By Xie Zhang, Chongyang Zhao, Qingyun Huang, Bing Xie, Xiaopeng Zhen

"Extracting vanadium from vanadium containing hot metal into vanadium slag by BOF is the main vanadium production process in China. In this paper, the influence of Si content in hot metal on the quality of vanadium slag is analyzed. Synthetic vanadium slag with different SiO2 content were melted at 1673 K and then cooled to 303K at the cooling rate of 3?/min. Optical microscopy, SEM, EDS and XRD were used to analyze the mineralogical phases and crystallization behavior of vanadium slag. The results show that vanadium slag mainly contains spinel phase and silicate phase; V is enriched in the spinel phases while Si is concentrated in Fe2SiO4 CaFeSi2O6 and (Fe,Mn)2SiO4 as silicate phase. The melting point of slag increases gradually with the addition of SiO2; whereas viscosity decreases with an addition of 15~19% SiO2 and increases with an addition of 19~27% SiO2.IntroductionVanadium is an important element which is used almost exclusively in ferrous and non-ferrous alloys. The major vanadium products include FeV, V2O5, V2O3, VN and Al-V-Ti alloy. Furthermore, vanadium slags are mostly produced by oxidizing the elements in V-containing hot metal during a duplex refining process. Therefore, the process of removing vanadium from hot metal has its significance on the subsequent process[1].The extraction of vanadium is greatly affected by the mineralogical composition of vanadium slag[2], the distribution of the elements between the spinel and silicate phases and its physic-chemical properties. These characteristics of vanadium slag have been studied in some details. It has been reported that Si mainly exists mainly in the form of silicate which wraps the spinel crystals while small amount of Si stands as phosphorus quartz or diopside[2]. Chen et al.[3, 4] points out, when SiO2 content in vanadium slag increased every 1%, V2O5 decreased 1.48%. Moreover, silicate phases would embarrass the oxidation of V-containing spinels through decreasing the exposing probability[5]. Meanwhile, melting point and viscosity of vanadium slag has been greatly influenced by the SiO2 content. Therefore, this work attempts to analyze the above-mentioned questions systematically."

Jan 1, 2012

By Vojteh Leskov?ek

The tribological load is the load on forging tools resulting from the relative motions between the plastically deformed workpiece and the die. In comparison to many other forming processes hot die forging has an especially disadvantageous tribological system. The advantages of the application of hard coatings, which are well known for cutting tools, are to a much lesser extent explored for casting, extrusion, molding and forging tools. Increasing the lifetime of these tools is an important task in surface engineering because of the complex loading conditions and often complicated tool geometry. The plasma-assisted chemical-vapor-deposition (PACVD) technique is well suited to depositing hard coatings onto large dies and molds. The aim of this study is to present and discus results obtained on a duplex PACVD hard coating in an industrial application like the hot forging of automotive parts. A new generation of vacuum-melted and remelted (VMR) hot-work tool steels has been developed; these can reach a hardness of 58 HRc, and have a fracture toughness at this hardness equivalent to that of standard hot-work tool steels at 45 HRc. This offers one of two advantages: the steels can be used at the higher hardness to provide resistance to wear or deformation, or, when used at a hardness of 47?49 HRc for hot forging, to provide temper resistance, nitriding behavior and adhesive wear resistance. The results presented here are from a preliminary investigation. The experimental results indicate that the introduction of a proper duplex PACVD hard coating will lead to an improved wear resistance and a longer lifetime for the hot-forging dies. Furthermore, by using a hard, low-friction coating excellent anti-sticking properties can be obtained. At this stage of the investigation it is also necessary to carry out pilot trials to determine the wear resistance and the tool life in practice.

