By J. S. Kirkaldy, R. C. Dorward

The solubilities of copper and gold in silicon and germanium have been determined by equilibration of the solid semiconductors with coexisting liquidus phases. The experimental results were combined with estimated activity coefficients of the liquidus alloys to determine the following partial molar enthalpies and excess entropies of solution for the systems: Solubility measurements were also carried out below the eutectic temperature of the copper-silicon system. The partial molar enthalpy and excess entropy of copper in silicon with respect to Cu3Si were determined to be 40.2 ±0.5 kcal per mole and 9.7 i 0.5 cal per mole — OK, respectively. It has been dentonstrated that nu-cleation and growth of intermediate compounds are retarded in copper-silicon diffusion couples. This points out the dangers of determining equilibrium solubilities by dijjusion methods. THE thermodynamic requirement for equilibrium between contiguous phases at constant pressure and temperature is that the chemical potential of each component be constant throughout the system. Equating expressions for the chemical potential of solute, component 2 say, in two phases, alpha and beta, gives

Jan 1, 1969

By P. B. Mee

The secondary re crystallization behavior of two vacuum-melted, nominally 3 pct Si-Fe alloys has been studied, one alloy being produced from pure electrolytic iron and semiconductor-grade silicon and the other from commercial-purity hot band. The vacuum-melted and vacuum-remelted alloys were found to develop {110}(hhl) and {lll)(hkl), respectively, on annealing in high vacuum and {100}(0kl) and {11l}(hkl), respectively on annealing in pure hydrogen of dew point, < — 60°C. H2S doping of the hydrogen or annealing in commercial argon was found to effect a reversal for the vacuum-remelted alloy from (111) to (100) secondary recrys-tallization, while prolonged vacuum annealing at 2 x 10-6 Tow resulted in a tertiary re crystallization from (111} to (110). The growth selection of the {lll}(hkl) component was found to be governed predominantly by the {111}/planar misorientation, the maximum deviation of the resulting secondaries being 5 deg. It is considered that the driving force for {111}(hkl) secondary recrystallization arises from the preferential lowering of ?111, possibly by phosphorus or nitrogen diffusion, just as oxygen and sulfur under certain conditions have been found to preferentially lower ?100. When heavily cold-rolled metals are annealed at high temperatures, primary recrystallization usually occurs rapidly and may be followed by considerable grain growth. However, in the presence of a fine dispersion of inclusions1"3 or with a strong matrix preferred orientation4&apos;&apos; the matrix may be stabilized and a secondary recrystallization may then be effected. Also, in vacuum-melted Si-Fe it has been shown possible to develop {100}(001) and {110}(001)6 surface energy driven secondary recrystallization textures. Further, it has been found that, on annealing very pure metals, grain growth normally ceases when a grain size approximately twice the strip thickness is acquired, due to the formation of V-shaped thermal grooves which result in an equilibrium being set up between surface and grain boundary stresses. If, however, a surface energy difference ??s, exists between adjacent grains (of the order of a few percent of the grain boundary energy ?b), then according to Mullins8 a secondary recrystallization may be effected, since the grains having lowest ?s would grow at the expense of their higher-energy neighbors. For clean bee metal surfaces ?110 should be lowest; however, for 3 pct Fe-Si (100) secondary structures have frequently been developed and have been attributed by Walter and Dunn9 to an alteration of the relative surface energies due to the preferential chemisorption of oxygen on (100) planes. Kohler,10 however, indicated that this reversal may be achieved by employing minute quantities of highly polar compounds in the annealing atmosphere, i.e., sulfur compounds, in par- ticular H2S being beneficial in (100) growth. This work has been verified by Kramer" using {100)/{110} bicrystals, while Mager12 demonstrated the importance of sulfur diffusion within the strip. Detert13 has intimated that carbon may be responsible for the preferential lowering of ?110 although no direct evidence has appeared yet to support this supposition. It must , be appreciated that the above-mentioned examples of surface energy driven secondary recrystallization were obtained with very pure vacuum-melted materials with oxygen contents (which is now known to be a critical factor") less than 35 ppm. During the course of a textural study on Si-Fe it has been found that under certain conditions (111) secondary recrystallization can be obtained by what is believed to be a surface energy growth selection mechanism. The purpose of the present paper is to briefly describe this result and to try and postulate the possible causes. EXPERIMENTAL Two vacuum-induction-melted, nominally 3 pct Si-Fe alloys were produced, one from pure electrolytic iron and semiconductor-grade silicon designated A and the other from commercial-purity hot band, designated B.

