Jan 1, 1965

By Gilbert L. Eggert

The effects of reactor irradiation on age hardening in a Cu-2 wt pct Be alloy have been investigated in two neutron-energy ranges. During some of the irradiations, specimens were exposed to high-energy fission neutrons which passed through a boron-10 shield; during other bombardments, the boron-10 was omitted and specimens were irradiated in a reactor thermal column, or the fuel configuration was modified to increase the thermal-neutron flux at a location in the core. Differences in length, X-ray diffraction angle, and hardness indicated that low-energy neutron irradiation made a small contribution to changes in the measured properties. The influence of defects generated by knock-om with less than the Brinkman critical energy or by prompt (n,y) recoil is suggested as the cause of this effect. EXPERIMENTS designed to test the effects of reactor irradiation on the properties of age-hardening alloys have to the present time employed fluxes un-differentiated according to neutron energy. Billing-ton and Siegell in 1950 were the first to perform such an experiment and to compare the results with those obtained by thermal aging. These authors concluded that precipitation in a Cu-2 wt pct Be alloy was not enhanced by the radiation. However, 4 years later, Murray and Taylor,2 working with specimens of the same Cu-2 wt pct Be alloy, reported that an increase in density, hardness, and resistivity which followed reactor irradiation resembled changes associated with thermal aging at about 100°C. (It should be noted that these authors reported that higher aging temperatures caused a decrease in resistivity.) cupp3 reported hardness results similar to those of Murray and Taylor. Koppenaal4 showed that irradiation-enhanced precipitation and irradiation defect hardening were not simply additive but that they acted separately in an irradiated alloy. Kernohan et a1.,5 working with Ni-Be, offered evidence that beryllium was removed from solid solution by reactor irradiation and suggested that the mechanism was one of increased diffusion through the use of vacancies in the structure. piercy6 also found that more precipitate particles were formed by fission-neutron irradiation of a Cu-Co alloy which contained a small amount of particles before irradiation. He proposed that the additional particles were caused by an appreciable amount of diffusion during the final cooling of displacement spikes. The retrogression of extant precipitate particles found by Murray and Taylor2 and Boltax7 as well as piercy6 indicated that nuclei were dissolved within a high-energy spike region and, upon resolidification of the perturbed volume, new nuclei precipitate and grow by enhanced diffusion. Bleiberg et al.' and Konobeevski et al.' explained phase changes obtained by irradiating fissionable alloys in terms of retrogression and re-precipitation in regions of high-energy spikes. Parsons and Balluffi10 used electron microscopy to verify that crystallization did indeed occur in displacement spikes which were formed in amorphous germanium by fast-neutron irradiation. The concept that low-energy neutron irradiation might cause structure-sensitive property changes in semiconductors by atomic recoil associated with the (n, y) reaction was first proposed by Schweinler" and walker." This thesis was tested by Cleland and crawford" and found to be valid. Coltman et al.14 exposed a variety of pure metals to thermal-neutron irradiation at cryogenic temperatures and attributed the resulting resistivity changes to the action of defects created by (n, y) recoil. The present work was undertaken to extend the concepts of Schweinler," walker," and Coltman et al.I4 to the case of an age-hardening alloy and to determine whether or not the action of defects produced by thermal-neutron irradiation would en-hance age hardening. EXPERIMENTAL PROCEDURE Omeea West Reactor Irradiations.* Thermal-

Jan 1, 1965

By E. M. Boatman, S. J. Pirson, R. L. Nettle

More than a decade ago some theoretically derived relationships were proposed that permitted the prediction of the relative ability of reservoir fluids (oil, gas, water) to flow simultaneously within the porous structure of rocks. While many successful predictions of fluid-flow ratios from wells have been made from electric logs, the theoretical deductions have not been subjected to laboratory verifications. For the relative permeability to liquid and gas, simultaneous flow of water and air was used, employing the familiar external-gas-drive technique. While in the process or water desaturation, the resistivities of the test cores (Woodbine sand) were measured. Their permeabilities varied from 10 to 280 md. The laboratory results indicated the need for changing the values of exponents in the theoretically derived formulas, whereas the form of the functions of resistivities and saturations remained as derived by theory. For the relative permeability to oil and water, the three-core dynamic technique was used on six cores. In this case it was found that the formulas were valid with but slight modification as derived by theory, to a sufficient degree of accuracy for engineering use and for well productivity prediction from electric logs. INTRODUCTION Conventional quantitative well log interpretation generally stops after reasonable values for formation porosities and water saturations have been established. Yet such in formation is insufficient to predict either the outcome or the desirability of well tests and completion, let alone the economic aspect of producing oil- and gas-bearing sections which might have been established by conventional log analysis. To give an engineering answer to such questions, it is necessary to predict the expected fluid flow ratios, the productivity index and the ultimate recovery from potentially productive wells. This problem requires in part for its solution a determination of the relative permeability characteristics of the potentially producing formations, both to oil (or water) and gas, and to oil and water.

