANSYS™ 6.1. Angular strength analysis of the microneedles was done using angular loading in ANSYS™, with the corresponding inaterial property settings. Using the force-displacement settings, forces of magnitudes in the range of 10 mN - 25 mN were applied on the microneedles at loading angles ranging from 30° to 90° was applied on needles. Square and circular shaped microneedles were modeled and the displacements and stresses generated were studied to characterize the angular strength of the microneedles. The buckling and force-displacement analyses show that O-N-O microneedles are more strong and robust as compared to needles of other materials. The analysis shows that while circular microneedles have uniform stress distribution, square microneedles have low stresses concentrated along the edges.INTRODUCTIONIn modem clinical and biomedical applications, drug delivery is done either by oral administration or by hypodermic injection. Hypodermic injection of drugs using needles is often painful. Hence, transdermal drug delivery techniques are increasingly being sought out as an alternative. In transdermal drug delivery the needles puncture the Stratum comeurn - the outermost layer of the human skin. The advantage of transdermal drug delivery (or transdermal measurement) technique, is that it reduces pain and tissue trauma."

Jan 1, 2004

By M. Radwan

This research reports on the synthesis of advanced silicon-based structural ceramics from mixtures composed of natural sand (Sinai white sand), reclaimed silicon and graphite by the nitriding combustion synthesis method. With pulverized sand (? 40 m), we found that the nitriding combustion can be realized at self-sustaining mode in the SiO2?Si?C system under 3 MPa nitrogen pressure. Depending on the composition of the starting mixtures, single-phase silicon oxynitride (Si2N2O) powder as well as new Si3N4?Si2N2O and Si2N2O?SiC composite powders with controllable chemical compositions were successfully developed. The measured thermograms of various combusted mixtures and the thermodynamic characteristics of possible exothermic reactions in this system were discussed to explain the nitriding combustion behaviour and mechanism. Near-full dense Si2N2O were fabricated from synthesized Si2N2O powder with 5 wt % oxide additive by the spark plasma sintering (SPS) method at 1600 °C. The dense Si2N2O samples had good mechanical properties (18.7 GPa Vickers hardness, 3.3 MPa m1/2 fracture toughness and 363 MPa strength) and excellent chemical and oxidation resistance. The synthesized composite powders were also densified to high densities (> 90 % of theoretical values) by SPS technique. The results obtained in this study can be seen as a new route to prepare important silicon-based structural ceramic powders with various compositions/properties from cheap starting materials which makes them potential for wide range of applications.

Jan 1, 2006

By M. A. Aziz

The electrochemical performance of a series of carbon materials produced from coconut shells, which are very cheap and readily available in Bangladesh was investigated for their viability as anode materials in rechargeable lithium-ion batteries. X-ray diffraction technique was used to measure the interlayer spacing (d002) of the produced carbon materials. A number of half-cells were prepared with the produced carbon materials from coconut shell as working electrode and metallic lithium as counter electrode with 1MLiPF6 electrolyte in a mixture of ethylene carbonate and dimethyl carbonate. The discharge-charge profiles were measured for the different half-cells by using Arbin 24-channel Cyler. The value of interlayer spacing of the coconut-based carbon material was found to be 0.397 nm at 900°C, which is most suitable for lithium-ion insertion into the carbon structure without any expansion. The specific discharge capacity of carbon material from coconut shell heat treated to 900°C was found to be 1015.65 mAh/g. The coconut carbon material heat treated to 900°C delivered 335.22 mAh/g reversible capacity, which is comparable to the commercial carbon/graphite presently used in lithium-ion battery systems. The irreversible capacity loss and coulombic efficiency in 25th cycle of half-cell made with coconut carbon material were found to be 0.16% and 99.83% respectively. The carbon material produced from coconut shell can, therefore, be used as a potential anode for rechargeable lithium-ion batteries.

Jan 1, 2006

By Wei Yu, Tiejun Chun, Jian Pan, Deqing Zhu

In this paper, the technology of producing fluxed pellets by using hydrated lime as binder instead of bentonite was carried out. Green balls with 0.8% bentonite and others with 2% hydrated lime were obtained under the same conditions of 1.5% coke, 1.45 basicity and balling at 8.5% moisture for 13 min in disc pelletizer. The properties of two types green balls were as follows: drop numbers of 4.8 to 5.0 times/0.5m, compressive strength of 19.7 to 24.2 N/pellet and thermal shock temperature of 280 to 385?, respectively. Comparing with bentonite as binder, the compressive strength of fired pellets with hydrated lime is elevated by 13.8% and climbs up to 3113 N/pellet under the following conditions: preheating at 1050? for 10 min and firing at 1300? for 15 min. The hydrated lime also improves the metallurgical performance of fired pellets. The reduction index was enhanced from 68.6% to 70.6%, RDI+3.15 increased from 90.1% to 98.8% and reduction swelling index dropped from 22.4% to 7.4%, respectively. Therefore, hydrated lime can not only replace bentonite as binder to enhance the firing behaviors of green balls, but also effectively improve the metallurgical performance of fluxed pellets which can be used as high quality feed for blast furnace.

