By J. P. Gous, J. J. Sutherland

"Transalloys is a silicomanganese (SiMn) producer located in South Africa, and uses only local manganese ores to produce SiMn alloy. The plant operates five open submerged arc furnaces (SAFs) with an annual capacity of 180 000 t of saleable SiMn.Maintaining tap-holes is critical for effective furnace operation, allowing proper drainage of the furnace with minimal operator interference. Using a claygun and drill arrangement installed at each furnace, tapping occurs every four hours. Tap-holes are maintained through mickey replacement and brick repairs. Three furnaces have SiC tap-holes and two have graphite tap-holes.This paper gives a review of SAF operation, furnace and tap-hole design, daily tapping operation, and maintenance practices for repairing tap-holes.IntroductionDefining tap-hole life cycle, Steenkamp et al., (2016) highlighted four main steps: installation during furnace relines, day-to-day operations, tap-hole maintenance, and tap-hole repair. The authors argued that the design of the tap-hole area should allow for all four stages in the tap-hole life-cycle. Design principles for each stage were presented using silicomanganese (SiMn) production as a case study. Here we present a further analysis of the case study by providing practical examples of how the tap-hole life-cycle is managed at Transalloys during the design, operation, and maintenance of submerged arc furnaces (SAFs) applied in the production of SiMn.BackgroundTransalloys is the largest producer of SiMn in Africa. Its smelter complex is based outside the town of eMalahleni, in the Mpumalanga Province of South Africa. Transalloys was commissioned in the mid- 1960s as a high- and low-carbon ferrochromium plant based on the Perrin process. In 1967 the plant was converted to SiMn production because of constraints in the ferrochrome market (Basson, Curr, and Gericke, 2007; Bezemer, 1995). Today, the installed production capacity is 180 000 t of SiMn annually. Plant operations consists of five SAFs (see ratings in Table I), operating 24 hours a day, 365 days a year (including maintenance), involving 280 permanent employees, with up to 120 contract employees on site at any given time."

Jun 1, 2019

By K. S. Liddell, L. A. Smith

"Kell is a hydrometallurgical treatment option for the recovery of platinum group metals (PGMs), gold, silver, and base metals from flotation concentrates to refined products on site. The process is cyanidefree, while eliminating emissions of sulphur dioxide, arsenic trioxide, and other toxic species often emitted by smelters and roasters. Kell has been tested on a range of concentrates, including PGMs (UG2, Merensky, Platreef, Great Dyke, Great Lakes, Lake Superior and others), refractory gold-silver, coppergold, and polymetallic concentrates. High extraction efficiencies (>95%) are achieved for value metals (Pt, Pd, Rh, Au, Ag, Ni, Cu, Co) and secondary metals (Sb, Zn, Pb, and others). Studies comparing Kell with smelter-refining show economic benefits: capex 18–33% of smelting; opex 51–66%; electricity consumption 13–46%; and environmental benefits: greenhouse gas emissions 57–61% of smelting, acidification 5–27%, human toxicity 37–62%, and freshwater ecotoxicity 43–55% of smelting. Synergies for Kell plants alongside smelter-refineries include utilization of recovered acid from sulphur abatement systems and excess capacity in precious metal refineries. Kell is unconstrained by concentrate grade and impurities, allowing the co-location of Kell plants for treatment of non-smeltable concentrates alongside existing smelters.Kell has been demonstrated in a nine-week integrated pilot campaign at 1:1000 scale, supporting a bankable feasibility study for a 110 000 t/a plant treating a UG2-Merensky concentrate at Pilanesberg Platinum Mine (PPM), owned by Sedibelo Platinum Ltd, which has along with South African Industrial Development Corporation (IDC), invested in Kell. Zimbabwean Mining Development Corporation (ZMDC) has signed a Memorandum of Agreement (MOA) with KellTech for a centralized PGM concentrate processing plant."

Jun 1, 2019

By L. Sahu, S. Bhattacharya, S. Dey

"An ideal procedure to determine the limits of flotation-based separation, as is the case with washability analysis for density separation, does not exist. Therefore, a procedure called release analysis, considered to be the counterpart of the washability process in density separation, was developed to evaluate the flotation characteristics of coal fines. Since flotation is a complex process it is necessary to know the maximum recoverable yield that could be achieved at a target ash level and what could be obtained by release analysis. Due to a number of limitations in the initial procedures, modifications were recommended by various researchers to generate an optimum separation curve. This paper presents a review of, and a discussion on, the chronological evolution of release analysis methodology over the decades. Notwithstanding the availability of a standardized release analysis procedure, such as BS 7530, the paper highlights the critical parameters involved in the procedures, such as coal type, feed characteristics, choice of reagents and dosage, operator bias, and design features of the flotation cell IntroductionCoal is a heterogeneous substance consisting of various combustible constituents (macerals) and associated mineral matter. The kind and abundance of the various macerals present in the coal, such as vitrinite, semivitrinite, exinite, and inertinite, determine the type of coal. As macerals are formed by biological degradation of different parts of the plant material, they have different properties based on their original composition. Coal cleaning processes are dependent on the differences in physical properties between the coal components (the macerals) and also between the macerals and the mineral matter. Thus the cleaning characteristics of the coal might vary from one type to the next. The cleaning processes influence the distribution and the concentration of macerals in the various size and density fractions of the cleaned product."

