P. L. Pratt (University of Birmingham, Birmingham, England)—The author has measured the hardening effect of isolated edge and screw dislocation boundaries in a remarkably elegant manner, and he proposes that the detailed structure of the boundary determines its effectiveness as a barrier to slip although "there are still unknown details of the distribution which may be extremely important." On p. 678 the author states "that for a good crystal (one having a yield of about 30 psi) a change in annealing temperature from 300" to 400 °C resulted in a negligible shift in the level of the stress-strain curve." Is this in agreement with the results of the earlier paper by Li, Washburn, and Parker8 in which such a change of temperature produced notable hardening in crystals with a yield of about 30 psi? Or were these earlier crystals, of the same nominal purity, less perfect than those used in this work? The experiment illustrated in Fig. 15, p. 681, shows that the boundary has sharpened after annealing at 400 °C, the temperature at which the hardening effect first becomes apparent. Did the author verify that no sharpening of the boundary occurred at, say, 300 °C where no hardening was found? This would seem to be an important check on the proposed mechanism, especially since zinc of this purity should polygonize at temperatures well below 400 °C within the annealing times used here. There seem to be at least two alternative explanations which could fit these facts: 1—The boundary may sharpen at 300 °C or even lower temperatures but be unable to contribute greatly to the hardening until jogged by thermal vacancies and other impurity atoms after 400 °C anneal. This mechan- ism, discussed in the earlier paper,' is believed to account for the thermal hardening observed by Blank'" in NaCl, as stated elsewhere: and by results from recent experiments which tend to confirm this view. 2—The dislocations in the diffuse boundary may be locked by impurity atoms at 300 °C and thus only sharpen the boundary at 400 °C with the aid of thermal vacancies. In this case it would be difficult to distinguish between the two sources of hardening (sharpening or jogging), using metal of this purity. Jack Washburn (author's reply)—The author wishes to thank Dr. Pratt for his discussion. In connection with his first comment, it should be pointed out that the temperature of testing in the present series of experiments was —196°C, whereas, in the earlier experiments he referred to,' it was 20°C. Therefore, the yield values should not be directly compared. It is likely that the crystals used in the present work were initially more perfect macroscopically than the large shear specimens used previously. The small size of the test section in the kink specimens made it possible to select regions of the large crystals, from which they were acid-cut, that were free of observable small angle boundaries. The sharpening of a microscopically diffuse boundary such as that in Fig. 15 begins in zinc of this purity well below 300°C. However, it is probably not justified to conclude that because a boundary looks sharp under the microscope it has attained the ideal structure. The author agrees with Dr. Pratt that jogging of dislocation lines is one of the structural features of a small angle boundary that should be important in determining its strengthening effect. More detailed information concerning the changes in boundary structure as a

Jan 1, 1956

J. D. Fast and J. L. Meijering (Philips Research Laboratories, N. V. Philips' Gloeilampenfabrieken, Eindhoven, Netherlands)— After the departure of our friend Dijkstra to the United States, investigations on the effect of alloying elements on the behavior of nitrogen in a iron were continued in Eindhoven. We too found internal friction curves with two separate peaks for iron containing nitrogen in addition to 0.5 atomic pct V or 0.5 atomic pct Mo. Our first publication on these investigations" appeared almost simultaneously with the paper now under discussion. At first sight our experimental results seem to be in harmony with their conclusions, but a closer examination reveals that in the case of the Fe-V-N alloy the abnormal peak is not controlled by one time of relaxation only. Whereas iron containing 0.5 atomic pct Mn or Mo absorbs an amount of nitrogen of about the same magnitude as that absorbed by pure iron under identical conditions, iron containing vanadium absorbs in addition one nitrogen atom for every vanadium atom. This last amount, far exceeding the first amount in the case under consideration, combines chemically with the vanadium and causes no internal friction. The "free" nitrogen in the vanadium alloy gives rise not only to a damping peak corresponding to that in pure iron but— due to the presence of VN particles in the metal—also to the abnormal peak at higher temperatures. The VN particles create interstitial sites around themselves where the free nitrogen atoms are bound much tighter than in the normal interstices. These abnormal interstices, therefore, will capture free nitrogen atoms rapidly, whereupon these give rise to the abnormal damping. The binding energy in the abnormal interstices is not the same for all, and with coarsening of the VN precipitate the distribution of these energies is displaced toward the side of stronger binding. This is deduced from a shift of the summit of the second peak toward higher temperatures (from 80" to 88°C in our experiments) caused by prolonged heating at 950°C. From the intermediate state where they cause the abnormal damping, the nitrogen atoms pass over rather rapidly into the fully precipitated state (iron