Jan 1, 2011

By W. G. Davenport

The flash furnace is used for smelting concentrate to (i) high-Cu matte and (ii) molten metallic copper. It is also used for converting solidified/crushed matte to molten metallic copper. This is flash converting. It consists (Table 20.1, Fig. 20.1) of: (a)tapping molten 65 to 72% Cu matte from a flash smelting furnace (b) granulating the molten matte to ?1/2 mm particles in a 103 m3/hour water torrent (c) crushing the granulated matte to 50 µm in a vertical roller mill (d)drying the crushed matte (e) feeding the dry particulate matte to a second flash furnace for oxidation converting to molten copper. In 2000, flash converting is being used by Kennecott Utah Copper (George, et al; 1995; Newman et al, 1998, 1999a,b). A second installation is being designed for the Chuquicamata smelter (www.outokumpu.com [October 12, 2000]), The potential uses of flash converting are: (a) as the second half of a flash smelting/flash converting coppermaking sequence (b) as a continuous converting alternative to batch submerged tuyere converting. This chapter uses our flash furnace matrix to determine the %O2-in-blast, industrial oxygen and oil requirements for converting solidified 65% and 72% Cu matte to molten copper. It then discusses choice of feed matte grade and other aspects of the process.

Jan 1, 2001

By C. Lupi

Electric arc furnace dust generated during the production of steels is regarded as hazardous waste because of the presence of leachable elements such as Cr, Pb, Cd .... Different processes are available according to the management policy chosen by the steelmaker: disposal. recycle and/or recovery. The feasibility of an hydrometallurgical Zn recovery process on fumes generated during the pyrometallurgical treatment of EAF dust has been investigated. The recovery of metallic iron, chromium and nickel as molten metal provides fumes very rich in zinc oxide ( 63.1% ) and poor in zinc ferrite. This secondary dust is still an hazardous waste and represents the raw material for the recovery of Zn and Pb. The waste material is first leached in 1.5 M sulphuric acid at 30°C to provide a Zn, Fe and Mn rich aqueous solution and a Pb and Ca sulphate rich sludge. The iron is eliminated by precipitation because is harmful to the following electrowinning process. The ftltered and purified leached solution is acidified in order to obtain good electrowinning conditions. A pure cathodic deposit of zinc is then produced in an electrolytic cell at laboratory scale.

Jan 1, 1996

By W. J. Guay

Scrubbing of simulated copper reverberatory furnace gases containing 1.0 percent sulfur dioxide with the minus 74 ~m fraction of the San Manuel tailings has shown sulfur dioxide removals of almost 100 percent over an effluent pH range of 3.1 to 4.6 and a wide range of liquid to gas ratios with absorptions of 11 to 17 Kg of sulfur dioxide per tonne of minus 74 um slimes. The high reactivity of the tailings slimes with S02 indicates that the reaction rate is not controlled by the slow dissolution of calcium carbonate in sulfurous acid which characterizes scrubbers using ground limestone. The interpretation of these results has been considerably enhanced by wet chemical analysis and emission spectrographic analysis which show that calcium and iron account for about 90 percent of the SO2 absorption with the rest being accounted for by aluminum, magnesium, potassium, and sodium. Mineralogic examination confirms the, chemical and spectrographic analyses showing that the major constituent removed from the slimes is calcium carbonate, with lesser amounts of chlorite and montmorillonite (silicates containing iron, magnesium, aluminum, and calcium) being removed.