Jun 1, 2019

By J. D. Steenkamp

"In July of 2016 and June 2017, major tap-hole repairs were carried out during the annual shutdown of two 63 MVA submerged arc furnaces producing ferrochromium in South Africa. The hot excavations of the tap-holes allowed for a study of the wear profiles. Subsequent thermodynamic calculations allowed for the quantification of the potential for chemical reaction between refractory and slag or alloy contributing to wear in the tap-hole area. Results from both wear profiling and thermodynamic calculations are reported here. IntroductionFerrochrome (FeCr) is an essential alloy in the production of stainless steel (Gasik, 2013). In 2017, 11.7 Mt of FeCr was produced (Pariser et al., 2018.). The main producers were China (39%), South Africa (29%), Kazakstan (12%), and India (8%).A number of grades of FeCr are available to producers of stainless steel, including high-carbon ferrochrome (HCFeCr) (Gasik, 2013). HCFeCr typically contains 60–70% Cr and 4–6% C (Basson and Daavittila, 2013). When the chromium content is lower (50–55% Cr) and the carbon content higher (6–8% C), it is referred to as charge chrome. Charge chrome is typically produced in South Africa due to the grades of ore available.FeCr is produced in submerged arc furnaces (SAFs) and in open arc furnaces (Mc Dougall, 2013) by carbothermic reduction of oxide raw materials. In a SAF the electrode tips are submerged in a porous charge mix. In FeCr production, the electrical energy is mainly liberated by resistive heating of the wet coke bed (Barker et al., 2007; Steenkamp et al., 2017). Thermally conductive lining design philosophies are typically applied in SAFs producing FeCr (Steenkamp, Denton, and Hayman, 2017; Coetzee, Duncanson, and Sylven, 2010; Coetzee et al., 2010).In July of 2016 and June of 2017, major tap-hole repairs were carried out during the annual shutdown of two 63 MVA SAFs producing FeCr in South Africa. The hot excavations of the tap-holes allowed for a study of the wear profiles. Both SAFs were operated on the same site, by two different operating crews, using the same raw materials. The major difference between them was that the SAF excavated in 2016 was an open SAF (referred to as Furnace A) and the one excavated in 2017 was a closed SAF (referred to as Furnace B). In an open SAF, a gap exists between the top of the steel shell and the roof, with the top of the burden being open to the atmosphere and the CO-rich off-gas being combusted as it escapes. In a closed SAF, the roof is attached to the steel shell and the CO-rich off-gas is collected from an offtake on the roof for further treatment and used in downstream processes.The paper presented here reports the macro-scale observations on refractory wear for the two SAFs, and studies the potential for chemical wear of refractory by slag and alloy as a potential contributing factor to the tap-hole wear observed."

Jun 1, 2019

By S. Annavarapu

"Fragment size distributions play an important part in the design and planning of block cave mining operations. Though several methods have been proposed for estimating fragment size distributions in advance of mining, the calibration of these estimating procedures to field measurements has been a challenge. The Block Size Estimator (BSE) program was developed for providing an assessment of primary fragmentation expected in a block cave mine using drill-core piece length data and joint characteristics from the exploration and geotechnical evaluation programmes. In order to validate the results from the BSE program, the drill-core piece length data and the joint characteristics in different rock types from the DOZ block cave mine in Indonesia were used to help generate fragment size distributions in different areas of the mine. The predicted fragment size distributions were compared with the fragmentation observed at the drawpoints during operation of the mine.This paper presents the details of the validation of the fragment size estimates by the BSE program using fragment size distribution data from the drawpoints at the extraction level at the DOZ block cave mine, and the challenges encountered in developing reasonable correlations between the estimated and measured fragment size distributions. IntroductionThe assessment of fragmentation is an important aspect of the design and planning of the block cave mining method, and forms an integral part of the design of the excavations at the extraction level and the selection of material handling systems for transporting the ore to the processing stations. Secondary blasting requirements can also be estimated based on the fragment size distributions developed for the block cave (Laubscher, 1994).Several methods of estimating fragment size distributions in block cave mines have been developed based on joint set parameters estimated from structural data from oriented core drilling campaigns and mapping of available excavations and outcrops. The BCF program (Esterhuizen, 1999) estimates the fragmentation using a combination of empirical, analytical, and rational methods to model the behaviour of materials during the primary and secondary fragmentation processes. The program JKFrag uses advanced tessellation of joint traces to create rock blocks and then generate fragment size distributions (Brown, 2002). Nickson, Coulson and Hussey (2000) presented the details of processing of the geotechnical data from the Mont Porphyre project, including an assessment of block sizes from the data collected on the core logging sheet. The distance between natural fractures was used to create distributions of block lengths, and a distribution of potential block sizes was estimated assuming that the blocks had equal dimensions in all directions. The results agreed closely with the results of the BCF program. Hadjigeorgiou, Grennon, and Nickson (2002) demonstrated the use of oriented borehole data to provide characteristic block size distributions for a mining project using a software package called Stereoblock, which generates a three-dimensional joint network for a given volume and calculates the volumes of blocks created by the intersections of these joints, simulated as circular planes. The distributions of joint orientation and joint spacing generated from statistical analysis of the oriented core data are used for the creation of the Stereoblock model. The diameter of the circular planes representing the joints is determined based on the mean and standard deviation of the joint trace length obtained from scan-line mapping."