Jan 1, 1954

Jan 1, 1953

C. M. Bishop (Aircraft Div., A. V. Roe Cnnada Ltd., Toronto)—Reference is made to the coherency hardening of ß due to ß' and also to the hardening of ß due to a coherent precipitation of the a phase. What is meant by the term "ß'?" Would not the coherency hardening of ß during cooling be due to precipitation of a sub-microscopic dispersion of a, as is the case during reheating a ß-quenched alloy? I feel that these two phenomena are essentially the same mechanism, i.e., precipitation of a from unstable or supersaturated ß. From the text, it would appear that Tables III and IV are intended to show the effect of the martensite transformation on the properties of Ti-Mn alloys. Referring to Table 111, the ß-quenched alloys would contain a greater proportion of retained ß than would the equilibrated alloy. Could not the increase in properties be attributed to this, along with possible coherency hardening of the ß? In the same way, the structures referred to in Table IV contain ß from which they could derive their hardness. It would appear to be difficult, if not impossible, to assess the role of the martensite transformation from the data contained in these tables. F. C. Holden, H. R. Ogden, and R. I. Jaffee (authors' reply)—In reply to the first question raised by Mr. Bishop, the term "ß"' designates an apparent retained-p structure which is harder than it is after the most rapid cooling from the ß field. It is thought to be the result of a coherent precipitation of a. The mechanism by which hardening takes place is undoubtedly the same as that involved in the early stages of aging of a re-tained-p structure, and we are in agreement with Mr. Bishop on this point. The term "ß'" to designate the anomalously hard retained-ß structure was agreed upon at a symposium in 1953." The authors do not agree that the quantity of retained ß and/or ß' in the ß-quenched specimens of Table III is necessarily greater than that of the 600°C equilibrated specimens. The ß-quenched specimen has a structure which appears to be completely a' formed by the martensite reaction. It is recognized that there could be some retained ß (or ß') between the a plates if the M, temperature is below room temperature. This is unlikely for the 3.4 pct Mn alloy where the M, is known to be at about 640°C. Therefore, the increase in strength cannot be attributed to the presence of a greater quantity of coherency-hardened ß, but, rather, the increase in strength must be attributed to the transformation products formed, e.g., a' (martensiti-cally formed a). Concerning the data in Table IV, we agree that it is difficult to estimate the role of the martensite reaction, since the 6.4 pct Mn alloy was retained ß in the quenched condition.

