By J. E. Forciea, R. W. Salmi

Operating and research personnel at U.S. Steel's Pilotac concentrator have evolved specifications for magnetic separators suitable for use in beneficiation of Mesabi magnetic taconite. These specifications were developed as a result of investigations into the operating and metallurgical problems at the Pilotac concentrator over a period of some ten years. This paper discusses primary magnetic separator specifications, but much of the information is also pertinent to secondary and tertiary magnetic separators. Of particular significance is the proposal of a new basis for specifying the magnetic field which includes consideration of both field strength and field gradient. Other areas of discussion include flowsheet service, operating conditions such as drum speed and pulp level, tank configuration, magnet strength including field gradient, sleeve bearing design, designation of corrosion resistant materials and other details that result in a metallurgically efficient machine that has low repair and maintenance requirements. The mechanical and metallurgical design of magnetic separators at the Pilotac plant, Minnesota Ore Operations, United States Steel Corp. has progressed from the original single-stage, belt-type machines to the present multiple-stage, drum-type units, In ten years of operation, the plant operating and research personnel, in consultation with manufacturers, have made design changes to improve mechanical, electrical and magnetic features to meet process needs as flowsheet designs developed and to incorporate new permanent magnet materials as they became available. Separator specifications were an end result of this effort. The latest specifications which were developed for the Minnesota Ore Operations' plant were not all-inclusive listings; they covered only those points indicated by plant experience. For example, magnet pole piece design and dimensions were not stated. The manufacturers were given freedom to use any design as long as the field pattern was as specified. The selection of the items to be included in the specifications was undoubtedly influenced by particular conditions at Pilotac such as composition of plant water, concentration characteristics of the ore, repair and maintenance facilities available and the research programs that had been conducted. Only the developments leading to the specifications for a primary or "cobber" magnetic separator are presented in this paper. However, the same general concepts are used to specify secondary and tertiary separators. The areas of interest discussed include flowsheet service, tank configuration, magnet design, bearings, materials of construction, and some minor mechanical details. FLOWSHEET SERVICE The primary magnetic separators in the Pilotac Concentrator flowsheet are located after the first stage of grinding as shown in Fig. 1.

Jan 1, 1965

By T. Yamasaki, S. Usu

Adsorption of potassium dodecyl xanthate from aqueous solutions on artificial and natural zinc sul-fides was studied by means of infrared absorption spectroscopy. The adsorption species and their stabilities varied depending upon the conditions of the surfaces of the zinc sulfides. Adsorption products were analyzed after they had been removed from the surface with pyridine. Zinc dodecyl xanthate was confirmed for surfaces covered with oxidized products while dodecyl alcohol and carbon disulfide were detected on purified or weakly oxidized surfaces. It is of great significance to study the adsorbed species of collectors on the surface of sulfide minerals with a view of increasing our understanding of the mechanism of flotation. Compared with other methods, infrared spectroscopy promises to be of particular value in determining the nature of the species adsorbed at the mineral/solution interface since it gives direct identification of the adsorption products; and, furthermore, it has an advantage over the electron diffraction technique which has been employed in similar problems in that infrared spectroscopy utilizes radiation of very low energy so that the probability of changing the unstable surface films during examination should be correspondingly decreased. Infrared spectroscopic studies concerned with sulfide mineral flotation have already been reported by several investigators on zinc sulfide-hexanthi01' and lead sulfide-xanthate2,3 systems. The purpose of the present study was to investigate the adsorption of potassium dodecyl xanthate (KDX) at the zinc sulfide-aqueous solution interface by means of infrared spectroscopy. Rarely is the pure zinc sulfide-xanthate system encountered in practical flotation since zinc sulfide is usually activated with small amounts of certain metallic ions, such as copper ion. However, investigation of the pure zinc sulfide-xanthate system appeared promising for studying the fundamental mechanism of the adsorption of xanthate on the sulfide minerals. Although there are few cases where xanthates having an alkyl radical higher than hexyl are employed in practical operations, KDX was used in this study since it was reported that the adsorbability of xanthate on zinc sulfide was increased with an increasing number of carbon atoms of the alkyl radicals.4 EXPERIMENTAL Samples: Experiments were made on artificial zinc sulfide and natural sphalerite. The artificial zinc sulfide was obtained commercially from Dainihon Toryo Co. as a fluorescent pigment of the purest grade A. Considering the fact that there are often cases where the surface of sulfide minerals are apt to be oxidized so that the adsorption of xanthate at sulfide mineral/solution interfaces may be substantially affected, two different procedures were employed in preparing the samples of the artificial zinc sulfide. 1) The zinc sulfide was washed with hot concentrated ammonium chloride solution (300 g per liter) to remove surface oxidation products and followed by washing with deoxygenated hot distilled water by centrifugation until the constant electric conductivity of the solution was reached (Sample I) (specific conductivity of the solution = 8.6 x l0-5 ohm-' cm-'). 2) Sample I in a suspension of 5% by weight was oxidized with a 1.5% aqueous hydrogen peroxide solution for about one hour, and then was washed with distilled water as mentioned in the preparation of Sample I (Sample 11) (specific conductivity of the solution = 1.0 x 10"4 ohm-' cm-'). Both Samples I and II were dried under vacuum and stored in a vacuum desiccator. The specific surface areas of the samples determined by the BET method using carbon dioxide gas were 19 x l04 cm2 per g for Sample I and 35 x l04 cm2 per g for Sample 11. In addition, a sample which was derived from Sample I was also prepared. In 40 ml of 3 x 10-2 M zinc sulfate solution was placed 2 g of Sample I for 2 hours, washed with distilled water by successive centrifugation until no sulfate ion could be detected and dried under vacuum (Sample 111). The purpose of this treatment will be described later. Natural sphalerite was carefully selected by hand, ground in a mechanical agate mortar for about 40