Jan 1, 2006

By Guohui Zheng

The ever increasing quantities of solid wastes generated by various industries are at the source of the growing need for proper waste disposal methods. Thermal treatment of combustible wastes is a proven technology which permits the reduction of hazardous material having to be landfilled. However, this method is not universally applicable to waste disposal. For example, the transferal of heavy toxic metals into the thermal remediation products is a major issue of public concern. This paper focuses on the analysis of morphology changes from solid sludge to ash which is a product of the sludge combustion. The morphological parameters analyzed were particle size and external surface. They were determined using Jeol 840 Super Probe. The experiments were conducted in a computer-controlled high-temperature combustion system consisting of the thermogravimetric furnace coupled with Fourier transform infrared spectrometer (TGA-FTIR). Sludge particles were made of complex fibers trapped in the aluminosilicate matrix. At low temperatures, up to 680 K, the solid residue looked similar to the initial sludge. Between 680 K and 1180 K the sludge underwent intensive burning and steadily changed into powdered ash. At the temperature of 1050 K the ash was composed of separate, flat flakes with sizes ranging from 5 to 20 um. At 1470 K the flakes aggregated into large particles. The surface observed at 1670 K was a mixture of mullite crystals. Such structure could result from the solidification of the ash material after its melting. Morphological changes influenced the distribution of metals in the solid residue. For example, Cr was concentrated in small aggregates. Such distribution should allow for recovery of valuable metals from the solid waste residue.

Jan 1, 1996

By Bengt T. Andersson

Outokumpu Consulting Engineers, Outokumpu Oy SF-02200 Espoo 20, Finland This paper describes experiences from some operating non-ferrous flash -smelters and focuses on the advances in smelter byproduct and gas treatment engineering design. In this context a summary is given of the specific technical and economic benefits achieved-by flash -smelting technology and oxygen enrichment. The paper will also briefly outline a few new process and equipment developments.

Jan 1, 1983

By R. Boom, Y. V. Meteleva-Fischer, B. Kraaijveld, H. Kuntzel

"Segregation of impurities during refining of metallurgical grade silicon (MG-Si) is an option to produce solar grade silicon (SG-Si). Directional solidification is a last step in production of SG-Si effective for removal of metallic impurities. The possibility is investigated to use metallic impurities originally present in MG-Si for removing boron and phosphorus. MG-Si has been treated using two methods: 1) alloying with calcium and 2) refining with Na2O-CaO-SiO2 slag, both by controlled cooling. The microstructure of silicon and the impurities distribution have been studied before and after the treatments. Using EPMA phosphorus and boron have been detected in 1-2 wt% concentration range in several intermetallic compounds in grain boundaries after both treatments. This observation points to a different possible mechanism of silicon refining from boron and phosphorus. Controlled cooling improves migration of phosphorus and boron to the silicide phases in grain boundaries, which can be removed by acid leaching treatment.2. IntroductionStandards for silicon solar cells and growing demand on “green” energy require economical and efficient route to the production of solar grade silicon. Refining of cheap metallurgical grade silicon is one of the promising options, where application of existing metallurgical approaches can result in cost-efficient production on industrial scale. Focus in refining is on impurities, which are most difficult to remove: B, P, Al, Ti, due to their large segregation coefficient in silicon and low vapour pressure [1]. Moreover, more environmentally friendly technology in comparison to the traditional Siemens process [2] will be in accordance with societal needs. Based on properties of common impurities in metallurgical grade silicon, alloying refining and slag refining are suggested as competitive techniques having potential effect on removal of impurities harmful for conversion of solar energy [3, 4]. Alloying with Ca followed by acid leaching was found to be effective for removal of Fe and Ti from silicon [5] and to enhance also removal of boron [6] and phosphorus [7, 8]. In the work of Inoue et al. [8] drastically increasing removal of phosphorus from silicon has been observed with an increase of Ca content and a thermodynamics-based explanation was provided. Since phosphorus has been found to condense in the secondary precipitate mainly composed of CaSi2, it can be removed together with iron and titanium by consecutive acid leaching treatment. Slag refining is one of the metallurgical methods proposed to be effective for refining of metallurgical grade silicon from boron [9, 10]. Slags with additions of the following oxides to silica have shown positive effect on removal of boron: CaO [11-13], Na2O [11,14]. Mechanism of slag refining from boron is based on oxidation of boron followed by its incorporation in the slag network [9,11]; the same mechanism is suggested for refining from phosphorus taking into account that oxides of boron and phosphorus are known as network-formers [15]."