Jan 1, 1955

Jan 1, 1957

G. D. Kneip, Jr., and J. 0. Betterton, Jr. (Union Carbide & Carbon Corp., Oak Ridge, Tenn.)—The authors have contributed to the theory of zone melting by considering the effects of the solidification of the final zone on the distribution curves for the finite length bar. However, they do not consider in sufficient detail the restrictions imposed by the particular metals involved. Eq. 4 has the analytical solution which is equivalent to Pfann's' equation for normal solidification of the final zone. For distribution coefficients less than one, it is apparent from this form of the equation that, as the solidification approaches completion, the concentration attains extremely large values which are inconsistent with the density of physical materials. The necessary restrictions then are that the solute concentration cannot exceed the density of the alloy, or more frequently, the solubility limit in the solid phase. Secondly, the distribution coefficient cannot be constant from 0 to 100 pet solute unless the liquidus and solidus coincide over this whole region. It would thus be more correct to impose limits on the solubility such as would be indicated by a typical eutectic diagram. Furthermore, in this case the assumption that the distribution coefficient remains constant is more likely to be realized. Eq. 4 should then be replaced by the following C,,(x) =k/L-x [ ?11 3 C11 (x)Ddx - ?11 4 Cn(x)dx= k[Cn (L-l)/k] [ L-x/l]x-1 L-l = x = L-l [kCenterlie/Cn (L-l)]1/k-1 The typical shape for the distribution curve in the final zone is indicated schematically in Fig. 12 for the simple eutectic case. The solidification proceeds according to Pfann's' expression until the concentration reaches the maximum solubility in the solid phasc. At this point, the concentration changes abruptly to the eutectic composition and remains at this value for the duration of the solidification. The width of the flat region, and the back reflection of this effect into the concentration curve on subsequent passes, depends upon the ratio of the eutectic concentration to the original concentration, upon the distribution coefficient, and upon the number of passes. Similar effects on the concentration curves in the first zone length would be expected in many systems for which the distribution coefficient is greater than one, and where the maximum solubility is not too much larger than the original concentration. The discussers agree with the authors that the assumption that the liquid is uniform in concentration should be considered with caution. Kneip and Better-ton' have shown, however, that in floating zone refining of zirconium, using induction heating, the distribution of iron agrees with theory which assumes a uniform liquid composition. Hence, in this case, the experimentally realized distribution coefficient agrees with the present phase diagram within the experimental uncertainty. L. Burris, Jr., C. H. Stockman, and I. G. Dillon (authors' reply)—The authors are happy to have received the comments of G. D. Kneip, Jr., and J. 0. Betterton, Jr., which provide additional insight into the zone refining process. It is true that the equations developed are inapplicable if the solute solubility in the solid phase is exceeded. However, this restriction on the use of the equations was clearly stated in the paper. A closer approach to

Jan 1, 1957

Jan 1, 1955

DISCUSSION, M. Cohen presiding A. H. Geisler and D. L. Martin (GeneTal Electric Research Laboratory, Schenectady, N. Y.)—We were rather interested to note the author's conclusion that the cubic to tetragonal transformation may be of the second order, for we have been able to show that the order-disorder transformation in an analogous alloy system is a first-order transformation with a discon-

Jan 1, 1952

P. Herasymenko (New York University, New York) —The authors' experiments on equilibria between water vapor and liquid synthetic slags represent a valuable contribution to our knowledge of the nature of liquid slags. They can be regarded as a proof of ionic splitting of water molecules dissolved in slags. The assumption that water dissolved in slag was com- pletely ionized was made in my report on hydrogen equilibria in steelmaking as early as 194010. In that paper, the first systematic data were given on the content of ionized hydrogen in acid and basic open-hearth slags. The paper probably escaped the notice of the authors, although they mention the articles published later by other investigators who reported erratic and

Jan 1, 1958

E. T. Turkdogan (British Iron & Steel Research Assoc., London, England)—I would like to suggest a different method for the treatment of the authors' data on the Si-0 equilibrium in liquid iron. Because the activity coefficient of silicon dissolved in iron is influenced by the concentration of silicon as well as that of oxygen, the equilibrium constant K2 of reaction 2 becomes a function of metal composition, and, as shown in Fig. 1, a plot of log KP1 at 1600°C against the weight percent of silicon gives a smooth curve. A similar curve is obtained when log Kzl is plotted against the oxygen content of iron. Before

Jan 1, 1955

DISCUSSION, G. Derge and D. J. Girardi presiding N. A. Gokcen (Michigan College of Mining and Technology, Houghton, Mich.)—While the authors present very interesting results on the effect of sulphur upon the solubility of oxygen, they have not established convincingly the lines of two-fold saturation (the valleys in Fig. 2) and the ternary eutectic point. Their contention that sample S-7, upon melting at

