By N. A. D. Parlee

The diffusion rate of hydrogen in liquid iron has been measured by a gas-liquid metal diffusion cell technique. The diffusion cell was formed by immersing an alumina tube containing hydrogen gas at 1 atm in a bath of stagnant liquid iron. The change in the composition of the melt in the cell was determined by measuring the rate of absorption of the gas in the cell. The appropriate solution to Fick's second law was used to examine the data and calculate diffusivi-ties. The absorption of hydrogen in stagnant pure liquid iron has been found to be diffusion-controlled. The results show that the chemical diffusion coefficient, D, of hydrogen in pure iron in the range of 1547" to 1726°C can be represented by the following Arrhenius relation: D(sq cnz per sec) = 3.2 x X exp(- 3300 i 1800/RT) where the uncertainty in the activation energy corresponds to the YO pct confidence level. Oxygen in the melt (above 0.015 pct 2) increased the apparent rate of absorption of hydrogen. The importance of diffusion data on liquid metals for predicting the rates of certain metallurgical processes has been recognized for a long time. Moreover, these data are much needed to test and develop theory for diffusion in liquid metals. Despite this practical and theoretical interest, however, relatively little reliable information about diffusion in liquid metals is available in the literature. This is particularly true for gas components such as hydrogen, oxygen, and nitrogen in liquid metals, where almost no data on chemical diffusion coefficients are to be found. This is probably due to a multitude of experimental difficulties particularly associated with high-temperature melts. In an effort to fill this gap in information, a research program was undertaken to study the diffusivities and rates of solution of gases in liquid metals. This paper presents the results of a study of the diffusion of hydrogen in liquid iron. EXPERIMENTAL METHOD Two methods for the study of the kinetics of dissolution of gases in liquid metals are being employed in this laboratory. Both involve the measurement of the volume of gas absorbed by the melt as a function of time and as such both avoid the uncertainties involved in chemical analyses of quenched samples for relatively small amounts of gas. In the first method, the gas dissolves in an inductively stirred melt and, in the absence of a slow surface reaction, the results are often interpreted in terms of mass transport across a liquid "boundary layer" between the homogeneous gas phase and well-stirred part of the melt. Other interpretations of the results of such experiments have also been described in the literature.1'5 In the second method a gas-liquid metal diffusion cell is used.' The gas dissolves in a cylindrical column of stagnant liquid metal and, in the absence of a slow surface reaction, the results are interpreted in terms of a non-steady-state diffusion solution to Fick's second law. The weakness of the first method is that while it gives information on the mechanism of absorption by stirred melts it yields an overall rate constant which even in the simplest cases depends on the nature and the thickness of the "mass transport layer" or "boundary layer". It yields no values of diffusion coefficients. The second method was used in this research because in many cases it is possible to determine the diffusion coefficient of the gas component in the liquid metal. In this research it has been utilized to measure diffusion coefficients of hydrogen in liquid iron. The apparatus used was essentially the same as that described by Mizikar, Grace, and par lee but certain modifications have been introduced to meet the elevated temperatures and special conditions of this research. Fig. 1 is a schematic drawing of the apparatus and Table I gives the identification of various parts in this figure. The diffusion cell, shown in detail in Fig. 2, was formed by immersing an impervious alumina tube (hereafter called absorption tube) in a bath of pure liquid iron contained in an alumina crucible. Two types of tubes were used, Morganite triangle RR and McDanel AP35. The crucible was contained in a vertical impervious alumina combustion tube (32 mm ID by 914 mm long) which was closed at both ends by water-cooled brass heads employing O-ring compression seals, Fig. 1. A protection tube enclosing a Pt, 5 pct Rh-Pt, 20 pct Rh thermocouple was introduced through the lower end of the combustion tube

Jan 1, 1968

By C. S. Yust, Lida K. Barrett

The change in shape of the void in a sirzterir~g copper mass has been investigated as a juntction of' density. A serial sectioning' technique was used to eoaltrate the irregular shape of the void at two levels qf density. A measure of the void size and configuration, the proximity number, is defined and used to describe the progress of void removal. The process of. void removal deduced front the observations of this study contrasts with current sintering models in that it takes into account the irregularity of structure of a sintering mass and demonstrates that isolated Porosity does not occur first as spherical pores, but as large, definitely nonspherical sections of the void void volume. The process of sintering, about which there is much practical and theoretical knowledge, has evaded a direct and thorough analysis despite the intensity with which it has been studied for 60 years or so. This is due, of course, to the complex structure of a sintering mass and the inability to observe directly the development of a fully dense solid from the initial particulate arrangement. Extensive theoretical analyses have been based on the adoption of one or another of several model systems, that is, by visualization and analysis of some sort of regular assembly or arrangement of geometric "particles" approximating the conditions of a sintering mass. It seems appropriate at this time to try to examine experimentally in some detail the extent to which a sintering mass of irregular particles dlffers from these models. Many models deal with neck growth and the initial stage of sintering and follow the direction established by ~ucz~nski' in 1949 for the sintering of spheres to flat plates. Recently Johnson and cutler2 have adapted these models to sintering of powder masses. coble3 has presented a mathematical model for sintering that applies to the middle and final stages of the process. These papers, without exception, assume a regular geometry, generally spheres in contact in a regular array. Rhines~ and coworkers, however, are studying the sintering process by applying a model based on the topological concept of genus which permits them to consider an irregular structure. whites has described the various models with the exception of that of Rhines et al., and the assumptions on which they are based and their shortcomings. The present paper examines the geometric changes that occur in the powder mass during sintering by examination of the void. The method is to analyze a series of partially sintered structures and to propose from this analysis the sequence of events which occur in the removal of the void space as a sintering mass progresses from a collection of individual particles to a solid body. The irregular nature of the stacking of particles and of the particles themselves will be taken into account. The significant points derived from this study are: first, accurate reconstructions of the irregular void shapes are presented; second, it is clearly established that closed porosity occurs first as widespread volumes of interconnected porosity, definitely nonspherical in shape; and third, a new factor, the proximity number, is defined, which serves in this paper as a tool for describing the void shape changes observed, and which will be used in a later paper as part of the basis of a mathematical model for sintering. While the specific material studied is copper, the observations are thought to be relatively general as indicated by comparison of the results with partially sintered structures in other materials presented in the literature, both metallic and nonmetallic. EXPERIMENTAL PROCEDURE Four series of specimens representing progressive stages of the sintering process were prepared by sintering high-purity copper powder for various time periods. A relatively large particle size was used so that the void-solid interface could be readily distinguished at low magnification. In three series of specimens a loose stacking of particles was obtained by pouring powder into an alumina mold and lightly tapping the mold. The green density of such compacts was approximately 40 pct of theoretical density. Two of these three series utilized irregularly shaped particles in the size range -230 +325 mesh, one series sintered in vacuum and one in hydrogen at 950°C. The third series of loosely stacked particles consisted of spherical particles in the size range -270 +325 mesh, sintered in hydrogen at 950°C. A fourth series was prepared from compacted irregular particles sintered in hydrogen at 950°C. The specimens for this series were formed by lightly pressing the irregularly shaped particles in a steel die; the green density of the pressed pellets was approximately 60 pct. The irregularly shaped particles used in this study are shown in Fig. 1. The density of these particles, measured by a toluene picnometer technique, is 98.2 pct of theoretical density. Each particle is highly convoluted, and in some instances appears in cross section to contain internal porosity. The density measurement, however, indicates that completely enclosed porosity is very small so that the individual particles have a highly irregular surface but are essentially fully dense copper. Therefore, most of the void space that appears in two dimensions to be isolated within the particle is actually at the particle surface and connected to the external void in the dimension not included in the plane of the cross section. The void space that appears as void surrounded by the par -ticle or within folds in the particle w~ll be r~fc\r?