Jan 1, 1965

By V. Koump, T. F. Perzak, R. G. Olsson

Jan 1, 1965

By D. L. McDanels, J. W. Weeton, R. W. Jech

An investigation was conducted to determine the stress-strain behavior and tensile properties of metallic composites and to relate them to the properties of the base materials. Tungsten fibers in a copper matrix were chosen as the model sys-tem to investigate these properties. Room-temp-atzcre tensile and dynamic -modulus tests were used To meet the demand for improved structural materials, considerable effort is being directed toward the creation of composite materials. One such material under investigation is the fiber-reinforced composite, in which a ductile, relatively weak matrix is reinforced with high-strength fibers. Some work has been done on the reinforcement of metallic matrices with metallic fibers1"5 as well as with ceramic-whisker reinforcement. Summaries of much of this work have been published by Mach-lin7 and Baske~.' Work done at the Lewis Research Center of NASA-" has involved the making and testing of composites composed of a fiber, tungsten, and a matrix, copper, which were insoluble in each other. An equation was presented that showed the relation between the ultimate tensile strength of the composites and the strengths and relative volume percents of the components. This relation was verified experimentally for composites containing fibers extending the full length of the specimen as well as for composites reinforced with short-length or discontinuous fibers. Since the publication of the preliminary results,9'10 additional data have been obtained. This paper presents these data as well as analyses of the stress-strain behavior and the mechanics of deformation of uni-axially oriented, fiber-reinforced metallic composites, in which both components are mutually insoluble. EXPERIMENTAL PROCEDURE Composites were made with high-purity copper as the matrix and 3-, 5-, and 7-mil-diam tungsten wire as the reinforcing fiber. Some specimens were made in which the reinforcing fiber extended completely through the full length of the composite test section. The fibers were placed in ceramic to determine these properties. The composites were reinforced with either continuous or discontinuos tungsten fibers. The tensile properties and stress-strain behavior of composites reinforced with either type of reinforcement were similar, and in both cases the full strength of the fiber was utilized. tubes to insure axial orientation and infiltrated with copper at 2200°F for 1 hr. Composites were also made with short-length (3/8 in. long) 5-mil-diam tungsten fibers as discontinuous reinforcement and infiltrated under the same conditions. The reinforcing fibers in both cases were longitudinally oriented in the direction parallel to the tensile axis. Room-temperature tensile tests were conducted on the composites, stress-strain curves were obtained, and ultimate tensile strength and elongation were measured. Dynamic modulus of elasticity, based upon the resonant frequency induced in the flexural mode of vibration, was also determined for the composites and the components. A more detailed discussion of the experimental procedure employed in this investigation may be found in Ref. 11. RESULTS Room-temperature tensile tests were conducted on 3-, 5-, and 7-mil-diam tungsten wires which had been annealed for 1 hr at 2200°F and show the tensile strength of the wires to be 331,000, 327,000, and 290,000 psi, respectively. Since all the composites were infiltrated under these conditions, the strengths were considered to represent the strength of the fibers in the composites throughout this study. The average tensile strength of the annealed copper used as the matrix in this investigation was 27,800 psi. Results of room-temperature tensile tests on composites reinforced with 3-, 5-, or 7-mil-diam tungsten fibers are plotted as functions of composition in Fig. 1. These data represent previously reported datag,l0 as well as data more recently obtained. The line shown on each curve represents a prediction of tensile strength as a function of composition; the calculation of this line was explained in Refs. 9 and 10. A similar plot is presented in Fig. l(d) for composites reinforced with short-length, discontinuous 5-mil-diam tungsten fibers. Again, both the previously reported and the recent data are presented, and the line shown is identical to that shown for

Jan 1, 1965

By R. Shuttleworth, R. Smith

A Knudsen effusion tnethod I~as been used lo measure the vapor pressure of pure iron in the temperature range 1000° to 1500°C. Neutron-irradiated , natural iron was used and the Mn'~proclzdced by the (n, p) reaction removed by evaporation at high temperature. The results can be represented by the equation: where pM - 1.088 x 107 atm and T, = 20,890°K. A value of 100.2 kcal per g- atom was obtained for AH;. THE vapor pressure of pure iron in the temperature range 1000" to 1500°C has been measured. Radioactive iron and a Knudsen cell technique were used and the Mn' produced by an (n, p) reaction removed by evaporation at high temperature. From the variation of vapor pressure with temperature values of the enthalpy and entropy of solid iron have been found. Previous workers2 used a Lang-muir method and measurements were made over a smaller temperature range than that in this work. EXPERIMENTAL The apparatus used was similar to that of Pyle and Shuttleworth, and McLellan and Shuttle worth. However, because of the higher temperatures the Knudsen cell was machined from tungsten bar and the flanged furnace tube was beryllia. Heating was by passing a high current (70 amp at 7 v for 1500°K) through a strip of tantalum foil laid across the top of the cell and through a turn of molybdenum wire around the furnace tube. This method of heating ensured that the top of the cell was slightly hotter than the base and prevented condensation and re-evaporation from the orifice. The temperature was measured by means of a pt/Pt 13 pct Rh thermocouple spot-welded to the base of the crucible. To ensure accurate temperature measurement the iron was in the form of a thin disc (0.75 cm diam by 0.075 cm) which lay on the base of the cell. The high-purity iron was irradiated in the Harwell pile for a week at a neutron flux of 1.2 X 10" neutrons per sq cm per sec. The isotopes fe'~ and Fe" are produced by (n! y) reactions but only Fe", half-life 45.1 days, is a emitter; Mn which is also a y emitter, half-life 300 days, is produced simultaneously by an (n,p) reaction.' Immediately after irradiation of natural iron the ratio of ~e" to Mn y activity was 100:l. However, manganese is very much more volatile than iron and almost all the y activity of the condensate is due to Mn'~. Thus it was essential to eliminate all the manganeses before any measurement of the vapor pressure of iron was made and this was done by preliminary heating for 20 hr at 1400°C. For each determination the iron was dissolved from the target with acid and the y activity compared to a known weight of iron. By means of a y-ray spectrometer the y-activity measurements were made at the 1.09-mev peak of the 17e5' spectrum where the background was of the order of 3 cpm. Despite the low specific activity of ~e" a mass of 10- " g of iron could be determined corresponding to a vapor pressure of about l0-'' atm. RESULTS The vapor pressures were calculated from the equation: Where m is the mass of iron effusing in a time t through an orifice of area a2, r is the radius of the target, Z is the distance from the orifice to the

