By Seksak Asavavisithchai, Natthida Jareankieathbovorn, Areeya Srichaiyaperk

"Recycling of ADC12 alloy scraps for fabrication of open-cell aluminium foams has been conducted via pressure infiltration method of replication process. The scrap, up to 50 wt.%, was melted with pure aluminium billet, followed by infiltration in a replicated mold of polyethylene foam structure. Compared with the pure aluminium foam, the compressive strength and hardness are higher for the foams with recycled scraps. The increase in foam mechanical properties is due to the presence of Si hard phase in Al matrix. The strength and hardness of the foams also increase with increasing contents of the scraps.IntroductionRecently, open-cell metallic foams have been brought to considerable attention of many industries due to their superior properties; such as large surface area, high specific strength, thermal conductivity, high service temperature and excellent anti-microbial activity, that cannot be found in conventional materials [1, 2]. Typically, open-cell foams are used in functional applications for which a requirement of high strength materials is not demanded. Good examples of such applications include heat exchangers, bone-replacement implants, interconnects, catalyst supports, and sound insulators.Among all types of open-cell metallic foams, aluminium (Al) is the most widely used base metal, due to low material cost, low density, low melting temperature and good corrosion resistance. To improve mechanical properties of Al foam, modification of foam microstructure with addition of alloy elements or ceramic particles is commonly carried out [3, 4]. ADC12 alloy is a typical die-casting Al alloy with high content of silicon (Si) close to the eutectic point in Al-Si binary phase diagram. The alloy is extensively used in the casting industry, due to high wear and corrosion resistance, low coefficient of thermal expansion and excellent castability [5]. The mechanical properties of Al-Si alloy are strongly dependent of Si content."

Jan 1, 2012

By Shadia J. Ikhmayies

"Nanocrystalline CdS thin films were prepared by vacuum evaporation on glass substrates at ambient temperature. The films were characterized by recording and analyzing their transmittance, X-ray diffraction (XRD) patterns, scanning electron microscope (SEM) images and Energy dispersive X-ray (EDAX) spectra. X-ray diffractograms revealed that the material is nanocrystalline with predominant cubic crystal structure and preferential orientation along (1 1 1) plane. SEM micrographs confirmed the nanostructure of the material and showed uniform and well covered surfaces. EDAX reports revealed that the films are cadmium rich and contain oxygen. The first derivative of the absorbance was used to estimate the effective bandgap energies of the nanocrystallites and the hyperbolic band model was used to estimate their radii. The results were compared with those obtained by XRD and SEM measurements.IntroductionCdS thin films are of considerable interest as they can be used in fabrication of solar cells and other opto-electronic devices. In particular, heterojunction solar cells with a narrow band gap base and wide band gap window have been investigated in an attempt to develop efficient, stable and low-cost solar cells [1]. The CdS quantum dot embedded in a glass matrix is one of the well-known quantum dot systems and its electronic and luminescent properties have been studied extensively [2].Three-dimensional confinement of carriers within the quantum dots leads to the blue shift of the optical band-gap and to modification of many properties of semiconductor material [3]. It has been argued that in these semiconductor nanoparticles the hyperbolic band model gives a better fit to the observed quantum size effect as compared to the effective mass approximation [4]."

Jan 1, 2012

By Jason Ganley, Yingjia Liu, Adam Dekich, William Tilson, Jeffrey Fergus, Dileep Kumar CJ