Jan 1, 1968

By J. S. Owens, R. W. Marsden, J. W. Emanuelson, R. F. Werner, N. E. Walker

The iron ores of the Mesabi Range occur in a 340 to 750-foot thick, Precambrian cherty iron formation termed "taconite." For about 65 years, extensive natural iron ore bodies were mined, and the ores either shipped as a direct ore or processed by gravity methods to a shipping grade iron ore. Since 1956, magnetite taconite ores, occurring in magnetite-rich horizons in the Biwabik iron formation, have been commercially concentrated and agglomerated. The transition from natural ores to concentrating-grade ores is progressing rapidly so that, in the near future, a major percentage of the iron ore shipped from the Mesabi Range will be as iron ore pellets produced from taconite. Natural iron ores of the Mesabi Range occur in the Biwabik formation as trough ore bodies in elongated channels and as irregular and tabular deposits in fractured areas associated with faults and folds. Ore bodies range in size from a few thousand tons to hundreds of millions of tons and may occur in any part of the iron formation. In some areas of strong ore development, ore was formed from the hanging-wall argillite to the footwall quartzite. The natural ores and beneficiating-grade natural crude ores were formed by the oxidation of the iron minerals, magnetite, greenalite, stilpnomelane, minnesotaite, and siderite, to hematite and goethite and by the removal of much of the silica in the cherty quartz and in the associated silicates by leaching. The ores are believed to have formed by the oxidizing and leaching action of surface waters. Magnetite taconite ores occur as stratigraphic zones in the Biwabik formation where it contains sufficient magnetite to be concentrated profitably, by magnetic methods, to give a magnetite concentrate that is agglomerated into a high quality product. Unoxidized taconite has an extensive distribution away from and between channels of oxidation and leaching but only a part of the unoxidized taconite is of ore grade. Two general types of magnetite taconite ore occur: ( 1) magnetite taconite of the Main Mesabi Range, generally west of Mesaba, which is composed of magnetite associated with cherty quartz, greenalite, stilpnomelane, minnesotaite, and carbonates and (2) magnetite taconite of the Eastern Mesabi, generally east of Mesaba, composed of magnetite associated with quartz, cummingtonite, actinolite, ferrohypersthene, hedenbergite, fayalite, hornblende, pyroxene, garnet, and biotite. The Mesabi taconite is a metasediment derived from an iron- and silica-rich chemical sediment that has been regionally metamorphosed and, on the eastern end, additionally metamorphosed by the Duluth Gabbro Complex.

Jan 1, 1968

By R. Grierson, L. J. Bonis

The high-temperature Strength oF TD nickel has been observed to be dependent upon the previons thermal and mechanical history of the material. Variations in both the level and the anisotropy of strength have been observed. 01 this paper- these variations are correlated with the storing of annealing resistant elastic strain energy in the matrix of the TD nickel. An x-vay line -broadening tecknique is used to measure the maLrTis elastie strain. THE inclusion of a finely dispersed second phase into a ductile matrix has long been recognized as an extremely effective method of strengthening the matrix both at high and at low homologous temperatures. It has been found, however, that the factors which determine the high-temperature strength are not the same as those which are important at low temperatures. Below 0.5 Tm the size and distribution of the second phase particles are of prime importance in determining the strength,')' while above this temperature the strength is mainly dependent upon the previous thermal and mechanical history of the alloy,3-7 This paper is primarily concerned with explaining the response of the high-temperature mechanical strength of one of these alloys (DuPont's TD nickel) to various thermo-mechanical treatments. It will be shown that this response is not associated with the occurrence of any form of dislocation substructure within the matrix of the alloy. It has been found, however, that a correlation does exist between the elastic strain level in the matrix and the previous thermomechanical history of the alloy and that the observed changes in elastic strain level parallel the measured changes in high-temperature strength. It therefore must be concluded that variations in high-temperature strength are a direct result of the variations in elastic strain level. MATERIAL TD nickel contains approximately 2 vol pct of Tho2 in an unalloyed nickel matrix. It is formed, as a powder, by a chemical technique and this powder is compacted to form ingots which are then extruded to give 21/2-in.-diam rod. Rod of smaller diameter is prepared from the as-extruded rod by swaging. In the studies reported in this paper, 1/2-in.-diam rod was used. This rod received an anneal of 1 hr at 1100°C prior to being used in any of these studies. EXPERIMENTAL TECHNIQUES Two methods were used to examine the structure of the nickel matrix of the TD nickel. These were: 1) transmission electron microscopy; 2) the analysis of the position and profile of X-ray diffraction lines obtained using the nickel matrix as the diffracting media. To prepare thin foils for electron-microscopical examination, slices of TD nickel approximately 0.050 in. thick were cut from the as-received 1/2-in.-diam rod. These were then chemically polished down to 0.045 in., rolled to 0.009 in., given a predetermined heat treatment, and thinned, using a modified Bollman technique, to provide the foils for observation. All observations were carried out at 100 kv, using a Hitachi HU-11 electron microscope. Specimens of the undeformed rod were prepared by grinding down the 0.050-in.-thick slices to approximately 0.015 in. and then thinning chemically and electrolytically to give the thin foils. The X-ray specimens were prepared by rolling 0.375-in.-thick rectangular blocks down to 0.075 in. The surfaces of the rolled material were ground flat, chemically polished to remove the layer disturbed by the grinding, and given a predetermined anneal in an inert atmosphere. They were then ground lightly to check their flatness and given a final chemical polish prior to being examined. The X-ray diffraction line profiles were measured using an automated Picker biplane diffractometer. A special specimen holder was built to allow a more accurate and reproducible positioning of the specimen. The line profiles were determined by carrying out intensity measurements at intervals of either 1/30 deg or 1/60 deg over a range of 3 deg on either side of the nickel peaks of interest. A piece of pure nickel which had been recrystallized to give a large grain size was used as a standard to give the X-ray line profile generated by a strain-free matrix. The analysis of the X-ray diffraction line profiles is a modification of that due initially to Warren and Aver-bach8and has been described elsewhere.3 This analysis gives a measurement of two parameters associated with the structure of the nickel matrix. These parameters are: 1) the size of the coherently diffracting domains within the nickel matrix; 2) the magnitude of the elastic strains in these domains. Both of these parameters are first determined in terms of a Fourier series. These series are obtained from other Fourier series which describe the measured profile of the X-ray diffraction lines. Thus, for both the coherently diffracting domain size and the elastic strain level, it is possible to plot Ft (the Fourier coefficient) against t (the term in the Fourier series), where t can be expressed in terms of a distance L and the Fourier coefficient Ft(S) (associated with elastic strain level) can be expressed in terms of the root mean square strain (e2)1/2. Thus a plot of (F 2)1/2 vs L can be obtained. Plots of this type are shown graphically in Figs. 6 and 8. Interpretation