Jan 1, 1954

T. L. Joseph (University of Minnesota, Minneapolis, Minn.)—Mr. Killian is to be commended for his inquiry as to why a decrease of 15.3 pct in coke consumption was accompanied by a decrease of only 1.9 pct in the CO/CO, ratio of the top gas. Although I encouraged him in his efforts to find a more significant and meaningful carbon-gas ratio, the method, calculations, and conclusions originated entirely with the author. Whether we agree entirely with the assumptions underlying his corrected ratio, I think we can all agree that a better ratio is needed, and that he deserves credit for recognizing the need and for doing something about it. To be most useful, the CO/CO, ratio for the top gas should reflect the way in which the carbon is gasified in the furnace, particularly the degree of oxidation and the extent of heat release. The effect of CO, from the decomposition of the limestone and the effect of the reaction of CO and water vapor in the upper part of the furnace on the quality of top gas should be isolated from the effect of more basic reactions such as ore reduction and solution loss. The reduction of sufficient iron oxide to produce a ton of pig iron and the accompanying changes in the proportions of the carbon gases can be expressed on a mol basis as follows: 16.5FeA + 16.5CO - 33FeO + 16.5CO, [1] 33FeO + 33.0CO = 33Fe + 33CO. [2] The CO, from eq 1 normally escapes from the furnace because it does not react with coke at the temperature of its release. However, as much as 50 pct of the CO, from eq 2 may react with coke because it is released at temperatures above 1000°C: 16.5CO. + 16.5CO2 = 33CO [3] Thus we see that the gasification of 16.5 mols or about 200 lb of C in solution loss will regenerate as much CO as is required for the last stage of reduction. The pronounced effect of reaction 3 on the final proportions of CO and CO, in the gas stream is obvious. It also follows that reaction 3 materially alters the heat release but it cannot be entirely eliminated in Lake ore practice. A previous study indicates that 100 lb of solution loss may be necessary to maintain the reducing power of the gas. A reduction of 100 lb from the normal level of 200 lb would mean that over 1,-000,000 additional Btu are released in the process. The 100 lb of additional carbon which will be burned at the tuyeres will release 437,000 Btu and the absorption of 583,000 Btu by eq 3 would be prevented. One of the chief objectives of sized ore burdens and more uniform distribution of the gas stream is to minimize solution loss by completing reduction higher in the furnace and in turn to release the maximum amount of heat from the carbon charged. It was odd, indeed, to find that the use of sized ore and sinter in the careful tests reported by Dobscha had changed the CO/CO2 ratio very little. The author has stressed the close correlation between his corrected CO/CO, ratio and production. A correlation of fuel consumption and the CO/CO, might be more logical. Fuel consumption on the prepared ore burden decreased 15.3 pct whereas the corrected CO/CO2 ratio decreased 19.0 pct. Although this agreement between the reduction in fuel and the reduction in corrected CO/CO2 ratio is not as close as the correlation with tonnage, it indicates the corrected ratio is superior to the normal ratio which decreased less than 4 pct. Some adjustment should be made for the reaction: CO + H2O = CO2 + H2 —700Btu [41 because there is evidence to indicate that about one half of the hydrogen is formed in the upper 21 ft of

