By J. Moore, D. Gault, R. V. Lugn

Impact of small projectiles with velocities between 0.9 and 7.3 km per sec on basalt produce craters chiefly by the ejection of fragments. Weight-size distributions of the ejecta are linear for part of the size range of the fragments. Cumulative weight-size distributions of the ejecta from different craters vary because of erratic formation of large fragments and a large percentage of ejecta below 0.1 mm. In the range of velocities studied, the crater depth is approximately proportional to the 0.75 power of velocity of the projectile. This relationship may represent a transition regime between the fluid impact regime and the undeformed projectile impact regime. The volumes per unit of projectile energy of the craters produced are comparable to those reported for lower speed projectile impact and drill bits. An experimental investigation of projectile impact on rock is being conducted jointly by the Ames Research Center of the National Aeronautics and Space Administration and the U.S. Geological Survey. Projectiles are launched with light-gas guns at the Ballistics Range of the Ames Research Center. The craters and ejecta produced in these experiments are being studied by the U.S. Geological Survey. Steel, aluminum and polyethylene projectiles weighing from 0.25 to 0.015 g were accelerated to velocities of 0.88 km per sec (2,900 fps) to 7.3 km per sec (24,000 fps) with a light-gas gun, using hydrogen as the propellant medium. Projectiles impacted the targets normal to plane rock surfaces in an atmosphere of air with a nominal pressure of 25 to 50 mm of mercury. The metal projectiles were mounted in supporting four-piece nylon sabots, which guided the projectiles down the launching tube. After launch, aerodynamic drag acted to separate the sabots from the projectiles. Impact velocities were determined with time measurements and spark photographs of the projectiles in flight. Ejecta were collected in lucite and aluminum containers placed around the target block. A small hole in the containers permitted projectile entry. Impact of projectiles of the size employed produced craters in the rock targets chiefly by ejection of fragments. The craters are small, roughly conical depressions with crushed and intensely fractured rock at the bottoms of the depressions. The ejecta are composed of pieces of the projectile and rock fragments ranging in size from a few tenths of a micron or less to several centimeters in maximum dimension. In this paper, the structural features of the craters, the weight-size distributions of the recovered ejecta, and crater depth and crater volume relationships are described. DESCRIPTION OF CRATERS Typical craters (Fig. 1) produced by experimental projectile impact in basalt are shallow, wide base

Jan 1, 1963

By R. Bakish, M. A. Badiali, N. W. Kirshenbaum

One pound of ultra pul-e molybdenum has been produced containing both metallic and nonmetallic impuvities close to or less than the limits of detection. various purification methods were investigated; althouglz the use of move than one purification step was consideved, it was found that a single, caefully-controlled sublimation of MoCl5 yielded a highly puvified product without prior treatment or recourse to repeated sublimation. Hydrogen reduction of MoC1, to metal was attempted at atmospheric pressure; however, reduced pressure was necessary to obtain substantial yields. The tubular deposits of metal were consolidated into bulk fovm by electron beam melting undev high vacuum yielding a very low gas content. Boblems involved in monitoring the puvity of these materials and analytical results obtained are also presented. THE pronounced effect of even trace amounts of impurities upon fundamental properties of materials is well known to metallurgists and solid-state physicists. Consequently, groups interested in basic studies of metals have in recent years immensely stimulated the preparation and production of numerous ultra-pure metals. Increased demand by scientists for these high purity materials has necessitated development of facilities to prepare them in significant quantities; the procedures reported here were devised to produce significant quantities of ultra-pure molybdenum. Previous work performed in the field of vapor phase purification and hydrogen reduction of several other refractory metal chlorides had demonstrated valuable techniques applicable to molybdenum.' Various purification and reduction steps were individually investigated. Those procedures which showed the most favorable results with respect both to attainment of high purity and to ease of operation were then incorporated in the process utilized to produce the metal.' STARTING MATERIALS It is well known that because of differences in volatility, chlorides may be separated by fractional distillation. It was presumed that distillation of molybdenum pentachloride offered a simple and straightforward method of purification due to its relatively low boiling point. Alternatively, sublimation of the solid chloride also appeared feasible since MoC15 has both a reasonably narrow temperature range in which it exists as a liquid (a property typical of refractory metal chlorides) and a low enthalpy of sublimation. Pertinent thermochemical data of MoC15 are given in Table I. It should be noted that this compound must be handled with care as it is extremely hygroscopic. Anhydrous MoC15 was obtained from the A Metal Climax Co. METHODS OF PURIFYING MOLYBDENUM PENTACHLORIDE Distillation. It was expected that distillation methods, while affording an efficient purification, would prove simple to control and would have a higher production rate than sublimation processes. Also considered was the possibility of effecting a high degree of purification by using both these volatilization methods in conjunction—possibly a distillation followed by sublimation of the solidified condensate. Distillation of MoC15 was investigated using a single stage distillation column packed with chemically resistant glass beads. Heating coils were wound around the column and collection tube (condenser). As-received MoCl5 was charged into a flask connected with the column using a side loading arm under an argon flow. After the column and condenser were brought to about 270" and 210°C, respectively, the apparatus was lowered until the flask was fully immersed in a constant temperature fused salt bath maintained at about 285 °C. Distillation was continued for about 10 or 15 min until 50 to 70 g of distillate had been collected. Analyses of these distillations indicated that several elements, e.g., Cu, Fe, Ni, Cr, and Mg, were lowered in quantity although not all were removed to the same extent. The occurrence of Na, B, Si, and A1 in the distillates appeared to be due to contamination, possibly from corrosion of the pyrex glass. An improved distillation system of larger capacity and longer distilling column was built. Improvements were effected in lowering the amounts of such impurities as B, Mn, Ni, Na, Mg, Cr, Cu, and Fe. These studies were pursued concomitantly with efforts to purify by sublimation; it was subsequently found that although improvements in purity were obtained by distillation, sublimation processes were simpler to control and effected a high degree of purity.