Jan 1, 1965

By P. Chiotti, J. T. Mason

Metallographic, thermal, X-ray, and vapor-pressure data were employed in establishing the Ce-Zn phase diagram. Nine compounds and three eutectics were observed. The eutectic compositions in weight percent zinc and temperatures are 10 pct and 495"C, 37 pct and 795°C, and 56 pct and 810°C. Three of the compounds, CeZn, CeZnn, and CeZne.5, melt congru-ently at 825°, 87.505°, and 980°C, respectively; the other six compounds, CeZns, CeZns.67, CeZn4.5, CeZn5.25, CeZn,, and CeZnll, decompose peritectically at 820°, 840°, 870°, 885", 960°, and 795"C, respectively. The compound CeZn5.25 is an AB5 type with a small range of composition which lies on the zinc-rich side of the 1 to 5 stoichiometry. Zinc vapor-pressure data obtained by the dewpoint method were employed in calczilating the thermodynamic properties of both the liquid alloys and solid compounds. The data for the A critical review of the information available on the Ce-Zn system up to 1960 has been given by K. Gschneidner, Jr.' Of particular interest is the work by J. schramm2 who investigated the region between 55 and 100 wt pct Zn and reported a CeZn,, compound which decomposes peritectically at 785"C, a CeZn, compound which melts congruently at 972"C, and five temperature horizontals at 79@, 817", 840", liquid alloys were fitted to the relation from which the relation was obtained by integration. In these relations F XS is the excess partial molal free energy, N is atom fraction, and the constants c and d have the values c = (-22,000 + 7.0T) and d = 6171,000 + 74.0T). Relations for the standard free energy of formation for the solid compounds were derived from the data. At 973°K the enthalpy in kilocalories per gram-atom z)aries from —11.3 for CeZnz to —8.21 for CeZn~l and the free energy in the same units varies from —7.1 joy CeZn, to -3.82 for CeZn11. and 942°C in the region between 55 and 75 wt pct Zn. No attempt was made to identify other features of the system. I. Johnson and R. yonko3 used a fused-salt cell to measure the electromotive force between pure cerium and an alloy consisting of zinc-rich liquid in equilibrium with CeZnll. Solubility data for cerium in zinc has been reported by J. Knighton et u1 .4 Johnson and Yonko give the following equa-. tions for the mole fraction of cerium in zinc and the standard free energy of formation of CeZnll:

Jan 1, 1965

By R. J. Reynik, F. R. Meeks

IN the classical paper1 of Mehl and Rhines entitled "The Rates of Diffusion in the Alpha Solid Solutions of Copper", the authors state: "It has been mathematically demonstrated that the treatment of the data as though the diffusion were taking place between two flat plates instead of radially in a cylinder has no appreciable effect upon the results. Were the bars of a much smaller diameter, a modification of the analytical treatment would have been required." Unfortunately, the errors in the reported concentrations are much too large to neglect, as shown in the results below. A planar treatment of diffusion data assumes that the reference planes separated by a nominal distance (AX) have identical areas. An adjustment must be made on the concentration data should the successive diffusion planes differ in area. The Mehl-Rhines' diffusion samples were cylindrical with copper electroplated onto copper-based alloys. Successive surface areas through which diffusion occurs are in the ratio ri/r1, where ri is the radial distance between the center of the sample and the center of the i th shell to which the host (alloy) atoms diffuse, and r1 is the radial distance between the center of the sample and the center of the innermost (i = 1) experimentally reported shell from which the alloy atoms diffuse. Hence, ri/r1 (i = 1, ..., n layers) is a dimensionless correction factor to be multiplied by the reported concentration data before planar-data analysis is attempted. In the forty-seven samples reported, the original interface between the copper alloys and the electroplated copper was located at a mean distance of 8.255 mm from the center of the samples. The successive layers, machined off the samples, were approximately 0.0762 mm thick. The distance (xi) at which concentration (ci) was reported was always a distance measured with respect to the original interface, that is, with respect to the fixed distance of 8.255 mm. Hence, the as yet undiscovered Kirkendall Effect was precompensated. The values of ri and r1 are therefore given by ri = 8.255 + xi and Y, = 8.255 + x,. The illustrative table below lists the position xi (mm), ri (mm), the value of ri/r1, the reported concentration (ci) in weight percent (only valid for radial analysis of data), and the corrected concentration [c'i = (ri/r1)ci] in weight percent (only valid for planar analysis of data). Similar tables can be constructed for the remaining forty-six samples. The corrected data can be used to re-evaluate the diffusion coefficients for the reported systems.