"Manganese cobalt spinel oxide coatings have been shown to be effective for preventing chromium volatilization from interconnect alloys, and the associated cathode poisoning, in solid oxide fuel cells. During high temperature exposure a reaction layer consisting of chromium containing spine! forms due to reaction with the chromia scale formed on the alloy. The electrical conductivity of this reaction layer is much lower than that of the coating material and thus can increase the overall area specific resistance (ASR) of the system. The approaches to reducing the ASR are to reduce the thickness and/or increase the electrical conductivity of the reaction layer, which includes both the high-chromium spinel phase and the chromia scale. In this paper the effects of transition metal dopants on the amount and properties of reaction products formed during the reaction of spine! oxide coating materials with chromia are presented.IntroductionThe high cost and difficulties involved with the processing of chromia based ceramic interconnect materials for SOFCs are driving the search for metallic interconnects [1, 2]. The reduction in the operating temperature of SOFC has allowed for the use of high chromium alloy steels for this application [3]. However, the volatilization of chromium from the chromia scale, and the associated poisoning of the cathode, remains a problem which needs to be addressed [ 4]. Though the application of manganese cobalt oxide spine! coatings on the alloy surface substantially reduces chromium poisoning of the cathode [5], the low electrical conductivity of the reaction layer formed between the chromia scale and coating affects the performance of interconnect. Incorporating transition metal ions in the reaction layer could alter the electrical characteristics and improve the performance. Copper and nickel doped manganese oxide spinels are widely used as thermistors due to their high electrical conductivity and negative temperature co-efficient of resistance characteristics [ 6, 7]. Hence doping of copper and nickel in manganese-cobalt spine! oxide composition may improve the electrical characteristics of interaction layer as well and is attempted here."

Jan 1, 2012

By Suleyman Tekeli, Serdar Salman, Bulent Aktas

"The effect of La2O3 content up to 15 wt% on phase stability, sintering and microstructure of cubic zirconia (8YSZ) was investigated. XRD results showed that the specimens containing up to 15 wt% La2O3 were composed of only cubic structure. Also, the specimens doped up to 5 wt% La2O3 revealed no La2O3 peaks, indicating that La2O3 was completely solubilized in the cubic structure. However, when> 5 wt% La2O3 was added, the peak of La2Zr2O7 compound emerged, showing that the overdoped La2O3 was not solubilized in the 8YSZ matrix. The lattice parameter of the 8YSZ slightly decreased with the increasing La2O3 content up to 1 wt% but further increase in the La203 amount resulted in an increased lattice parameter. The comparison of grain size of the 8YSZ specimens with various La2O3 content showed that grain size slightly increased with the increasing La2O3 content up to 1 wt% but further increase in the La2O3 amount resulted in a decreased grain size.IntroductionAt atmospheric pressures, three polymorphic forms of Zr02 are stable at different temperatures i.e. monoclinic, tetragonal and cubic. A high-pressure orthorhombic form of Zr02 has also been reported[l]. The successful production of pure Zr02 bodies is not possible all the time due to the large volume expansion associated with the martensitic tetragonal-monoclinic transformation. This fact restricts the applications of zirconia, in spite of its excellent mechanical and thermal properties. However, the stabilization of the high temperature polymorphs at room temperature as stable phases is made possible by addition of suitable dopants. Fully stabilized cubic Zr02 and partially stabilized tetragonal Zr02 show interesting properties and are widely used as ionic conductors, coatings and gas sensors in solid oxide fuel cells and structural applications[2]. Most frequently used dopants include Y203, CaO, MgO and Ce02, although other oxides, such as those of rare earth elements, can also act as stabilizers of the high temperature structures. The incorporation of aliovalent cations to the lattice, forming substitutional solid solutions, allows to control the concentration of anionic vacancies in the structure. This aspect is particularly important in designing ionic conductors[3], and is also determinant in the stabilization process[ 4]. The process of stabilization with larger ionic radii dopants is rationalized by the crystal chemistry model[ 5], that describes the dopant cations as typical stabilizer when they have larger ionic size, lower charged state and higher ionicity than Zr4+ The ionic radius of Zr4+ is 0.84 Å and that for La3+ is 1.016 Å [6]."

Jan 1, 2012

By Sundarrajm Suresh, Hrushikesh G. Pimpalgaonkar, Thiyagarajan Paramadayalan

In this paper, a model of a fuel cell system has been proposed to account for the membrane physics at the micro level which is coupled with the macroscopic flow and mass transport phenomena occurring in a single channel of a Polymer Electrode Membrane Fuel Cell (PEMFC) system. We have developed a novel approach to model the catalyst layer electrochemical processes in a Membrane Electrode Assembly (MEA) and coupled it with mass transport and fluid flow calculations at the channel level using STAR-CD commercial software. The predicted values of the cell voltage from this micro-macro model are validated with experimental data available in the literature. A sensitivity analysis has been carried out to study the effect of the design and operating parameters such as catalyst loading and initial temperature on the overall performance of the PEMFC. The results indicate that the cell voltage increases at higher platinum catalyst loading and is also independent of the choice of initial cell temperature.