Jan 1, 1968

By Bauer, Alan

In considering blasting it is necessary to consider the drilling and explosives since one is generally concerned with the total cost of muck of a certain size in the pit or through the crusher. To get a current idea of the drilling situation in open pit mines plotted in Fig. 1 are the drilling costs per ton of material vs. hole diameter for rotary drill holes in large limestone, iron ore and taconite operations. The exception is the 2-in. diam hole which was drilled with a percussion drill in limestone.

Jan 1, 1968

By Fred H. Perfect

The thermite process, now approximately 80 years old, has heretofore been practiced in ceramic vessels. This paper outlines the successful production of several million pounds of alloy produced in zuater-cooled copper vessels. THE high temperatures necessary to produce fluid high-alumina slags have probably discouraged earlier workers from attempting to utilize water-cooled vessels. The following is a report of the successful application of this method, together with a report of the physical and chemical problems which had to be solved to make the process practical. About 1955, when Reading Alloys was more concerned with the production of ferrotungsten than with most other types of alloys, it was found to be exceedingly difficult to predict the reaction rate that one would experience from one tungsten ore to another . This difficulty was increased for two reasons: the physical state of the ore as received was seldom uniform, and the size of the mass to be reduced is a very important factor in developing the proper mix for the final reaction rate and temperature. For example, the reduction of ferric oxide with aluminum would theoretically produce temperatures of about 2600°C, and, in spite of the losses due to radiation, the energy is quite sufficient to produce a very fluid slag and iron effecting a very clean separation. On the other hand, the reduction of ferrous oxide with aluminum, while it is not as energetic as the first reaction, nevertheless should give temperatures above 2000"C, which should cause separation of alumina and iron, but, in practice, this is not the case and good fluid slag is not obtained. The heat of reaction, calculated from the thermo-dynamic heats of formation of the constituents of the reaction, offers a convenient guide to the feasibility of a thermite reaction. Thus, the values listed in Table I can be used as an approximate guide for estimating the results which may be expected in the reduction of various oxides and combinations of oxides using aluminum as the reducing agent. As a generalization, those reactions releasing approximately 600 cal per g of total mass represent the lower limit at which to expect separation of slag and metal. On the other hand, those reactions which release 1100 to 1200 cal per g are too violent to be used successfully without the addition of considerable inert material, such as lime, fluorspar, and so forth. Reaction rate is also a very important factor. This, of course, is governed very largely by the sizing and intermingling of the oxidant and reductant and by the starting temperature of the reactants. This is why those figures shown in Table I can only be a general guide. Further, it must be understood, that by adding powerful oxidizing agents, such as nitrates, chlorates or metallic oxides, such as molybdenum trioxide or chromium trioxide, certain problems respecting low temperatures are not necessarily solved. This is true in the addition of oxidants, such as sodium chlorate. By adding too high a concentration of sodium chlorate as a booster for a particular reduction, explosions are generated. Generally, they are of an intermittent type so as to give a Roman Candle effect to the reduction itself; with each surge resulting from a minor explosion more and more material is thrown

Jan 1, 1968

By Arthur L. Hawthorne

10.1-1. Relative Position of Maintenance as Compared to the Overall Mining Costs. The basic issue regarding the importance of maintenance in the modern mining industry must be faced squarely by the top manage- ment of each company before any real progress can be made in organizing a maintenance program for optimum effectiveness. Just a few decades ago the maintenance at coal mines consisted primarily of a blacksmith for sharpening picks and shoeing mules; as a result, probably less than 5%of the total mining cost went to maintenance and some 80% was operating expenses (operating labor). With each succeeding advance in equipment design towards larger, more complex, and more productive units, the pendu- lum swings the other way. As an example, haulage trucks have progressed through various stages in the past 20 years from 15-ton units to a 240-ton truck now in the "shakedown" or experimental stage. The following com- parison between 15-ton, 50-ton, and 100-ton haulage trucks clearly illus- trates this changing cost pattern in terms of percent of overall costs for running each size unit. [Maintenance 24% 44 % 51 % Operating labor 59 % 33 % 16% Operating supplies (fuel oil) 4 %. 4% 3% Labor burden and vac. pay 6 % 4% 3% Depreciation Total] From the preceding figures it is interesting to note that, as a rule, operat- ing costs go down as the equipment gets larger and the maintenance costs increase with the larger units. This same trend in cost variation applies to nearly all mechanical equipment used in surface mining from the large