Jan 1, 1963

By T. H. Alden

Using alternating tension-compression straining, the hardening of magnesium oxide single crystals was studied up to large stresses and strains. At 0.25 pct plastic strain amplitude, the hardening curve is approximately linear with slope 25,000 psi from the shear yield stress, 7 to 8000 psi, to 35,000psi. Above this stress, the slope decreases. The strain hardening behavior of MgO is considered qualitatively similar to that of metal single crystals. The relatively high stress attainable by strain hardening is associated apparently with the high yield stress on the cross-slip system, (001) <110>. Cleavage fracture during testing is uncommon. It is argued that the centers of high internal stress at glide band intersections, at which cracks tend to nucleate, are dispersed by cyclic strain. Special features of the glide band structure produced by cyclic strain and revealed by dislocation etch pits, support this view. Strain hardened MgO has mechanical properties greatly superior to the as-received material: yield stress, greater than 100,000 psi; elongation to fracture about 1 pct. A material is said to strain harden if the yield stress increases with an increment of plastic strain. This definition is usually applied for straining done in one direction, but is also applicable when the strain direction is periodically reversed, Fig. 1. For certain metal single crystals, data are available which permit a comparison of the hardening behavior for cyclic straining and for tension straining.&apos;-4 With certain qualifications, these data show that the same processes of hardening are operative in each type of test.5 Despite this fact, the importance of the technique is not immediately evident, although tension-compression studies of the common metals appear to suggest some deficiencies in theories of strain hardening developed exclusively on the basis of tensile tests. However, a recent observation suggests that the cyclic straining method may be very useful for studying semibrittle crystals in which large plastic strains are not accessible in unidirectional testing. The observation is that zinc crystals, when strained in tension-compression at -52°C, do not fail by cleavage at low stress (-500 psi)6 as they do in tension, but harden to a limiting stress of more than 5000 psi over a total plastic strain of about 600 pct.2 An important characteristic of the behavior of zinc crystals is the high stress, relative to the yield stress, attainable by strain hardening. By comparison, the hardening of aluminum single crystals tested by an identical technique saturates at 1100 psi. This difference is best explained by the cross-slip hypothesis of dynamic recovery.7,8 In zinc, cross slip is difficult because of the high yield stress for glide on planes other than the basal plane in the < 1120 > zone. The present work was undertaken in order to test whether these methods and ideas are applicable to other materials. Magnesium oxide single crystals, in common with most crystals of the rock-salt structure, deform plastically but fail by cleavage after a small strain when tested in tension. It was hoped that larger strains would be attained using tension-compression. There is, in addition, evidence 8a which shows that slip on the probable cross system, (001) < 110>, is difficult in magnesium oxide; it may therefore be possible to attain high stresses by strain hardening. 1) EXPERIMENTAL PROCEDURE Experimental methods used in this study were based in part on techniques reported in papers of Stokes, Johnston, and Li.&apos; MgO blocks, purchased from Norton Co., were used without further annealing. Specimens were cleaved to dimensions approximately 0.125 in. sq and 1 in. in length. The gage section, formed by chemical polishing, was sprinkled with 280 mesh silicon carbide particles in order to introduce fresh dislocations. The crystals were then cemented into cylindrical aluminum adapters and clamped in an Instron testing machine. One of two alternating straining programs was used. In the first, total cross-head travel was established and increased in steps after various numbers of cycles. In the second, a capacitance gage was used to directly measure the elongation of the specimen and the crosshead was controlled so as to keep the plastic strain amplitude constant. The straining was always symmetrical with respect to the initial, zero strain condition. While both procedures produce strain hardening, only the latter permits a measure of the total plastic strain so that hardening curves may be drawn. Constant plastic strain amplitude tests were done

Jan 1, 1963

By Arnulf Muan, Egil Aukrust

Activities of COO in the three solid solution series COO-MgO, COO-MnO, and COO-"FeO" have been determined at 1200°C by equilibrating oxide samples with a metal phase (cobalt or a Co-Fe alloy) in atmospheres of known oxygen activities. The systems COO-MgO and COO-MnO are ideal, within limits of experimental error, whereas the system COO-"FeO" shows a slight positive deviation from ideality at the temperature of this investigation. KNOWLEDGE of activities of oxide components in solid solutions is necessary for the calculation of the cation distribution among coexisting oxide phases in many important metallurgical, ceramic, and geochemical systems. Very few activity-composition curves are available for such systems at the present time. A start on the prodigious job of obtaining such data has been made by studies of solid solutions with simple sodium chloride type structure containing NiO or "FeO" as a component.1-3 The present paper describes similar studies for solid solutions with sodium chloride type structure containing COO as a component. For the systems COO-MgO and COO-MnO, the activity solid solution is determined by the equation Here po and are the oxygen activities of the gas phase in equilibrium with the phase assemblages metallic cobalt plus oxide solid solution, and metallic cobalt plus pure COO, respectively. In the system CoO-"Fe07&apos;, the metal phase is a Co-Fe alloy rather than pure cobalt. In this case the activity of COO in the oxide solid solution is calculated from the equation where a& is the activity of cobalt in the metal phase. Because the system Co-Fe is close to ideal4 and the metal phase appearing in the present work contains less iron than cobalt even at the lowest COO concentrations of the oxide phases used may be set equal to N . Hence, Eq. [2] becomes The value of Nc, can be estimated from the relative stabilities of the oxides COO (see below) and I) EXPERIMENTAL METHOD Two different but closely related procedures were used in the present investigation to determine the activity-composition curves. In one method, the oxide solid solutions were equilibrated against

Jan 1, 1963

By F. J. Smit, S. C. Sun

Flotation variables were investigated for the re-clamation of phosphate from a Florida washer slime. Under optimum conditions, 92% of the phosphate was recovered. Further cleaning of the rougher flotation concentrate resulted in a product containing about 30% P2O5 with a phosphate recovery of 65%. The enormous amount of slimes rejected in the Florida pebble phosphate fields, containing roughly one-third of the phosphate in the pebble matrix,1 has long been considered as a serious problem to the industry. The mere disposal of these slimes has posed an almost insurmountable task for several investigators.2-5 Some companies still resort to huge surface dams, some covering 1800 acres, for slime disposal.6 Information on the recovery of fine phosphate from these slimes is scanty. Dry separation8 and electrostatic beneficiation8 were suggested, but would necessitate radical changes in the present mining and concentration methods. Haseman10 proposed the selective flocculation of colloidal phosphate with starch, while Ralston11 suggested the removal of clay from the matrix by amine flotation. Leaching of the slimes for recovering the small amount of uranium was attempted by the Battelle Memorial Institute12,13 but proved to be economically unfeasible. The purpose of the present investigation was to determine the optimum fatty-acid flotation conditions for reclaiming the phosphate discarded with the Bartow washer slime. Prior to the flotation experimerits, however, the size distribution and the minera-logical composition of the employed slime had to be determined.