Jan 1, 1965

By E. T. Peters, L. E. Tanner

In the course of a study concerned with the rnechanical behavior of the intermetallic compound CO3V, both structural observations and anomalous electrical-resistivity behavior indicated the presence of a new high-temperature phase in an alloy with the stoichiometric composition, Co-22.4 wt pet V. The evidence, which is given below, suggests that the new phase is situated between the low-temperature ordered hexagonal phase, k,1, 2and the high-temperature disordered fee solid solution, a,3 within a small range of temperature in the vicinity of 1070°C. Structural studies included X-ray diffraction analysis* and electron-transmission microscopy examination* of stoichiometric composition speci- mens homogenized for 1 hr at 1200oC and either air-cooled or water-quenched. The air-cooled specimens yielded X-ray diffraction evidence of the k phase, while electron microscopy revealed a microstructure of both heavily and moderately faulted regions as shown in Fig. 1. The high density of stacking faults (or fine twins) in region A is reminiscent of hexagonal cobalt following its allotropic transformation.4 Selected-area diffraction from this region revealed distinct superlattice reflections of the ordered hexagonal phase, as well as continuous rel-streaks which were normal to the fault planes in the micrograph. The latter is indicative of extremely small spacings between the faults.' Regions such as ß were found to be only partially transformed to the k phase. Attempts to study the antiphase domain structure by either bright- or dark-field techniques were unsuccessful in these initial studies. This was due to the low intensity of the superlattice reflections arising from the closeness of the cobalt and vanadium scattering factors. Quenching Co3V from above Tc appears to suppress the formation of the k phase. Both X-ray and electron-diffraction results indicated that the disordered phase, a, was partially ordered during severe cooling and that the structure of the ordered phase was of the L12 (Cu3Au) type,6 designated here as a'. As in the case of the hexagonal phase, examination of the domain structure was unsuccessful; however, significant information concerning the morphology of this condition was revealed by the appearance of dislocation arrays. In particular, it

Jan 1, 1965

By D. L. Sikarskie, B. Paul

A theory is presented for the static penetration of a single rigid wedge into brittle material. The material considered is one which exhibits both crushing and chipping phases in the penetration process. If the wedge angle and three parameters are specified, the theory predicts forces and associated penetrations during both the crushing and chipping phases. For certain ranges of the parameters agreement with the limited experimental data available is promising, except for the initial phase of the penetration process where refinements on the proposed theory are required. The theory also predicts that for certain values of the wedge angle and other known parameters, the chipping process does not occur and penetration is due entirely to crushing. When viewed in detail, the drilling of rock by percussive means involves, among other things, system dynamics, actuating forces, dynamic stress levels and the actual penetration mechanism of the bit into rock. If rock drills are to be significantly improved, a thorough understanding of the entire system would be highly desirable. In this paper, one aspect of the system, namely the mechanism of penetration of the bit, will be studied in detail. It has been found1 that for the velocities encountered in percussive drilling (of the order of 20 fps) a static analysis adequately describes the penetration process, at least for some rocks. Hence, we will only be concerned with describing analytically the static penetration of a single wedge shaped tool. It will further be assumed that the wedge is long enough to permit a two-dimensional analysis. Numerous authors have studied the static penetration of a wedge into rock. The following papers give some of this work and provide additional references to other work. Cheatham2,3 has assumed the rock to behave plastically and has obtained force-penetration equations for both Coulomb-Mohr and parabolic yield criteria. Evans and Murrell4 have studied the penetration of two types of coal and have found equations relating the penetration characteristic (P/dSc) to wedge angle for the various strength coals tested. race' attempted to find a correlation between hardness as determined by indenting the material and other mechanical properties and concluded that the results of such a test are generally inconclusive. His paper however contains a very extensive bibliography on the indenting of many different materials. Gnirk6 also has a fairly complete literature review on the static penetration of rock, of which he makes use in his indexing studies. A wide range of behavior is found in the wedge penetration of different rocks under different external conditions. For example, a rock that is essentially elastic-brittle at standard pressure may become elastic-plastic at a high confining pressure.7 It has also been observed4. " that some rocks will merely be crushed and indented by a wedge, whereas others will crack and form chips, furthermore the existence or non-existence of chips depends in great measure on the geometry of the indentor, type of rock and the depth of penetration. Hence, to attempt a theory which embraces all possible behavior is not practical at present. We, therefore, confine our attention to predicting the force-penetration characteristic and volume removal behavior for a type of rock which exhibits both crushing and chipping phases in the penetration process. Such behavior is characteristic of the harder rocks such as granites and represents a more difficult problem than the behavior of softer rocks such as coal and certain sandstones. In this preliminary study an attempt will be made to describe only the essential features of this complex penetration process. A qualitative description of these essential features is obtained with the aid of Fig. 1.1, where a wedge of vertex angle 28 is shown at some intermediate stage of the penetration process. As the wedge advances, the rock is fragmented (i.e. crushed) in some local region surrounding the wedge, the shape of this region being unknown. Simultaneous with the fragmentation in this local region, essentially elastic stresses are assumed to be building up in the surrounding rock. When a certain penetration level, di+1, is reached, the stresses along some surface are sufficient to cause failure and a chip is thus formed. The process now repeats, i.e., a crushing phase followed by the formation of a chip.

Jan 1, 1965

Jan 1, 1965

By H. D. Williams, R. A. Scriven

The distribution of elevation angle of finite plane facets distributed symmetrically about a given axis is derived in terms of the angular distribution of lines which these facets produce in a plane section parallel to the axis. It is assumed that the facets are not markedly elongated in preferential directions. The theory is intended for application to the angular distribution in polycrystalline metals of slip planes and of particular grain boundaries on which certain phenomena such as cavitation can occuv. Illustrative examples are given in closed form and simple numerical techniques are de-ueloped for practical application. The results are applied to the distribution of cavitated boundaries in a copper specimen after fatigue at 400°C and it is found that voids form on the boundaries that exper~enced maximum shear stress. When investigating the distribution of elevation angle between a given axis and planes symmetrically distributed about this axis the angular distribution observed in a plane section parallel to the axis is not necessarily the same as the required distribution. Consequently a technique for processing the results obtained by sectioning methods is required. An example where such a technique would find application is in the problem of intercrystalline void formation during uniaxial tensile creep. Two theories have been proposed to explain this cavitation in terms of the normal and the shear components of stress, respectively. Hull and Rimmer (1959) postulate that the growth of intercrystalline voids is controlled by the rate of supply of vacancies from the grain boundary, the local vacancy concentration being proportional to the normal stress on the boundary. Gifkins (1956) considers that slip arising within a grain causes a ledge to be formed at the grain boundary which is subsequently opened up into a cavity by grain boundary sliding. It might be possible to differentiate between these mechanisms by determining the angular distribution of grain boundaries containing cavities since the former theory predicts a predominance of cavitated facets normal to the stress direction whereas the latter should favor an angle of 45 deg to this direction. In a similar manner an indication may be obtained of the type of mechanism responsible for intercrystalline cavitation during high-temperature fatigue. Davies and Wilshire (1962) have analyzed the slip-plane distribution in a nickel specimen but the problem was not treated in any detail nor was any account taken of the finite extent of the planes being sectioned. Hilliard (1962) has given a very general account of how anisotropy in the microstruciure can be related to measurements taken in one or more plane sections by expressing both the measured and the true angular distributions as expansions in spherical harmonics.* The present analysis is con-