Jan 1, 1969

By R. N. Stevens

Any consideration of the errors involved in determination of ?gb by previous workers should discuss their experimental methods in terms of the appropriate theoretical equation; this the authors have not done in a number of cases. To facilitate the present

Jan 1, 1969

By Roy T. Southin*

The finding of Wojciechowski and Chalmers that columnar crystal growth can be stopped by an already existing network of equiaxed crystals is supported by other recently reported work on both static and mechanically stirred ingots.27,28 Support for the dendrite arm fragmentation mechanism, too, can be obtained by comparing the effects of spinning on ingots cast in a material which has a dendritic solid/liquid interface during solidification with one which has a cellular interface, since no evidence of change at the interface, other than a change in growth direction, can be found in the cellular material. But there are alternative ways of producing an equiaxed zone in materials which characteristically solidify with a cellular interface. For example, interrupted spinning of a normally cast ingot can do it. In this case it has been shown28 that the equiaxed zone is caused by the showing of dendritic particles from the top surface of the ingot to nucleate a network of equiaxed crystals which forms a barrier to the continued growth of the columnar grains. This showering has also been shown to be a major effect in materials solidifying with dendritic interfaces. It has also been proposed28,29 that, for an equiaxed zone to form, not only must nuclei be present ahead of the interface but also these nuclei must grow to sufficient size to be a barrier to the further growth of the columnar grains. A further requirement is that a network of these grains continually be produced ahead of the growing interface; otherwise there is a reversion to columnar growth as found by Wojciechowski and Chalmers. In normally cast ingots it is possible for nuclei ahead of the interface to grow since during a large portion of the solidification time there is no temperature gradient ahead of the interface,30 and, in fact, the liquid may be slightly undercooled.29 This then is the major difference between the work under discussion and normal industrial solidification conditions, since Wojciechowski and Chalmers imposed a considerable temperature gradient in the liquid. The statement in the Wojcieshowski and Chalmers paper that one needs to lower the temperature gradient

Jan 1, 1969

By O. G. Paasche, Yuan-Shou Shen

THERE is a disagreement among the various authors about the exact manner of transformation of ZrCr2. Rostokerl and others2 stated that ZrCr2 had a C-14 (MgZn2) type of structure below 1000°C and a C-15 (MgCu2) type of structure at temperatures above 1000°C. Alisova3 and others4 reached the opposite conclusion and stated that the transformation temperature is close to the melting point of ZrCr2. A literature survey shows that various investigators3&apos;= who homogenized the specimens at a temperature higher than 1000°C have concluded that ZrCr2 had the C-15 structure at room temperature. Meanwhile, Jordan et al.4 reached similar conclusions without annealing the specimen. Other investigators1,2,6,7 who X-rayed the specimens in the as-cast condition without annealing reached different conclusions. The investigation reported herein was conducted with the aim of exploring the exact manner of transformation of ZrCr2 by various heat treatment tests. The alloys for this examination were prepared from iodide-reduced zirconium crystal bars, 99.9 pct purity, and electrolytic chromium, 99.9 pct purity. They were melted in a nonconsumable electrode arc furnace with water-cooled copper crucible in a helium atmosphere. The melting loss of each alloy was less than 1.5 pct by weight. Chemical analysis of a randomly selected specimen indicated that there was a very close agreement between calculated and analyzed compositions. Before being heat-treated each specimen was encapsulated in a vycor or quartz tube inside which an argon atmosphere was maintained at a pressure of lower than 1 atm. In determining the crystal structure of each specimen with a Debye-Scherrer camera, the standard procedure8 for X-ray quality analysis (Hanawalt method) was followed. The different series of heat treatment tests in this investigation are tabulated in Tables I and 11. The tests in Series I, specimens from 1-1 to 1-9, which were similar to Rostoker&apos;s experiment1 indicated that the transformation temperature seemed to fall between 870° and 900°C and that the crystal structure of ZrCr2 at lower temperature seemed to be of the C-14 type. However, once the compound is transformed to C-15 type, it is impossible to reverse the transformation back to the C-14 type by first heating the specimen above 900°C and then annealing it slowly below 900°C as shown in Experiments II-1 to II-3. Thus, it appears that the specimen of ZrCr2 will transform from C-14 to C-15 structure when heated above 900°C but will not transform from C-15 to C-14 when annealed slowly passing 900° C even after the extremely slow cooling process such as indicated in the experiment of Specimen II-3. As a valid transformation temperature is a temperature at which the transformation is reversible, therefore the temperature 900°C (or other temperature close to 900°C) is not the transformation temperature for ZrCr2 and the C-14 structure is not the stable structure of ZrCr2 at lower temperatures. The C-14 structure is retained at room temperature because the transformation to C-15 structure is very sluggish and the fast cooling after melting does not allow enough time for the transformation to take place. Additional energy is required to alter the metastable condition of the C-14 structure. The sluggishness of this transformation was again demonstrated through another series of experiments. Four specimens with C-14 structure were taken. Then they were annealed at 900°C but each specimen was soaked for a different period of time, Table 11. X-ray diffraction patterns of this group indicated that the C-14 structure gradually disappeared as the soaking period was lengthened. The figures listed under the column "C-14 Structure, pct" were estimated from the intensity of the d = 2.330 line of the diffraction pattern corresponding to the structure. Notice that the intensity of this line became weaker for longer soaking periods. To determine the transformation temperature of ZrCr2, specimens with C-14 structure (as-cast condition) were annealed at 1300°, 1400°, 1500°, 1550°, and 1600°C, respectively. A final specimen was first heat-treated to 1500°C in order to transform it to C-15 structure, then heat-treated at 1600°C again. From the X-ray analyses of this series of tests, Specimen Nos. III-1 to III-6, it is evident that a transition from C-15 structure at lower temperatures to the C-14 structure occurs at some temperature between 1550° and 1600°C.