Jan 1, 2012

By Lucas Nana Wiredu Damoah, Lifeng Zhang

"The use of electromagnetic field to remove suspended particles from metals such as aluminum by pushing to the boundary has been well studied. However, the potential of this method is yet to be exploited for the removal of inclusions from silicon. Considering the increasing amount of Top-cut SoG-Si scraps year upon year, there is the need to harness all the potentials of technologies to recycle this materials to ensure sustainability. This study investigates, and discusses new results on the effect of processing parameters such as composition, coil current, and frequency on the removal of inclusions from silicon under high frequency AC electromagnetic field.IntroductionThe solar cell silicon making industry requires pure and clean silicon in order to maximize the conversion potential of the solar cell material. The conversion efficiency of solar cells is limited by minority carrier recombination at dislocations and those intra-granular defects such as impurities, small clusters of atoms, or precipitates [1]. Recent global developments in the energy sector with a drive for the production of clean, reliable, and affordable energy have stirred a rapid growth in the production of photovoltaic (PV) cells.[2] Thus over the years, silicon based PV cells has seen a lot of growth as it has a PV market share of over 90 % [3] either as single-crystalline silicon, or multi-crystalline Si (MC-Si), or amorphous Si [4]. MC-Si produced by directional solidification of solar grade silicon melt dominates the silicon PV market. During the directional solidification process, SiC and Si3N4 particles within the melt are pushed by the solidification front to the top of the ingot which is the last to solidify. Therefore the top of the ingot is cut generating what is known as top-cut solar silicon scraps. The Si3N4 particles are mainly from the coating material at the inside surface of the silica crucible and from the air absorption during solidification process. The SiC particles mainly stem from the carbon reduction process of the primary production of silicon [5]. For sustainability the silicon in the top-cut silicon scraps must be recovered. Therefore methods for removing non-metallic particles, such as SiC and Si3N4, from the silicon are important in order to recycle the top-cut scraps to a useful feedstock for the silicon solar cells manufacturing."

Jan 1, 2012

By Bo Yan, Jiaquan Zhang, Haibo Sun

"Based on the validation of steady-state isothermal mathematical model by a 0.4-scale water model for the single-strand slab casting tundish, the effect of varying pouring temperature on the flow, temperature field, and residence time distribution(RTD) of the liquid steel was studied by a transient hydrodynamic model. Due to the decreasing temperature of ladle stream over a casting period of 50 min, the direction of vortex flow at the downstream side of dam changes to clockwise from the anticlockwise at 4 min after the new teeming, and reverts to anticlockwise direction again at 43 min. Meanwhile, the melt flow state in the dam hole is also varying with time. For conventional isothermal water modeling, the RTD parameters obtained are much different as compared with the non-isothermal ones. For the flow control devices(FCD) design, however, the identical optimal scheme can be concluded from the point of view of isothermal modeling.IntroductionOriginally, tundish was adopted as a buffer and distributor to hold and allocate molten steel for sequence casting upon ladle exchange and to provide a desired steel flow rate to the mould below. With the increasing demand to strand quality, the tundish has become a critical metallurgical reactor to enhance inclusions removal, avoid reoxidation of molten steel, and prevent slag entrapment. The general trends to obtain these metallurgical effects are to optimize steel flow pattern and to extend the residence time of molten steel in the tundish through increasing the volume of tundish and/or using FCDs in the interior of the tundish."