Jan 1, 1965

By Mark J. Klein, A. H. Clauer

The Snoek peak induced by solute nitrogen in chromium was studied. A rapid quenching rate is required to maintain nitvogen in solution in sufficient concentrations to be detectable by internal-friction techniques. An expression for the tertninal solubility, c, of nitrogen in weight pevcent is log,,c = -4130/T + 1.05. The diffusion of nitrogen in zhromium determined by internal friction is SNOEK&apos;S theory1 of the stress-induced ordering of interstitial solute elements in the bcc lattice has been used to deduce information on the behavior of interstitials in a number of bcc metals. Under the proper conditions, internal-friction studies of "Snoek peaks" permit a determination of diffu-sivities, solubilities, and precipitation kinetics of interstitial elements. Internal-friction studies of this type have been reviewed by Nowick,&apos; Wert,= Powers and Doyle,4 and others. The behavior of interstitial atoms in Group V-A metals and iron has been rather extensively studied in this way, and results are reasonably self-consistent. However, the study of interstitial elements using internal friction in the Group VI-A metals—tungsten, molybdenum, and chromium—is much less clear. Thus far, internal-friction studies have revealed a peak in tungsten tentatively attributed to carbon5 and a peak in chromium associated with nitrogen. In chromium, Bungardt and Preisendanz6 observed a peak at 180°C for a frequency of -1 cps which they associated with nitrogen. More recently, de Morton7 determined the diffusivity of nitrogen in chromium from studies of a nitrogen peak at 160°c for a frequency of -1 cps and from elastic aftereffect measurements. The objective of this investigation was to study the nitrogen peak in greater detail, to obtain information on the behavior of nitrogen in chromium. This information is of interest because nitrogen is known to have an embrittling effect on chromium. However, efforts to deduce the role played by nitrogen in influencing the mechanical behavior of chromium are handicapped by lack of information on its behavior and distribution in chromium. EXPERIMENTAL PROCEDURES The chromium wires used in these studies were drawn from arc-melted iodide-chromium stock that had been extruded, swaged, and centerless-ground to 0.25 in.-diameter rods. Internal-friction measurements were made in an evacuated torsional pendulum similar to the one described by Kê,8 utilizing wires 0.048 to 0.030 in. in diameter. A series of analyses of the fabricated wires showed that the major impurities were approximately 100 ppm Fe and a combined interstitial content of 50 to 100 ppm C, O, N, and H. A typical interstitial analysis of the wires after processing is 15 ppm C, 2 ppm H, 50 ppm O, and < 5 ppm N. Interstitial concentrations were determined by vacuum-fusion, combustion-conductimetric, and micro-Kjeldahl analyses. In general, vacuum-fusion analysis yielded a lower nitrogen concentration than did micro-Kjeldahl analysis. For consistency, the nitrogen concentrations reported in this investigation were determined by the former method. Heat treatments were carried out by encapsulating the specimens in quartz tubes containing argon. The fabricated wires were annealed at 1150°C for 1 hr to produce uniform recrystallized grain size of about 0.015 mm. Nitrogen and carbon were added to the fabricated wires by encapsulating them in a quartz tube containing ammonia or methane, and annealing them at 1150°C for 48 hr. In some instances, carbon was also introduced by coating the wires with carbon black prior to annealing.