Jan 1, 1965

By L. V. Gregor, C. F. Aliotta, P. Balk

The structure of silicon surfaces, thermally oxi&zed in dry oxygen and in steam, was studied using the electron microscope. It was found that the structure on the original (etched) surface is retained at the outer surface of the oxide, whereas the oxide-silicon interface is smoothed out considerably. This supports the idea that, both in oxygen and in steam, the oxidation reaction occurs at the oxide-silicon interface. Mechanical damage of the original silicon surface affects the rate of oxidation. It also changes the chemical properties of the oxide, as shown by the enhanced rate of etching in buffered HF at the locations of damage. However, the oxide at the originally damaged surfaces still exhibits a high electrical breakdown strength. Exposure of thermal oxides to P205 or BzOs vapor, which will yieldphospho- or borosilicate layers, results in complete annihilation of all fine structure on the surface. Reaction of silicon with C02 gives a surface film which probably does not consist of pure SiO,. THERMAL oxidation of silicon yields uniform and strongly adhering oxide films which are normally amorphous and continuous. Contamination and surface imperfections have been reported to cause local crystallization and the formation of pinholes."' The parabolic-rate law of film growth observed by several workers for the oxidation both in steam and in dry oxygen at higher temperatures suggests that diffusion of one or more reactants through the oxide is the rate-deter mining step. One of the dif-fusants is an oxygen species and oxide is continuously formed at the oxide-silicon interface. This was concluded for high-pressure steam oxidation by Ligenza and spitzer5 from an infrared-absorption study of the isotopic exchange of oxygen. Jorgensen arrived at the same conclusion for the oxidation in dry oxygen by measuring during oxidation the resistance change between silicon and a porous platinum marker electrode in the oxide. Recently, Pliskin and Gnall' reported similar conclusions concerning the growth mechanism from controlled etch studies using a phosphosilicate marker. The work communicated in the present paper was aimed at studying oxide growth on locally damaged silicon substrates and relating it to the chemical behavior and electrical breakdown properties of the films. Since etched and oxidized silicon surfaces normally appear to be very smooth when examined by optical microscopy except for some occasional pits, it was decided to use the electron microscope as a tool. In this way, the detection of surface roughness and damage on a scale comparable to or smaller than the thickness of the film is possible. Also, the microstructure of the original substrate surface constitutes a built-in marker which represents a minimum of perturbation to the growing oxide layer, and no foreign material is introduced. Thus information on surface reactions and additional evidence on the location of oxide formation in steam and in oxygen could be obtained. EXPERIMENTAL Electron micrographs7 were obtained using a Philips EM100 electron microscope. Collodion surface replication was used since this is a nondestructive technique and thus permits replicating the same surface at different stages of processing. In order to establish the effect of different treatments it was found essential to make successive observations of the same area by using a reference point. Reference points were conveniently provided by scribing a small v mark on the original surface with a silicon carbide tip. This procedure yields damaged and damage-free areas near the reference point. Upon replication, the samples were thoroughly cleaned before subjecting them to the next process step. Mechanically lapped silicon wafers (Dow-Corning, 100 ohm-cm p-type, cut perpendicular to the (111) direction) were chemically polished in a rotating beaker with a mixture of 1 part HF (48 pct), 2 parts glacial acetic acid, and 3 parts HNO3 (70 pct) by volume. This procedure yields a smooth surface with a faint "orange peel'' structure due to a "ripple" less than 20002i deep. Oxidation in steam or oxygen was carried out in an Electroglas tube furnace. Steam oxidations were always preceded and followed by a brief exposure to oxygen at the same temperattre. The thicknesses of the oxide films under 3000A were determined with a Rudolph Model 436-2003 ellipsometer,' whereas those over 3000A were measured using the VAMFO technique. In the present study, a solution of 300 g of N&F in 25 ml HF (48 pct) and 450 ml water was used to detect areas of increased chemical reactivity in the

Jan 1, 1965

By James C. M. Li

The thermodynamics of the set of functions including the activation enthalpy. the activation free energy, and the activation entropy for the motion of dislocations at low temperatures is formulated without a specific model or a mechanism. The behniiior near absolute zero of all these functions and of other relevant quantities related to dislocation mobility Is examined in the light of the third law of thermodynamics. The velocity measurements of Stein and Low for edge dislocations in Si-Fe are used .for illustrotion. In the plastic deformation of crystalline materials, a fundamental assumption, which is supported by direct measurements using etch-pit techniques,'-4 is that the average velocity of a certain mobile dislocation is a single-valued function of temperature and the effective shear stress exerted on the mobile dislocation: Sometimes under certain assumptions, even without direct dislocation-velocity measurements, an activation volume can be obtained from a change in strain rate in a simple tension test. Similarly an ac tivation enthalpy can be obtained by changing the temperature in a creep test. However, the assumptions involved should be studied carefully before using the results of these tests. Consider, for example, a tensile specimen at some stage of deformation with a distribution of mobile dislocations. Let the total length of dislocations of type i be pi per unit volume. The Burgers vector of these dislocations is hi which makes an angle ?i with the tensile axis. With respect to the same tensile axis, let the normal of the slip plane of these dislocations

Jan 1, 1965

By Donald B. Evans, Robert D. Pehlke

The solubility of nilrogen in liquid binary alloys of iron with Litanium. zivconium, columbium, vanndiurn, and tantalum was measured for alloy composiLions up to the solalbility limils of lhe alloy nitrides. All five alloying agents were found to decrease markedly the activity coefficient of nitrogen in liquid ivon. The metal/nitvogen mole ralios in the alloy nitrides formed were generally .found to be slighlly greater than 1.0, but in no case greater than 1.5. From the experimental data, the standard free energies of fortmation of titanium and zir-conium nitrides have been calculated for the Lemperaluve range 1550° to 1750 C. The solublily Products for columbium, tantalum, and vanadium nitrides are also reported. A number of research investigations have examined the effect of refractory metals on the solubility of nitrogen in liquid iron. Although data on zirconium are not available, investigators are in agreement that titanium, vanadium, columbium, and tantalum markedly increase the solubility of nitrogen in liquid iron. This fact alone makes desirable the acquisition of thermodynamic data for these elements in liquid iron. Since refractory metals are known to be stable nitride formers, they have been suggested as steel denitrifying agents, and some of their nitrides have recently been considered as containment materials for liquid iron and iron alloys. Most available thermodynamic data for these metals relate to their dilute concentrations, but effective thermodynamic treatment of these applications requires data at concentrations near the solubility limit of the alloy nitride. Although some work has been done at relatively high alloy concentrations in liquid iron (particularly for vanadium 2,3 and titanium 2,4), the results have been somewhat contradictory. Disagreement may be partly attributed to the fact that the compositions of most refractory metal nitrides have been shown to be nonstoichiometric, and to vary 2,5-8 depending on the temperature and nitrogen gas pressure with which the solid nitride phase is in equilibrium. One purpose of this study consequently has been to determine the compositions of the refractory metal nitrides precipitated from a liquid iron solution. EXPERIMENTAL PROCEDURE Rao and Parlee2 and Evans and Pehlke 9 have discussed the technique for measuring the solubility product of an alloy nitride phase in liquid iron by finding the point of departure of the nitrogen solubility from Sieverts' law. The method consists of measuring the solubility of nitrogen in a melt of iron containing a known concentration of a second metal as a function of the nitrogen gas pressure over the melt. In this study the second metal was one of the refractory metals titanium, zirconium, columbium, vanadium, or tantalum. When the nitrogen pressure at which the refractory nitride forms is reached, a deviation of the measured solubility of nitrogen in the melt from Sieverts' law is observed in the form of a "pressure halt." The concentration of nitrogen in the melt associated with this breakpoint in the nitrogen-absorption curve is then used to calculate the nitride solubility. The Sieverts method was used to measure nitrogen solubility as a function of nitrogen pressure and temperature. The experimental equipment for this technique has been previously described in detail. 1,9 Charge materials used were vacuum-melted high-purity iron (Ferrovac-E) and the best commercial grades of the refractory metals obtainable (in all cases at least 99.8+ pct pure). Recrystallized alumina crucibles were used to hold all melts except those containing zirconium, for which zirconia crucibles were necessary. Temperatures were measured by a disappearing-filament type optical pyrometer sighted vertically downward on the melt surface through a 1/4-in.-diameter sight hole in the crucible lid. By means of a technique previously described, 9 in which the refractory-metal nitride was precipitated at one temperature then redis-solved by raising the temperature 50°C and precipitated again at a higher temperature, it was possible to obtain data over a temperature range of up to 200°C on a single melt. It was found that this technique could not be used with melts containing zir-