Jan 1, 2012

By Alexey T. Kovalev, Irina A. Khabarova, Valentine A. Chanturiya, Igor Zh. Bunin, Elizaveta V. Koporulina

"The paper presents new theoretical and experimental results about mechanisms of disintegration of mineral complexes and structural transformations of the sulfide surface under high-power nanosecond electromagnetic pulses (HPEMP). The heated gas outflow from nanosecond breakdown channels of sulfide minerals under HPEMP is considered. It is shown that the gas outflow from channels can be an additional destructive factor in the processes of the electric pulse discharge disintegration of mineral complexes. It is shown that the effect of HPEMP changes chemical surface composition and, respectively, technological properties of pyrrhotite and pentlandite. Morphology and elementary composition of new micro- and nanoformations on mineral surface of pentlandite and pyrrhotite have been investigated using up-to-date methods of SEM/EDX and Scanning Probe Microscopy. Preliminary electropulse effect on mineral products before flotation allows producing optimal conditions for flotation separation of pentlandite and pyrrhotite owing to forming the new nanophases and defects on the surface of sulfides.IntroductionThe effectiveness of High-Power Nanosecond Pulses in the disintegration and liberation of fine disseminated mineral complexes and the recovery of micro- and nanoparticles of precious metals from refractory ores was demonstrated in [1, 2]. Possible mechanisms of selective disintegration were considered in [1-3]. It has been shown both theoretically and experimentally that electric breakdowns can play an important role in the nanosecond pulsed treatment of milled minerals (e.g., semiconductor sulfides and quartz with particle sizes of 100 µm to 2-3 mm) that are carriers of finely disseminated gold and other valuable components. Electric discharges in such minerals are accompanied by a destruction of integrity in the form of breakdown channels and the formation of a system of cracks around these channels [3]. The development of the domains of induced cracks around the channels is determined by the pressure of evaporated material in the breakdown channel. Upon an instantaneous energy release in a channel (nanosecond discharges), the change in its transverse size and in the gas density and pressure in the channel is determined by (i) the radial motion of the evaporation wave, (ii) the radial expansion of the channel, and (iii) the heated gas outflow from the channel. The evaporation wave moves with a speed on the same order of magnitude as the speed of sound (or greater) and travels a distance of around the initial channel radius, i.e., a much smaller distance than the breakdown channel length."

Jan 1, 2011

By S. A. Shuey

The present industrial practice used to separate aqueous cobalt from nickel is multistage solvent extraction processing. This paper describes a different but simpler treatment technology. The proposed technology has been applied to cobalt/nickel hydroxide intermediate solids produced from the treatment of Electrochemical Machining (ECM) waste sludge, The process consists of dissolving the cobalt/nickel hydroxides in basic cyanide solutions. Cobalt and nickel form aqueous .solution metal cyanide complexes. Nickel can be selectively precipitated from the solution as a nickellic hydroxide solid. Cobalt can be recovered from the leach solution by precipitation of a cobaltous/cobaltic cyanide double salt. The double salt product can then be subsequently treated to produce an appropriate cobalt product. The process chemistry, proposed fiowsheet and preliminary reagent costs are presented and discussed.

Jan 1, 1998

By I. Gaballah

Cadmium is toxic to plant, animals and humans. The council directive of the European Communities No 8315 13lEEC has fixed an upper limit of 200 ppb for the release of cadmium in industrial effluents. The conventional method of neutralization/prccipitation ( NIP ) is inefficient to reach this limit. The objective of this study is to test the efficiency of the trees modified bark to remove cadmium cations from industrial effluents after the conventional treatment by NIP. Laboratory scale tests with synthetic solutions show that the cadmium removal depends upon pH and initial concentration. About 99.9 %, 99 % and 96 % of the metal are removed from synthetic solutions containing 10, 100 and 1000 ppm respectively. Pilot plant trials ( 1 m3 ) with an industrial effluent bearing about 500 ppb of cadmium lead to the almost complete elimination of the cadmium ( final concentration is lower than the analytical detection limits < 20 ppb ).

Jan 1, 1994

By E. James Quinn

Solvent extraction technology using EHEHPA (2-ethylhexyl phosphonic acid, 2-ethyhexyl mono ester) is the norm for industrial separations of rare earth elements. This process has some shortcomings, including a large number of stages compared to most SX processes and high acid requirement for stripping of the heavy rare earths. In this work, we examine a number of alternative mixed solvent extraction systems: (i) Mixtures of organophosphonic and phosphinic acids such as EHEHPA/Cyanex 272 or Cyanex 572; (ii) Ionic liquid mixtures of EHEHPA with quaternary ammonium chloride (Aliquat 336); and (iii) Mixtures of carboxylic acids for yttrium/lanthanide separations. We discuss and compare the efficacy of these systems with reference to the Nd/Sm separation, which is of industrial significance. Based on the extraction chemistry and the use of modelling tools to define the counter-current solvent extraction circuit, we present a techno-economic analysis of a separation plant and discuss the impact of various solvent systems on the capital expenditure (CAPEX) and operating costs (OPEX).