May 1, 2019

By G-L. Wu, S-W. Wu

"The hot deformation behaviour of Nb-Ti microalloyed high-strength steel was investigated. Hot compression tests were conducted in the temperature range 900 to 1100°C under strain rates of 0.1, 1, and 5 s-1. Dynamic recrystallization (DRX) occurs as the main flow softening mechanism at high temperature and low strain rate. The hot deformation activation energy was calculated to be about 404 699 J/mol. The constitutive equation was developed to describe the relationship between peak stress, strain rate, and deformation temperature. The characteristics of DRX at different deformation conditions were extracted from the stressstrain curves using the work hardening parameter. The Cingara-McQueen equation was developed to predict the flow curves up to the peak strain. The processing maps were obtained on the basis of a dynamic materials model. The results predict an instability region in the temperature range 1010 to 1100°C when the strain rate exceeds 0.78 s-1. IntroductionThe 700 MPa grade HSLA steel is widely used in engineering machinery, automotive beams, carriages, and axle tubes, etc. (Pan et al., 2017 ). Generally, such grades contain a moderately high amount of Mn (approx. 1.4% and above), and microalloying elements like Nb, Ti, V, and Mo to impart the desired strength and toughness through solid-solution strengthening, precipitation hardening, and grain refinement dislocation strengthening (Chen and Yu, 2012; Opiela, 2014). However, the production costs can be greatly reduced by replacing part of the Nb, V, or Mo with inexpensive Ti and adopting the compact strip production CSP process (Opiela, 2014; Chen et al., 2015). Furthermore, the microalloying technology coupled with new-generation thermomechanical control processing (NG-TMCP) has proved efficient for achieving the proper balance between strength, toughness, ductility, and formability by means of a suitable combination of chemical composition and thermomechanical treatment parameters (Shukla et al., 2012; Wu, Zhou, and Liu, 2017).In hot forming processes, the complex microstructural evolutions are often induced by multiplicative hot deformation mechanisms, such as work hardening (WH), dynamic recovery (DRV), and dynamic recrystallization (DRX) (Zhang et al., 2014; Liang et al., 2015). Dynamic softening behaviour during hot processing has generated considerable interest because component properties are influenced significantly by its corresponding microstructural evolution (Wu et al., 2010). During deformation in the DRX process, deformed grains are replaced with substructures and newly formed fine and uniformly distributed grains. This occurs only when a critical strain for the onset of DRX is reached, and at the same time, the minimum rate of energy dissipating is reached (Ferdowsi et al., 2014). DRV occurs at a high strain rate and low temperature, reducing the stored energy greatly and making DRX difficult (Liang et al., 2015). The microstructural changes during DRX are sensitive to the processing parameters, such as strain rate, deformation temperature, and strain (Zhang et al., 2014; Ferdowsi et al., 2014). Therefore, in order to optimize the hot processing parameters, it is important to understand the behaviour of hot deformation visà- vis control of microstructural evolution."

May 1, 2019

By L. Makua, K. Langa, Ndlovu. S., C. Saguru

"Global demand for the three platinum group metals (PGMs) Pt, Pd, and Rh has been steadily growing due to their widespread use in emission control, industrial catalysis, and numerous other applications. The primary supply of PGMs is currently the mining industry. However, legislative, operational, and environmental challenges faced by many mining operations result in erratic supply patterns and deficits for these three metals. Naturally, recycling scrap material to recover Pt, Pd, and Rh has therefore aroused research interest in the scientific and engineering communities. Given that the majority of the global demand for these three metals is driven by emission control devices, autocatalytic converters are therefore a significant source of already processed and beneficiated PGMs for recycling.Although pyrometallurgical processes dominate the recycling industry, hydrometallurgical processes may offer certain advantages, chief among these being lower emissions and reduced energy consumption. In this investigation, scrap converter material was leached in acidic chloride media and the leach liquor subjected to solvent extraction and cloud point extraction (CPE) to recover the PGMs. The recoveries for Pt and Pd using Alamine 308® dissolved in kerosene with decanol as a modifier were 95% and 81%, respectively. The maximum recoveries using CPE after complexation with 2-mercaptobenzothiazole (2-MBT) in the presence of Triton X-100 and tin (II) chloride dihydrate as a reductant were 97% for Pd, 96% for Pt, and 91% for Rh. This demonstrates that CPE, although relatively new, may have some potential as a breakthrough PGM recovery technology. IntroductionPlatinum group metals (PGMs) have found a wide variety of applications in different industries due to their chemical, catalytic, and physical properties. PGMs are essential in automobile emission abatement, petroleum refining, and the pharmaceutical and electrical industries (Carabias-Martinez et al., 2000). However, the abundance of PGMs in the Earth’s crust is low and their primary sources are fast depleting (Crundwell et al., 2011).The high demand for PGMs, together with social, economic, environmental, and political aspects related to their production, has led to concerns about their future supply. This has resulted in renewed interest in recycling end-of-life material. PGM supply from recycling has doubled over the last decade, and currently contributes 22% to global supply (Johnson Matthey, 2016). This is in part due to the environmental, social, and operational challenges associated with mining of PGMs. For example, labour unrest, energy cuts, declining commodity prices, and declining ore grades have collectively made the mining landscape economically challenging (KPMG, 2015). On the other hand, the high content of PGMs in secondary sources makes their recovery from the increasing quantities of waste products important from a resource conservation viewpoint. Moreover, PGMs obtained through recycling have been demonstrated to have a 1% environmental cost from a life-cycle perspective, whereas PGMs obtained from mining contribute the remaining 99% of environmental cost (Bossi and Gediga, 2017). Sustainable resource recovery and the economic incentive of recycling have therefore been major drivers to justify investment in PGM recycling. The autocatalytic converter industry accounts for about 70% of the global consumption of these metals (Johnson Matthey, 2016) and therefore recycling spent converters has become a major source of Pt, Pd, and Rh (Figure 1)."

