Thermodynamics and kinetics? of the removal of Va elements (As,Sb,Bi) from copper were investigated 1n the fire relining by alkaline carbonate fluxes such as Li 2co3 , Na 2CO3 and K2CO3. The distribution coefficients of As, Sb and Bl between alkaline carbonate fluxes and mo) ten copper were ?obtained at 1200°C under the different oxygen potentials. As and Sb were easily removed from copper to fluxes as pentavalent oxide form. On the other hand, Bi was hardly removed except by a Ll2CO3 flux. The removal rates of Va elements from copper were also measured In the temperature range of 1150°C.- 1250°C. The removal rates of As and Sb were much higher than that of Bi. The removal rates of Va elements showed the same order of the distribution coefficients. The removal rate could be expressed by following equation. (1).

Jan 1, 1987

By B. Zeytuncu, O. Yucel, O. H. Celik, M. H. Morcali

"The Taguchi method was used as the experimental design to determine the optimum conditions of cementation behavior of the ruthenium chloride solution. Cementation was carried out using metallic zinc powder. The experimental conditions were studied in the range of 25-45°C for reaction temperature (A), 30--60 min for reaction time (B), 0.5-1.5 for pH of solution (C), and 30--50 mg for zinc powder (D). Experimental parameters and their levels were determined in the light of preliminary tests. Orthogonal array (OA) L9(34) consisting of four parameters each with three levels, was chosen. The optimal conditions found for ruthenium, such as a reaction temperature, reaction time, pH of the solution and mass of zinc, are respectively: 45°C, 45 min, 1.5 and 50 mg. Under these conditions, the ruthenium cementation efficiency obtained by theoretically and experimentally was in good agreement, which were 99.8% and 99.7% respectively."

Jan 1, 2013

By James P. Bennett

The U.S. Bureau of Mines, Tuscaloosa Research Center, is conducting a review of the usage of different types of refractories, the current industrial practices to recycle/dispose of spent refractories, and the concerns associated with these practices. This information will serve as the technical basis for initiating a research program to recycle or find alternate uses for spent refractory materials. Approximately 1.6 million metric tons of clay based and 1.2 million metric tons of non-clay based refractory materials were manufactured in the United States in 1992 alone, representing a value of almost 2 billion dollars. Landfill has been and remains the disposal means of choice. Issues such as environmental regulations, concerns over landfill disposal, future liability, and product stewardship programs have brought about increased emphasis for recycling or alternate material use. Information on refractory consumption and the issues associated with recycling or disposing of used materials will be discussed, including current recycling practices.

Jan 1, 1995

By Dong Hoon Han

The simultaneous sulfation by sulhr dioxide and oxygen of CaO and MgO in calcined CMA (calcium magnesium acetate) were investigated. he experiments were carried out in the temperature range from 700 to 830 "C and at the SO2 concentrations of 0.3 to 1 mol %. The oxygen concentration was kept at 5 %. Each sample was calcined completely before the temperature was lowered to the sulfation temperature. According to the ranges of partial pressure of sulhr dioxide and temperature, there exist three regions for the sulfation reaction: region I in which neither oxide is sulfated, region I1 in which only CaO is sulfated, and region 111 in which both oxides are sulfated. It was shown that the MgO in calcined CMA is sulfated at a rate comparable to that of CaO by forming a mixed sulfate phase. Thus, unlike MgO contained in other desulhrization materials, the MgO content in calcined CMA can be fully utilized for flue gas desulhrization.

Jan 1, 1999

By R. Padilla, M. C. Ruiz

Arsenic, antimony and bismuth are commonly found in copper concentrates usually as the minerals enargite, stibnite and bismuthinite, respectively. Concentrates having high levels of arsenic and antimony must be pretreated before smelting. Roasting is the preferred method for removing these toxic impurities from concentrates; However, the removal of As, Sb and Bi in oxidizing roasting by volatilization may not be complete due to the slow reaction rates at 500- 700 °C. Oxidizing/volatilization data were obtained from pure mineral mixtures and from arsenic rich copper concentrate. The reaction mechanism for the volatilization of arsenic and antimony were discussed. Near 100% As and over 95% Sb volatilized in the oxidation of a mixture of pure minerals at 700 °C, 1% oxygen, while over 95% As, and 35% Sb volatilized at 600 °C in 1% oxygen atmosphere when using a copper concentrate containing 3.51% As, 0.14% Sb, and 0.01% Bi. Bismuth did not volatilize.