Jan 1, 2012

By Tiruttani Munikamal, Suresh Sundarraj

"A numerical model of the induction hardening process of steel cranks has been developed and the predicted results of temperature and phase distribution during this solid state phase transformation process are verified with experimental data from the literature. This heat treatment process involves heating the crank to the austenitic temperature range followed by rapid quenching in water to harden the surface of the crank. The model has been developed using ABAQUS, commercial FEA software. The formation of martensite, pearlite, and retained austenite phases are modeled and implemented through a user defined function in ABAQUS. A sensitivity study on the various process parameters affecting the amount of phase distribution has been carried out.IntroductionThe type of surface and sub-surface microstructure as well as the residual stresses that are present in a component after manufacturing, significantly affects it fatigue performance. The wear resistance of the automotive components such as crankshaft, gears, camshaft and bearings depends on the surface hardness. In order to achieve the surface hardness, these steel components are subjected to a type of quench hardening heat treatment process. There are several heat treatment processes available for the industrial application to improve the mechanical properties of the final part. Case hardening using induction heating is one of the widely used industrial techniques for improving the surface microstructure of a steel component. It consists of two stages i.e. induction heating cycle, followed by quenching in a fluid medium (usually water or oil)"

Jan 1, 2012

By Jinfu Xu, Youqing Cao, Yuting Lv, Hang You, Peng Jiang

"In present work, we reported the fabrication of composites consisted of M42 powder metallurgy high speed steel and 45 steel at one step via spark plasma sintering (SPS) technology. The interface microstructure, compositions and microhardness with the interface forming mechanism were investigated. The results show that the morphology and microhardness within the M42/45 steel interfaces exhibit a gradient distribution. The interfaces possessed a transition layer up to 10.2 ?m with few distortions and microcracks. The formation of M42/45 steel interfaces were driven by both fusion and diffusion processes. The former one was primary at the early sintering process, while the later one becomes dominant over the followed sintering process.IntroductionPowder high-speed steels have been widely used in cutting tools, cold-hot tools and dies, as well as in cut materials and structure parts with wear resistance and high-temperature resistance, due to its high hardness, good wear resistance, desirable cutting toughness and favorable hot hardness [1-2]. For materials of some parts in practical production, not only the favorable toughness is required to resist the impact action, but also the high hardness and exceptional wear resistance are demanded. According to the functional requirements and working conditions, bimetal composite materials are prepared in a certain mode, proportion and distribution, by designing two metals with different chemical and physical properties [3-6]. Considering the composites exhibit different properties in different positions of the parts with a combination of the advantages of two metals, they can obtain enhanced properties that the single one can not achieve."

Jan 1, 2012

By Merete Tangstad, Gabriella Tranell, Jeff Kline

"Raman spectroscopy as an instrumental technique for the determination of silicate structure is widely accepted. This method was utilized for analysis of structural modifications associated with the addition of network modifying species. Silicate melts are described by the extent of oxygen bridging. Therefore, understanding the effect different oxides have on modifying the silicate structure will provide valuable information regarding the removal of boron from silicon in slag refining processes. Samples ranging from CaO/SiO2 = 0.56-1.2 were evaluated with and without varying concentrations of B2O3. The addition of CaO to SiO2 revealed Q2 species constitute 45% of the Qn species and addition of B2O3 to the high concentration CaO system results in an increase in Q2 and a decrease in Q0 . The disappearance of the Raman band associated to the three-member ring in the low concentrated CaO system indicates boron addition and destruction of the ring.IntroductionExtensive studies on the structure of silicate systems have been performed using Raman spectroscopy with consensus on the Raman shift associated with different bridging oxygen units [1]. Most of these studies are motivated by the lack of a fundamental understanding of the processes involved in petrology. Due to this, an opportunity exists to build on the knowledge obtained from these studies and conduct more research on slag structures relevant to industrial applications, as these systems are often compositionally similar to magmatic melts. Raman spectroscopic studies of industrial slags will provide insight into the possible structural modifications necessary to enhance removal of impurity species from the metal phase to the slag phase."