Jan 1, 1965

By Hsun Hu, R. S. Cline

The effect of rate of deformation on texture formatiotz has been studied with cube-oriented single crystals of 3 pct Si-Fe, compressed 80 pct at two widely different rates. Compression at a low rate (crosshead speed, 0.1 ipm) produces large orienta-tional changes and coarse deformation bands, whereas little change in orientation is observed, particularly at the surface of the crystal, when compressed at a high rate (impact velocity, -500 ips). Thin plates of mechanical twins are produced at the high rate, but their contribution to the deformation texture is practically negligible. The crystal deformed at a high rate has a lower hardness and a more uniform dislocation structure and is morc resistant to recrystallization. There is also a dilference in the recrystallization texture between the slowly and rapidly compressed crystals. These results indicate that plastic flow is less "turbulent" at high strain rates than at low strain ratcs. THE behavior of metals under high-speed deformation has been the subject of wide study in the past decade. Most of these works were concerned with mechanical properties during testing at high rates of loading, the resulting structures, and the theoretical aspects of the observed phenomena. The present status of knowledge and research activities in this field has been documented in recent publications.17&apos; There is, however, very little information available in the literature concerning the effect of high-speed deformation on the texture formation in metals. The possibility of an effect of rate of deformation on texture is suggested by the microstructural differences observed between normally and very rapidly deformed samples. Aside from the strong tendency for twinning (and phase transformation in certain metals) in high-speed deformation, the slip-line patterns and the dislocation configurations show marked differences as a result of large differences in the strain rates. For instance, in mild steel in static and dynamic compression, Campbell and co-worker3,4 observed that coarse slip occurred on several systems in specimens deformed at normal strain rates, whereas specimens deformed rapidly showed only fine slip on fewer systems, the slip-line pattern being very similar to that in specimens deformed at low temperatures and at normal strain rates. The absence of multiple slip was also noticed by Dieter5 in shock-loaded nickel. The dislocation configuration in an iron shock loaded at 70 kbar pressure was shown by Leslie et al.6 to be similar to that produced by light rolling at low temperature—the dislocation lines were mostly straight and uniformly distributed. These observations suggest that the mode of deformation at high strain rates is notably different from that at low strain rates. Consequently, the nature and the extent of lattice reori-entation during deformation should also be different. This investigation was undertaken to test this idea. MATERIAL AND METHOD The remaining part of a single-crystal ingot of a 3 pct Si-Fe alloy,* prepared for an earlier investi- gation,1 was used in the present studies. Specimens 9/16 in. square and 0.365 in. thick were cut from this ingot with (001) planes parallel to the square surfaces, and the [loo] and 1010] directions parallel to the edges of the specimen, within ±1 deg. These machined crystals were etched to remove distorted metal, and annealed at 1300°C for 24 hr in a purified helium atmosphere. The annealed crystals had a hardness of 161 Dph. The crystal orientation was rechecked with X-ray back-reflection techniques. In high-strain rate experiments the crystal was compressed in a Dynapak machine to approximately 80 pct reduction in thickness (from 0.360 to 0.070 in. with an impact velocity of -500 ips). Thus, the duration of loading was approximately 6x 10-4 sec, and the average strain rate was about 103 sec-1. As a result of this rapid, severe deformation, the specimen became a roughly circular thin disc. The original shape of the crystal, however, could still be recognized by a diffusely outlined square area in the center of the disc. For compression at a low speed, the crystal was deformed in a universal testing machine at a rate of crosshead movement of 0.1 ipm. Compared with

Jan 1, 1965

By R. E. Ogilvie, H. C. Gatos, R. E. Hanneman

The effect of high pressure on the stability of the (any phase transformation in the Fe-V system was studied by experimental and theoretical methods. The maximum solubility limit of the y loop of the atmospheric phase diagram was found to increase by a factor of five at 40 kbars pres-sure. The solubility limits of (Y and y phases are calculated on an approximate thermodynamic basis at pressures of 20, 40, and 50 kbars as a function THE high-pressure behavior of the a =^ y transformation in iron and iron-base alloys has been the subject of considerable interest recently. For those binary or higher-order alloy systems possessing a closed y loop, the effect of pressure is to extend the region of solubility of the more dense y phase. Although quite accurate calculations have been made of the a y temperature-pressure diagram of pure iron,&apos; only very approximate thermodynamic calculations or experimental measurements have been made of the pressure dependence of a ^ y equilibria in binary systems exhibiting a y loop.2"4 of temperature and are found in excellent agreement with experimental results. The experimental high-pressure phase diagrams were determined using binary diffusion couples diffused under simultaneous conditions of high pressure and temperature and analyzed with an electron microbeam probe. Approximate calculations of the stabilizing effect of high pressure on the o phase are qualitatively confirmed by experimental results. These previous calculations have primarily dealt with the slopes of the allotropic a (Y= y phase boundary at terminal solubility. The lack of detailed understanding or accurate experimental results of the pressure dependence of the two-phase a ^ y field has been due, in part, to the types of experimental methods previously employed. The primary purposes of the current paper are twofold: 1) to develop and make use of thermodynamic expressions with the aid of supplementary data, to approximately calculate the pressure dependence of the entire y loop and the two-phase ((Y + y) width in the Fe-V system; and 2) to accurately determine the corresponding experimental high-pressure phase diagrams. The current paper describes the powerful method used which enables the simultaneously measurement of phase equilibria and diffusion under high pressure and temperature. A second paper, part 11, will deal with the effect of high pressure on binary diffusion in the Fe-V system.

Jan 1, 1965

By J. F. Nester, J. B. Schroeder

COMPOUNDS of rare-earth and iron-group elements are of technical interest because of their unusual magnetic properties. To date, however, all magnetic measurements1-4 have been made with polycrystalline, often polyphase, samples. For the measurement of anisotropic properties, single-crystal samples are necessary to avoid the averaging effect of randomly oriented grains. The purpose of this note is to describe a technique with which we have grown relatively large single crystals of YCo5, NdCo5, DyCo5, and "YFe9". Crystal growth of these materials is complicated because: 1) the binary equilibrium diagrams are, in general, not well-established; 2) in those cases where phase-equilibrium data are available, the compounds of interest are generally formed by peritectic reaction; 3) the molten component metals are chemically very reactive, making contaminaticn of the melts by the crucible material a serious problem. Techniques such as arc or levitation melting followed by strain annealing have been tried5)&apos; in the past with these materials, but with little success because of the peritectic reactions and the inherently poor process control. For this reason we chose to use the zone-melting technique of Mason and cook7 for our work, since past workers8 have had some success in preparing single crystals of peritectic compounds by this method.