Jan 1, 1965

By W. I. Duvall

A brief review of the resonant frequency and ultrasonic pulse methods for obtaining elastic constants of rock samples shows that the equations for an iso-tropic elastic solid commonly used to calculate Young's modulus, modulus of rigidity and Poisson's ratio can result in appreciable error if the rock is even slightly anisotropic. Consideration of the equations that relate bar velocities and free medium velocities to elastic constants for orthotropic, transversely isotropic and isotropic solids shows that a combination of the two methods can be used to determine average elastic constants for a single sample of rock. The determination of elastic constants in different directions requires a large number of tests on oriented samples. The use of both the resonant frequency and ultrasonic pulse methods is recommended so that the determination of both Young's modulus and modulus of rigidity is independent of the determination of Poisson's ratio. The dynamic elastic constants of rock can be determined in the laboratory from measurements on small samples which may be in the form of right circular cylinders (diamond drill core). Either the resonant frequency6 or ultrasonic pulse method1 can be used to determine the longitudinal and shear velocities in the same specimen. The resonant frequency method provides a measure of the longitudinal bar velocity, V,, and the torsional bar velocity Vt; whereas the ultrasonic pulse method provides a measure of the free medium longitudinal velocity, Vp, and the free medium shear velocity, V, . The elastic constants (Young's modulus E, modulus of rigidity G, and Poisson's ratio v) are calculated from the density of the specimen, p, and one of the pairs of velocities by means of equations from isotropic elastic theory. For the resonant frequency method the equations are: It should be noted that Eq. 5 is derived from Eq. 4 and 6 and the relation between the elastic constants for an isotropic solid as given by the first part of Eq. 3. The in situ determination of dynamic elastic constants is accomplished by generating a complex seismic pulse in the rock and measuring the arrival times for the longitudinal and shear phases of the pulse at two distant points.5 From these travel times and the distance of the travel path both Vp and Vs are determined. The density of the rock is determined from samples in the laboratory, and Eq. 4 to 6 are used to calculate the elastic constants. These three methods involve the assumption of isotropy and perfect elasticity, and require the use of the relation v = (E/2G) - 1, which holds only if the elastic constants are the same in at least two directions. The calculation of v by means of Eq. 3 introduces considerable error, as a 1% error in V, and V, results in a 20% error in v. If frequencies for samples with a length-to-diameter ratio greater than four and a length greater than 8 in. are measured carefully, the experimental error can be kept to 1%. However, it is not unreasonable to expect that the variation in Vb and Vt with direction may exceed 1%. Thus, for even a small percentage of anisotropy the use of Eq. 3 can result in considerable error in v. The calculation of v by Eq. 5 also involves some uncertainty as a 1% error in Vs and Vp can result in a 6% error in v. By means of the pulse method both

Jan 1, 1965

By L. A. Rapport, J. R. McCord, W. P. Drews, K. H. Coats

Water movement about an oil or gas reservoir can be predicted provided an aquifer influence function is known. This function is generally determined from an electric analyzer study or by fitting an idealized mathematical model to field data. A prohlem arises in determining that influence function which best reproduces field data and satisfies certain smoothness requirements, without making any idealizations concerning aquifer geometry and heterogeneity. This study shows the problem to be solvable through the linear programming technique and presents applications to one oil reservoir and two gas storage reservoirs. In addition, a theorem is stated and proven which confirms influence junction smoothness requirements heretofore accepted on physical intuition and establishes additiotzal smoothness constraints formerly not recognized. INTRODUCTION The pressure decline accompanying production results in water encroachment into oil and gas reservoirs situated adjacent to aquifers. The importance of this water movement derives from the significant dependence of production rate upon reservoir pressure and of pressure, in turn, upon water encroachment. Pressure and rate of water movement are uniquely related through an "influence" function which may be in the form of reservoir pressure response to a unit water encroachment rate or of water movement caused by a unit reservoir pressure drop. This influence function reflects the heterogeneity and geometry of the aquifer and is therefore particular to each reservoir. If the influence function is known, then reservoir pressure may be predicted from a production rate schedule, or vice-versa, with the aid of the material balance equation which relates water influx to reservoir production and pressure. The problem of determining this influence function for a given reservoir has been approached in three different ways. Van Everdingen and Hurst calculated and tabulated certain influence functions pertinent to idealized mathematical models which satisfy simplifying assumptions such as aquifer homogeneity and elementary reservoir-aquifer geometries.' Other studies developed additional tables for a variety of elementary reservoir-aquifer geometrical con- figurations and demonstrated their validity and utility.:' Hicks, et al. described the use of an electrical network to determine an influence function giving "best" match of field history and allowing prediction of future performance.' Finally, Hutchinson and Sikora5 and Katz, Tek and Jones attempted to develop a calculation method for deriving the influence function directly from field data with no idealizing assumptions concerning aquifer geometry and homogeneity. They encountered difficulties with inaccuracies in field data and with satisfaction of well-known smoothness requirements of the influence function. This study is concerned with the determination of influence functions from field data and, more specifically, treats the following problem: given field pressure-production data of arbitrary accuracy, how does one determine the influence function which, subject to satisfaction of known smoothness requirements, gives best agreement with field history? A rigorous solution to this problem is ohtained through linear programming as described below. Example applications to one oil and two gas storage reservoirs are presented. In addition, a theorem is proved which confirms influence function smoothness requirements heretofore accepted on physical intuition and establishes additional smoothness requirements formerly not recognized.