Jan 1, 2015

By Zhi-xiang Cui

Dongying Fangyuan Nonferrous Metals Co., Ltd. has developed a new technology to produce anode copper from concentrates through only two furnaces. This new technology is called the Two-Step Copper Smelting Process. This paper presents the commercial application of the Two-Step Copper Smelting Process and its operating conditions. The key features of the Fangyuan Two-Step Process are as follows: (1) feed materials, including concentrates and flux, are mixed without pretreatment and fed into the Submerged Lance Smelting (SLS) furnace; (2) high grade white metal (WM) produced by the SLS furnace is transferred via WM conduit into one of the two Submerged Lance Converting and Refining (SLCR) furnaces; and (3) the two SLCR furnaces blow alternatively to maintain continuous operation of the whole production chain. The new smelter started operation in October 2015 with a processing design capacity of 1.75 Mt/year of mixed feed and has been operating for over 30 months.

By J. W. Dini

Introduction The mission of the Materials Fabrication Division (MFD) is to provide fabrication services and technology in support of all programs at Lawrence Livermore National Laboratory (LLNL). MFD involvement is called for when fabrication activity requires levels of expertise, technology, equipment, process development, hazardous processes, security, or scheduling that is typically not commercially available. Customers are encouraged to utilize private industry for fabrication activity requiring routine processing or for production applications. MFD is .a large diversified service organization including approximately 400 full time employees. The group provides a wide variety of processes including all common machining and fabrications operations, laser and water jet cutting, electrical discharge machining, lapping, electron beam and laser welding, vacuum brazing, heat treating, forming, electroplating and metal finishing, optical polishing and grinding, vacuum coating, vacuum engineering and a variety of plastics operations. These operations occupy more than 1,250,000 square feet of floor space. For more detail on the many fabrication related services available from MFD, see Reference 1.

Jan 1, 1992

By W. Kasprzak

Press-fit systems are widely used to seal oil lines in the automotive engine components. In the case studied a ball plug made from the 7075 A1 alloy was inserted into a 319 Al alloy cast component. The oil lines were subjected to the required component service pressure. This paper addresses the analysis of the ball plug/casting hole press-fit performance. The tools used to investigate the plug system included: the SEMIEDS technique for the assessment of the plug and the casting hole wall surface integrity; image analysis methods for the characterization of the ball plug/casting hole interface; matrix microhardness measurements of the plug and casting components; laboratory ball plug insertion, speed and force correlation; as well as the ball shearing mechanism analysis. Laboratory tests indicated that optimization of the aluminum matrix hardness in the 319 A1 alloy cast components resulted in considerable improvement of the press-fit system sealing properties.

Jan 1, 2002

By G. Roy Chaudhury

Adsorption techniques are comparatively low cost and effective for treatment of arsenic contaminated drinking water. Various adsorbents such as alumina, ferrihydrite and manganese ores have been used, but there has been little investigation of modifying the structure of ferrihydrite to improve its adsorptive efficiency of As(III) and As(V). In the present study the incorporation of manganese oxide into the ferrihydrite structure was carried out and the prepared materials used in arsenic adsorption experiments. The compounds were X-ray amorphous, but TGA/DTA and FTIR analysis showed some structural characteristics. Sorption studies reported in this paper indicate the excellent arsenic removal properties of the manganese/iron compounds with a loading capacity of 0.3 mmol/g. Adsorption follows first order kinetics and the results fitted to adsorption and mass transfer models. Arsenic levels in water containing 1 mg/L As(V) were reduced by 50% in 20 minutes and 90% in 60 minutes using 1 g/L manganic ferric oxyhydroxide.

Jan 1, 2003

By Corby Anderson

The efficient separation of palladium from the transition metals copper, nickel and iron can be effected by passing a leach solution of these metals through a column of the silica polyamine composite material, WP-1, patented by Purity Systems Inc (PSI), Assignee, University of Montana with exclusive license to PSI. The separation can be done at the intrinsic pH of a nitrogen species catalyzed (NSC) oxidative pressure leach solution (~0) and stripping of the palladium from the composite can be effected with hydrochloric acid/ammonium chloride solutions at 50oC. Batch capacities of the composite for palladium are ~ 1.8 mmol/g resin. The possibilities for isolating the metal from the strip are discussed. Given the proven longevity and rapid capture kinetics of the polyamine composites, this new approach should prove to be an economically viable alternative to the multi-step concentration processes practiced in the PGM industry to date.

Jan 1, 2003

By Shengli Wu, Jinming Zhu, Wei Huang, Xinliang Liu

The sinter of high basicity would interact with lump ores or acid pellets in the cohesive zone of blast furnace due to the difference of chemical composition and micro structures. The results of this work showed that the softening-melting properties of lump ores and acid pellet would be obviously improved by the high temperature interaction. However, the high temperature interaction index (INI) would be influenced by many factors, such as chemical composition, porosity, interaction interface and so on. The INI between sinter and porous limonite lump ore (L-2) was much higher than that of dense hematite lump ore (L-1) and acid pellet (P-1). In addition, though the softening and melting properties of L-2 were poorest in respective iron ores, the softening and melting properties of integrated burden B (consist of sinter and L-2) were not worse than other integrated burdens due to the strong high temperature interaction.