Jan 1, 1969

By A. F. Crawley

THIS paper describes part of a series of density measurements on low melting point metals being undertaken at the Mines Branch, Department of Energy, Mines and Resources, Ottawa, Canada. This program has received support from the Canadian Zinc and Lead Research Committee and the International Lead and Zinc Research Organization. Examples of the type of work being done have already been given in earlier papers&apos; , which deal with the densities of lead, tin, and some of their alloys. Densities were measured using a graphite pyc-nometer by a technique which has already been described." The cadmium and indium, supplied by the Consolidated Mining and Smelting Co. of Canada were of 99.999 pct purity. Density determinations on indium, as for lead and tin,1,2 were made under a vacuum of about 5 x 10-6 torr because the oxidation and vaporization characteristics of the metal do not create experimental difficulties. This contrasts markedly with cadmium which, even at the relatively low temperatures of our experiments, has a high vapor pressure and a strong oxidation potential. To suppress the harmful effects of these properties, determinations on cadmium were made with success under an atmosphere of argon, the technique having been previously established in this laboratory for measurements on zinc.3 The densities of cadmium and indium are listed in Table I and plotted in Figs. 1 and 2. From the graphs, it is readily observed that the densities of both metals vary linearly with temperature. This relationship expressed mathematically is of the form:

Jan 1, 1969

By S. Nenno, T. Saburi, Y. Mizutani, M. Yomarnoto, K. Komatsu

In the equilibrium phase diagram of the Ni-Mo sys-tem1,2 available at present, intermetallic compounds (or ordered phases)ß(Ni4Mo) and ?(Ni3Mo) are known to exist to the nickel rich side. In our recent investigations on Ni-Mo alloys, however, it has been found that the quenched alloys from the high temperature region containing more molybdenum than the Ni4Mo do not decompose directly into 0 and when annealed isothermally below the peritectoid temperature, i.e., 865°C. This note is to report the existence of Pt2Mo type superlattice (possibly ordered Ni2Mo) as a metastable phase in the early stage of decomposition. Alloys containing 20.1, 22.7, and 24.4 at. pct Mo were prepared by vacuum-melting electrolytic nickel of 99.9 pct purity and molybdenum powder of 99.9 pct purity in an alumina crucible. From the resulting ingots, sheets 0.3 mm thick were obtained by forging, hot-, and cold-rolling. The sheet specimens were water-quenched from ! region and subsequently annealed for various periods of time at temperatures below the peritectoid temperature. On these specimens were made optical-microscopic and transmis-sion-electron-microscopic observations. Fig. 1- Optical micrograph of the 22.7 at. pct Mo specimen annealed for 100 hr at 700°C after quenching. (ß + ?) region, B, nucleated along a grain boundaries are invading the preexisting (ß + Ni2Mo) region, A. Details of A are observable only by electron microscopy. Etchant: 60 pct HNO3-40 pct CH3COOH.