Jan 1, 1965

By D. H. Baldwin, R. E. Reed-Hill

WITH the polarized-light microscope, the basal-plane trace may be located on hcp crystal surfaces to an accuracy of approximately 1 deg. This determination can also be made on very small crystalline areas, approaching a micron in width. Measured basal-plane trace distributions on selected specimen surfaces can yield1,2 valuable texture information. However, the polarized-light microscope is probably best suited to orienting

Jan 1, 1965

By G. W. Powell

ACCORDING to crank,' the accumulation equations for inter diffusion in a binary system whose molal volume is a function of concentration are

Jan 1, 1965

By Roshan B. Bhappu, Ronald J. Roman, Dexter H. Reynolds

The reaction between manganese dioxide and molybdenite in a water- sulfuric acid medium was studied at atmospheric pressure and from 25° to 103°C. Both solids are dissolved to give, as final products in solution, Mo(VI), S(VI), and Mn(II). Stoichiornetric relationshifis are most simply represented by the equation MoSz + YMnO2 + 15H+ - HMoO-4 + 2HSO-4 + 9Mn++ + 6H20 The rate of this reaction was found to be dependent on temperature, manganese sulfate concentration, acid concentration, and, in a complex way, the surface areas of both manganese dioxide and molybdenite. Both the total amount of manganese dioxide and tnolybdenite and the ratio of manganese dioxide to molybdenite played a part in determining the over-all rate of the reaction. The effect of acid concentration on the rate was also dependent on the ratio of manganese dioxide to molybdenite. SEVERAL reports in the literature describe reactions using manganese dioxide in water-sulfuric acid media as an oxidizing agent. Nearly all previous work describes interactions between an ion and manganese dioxide, such as the oxidation of ferrous to ferric iron,' or the interaction between a molecule in solution and manganese dioxide, such as the oxidation of toluene to benzaldehyde.2 Only a few references describe the use of solid manganese dioxide to oxidize another solid in sulfuric acid. One report3 states, "Manganese dioxide in dilute sulfuric acid solutions had no beneficial effect (in leaching copper from chalcopyrite), but in more concentrated acid solutions the rate of solution was about the same as that for permanganate." In 1902 a German patent4 described a process which used manganese dioxide in strong (50°Be') sulfuric acid for oxidizing chromite ores to soluble iron and chromium salts. The process consisted of mixing the sulfuric acid with the finely ground ore and manganese dioxide. The pulp was then heated to about 120°C and an electric current passed through it. The manganese dioxide apparently dissolved in the strong, hot acid solution, oxidized the iron and chromium and itself was reduced to manganese 11! then was oxidized at the anode back to manganese dioxide, and the cycle repeated. An extensive study5 of the kinetics of the oxidation of pyrite with manganese dioxide indicated that in dilute sulfuric acid solutions (about 0.1 N) and at elevated pressures the dissolution of the pyrite was brought about by air oxidation of the iron to ferrous sulfate, followed by manganese dioxide oxidation of the ferrous sulfate to ferric sulfate. The mechanism proposed by the authors involved the oxidation of the iron at the surface of the manganese dioxide. Also! the oxidation of sulfide sulfur to sulfate was credited to the oxygen in the air, not to the manganese dioxide. Since the metallurgical literature is lacking in information concerning the use of one solid to oxidize another solid. the current investigation was under-

Jan 1, 1965

By G. A. Alers, F. Borik

Rolled sheet products are elastically anisotropic and a large number of measurements of Young's modulus and rigidity modulus are necessary to completely specify their elastic properties. This paper describes and uses a simple measurement technique to obtain the nine elements of the elastic modulus tensor from which all the elastic The elastic properties of a polycrystalline material are usually specified by giving the Young's modulus E and the rigidity modulus G. Unfortunately, these two moduli by themselves are insufficient to completely specify the elastic properties because the rolling process introduces a preferred orientation which makes the material properties can be deduced. In particular, the variation of Young's modulus and the rigidity modulus in the principal planes of a sheet of ausformed steel were deduced. Furthermore, the variation of Young's modulus in the rolling plane was compared with direct measurements. anisotropic. This anisotropy makes E and G functions of the orientation of the test specimen in the sheet so that a complete description of the elasticity requires many measurements on a large number of specimens. A more fundamental approach to the problem is to consider the sheet as a single crystal and measure the elements of its elastic modulus tensor. Although this appears formidable, there have been developed recently high-frequency ultrasonic techniques which yield these tensor elements directly. The symmetry of a rolled sheet is such that it behaves elastically as if it were an orthorhombic