Jan 1, 2012

By Antonio Martin, Jesus Hurtado, Francisco Jimenez

"Atlantic Copper is one of the largest copper producers in Europe. Its production facilities, including a primary copper smelter and an electrolytic refinery, are located in Huelva, on the southwest coast of Spain. These installations enable the smelting of over 1 million tpy concentrates to produce up to 260,000 tons per year of cathodes and 900 ktpy of sulphuric acid.Since 1970, several improvements have been made at the Converters Area such as modifications of primary hoods, operations with an OPC system, installation of scrap chargers, the recent installation of the secondary hoods and other environmental projects. All these modifications have been aimed at increasing the capacity of our smelter while keeping our continuous environmental commitment.This paper describes the modifications and improvements carried out at the converters area and our proposals for future developments."

Jan 1, 2012

By Reza Kamali, Mohsen Bashiri, Hadi Fanisalek

"Nomenclature: A: area (m2), C: heat capacity (WIK), cp: specific heat (J/Kg K), d: internal tube diameter (in), F: correction factor for multi-pass and crossflow heat exchanger, h: convective heat transfer coefficient (W/m2K), k: thermal conductivity (W/mK), L: length (m), m: mass flow rate (Kg/s), W: flow rate, N: number, Q: heat rate (W), R: thermal resistance, T: temperature (°C), U: overall heat transfer coefficient (W/m2K), ;1,,P: pressure drop (Pa), ;1,,T: temperature difference (°C), p: density (lb/ft3), N: number of tube passes, U,: velocity in tubes, iJh: head loss in feet of flowing fluid, Up: velocity in the pipe leading to and from the heat exchanger (ft/sec), µ: viscosity ( cp ), Llpf frictional pressure loss (psi/l 00 equivalent ft of pipe) Subscripts: b: baffle, c: cold, cf counter flow, ex: exchanger, f: fouling, h: hot, i: inlet-inner, ib: inlet baffle, lm: logarithmic mean, m: mean, o: outlet-outer, s: shell, t: tube, w: wall AbstractThe main bottleneck for primary aluminum production industry is dealing with a huge amount of input energy. The fact is that part of provided energy to aluminum production smelters will be lost as waste heat and it never used for aluminum production. One part of waste heat is escaping from the potroom exhaust gases, which was studied for possible recovery in a desalination plant to produce distilled water and the paper was presented in 2011 TMS Annual Meeting. However, it was shown that waste heat recovery plant to produce distilled water is highly profitable but the main fact is that the exhaust gases from potroom are highly corrosive, abrasive and dusty. The main challenge for desalination plant construction, which is using aluminum smelter exhaust gases as the main heat source, is the highly corrosive environment that makes the situation difficult and complicated for equipments design and plant construction. In this paper, we are trying to study a detailed investigation regarding the heat exchangers fouling, corrosion in heat exchangers including heat exchangers' material, how often we need to shut down the plant for maintenance or cleaning, and plant thermal efficiency with considering fouling."

Jan 1, 2012

By Junhong Noh, Kug Sun Hong, Jung-Kun Lee, Bo Ding

"The photocatalytic splitting of water into H2 and O2 by oxide nanoparticles has received much attention. However, the full potential of photo-catalysts for efficient hydrogen generation out of water has not been fully realized yet due to unresolved limitations including the low electrical conductivity and ineffective carrier extraction. Here, we report composite oxide materials consisting of 1-dimensional (1-D) transparent conducting oxide (TCO) core and TiO2 shell. Highly conductive ITO nanowires were grown on a flexible SUS mesh as a core component. The photoelectrodes consisting of these 1-D nanocomposites have increased carrier mobility due to the TCO core, while the TiO2 shell provides the photocatalytic functionalities. In addition, the built-in-potential at the interface between TCO core and the TiO2 shell improves the collection of charge carriers from TiO2 to TCO. These factors altogether contribute to increasing the photocurrent of the device under light.I. IntroductionPhotocatalytic behavior of semicondcutors has been extensively explored since it was discovered in TiO2 in 197Os. When TiO2 is exposed to UV light, the light is absorbed and electron/hole pairs are generated in the conduction and valeence bands. Holes in valence band will oxide/mineralize pollutant target directly or indirectly (via mediator hydroxyl radical). If the adsorbed A is O 2, O 2 will react with electron from conduction band to generate hydroxyl radical as described in the second set ofreactions. The photocatalytic reaction is schematically explained in Figure 1.Photoelectrochemical (PEC) cells using the photocatalytic reaction have attracted emerging interest as a potential route to convert solar radiation into useful forms of energy by reaction such as water splitting to generate hydrogen1 or the reduction of carbon dioxide.2 Another application ofphotocatalysis is water splitting and CO2 reduction, both of which utilize the electrons that are optically excited to the conduction band. 3•4 For this purpose, the conduction level of the semiconductor should be higher than hydrogen production level (EHZ1HZO) while the valence band should be lower than water oxidation level (Eo21112O). Electrons and holes will be generated on the semiconductor site, and holes generate O 2 at semiconductor site, while electrons will migrate to counter electrode to execute reduction forming H2. In addition to that, materials should be chemically stable to resist photocorrosion and have long lifetime of electron/hole pairs. TiO2 is a suitable material from the viewpoint of band arrangement and chemical stability requirement"