Jan 1, 1953

E. A. Loria (Product Metallurgical Engineer, Crucible Steel Co. of America, Pittsburgh)—In this interesting paper, our introductory work was quoted. We would like to call attention to our sequel paper on the experimental determination of oxygen in cupola-melted cast iron,20 which was not mentioned. Vacuum-fusion oxygen values (as well as hydrogen and nitrogen) were reported for nine heats of cast iron melted in the Battelle 10-in. cupola under normal operating practice and under oxidizing conditions. The oxygen analyses ranged from 12 to 68 pprn compared to the author's computed range of 10 to 80 ppm. The average amount of oxygen found in our irons was about 20 pprn and changes in the silicon content of the iron from 1.32 to 2.35 pct had no consistent effect on the oxygen content of the iron. The gas determination specimens were poured in split steel molds that produced a clean pin, 3/8 in. diam and 2 in. long. Because freezing was almost instantaneous, the pins were entirely white iron (nongraphitic). In the early stages of the investigation, the pins were transferred to a mercury-filled trap system immediately after pouring. This was done to collect gas evolved between pouring and analysis. However, it was found that during storage for 4 weeks gas evolution was negligible. Because the vacuum-fusion analysis was usually completed within 4 days of pouring, pins from later heats were not stored in the mercury-trap system. We found some evidence that cast iron picks up oxygen during long storage, because of rusting. Earlier work by the British Cast Iron Research Association has shown that cast irons may be stored for a long time without significant change in their oxygen content. The practical significance of this study (and our own) would be in the improvement of cast-iron quality. Has the author investigated this aspect and reached any conclusions on the effect of oxygen on the mechanical properties of cast iron? The second phase of our study was to determine the properties of the test bars poured simultaneously with the gas analysis specimens. We realize that there may be complicating factors attendant in this procedure.21 Results from many test specimens measuring chill depth, transverse flexure and deflection strength, spiral fluidity, and sensitivity to hardness of gray irons ranging from 12 to 68 pprn oxygen showed that the lowering of transverse strength was the only significant undesirable effect of high oxygen content. A statistical study of the chill test results21 showed that the iron containing 22 to 46 pprn oxygen had forced chill depths that were 2/32 in. below the expected value from their composition, and irons containing less than 16 ppm oxygen had forced chill depths averaging 1/32 in. greater than the expected chill depth. Higher oxygen contents, within the range of 12 to 68 pprn did not increase forced chill depth. With the wedge tests, there was a good linear relationship between carbon equivalent of the irons and their chill depth. The results indicated that oxygen contents below 50 ppm in the iron did not affect chill depth. With 50 to 70 ppm oxygen in the iron, oxygen appeared to have a slight graphitizing tendency. These results are in disagreement with the common belief in gray iron foundries that "oxidized irons" produce high chill depths. It would be appreciated if the author would comment on this subject. Gustaf Ostberg (author's reply)—In Fig. 1 the legend of line I should read 2 pct C, 1 pct Si. The author wishes to thank Mr. Loria for calling attention to his later work, which was published after the present paper was concluded. The range of oxygen contents quoted seems to agree well with the author's values. The lack of response to variations in silicon content is probably due to the fact that the oxygen content in most cases was below the saturation level. The absence of temperature dependence, even in the case of saturation, is understandable if the difficulty in formation and escape of the deoxidation products is taken into account.

Jan 1, 1960

J. B. Cohen (AVCO Mfg. Co.)-The model presented by the authors is only one of several possible mechanisms for low-temperature aging. It is true that the motion of dislocations to the copper atoms, followed by diffusion along the dislocation lines, is one such mechanism. However, the details of such a process which would :result in copper-rich platelets on (100) planes in the f.c.c. matrix are not clear. Furthermore, there is at least one other mechanism that may be used to e.xplain the authors' results, so that the data do not clearly favor the Turnbull model. The zones may form by "normal" diffusion. The diffusion constants would be higher at room temperature than extrapolated data would suggest due to vacancies trapped in the specimens in the quench. The diffusivity would then be multiplied by the ratio of the number of vacancies present at the solution temperature to that present at room temperature. These vacancies could remain in the alloy specimen for long times at room temerature, due to interaction with the copper atoms. ' The activation energy for diffusion is smaller than that for bulk diffusion at elevated temperatures for it is only that for the motion of vacancies existing after the quench; after these are used up, the aging process effectively ceases. It is somewhat questionable if the laws governing transformation kinetics can be directly applied to changes in elastic moduli, especially in the case of aging where the structure and the composition of the zones may be changing during aging, If such laws are assumed, it is possible to explain the exponential factor of % with this vacancy model. It is probable that the structure of the zones and the matrix match only on (100) planes. Certainly the precipitates that form in this system after various aging treatments show orientation relationships similar to those of the zones. Strains on the edges of the zone may set up fields which do not allow the zone to grow in an edgewise manner. The exponent in the growth of a thin plate in a direction perpendicular to its face would be %. It may also be that copper atoms are attracted to dislocations. If this is the rate-controllin factor in the growth process Ifthisthen an exponent of % or % may arise. The writer would like to know if the authors have tried plotting l/a; proportional to as might be expected for "dislocation drainage." R. H. Doremus (General Electric Research Laboratory)—An important new method for following the growth of Guinier-Preston zones is presented in this paper, and I wish to congratulate the authors on their experiments. Their interpretation of the results, however, is doubtful in certain respects. To determine the exponent m in Eq. [4] the authors plotted -log at against t to various powers (their Fig. 6). The initial value of frequency used for these plots was found by extrapolating the data to zero time. In Fig. A the data from their Fig. 2 are plotted against a linear, rather than logarithmic, time scale. To obtain graphs similar to their Fig. 6 for these data one must use an initial frequency of about 52720; such a plot for m = % is shown in Fig. B. The straight line in Fig. B fits the data in an intermediate range only. The curve drawn in Fig. A was mapped from this line; comparison of