Jan 1, 1965

Jan 1, 1965

By Robert E. Green, Kenneth Reifsnider

A microscopic X-ray diffraction technique was employed for the simultaneous study of the behavior of several families of lattice planes, whose local orientatiotz changes are manufestations of internal distortions resulting from specimen deformation. Photographs taken using aluminum were single crystals 1/64 in. In diam are presented which illustrate the appearance of various types of deformation- or growth- induced structural variations. Slip and lattice bending were detected in tensile tests for strains as small as 0.1 pct. Evidence of deformation bands, lineage structure, and void formation wns also shown. AmONG the most important methods of studying internal stresses in metals is the utilization of various X-ray techniques. The general subject of X-ray metallography has been treated in a most excellent manner by Taylor,1 and the use of X-rays for the direct observation of imperfections in crystals has recently been reviewed in an article by Newkirk2 and in the book edited by Newkirk and Wernick.3 Since the inception of metallographic X-ray analysis, there have been numerous technological developments and refinements, each with its particular advantages and disadvantages and, acrording to these, its particular applications. X-ray diffraction techniques can be divided into two general categories, that of X-ray diffraction microscopy and that of X-ray diffraction macroscopy. In the former are included such methods as those of Berg-Barrett, Lang, and Schultz2,3 which are concerned with microscopic imperfections such as dislocations. The second category includes all work concerned with the study of the condition of a crystal lattice structure as indicated by the marroscopic detail in its diffraction patterns. An example of this is the study of the diffraction manifestations of inhomogeneous plastic deformation as manifested by formation of deformation bands and inhomogeneous lattice rotations. The method used in the present investigation was an X-ray diffraction macroscopy technique. The geometry and analytical aspects of the method were similar to those of Julien and Cullity.4,5 The source was collimated with a single slit in a manner simi- lar to the "parallel beam'' method of Barth and Hosemann6 except that a continuous spectrum of radiation was employed. The apparatus produced large-beam transmission Laue patterns of thin cylindrical aluminum-wire crystals, which were deformed either in tension or torsion. Although the conventional X-ray target and interposed slit were not capable of the high resolution obtainable with a fine-focus X-ray source as employed in a microfocus apparatus, resolution was a secondary consideration in our technique, and was sacrificed to obtain sufficient intensity along a sizable length of the specimen. By using a grid indexing technique similar to that of Barth,7 we were able to study several diffraction lines from various planes simultaneously. The results of these tests give additional information with regard to the inhomogeneous deformation of single crystals, and the indexing procedure used provides a correlation between portions of the test specimen and portions of a diffracted beam. EXPERIMENTAL TECHNIQUE The experimental arrangement used is shown schematically in Fig. 1. A source of continuous X radiation from a vertically mounted Machlett X-ray tube possessing a copper target and operated at 20 kv and 10 ma was passed down a horizontal lead tube 80 cm long which terminated in an adjustable vertical brass slit. The slit opening was adjusted to correspond with the diameter of the test specimen. In front of the brass slit it was possible to place a screen wire mesh, one horizontal strand of which was a lead wire which served as a fiduciary mark, the screen itself serving as an indexing system as will be described later. Behind the screen was the test specimen which consisted of an aluminum single crystal wire 1/64 in. in diameter and 3 in. long. These 3-in.-long crystals were cut from

Jan 1, 1965

By J. E. McDonald, J. G. Eberhart

A model is discussed from which the work of adhcslon .tor liquid transition metals on aluminum oxide surfaces can he calculated, A close-packed (00011 oxygen surface on A12O3 is assumed with two different types of surface sites: one type involving metal-oxygen bonds and the other man der Waals into actions. The work of adhesion is thus expressed as the sum of these two bonsding free energies. Calculated works of adhesion for nickel, titanium, chromium, and zirconium on sapphire agree well with the experimentally determined quantities. The model is extentled to the calculation of the work of adhesion and shear stress required to remove a thin metal film from a sapphire substrate and is in good agreement with experimental values. The obsewed dependence of the work of adhesion on the free energy of oxide formation of the metal is shown to also provide an interpretation of the tittle dependence of thin-film adhesion. THIS paper presents a model for the type of bonding which occurs across a metal-A12O3 interface. The model is used to explain the results of two types of experiments in which such an interface exists: 1) the adhesion of thin metal films on Al2O3 substrates and 2) the wetting of A12O3 by liquid metal drops. The adhesion of thin films to various substrates has been the subject of a variety of investigations.'-' Benjamin and weaver3 and Bowie,6 using the scratch test developed by Heavens,10 studied the adhesion of metallic films to glass substrates. Their observations for noble-metal film adhesion agree well with an adhesion model involving a van der Waals type of bonding between the film and the substrate. For films of metals whose free energy of oxide formation. ?F°f, has a negative value. Benjamin and weaver3 and Bowie6 found a time-dependent adhesion with an initial value that can be interpreted in terms of van der Waals interactions but a larger terminal value which was related to ?F°f, Karnow-sky and Estill7 deposited films on sapphire at elevated temperatures and noticed no time dependence of film adhesion but a similar correlation with ?F°f. Because of the kinetic problems associated with thin-film adhesion it is desirable to examine adhesion in an equilibrium system. The wetting behavior of liquid-metal drops on Al2O3 provides such a system. Systems of this metal-ceramic type have been studied extensively.11 Humenik and Kingeryl2 have measured the wetting of A12O3 (and other substrates) by several metals and have pointed out that the wetting ability of these metals increases with increasing values of -?F°f. It is thus seen that thin-film adhesion and metal wetting on A12O3 are both related to the tendency of the metal to react with the surface oxide ions of the Al2O3 substrate and, because of this, both phenomena should be explainable by an appropriate model for the metal-Al2O3 interfacial bonding. In the sections that follow, wetting and adhesion data on A2O3 are reviewed and a model is presented by which these phenomena can be interpreted. ANALYSIS OF WETTING EXPERIMENTS In an equilibrium system involving a liquid-metal drop on a solid Al2O3 substrate, the work of adhesion, WAD, is defined by the Dupre, equation as WAD = ?s + ?L -?sL [1] where ?s and ?L are the surface free energies of the solid substrate and the liquid drop, respectively, and ?sL is the interfacial free energy. The work of adhesion is the work required to separate a unit area of the solid-liquid interface into two surfaces. The work of adhesion is usually determined from a sessile-drop experiment in which yL and the contact angle, ?, are measured. The Young-Dupr6 equation is then used to calculate WAD Wad = ?L (1+ cos ?) [2] The literature of this subject has been examined and Table I shows work of adhesion data for various liquid metals as measured on A12O3 substrates. The standard free energy of oxide formation of the metal at the temperature of the wetting experiment, ?F°f . is also tabulated in kcal per g-atom of oxygen. The data is grouped according to the gaseous atmos-

