Constituents and Porosity of Lead Concentrate Pellets Produced in the Trepce Plant

"Both composition and porosity of pellets are the main parameters influencing the reductive melting process in water-jacket furnace during the roasting of sulfide lead concentrate. Roasting in a smelter located in Trepçë is done at about 9000C, for pellets which are composed of PbS, CaCO3, Fe2O3, and SiO2. In order to faciltiate the formation of slag in the reductive melting, the pellets must have the proper content of CaO, SiO2, and FeO, and porosity. The plant’s practice indicates that pellets with porosity of 18% do not melt adequately in the water-jacket furnace. The optimum porosity for the proper melting of pellets needs to be 32-40% and can be achieved when pellets are loaded with more than 10 wt.% CaO. Pellets with less than 10% CaO have a limited network of pores, such that reactive gases cannot reach the entire ore structure. Also, the composition of the pellets must satisfy the ratio of CaO : SiO2 : FeO = 1 : 1.2 : 1.8 to facilitate the formation of slag in the reductive melting process.IntroductionAgglomeration roasting of sulfide lead concentrate is an important phase in the production of lead by reductive melting [1-6]. The reductive melting process is a complex process with contradictory effects of several technological indexes which many times are hard to measure and determine. In this process, loading the water-jacket furnace with pellets of optimized composition and structure can reduce the consumption of coke, and achieve high level of lead recovery. Pellets (agglomerates) should be porous, but at the same time they should have necessary mechanical strength. ‘Self-melting’ ability of pellets is controlled by the types and quantities of fluxes blended into the pellet composition. Three major additives and their role are:"