Jan 1, 1960

John Chipman (Massachusetts Institute of Technology, Cambridge, Mass.)—After looking over the authors' shoulders for several years and after many discussions on the interesting diagrams of the types shown, it is a pleasure to see a formal paper published on this subject. There can be no doubt of the practical usefulness of the concepts shown. Inclusion formation in steel is such a highly complex matter that any system for understanding the subject is bound to be welcomed by those who must work with steels and who see in their day-to-day experience the good and evil effects of inclusions. A feature of the work with which the discusser has been concerned, and which he would now like to attempt to explain, is the relation between the schematic diagrams which the authors use and the phase diagrams for related systems. Obviously, the authors' diagrams are in no sense complete phase diagrams. However, there is a relation between this type of diagram and the true phase diagram, and the understand- ing of this relation ought to help in understanding the general picture which the authors are presenting. Consider the authors' Fig. 4, which shows the liqui-dus relations in the Fe-Mn-S-0 system. To show the complete relations between temperature and composition in these four ternary systems would require four triangular prisms, the vertical axes of which would represent temperature. The four triangles of Fig. 4 represent basal projections of certain lines from the four prismatic phase diagrams. Readers of the paper are all more or less acquainted with this type of projection and its usefulness and limitations are generally understood. In order to concentrate on the interesting parts and to minimize the less interesting features, the composition scale may be shifted to de-emphasize regions containing gaseous sulphur and oxygen. Such a diagram is shown in Fig. 16, which is a distorted version of the authors' Fig. 4. Here the oxide of iron is wiistite, denoted by W, and it is to be noted that between W and MnO lies the entire MnO-FeO "binary" system. Similarly, between MnS and FeS lies another binary whose

Jan 1, 1956

R. W. Guard (General Electric Co., Schenectady)— The method of fractional replication discussed by the author has proven very valuable to us in applied research connected with alloy and process development where many of the same experimental difficulties exist. Several of our experiences may be of assistance to those who want to apply the method in these fields. Contrary to the author's observation that interactions are rarely significant, we have found in a number of cases that first order interactions exist which are significant and metallurgically important. Because of this difference there are two further precautions which should be taken in order to minimize the difficulties from this point. First, in evaluating the importance of