Jan 1, 2015

By Qiang Zhong, Bin Xu, Qian Li, Wei Gao, Yongbin Yang, Yaxuan Wang

Lump coal with high volatility is used for providing heat and reductive gas, and ensuring permeability in COREX. However, it is apt to be pulverized in transport and storage process. Therefore, comprehensive utilization of the pulverized coal to produce coal briquettes with appropriate binders is significant, among which the molasses binder cannot meet the technological requirements. In this paper, coal tar pitch binder and BJ additive were used in briquetting and carbonizing process of coal powder. The results showed that BJ effectively activated cold state cohesiveness of the pitch and make it bond the coke particles to a firm briquette at room temperature .Carbonizations of coal and coal tar pitch achieved obvious constriction and formed a carbonized skeleton. The drop resistance of wet briquettes reached over 50 times/1meter. When cured at 1000 °C for 1h under nitrogen atmosphere, the compressive strength of carbonized briquettes came to 6.43 Mpa.

Jan 1, 2016

By Chengyi Ding, Xuewei Lv, Changyang Ji, Rende Zhang, Xiangwei Zheng

Inexpensive and high-quality sinter has an extraordinary position in iron making, and there are many factors influencing the sintering. This research takes the basicity and coal dosage as research subjects to do the experiments based on cost analysis with sinter pot experiment system. Linear program is taken to make the schemes of ore blending. During the experiments of changing basicity from 1.6 to 2.3, the properties and microstructures of the sinter are studied. It comes to a conclusion that increasing the basicity is beneficial to sinter quality but leads to higher cost. To further ascertain the cost of sinter and the potential of saving coke, the work of improving coal dosage is taken on the basis of experiments of changing basicity. Through analyzing the results, a formula (Y=1849+261.1R-130.6C) is proposed which indicates the relation among the cost, basicity and fixed carbon content. And it works well for actual production.

Jan 1, 2015

By Nobuaki Sato

For decontamination of SO2 containing waste gases from industries such as ferrous and non-ferrous metal companies, desulfurization with hydrogen production by the reaction of Br2 and SO2 was proposed as bromine-sulfur (BS) process. In this process, SO2 is fixed as H2SO4 in the presence of Br2 and H2O forming H2SO4 and HBr. Then hydrogen is produced by the decomposition of HBr and Br2 as byproduct is recycled. The reaction of Br2, SO2 and H2O was found not to occur in liquid phase but to occur in vapor one. The production ratios of H2SO4 and HBr showed a maximum at temperatures around 60 oC. The highest production ratio was obtained at 70 oC with a mixing ratio of Br2:SO2:H2O=1:1:10. The experimental results were discussed with thermodynamic consideration.

Jan 1, 2006

By Yu Yamashita

There have been increasing in melting recycled scraps in copper smelting processes, and thus growing interests in the chlorine behavior. In this study, chloride dissolution in FeO-Fe2O3-SiO2slag (SiO2sat.) at 1523 K has been measured with varying in PCl2 from 1.13x10-8 to 1.30x10-7atm. and the oxygen partial pressures encountered in typical copper smelting furnace, i.e. PO2=10-8 to 10-10 atm. Discussion is made on the chloride capacity of FeO-Fe2O3-SiO2 slag in terms of its characteristics and the dissolved chlorine species. It has been shown that the mostreasonable dissolution reaction and chloride capacity can be expressed by the following reactions, where chlorine dissolves in the form of Cl-; here, aO2-, oxygen ion activity, is shown a function of oxygen partial pressure in the atmosphere. [ ]

Jan 1, 2006

By Robert De Saro, Willis Bateman, Ramesh Jain

A Vertical Floatation Melter (VFM) has been developed (sponsored by DOE) which simultaneously decoats and melts organic laden scrap in a single unit. Scrap aluminum is fed into the top of the VFM where it falls through a cone. Hot gases flow upwards through the cone, imposing a variable drag force on the scrap. Equilibrium is reached in which the scrap weight equals the drag force and the scrap becomes suspended. The gases strip off and vaporize the organics. Next, the scrap reaches a liquid state, taking on a more aerodynamic teardrop shape, allowing it to fall into a holding furnace. Heat transfer coefficients are 10 times higher than that of a conventional furnace, allowing rapid melting at a low gas temperature. Typical energy use is well under 2,324 joules/g (1,000 Btu/lbm) with a metal yield from 92 to 98%. This paper reports on the operation and data of a 453 kg/hr (1,000 pph) pilot-scale VFM.