By Guan-zhou Qiu, Shui-shi Liu, Yu-feng Guo, Tao Jiang

"The preparation of high-quality synthetic ruitle from electric furnace titanium slag was systematically investigated by activation roasting followed by acid leaching process. The results showed that impurities such as Ca and Mg in titanium slag can be effectively removed and TiO2 grade of the product was markedly improved by the process. High-quality synthetic rutile containing 88.54% TiO2, 0.42% (CaO+MgO) was obtained under the conditions that roasted with 7.5%(wt) H3PO4 at 1000 oC for 2h, followed by two-stage leaching in boiling dilute sulfuric acid for 2h. Mechanism studies showed that anosovite solid solution and silicate minerals were reacted with phosphoric acid in the roasting process. As a result, titanium components in titanium slag turned into rutile (TiO2) and impurities were transformed into acid-soluble phosphate and quartz.IntroductionWith the gradual depletion of natural rutile and the rapid development of titanium industry in China, the natural rutile reserves cannot satisfy the requirement for production of titanium pigment and titanium sponge. Ilmenite is, therefore, becoming main raw material for titanium industry. However, because of its low TiO2 grade, it generally requires preconcentration to titanium-rich material such as titanium slag or synthetic rutile [1-3].Ilmenite resources are extremely rich in Pan-xi area of China, which account for 90.54% of total ilmenite reserves in China [4]. The titanium slag produced by electric smelting of ilmenite concentrate has high contents of Ca and Mg, and is not suitable as a raw material for chloride process and titanium sponge production. Therefore, upgrading titanium slag to prepare raw material suitable for chloride process and titanium sponge production has important significance for the development of China's titanium industry."

Jan 1, 2011

By Qiang Zhong, Bin Xu, Qian Li, Yongbin Yang, Tao Jiang

Viscosity of slag determines the production efficiency, energy consumption and distribution of elements between metal and slag, which is very important for pyrometallurgy. Slag of goldantimony ore blast furnace smelting has seldom been studied. In this paper, the viscosities of gold-antimony ore smelting slags of different composition have been studied by the rotating cylinder method. The results showed that, for a slag of 38.95% SiO2, 16.17% CaO, 25.97% FeO, 10.25% Al2O3, 5.17% MgO, the viscosity can be decreased by reducing 3.24%-8.5% SiO2 or increasing 3.31%-9.56% CaO content. Complex SixOy z- from SiO2 acts as the main cause for the high viscosity in a slag of high SiO2. The increasing of CaO causes the decreasing of the amount of SixOy z- and the O2- dissociated from CaO breaks the complex SixOy z-, which can decrease the viscosity. Viscosity of different composition slag in the appropriate range temperature can be calculated from the Arrhenius equation.

Jan 1, 2015

By Ahmet Haxhiaj, Jaroslaw Drelich

"Both composition and porosity of pellets are the main parameters influencing the reductive melting process in water-jacket furnace during the roasting of sulfide lead concentrate. Roasting in a smelter located in Trepçë is done at about 9000C, for pellets which are composed of PbS, CaCO3, Fe2O3, and SiO2. In order to faciltiate the formation of slag in the reductive melting, the pellets must have the proper content of CaO, SiO2, and FeO, and porosity. The plant’s practice indicates that pellets with porosity of 18% do not melt adequately in the water-jacket furnace. The optimum porosity for the proper melting of pellets needs to be 32-40% and can be achieved when pellets are loaded with more than 10 wt.% CaO. Pellets with less than 10% CaO have a limited network of pores, such that reactive gases cannot reach the entire ore structure. Also, the composition of the pellets must satisfy the ratio of CaO : SiO2 : FeO = 1 : 1.2 : 1.8 to facilitate the formation of slag in the reductive melting process.IntroductionAgglomeration roasting of sulfide lead concentrate is an important phase in the production of lead by reductive melting [1-6]. The reductive melting process is a complex process with contradictory effects of several technological indexes which many times are hard to measure and determine. In this process, loading the water-jacket furnace with pellets of optimized composition and structure can reduce the consumption of coke, and achieve high level of lead recovery. Pellets (agglomerates) should be porous, but at the same time they should have necessary mechanical strength. ‘Self-melting’ ability of pellets is controlled by the types and quantities of fluxes blended into the pellet composition. Three major additives and their role are:"