May 1, 2019

By J. G. M. Mukoya, B. Adebayo

"This work was carried out to determine the influence of rock properties and drilling machine parameters on the penetration rate at the SJ pit of Rössing Uranium Mine, Namibia. Rock properties (uniaxial compressive strength, tensile strength, and modulus of elasticity) of samples collected were determined in the laboratory. Drilling experiments were conducted in which feed pressure, air pressure, rotary speed, weight on the bit, and torque were varied to measure their effect on the penetration rate. The uniaxial compressive strength varied from 90–180 MPa for layered marble-quartzite and banded gneiss. Increases in feed pressure, weight on the bit, and rotary speed beyond the optimum level led to a decrease in penetration rate and caused the drill bit to ‘stall’. Results of the study revealed that penetration rate increases with an increase in the feed pressure and air pressure. After reaching a maximum value, the penetration rate begins to decrease despite increasing feed pressure. A very high torque causes the drill bit to stall, since the feed pressure is too high and the air pressure is not sufficient to remove the cuttings from blast-hole at maxium bailing velocities. The average penetration rate varied from 19 to 45 m/h for phase 2 of the pit, and from 17 to 68 m/h for phase 3. The optimum drilling machine parameters obtained in phase 2 and phase 3 were slightly lower than those currently being used at the mine. The trials of the optimum machine parameters will assist in reducing the cost of drilling, which varied from N$29.48 to N$36.31 per metre for the tricone bit. IntroductionDrilling and blasting contribute most to the operational cost in opencast mining and have the potential to influence the cost of downstream operations (Aipanda, 2011). The drillability of rocks depends not only on the rock properties, but also on the drilling tools and operational variables. In rotary drilling, rotational speed, thrust, and flushing are the operational variables, and are known as the controllable parameters. Rock properties and geological conditions are the uncontrollable parameters. Although, many attempts have been made to correlate drillability with rock properties, the rock characteristics affecting rotary drilling have not been entirely defined (Hartman, 1962; Kahraman, Bilgin, and Feridunoglu, 2003). The drill bit is forced into a rock surface from the rotary power head, hence creating stresses and cracks at the bit-rock interface. The performance of a particular bit in any formation i"

May 1, 2019

By H. Cevizci

"Numerical simulation of the plaster stemming method (PSM) was performed and compared with the conventional drill cuttings stemming method (DCSM). Many earlier in situ tests have proved that PSM can use the blast energy more efficiently than DCSM. Despite PSM generating more blast vibrations, it has advantages over DCSM such as better fragmentation and lower cost per unit volume of rock blasted. In this study, numerical simulation with Autodyn software using a 2D tool was employed to prove the efficiency of plaster stemming by comparing parameters such as pressure, Y-velocity, Y-force, internal energy, acceleration-Y, and compression. For example, the maximum pressure attained at the top of explosive column was 7 395 MPa for DCSM whereas it was as high as 11 945 MPa for PSM. Most of the computed parameters were significantly higher in PSM than those obtained for DCSM. This paper is the first study elucidating the efficiency of PSM by numerical simulation. It is concluded that PSM can save substantial amounts of money and effort. IntroductionThe stemming of blast-hole collars in surface mines with an inert material redirects blasting energy to the rock more efficiently, thus the blast-induced energy is utilized more effectively in breaking rock. With proper stemming, the gases should not escape due to loose stemming material. More efficient stemming with better confinement therefore increases the blast fragmentation. In addition, the distance of scatter is increased, giving rise to a looser rock pile that can be more easily loaded and transported. In order to improve the performance of a blast, stemming is used to help maintain the gas pressure over time (Konya and Konya, 2018). Proper stemming has been shown to increase the explosive efficiency by over 41% (Snelling and Hall, 1912).The most common stemming material in open pits and quarries is drill cuttings because of their ready availability at blast sites and the drill cuttings stemming method (DCSM) is a low-cost method. However, it has a major disadvantage in that dry drill cuttings eject very easily from blast-holes during an explosion, thus a great percentage of the blast energy is wasted and lost to the atmosphere. Cevizci (2012, 2014, 2013, 2017) studied blasting parameters in open pits and obtained better results with the plaster stemming method (PSM) in many limestone, basalt, and clay quarries. Moulding plaster is preferred for stemming because of the fast hardening time of 25–30 minutes."