Jan 1, 1970

By S. P. Ray, B. D. Sharma

THE activation energy values for self-diffusion in pure metals have been correlated with a number of physical properties such as melting points,1 valences,&apos; Debye temperatures,3 and cohesive energy densities.4 Extending the melting point correlation, the self-diffusion activation energy values for the alloys can be similarly correlated with the solidus temperatures. For metals and alloys which exhibit phase transformations, such a correlation is not feasible because of the uncertainty of various physical properties of the corresponding phases. Using thermodynamical approach, Ardell5 calculated the hypothetical melting points of the low melting phases of the polymorphic metals. However, these calculated melting points do not show reasonable correspondence with the activation energy of self-diffusion. Recently, a new approach treating metals and alloys as electron concentration phases has been developed by Engel6 and Brewer.7 These workers have attempted to correlate the crystal structures with the electron configurations of the atoms existing either in ground state or in an excited state of low promotion energy. The basic postulate of this theory is that whereas the contribution to the bonding of the metal comes from the interaction of both d and (s-p) electrons existing either independently or in hybridized states, the existing crystal structure is controlled by the (s-p) electrons alone. Specifically, a metal is supposed to crystallize in bcc, hcp, or fcc phase provided the metal has one, two, or three valence electrons per atom in the (s-p) configurations. The diamond, or ZnO and ZnS structures, occur with four (s-p) electrons per atom. Secondly, the contribution of d electrons to bonding is supposed to increase with atomic number

Jan 1, 1970

By H. C. Gatos, J. T. A. Pollock, V. Sadagopan

PREVIOUS investigations on the effect of neutron irradiation on the superconducting properties of bulk transition metals indicated that little or no change occurred in poly crystalline disordered materials, particularly if cold-worked prior to irradiation. Only the superconducting properties of ordered intermetal-lic A15 compounds were found to be sensitive to irradiation, and the observed reduction in Tc and increased magnetic hysteresis or critical current densities were attributed to the introduction of flux pinning vacancy clusters and disorder in the lattice. Since the former would also be expected to be present after irradiation in disordered alloys, the general conclusion was that the disordering effect of the irradiation was the primary reason for the changes observed. The present note reports some unusual effects of neutron irradiation on cold worked Nb(Cb)-Ti-V alloys. Specimens with nominal composition as given in Table I were prepared by repeated arc melting, taking the usual precautions, and homogenized at 1000°C for 24 hr prior to a reduction of 15:l by cold rolling. Samples of size 1 by 1 by 25 mm were sliced from the rolled strips. The sarmples chosen for irradiating were sealed in a cadmium tube (wall thickness 1 mm) prior to exposure in a fast neutron flux of 3.7 x 1019 neutrons per sq cm in the swimming pool reactor of Union Carbide Corporation&apos;s Sterling Forest Reactor. During irradiation the temperature of the samples was maintained below 70°C. The irradiated samples were stored at room temperature for approximately 1 year allowing the radiation levels to reach a safe handling value. Tc measurements were made employing a self-inductance coil technique. Jc data at 4.2"Kwere obtained using a four lead resistivity method. The latter measurements were made at the Francis Bitter National Magnet Laboratory by setting the perpendicularly applied field and increasing the direct current through the sample until a potential of about 10-6 v was detected. Tc values for the nonirradiated samples are listed in Table I together with the change in Tc after irradiation. A decrease in Tc of 0.25 or 0.3"K was measured for three of the four samples, the exception being the Nb-30 at. pct V-20 at. pct Ti alloy which showed a decrease of 0.5K. Jc vs applied field data are plotted in Fig. 1 for the Nb-20 at. pct V-30 at. pct Ti alloy. These curves are typical of the four alloys and surprisingly indicate that a degradation occurred in all the samples after irradiation. Hc2 values, obtained by extrapolation to zero current, are 8 to 15 pct lower than those measured for the nonirradiated specimens. The reasons for the degradation of Tc and jc ob-served in the alloys on exposure to neutron irradiation are not immediately apparent. The temperature at which the samples were maintained during bombardment (<70°C) and stored (20°C) make it highly unlikely that any significant change in the dislocation density of the materials through thermally activated migration and annihilation would occur. The explanation must lie in the type of damage produced by the bombardment. McEvoy et a1. reported no change in superconduct-