Jan 1, 1981

By Jonkion M. Font

An expression for the distribution ratio of arsenic between slag and copper matte or liquid copper was developed by both, an extension of the Reddy-Blander model for deriving a priori the arsenic capacity, and by a relationship between the arsenic capacity and the arsenic distribution ratio. In this study, the a priori arsenic capacities in the FeO-SiO2, CaO-SiO2, MgO-SiO2, FeO-CaO-SiO2, FeO-FeO1.5-CuOo.5-MgO-SiO2, FeO-FeO1.5-CuO0.5-CaO-MgO and FeO-FeO1.5-CuO0.5-CaO-MgO-SiO2 slags were calculated at 1573 K. The a priori arsenic distribution ratio between the FeO-FeO1.5-CuO0.5-CaO-MgO-SiO2 slag and copper matte (L s/m as), and between the FeO-FeO1.5-SiO2 or FeO-FeO1.5-CuO0.5-CaO-MgO slag and liquid copper (L s/Cu as) were calculated. The model calculated data are found to be in good agreement with the reported experimental data. The availability of reliable thermodynamic data for slag components and impurities in the slag-matte-metal system is essential for the accurate prediction of impurity capacities and distribution ratio data. The arsenic distribution ratio model developed here, can be extended for prediction in multi-component slags and mattes or liquid metal, and thereby may lead to the development of new slag systems for the efficient removal of arsenic in the copper smelting, converting and refining processes.

Jan 1, 2003

"Hematite pellets were electro-deoxidized to iron in molten sodium hydroxide to produce iron containing about 10-wt % oxygen. The anodic reaction was the evolution of oxygen on an inert nickel anode. Before the electrochemical reaction, there is a reaction between sodium hydroxide and ferric oxide to form sodium ferrite and, in order to compensate for the reduction in sodium oxide content, 1 wt % sodium oxide is added to the melt. In a laboratory cell, the cell voltage was 1.7 V with a current density of 5000 A m-2, a current efficiency of 90% and an energy consumption of 2.8 kWh kg-1.Introduction The iron and steel industry contributes about 2.3 bn tonnes/annum of the carbon dioxide to the atmosphere, which is about 10% of the total, and some believe that, in order to prevent a catastrophic rise in the earth’s temperature, carbon dioxide emissions must be reduced by 50% come 2050. However, by 2050, it is likely that the iron and steel industry would have grown significantly so that the production may have risen to 2 or 3 bn tonnes/year so in order to meet the 50 % reduction on today’s figure, the carbon dioxide may have to be reduced to 25% or less, which is a very demanding requirement. There are probably three ways of reducing the carbon dioxide output:1. By capture and sequestration, but this may be technically very demanding.2. Reduction using hydrogen in place of carbon."

Jan 1, 2009

By K. Osseo-Asare

Aqueous stability diagrams (25°C) are presented for the systems M-H2O and M-Oxalate-H2O where M=Sm, Nd, Co, and Fe. With the aid of these diagrams (i.e., Eh-pH and log[Metal]- log[Oxalate]), the solution-chemical constraints on metal dissolution and precipitation are identified. By comparing the corresponding stability diagrams, conceptual flowsheets are developed for metal recovery from Sm-Co and Nd-Fe-B magnet scrap.

Jan 1, 1997

By Gaifeng Xue, Xiaohong Xu, Meng Liu, Yijie Song, Guotao Xu, Jixiong Liu

BN (Boron Nitride) based composites were prepared with hot-pressing by using h-BN as main material in ceramic preparation process. The relative density, bending strength, vickers’ hardness, thermal shock resistance, thermal expansion coefficient, thermal conductivity, phase composition and microstructure were tested and analyzed by using modern testing technology. The results indicate that the best formula is B, the relative density is 97%, the bending strength is 260 MPa, the hardness is HV5 343kg/mm2, the thermal expansion coefficient is 2.8×10-6℃-1, the thermal conductivity is 22 W/(m.K) and have no crack after thermal shock for 20 times by water cool. XRD analysis indicates that the main phase compositions are h-BN, β-Si3N4 and sialon. SEM studies show that the grains wrapped up by solid solution.

Jan 1, 2015

By Chai Li-yuan

The anodic behavior of AZ31 magnesium alloy in NaOH alkaline solution was investigated in this paper. The effects of anodizing parameters, such as applied current density, concentration of NaOH and temperature of the solution on the formation, structure and surface morphology of the anodic films were also studied. The formation of the anodic film was analyzed by analyzing the anodic polarization curves, the potential-time curves and XRD, SEM graphs of samples obtained at different anodizing time. The results of corrosion resistance tests, XRD and SEM observation showed that the temperature greatly affected the formation and anti-corrosion property of the anodic film, but the concentration of NaOH not. The film with best anti-corrosion resistance was obtained at applied current density of 10mA/cm2, 353k in 1mol/l NaOH solution.

Jan 1, 2006