May 1, 2019

By X. Xiang, W. Xia, J. Yin

"TiCl4 slurry containing valuable metals is an unavoidable by-product of the titanium ore chlorination process. The recovery of these valuable metals, which include titanium, niobium, tantalum, and aluminum, is an urgent issue to tackle in the titanium industry. The results of this investigation show that the valuable metallic elements can be recovered from the slurry by evaporation in a sealed container and leaching with dilute hydrochloric acid. After evaporation at 200°C for 60 minutes, nearly 99% of the titanium was recovered in the form of TiCl4, which was formed by the reaction of the TiO2 in the slurry with AlCl3. After evaporation, metals like niobium, aluminum, and tantalum remained in the residue. By leaching with 2.1 mol/L HCl at a L/S ratio of 6:1 mL/g at 80°C for 60 minutes, the soluble metals, such as aluminum, iron, and copper were all removed from the residue, and the niobium and tantalum were further enriched in the leach residue. A concentrate containing 53.40 wt% Nb and 5.57 wt% Ta was obtained by washing the leach residue with dilute aqueous ammonia under stirring. A potential waste water purifying agent containing 263.75 g/L AlCl3 was produced by purifying the leaching solution with Al(OH)3 and modified polyacrylamide. IntrodutionTitanium tetrachloride (TiCl4) is an important intermediate in titanium metallurgy that is widely used in the production of titania and titanium sponge (Akhtar, Xiong, and Pratsinis, 1991). In conventional titanium metallurgical processes, high-titanium materials such as synthetic rutile and high-titanium slag are reacted with chlorine to produce TiCl4 in a fluidized-bed furnace. Accompanying elements, such as Al, Nb, and Fe also react with chlorine to form chlorides, which are mixed with gaseous TiCl4 (Anderson, 1917). In the condensation process, gaseous TiCl4 is refrigerated and high-boiling-point chlorides are precipitated in the liquid TiCl4 to form a slurry containing 50~60 wt% TiCl4 (Wang, Xiang, and Wang, 2012).Various methods have been proposed to recover TiCl4 from the slurry, including microwave heating and spray drying (Wang, Xiang, and Wang, 2012, Wang et al., 2010a). To date, the only way to recover the TiCl4 is to return the slurry to the fluidized-bed furnace. However, this causes fluctuations in the temperature in the furnace, resulting in incomplete reaction between titanium-rich materials and chlorine. Therefore, the slurry is often rinsed with water and neutralized by adding lime, which caused serious environmental pollution and wastes a valuable resource (Roy, Bhatt, and Rajagopal, 2003)."

May 1, 2019

By E. A. van Wyk, M. R. de Villiers

"Mining companies strive to increase and maintain production, while simultaneously remaining competitive in the global economy. Furthermore, they must ensure workers’ safety and maintain good safety records. The use of virtual reality (VR) facilitates the development of tools and systems for various purposes that can improve knowledge and understanding of the work environment. VR is a rapidly growing technology that uses the ever-increasing power of computing to simulate real-world and imaginary environments and situations with a high degree of realism and interaction. The availability of 3D modelling tools and simulation programming engines that work effectively with a mid-range desktop PC and standard 3D graphics card, make VR technology viable and attractive for mainstream training applications. The design, development, and implementation of interactive VR training systems is proposed as an innovative approach to augment safety training. However, in order to assess the impact of such VR training systems it is of particular importance to determine the effectiveness of the design of such systems. This article proposes an evaluation framework for this vital purpose. This framework comprises criteria to assess VR training systems, specifically relating to usability, instructional design, VR systems design, and mining industry context-specific aspects. Although the framework was developed as an evaluation tool to assess effectiveness of the design of such systems, it can equally well be used as a set of design principles to inform the design of VR training systems for mining. IntroductionMining in South Africa has been the main driving force behind the history and development of Africa’s richest and most advanced economy (Coka, 2012). The South African mining industry is frequently criticised for its poor safety record and high fatality rate (Stoddard and Skweyiya, 2016). Inadequate or insufficient training is often cited as a root cause of accidents (Van Wyk and De Villiers, 2009; Tichon and Burgess-Limerick, 2011). Virtual reality (VR) is a rapidly growing technology that utilizes the ever-increasing power of computing to simulate real-world and imaginary environments and situations with a high degree of realism and interaction (Webber-Youngman and Van Wyk, 2013). VR is currently being used or investigated as a training solution in a variety of industries. VR technology has developed rapidly and costs have fallen to levels where it can now be considered for mainstream training applications. The availability of 3D modelling tools and simulation programming engines that work effectively with a mid-range desktop PC and a standard 3D graphics card, make VR even more attractive to mine training centres (Van Wyk and De Villiers, 2009)."

May 1, 2019

By C. Liu, F. Ye

"To extend the variety of lump ores that are used in the COREX shaft furnace and to optimize iron ore blending, the original evaluation method for iron ores that was proposed by Voestalpine AG has been improved. Physicochemical and metallurgical properties of iron ores, including Sishen lump ore and CVRD pellets, which are currently used in the COREX process, and three other lump ores, were assessed and compared. Ore matching principles were proposed and five optimized iron ore blending schemes designed and verified by laboratory experiments to prove the effectiveness of the improved evaluation method. The replacement of Sishen lump ore by the alternative L2 and L3 lump ores without varying the proportion of CVRD pellets could improve the degree of reduction and rate of metallization, and decrease the bonding index. Based on the results of laboratory test work and industrial- trials, an ore blending scheme of 60% CVRD, 20% L2, and 20% L3 is recommended for use in the COREX process. IntroductionIn recent years, problems such as environmental pollution and a shortage of coke and coal resources for blast-furnace ironmaking have become increasingly apparent. Based on sustainable developments in the iron- and steelmaking industries, the environmentally friendly COREX smelting-reduction process with low energy consumption was developed and introduced (Zhou and Du, 2013; Song, Lv, and Yin, 2015; Xu et al., 2016; Kurunov, 2010). The evaluation system for lump ore that was proposed by Voestalpine AG recommends that only Sishen lump ore from South Africa be used in the COREX process, because of the stringent physicochemical and metallurgical property requirements. This situation significantly hampers improvements to the technical and economic aspects of the COREX ironmaking process, especially in China (Eberle, Siuka, and Bohm, 2006). No theoretical or technical basis has been provided for the evaluation system, and the assessment approach for iron ores also presents problems that need to be discussed and resolved.The COREX process consists of two reactors: the prereduction shaft furnace and the melting gasifier as shown in Figure 1 (Wu et al., 2017). Pellets and lump ores which are charged to the prereduction shaft should have a good reducibility and metallization with a low degradation index (Li et al., 2016; Wu et al., 2011; Kumar et al., 2009; Kang, Gupta, and Sahajwalla, 2007). The properties and microstructure of the iron ore pellets which are required to achieve a high productivity and a lower fuel rate in the COREX process have been investigated (Umadevi et al., 2011). Some efforts have also been made to investigate the behaviour of lump ores in the COREX shaft furnace, including the disintegration characteristics and the reduction degradation (Umadevi et al., 2011; Zhou et al., 2015; Xu et al., 2013; Li, Feng, and Zou, 2013; Hou et al., 2014). However, few studies have focused on the optimization of ore blending for partial or total substitution of the expensive Sishen lump ore by other, cheaper lump ores to reduce the production cost. The technology for the utilization of blended lump ores in the COREX process is still in its early development stages (Zhou et al., 2017; You et al., 2017)."