Jan 1, 2012

By C. A. Nogueira, F. Margarido

"A research work has being carried out annmg at evaluating the possibility of treating simultaneously several electrochemical systems of spent batteries using the same process, in order to overcome the high costs and difficulties of selective collection and sorting. Zn-Mn02 systems, representing more than 75% of portable battery market, shall be treated in dedicated processes. The treatment assessment using a single hydrometallurgical process of the other major systems (NiCd, NiMH and Li-ion), having Ni and Co as main metals, was the aim of the research work here reported. Sulfuric acid leaching was demonstrated to be adequate for dissolving more than 90% of the metals of interest contained in batteries. The subsequent separation of metals by solvent extraction, using organophosphorous extractants like DEHPA and Cyanex 272, allowed the production of pure solutions of rare earths, cadmium/manganese, cobalt, nickel and lithium, enabling their further recovering.IntroductionRecycling is the best approach for end-of-life management of spent batteries mainly by environmental reasons but also motivated by resources conservation and, in some cases, by economic profits. Most relevant electrochemical systems of portable cells are Zn-Mn02 (ZMB, alkaline and saline), nickel-cadmium (NiCd), nickel-metal hydride (NiMH) and lithium-ion (LIB). These batteries are collected, sorted and usually treated separately, applying for pyrometallurgical or hydrometallurgical technologies, the former being the most common.Several processes have been developed and some of them industrially applied, as described in some available review papers [l, 2]. In Europe for ZMB systems the oldest processes are Batrec [3] and Citron [4]. Although having differences in details, both are based on pyrometallurgical recovery of zinc by distillation, in metallic or oxide forms, being manganese retained in the slag together with iron. Hydrometallurgical alternatives are also available, like Zincex [5] and Recupyl [ 6] processes, both using sulfuric acid solutions as leachant. The application of the existing technologies to battery recycling, instead of using dedicated processes, is other alternative already tested, being the Waeltz furnace or the Imperial Smelting some examples."

Jan 1, 2012

By B. Balamurugan, D. J. Sellmyer, J. E. Shield, G. C. Hadjipanayis, Damien Le Ror, R. Skomski