Jan 1, 1968

By H. C. Brassfield, R. E. Fryxell, E. C. Duderstadt, E. A. Aitken, P. K. Conn

Permeation rates of hydrogen through are-cast tungsten were measured at temperatures from 1300" to 2600°C with hydrogen pressure differentials of 1 and 0.1 atm across isothermal membranes. Rates were nearly Proportional to square root of pressure, were inversely ProPortional to membrane thickness, and were temperature-dependent according to the equation: p = permeation coefficient in cu cm (stp)-mm per sq cm-min-atmlr2, R = gas constant in cal per mole-OK, T = absolute temperature in OK. Permeation rates of oxygen through tungsten were deternlined in the range 1965" to 2300°C and at calculated oxygen (02) pressures of 3.3 x 10-4 to 2.2 x at?n using sealed capsules containing Kmown quantities of tungsten oxide. Permeation coefficients obtained in this manner had a temperature dependency in the range of 40 to 45 kcal per mole of permeating species. Permeation coefficients for oxygen were higher than those for hydrogen in the temperature range studied. This is probably the result of oxygen solubility being much greater than hydrogen solubility at these temperatures at a gzven pressure. The purpose of this investigation was to determine experimentally the permeabilities of hydrogen and oxygen through polycrystalline tungsten at temperatures ranging from 1300° to 2600°C. Permeation rates of hydrogen through tungsten have been measured at temperatures up to 925°C,but no previous measurements have been reported for the temperature range covered in this investigation. Some diffusion measurements3&apos;&apos; and solubility measurements3 have been made for hydrogen at temperatures below 2200°C. No previous permeability studies of oxygen through tungsten are known to the authors; however, efforts have been made to determine diffusion rates5-&apos; and solubilities PERMEATION THEQRY Permeation has been defined by ortton" as the overall steady-state flow process from the gas phase on one side of a membrane or wall to the gas phase on the other side and includes the steps of adsorption, solution, diffusion, exsolution, and desorption; in a given temperature range, any of these processes may be rate-controlling. For diatomic gases, which dissociate prior to diffusion, the quantity of gas which permeates through a membrane or wall at a given temperature is directly proportional to the surface area of the membrane, the length of time of permeation, and the difference between the square roots of the pressures on each side of the membrane, and it is inversely proportional to the thickness of the membrane when diffusion-controlled, thus: q = total amount of gas permeating a membrane, p = temperature-de pendent permeation coefficient, A = area of membrane exposed, / = time, p i = gas pressure of high-pressure side, p2 = gas pressure of low-pressure side, d = thickness of membrane. When the surface reactions are not rate-controlling steps and the solution of the gas in the metal follows Henry&apos;s law, the permeation coefficient, P, is equal to the product of diffusivity and solubility. The permeation coefficient is also temperature-dependent according to the equation: Po = permeation constant, Q = activation energy, R = gas constant, T = absolute temperature. MATERIALS The tungsten materials used in this investigation were greater than 99.9 pct pure. The interstitial impurities ranged from < 1 to 50 pprn C, 7 to 35 ppm O, less than 15 pprn N, and undetectable quantities of hydrogen. Previous high-temperature studies of are-cast tungsten have shown that thermal treatment similar to that which the hydrogen permeation cells experienced reduces the carbon content from starting levels of 50 to 60 ppm to about 30 ppm. Metallic impurities were in the low (1 to 50) ppm range. The argon gas used in this investigation contained about 8 ppm N. None of the following gases were

Jan 1, 1968

By Allen V. Heyl

This old district is a major zinc and lead source and minor copper and barite source. Ores are chiefly in the Galena Dolomite and in limestones and dolomites of the Decorah and Platteville Formations, all of Middle Ordovician age. Locally, deposits have been mined from Lower Ordovician dolomites and Upper Cambrian sandstones. Small deposits of lead, zinc, and iron sulfides have been found in Upper Ordovician Maquoketa Shale and in Lower and Middle Silurian Edgewood, Kankakee, and Hopkinton Formations. No post-Precambrian igneous rocks are known in the region, and the granitic and metasedimentary Precambrian basement rocks unconformably underlie the district at depths of 1500 to 2000 feet. The strata are gently flexed and faulted, probably largely the result of gentle compressive and rotational adjustments in the underlying crystalline basement, especially along lineaments between basement blocks. Folds of three orders ·of magnitude are recognized, and many related reverse, strike-slip, and normal faults of small to moderate displacements are present. Zinc-lead deposits are commonly linear, arcuate, or elliptical in plan. Most ore occurs as vein fillings in fractures and as breccia fillings and lining vugs, but some is in bedded replacements and impregnations of wall rocks. The ore is in shears, small reverse and bedding- plant faults, joints, and solution-slump structures related to intermediate and small folds. The main primary minerals in their general sequence of deposition are quartz, illite, dolomite, pyrite, marcasite, cobaltite(?), sphalerite, galena, chalcopyrite, millerite, barite, and calcite. Wall-rock alterations include solution of the carbonate rocks, silicification, dolomitization, clay alteration, and sanded dolomite. Oxygenisotope, trace-element, lead-isotope, and sphalerite- stratigraphy studies are in progress. Fluid inclusions in sulfide and gangue minerals are filled with concentrated brines at 120° to 40°C. Sulfides are directly replaced by supergene minerals above the water table at 50 to 100 feet in depth. In this relatively cool climate and limestone environment, smithsonite is in pseudomorphs after sphalerite; solution transport and redeposition of supergene minerals are rare. Ore genesis is postulated by rising hot-water solutions-a mixture of heated connate, magmatic, and meteoric waters.