May 1, 2019

By K. Thambi

"A recent amendment to Section 36(11)(e) of the Income Tax Act, 53 of 1968 (Tax Act) now extends the allowable deduction of ‘capital expenditure’ incurred by mining companies pursuant to the Mineral and Petroleum Resources Development Act 28 of 2002 (MPRDA). In terms of the Taxation Laws Amendment Bill 2016 (TLAB 2016), the allowable deduction has been extended to include expenditure incurred on infrastructure in terms of Social and Labour Plan (SLP) requirements as per the MPRDA. Interestingly, what necessitated the amendment was the need to recognize SLP requirements and to circumvent administrative difficulties for mining companies and the South African Revenue Services (SARS) in differentiating the use of developmental infrastructure by employees or the community. The successful implementation of such a deduction hinges on a sound SLP system. However, given the challenges within the current SLP system, this amendment could be considered somewhat premature. IntroductionSection 36(11) of the Income Tax Act 58 of 1962 (Tax Act) enabled mining companies to deduct certain capital expenditure in lieu of its other sections. In particular, it made provision for mining companies to deduct capital expenditure incurred pursuant to the Mineral and Petroleum Resources Development Act 28 of 2002 (MPRDA), but excluding capital expenditure incurred in respect of infrastructure or environmental rehabilitation. As such, mining companies could only deduct such capital expenditure that related directly to their employees and not to the wider community (Clegg, 2018).In terms of the Taxation Laws Amendment Bill 2016 (TLAB, 2016) (South Africa, 2016a), the recent amendment to Section 36 extends the relief provided under section 36(11)(e) to include capital expenditure incurred on infrastructure in terms of the Social and Labour Plan (SLP) requirements of the MPRDA. In other words, the capital expenditure incurred by the mining company for the benefit of the people living in mining communities. To qualify for such a deduction, the infrastructure erected or developed by the mining company should reflect what was agreed between the mining company and the Department of Mineral Resources (DMR) as per the SLP requirements of the MPRDA (TLAB 2016)."

May 1, 2019

By F. Mwaura

"The aim of the audit was to determine whether the mining project environmental impact assessments (EIAs) in Kenya are undertaken according to international best practice. A sample of 50 EIA reports for the 2007–2016 period was evaluated using 18 criteria in the Environmental Law Alliance Worldwide (ELAW) guidelines. The findings showed that only two criteria were considered ‘excellent’ according to the ELAW guidelines, namely baseline environmental assessment and prediction of physical impacts. Six criteria were found to be ‘satisfactory’, including prediction of social impacts, analysis of alternative options, and impact mitigation. The reports were quite weak in terms of: consideration of all phases in the mining cycle, environmental regulatory framework, prediction of biological impacts, stakeholder consultation and engagement, integration of human right issues, and integration of climate change and cost-benefit analysis. It is therefore recommended that the Kenyan National Environment Management Authority (NEMA) should consider tightening the EIA terms and conditions in the approval of statutory terms of reference (ToR) for full-scale mining EIAs to ensure improved performance of EIA as a tool for environmental protection. IntroductionThe nexus between society and the environment has continued to generate interest because the environment is the source of goods and services that sustain the various needs of human beings as outlined in the UN sustainable development goals (SDGs) (Armstrong and Peart, 2000; Sutton 2004; Chakrabarti 2007; Strange and Bayley 2008). All the five generic categories of societal needs, namely physiological needs (food, water, clothing, medicines, etc.), residential and occupational needs (shelter, transport, energy, etc.), economic needs (tradeable goods and services), leisure and recreational needs (tourism), and cultural and spiritual needs (e.g. sacred resources and ecosystems) (Mwaura et al. 2016) are addressed by the environment. Consequently, a wide range of development sectors have been established around the world in order to address the above needs (Lederer, Galtung, and Antal, 1980; Rammelsberg et al., 2006; Noonan, 2014). All these development sectors rely entirely on the environment for their proper functioning, as shown in Table I."