Jan 1, 2011

By Moto Goto

Onahama Smelter of Onahama Smelting & Refining Co., Ltd. has two green- charge reverberatory furnaces; the old furnace was constructed in 1965 and the new one in 1973. This paper discusses the use of oxygen-oil burners in a green-charge reverberatory furnace and also compares the copper loss in slag between the two furnaces at Onahama Smelter. During the past ten years of operation, no shutdowns of the old furnace were necessary and the smelting capacity was increased by 25% by the use of two oxygen-oil burners. These burners are suitable for a green-charge reverberatory furnace to in- crease the smelting capacity without causing an increase of the exhaust gas volume and refractory erosion. After two years of operation of the old furnace, a bottom build-up in the charging zone of approximately 50 centimeters was experienced, and this build-up has stayed at this level since then. In 1973, a new additional reverberatory furnace was put into operation. Copper content in slag of the new furnace was lower by approximately 0.15% than that of the old one during the first several months after the start-up. Investigations were then made on the effect of the bottom conditions in the charging zone on the copper content in slag.

Jan 1, 1976

By N. J. Themelis

The basic chemical, thermal and transport principles that underlie sulfide smelting of. copper, nickel and lead are reviewed. Two basic types of modern smelting processes are distinguished?: flash-smelting, where the predominant reactions occur between oxygen-bearing gas and concentrate particles dispersed therein; and bath-smelting where the concentrate is enveloped and reacted in a turbulent bath of matte, slag and gas. The controlling heat and mass transfer phenomena are discussed, and appropriate correlations are proposed.

Jan 1, 1983

By F. Baldini, M. S. Borges

"The proposed method emphasizes the optimization of waste management with regard to the exploitation of raw materials incorporated in the remains of industry, as well as the economics of natural resources as an environmental impact assessment. This system [tool] allows: (a) the conversion of an environmental liability into an asset by finding a line of appropriate research for each type of waste and the development of new materials applicable to other industries, (b) the performance of internal control of the waste generated (production, storage, final destination) as well as legal conformity.Objectives:1.1 General objective:To design a collaborative system for socio-environmental management of industrial waste.1.2 Specific objective:Develop evidence of concepts;Evaluate the deployment of the inventory of waste in an industry;Enable the conversion of an environmental liability into an asset by finding a line of research appropriate to the waste: a case study;Evaluate the environmental legislation in the legal mechanisms that influence company decisions.IntroductionThe global economy is undergoing major changes, among these changes; it should be highlighted those related to technological progress and environmental quality.While the industrialized countries and higher levels of economic growth dominate modem technology, developing countries are identified by a different growth pattern, using the annual growth rate of Gross Domestic Product per capita [3, 18].Growth is when the GDP grows, in percent, over the previous year. Development, on the other hand, is when the countries change their technologies and improve their internal structure. Thus, the growth considers the accumulation of wealth, while the development is concerned with the distribution of wealth, improvement of the quality oflife and environmental quality [3, 18].As the UNESCO report shows (1999), the biggest problem is between consumption and development, what is produced and the end that is given to the product. Therefore, product and by-product have equal importance in the quantity produced [29].On one hand there is a positive relationship between indicators of economic growth and technological progress, however, on the other hand, these transformations are a paradox, confirmed by the dramatic use of environmental resources and the lack of technologies for recycling of industrial scrap."

Jan 1, 2011

By Pengfu Tan

A thermo-chemical model of the copper P-S converter and a viscosity model for the converter slag have been developed to predict the behavior of magnetite in the converter slag, amounts of slag and matte, compositions of slag and matte, volume of the bath, bath temperature, slag blow endpoint determination, SEMTECH OPC signals, and the viscosity of converter slags. The predictions of bath temperature, slag and matte compositions, and magnetite content in the slag have been validated by the industrial data. The effects of fluxing strategy, returns and skim charges, oxygen enrichment, and temperature on the magnetite formation in the slag have been predicted and discussed. The effect of oxygen potential, SiO2/Fe in slag, detection of slag blow endpoint, and temperature on Fe3O4 content in converter slag, slag viscosity, liquidus temperature of converter slag and skimming operation has been modeled and discussed as well. Some applications of the industrial operations have been presented.