Jan 1, 1970

By M. C. Flemings, R. Mehrabian

In a recent series of papers,1-3 it was shown that a variety of apparently different types of macrosegrega-tion result from the same basic mechanism, the inter-dendritic flow of solute rich liquid to feed solidification and thermal contractions. The important parameter governing sign and extent of segregation was shown to be (v.?T)/ where v is interdendritic flow velocity, ?T is temperature gradient, and E is rate of temperature change. It was proposed in one of the previous papers that the "negative cone of segregation" often found at the base of large ingots results from the large value of (v. VT)/E expected to pertain there. The reason why this parameter is expected to be large in that location is the high flow velocity to be expected there, as discussed earlier,&apos; and as shown schematically in Fig. 1. In this note, two experiments are summarized which are intended as laboratory simulations of the inter-dendritic flow behavior sketched in Fig. 1 and, therefore, of the "negative cone of segregation". Experimental procedures employed are as described in the the earlier work.3 Alloy cast was nominally Al-4.5 pct Cu. Fig. 2 shows one of these ingots, a "prism" ingot, 6 cm high by 12 cm wide by 10 cm long, unidirectionally solidified from a water cooled base. In this ingot, in-terdendritic flow velocity increases near the upper portion of the ingot because of the gradually decreasing ingot cross-section. Calculations were presented earlier of the negative segregation to be expected in this type of ingot,&apos; and results presented in Figs. 2 and 3 agree closely with those of earlier calculations. A more direct (although less easily calculable) simulation of the "negative cone of segregation" is the

Jan 1, 1970

By David N. French

In a recent paper, Miyoshi, Hara, and sugimotoL have shown that hardness increases and crack resistance decreases with polishing time in tungsten car-bide-cobalt alloys. They attribute the changes in hardness and crack resistance to cold working in these alloys. More recently Exner2 explains the decrease in crack resistance with the amount of material removed (polishing time) by suggesting that polishing removes a high compressive residual surface stress due to the initial grinding operation. He cites previous work on steel to show grinding can induce surface compressive stresses but offers no direct experimental measurements to support this in cemented tungsten carbides. In recent work we have observed changes in residual stress in the W C phase as measured by X-ray diffraction techniques with changes in polishing conditions.3 As a result of the work of Miyoshi et al.,L a brief study was undertaken to investigate the effects of polishing and grinding on the residual stress in the WC phase and have been reported.4 A single composition of tungsten carbide —10 wt pct Co was used. Two initial conditions were studied: an annealed condition with about -30,000 psi residual stress from the differences in thermal coefficients of expansion of WC and cobalt and, on the same specimen, a surface ground with a 150 grit diamond wheel. Stress was measured in the WC phase using X-ray diffractometry as a function of the amount of material removed by metallographic polishing with 6 diamond paste. The results are shown in Fig. 1. Two things are noted, 1) polishing with 6 p diamond paste has little effect on the annealed sample and 2) the magnitude of the grinding stress is markedly reduced as material is removed. By the time 0.1 mil is removed the surface has a metallographic polish satisfactory for light microscopy examination. Thus the surface, even though polished, can still retain most of the stress due to grinding. Since WC is itself slightly ductile, it seems reasonable that high compressive stresses can be generated in the surface by the plastic deformation accompanying grinding. Exner2 suggests, by analogy with steel, that as a result of grinding both WC and cobalt in the