Jan 1, 1965

By R. Grierson, R. N. Parkins

The m.echanica1 properties, at high lzomologous temperatures, of the intermetallic compounds InzBi and Mg17A112 were measured as a .function of temperature, applied strain rate, previous thermal and mechanical history, and composition. Mgl,Al12 was investigated ilz compression, whereas Zn,Bi was investigated in tension. A decrease inflow stress with increasing strain was observed jor both alloys. The results obtained are discussed in terms of the dislocation-multiplication processes in these materials. MANY intermetallic compounds are reported to undergo a brittle-ductile transition at high homologous temperatures.' There is evidence in the literature that some of these compounds exhibit a large yield drop when plastically deformed.'j3 Both of these forms of behavior are shown by the covalent elements germanium and silicon4,5 and also by certain ionic compounds.8 The present work is a study of the deformation, at high homologous temperatures (>2/3 Tm), of two intermetallic compounds, In2Bi and Mg17Al12. InzBi has a disordered hexagonal structure7 (c/a = 0.598) and a solubility range of 32.3 — 33.2 at. pct Bi.8 It has a melting range from 72° to 89°C. Mg17Al12 has an ordered bcc (A12 type)7 structure and exists over the range 50 to 60 at. pct Mg8 with a melting range from 437° to 462°C. We have been unable to find any reference to previous investigations of the mechanical properties of BiIn,. Novikovg has reported that cast samples of Mg17A112 show ductility, when bend-tested, at temperatures above 380°C. EXPERIMENTAL Ingots of In2Bi and Mg17Al12 were melted under an argon atmosphere and cast, in situ, in a graphite crucible. The materials used were of 99.99 pct purity. The alloys prepared contained 66.9 at. pct In in the case of In2Bi and 58.4 at. pct Mg in the case of m17A112. The ingots were homogenized and then extruded. Two-in.-diam Mg17Al12 ingots were extruded at 375°C to give 3/8-in.-diam rod. The rate of formation of this rod was 0.25 in. per min. One-in.-diam InzBi ingots were extruded at 20°C, using a rate of 1 in. per min, to give 1/8-in.-diam rod. In both cases the extruded rod had a recrystal- lized, fine-grain, structure. (For Mg17Al12, d = 11.2 µ; for BiIn2, d = 22 µ.) Mechanical-property determinations were made in a hard-beam machine, in tension in the case of In2Bi and in compression with Mgl7Al12. The tensile tests were on specimens having a gage length of 1.1/2 in. and a diameter of 1/8 in. The compression tests on Ml7A112 were on specimens of 3/8 in. diam by 3/8 in. high and the ends were coated with poly-tetrafluorethylene to minimize friction. RESULTS In2Bi. Fig. 1 shows, particularly at the higher applied strain rates, that In2Bi exhibits a marked yield drop as the deformation increases to about 2 pct, after which the material shows neither hardening nor softening up to 15 pct strain. The magnitude of the yield drop, the stress in the region of flow under constant stress (the stress plateau), and the 0.5 pct proof stress were all dependent upon the applied strain rate according to an expression of the form

Jan 1, 1965

By K. N. Weaver

In the early 1950's the cement industry began putting a new emphasis on geology. This article points up some of the industry's raw materials problems that geologists are uniquely qualified to handle. Portland cement can be made from relatively abundant industrial minerals and rocks, and this may explain why cement producers placed little emphasis on geology during the early days of the industry. After World War 11, however, the industry began to recognize the need for geological exploration and some of the larger companies began to build a permanent geological staff. This development has its roots in: 1) The rapid expansion of the industry. After World War II and continuing into the early 1950's the demand for cement far exceeded the production capacity. This placed a great deal of pressure on the producers to enlarge capacity at their plants and to develop new sites. 2) The closing of many cement plants due to inadequate raw materials. Producers feared lack of raw materials due to inadequate exploration and evaluation. 3) An ever increasing pressure for upgrading of the quality of portland cement, necessitated upgrading the quality of raw materials. 4) The increasingly large capital investment needed to build new cement plants required a higher degree of accuracy in reserve calculation. These reasons are more or less self explanatory and will not be elaborated on. They are outlined to illustrate the probable evolution of thought among cement management to justify the development of a geological staff. In the author's personal experience the geologist must continually readjust to changing conditions within the industry. For example, cement production capacity grew so rapidly that today production is only about 70% to 75% of rated capacity (73.8% in 1963). Therefore, whereas the geologist's function during the active expansion of capacity was primarily one of exploration, one of his major functions today is the development of existing reserves. This assumes of course that reserves at existing plants have been proven to be adequate in terms of the company's reserve policy. Through the proper development of raw materials, the geologist can markedly influence quality control, production and long range planning. Examples of several of the operations of Medusa Portland Cement Co. will illustrate how proper attention to geologic detail pays off in the above areas. Because limestone is the major raw material of port-land cement, the examples will be concerned with it. DEVELOPMENT OF GEOLOGIC DETAIL One of the prime objectives of an exploration or development project should be the establishment of the stratigraphy and structure of the deposit. The basic tool for exploration and development is still the core drill, and the geologist must gain a maximum amount of information from a minimum amount of drilling. In order to obtain this objective the following is essential: 1) Adequate detailed geologic logging of cores. The core is first logged and separated into lithologically distinct units. In order to make the lithologic breaks as meaningful as possible, representative pieces of core (not all) are etched in dilute HCI. This removes the "drill polish", brings out the structure of the rock and indicates the proportion of dolomite and argillaceous material because dolomite and argillaceous material etch in relief. In this way the lithologic breaks become clearer and one gains a general idea of the chemical makeup before analysis. This method of logging lessens the probability of including two types of stone, e.g. limestone and dolomite into the same sample for chemical analysis. 2) Representative sampling for chemical analysis. After logging, the lithologic units are sampled for chemical analysis. A representative analysis can be obtained by extracting a 1-in. sample for every foot of core. For example, a lithologic interval of 10 ft to 20 ft would yield ten 1-in. samples taken at 11 ft, 12 ft, 13 ft... and 20 ft. These samples are then crushed, pulverized and split into a sample for chemical analysis. This sampling method represents a significant saving of time over splitting the entire core. 3) Preparing the core as a record. Because of the expense of storage and the difficulty of handling large amounts of core, only representative samples of each lithologic unit are saved for reference. An