"Rare-earth transition-metal (R-TM) alloys show superior permanent magnetic properties in the bulk, but the synthesis and application ofR-TM nanoparticles remains a challenge due to the requirement of high-temperature annealing above about 800 °C for alloy formation and subsequent crystalline ordering. Here we report a single-step method to produce highly ordered R-TM nanoparticles such as YCO5 and SmCO5, without high-temperature thermal annealing by employing a cluster-deposition system, and we investigate their structural and magnetic properties. Nanoparticles of size = 10 nm are monodispersed (s /d ~ 0.15) and have Hc values at T = 300 K of 8.0 and 4.5 kOe for YC05 and SmC05, respectively. Alignment of the easy axes is performed via a field applied to the clusters before deposition. These processing steps are highly desirable to create and assemble R-TM nanoparticle composites for future permanentmagnet applications.IntroductionMagnetic nanoparticles with high magnetocrystalline anisotropies (Ki > 1 MJ/m3) are required for permanent-magnet, recording-media, and other significant applications [1-3]. In this regard, bulk rare-earth transition metal alloys (R-TM) especially RC05 (R = Y and Sm) crystallized in the hexagonal CaCu5-type structure have shown a large Ki = 5 MJ/m3 (YC05) and 22 MJ/m3 (SmCo5) along with an appreciable saturation-magnetic polarization (Js, > 10 kG) and high curie temperatures (Tc > 1000 K) [2]. The challenges in controlling the size, sizedistribution, phase purity and crystalline ordering, however, limit the research on RCo5 nanoparticles [4,5]. The conventional arc-melting technique requires high-temperature annealing for alloy formation and subsequent crystalline ordering, which causes excess growth and thus results in nanocrystalline powders of particles sizes larger than 30 nm [6, 7]. Low-temperature wet-chemical techniques yield SmC05 nanoparticles of sizes smaller than 20 nm [5], but the control of phase purity is challenging due to the presence of surfactants and formation of other secondary phases [8]."

Jan 1, 2012

By Feng Chen, Lirong Chen, Yufeng Guo, Wenjie Weng, Tao Jiang

"In this paper, the carbonthermal reduction behavior and the influencing factors of Panzhihua ilmenite under the condition of carbon-burdened were systematically investigated. The results show that the ilmenite forms into titanium nitride during the reduction process at 1200 °C under the condition of carbon-burdened. Carbon-burdened is beneficial to the reduction of iron oxide, but less favorable for the growth of iron grain.IntroductionThe titanium ferrous resources are very rich in Panzhihua-xichang area, accounting for about 38.85% of the world's proved reserves [1]. However, TiO2 grade of this kind of ilmenite is low and calcium magnesium content is high, it generally requires preconcentration to titanium-rich material—titanium slag or synthetic rutile.Chlorination process is an advanced method for production of titanium dioxide, which should takes high quality titanium-rich material with low content of calcium and magnesium as raw materials (the content of MgO and CaO are less than 1.0%). Ilmenite in Panxi area, however, contains high calcium and magnesium; it is not suitable as a raw material for chloride process. Methods of producing titanium-rich materials which have been applied in industry are electric smelting, various acid leaching and reduction rust [2-5]. There still exist some problems such as CaO and MgO removed not thoroughly, low resource utilization, high energy consumption and environmental pollution."

Jan 1, 2012

By Xiang (Frank) Chen, Mikhail A. Sokolov, Randy K. Nanstad

"Nickel-base Alloy 617 is being considered as a structural material for application in the secondary heat exchanger of the New Generation Nuclear Plant, a very high temperature gascooled reactor. Thermal aging of Alloy 617 plate and welds is being performed with tensile, Charpy impact, and fracture toughness tests conducted at temperatures to 950°C. Results of testing for thermal aging to 5,300 h have been obtained and are presented; varying effects of thermal aging temperature and time on fracture toughness are observed. The 9Cr-1MoV (Grade 91) ferritic steel is a candidate for structural applications in the sodium fast reactor. Fracture toughness testing of unaged Grade 91 steel has been performed to evaluate specimen size effects in preparation for future testing of the material in the thermally aged condition. Results for material in the mill-annealed and heat treated conditions are presented and show that this heat of Grade 91 steel does not indicate a small specimen bias on the fracture toughness Master Curve reference temperature.IntroductionThe behavior of advanced engineering materials will be a critical factor in the performance of Generation IV reactors. In the case of materials utilized for reactor internals and pressure vessels, the effects of irradiation and long time thermal aging are major issues. The environmental conditions for some of the Gen IV reactors are generally beyond present day reactor technology, requiring new experimental data as well as analytical predictions of expected behavior of candidate materials at conditions for which there are only sparse or no experimental data. The radiation environments and several key materials issues for some Gen IV systems are summarized in Section 5 of [l] as a starting point for modeling and microstructural analysis of Generation IV materials. More detailed descriptions of materials research and development needs and recommended activities for the SCWR, VHTR, and GFR are provided in references [2, 3, 4], respectively. Mansur, et. al. provide an interesting comparison of materials needs for Generation IV reactors to corresponding needs for fusion reactors and spallation neutron sources in [5]. The two primary candidate reactor systems currently undergoing significant research and development by the U.S. Department of Energy (DOE) are the New Generation Nuclear Plant"