Jan 1, 1963

By F. X. Spiegel, D. Bardos, Paul A. Beck

Ti6NileSi7)G is known to be cubic, with 116 atoms in the unit cell. In the present work four new G sili-cides were found with other transition elements and five G germanides. The titanium-group elements are very efficient in forming G phases. The vanadium -group elements are somewhat less efficient, and the chromium-group elements do not form any. Cobalt can replace nickel in most cases, but it is somewhat less efficient. Iron was not found to form any G phases. Germanium is somewhat less efficient than silicon. The (TiNiSi)E phase has been previously identified by Westbrook. However, its crystal structure has not been determined. In the present work the E phase was found to have an orthorhombic unit cell with lattice parameters a. = 7.02, bo = 5.18, co = 11.11A. A large number of other E phases were found at the same stoicheometric ratio in ternary systems of silicon and germanium with transition elements. Lattice parameters similar to those for TiNiSi were measured. The number of atoms per unit cell is estimated at 30 to 36. The vanadium-group elements are somewhat more efficient in forming the E phase than the titanium-group elements. Chromium-group elements were not found to form any E phases. Cobalt is somewhat less efficient than nickel, and iron is less efficient than cobalt. Germanium is not as efficient as silicon. ThE ternary silicide designated as G-phase was first identified by Beattie and versnyder1 and by Beattie and Hagel2 at the approximate composition TiNi2Si. Westbrook et al.&apos; gave the composition as Ti2Ni7Sis. This phase was found to be fcc with a. = 11.201A and 116 atoms per unit cell. Beattie4 and more recently independently Hladishevskii, Kripyakevich, Kuzma, and Teslyuk5 were able to show that this structure is isotypic with MgeSi7CuLe and Th6Mn23. The latter structures had been determined by Florio, Rundle, and snow,&apos; Nagorsen and Witte,7 and Bergman and Waugh.8 According to the crystal structure, Ti8Ni6Si7 may be considered as the ideal composition. The Russian investigators5 identified six additional ternary phases isotypic with Ti6Ni6Si7, in which titanium is replaced by Mn, V, Nb, Ta, Zr, and Hf, and one, namely MneNil6Ge7, in which germanium replaces silicon. They also found that Cr6Ni6Si7, which does not occur as a ternary phase, can be stabilized by replacing 1 at. pct of the Cr by V, Mn, or Ta. Another ternary silicide was found by Westbrook et al.3 at the composition TiNiSi, and it was designated by them as the E phase. The crystal structure of this phase has not been deter-

Jan 1, 1963

By A. H. Daane, B. J. Beaudry

The Sc-Y and Sc-Zr systems were studied by thermal and X-ray methods. Both systems are characterized by complete solid solubility in the low temperature hexagonal form and in the high temperature bcc form. In the Sc-Y system, there is a minimum in the solidus at 50 at. pct and 1365°C, while the solidus in the Sc-Zr system follows a nearly straight line relationship between the melting point of scandium and zirconium. There is a minimum in the temperature of transition from hexagonal to bcc in the Sc-Y system at 43 at. pct Y and 1175°C; while the temperature of transition is raised in the Sc-Zr system to a maximum of 1415 °C at 30 at. pct Zr. INTEREST in the metals of the first transition series has usually stemmed from their useful properties; however, there is now a great deal of interest in determining the fundamental nature of these metals. Since scandium is the first of these transition metals, a study of the preparation and Properties1 and the alloying behavior of scandium2 was initiated. In a continuing study of the alloying behavior of scandium, the systems of scandium with zirconium and yttrium have been established. Extensive solid solubility in both the Sc-Zr and Sc-Y systems was expected from application of the classical rules of Hume-Rothery. Also, the modified Darken and Gurry plot as suggested by Gschneid-ner3 showed ideal conditions for solubility in the Sc-Zr system with less favorable conditions in the Sc-Y system. The effect of scandium on the transformation temperature of zirconium and yttrium was of interest, since a recent empirical observation by Uly and Burr4 predicted that the solute scandium would raise the transformation temperature of zirconium and lower the yttrium transformation. In addition to noting the validity of the above predictions, the SC-Y and Sc-Zr systems were established. EXPERIMENTAL METHODS Materials. The metals employed in this investigation were crystal bar zirconium, distilled scandium prepared by the method described by Spedding, et al.1 and yttrium prepared by the method described by Carlson, et a1.5 The major impurities present in these metals are listed in Table I in ppm. Alloy Preparation. All the alloys examined were initially formed by comelting the two metals in a nonconsumable electrode arc-melting furnace under an atmosphere of purified helium or argon. The buttons were inverted at least five times and re-melted each time to ensure homogeneity. During preparation of Sc-Zr alloys, approximately 1 wt pct was lost which was attributed entirely to the loss of scandium by distillation. When preparing Sc-Y alloys, approximately 1.5 wt pct was lost, but it was assumed that the intended composition was maintained, since the relative weight lost when arc melting the component metals was nearly the same. Samples weighing 15 to 20 g were prepared for time-temperature thermal analysis, while only 1- to 2-g samples were prepared for the optical pyrometer and X-ray diffraction studies. Thermal Methods. The solidus and the melting points of the metals were determined by an optical pyrometer method described previously.2 The temperatures at which the transformation from hexagonal to bcc occurs were determined by differential thermal analysis. Several points on the solidus and liquidus in the Sc-Y system were also determined by this method and are in good agreement with those obtained by the optical pyrometer method. The procedure followed in the preparation of samples for thermal analysis and the furnace used have been described elsewhere.2&apos;6 Since a limited quantity of scandium was available, most of the alloys were not melted during thermal analysis, thus avoiding contamination by the crucible. The alloy could then be reused and the composition changed by adding the desired quantity of solute to obtain the next alloy. Heat Treatment and X-Ray Methods. In order to ensure homogeneity, the "as arc-melted" alloys Were wrapped in tantalum foil, sealed in quartz capsules and heated at 1100°C for 15 hr and then cooled at a rate of 8 deg per min. Samples for X-ray diffraction were filed from these heat-treated alloys, sealed in 1/8 in. by 1/2 in. tantalum capsules under