May 1, 2019

By P. P. Kim, M. Tangstad, T. A. Larssen

"The kinetics of MnO and SiO2 reduction in SiMn slags based on Assmang/Comilog ore and HCFeMn (highcarbon ferromanganese) slag were investigated between 1500 and 1650°C under a CO atmosphere. The results showed that charges containing HCFeMn slag had relatively faster reduction rates than those without. The difference in the driving force for MnO reduction was insignificant among the SiMn slags at 1500°C, which implies a low contribution of the driving force for reduction rate. The slag viscosities were also rather similar, around 1 poise at 1500°C, which could not explain the different reduction rates. Instead, the different charges containing various sulphur contents are believed to give rise to the varying reduction rates. The estimated activation energies for MnO reduction were around 500–920 kJ/mol for charges containing HCFeMn slag, and between 250–300 kJ/mol for those without. Based on the estimated kinetic parameters, the considered rate models were able to describe the reduction of MnO and SiO2 in SiMn slags between 1500 and 1650°C. IntroductionManganese ferroalloys such as ferromanganese (FeMn) and silicomanganese (SiMn) are important ingredients in steel production due to the beneficial effects of manganese on the physical properties of steel. Mn enhances the strength, toughness, and hardness of steel products, and both Mn and Si are used as deoxidizers to prevent the development of porous structures (International Manganese Institute, 2014; Olsen, Tangstad, and Lindstad, 2007; Subramanyam, Swansiger, and Avery, 1990; Tomota et al., 1987).The thermodynamic background of manganese ferroalloys is well established (Olsen, Tangstad and Lindstad, 2007), but kinetic information is rather scarce, especially for the SiMn process (Tranell et al., 2007; Tore-Andre Skjervheim, 1994). The absence of kinetic information makes it more difficult to understand the reduction mechanisms of MnO and SiO2. It is not clear how different raw materials affect the SiMn process. The main metal-producing reactions in the SiMn process are described by Equations [1] and [2]:"

May 1, 2019

By A. Sokolov, M. Demsky, E. Hasikova, V. Gostilo

"Previously, we upgraded and implemented two gamma activation assay (GAA) systems designed to analyse the gold content in raw ores at Zarafshan laboratory, Uzbekistan, and achieved a detection limit of less than 0.05 g/t under actual industrial conditions. Having started to design a fully modern, industrial GAA system for mining companies, this paper analyses the advantages, disadvantages, and special features of all major system components that can influence the sensitivity and accuracy of the analysis. The results of a study to optimize the detector geometry and sample size are presented and the performances of the linear electron accelerator, detector array, and sample transportation system of a modern, industrial GAA system for analysing gold, silver, and rare earth elements are considered. IntroductionGamma activation analysis (GAA) has considerable potential as a future replacement for traditional fire assay analysis in gold mining (Hoffman, Clark, and Yeager, 1998; Morse, 1977; Bourmistenko, 1986, 1981; Sammut, 2016; Tickner et al., 2017). The essence of GAA is to irradiate ore samples with high-energy gamma quanta generated by an electron linear accelerator (LINAC) and then to use a gamma spectrometer to detect the induced activity of the excited gold nuclei. The advantages of this method are discussed in detail elsewhere (Hoffman, Clark, and Yeager, 1998; Morse, 1977; Bourmistenko, 1986, 1981; Sammut, 2016; Tickner et al., 2017), where it is shown that GAA is uniquely suited to analysing ore samples when mining for gold, other precious metals, and accompanying elements.These advantages were realized in three industrial GAA laboratories that were commissioned in Zarafshan, Uzbekistan in 1977, in Magadan, Russia in 1979, and in Batagay, Russia in 1986 (Bourmistenko, 1986; Nii Tekhnicheskoy Fiziki I Avtomatiki, n.d). In 1989, a fourth industrial GAA laboratory was commissioned at a gold mine in Tommot, Russia. However, the project was subsequently halted due to economic reasons (Moshkov and Tjamisov, 2017). Currently, only the laboratory of the Muruntau mine in Zarafshan, Uzbekistan is in operation. The gamma activation method for gold determination is widely applicable at this mine owing to its high productivity and low cost of analysis. An outstanding aspect is the performance of more than one million analyses per year."

May 1, 2019

By R. W. O. Kersten

"The aim was to investigate stable pillar design procedures currently in use on chrome and platinum mines, subject them to a critical appraisal, and review some of the alternatives proposed in the literature. It is concluded that these pillar design methodologies suffer from drawbacks that can be detrimental to the mining industry and that an improvement is essential.It was decided that the increased availability of analytical models and failure criteria could be exploited to update the empirical to an analytical/empirical method. The proposed methodology adopted FLAC2D simulations using the Hoek-Brown failure criterion to calculate full stress-deformation curves for typical pillars. The mine stiffness concept was introduced to determine the pillar load, integrating the influence of the pillar and strata stiffness and mining geometry.The proposed methodology was calibrated by comparing experimental and predicted deformations and failure depth of pillars in one hard-rock mine. The conclusion was that the methodology is an improvement over the one currently in use. An improved factor of safety is given by the intersection point of curves for the stiffness of the system and the pillar strength. IntroductionThe paper describes part of the findings of a PhD thesis (Kersten, 2016) on an alternative stable pillar design methodology. This publication contains sufficient information to implement the method for further interpretation and testing. A detailed comparison of measured and predicted data is dealt with in the thesis, and the results show that there is promise in the methodology.The design of stable pillars in mining is of fundamental importance, not only in the Bushveld Complex mines but throughout the mining industry. Wherever mining occurs, pillars are formed at some stage and it is essential to predict their behaviour, i.e. whether they will burst, yield, or remain stable. Although of crucial importance, pillar design still suffers from major shortcomings and weaknesses."