Jan 1, 2012

By David Roha, Øyvind Mikkelsen

"Significant resources have been spent throughout the years in the investigation of production of aluminum by carbothermic reduction. Due to the technological challenges involved, the efforts have not yet resulted in a commercial process. An initiative to overcome issues that prevented previous attempts to succeed was taken by Alcoa through the Advanced Reactor Process. The research program has resulted in technical developments which have resolved many of the previous issues. The knowledge about the process has continuously improved through physical and computer modeling as well as by experimentation at various scales. The technical achievements together with improved process understanding have resulted in a reactor design able to continuously operate the process for several weeks at the time, with hundreds of kilograms of alloy in every tap.IntroductionThe Hall-Heroult process has since its invention in the late 19th century, been essentially the only process used for commercial production of primary aluminum. The process has so far proved to be superior to all potential process alternatives and has continuously been improved. Although the Hall-Heroult is a reliable process it also has challenges:"

Jan 1, 2012

By Kurt Svens

"As zinc consumption is gradually increasing all the time in the world, many zinc plants are looking for possible expansions. As the sulphuric acid market as well as the fertilizer market in many areas is saturated, the costs for the roasting-acid plant section of the zinc plant will create problems when making feasibility calculations for possible expansions. For solving the customers' situation, two proven zinc concentrate direct leaching technologies are available. A third one, which is possible, does not have any industrially proven applications in the zinc area.IntroductionTime to time, the zinc plants in the world scrutinize their operations with respect to their cost efficiency, the total zinc recovery and the near-by or far-away consumer markets, especially the for zinc and sulphuric acid. Their preliminary profitability calculations can show that a possible total expansion is not economical, when they are looking to expand the whole roasting/acid plant - leaching - solution purification - electrowinning - casting route, as the possible market price for the sulphuric acid is low or the sulphuric acid market is too far away. Based on these facts, their economical study often indicates that implementing a zinc concentrate direct leaching option could be more favourable. Regarding this situation, several aspects concerning three alternative direct leaching methods will be discussed, of which pressure leaching and the atmospheric leaching processes have several industrial applications in the zinc industry, as the ultrafine grinding - conventional leaching process at present has none. As iron is also dissolved during zinc concentrate direct leaching, iron removal processes generally used in the zinc industry are additionally discussed below."

Jan 1, 2012

By Erik Olsson, Gunilla Hyllander, Stefan Schuster, Lena Sundqvist Ökvist, Maria Lundgren, Michael Hensmann, Olavi Antila

"Residual materials from the integrated steel plant itself or other sources often contain valuable compounds of e.g. C and Fe. Dust and sludge have to be agglomerated to be able to recycle to the blast furnace (BF) via top-charging. By injection of the materials, preparation methods in terms of e.g. drying and/or screening only, can be used. Alternative carbon materials (ACM) in terms of BF dust and sludge have been successfully injected up to levels of 60 kg/tHM in the LK.AB Experimental Blast Furnace (LKAB EBF®). Efficiency in recovery of valuable compounds as well as the behavior of undesired elements have been evaluated and are discussed.IntroductionTraditionally, recycling of steel in-plant fines is made via the sinter plant and blast furnace route. Steel plants operating with 100% pellet as ferrous burden and have no sinter plant. There are limited areas for land fill and costs are caused for preparation of landfills and deposit fees. Very fine paniculate dusts or sludges cause decreased productivity and increased coke rate in the sinter plant, and therefore other ways for recycling must be considered. Injecting them into the BF could be an economically and technically feasible alternative. Additionally, as the materials contain valuable compounds of e.g. C and Fe."

Jan 1, 2012