Jan 1, 1970

By J. C. Williams, M. J. Blackburn

MANY aspects of the formation of the metastable w phase in titanium-transition metal alloys have been described in several recent papers.1-4 These papers have reviewed earlier work on the w phase and have further defined most of the important features related to the formation of this phase, e.g-., its crystal structure, composition, and morphology. There are, however, several important points regarding formation of the w phase in titanium alloys which have been described in less detail. Two of these are the relationship between lattice misfit and w phase morphology and the influence of lattice misfit on the mode of formation of the equilibrium a phase. In this communi- cation we will present transmission electron microscopy results relevant to these two points. The alloys used in this study were prepared by non-consumable electrode arc melting, each 30-g button being remelted a minimum of twelve times. The alloy compositions we have studied are listed in Table I. Thin foils were prepared using standard techniques described elsewhere. Two distinct c&apos; phase morphologies have been reported in earlier papers. The phase is ellipsoidal in the Ti-Mo3 and Ti-Nbl system and cubical in the Ti-V3 system. Results of the present study show that the w phase is also cubical in Ti-Mn, Ti-Fe, and Ti-Cr alloys as illustrated in Fig. l(b) to (d). Fig. l(a) shows the ellipsoidal morphology in Ti-MO3 for comparison purposes. It was suggested in an earlier paper3 that the w phase morphology may be controlled by the lat-

Jan 1, 1970

By W. V. Youdelis, W. H. Bear, G. Cochrane

HERETOFORE, there has been very little study of the effects of various metallurgical factors on the behavior of thermoelectric materials, the need for which is evident if optimum processing and design of thermoelectric devices is to be realized. Accordingly, we have undertaken such an investigation on the thermoelectric materials bismuth and Bi-Sb alloy and in this paper present some preliminary results which merit consideration, in particular the relatively high thermoelectric power and figure of merit values obtained for the Bi-12Sb (at. pct) alloy powder compacts. The thermoelectric parameters for ingot and powder compact specimens are determined and the results are compared with published data for single crystals. Preparation of Materials. The bismuth and antimony used in this investigation are six nines pure. Melting and casting of the ingots was carried out in air for expediency, since most oxidation unavoidably occurs during the preparation of the powder by filing of the ingots. Chill cast ingots of pure bismuth were prepared by pouring the melt into split copper chill molds, and unidirectionally solidified ingots of bismuth and Bi-Sb alloy were obtained by slow directional cooling in pyrex tubes. All melts remained bright during melting and casting, indicating minimum oxidation. Powder for the powder compact samples was obtained by filing the ingots with a fine and coarse file to give a variation in the particle size of the compacts. The particles in the fine powder compacts varied in size from approximately 28 pct less than