Jan 1, 1965

By W. A. Jr. Slippy, E. P. Dahlberg, R. B. Reed-Hill

A large room-temperature mechanical-hysteresis effect under cyclic tensile loading was observed in zivconium specimens prestrained at 77°K so as to form large numbers of (1121) twins. The observed hysteresis loss was a maximum when the prestrain was just under 1 pct It also depended strongly on the maximum applied cyclic stress, but only moderately on loading rate and temperature (-72°to 100°C). The phenotnena have also been studied in terms of the elastic aftereffect where the data has been found to cotlforln closely to the functional relationship between strain and time, c = -RT/a In tank ft. t to)/Zr, for strains cts large as about 10-4 This eyication can be derived directly from the strain-rate equation There may be important commercial implications to the present discovery since it appears that within rather wide limits it may be possible to obtain any desired magnitude of damping capacity in zirconium melal. The damping propevties may also be given directional characteristics. It is shown that the observed anelaslic phenomena can he explained on the assumiplion that they are the resuilt of stress-induced twin-boundary movements in which the average twin increases its thickness by only a few percent. In polycrystalline zirconium, a grain is least favorably oriented for slip when its basal plane, containing the (1130) slip directions, lies nearly perpendicular to the principle normal stress. Mechanical twinning is favored by this orientation and under simple tensile deformation at room temperature the primary twinning mode is {1012).&apos; The (1012) twinning shear is small (0.17) so that, during deformation, twin growth does not greatly enhance ductility. At 77°K, on the other hand, the predominant twinning mode shifts to {1121), and many thin (1121) twins can form at small strains.&apos; Twins thus nucleated can grow readily during subsequent room-temperature deformation and permit easy deformation in unfavorably oriented grains. In addition, the (1131) twinning shear is large: 0.63. These facts have lead to a process&apos; for greatly improving the room-temperature ductility of zirconium when it contains a sizable fraction of grains with basal planes nearly normal to the stress axis. Optimum results are obtained by slightly less than 1 pct prestrain. The effect is large so that a 50 pct elongation increase is readily attained. A large room-temperature mechanical-hysteresis effect has also been observed in zirconium specimens prestrained at 77°K. The present paper is concerned with some aspects of this effect which the experimental observations strongly indicate is primarily the result of strain-induced {1121) twin-boundary movements. This clearly suggests that mechanical twins formed by plastic deformation can cause anelastic effects similar to those previously observed2 for annealing twins and twins associated with phase transformations. EXPERIMENTAL PROCEDURES All specimens were prepared from arc-melted sponge zirconium plate stock as previously described,3 which has a preferred orientation with basal planes aligned parallel to and uniformly distributed around the rolling direction. Both lonti-tudinal and transverse tensile specimens, with axes parallel and transverse, respectively, to the plate rolling direction, were cut from this plate. In a longitudinal specimen most grains are favorably oriented for slip, while in a transverse specimen a large fraction are unfavorably oriented. Prestraining at 77°K was performed in two ways. In one, annealed zirconium plate stock was cooled in liquid nitrogen and then rolled in the transverse plate direction to strains varying from 0.5 to 12 pct. Cylindrical 1/8-in.-diameter by 1-1/4-in.-gage-length tensile specimens were machined from this material. In the other, previously machined tensile specimens were prestrained in tension at 77°K between 0.2 and 3.8 pct. Type FA 25-12 SR4 strain gages were cemented to all specimen gage sections. All tests were performed on an Instron testing machine of 10,000-lb capacity. EXPERIMENTAL RESULTS Fig. 1 shows a typical two-cycle room-temperature stress-strain diagram for a specimen prestrained 0.65 pct by rolling at 77°K. The maximum stress in both cycles was 14,500 psi. Note that in the first cycle the loading and unloading curves are unsymmetrical so that a residual strain, er, remains after unloading. In the second cycle the stress-strain curves form a nearly symmetrical hystere-

Jan 1, 1965

By D. H. Baldwin, R. E. Reed-Hill

DURING the course of experiments involving oxygen equilibrations with a high-purity Pd-5 at. pct Rh alloy, the appearance of a subscale was noted. Most of the heat treatments in a pure oxygen atmosphere were performed at 900°C. The presence of the subscale was noted when the oxygen partial pressure was in excess of approximately 95 mm, up to 1 atm, the highest pressure used. According to available thermodynamic information&apos; on the free energy of formation of Rh2O3 (the only reliably reported solid oxide of rhodium), this oxide should not be stable under these conditions, nor, of course, any oxide of palladium. Extraction of the subscale from the matrix was affected by treatment with aqua regia, and the resulting X-ray diffraction powder pattern is shown in Table I. This pattern is not that of Rh2O3, nor that of any known rhodium or palladium oxide. It can be indexed on a hexagonal lattice with a. = 5.22Å and co = 6.0Å. In addition to this unknown material, there was a weak Rh2O3 pattern. An X-ray fluorescence analysis of the powder gave 3214 palladium counts per sec and 5381 rhodium counts per sec, thus indicating the likelihood of a double oxide of palladium and rhodium. In view of the fact that the above result was obtained on a single sample, it is perhaps best not to insist upon the above ratio of about 0.6, but possibly to tentatively assume 0.5 or 1/1. The small amount of Rh2O3 in the X-ray pattern might have occurred on cooling, and it seems possible that the double oxide, below some temperature level, is not as stable as Rh2O3. To examine this point, some of the extracted double oxide was heated on a sheet of pure palladium in air at 900°C, and allowed to furnace-cool over a period of several hours. The X-ray diffraction pattern of the powder showed approximately the same intensity of Rh2O3 and the "hexagonal" oxide as before, but, in addition, a rather faint pattern of another crystalline species made its appearance. This finding again suggests partial transformation of the major (double) oxide to other oxides on cooling from 900°C. Application of the phase rule shows that only one equilibrium oxide (subscale) could have been present at temperature. Vacuum-fusion, oxygen analysis of the extracted subscale showed 7.7 ± 0.7 pct O. Combining this information with that of the X-ray fluorescence analysis suggests the formula PdRhO. This compound should have an oxygen content of 7.07 pct, which is within the range of error of the oxygen analysis. However, until a more careful stoichiometric study is made, it is suggested that the formula be written