May 1, 2019

By M. J. Voigt, R. A. Govender, A. Mainza, L. Bbosa

"Mineral texture is a critical factor which controls ore variability and is an important attribute in geometallurgy. In relation to downstream processes, it affects the fracture pattern during breakage, where rock strength is inherently a function of mineral texture. Because of the subjective nature of mineral texture, it has not been easy to quantify, especially in the context of a measurement suitable for use in geometallurgical programmes. The aim of this paper is to present the first steps in developing a 3D mineral texture quantification method for drill core and to assess its sensitivity to differences in rock strength using a case study. The methodology includes classifying the textural information using the 3D grey level co-occurrence matrices (GLCM) and X-ray computed tomography (XCT) coupled method. Rock strength tests were performed using the split Hopkinson pressure bar (SHPB). The case study investigates a heterogeneous polymetallic sulphide deposit and a homogeneous shale subdivided into three ’mineral textural types’. The variability is largely captured by the GLCM matrices, and preliminary trends can be observed where the shale is finer grained and has a higher yield strength in comparison with the coarser grained polymetallic sulphide ore. IntroductionModern mining requires the exploitation of lower grade and more complex, heterogeneous orebodies to address the growing industry demands. Historically, processing plants were designed and built based on average ore characteristics and therefore are relatively inflexible when facing the full spectrum of ore variability in heterogeneous orebodies (Lamberg, 2011; Lotter, 2011; Schouwstra et al., 2013). The practice of geometallurgy represents an opportunity to manage ore variability in the mining industry (Powell 2013; Baum, 2014; Yildirim et al., 2014; Nguyen, 2013). It focuses on quantifying the relationships between ore characteristics and their downstream mining and processing responses, often starting with small-scale laboratory testing. The purpose of geometallurgy is linked to maximizing the net present value (NPV) of an orebody by minimizing technical and operational risk – where ‘ore variability’ is considered one of the most significant technical risks."

Apr 1, 2019

By V-P. Takalo, M. Natsvlishvili, M. Hicks, S. Khizanishvili

"The complexity of copper-gold ores leads to large variations in recoveries and concentrate grades in the processing plant. Detailed chemical and mineralogical studies revealed considerable variation in the ratios of chalcopyrite, chalcocite, and oxidized copper minerals in the ore types studied. The end-member ore types are chalcopyrite-dominated and chalcocite-dominated, while most of the ore types plot between these end-members. In addition, increasing amounts of copper oxide and sulphate minerals result in a decreased response to flotation. Good recoveries and concentrate grades can be achieved from the chalcopyritedominated ore type, while the more altered chalcocite-dominated ore type is more challenging to enrich. IntroductionRich Metals Group (RMG) Copper in Georgia (Figure 1) produces copper-gold concentrates from two open pit mines, Madneuli and Sakdrisi, both located in the Bolnisi mining district in South Georgia. RMG and Outotec began a cooperative project with the aim of improving the recoveries and metal grades in concentrate by gaining an increased understanding of the ore variability and developing more efficient procedures for ore blending, grinding, and flotation. This type of mineralogy-led approach has already been used for other complex ores such as iron oxide copper-gold ores (Hunt, Berry, and Bradshaw, 2011), for iron ores (Lund, Lamberg, and Lindberg, 2013), and for Kupferschiefer ore deposits (Rahfeld et al., 2018).The project started with process audits and mineralogical and chemical characterization of process samples, followed by detailed chemical and mineralogical characterization of six different ore types with simultaneous flotation test work on the same samples. Since neither the recoveries nor the concentrate grades correlate with the head grades of the ores, the modal mineralogical composition, together with the ore hardness, proved to be the most promising approach in developing the geometallurgical classification of these ore types."

Apr 1, 2019

By N. Baloyi, P. Popoola, M. Tlotleng, S. L. Pityana

"The advantages of using Nb and Ti-Nb coatings for improving the hardness and corrosion resistance of Ti6Al4V were investigated. It has been reported that Ti6Al4V used in orthopaedic implants tends to release toxic Al and V ions into the surrounding tissue. Thin layers of Nb and Ti-Nb were deposited on Ti6Al4V substrates using a laser metal deposition technique. The deposited material was analysed using optical microscopy, scanning electron microscopy coupled with energy dispersive spectroscopy, and X-ray diffraction. The corrosion behaviour of the deposited layers was investigated using a Metrohm Autolab PG Stat101 compact potentiostat at 25°C in simulated body fluid. A Vickers hardness system was used to study the mechanical properties. Both Nb and Ti-Nb coatings exhibited good metallurgical bonding with the substrate. The microstructure and the XRD analyses for the Nb system showed that the ??-Nb phase was most dominant, while the Ti-Nb system comprised a mixture of the ?? and ?? phases. The average hardness of the Ti6Al4V substrate was 350 HV0.3, with a slight increase for the Nb coating (363 HV0.3) and a much higher hardness from the Ti-Nb coating at 423 HV0.3. The corrosion results show that the deposited Nb was more corrosion-resistant in the solution than either the Ti6Al4V substrate or the Ti-Nb coating. IntroductionMetals such as CoCrMo, 316L stainless steel, and NiTi alloy are used for manufacturing biomedical implants because of their distinct properties, including low Young’s modulus and resistance to corrosion (Ryan, Pandit, and Apatsidis, 2006). These implants are required to remain in the body of the patient for many years. Due to a favourable combination of mechanical and corrosion properties, titanium (Ti) and its alloys have emerged as the material of choice for biomedical implants. Nevertheless, their use is not entirely without challenges. For example, in total hip replacement, surface degradation and release of metal debris from metal erosion caused by friction limit the service life of the implant (Oldani and Dominguez, 2012; Manivasagam, Dhinasekaran, and Rajamanickam, 2010). Ti6Al4V is generally regarded as the material of choice, but it has been found that over extended periods of time, the combination of surface corrosion and erosion releases toxic aluminium (Al) and vanadium (V) ions into the body (Khan, Williams, and Williams, 1996). This has led to the investigation of titanium alloys containing niobium (Nb), zirconium (Zr), tantalum (Ta), and molybdenum (Mo) as substitutes for the aluminium- and vanadium-containing Ti6Al4V (Okazaki et al., 1997)."

Apr 1, 2019