Jan 1, 1968

By G. S. Cole

The temperature has been measured ahead of stationary solid-liquid interfaces under conditions approximating luzidirectional heat flow and therefore unidirectional solidification. Natural convection flow patterns may be deduced from the temperature distributions , temperature fluctuations, and shape of the interface. Fluid flow increases with the height and the rate of heat transfev through the interface and this is further manifested by a deviation of the interface from aflat vertical plane. The influence of fluid flow on solute inhomogeneity during alloy crystal growth can be inferred from the observed temperature distributions. A buoyancy force exists in the liquid ahead of a vertical solid-liquid interface, caused by a difference in density between cold fluid near the interface and warmer fluid in the bulk liquid. When the viscous and inertia forces in the melt exceed this buoyancy force, a flow of fluid takes place, termed natural or free thermal convection. Natural convection in purely liquid systems has been extensively studied for many years. 1"u On the other hand, fluid flow during horizontal crystal growth has oniy recently been the subject of experimental investigation."-25 The requirements for horizontal crystal growth differ from other heat flow systems. The small aspect ratio (ratio of height of cold wall to length of fluid) has never been considered. The uniform furnace gradient which supplies heat radially (and not necessarily symmetrically) differs from previous boundary conditions of uniform heat flux at the cold and hot ends. And most important of all an isothermal s/l interface is present which can adjust its shape and position to conform to heat and fluid flow. All of these boundary conditions involve complexities which cannot be readily solved analytically. Preliminary observation has demonstrated the penera1 shape of the natural convective flow pattern in transparent media.20&apos;24&apos;25 The flow is circulatory, directed toward the interface at the surface of the liquid, down and away from the interface at the bottom, and then up at the hot end of the melt. During crystal growth such a flow may interact with the solute boundary layer at the s/l interface to affect solute incorporation.M&apos;1B|28&apos;i!T Evidence has also been presented recently to show that thermal convective flow will affect the structure of ca~tin~s.~~-~~ The rate of heat transfer (conduction plus convection) in a given fluid system is a function of the temperature difference between the hot end of the liquid and the s/l interface and the height of the interface. At the lowest values of these variables* all heat is *It has been shown&apos; that adverse temperature gradients as low as O.OOS°C oer cm are sufficient to cause convection. transferred by conduction. When the temperature difference or interface height are increased, laminar fluid flow commences and heat transport takes place by laminar convection as well as by conduction; turbulent heat transfer takes place at higher values of these variables. In the transition region between laminar and turbulent flow, boundary layer separation takes place; fluctuations in temperature are also noted and increase in amplitude and frequency as turbulence becomes dominant. In this paper, fluid flow patterns in the melt ahead of a stationary interface are deduced from observations of temperature distribution and fluctuations, heat flow rate, and interface shape. The fluid flow ahead of advancing interfaces and the effect of such flow on solute incorporation may be inferred from these measurements on stationary interfaces. Observations during enforced fluid motion will also be considered. EXPERIMENTAL PROCEDURE The metal was contained in a lava boat 10 cm in length, 1+ cm in width, and 2 cm in height, as shown in Fig. 1. A water-cooled, molybdenum block heat-sink is at one end of the boat; surrounding this assembly is a slotted stainless-steel tube noninductively wound with a nichrome heating element. Temperature was measured by 38-gage Chrome1 vs Alumel thermocouples sheathed in 0.05-cm-diam graphite-coated stainless-steel tubing, which were moved longitudinally and vertically through the melt by means of a two-dimensional motorized micrometer stage. In some experiments the thermocouple junction was exposed, but in the majority of experiments the junction was welded to the sheath tip; no significant difference

Jan 1, 1968

By Harold R. Larson, John F. Elliott

The standard free energies of formation of several nzetallic sulfides have been measured by a reversible electromotive-force cell employing stabilized zir-conia as the electrolyte. The oxygen potential at the cathode was fixed by the use of pure oxygen gas at 1 atm. It was established at the anode by bringing to equilibrium the reaction between the sulfide and oxide species present. Thus, Gf: for the sulfide could be obtained from the cell potential and the standard free energies of formation of the oxides participating in the reaction. The results in calories per cam rnole for the temperature range 850" to 1100°C are: Use of the reversible electromotive-force cell having an oxide-ion electrolyte to obtain the standard free energies of formation of some of the more stable metallic sulfides offers a convenient experimental method that is very productive. It also avoids some of the problems inherent in the experimental methods&apos; for such studies which rely on precise determination of gas compositions, particularly if these compositions lie near the limits of our capabilities for accurate chemical analyses. The reaction equilibrium between the lowest sulfide of a metal, SO2 at a fixed pressure, and an oxide of the metal has a characteristic oxygen potential. For example: and for metals whose lowest sulfide is much more stable than the oxides of the metal, the equivalent reaction might be:

Jan 1, 1968

By John E. Murphy, Ernest L. Ohle

Hematite-magnetite ore bodies at Iron Mountain, Missouri, have produced nearly 9 million tons of iron ore concentrates since 1844. The ore minerals occur principally as open-space filling in fractured and brecciated andesite porphyry with very minor replacement of the wall rocks. The enclosing rocks are Precambrian in age and consist of a series of dacite, rhyolite, and andesite flows aggregating about 2000 feet in thickness. All of the ore is in andesite and the mineralization is Precambrian in age. The shape of the ore bodies, the breccia character of the ore, and the gangue mineralogy are believed to be unique. One of the two main ore bodies is crudely dome-shaped with a tendency for development of concentric mineralized shells; the other is an elongated lense in plan but hook-shaped in cross section. Both have strong linear elements striking northeast, east-west, or northwest. Various modes of origin for the structures and for the tension breccias have been suggested, but none is completely satisfactory. Hematite is the main ore mineral; magnetite is subordinate. Important gangue minerals are andradite, quartz, calcite, actinolite, apatite, epidote, and chlorite. Although some evidence favors injection of an iron-rich melt, other evidence suggests ore formation by a high temperature, water-rich solution.

Jan 1, 1968

By Gerhard Derge

The rapidity of oxygen steelmaking has created renewed interesl in the mechanisms and kinetics of the various processes involved. These studies can now be approached with increased confidence because of the more adequate thermodynamics, physical chernislry, and relevant engineering infornzation available. These combine to offer promise of useful control and automation if the details of each specific problem can be sufficiently well-defined. The hot filament microscope provides new insig-hi into many of these problems by direct observation at temperature, allowing the appraisal of the relative importance of thermal gradients, convection, and intermediate phases. All of these have a direct bearing on the overall rates and control of most pyrometallurgical processes. It is one of the special privileges of the Howe Lecturer to become better acquainted with this distinguished man. All of us interested in the metallurgy of iron and steel have developed some sense of his widespread influence by the annual reference to his work in these Memorial Lectures. Each lecturer since 1923 has been able to identify his personal specialty with the broad interests of Professor Howe. This has become even more rewarding with the background information from Professor Gensamer&apos;s monograph, "Henry Marion Howe&apos;s Contributions to Metallurgy, which brings out his happy combination of intellectual and professional activities. Beyond this, I found my personal bond with Professor Howe in his book on The Metallurgy of Sleel first published in 1891.&apos; After a detailed discussion of the dephosphorizing action of slags, he relates the mineral species identified in the frozen sample to the chemistry of the fused slag with the question, "Is it not most philosophic to hold that these independent entities were wholly integrated in the initial magma; that their presence in it was wholly