Jan 1, 1963

By C. D. Allman

Specifications for coal at the Grand Lake thermal electric station read in part: "Coal will be Rom Minto Bituminous (strip operation). Maximum lump 3x3x4 ft. Very corrosive, abrasive and when damp, sticky. Coal may consist of frozen lumps of coal, snow and ice." To maintain quality control it was necessary to develop an automatic sampling system capable of: 1) sampling from one 10-ton truckload every 1½ min; 2) permitting an operator to automatically take a sample from each truckload; 3) depositing the sample in a pre-selected container, one of a possible 10; and 4) performing the sampling operations in accordance with latest ASTM specifications for sampling coal with an ash content of 35%. This paper tells how these and other problems were resolved and describes the equipment used. The New Brunswick Electric Power Commission issued detailed specification No. 5351-5009 outlining the scope of work and general requirements for a mechanical coal handling system to be installed at the Commissions Grand Lake Generating Station. The thermal station is located at Newcastle Creek, some 40 miles east of Fredericton, N.B. Canada, on the shore of Grand Lake. This particular location is immediately adjacent to the Minto strip mining coal area of New Brunswick. Contained in the specifications, but not detailed specifically was an automatic coal sampling system. The system outlined, was to be designed and specified by the individual equipment tenderers. In conjunction with the Hardinge Co., the Barber-Greene Co. designed a sampling system which was contained in the general contract proposal. The system as designed originally, however, presented certain limitations to a continuous coal handling system and was ultimately changed. However, it was only through preliminary study and design that problems created by the specifications were determined, and these problems discussed and finally negotiated with the NBEPC engineering staff created the subsequent sampling system now being installed by Barber-Greene. It must be considered that where the original specifications did not detail the mechanical equipment, it was necessary to present a system which would correspond to the intent of specification and for which Barber-Greene would be responsible as to function, but remain in a competitive position with regard to the tender considered primarily on a price basis. The system now being installed, contains basically all the components which were detailed originally, with the exception of the holding bin arrangement, which was changed to allow a continuous operation of the entire coal handling system. SPECIFICATIONS The specifications covering the sampling system follow. 4.5 Sampler: An automatic sampling system shall be installed capable of sampling one-truck load of coal every 1½ min. When the coal is dumped into the receiving hopper, the operator shall push a button and the sampler shall automatically take a sample of that particular coal when it reaches the sampler. Then the sample taken shall be crushed and reduced in quantity to a workable sample and deposited in a pre-selected container, one of a possible ten. All samples and sampling operations shall be in accordance with the latest edition of ASTM designation 492 for sampling coal with an ash content of 35%. The coal for the initial sample shall have maximum sized lumps of about 3/4 in. and the final sample shall be adjustable from 2 to 5 lb per sample and capable of passing through a sieve with 1/8-in. diam openings. It should be noted that, because of the time delay between the time the sample is requested and when it is actually taken, the operator may call for one or two additional samples from different coal before the first sample is completely refined and in the final sample can. Coal is received from a number of different suppliers on the same day, therefore, the system shall be designed so that there is no possibility of mixing or contaminating the coal from the different suppliers. All coal rejected from the sample shall be returned to the main conveyor. All chutes, hoppers, etc. shall be designed in accordance with Section 4.6 of these specifications. 4.6 Chutes, Hoppers, etc. All chutes and hoppers

Jan 1, 1963

By Nichols J. Grant, Bill C. Geissen

In low temperature phase diagrams, liquidus curves below about 1500°C are relatively easily established, e.g., by thermal analysis or separation of coexisting solid and liquid phases, followed by chemical analysis. Experimental difficulties increase considerably at higher temperatures and in systems involving more reactive metals. Although there are now thermocouples available for use from 1600" to 2400°c, as summarized by Caldwell,&apos; the need for frequent calibration, aging, and contamination problems, and unavailability of suitable protection tubes has sharply limited their use at higher temperatures. Many of the high melt- ing metals are found to react with refractory oxides. TO avoid such problems, a frequently used procedure is the diffusion and saturation method, as described by Spedding et a1.&apos; for the system La-C. This technique involves the annealing of one metal or a suitable alloy in a crucible of the other element at a temperature above the melting point, followed by chemical analysis of the center of the melt, after equilibrium is established. Further, if an alloy system is to be investigated employing the electron microbeam probe, and calibration charts have been established, it may be possible to measure the alloy concentration at the center of a cored as-cast structure, and to conclude from this points on the liquidus curve in a manner similar to the one to be described. It is known that in phases with a broad homogeneity range the rapidly cooled, cored, as-cast structure of an alloy presents concentrations having different lattice constants; this spread of lattice constant values contributes to the broadened lines of a powder pattern for the as-cast condition. The region of the crystal which is first to solidify will then correspond to the edge of the lines if the change of the lattice parameters with concentration is monotonous. In the course of the determination of the Ta-Tr phase diagram,3 it became evident that such behavior made it possible to construct the

Jan 1, 1963

By E. Douglas, D. N. Collins, J. R. Stevens

E. Douglas (Dept. of Scientific and lndustrial Re-search, Warren Spring Laboratory, Hertfordshire, England) — The authors are to be congratulated on the considerable improvements they have made in tailoring efficiency and selectivity terms which are generally superior to the alternative forms in current use. However, I feel that their efficiency expression is limited to lower-grade feeds; its accuracy reduces as the feed grade increases. For example, its application to such processes as the beneficiation of glass sands, refractories and clays will invoIve considerable inaccuracies. The reason for this lies in the direct use of recovery, which, with high-grade feeds, biases their empirical expression, R(1 - c/h). With a 90% grade feed, the recovery weighting for the slightest degree of beneficiation, over a zero efficiency sampling operation, will be 90+%+ I disagree with their second basic requirement which states that there can be no fundamental basis for any single quantifying expression. A formula giving a comprehensive representation of concentra- tion efficiency can be derived fundamentally accord-to the procedure outlined in the literature. &apos;&apos; This formula, called the Basic Efficiency formula, is