Jan 1, 1965

By S. Leber

Pole figures and pole distributions were used for the quantitative detevinination of the preferred orientations in swaged tungsten rods and the effect of subsequent wire drawing on the texture. In the swaged rod, the preferred orientation could best be described as a pseudo (111-112) [110] cylindrical texture. A secondary component was assigned the indices (110) [001]. Further reduction by swaging retained these cylindrical textures. Wire drawing caused lattice rotations about the wire axis, converting the cylindrical texture into a normal fiber texture. The conversion was initiated and proceeded lnost rapidly in the center of the wire. The (110) /001] component was converted into a (110) fiber texture by wire drawing. The effective rotations were about axes contained in the lransverse plane. The preferred orientation associated with tungsten wire usually has been assumed to consist of a (110) fiber texture. This implies rotational randomness around the wire axis. Leber1 has shown that rotation about the wire axis may be restricted resulting in a preferred orientation designated as a cylindrical texture. Specific crystal planes tended to remain aligned parallel to the wire surface. This texture seemed to be the result of the swaging operation used in the intermediate stages of fabrication. Bhandary and cullity2 detected similar textures in swaged iron wires. Peck and Thomas3 suggested that the preferential alignment of crystal planes parallel to the wire surface was the result of tangential flow, characteristic of swaging. Wire drawing, following swaging, twisted the crystals about axes parallel to the wire axis, converting the cylindrical texture into a normal fiber texture.4 In this investigation, quantitative techniques were used to more accurately characterize the cylindrical texture and to study its conversion into a normal fiber texture. PROCEDURE The material investigated was lamp-quality tungsten. Three ingots were rod-rolled and swaged to 112 mils diameter, and were then drawn to 10-mil wire. Samples were obtained after each drawing pass. (110) and (200) pole figures were obtained from samples prepared as shown in Fig. 1. To form the sample shown in Fig. l(a), l-in. lengths of wire were glued side by side to form a l-in. square. The composite was ground and electropolished to form a diametral reference surface. For certain specific tests, samples were prepared as shown in Fig. l(b). This composite was made from 10-mil-thick strips prepared by grinding on parallel longitudinal planes. The polished reference surface in this case was, in essence, the wire surface. The two forms of samples [~igs. l(a) and l(b)] were related by a 90-deg rotation around the wire axis. Because of ease in preparation, most data was obtained from the diametral samples. The X-ray data were obtained using a Siemen's pole-figure goniometer. These data were not corrected for absorption or defocusing effects, since only the angular locations of the intensity maxima were of interest. Regions of the pole figure more than 80 deg from the center were not investigated. Partial monochromatization was achieved by the use of unfiltered copper radiation and a krypton-filled proportional counter. No evidence of spurious white radiation effects5 could be detected. Therefore, more elaborate X-ray techniques were not required. Intensity levels were chosen to show all pertinent details of the orientation distributions. The reference plane for the pole figures was the diametral section. The orthogonal reference directions, shown in Fig. 1, were the wire axis, the radial axis per-

Jan 1, 1965

By F. M. Smith, R. H. Moore, J. R. Morrey

Electrodiffusion in y cerium reported by Henrie has been confirmed and a Preliminary estimate made of the relative rates of electrodiffusion of iron, cobalt, and nickel. These diffuse to the anode at rates decreasing in that order. In addition, copper and manganese exhibit slow, but detectable, diffusion to the anode and molybdenum exhibits detectable diffusion to the cathode. The electrodiffusion of carbon, .zirconium, antimony, magnesium , and silicon in y cerium could not be detected. Iron and cobalt diffuse in y cerium at rates proportional to the current density and with no apparent dependence on temperature. Decreasing polarization of iron and cobalt with increasing temperature, which cancels the expected rate increase, would account for this behavior. The electrodiffusion rate of iron in y uranium and in E plutonium has been measured. Diffusion of iron is anode-directed. Tin was found to diffuse to the cathode, in y uranium, at an appreciable rate. In all of these solvent metals, negative ions diffuse to the anode and positive ions to the cathode. The potential field effect appears to account satisfactorily for these results. FROM early experimental work summarized by Jost1 and Seith,2 the driving force for electrodiffusion was attributed to the potential field acting on ions in a metal. More recently, Heuman,3 Wever,4 and Huntington5 have shown that momentum interchange between conduction electrons and mobile entities in the metal contributes to electrodiffusion. Electron momentum interchange is anodically directed and the direction of diffusion resulting from the field force is dependent upon the charge on the diffusing entity. These two effects may either reinforce or oppose each other. Glinchuk6 has pointed out that momentum transfer in defect conductors should be cathode-directed and this appears to be the case as demonstrated by wever's4 work on iron. Barnett's7 work, on the other hand, indicates that, even in defect conductors, electrons show a negative E/m ratio when accelerated with respect to the lattice and should lead to anode-directed momentum transfer. In discussing this problem, Wever and seith8 suggest that defect electrons interact preferentially with activated ions so as to allow a net movement toward the cathode while still maintaining an electron momentum transfer in the anode direction. Williams and Huffine9 and Henriel0 have demonstrated that electrodiffusion may be useful for purification of yttrium and cerium. In yttrium, Williams and Huffine note that movement of several metallic impurities toward the anode is in keeping with observations in most other metallic systems and indicates that yttrium remains a normal electronic conductor at least to 1230°C. Close inspection of their data shows, however, that oxygen, nitrogen, and the transition elements diffused toward the anode, while nontransition elements diffused toward the cathode. This suggests that potential field effects may have been appreciable. The present work was concerned with the applicability of electrodiffusion as a technique for purification of plutonium, but, because of the obvious hazard inherent in work with this metal, experiments to develop the technique were carried out using cerium and uranium. The results of electrodiffusion measurements on these metals and on plutonium are reported here. EXPERIMENTAL The metal specimens prepared for this work were 6 in. long, 1/4 to 1/2 in. wide, and 1/16 to 3/32 in. thick. The uranium specimens were machined from a bar which analyzed 310 ppm Fe and the electrodiffusion of iron was followed by spectrographic and by chemical analysis. Cerium and plutonium specimens were cut from sheet rolled from ingots obtained from molten salt-metal equilibrations during which radioactive tracers were introduced. The electrodiffusion of the tracers was subsequently determined by counting methods. The specimens were electrolyzed between nickel electrodes containing resistance heaters used to equalize the specimen and electrode temperatures, thereby reducing thermal gradients. The temperature of the electrodes adjacent to the ends of the specimen was measured with chromel-alumel thermocouples which were connected to the heater controls. The surface temperature of the specimen at a point midway between the electrodes was measured with a sapphire rod pyrometer, the output of which controlled the dc power supply. This assembly was enclosed within an evacuable chamber containing a quartz viewing window. The temperature of the specimen over its entire length could be scanned with a portable pyrometer through

Jan 1, 1965