Jan 1, 1968

By R. T. Hukki

The purpose of this paper is to present an analysis of the unit operation of grinding and the circulating load, of the unit operation of classification and the circulating load, and of the two superimposed into one operation to clarify the overall trend of events relating the circulating load to the capacity of the closed circuit grinding system, to the specific surface area of the final fine product, and to the energy consumption in the closed circuit grinding process. The capacity of the closed circuit is frequently, if not always, determined by the classifier, not by the mill." With these words a startling idea was expressed in 1934 by Dorr and Anable.1 Today, some 30 years later, grinding in closed circuit is universally accepted. The basic curve presenting the capacity factor versus circulating load by Dorr and Anable has obviously been so convincing that not a single authoritative investigation regarding its validity seems to have been conducted. The only major subject of discussion appears to have been the relative merits of the &apos;high&apos; and &apos;low&apos; circulating loads. It seems to be universally agreed that much still remains to be hoped for regarding sharpness of classification. BASIC CURVES FOR CONSTANT MILL LOADING Fig. 1 presents a series of basic curves for constant mill loadings in function of new feed rate and circulating load. The mill loading indicated by each curve is the sum of hourly tonnages of new feed and circulating load. For example, at point 0 where the new feed rate is 100 t/h and the circulating load 300%, or 300 t/h, the mill loading is 400 t/h. In closed circuit grinding, the new feed rate corresponds to the rate of finished classified material produced. Although at this stage the effect of classification is excluded in construction of the basic curves, the trend indicated by these curves is strongly in favor of closed circuit operation under relatively small circulating loads. A study of the curves reveals that, e.g., a mill operating under a load of 200 t/h at point P where the new feed rate is 50 t/h and the circulating load 300% will also operate under the same total load at point Q where the new feed rate is 100 t/h and the circulating load 100%. In other words, a reduction of circulating load from 300% to 100% would lead to doubling of the new feed rate and doubling of the rate of production of finished material, without a change in the total mill loading. The obvious question is, is it also possible by a reduction of the circulating load in a closed industrial grinding circuit to increase the production of finished classified material and, if so, how and to what extent? GRINDING TESTS BY DORR AND ANABLE In a series of open circuit grinding tests reported by Dorr and Anable1 limestone was ground at various feed rates in a 3-ft ball mill. The original data are reproduced in Table I. It can be seen that with the increased feed rate production of -65-mesh material increased and the energy consumption per unit weight of the -65-mesh product decreased in the reverse ratio. The data shown in Table I have been reproduced for our purposes in Table II for a scale corresponding to grinding in a large industrial mill. This reproduction

Jan 1, 1968

By J. M. Steininger

The mechanism of flotation of sphalerite with sulthydryl compounds of different acidities has been interpreted in terms of chemisorption of unionized collector molecules on hydroxylated zinc surface sites. At a constant collector concentration of 1.5 x 10 -4 M, the upper pH limit of flotation has been found to be directly and closely related to the negative logarithm of the collector acidity constant, pKa The experimental results indicate that flotation is prevented when about 95% of the collector is ionized. At low pH, collector adsorption decreases because of the reduction in number of hydroxylated zinc surface sites. These two effects explain why sphalerite does not float with the more acidic sulfhydryl compounds. Typical anionic collectors for sulfide minerals are short chain xanthates or dithiophosphates which are nearly completely ionized in the generally alka- line flotation circuits.1,2 Flotation mechanisms have therefore been usually interpreted in terms of ionic collector adsorption and competition with ionic depressants of the same sign as the collector. A few attempts have been made, however, to consider adsorption of neutral collector molecules. Contact angle measurements obtained by Wark and cox3 have been interpreted by Cook and Nixon4 as representing adsorption of the free acid molecules on sulfide minerals such as pyrite, galena, chalcopyrite, and sphalerite. Cook and Nixon tried to show that the free acid concentration of the collector was substantially constant along the curves relating collector addition and minimum pH for bubble adherence. However, in a review of the subject,5 Sutherland presented new data on the flotation of pyrite with mercaptobenzothiazole which did not support the hypothesis of constant concentration of either collector ions or collector free molecules. He further showed that, with the assumption of constant occupation of surface sites, both theories lead to relations between pH and collector addition having similar mathematical expressions. In fact, with the more likely assumption of variable occupation of surface sites which results in more complex relationships, it appears impossible to