Jan 1, 1963

By S. E. Bronisz, Dana L. Douglass

a Uranium was deformed by cold rolling, and the effects of this plustic deformation on the microstruc-ture of the metal were observed by the technique of transmission elecbon microscopy. The recrystalli-zation of selected cold-wmked samples was also studied by this method. The samples were prepared for examination by electrolytic thinning in a standard metallographic electrolyte which has not been previously reported as being used in producing thin foils of uranium. The microstructural changes observed in the a uranium were generally similar to those seen by optical microscopy. The changes in the microstructure of a uranium following cold work and recrystallization treatments have been the subjects of several studies employing optical and X-ray techniques.12-19 These studies indicated that twinning was the redominant mode of deformation at room temperature20 and that the regions of high energy associated with the deformation twins were preferred sites for the initiation of recrystallization.15,18, Recently several workers have prepared thin foils of uranium suitable for examination by transmission electron microscopy.&apos;-lo The foils thus prepared have been used to study fission fragment damage; a particular dislocation reaction,&apos; and gas precipitation." At this laboratory the microstructural changes occurring during the cold working and recrystallizing of a uranium samples have been studied by using transmission electron-microscopy techniques. The foils used in this work were electrolytically thinned in a polishing bath not reported previously in the literature as being used for this purpose. EXPERIMENTAL PROCEDURE The uranium used in this investigation was depleted a uranium sheet 4 mils thick. The results of a spectrochemical analysis of this material are shown in Table I. The as-received uranium was cut into strips, 1 in. wide by 5 in. long, and annealed in vacuo at 600°C for 2-1/2 hr. The resulting microstructure consisted of relatively uniform, equiaxed grains having diameters of 10 to 50 p. Cold Working. The cold-worked samples were prepared by rolling several of the annealed uranium strips to various thicknesses. The strips were reduced 3.5 ± 0.5, 6.0 ± 0.6, 10.0 ± 0.5, 19.5 ± 1.0, and 28.5 ± 2.0 pct in thickness. It was not possible to achieve these reductions with a single pass through the rolling mill, so the strips were turned end for end during the rolling procedure. The cold-rolled strips were stored in dry ice until samples from them could be thinned and examined (within 24 hr after rolling). Annealing. The samples used in studying the re-crystallization behavior of a uranium were obtained by annealing sections of the strips which had been reduced 10.0 and 28.5 pct. These samples were sealed in evacuated Pyrex capsules and were annealed in a tube furnace at temperatures from 200" to 600°C and for times from 1/2 to 2 hr, see Table l. Thinning: The samples from the rolling and heat treatments were prepared for examination in the electron microscope by electropolishing in a bath composed of 25 g chromic acid, 133 ml glacial acetic acid, and 25 ml water. This electrolyte has been used and recommended for preparing specimens for optical metallography It was necessary to mask the edges of the sample with a stop-off paint in order to prevent preferential attack in these areas. The paint used was made by dissolving polystyrene in benzene. The electrolytic cell consisted of a cylindrical stainless-steel cathode placed in a beaker containing the electrolyte, with the sample as the anode positioned at the cell axis. The temperature of the electrolyte was held below 15°C by cooling with liquid

Jan 1, 1963

By H. H. Kellogg, T. R. Ingraham

Three anhydrous zinc sulfates have been identified. They are: ZnSO,(a), stable below 1007°K; ZnS04(/3), stable above 1007OK; and ZnO.ZZnSO,. The decomposition pressure of each sulfate has been measured and the following relations calculated from the results: The measured data have been combined with the known themzodynamic properties of ZnS, ZnO, Zn, SO,, and SO, to yield univariant and bivariant phase diagrams for the system Zn-S-0. The application of these diagrams to problems of roasting zinc concentrates is discussed. PRESENT knowledge of the equilibrium chemistry of the system Zn-S:O, so essential to scientific control of zinc-blende roasting, is deficient in several respects. A basic sulfate of zinc has been reported by many investigators, but its composition is in doubt and its thermodynamic properties have not been measured. Our scanty knowledge of the properties of the normal sulfate at roasting temperatures is based on old and inexact studies. A crystal transformation in the normal sulfate, involving a sizable heat effect, has been noted by several investigators but has never been quantified. The studies reported herein were designed to fill these gaps in knowledge and to make possible a reasonably complete thermodynamic description of the system Zn-S-0 at roasting temperatures. The results make possible a far more exact understanding of zinc roasting chemistry than was hitherto possible. EXPERIMENTAL The principal experimental technique employed was the measurement of the total gas pressure developed from decomposition of either ZnSO, or ZnO2ZnS0, in a closed system. The apparatus employed was essentially the same as that described by Warner and lngrahaml and Flengas and tngraham.&apos; The unusual feature is a flexible Pyrex bellows used to separate the reaction gas mixture (S03, SOz, and 02) from the mercury in the manometer and thus prevent corrosion of the mercury by SO3. The bellows operates without evidence of hysteresis and, barring accidents, may be used for several months. The response of the bellows varies from manometer to manometer, but is generally of the order of 0.6-cm displacement for a l-cm change in pressure. The response for all manometers has been linear over the range 0 to 1 atm. To prevent condensation and polymerization of sulfur trioxide, the bellows-manometer was maintained at 100.0" * 0.5" by a circulating bath of silicone oil. The connecting tubing between the manometer and the furnace was maintained at 100.0" * 0.2"* also, with a stirred air bath. The open end of the manometer was connected with a chamber which was maintained at a known pressure. The pressure could be varied so that readings of the height of the mercury column, measured with a cathetometer, could be made with both rising and falling mercury column. By using the average of the readings, any error due to sticking of the mercury column was minimized. The sample was placed in a 2-in.-long platinum boat formed into the shape of a half-cylinder. The sample was prepared as a fine powder and pressed against the inner wall of the platinum boat. A silica thermocouple well, covered with a platinum sleeve, was placed lengthwise along the center of the boat. The temperature of the sample was read on a calibrated Pt-10 pct Rh theirnocouple. The temperature profile of the furnace was constant within ± 0.2 C over the length of furnace occupied by the sample. The horizontal furnace used to contain the sample and the quartz reaction tube was electrically heated, with the control thermocouple placed 1/4 in. from the windings. A Brown Pyro-O-Vane temperature controller with a 3-sec response time was used to maintain the furnace temperature. Before beginning a run, the apparatus, including the bellows manometer, was thoroughly washed in sib with acid and distilled water to remove any

Jan 1, 1963

By R. G. Ward

The temperature gradient in the subhearth metal or "salamandern of the iron bhst furnace results in the establishment of gradients in the concentrations of silicon, manganese, carbon, and sulfur. The temperature and compositional variations observed in three blast furnaces are analyzed according to irreversible thermodynamics and the systems appear to be close to the steady state condition. Apparent heats of transport, Q, for silicon, manganese, carbon, and sulfur are found to be respectively -17.5, -5, -2.1, and+22k cal per g mol. In conclusion the significance of thermal diffusion in extraction metallurgy is briefly discussed. INCREASING interest has been shown in recent years in the application of irreversible thermodynamics to metallurgical problems. In particular studies have been made of the transport of matter in thermal gradients1-&apos; and under chemical gradients imposed by a binary solvent However, no detailed example in extraction metallurgy has been reported although gradients are the essence of many extractive processes. The case of the distribution of elements in molten blast furnace iron under a thermal gradient is discussed here. DATA In blast furnace operation the hearth bottom is often extensively destroyed by molten metal, and the metal may penetrate perhaps 10 ft into the furnace foundations forming a "bear" or "salamander". Several hundred tons of molten metal may thus exist beneath the level of the conventional tap hole and remain relatively undisturbed for several years under a thermal gradient. This system is subject to little convective stirring because the temperature decreases from top to bottom, and mechanical stirring due to movements in the stack and to tapping operations is unlikely to penetrate far into the metal. The system may thus be regarded as static