Jan 1, 2000

By Neal Schwartz, Robert De Saro, Richard Rosenthal, Ed Kear

"A Stack Melter has been installed and is currently operating at Lexington Die Casting. The Stack Melter consists of a 1 meter (3 foot) diameter refractory tube, 2 meters (7 feet) high. Specification ingots are continuously fed to the top of the melter and piled to nearly the top. A burner fires through the scrap which melts the lower portion and preheats the upper portion. As the lower portion is melted, it is drawn out and the upper preheated scrap falls to a lower level where it in tum melts. The molten metal is fed to one of two holding furnaces for eventual delivery to a casting machine.The Stack Melter's energy use is approximately 2900 joules/g (1,250 Btu/lbm), resulting in an overall energy savings of about 58%. This energy savings is brought about primarily because the flue gases preheat the scrap and the flue gas temperature is dropped to well under 528°C (1000°F)."

Jan 1, 2000

By E. T. White

The population balance is one of the basic relations for a:n:aIysing particulate minera1 processing operations. It is an exact relation. The principles of the population balance are reviewed and applications in the minerals industry discussed.

Jan 1, 1996

By M. Tamura, K. Fujita, K Shinozuka, H. Daimon, H. Esaka

"In-situ observation of unidirectional solidification using transparent substance has been performed to investigate the growth direction of solid phase. Cell or dendrite of which preferred growth direction is not parallel to the heat flow direction was observed with various solidification conditions. Dimensionless growth direction (p) changes from 0 to 1 with increasing growth velocity at a constant temperature gradient. Introducing the dimensionless growth velocity, the relation between p and growth condition could be correlated.IntroductionTransition in macroscopic solidified structure from chill to columnar zone which is found in normal castings takes place via grain selection1). Cast products such as turbine blades are unidirectionally solidified, grain selection plays an important role to choose suitable crystals which have reasonable orientation in the region called ""starter"", which is a very initial part of casting2). Therefore, grain selection is a very important process in the formation of casting structure. The present authors have been studying on the process of grain selection using succinonitrile, which is a transparent organic substance and have found that the growth distance necessary for grain selection depends upon the solidification condition3-5). When the solid/liquid interface is dendritic, the grain selection occurs quickly. On the other hand, when the solid/liquid interface is cellular, it occurs slowly. We supposed that the growth direction of dendrite is different from that of cell when the substance is unidirectionally solidified. Indeed, Kurz and Fisher wrote in their text book that dendrite grows along its preferred growth direction, <100>, regardless of heat flow direction and that cell grows along heat flow direction regardless of its preferred growth direction1). However, there is no quantitative description about the growth direction when the solid/liquid interfacial morphology is cellular. Furthermore, there have been little works6) to study the growth direction of cell and dendrite."

Jan 1, 2000

By Y. W. Chung, W. I. Chia

"The interaction of water vapor with single crystal Ni3(Al,Ti) and polycrystalline Ni3Fe, with and without the presence of oxygen, has been studied with Auger electron spectroscopy, photoemission spectroscopy, thermal desorption and isotope exchange. Water dissociates to produce atomic hydrogen above 200 K on both Ni3(Al,Ti) and Ni3Fe surfaces. For Ni3(Al, Ti), the reaction is structure-sensitive. Pre-adsorbed or co-adsorbed oxygen on Ni3(Al,Ti) and Ni3Fe significantly suppresses hydrogen production due to water dissociation. This suppression process occurs more efficiently on Ni3Fe than Ni3(Al, Ti).IntroductionOrdered intermetallic compounds such as aluminides, silicides and titanides are very attractive for structural applications at high temperatures. This is because these intermetallics tend to form adherent oxides in oxidizing environments which protect the base materials from excessive oxidation and corrosion. In addition, they have low density, relatively high melting points and good high-temperature strength. However, the moisture in air severely embrittles many ordered intermetallics such as FeAl [1-3], Fe3A1 [4,5], C03Ti [6,7], (Co,Fe)) V [8], Ni3Si [9], Ni3(Si,Ti) [10], Ni3(AI,Mn) [Ill, and Ni3A1 [12-14], resulting in low 'ductility and brittle fracture at room temperature. Recent studies by Liu and coworkers (see review by George and Liu [15]) provide a qualitative description of the mechanism for this moisture-induced embrittlement. During elongation testing, cracks are formed, thus exposing fresh alloy surfaces. One or more active components of the alloy react with water vapor in the environment to produce atomic hydrogen which penetrates into crack tips and causes hydrogen embrittlement. This is similar to that proposed for moisture-induced embrittlement of aluminum alloys [16]."

Jan 1, 1996