Jan 1, 1965

By E. E. Gardner, P. A. Schumann

A description of a new four-point probe configuration which permits measurement of epitaxial layer resistivity is given. An analytic solution to the potential distribution due to a point current source on a multilayered structure is briefly described. Typical solutions for this probe configuration are presented. Probe spacing, layer thickness, substrate resistivity, and substrate thickness enter into the calculation. Correction factors for typical cases are given. A brief description of the construction of a probe which can achieve a small spacing of 15 is presented. The prohe is constructed so that all points are adjustable by micrometers and the probe spacing and configuration can be easily altered. Measurements of layer resistivity with the four-point probe are compared with those taken with the three-Point probe and diode-capacitance techniques. TWO techniques of obtaining profiles of N/N+ epitaxial structures are given. The reproducihility of the probe spacing and resistivity measurement is discussed. The effects upon the resistivity measurement of errors in the measurement of the lager thickness, substrate resistil)itv, and substrate thickness are presented. SINCE its introduction by valdes&apos; in 1954, the four-point probe has been the most widely used tool for determining semiconductor resistivity. Its usefulness ranges from the evaluation of bulk semiconductor ingots to the characterization of impurity profiles in diffused structures. In general the four points, two current probes and two potential probes, are placed on one surface of the material being tested either in an in-line array or in a square array. Numerous correction factors1 8 have been worked out for these configurations which are dictated by the finite geometry of the sample being tested. One method of evaluating thin wafers has been proposed which has two probesg on each side of the wafer. Further modifications have added a fifth&apos;&apos; and a sixth" probe. One paper1&apos; has discussed the accuracy of the four-point probe and the precautions necessary in its use. With the exception of the method where two points are placed on opposite sides of the wafer, the four-point probe is restricted to evaluation of wafers with a homogeneous resistivity or to the case where an isolating junction exists between the substrate and the layer (epitaxial or diffused) being evaluated. Due to the relative resistivities and thickness, the resistance of the epitaxial layer is much greater than that of the substrate, and consequently a majority of the current flows through the substrate. The potential distribution at relatively large distances from the current sources is determined by the substrate resistance, and hence the AV/I value is a measure of the substrate resistivity and not that of the epitaxial-layer resistivity. In the immediate vicinity of a current source the potential distribution is determined by the layer resistivity among other factors. Consequently, if the potential probe is placed very close to the current source, then with appropriate correction factors it is possible to determine the layer resistivity. This was the theoretical basis for using two closely spaced probes on opposite sides of an epitaxial wafer. However, due to mechanical problems, it is desirable to place the four probes on the same side of the wafer. This paper discusses the potential distribution in

Jan 1, 1965

By J. M. Dahl, L. H. Van Vlack

STAFF: Editor, Gerhard Derge Associate Editor, Paul G. Shewman Carnegie lnstitute of Technology Schenley Park Pittsburgh, Pa. 15213 Editorial Assistant, M. A. Redmerski Production Editor, Otto T. Johnson THE METALLURGICAL SOCIETY: Jack H. Scoff, President; Richard C. Cole, Post-President; Harold B. Emerick, President-Elect; Ralph L. Hennebach, Treasurer; Robert W. Shearman, Secretary; Donald A. Parks, Assistant Secretary; Leslie S. Wilcoxson, Assistant Secretary. PUBLICATIONS COMMITTEE OF THE METALLURGICAL SOCIETY: R. E. Lund, Chairman; T. E. Dancy, H. B. Emerick, P. R. Gouwens, R. E. Grace, J. H. Jackson, H. H. Johnson, A. E. Lee, Jr., R. R. Nosh, R. D. Pehlke, and Paul Queneau. Review and selection of monuscripts is under the supervision of the following Publications Committees: Extractive Metollurgy Division: R. E. Grace, Chairman; G. M. Bell, D. W. Bridges, J. M. Cigon, G. W. Healy, T. A. Henrie, R. D. Holli-day, C. E. O&apos;Neill, C. S. Sami s, A. W. Schlech-ten, and Charles Shull . Iron and Steel Division: R. D. Pehlke, Chairman; T. P. Floridis, Arnulf Muon, G. R. St. Pierre, E. T. Tuckdogon, L. H.Von Vlack, and J. M. Uys. Institute of Metals Division: H. H. Johnson, Jr., Chairman; J. B. Clark, Vice Chairman; M. R. Achter, G. F. Bolling, J. O. Brittain, G. P. Conard, II, L. A. Girifolco. G. T. Hahn, J.P. Hirth, L. Himmel, G. T. Horne, George Krauss, C. F. Leitton, Jr., J. D. Livingston, R. D. Monning, H. M. Otte, S. V. Radcliffe, R. E. Reed-Hill, H. C. Rogers, O. Sherby, M. T. Simnod, G. R. Speich, E. A. Steigerwold, R. A. Swolin, W. A. Tiller, W. R. Upthegrove, J. B. Wagner, Jr., Derek Walton, H. W. Weart, W. W. Webb, and D. WiIsdorf. Published monthly by the American lnstitute of Mining, Metollurgicol, and Petroleum Engineers, Inc., 345 East 47th Street, New York, N. Y. 10017. Telephone PLAZA 2-6800. Subscription $30 per year for non-AIME members in United States and North, South, and Central America; $32, foreign; $7.50 for AlME members. Single copies, $6.00, single copies foreign, $6.50. The AlME is not responsible for any statement mode or opinion expressed in its publications . . . Copyright 1965 by the American Institute of Mining, Metallurgical, and Petroleum Engineers, Inc. . . . Registered cable address, AlME New York . . . Indexed in Engineering Index, lndustrial Arts Index, and Chemical Abstracts . . Second class postage paid at New York, N. Y., and Ann Arbor, Mich. Volume 233, Number 1.