Jan 1, 1963

By Charles L. Guettel

The temperature coefficients of electrical resistance of 31 alloys in the nickel-rich corner of the Ni-Cr-Fe system were determined. The results indicate that a range of binary Ni-Cr alloys has lower temperature coefficients than a specific region of Ni-Cr-Fe alloys which has been reported and quoted by others as providing the lowest coefficients in the ternary system. DESIRABLE properties of resistivity and temperature coefficients of resistance have been the basis for the successful commercial application of various Ni-Cr and Ni-Cr-Fe alloys. In particular, low or negligible temperature coefficients of resistance are necessary for wire used in precision wire wound resistors and potentiometers involved in closely controlled electrical and electronic circuitry. Alloys most successfully applied to this purpose basically have not been ternary Ni-Cr-Fe alloys but rather heat-treated Ni-Cr alloys in the region of approximately 73 to 79 pct Ni and 20 pct Cr with significant additions of other elements such as aluminum, silicon, iron, copper, manganese, and cobalt. While the addition elements play a vital role in the nature and control of the temperature-resistance curve of any one of these alloys, the inherent relatively low temperature coefficient of the binary Ni-Cr base composition itself in the approximate region of 80 pct Ni and 20 pct Cr contributes fundamentally to the eventual negligible temperature coefficient obtained with the applied alloys. W. A. Dean 1 has reported mean temperature coefficients (20&apos; to 100oC) of as-cast samples for the Ni-Cr-Fe system, the nickel corner of which is given in Fig. 1. Dean had to use as-cast samples because alloys from a considerable region of the system were unworkable. Dean refers to the work of Hunter and sebast2 who used annealed wire samples to show that, for chromium contents of 10 to 25 pct, the temperature coefficient increases as the iron content is increased at the expense of nickel. Although the data of Hunter and Sebast were limited in the nickel-rich areas to eight samples of 60 to 91 pct Ni with only four samples containing iron, the possibility that no Ni-Cr-Fe alloy has a lower temperature coefficient than certain binary Ni-Cr alloys should have been given serious consideration. However, Dean&apos;s work has been referred to by J. S. Marsh,3 who, quoting Dean, states that for the temperature coefficients "the smallest values-about 0.0001 per oC (100 ppm)—were found for alloys containing about 55 pct Ni and 20 pct Cr" (balance iron). A region such as that reported by Dean would be significant to those trying to develop alloys for the applications described. Therefore, a series of three-pound laboratory open-air induction melts of Ni-Cr and Ni-Cr-Fe alloys were melted, conventionally processed to 0.005 in. diam wire, and continuously strand annealed at 1900° F. The basic Ni-Cr compositions, with balances essentially iron other than usual minor impurities, and the corresponding temperature coefficients of resistance and resistivities are given in Table I. The resistivities are approximate and are not to be considered as a basis for relating them to their position of composition in the ternary system. The wire diameters were determined with a micrometer, and not by weight and density measurements which would be required for accurate resistivity values. However,

Jan 1, 1963

By Laurence Pellier

Electron microscopical studies were made of the effect of sensitization at 1200oF on a Type-.104 stainless steel with high carbon and low nitrogen and oxygen contents, after solution annealing and after cold working. The loci of the carbide precipitates in the early stages of sensitization were followed in dry stripped plastic replicas. Some observations were made by direct electron transmission on thinned films. Intragranular dislocations showed a high degree of stability through the annealing necessary to produce sensitization. I HE present work was undertaken to determine the effect of sensitization, at 1200°F, for 1/2 hr, on the electron microstructure of a Type-304 stainless steel with high carbon, and low nitrogen and oxygen contents, after solution annealing and after cold working. Many electron microscopical studies of sensitization of 18-8 stainless steels have already been made. Most of them utilized extraction replicas, from which the morphology and composition of the precipitated carbides could be established.&apos;-" ry stripped replicas were seldom used for such studies, although it was demonstrated that they are applicable, in general, to EurveYs of the general microstructure of many alloys&apos; and, in particular, to the observation of precipitated carbides in austenitic stainless steels.3