Jan 1, 2009

By Zhigan Deng

Cooling crystallization was used to separate iron (III) and nickel (II) from acidic sulfate solution produced by leaching of molybdenum-nickel black shale. The effect of K2SO4 concentration, crystallization temperature, solution pH and crystallization time on recovery of nickel (II) and precipitation of iron (III) was investigated, in order to obtain effective separation of nickel and iron. The optimum parameters determined were as follows: 200 g/L K2SO4, 10 °C crystallization temperature, solution pH of 0.5 and 24 h crystallization. Under these conditions, 97.6% nickel (II) was recovered as K2Ni(SO4)2, 6H2O crystals and only 2.0% of the total iron (III) was precipitated. Recrystallization yielded K2Ni(SO4)2, 6H2O crystals with a purity of 98.4%.

By S. N. Ojha, Gouthama, R. K. Mandal

"Spray deposition processing of liquid immiscible alloys, based on AI-Pb and Cu-Pb systems have been investigated. Process variables have been optimized to generate uniform dispersion of ultrafine second phase particles in· the matrix of the primary phase. Mechanisms governing the microstructural evolution in this synthesis methodology are discussed. Results of the present investigation are used to demonstrate that rapid solidification of atomized droplets initially provides a high nucleation rate of the second phase during the liquid phase separation. The solid matrix phase nucleates at a later stage and grows with a high velocity enabling trapping of the dispersed phase. Subsequent alteration in the size and size distribution of the second phase is suggested to arise further during deposition of high velocity droplets. Possible reasons for this effect are brought out. Microstructural features of atomized powders and spray-deposits of these alloys are presented to support the present approach of synthesizing composites. IntroductionIn recent years, synthesis of advanced materials with metastable microstructures and ultra fine dispersion of second phase particles has led to the development of novel techniques of materials processing. The other requirement of such a processing methodology is to achieve near-net shape geometries in less number of processing steps. The solidification processing method via spray deposition route qualifies these criteria. This process primarily involves atomization of a melt by high energy gas jets into spray of droplets which are subsequently propelled by the kinetic energy of the gas towards a deposition substrate to build-up a thick high density preform. Although the concept of spray deposition was pioneered by Singer [1] in the early seventies, the fundamentals of the deposition process has been understood only recently [2-4]. Several benefits of spray deposition processing are by now well established [5,6]. Rapid solidification effects are inherent in spray deposition processing due to high heat exchange rate at the droplet-gas interface and also on the deposition surface by force convection. Since considerable heat extraction occurs from the atomized spray prior to droplet consolidation, a relatively low processing temperature is ensured in this process. As a result deleterious coarsening phenomenon can be minimized. In addition, controlled maneuvering of the substrate provides the capability of the process in producing disc, sheet or tube shape preforms of difficult to work materials in a single operation. A significant improvement in properties, resulting from microstructural homogeneity and refinement in grain size induced by spray deposition has been reported for several alloy systems [7,8]."

Jan 1, 1994

By Esperidiana A. B. Moura, Célio H. Wataya, Roberta A. Lima, Rene R. Oliveira

Biodegradable starch/copolyesters/silica nanocomposite films were prepared by melt extrusion, using a twin screw extruder machine and blown extrusion process. The influence of the silica nanoparticle addition on mechanical and thermal properties of nanocomposite films was investigated by tensile tests; X-rays diffraction (XRD), differential scanning calorimetry (DSC) and Scanning electron microscopy (SEM) analysis and the correlation between properties was discussed. The results showed that incorporation of 2 % (wt %) of SiO2 nanoparticle in the blend matrix of PBAT/Starch, resulted in a gain of mechanical properties of blend.

Jan 1, 2015

By A. Kontopoulos

Refractory sulfide gold ores or concentrates require an oxidation pretreatment step to yield the contained gold amenable to the subsequent leaching step. The process options for oxidation pretreatment can be broadly classified as follows: roasting, high or low pressure oxidation bacterial oxidation, chemical oxidation, each with a number of alternative suboptions. Roasting and high pressure oxidation are being applied on an industrial scale; the stage of development of the other options range from preliminary laboratory to advanced pilot plant- In this paper, the major technical, environmental and economic aspects of the above processes are being discussed. Future industrial trends will also be considered. Particular emphasis will be placed on the treatment of arsenical ores and concentrates, where safe plant operation as well as, handling and disposal of the arsenic containing products and/or effluents &apos;and residues is of paramount importance.

Jan 1, 1990