Jan 1, 1968

By P. L. Weston, S. E. Khalafalla

A systematic study was made by the Bureau of Mines on the effect of so me hypothesized accelerators for the process of wustite reduction in carbon monoxide. When small concentrations of promoter materials in the order of 0.69 at. pct were added to the reducible charge, the rate of reduction to iron was increased. Promotion phenomenon prediction was made in light of a suyface reduction mechanism with the aid of Vol&apos;kenshtein&apos;s effect regarding the propagation of crystal lattice disturbances by small amounts of relatively larger interstitial ions. The acceleration produced by a typical promotor, such as potassiunl, increases with protnoter concentration up to a maximum, beyond which the reduction rate decreases. Concentration for maximum promotion depends on the nature and physicochemical properties of the promoter. The extent of reduction rate enhancement is found to be directly proportional to the atomic volume and electronic charge of the additive. DESPITE the enormous volume of literature on iron oxide reduction, very little is reported concerning additive or impurity effects on this important metallurgical process. The beneficial effect bf calcium compound additions on the reducibility of iron oxide sinters has been reported by Tigerschiold,1 vor dem Esche,2 and Edstrom. Doi and Kasai~ found that the addition of lime or limestone to iron ores helps to break up any unreducible compounds, such as fayalite or ilmen-ite. and thus free the combined iron for reduction. Schenck et al. 5 suggested that the increased reduction rate obtained when adding lime could be accounted for by the instability of wustite in the presence of lime. Acid-base slagging reactions resulted in wustite disproportionation according to The dicalcium ferrite formed will yield iron and calcium oxide during reduction. Regenerated calcium oxide dissociates more wustite. This mechanism has been used by Seths and white7 to explain their experimental results. Recently, Strangway and ROSS&apos; attributed the calcium carbonate acceleration of iron oxide agglomerate reduction to increased porosity, both initial as well as that developed during reduction. Aside from calcium carbonate, or oxide, no other promoter was noted in the literature, except for a brief mention by Barrett and woodg on the effect of sodium carbonate and aluminate as activators for the hydrogen reduction of magnetite at 600°C. The present investigation systematically studied a host of other promoters, including calcium and sodium, in an attempt to elucidate the mechanism by which promotion takes place and to fit the results into a simple chemical model. To attain this goal, the effect of promoter physical properties, such as atomic volume, electronic charge, and concentration are related to wustite reduction kinetics in this paper. Wustite reduction to iron, rather than the overall hematite reduction, was chosen since this reaction is known to be the slowest, and hence the rate-deter mining step for the overall iron oxide reduction process. EXPERIMENTAL PROCEDURE Raw Materials and Their Preparation. The pure or impregnated wustite pellets were prepared from minus 400-mesh chemically pure hematite powders. A known weight of hematite was thoroughly and uniformly mixed with a calculated weight of the additive. The mixed paste containing 35 wt pct water was gradually heated from 400" to 1200° C and fired at 1200°C for approximately 4 hr in an air atmosphere. After cooling, the sinter was pulverized to minus 100 mesh and pelletized into minus 4- plus 5-mesh spheres. Pellets were fired, similarly to the paste mix, air-cooled, sized, and stored. An appropriate weight of the charge (20 g) was placed in a zirconia reduction tube maintaining a uniform oxide bed height of 1 cm and a cross section of 7.1 sq cm for all of the test runs. The samples were supported in the vertical reaction tube by a bed of fragmented insulating firebrick plus 3- to 6-mesh alumina beads. The hematite was then transformed to wustite by reduction with a 30 pct CO2-70 pct CO gas mixture at 1000°C in a globar furnace. Complete conversion to wustite was ascertained by a continuous infrared gas analyzer recording the CO-CO2 content of the effluent gas until no carbon monoxide was absorbed from the inlet gas, and inlet-outlet gas analysis remained constant for 30 min. The wustite sample was then reduced with 100 pct CO at 100WC. From the recorded data, an initial rate of reduction was determined by the initial slope of the graph percent reduction vs time. In order to estimate the accuracy of the data, five separate determinations of the reduction curve of pure wustite, under otherwise identical conditions, were performed. The maximum deviation from the average reduction at 14 min amounted to 2 2 pct reduction. This deviation corresponds to 3.8 pct variation based on the percent reduction of the sample. Aiiy impurity effect below the limits of this maximum deviation was considered a spurious result. If the effect exceeded + 4 pct, then it was considered as a positive one. Considerable care was exercised in determining the initial rate from the slope of the initial segments of the curve. Each reduction curve was examined separately on large graph paper and the best tangent to the curve at zero time was drawn. The slope of this tangent was taken as a measure of the initial fractional reduction per minute. Although the time required to reach 50 pct reduction may be of special practical significance, initial rate measurements are invaluable in fundamental studies. These rates provide a measure of the process kinetics on the initial

Jan 1, 1968

By P. Nyul, S. Caplan, M. F. Lamorte, T. Gonda

Therrnal resistance is measured on GaAs laser diodes in the temperature range 77" to 300°K. These data show that typically the thermal resistance increases fifteen times from 77 to 300°K. The increase is attributed to the decrease in thermal conductivity of Gds. Nornzalized thermal-resistance experimental and calculated from published thermal-conductivity data) values are compared and good agreement shown. In many practical applications, it is desirable to obtain high average power output from laser diodes. Average power output is determined in large measure by the external efficiency and thermal resistance of the diode.&apos;-3 The average input power with which a laser diode may be pumped is dependent on the thermal resistance. Thermal resistance has been studied over the temperature range from 77" to 300°K which is usually of interest in practical applications. This correspondence presents data on thermal resistance for GaAs laser diodes and compares them to values calculated from thermal-conductivity data. Junction heating arises from three distinct components: 1) joule heating, 2) nonradiative recombinations, and 3) reabsorption of radiation. In high-threshold lasers, joule heating predominates.4 Typically, the nonradiative recombination is not negligible and contributes significantly to junction heating. The loss caused by reabsorption may be of the order of the joule-heating loss.&apos; The fabrication and the geometry of laser diodes have been described in other publications.5 The data presented were obtained from diodes which were fabricated from the same region of a wafer to minimize differences. Fig. 1 shows four types of heat sinks employed in this study. In types 1 and 2, the laser cavities are alloyed; pressure contacts are employed in types 3 and 4, and indium is plated on the inside faces to improve the intimacy of contact between the diode and the heat sink. The thermal resistance R is defined by the following relationship: where AT is the junction-temperature rise above the heat-sink temperature for the diode power dissipation Pd. For measurement of thermal resistance, a direct current is passed through the junction, in the range from 1 to 50 pct of threshold. The diode is placed in the laser mode by superimposing a current pulse of low-duty cycle on the direct current.3 Junction-temperature rise is obtained from the time-resolved laser spectrum at the leading edge of the current pulse.&apos; Typically, the laser line shift is 2.5A per OK. The resolution employed in these experiments is 0.5A; therefore, the accuracy in the temperature measurement is 0.2K. Typically, the temperature rise is 2" to 20°K. The power dissipation is the difference between the dc power input, and the radiation power exiting the diode. The measurement accuracy is less than 1

Jan 1, 1968

By Arthur R. Still, Paul Gilmour

The ore deposit of the Iron King mine occurs in a group of steeply-dipping metamorphosed eugeosynclinal volcanic and sedimentary rocks of Precambrian age. Within this sequence, the ore deposit lies at the contact of a unit made up of rhyolitic tuff and interbedded andesite and a structurally underlying series consisting of andesitic tuffs, minor rhyolitic tuffs, and argillaceous sediments. Field evidence suggests that these rocks have been overturned. The ore deposit is made up of a series of overlapping, conformable or bodies consisting of massive pyrite and associated lenses of massive quartz. These contain recoverable amounts of gold, silver, lead, zinc, and copper. A parallel zone of copper mineralization occurs within the hanging-wall rocks. The deposit is considered to belong to a large and important group characterized by mineralogical composition and the lithology and structural type of the host rocks. Evidence regarding the origin of the deposit is reviewed, and it is concluded that the ore bodies were formed through the agency of volcanic hot springs on, or near, a submarine surface of deposition