Jan 1, 1963

By H. W. Knott, M. H. Mueller

The crystal structures of Ti2Cu, Ti2Ni, Ti4Ni2O, and Ti4Cu20 have been determined using powder specimens examined by X-ray and neutron diffraction. Lattice constants have been determined for all four phases using X-ray powder diffraction films. Atom positional parameters of all four phases have been determined from observed neutron intensities. X-ray diffraction calculated intensity data have been presented also for the phase Ti2Cu to point out the particular suitability of neutron diffraction in this case. Interatomic distances have been determined using the positional parameters obtained from neutron diffraction. ALTHOUGH some investigations of the crystal structures have been made of these four compounds previously,&apos;-13 it was the purpose of the present investigation to expand the previous work in order to locate the various atoms, determine their coordinates, and to confirm or to correct some of the previous work. It was convenient to group these four compounds together since they are related chemicallv and/or structurally. The compound Ti2Cu is tetragonil; and Ti2Ni, Ti4Ni2O, and Ti4CU2O are all large fees of the same space group. Ti2Cu has been previously reported as a fee phase by Laves and Wallbaum;1 and Rostoker2 which was possibly the oxide phase, Ti4Cu20. Joukainen, Grant, and Floe;3 and Trzebiatowski, Berak, and Ramotow-ski4 have also reported a phase of this composition. karlsson5 has reported a small fct phase of the composition Ti3Cu which may be the presently discussed Ti2Cu phase. More recently Ence and Margolin6 have reported a small fct phase for Ti2Cu and the present authors7 together with Nevitt8 have briefly reported it to be a bet related to the fct with a co three times the length of the co of the fct and have also reported that this phase has a very limited composition. Further refinements will be reported which have varied some of the parameters of this bct structure slightly. Ti2Ni has been reported as a fee phase by Laves and wallbaum;1 Duwez and taylor;9 Rostoker;2 Poole and Hume-Rothery;10 and Yurko, Barton, and parr.11 In a later paper Yurko, Barton, and parr12 have given the complete structure of this phase based on an X-ray diffraction study which was independently confirmed with neutron diffraction by Mueller and knott.7 Additional crystal structure information will be given. Ti4Ti2O, Ti4Cu2O, and a number of other compounds including Ti4Fe2O have been reported as fcc phases by Rostoker,2 and more recently Nevitt13 has confirmed the Ti4Ti2O phase. Rostoker,2 however has reported diffraction lines for Ti4Fe2O which do not have all odd or all even indices. These lines, therefore, cannot be observed if this compound has a fee structure. This same error has crept into the diffraction results reported for TiNi2O and Ti4Cu20 in the ASTM powder data which has been credited from Rostoker&apos;s data. Complete crystal structures of these two phases will be presented. Although all four of these structures have large unit cells and hence do not lend themselves for completely resolved neutron powder patterns, a sufficient number of individual reflections was observed for solving the structure. They also serve as good examples of some of the advantages to be gained by using both neutron and X-ray diffraction techniques. EXPERIMENTAL PROCEDURE All of the alloys were prepared by arc melting. The starting metals had the following purity: Cu 99.999 pct, Ni 99.83 pct, and Ti 99.92 pct. Oxygen was introduced into the two oxide phases as chemically pure TiO2, with the remainder of the titanium coming from the above mentioned metal. All of the sample buttons were annealed in evacuated Vycor tubes, the two binary phases for 5 days at 700°C and the two oxide phases for 3 days at 900°C. Oxygen analyses were performed on all four phases by two independent laboratories with the following amounts of oxygen present in atomic percent; Ti2Cu-0.06, Ti2Ni-1.03, Ti4Ni2O-13.95, and Ti4Cu20-13.87. The stoichiometric amount for the oxide phases is 14.29 at. pct. Since all of the samples were very brittle they were easily reduced to a powder for diffraction measurements. The lattice constants given in Table I were determined for the four compounds from X-ray diffraction patterns of powder samples exposed to filtered copper radiation using a 114.59 mm diam Debye-Scherrer type camera using the Straumanis loading. None of the patterns showed a detectable amount of a second phase. The lattice constants were obtained from an IBM 704 computer program employing a least squares treatment with systematic correction terms as previously reported.14

Jan 1, 1963

By T. P. Chen, F. W. Bowdish

Studies made with a captive bubble apparatus on the sulfidization and collection by amyl xanthate of true chrysocolla specimens have defined the ranges of pH value and sulfide concentration which permit contact between the bubble and the mineral surface. Titanium compounds were the most effective of the materials found to activate the sulfidization of chrysocolla. With titanium activation, the contact angles and the ranges of pH value and sulfide wncentration giving bubble contact were all increased. Chrysocolla ores were concentrated by flotation. Chrysocolla ores occur at many localities in grade and quantity sufficient to make mining and millin feasible, but no satisfactory method of concentratio has been found. Although chrysocolla may be leached with acid, only those ores without acid-consuming gangue may be leached economically. Because of its potential importance, a study of the conditions nece sary for flotation of chrysocolla has been carried ou The literature contains a few references to flotation of chrysocolla. Two methods were developed by the U. S. Bureau of Mines.1,2 The first consisted of a fatty acid soap and a high xanthate as collectors of chrysocolla from a synthetic ore, while the second involved the use of hydrogen sulfide and xanthate. Ludt and DeWitt3 demonstrated the difference in adsorptive powers of chrysocolla and quartz for bas triphenyl methane dyes and suggested the use of butyl, hexyl or octyl-substituted malachite green as collector. Jackel4 emphasized the effects of combin tions of reagents such as Aerofloat 31, pine oil, and Reagents 404 and 425 with sodium sulfide and zinc hydrosulfite as conditioning agents. Although he reported recoveries of 89% from a synthetic ore and 98% from a natural ore containing azurite, malachite, chalcopyrite and chrysocolla, careful application of Jackel&apos;s method to chrysocolla from Tyrone, N.M., failed to give a high recovery. MATERIALS AND TECHNIQUE Samples from Inspiration, Ariz., and Tyrone and Magdalena, N. M., were used for experimentation and verified as true chrysocolla by leaching tests, specific gravity tests and X-ray diffraction. Chrysocolla does not dissolve at pH 4, although malachite and azurite do. Chrysocolla is about half as dense as the copper carbonates. X-ray diffraction analyses by the powder camera method confirmed the samples as true chrysocolla. A captive bubble apparatus, which cast an enlarged image of the air bubble and the mineral surface upon a screen, was used to check on the character of the surfaces. The specimens were prepared by grinding a flat surface on a glass plate using fine abrasive; then they were washed and kept in distilled water until they were to be treated with reagents. Before each reagent treatment, the specimen was carefully checked for cleanliness in the captive bubble apparatus. It was assumed that the surface was clean if, after fine grinding and washing of the specimen, the bubble would not stick. Specimens were handled with glass forceps, and precautions were taken to avoid contamination of the mineral surfaces. Contact angle measurements were carefully made several times on each treated specimen to obtain reliable average values. EFFECT OF pH VALUE AND SODIUM SULFIDE CONCENTRATION In each experiment, a specimen with a freshly ground surface was immersed for 10 min in a solution of sodium sulfide, washed and immersed for 15 min in a solution containing 30 mg per 1 of potassium amyl xanthate. The specimen was then washed again in distilled water and tested for contact angle in the captive bubble apparatus while submerged in distilled water. In this series of experiments, the pH of the sulfidizing solution was varied from 3 to 7, and the concentration of sodium sulfide, containing 60% Na2S, was varied from 50 to 650 mg per 1. Many combinations of pH value and sulfide concentration resulted in no contact between the bubble and the surface, but over a limited range of conditions, contact angles varying from 24ºto 52ºwere obtained. The data in Fig. 1 show sulfidization conditions that lead to bubble contact and those that do not. The region of contact is surprisingly small, which may indicate why flotation of chrysocolla involving sulfidization has proven so difficult in practice. Several features of the system are illustrated in Fig. 1. In the region between pH values of 4 and 6 with sodium sulfide concentrations below about 350

Jan 1, 1963

By L. Adler

The author recently proposed a technique for handling the effect of planes of weakness on failure in geologic material.1 The technique employed an "extended" Mohr&apos;s rupture envelope, on which was superimposed a generalized three dimensional stress representation. Subsequently, the method was applied to so-called two-dimensional stress states" which were in reality degenerate three-dimensional ones. Since a two-dimensional stress solution usually refers to a plane stress condition, the terminology was confusing. The distinction between a plane stress state and a degenerate three-dimensional one is shown in Fig. 1. The solution of problems involving a generalized three-dimensional stress state is greatly aided by continual reference to the basic principle that no stress components can act on a plane, oriented as is the weakness plane, which lies outside of the weakness plane&apos;s rupture enVelope.2 This is shown in Fig. 2; and if it is also remembered that the radii of the Mohr&apos;s Circles give the orientation of such a plane, solutions are easier to follow, and perform. Sample Problem 1: Site Location (generalized three-dimensional case).&apos; Given: 1) Both rupture envelope for the solid and plane of weakness. 2) Existing principal stresses and orientations in space (?12, ?13) obtained from a stress analysis of the proposed structure. Find: Permissible orientations of the weakness plane in order to select a suitable site.