Jan 1, 1970

By G. R. Belton, Y. K. Rao

A galvanic cell, using liquid MgCl2 or MgC12-CaC12 mixtures as the electrolyte, has been used to determine activities in Mg-A1 liquid alloys between 700&apos; and 880°C. The incovporation of a chlorine electrode in the cell also allowed measurements to be made of the standard free energy of formation of MgCl2(l). The results are shown to be in good agreement with thermo-chetrlical values from the literature, and this is taken as evidence that the small, known solubility of magnesium in iMgCl2 introduces no significant error in galcanic cell measurements. Within experimental error, the activity coefficients and relative partial molar enthalpies at 800°C are shown to be represented by the following "subregular" solution equations: logy~~ =-0.68(1 -xMgj3 log yAL =-1.02(1 - XMf + 0.68(1 - XMf H.M = -4400(1 - %)3 / cal Mg 7Ag&apos; HZ =-6600(1 - xA1)&apos; + 4400(1 - XMf cal SCHNEIDER and toll&apos; have used a transpiration technique to measure the vapor pressures of magnesium over Mg-A1 alloys between 544" and 594°C. amsstad,&apos; however, has since suggested that the extrapolation to zero flow rate, used by these authors in interpreting their apparent pressure vs flow rate data, gives unreliable results. Rogers, Tomlinson, and Richardson,3 in interpreting the results of solution equilibria between Mg-A1 alloys and liquid MgC12, also considered the measurements of Schneider and Stoll to be unreliable and preferred to derive activities for the alloys from the earlier boiling point determinations of ~eit~ebel~ and the partial molar heats recommended by Kubaschewski and ~atterall.~ These latter heats were based substantially on the early calorimetric work of Kawa-kami but, unfortunately, his work on other systems has sometimes been found to be inaccurate.7 Rogers et al., in the above-mentioned paper,3 tentatively concluded that the most likely species responsible for the limited solubility (0.3 mole pct at 800°C) of magnesium in MgC12 were Mg° (neutral) and Mg2++. Two more recent studies8,9 have supported Mg2++ as the soluble species. In the present study, activities in Mg-A1 alloys have been determined by means of a galvanic cell involving liquid MgCl2 or MgC12CaCl, mixtures as the electrolyte. Since the reactive nature of magnesium precluded simple Faraday yield experiments, a chlorine electrode was incorporated in the cell in order that the performance of the cell could be checked by measurements of the heat and free energy of formation of MgC12. This procedure was considered necessary since it has been suggested1&apos; that the solubility of a metal in a molten salt might introduce electronic conductivity; also, previous determinations of the standard electrode potential for MgC12 differed by as much as 70 mv11-13 EXPERIMENTAL Materials. Analyses of the materials used in preparing the alloys and the electrolyte mixtures are presented in Table I. The alloys were prepared by induction melting weighed amounts of the metals in a graphite crucible held under an argon atmosphere. Pure anhydrous magnesium chloride was prepared by heating the mixture MgCl, . 6H20 +NH4C1(1:1) to 650°C, followed by melting under dry argon. The melting point of the dry MgC12 was found by differential thermal analysis to be 714.8oC, which compares well with the accepted value of 714C.14 This agreement was taken to be an indication of the high purity of the dried salt. Table I. Compositions of Materials, wt pn Impurity Mg Al MgCI2 CaCI, Ba - - 0.005 Ca - - 0.010 Cu 0.02 0.02 Fe - 0.10 0.001 0.010 Pb 0.01 - 0.001 0.005 Mn 0.15 0.001 Si - 0.10 Sr - - 0.005 MBSO* - 0.040 ARGON TUNGSTEN CHLORINE LEAD—411 11 II ALUMINA &apos;A I / ave GRAPHITE on irA~_ ( ^"l ROD MAGNESIUM S>ILICA~^ /, OR ALLOY-. I /A] ___________ -«^- _ ELECTROLYTE I y FRITTED DISCS Fig. l—Arrangement of chlorine and metal electrodes in electrolytic cell.

Jan 1, 1970

By A. G. Guy

In a special type of electrodiffusion experiment the entire specimen is at constant temperature. The vacancies are then created at one end of the specimen and flow to the other end where they are destroyed. The energy required to operate the corresponding sources and sinks results in a super saturation of vacancies at one end of the specimen and an under -saturation at the other end. This gradient in vacancy concentration produces a chemical-diffusion flux, J(D), of vacancies in addition to the flux, J(E), caused by the electric current. Using the experimental data of Ch. Herzig,5 it is shown that a super saturation of 1 pct can cause J(D) to be about 25 pct of J(E), and thus account for the anomalous behavior of short specimens. THERE are advantages in a phenomenological treatment as contrasted to an atomistic one. For example, there are many reactions involving the element copper that are quantitatively and usefully understood from a phenomenological viewpoint, even though electron theory is not yet able to predict whether copper should be fcc or cph.&apos; Similarly, the lack of a complete atomic theory of vacancies need not prevent the development of a treatment based on thermodynamics and chemical kinetics. In the following discussion, models will be used for the vacancies and for the mechanisms by which they move or are created or destroyed, but the phenomenological treatments are not dependent on the details of these models. The important product of a phenomenological analysis is an equation that describes the relation among the measurable quantities determining the behavior of the system. Based on such an equation, experiments can be performed to study these quantities in detail. Eventually atomic theory will supply an adequate theoretical base for the phenomena in question. A chemical species whose chemical potential was invariant during reactions in binary and ternary systems of varying composition would indeed be an anomaly. Yet this is the role that has frequently been assigned to the vacancies in pure metals, in dilute solutions, and even in ordinary alloys. The weight of available evidence supports the view that supersatu-rations of vacancies are on the order of 1 pct in usual diffusion processes.&apos; Although it may seem strange that such a small deviation from equilibrium could significantly affect the thermodynamic properties of the vacancies, it is well known that the driving force for an ordinary chemical reaction is the departure of the components from their equilibrium state. Similarly, the reaction of vacancies that results in the formation of pores in various types of diffusion3 can reasonably be attributed to the supersaturation of vacancies. In the present paper, it will be shown that small degrees of supersaturation can significantly affect the kinetics of the diffusion process itself. ISOTHERMAL ELECTRODIFFUSION Two different experimental techniques are convenient for studying the behavior of vacancies in a pure metal in the presence of an electric field. Gilder and Lazarus4 studied self-electrodiffusion in a gold specimen in which only the central portion was at high temperatures. In this case the significant vacancy sources operate inside the specimen in the presence of a temperature gradient. In the laboratory of Th. Heumann a method has been devised for studying self-electrodiffusion at constant temperature.5 In principle, there is then no effect of thermodiffusion. It will now be shown why in this case the significant ATungsten disks \^^ ^^ ^Gold disks^^ ^^"T>.... "TTZA ? Up Iy&apos;7 markers ///// ////// initial plane p I y/y/y of joining \I 7//// V7//A_________I_________V//// -I 0 +I Distance from center of specimen (a) -— Direction of flow of electrons —Direction of flw of vacancies %yy} Matano I z~irkendall /%W, vy/A inlerfacej "interface ///// -} HfiK- +/ 0 Distance from center of specimen (6) Fig. 1—-Schematic illustration of the essential features of isothermal self-electrodiffusion. (a) Initial condition of specimen. (b) Condition of specimen after electrodiffusion.