Jan 1, 1957

J. Chipman (Massachusetts Institute of Technology, Cambridge, Mass.)—The fact that the experimental work has been applied to copper rather than iron and that the paper is presented to the Iron and Steel Division, I regard as rather significant. It shows the unity of metallurgy and the fallacy of trying to cut it up by metals. This result for the solubility of sulphur in molten copper correlates with Professor Schuhmann's finding that the published data on the other side of the copper-sulphur miscibility gap are also in error. I should like to ask the author to say a little bit more about the sulphur capacity of the slag. T. Rosenqvist (author's reply)-—I hope that Dr. Chipman will find the derivation of the expression for sulphur capacity more clearly explained in the printed version of the paper than in the oral discussion at the meeting. I feel that this quantity, which actually is the ratio of two activities, can be measured more easily than the individual activities. Even if the ratio CaO/CaS is chosen as the standard state, the expression can be used for any slag, even for slags completely free of lime, and it represents a way to put the desulphurizing power of all slag constituents into one bag. Some doubt has been expressed as to whether oxygen ions really exist in calcium oxide and in molten slags. From a thermodynamic view point that question is of minor importance. The term oxygen ion activity, or any activity for that matter, is defined rigorously by the equation: activity = exp u/RT, where u is the change in free energy connected with the transfer of one mol of ions from the standard state into the slag. Whatever happens to the ion in the slag is of no concern to the thermodynamicist. Regardless of whether the ion is "free" in the slag or not, or whether it is present in a very small amount, its activity can always be expressed, and for a thermo- dynamic calculation that is all we need. However, ionic activities will only be of some real value if they are simple functions of the slag composition, or can be measured easily. Concerning the real nature of the oxygen in the slag, my feeling is that the oxygen atom has a rather multiplex nature depending on how strongly it is tied by covalent forces or polarized by the other atoms or ions present. The oxides of iron, cobalt, and nickel differ from calcium oxide and blast furnace slags as to the amount of free electrons that can give rise to electronic conductivity. In slags we know that the conductivity is mostly ionic. The fact that reversible emf's can be obtained with oxygen electrodes in certain salt melts, indicates a significant amount of oxygen ions in these melts. But extended work, e.g. polaragraphic studies and measurements of transference number; are needed to obtain quantitative information about the real structure of the slags. D. E. Babcock (Republic Steel Corp., Youngstown, Ohio)—-With reference to the ion, it might be well to remember Dr. Moses Gomberg. All of his life he had no use for the ionization theory and he contributed greatly to the field of chemistry on the assumption there was no such thing as ions. I do not think we have to worry about whether the oxygen is ionic or not. I think one thing specifically should be brought to your attention and this I think is one of the important contributions of Dr. Rosenqvist. He pointed out what we know as oxygen potentials or what is described as oxygen potentials. I have used this concept for a long period of time and I want to state that if this concept is properly applied, it vitiates much of what we have in the literature, or makes our usual ideas regarding oxidation seem primitive. That one thing is more valuable than almost all the rest of the discussion as a fundamental basis on which to build a reasonable in-

Jan 1, 1952

E. Hill, South Norwalk, Conn. (communication to the Secretary*) :—The phenomenon described by Dr. Ledoux, involving an apparently abnormal high temperature in the air-cylinders of compressors, has not been, so far as I know, discussed in technical literature. The common formula for the adiabatic compression of dry air does not account for heat suficient to flash ordinarily decent cylinder-oils, nor do the text-books include in their theoretical statements any quantitative consideration of the effect of leaks in the ideal machines which they contemplate. This lack I have endeavored to supply by preparing, in the form of a circular, for the use of the customers and correspondents of the Norwalk Iron-Works, a brief mathematical

Jan 1, 1904

Edward Keller, Baltimore, Md. (communication to the Secretary*) :—The authors of this paper are to be commended for their industry and congratulated upon the many interesting results which were the fruit of their researches. While thoroughness has marked their work in general, yet on a few points in particular they have touched but lightly, for which reason, it would appear to me, they have hit wide of the mark in their respective conclusions. The work alluded to pertains chiefly to the occurrence of magnetic iron oxide (ferroseferric oxide) in copper-mattes. Because the authors find that the magnetic residue, left by the dissolved sulphides, varies largely in quantity according to the strength of nitric acid used (with potassium chlorate) in dissolving the mattes, they conclude :— "It appears, therefore, that the ferroso-ferric oxide is the result of precipitation by the oxidizing agent, rather than an original constituent of the matte." In this part of their investigation, Messrs. Gibb and Philp have ignored some well-established data,. In the first place, they have overlooked the fact that there are mattes which are strongly magnetic and others which scarcely show any magnetic property. There is nothing in their work tending to explain this variation. They Seem to have tested none of their products for magnetism. Secondly, they have overlooked the fact that magnetic iron oxide probably exists in all ore-charges in the copper-matting furnaces, and, under the given conditions, that this oxide is very difficult to reduce and to combine with silica to form slag. Thirdly, they pay no attention to the varying specific gravity of the several grades of copper-matte, which may exceed, equal, or fall below that of the magnetic oxide. These are .essential points which, I believe, clearly in-

Jan 1, 1906

Lawrence Addicks, Perth Amboy, N. J. (communication to the Secretary*): The excellent series of photo-micrographs given in this paper shows clearly the relation between micro-structure and cuprous oxide in refined copper. The authors suggest that this method of examillation might be substituted for the " button " method now used to control the refining of cop

Jan 1, 1904