Jan 1, 1968

By R. J. Wagner, G. H. Gronhovd, A. J. Wittmier

The paper describes the results of a series of full-scale boiler tests run to determine the ash fouling characteristics of a North Dakota lignite as a function of sodium content of the coal. Four levels of sodium were investigated and rate of fouling was determined both by boiler performance and by specially constructed probe equipment. Discussed is information on chemical and physical properties of the ash deposits. The vast lignite deposits in North Dakota are becoming increasingly important as a source of low-cost fuel for power generation. A new 200-megawatt lignite-burning plant located near Stanton, N.D., was placed in operation early in 1966. Another 172-mega-watt unit in the same area is scheduled for operation late in 1966, and plans have recently been announced for a 212-megawatt unit to be in operation by 1970. If these plants show good performance, western North Dakota could become a major power production center for a large geographic area in the upper midwest. One of the problems associated with the use of lignite in power boilers is its tendency to form troublesome ash deposits on boiler tube surfaces. This problem varies considerably from one lignite-fired boiler to another and is dependent upon such factors as source of lignite, boiler design, load factor, tube metal temperatures, and soot-blowing practices. This report presents data on sodium content* variation in a North Dakota mine, describes the results of a series of tests performed to determine the relationship between ash fouling tendencies and the sodium content, and tells how the mining company and electric utility have coordinated their operations to reduce the ash fouling problem. GENERAL BACKGROUND Until recent years it was generally assumed that North Dakota lignite from a given mine had qualities peculiar to that mine, but that within the mine, the lignite was quite uniform. In 1959, the Otter Tail Power Co. installed a 53.5-megawatt lignite-burning unit at its Hoot Lake plant, Fergus Falls, Minn. Shortly after the unit was put into operation, it was noted that at certain times under high load conditions, ash fouling problems were quite severe, but not consistent or predictable. Each time fouling occurred in the unit the position of the loading shovel at the mine was noted. Within two years it became apparent that there were certain areas in the Knife River Coal Mining Co. mine at Beulah, N.D., where the lignite apparently had a high fouling tendency for the Hoot Lake unit. Results from analyses of the coal did not show large differences in moisture percentage, ash percentage, heating value, or ash fusion temperature between the highly troublesome and less troublesome coals. After three years of operation, the troublesome areas had been quite well defined and the mining company started a procedure of bypassing these areas when load conditions at the plant were high and then returning to the troublesome areas to load the lignite during the summer months when peak loads were lower. It was noted that the lignite from the areas which caused severe fouling under high load conditions produced much less fouling at the lower summer loads. However, bypassing certain areas in the strip pit caused the mining company to disrupt their continuous loading schedule, which in turn upset their continuous stripping schedule and made for less efficient mining operation. Meanwhile, at the Hoot Lake plant, the number of soot blowers on No. 2 boiler had been increased from 30 to 55, and a very rigorous blowing schedule had been adopted resulting in soot blowers operating at least some part of 21 hrs per day. Fouling problems continued, with a resulting reduction in plant economy and reliability. During this period the Federal Bureau of Mines Coal Research Laboratory at Grand Forks, N.D., had initiated various research programs relating to the study of lignite ash and ash fouling problems. One project was a survey in which full seam samples were obtained from various locations in all the major

Jan 1, 1968

By H. Pew, J. H. Field

To alleviate pollution more restrictive legislation is being enacted, either limiting emission of pollutants or the type of fuel that can be utilized. The nature and magnitude of air pollution problems affecting the mining, preparation, coking and combustion of coal are described. Methods for combatting particulate emissions by use of mechanical separators and electrostatic pre-cipitors are discussed. Proposed methods to meet the problem of gaseous emissions currently receiving considerable attention are described, with special emphasis on methods to decrease pollution by sulfur oxides. Concern about air pollution goes back several centuries, but until very recently most effort has been aimed at coal smoke and other visible pollutants. The classic example of a &apos;successful&apos; campaign for smoke abatement and control is the fruitful combined effort of the city of Pittsburgh and its surrounding Allegheny County, which eventually led to the reconstruction of downtown Pittsburgh at an estimated cost of one billion dollars. Historically, the city&apos;s downtown Golden Triangle district had been afflicted by pollutants evolving from steel mills, from a variety of other industries, and from railroad locomotives. Efforts to alleviate the situation prior to 1943 were virtually ineffective. In 1945, however, a comprehensive redevelopment plan was prepared and backed by state authority. Within a few years a clean, modern metropolis has evolved where once stood America&apos;s famous &apos;smoky city.&apos; But the victory in Pittsburgh, as in various other American cities, has not solved the national problem. Current estimates indicate that 133 million tons annually of air pollutants from all sources still are emitted annually into the atmosphere above the United States. About 10% of this annual effluent is particulate matter so that most of the remaining pollution problems will be solved only when other effluents are reduced. Essentially, these are sulfur oxides, nitro- gen oxides, hydrocarbons, and carbon monoxide. Over the years, both states and local communities have tended to increase the restrictions on smoke and fly ash — problems mostly of concern in the combustion of coal. Prior to the middle 1950&apos;s, ordinances sometimes permitted emissions of smoke equivalent to as much as No. 3 on the Ringlemann scale. Since 1956, no ordinance has been passed which allows smoke of greater than No. 2. Under today&apos;s conditions of improved fuels, equipment and practice, a few communities have passed laws prohibiting emission of smoke of any density darker than Ringlemann No. 1. The majority of existing laws on fly ash emission in the U.S. limit emissions equivalent to 0.85 lb of fly ash per 1000 Ib of flue gas. In recent years, however, regulations which have been adopted give cognizance to the higher level of performance now obtainable with improved equipment. A comparison of the restrictions of five codes adopted since 1960 is given in Table I. The most stringent of these is the one for New York City which provides for a maximum emission of 0.6 lb fly ash per million Btu heat release (equivalent to roughly 0.51 lb/1000 lb of flue gas). The first comprehensive effort to restrict the emission of SO2 resulted from the passage of a 1937 law in St. Louis. This regulation stipulated that coal containing in excess of 23% volatile matter and 2% sulfur must be washed, thereby presumably producing some effective reduction in the input sulfur content. This was followed in 1949 by a Los Angeles County law which prohibited the emission of SO2 in concentrations greater than 0.2%. Most SO2-restrictive legislation passed since that date has been based on this limiting 0.2% SO2 by volume, although modifications are occasionally permitted under selected conditions, sometimes based on the fact that certain limiting ground concentrations are not exceeded — such as in the rules adopted by the San Francisco Bay area. To date, no legislation has been passed in the U.S. to limit the generation of nitrogen oxides from the combustion of fossil fuels. However, such oxides are considered to be of potential importance in air pollution control because of their possible detrimental effects on health and their reported role in the formation of photochemical smog. Interest in reducing oxides of nitrogen from powerplant and auto exhausts is increasing and regulations limiting their quantity can be expected in the future.

Jan 1, 1968