Jan 1, 1965

By John D. Verhoeven

A technique has been developed for carrying out normal freezing experiments with a current density of 2000 amp per sq cut passing through the solid-liquid interface. The equation relating the effective distribution coefficient to the equilibrium distribution coefficient in electric field-aided solidification, originally developed by Huckc et al.,1 has been modified for the case of concentrated solutions. Preliminary experiments on the Sn-Bi system give qualitative agreement with the equation. The data are analyzed by a slightly novel use of the normal freeze equation which allows one to determine the effective distribution coefficient more easily. Very extensive mixing in the liquid was found at these high current densities and it is postulated that the mixing results from a vertical component of the magnetic Lorentz force generated by the electric current. In the search for techniques of obtaining ultrahigh-purity metals the inefficient but very effective technique of electrotransport has received little attention. Electrotransport is most effective in the liquid state and a natural application, therefore, is to apply an electric field across the liquid zone of a zone-melting experiment. The present investigation was undertaken to study the effect of an electric field upon solidification of metals, so that the usefulness of electrotransport in such solidification experiments as zone melting could be determined. In zone-melting and normal-freezing experiments it is difficult to achieve complete mixing in the liquid in the immediate vicinity of the solidifying interface. Consequently a solute build-up will occur at the interface in the portion of the liquid where complete mixing does not occur (an equilibrium distribution coefficient, ko, less than one, and unidirectional atom motion will be implied throughout). This local solute build-up produces a corresponding rise in the solute concentration in the solid so that the ratio of the solute concentration between the solid and the bulk liquid is larger than the equilibrium distribution coefficient. This ratio is defined as the effective distribution coefficient, k,. The differential equation describing the solidification process may be derived by applying the continuity equation to an expression for the net solute flux at the interface. The solution to this differential equation then allows one to determine the solute distribution in the liquid and the relationship between k0 and ke. One of the most useful solutions to this equation was first derived by Burton, Prim, and Slichter,&apos; in which they assumed that a) the equilibrium distribution of solute was maintained on the plane of the interface, 11) the solute build-up ahead of the interface in the liquid disappeared at a distance 6 from the interface, and c) the solute distribution in the liquid was invariant with time. The following well-known relation between ko and ke was then obtained, where R is the rate of solidification and D the diffusion coefficient of the solute in the liquid. This equation appears to correlate the data from a number of different types of solidification experiments very well. Application of an electric field across the solid-liquid interface can produce an additional flow of solute atoms as a result of the electrotransport. When the polarity of the field is such as to direct the electrotransport flux away from the interface the solute build-up may be diminished, even to the point of producing a solute depletion and a consequent ke smaller than ko. The quantitative description of this process and the resulting form of Eq. [I] was first given by Hucke et al.1* and then inde- where E is the electric-field intensity and U is the differential mobility, i.e., the velocity of the solute atoms with respect to the solvent atoms per unit electric field. Both authors follow the method of Burton, Prim, and Slichter in their derivation, the only difference being the additional electrotransport term in the flux equation. It has been pointed out1,3 that Eq. [2] predicts the possibility of a noticeable increase in the purification of materials by solidification in an electric field. The validity of Eq. 121 has not been checked experimentally and it is possible that other factors&apos; arising from the presence of an electric field across

Jan 1, 1965

By R. M. Goldhoff, H. J. Beattie

The high-temperature properties of a 1 Cr-Mo-V forging steel are described. A series of controlled heat treatments was designed to delineate the effects of austenitizing and tempering treatments, temile strength, and grain size on such properties. Studies indicate that the mechanical properties and their varlations under creep can be described by the initial metallurgical structures and their changes droPirzg exposure, particulavly the carbide reactions. Such structures are described and correlated with the mechanical properties. FOR many years the large steam turbine industry has relied on the 1 Cr-Mo-V type forging steel for critical applications. Because of its adequate heat resistance and relative economy, it is currently in use in the temperature range up to about 1050" to 1075°F. Attempts to understand the large property variations attainable in this steel involve the structural modifications due to the wide latitude in its heat treatment. The heat treatment essentially involves a two-step process which includes solution-ing of carbides in the austenite range followed by a suitable tempering treatment below the critical to adjust the level of properties. The latter step is referred to as "secondary hardening" and is basically an ordinary aging reaction involving carbides. In the commercial heat treatment of large components of such steel, homogenizing and stress-relief anneals may be included and have some importance in determining subsequent properties. Several studies of the engineering properties of this steel as a function of transformation micro-structure have been reported.1 3 However, in this steel the carbide reactions, which are a function of composition and heat treatment, appear to be the property-controlling factor rather than the micro-structure defined as a transformation product. Thus, the tempering resistance of this type of alloy steel is mainly a function of the size and distribution of alloy carbides.4 However, it is also necessary to consider the stability of the microstructure and the effect of dynamic carbide reactions on subsequent properties. It is the purpose of this paper to show the interdependence of properties and corresponding structures, particularly carbide reactions, developed for a limited set of controlled heat-treatment conditions applied to 1 Cr-Mo-V steel. MATERIALS AND PROCEDURE The material for this work came from a large production forging whose chemical composition is shown in Table I. The property data accumulated on this steel as a function of heat treatment were room-temperature tensile and smooth- and notch-bar creep rupture at 1050°F (notch geometry: shank diameter = 0.357 in., depth = 50 pct, radius = 0.005 in.). To achieve controlled structural variations the temperature and time of both austenitizing and tempering were varied in a manner to produce a series of eight steels each at one of two grain sizes and one of two hardness levels in proper combination for valid comparisons. This will be clear upon examination of Table I. Structural studies involved the use of optical and electron microscopy as well as X-ray and selected-area electron diffraction. To reveal the nature of carbide precipitations, electrolytic extraction techniques were used with subsequent analysis of the residue by X-ray diffraction. Weight losses of the steel specimens during electrolysis were measured and successive chemical fractionations of the residues were applied and checked by X-ray examination. The details of fine structural distributions, morphologies, and crystallography of the precipitates as well as dislocation distributions were investigated by examining in the electron microscope three common types of preparation. a) Relief Replicas. Mechanically polished sections were etched in 2 pct nital, replicated with a nitrocellulose film, which was shadowed by chromium vapor deposited at a glancing angle of 20 deg. b) Extraction Replicas. A thin film of carbon was vapor-deposited on the polished and etched surface. The carbon films were then etched off and gathered on electron-microscope supporting grids. The carbides left imbedded in the carbon replica in their original distribution were then examined crystallo-graphically by selected-area electron diffraction. c) Thin Films. Specimens were mechanically ground and polished down to a thickness of 0.001 to 0.003 in. Final thinning was done electrolytically in a "chrome-acetic" electrolyte. When holes began to appear in the foil, the voltage was interrupted and applied in several 1-sec bursts. Sections of the foil between holes were thin enough to pass a 100-kv electron beam that carries an image.

Jan 1, 1965