Jan 1, 1963

By G. R. Kotler, W. A. Tiller, W. C. Johnston

Experiments carried out on 100 g samples of molten tin and Sn-Pb alloys showed that the magnitude of the field strength, H, does not effect the supercooling, aTn, at which the initial nucleus of solid forms. However, the nuwlber of nuclei forming per cc, n, is found to increase greatly with H for fixed ATN and to increase with ATN for fixed H. The value of n increases greatly with the presence of solute and is found to he indefiendent of the cooling rate of the simples. Further, the most effective time for stirring to enhance n is immediately following the initiation of recalescence. The effect of inducing nucleation with the aid of a mechanical impact both in the presence and absence of stirring has also been studied. All proposed mechanisms for the enhancement of n by physical means seem to be inadequate in accounting for these results. IN any real nucleation experiment there are two effects influencing the results that would not be predieted from classical homogeneous nucleation theory. These may be separated into chemical and mechanical effects. The chemical effects are twofold. 1) Nucleation catalysts are present which enhance the nucleation frequency of new grains over that predicted by classical homogeneous nucleation theory.&apos; 2) Solute will restrain the growth of nuclei so that many others may form.2,3 The mechanical effects are also two-fold. 1) Vibration (sonic or ultrasonic) of the freezing liquid enhances the nucleation frequency of new grains over that given by the chemical effects alone.4-6 2) Macroscopic fluid-flow effects produce the same effect as l).&apos;7&apos; It is also possible to influence the nucleation experiment by certain physical effects such as the application of electric and magnetic fields.9 From classical homogeneous nucleation theory one would predict the following relationship between the nucleation rate, N1 (number of nuclei formed per unit volume per unit time), and bath supercooling, AT, for an isothermal experiment.

Jan 1, 1963

By Anton Sawatzky, Erich Vogt

By means of mathematical solutions to the appropriate diffusion equations, we describe the kinetics of the thermal diffusion of hydrogen in Zircaloy-2 for the various temperatures and concentrations encountered in a heavy water moderated reactor. When the hydrogen concentration is below terminal solid solubility only the a Phase is present. Redistributions are then described in terms of the characteristic functions of the difhsion equation. For higher concentrations both the a and 6 phases are present. We assume the two phases to be always in equilibrium. For moderately small hydrogen concentrations exact solutions of the two-phase equation approach the the approximate solutions derived by Sawatzky and for all concentrations the exact solutions exhibit the qualitative features of his result: the two-phase concentration increases with time, everywhere; in the absence of a hydrogen current at the hot end of the sample an a-phase region always exists there; the interface of the a + 6 , a-phase boundary moves toward the cold md of the sample and the hydrogen concentration is discontinuous at the interface. Simultaneous solulions of the a and a + 6 hydrogen distributims and of the concomitant interface motion are obtained and compared to the observations of Sawatzky and Markowitz. The kinetics of the hydrogen diffusion process are shown to lead to m apparent heat of transport of the a phase which is lower than the actual value (even for samples with long anneals) thus resolving at least partially the disparity between experimental measurements of this quantity. A number of recent papers1"4 have reported measurements on the diffusion and redistribution of hydrogen in Zircaloy-2 under temperature and concentration gradients. These studies were instigated by problems arising from increasing use of Zircaloy-2 as a fuel element cladding material in pressurized-water power-reactors. The Zircaloy-2 picks up hydrogen during the operation of the reactor: the consequent precipitation of zirconium hydride in the Zircaloy-2 has pronounced effects on its mechanical properties. The Purpose of the present Paper is to describe the kinetics of the thermal diffusion of hydrogen in Zircaloy-2 for the various hydrogen concentrations and temperatures likely to be encountered in reactors. When the hydrogen in the Zircaloy-2 is entirely in the solid solution phase (a phase), the differential equation for thermal diffusion is well known and the redistribution can be described by standard mathematical methods some of which are given in Section 11 below. The treatment of the a + 6 (hydride) region differs from the earlier treatment of sawatzky3 by taking into account several modifications of the two-phase diffusion equations as suggested to us by Markowitz4 and Kidson.5 Even with the modifications the results obtained in our more complete treatment are substantially the same as those found by Sawatzky. As we show, the difference between the results of sawatzky3 and kIarkowitz4 is largely due to the difference in the geometry of their experiments. In the next section we derive the modified two-phase equation for arbitrary geometry. The exact solution of this equation is given in Section III for linear and cylindrical geometry. It is shown that Sawatzky&apos;s approximate solution is quite accurate for almost all the temperatures and hydrogen concentrations which are actually encountered. In Sawatzky&apos;s approximate theory the hydrogen concentration everywhere in the two-phase region increases continuously. As his paper pointed out, this result, together with hydrogen conservation, implies that in a sample with no hydrogen current flowing into the hot end a two-phase region is always accompanied by a single-phase region at the hot end of the sample. The net hydrogen gain in the two-phase region is supplied by the decrease of hydrogen in the single-phase region and by the movement of the (a, a + 6) boundary toward the cold end of the sample. Hydrogen conservation at the (a, a + 6) boundary leads to a discontinuity in the concentration and its derivative there. In Section IV it is shown how these qualitative features of the thermal diffusion kinetics arise from the simultaneous solution of the a-phase differential equation and a + 6 phase equation. Methods derived by us previously for the solution of the redistribution in both phases and the accompanying motion of the boundary are used to obtain approximate solutions valid for large times. The solutions account well for the observed redistributions of Sawatzky and Markowitz. It is shown how the continuing motion of the (a, a + 6) boundary leads to measured values of the heat of transport lower than the actual value, even for specimens with relatively long anneals.

Jan 1, 1963