Jan 1, 1970

By W. C. Clarke

An empirical study of the nature of the embrittle-ment which occurs in martensitic and semiaustenitic precipitation hardening stainless steels upon exposure at temperatures of from about 550" to 875°F has been undertaken. This work was aimed at determining cazusation and means of controlling this phenomenon. A commercial copper bearing precipitation hardening alloy was used as a basic material for study. The effect of heat treatment variables was studied as was the effect of variations in analysis. It is concluded from the evidence that martensitic and semiaustenitic precipitation hardening stainless steels are subject to 885°F ernbrittlement similar to that observed in the straight chromium stainless steels. A characteristic of precipitation hardening stainless steels which has limited their use in certain applications is that they embrittle when held at temperatures in the range of from about 550" to 900°F. This is true to a more or less degree in all currently available alloys, either the basically martensitic type or the semiaustenitic type. The rate of embrittlement varies markedly with exposure temperature, being low at 550" to 600°F and in-creasing as the temperature increases. In spite of this embrittlement, these alloys with their unique combination of high mechanical strength, reasonable toughness, and good corrosion resistance are used in many hundreds of applications. Nevertheless, there are potential applications where the embrittle-ment described is a limiting factor. The purpose of this investigation was to study the embrittlement of these alloys and to find a way to control or eliminate it. GUIDELINES USED IN PRESENT WORK The work reported in this paper is based on a study of 17-4 PH*, a very widely used alloy. It has been used *Trademark of Armco Steel Corp., licensor. in pressurized water and boiling water atomic reactors operating at about 550°F for a number of years. As the life of such equipment is extended or operating temperatures are raised, the possibility of embrit-tlement becomes of increasing concern to materials engineers. Much investigation work was done with respect to the use of 17-4 PH at 550°F. K. C. Antony&apos; states "Such estimation" (of an activation energy for the diffusion of chromium in iron) "would indicate W. C. CLARKE, Jr. is Senior Research Engineer, Advanced Materials Division, Armco Steel Corp., Baltimore. Md. This manuscript is based on a talk presented at the symposium on New Developments in Stainless Steel, sponsored by the IMD Corrosion Resistant Metals Committee, Detroit, Mich., October 14-15, 1968. significant secondary aging is improbable at temperatures less than 700°F within normal component service life". This statement is modified however by the recognition of the accelerating tendencies of applied stress and internal stress as well as the possible effect of irradiation. In this investigation of 17-4 PH, the H 1100 (1900°F-1 hr oil quench or air cool + 1100°F-4 hr-air cool) condition was used, partly because this condition is normally used in atomic reactors. As shown later, the precipitation hardening temperature has no real bearing on the rate of embrittlement. An exposure temperature of 800°F was selected since embrittlement at 800°F is rapid, permitting development of relative data in time periods of 400 to 500 hr. For those not familiar, a nominal present day analysis of 17-4 PH is: C Mn P S SiCrNiCuCbN 0.04 0.30 0.015 0.015 0.60 16.00 4.30 3.25 0.23 0.030 TYPICAL BEHAVIOR OF 17-4 PH Figs. 1 and 2 show the behavior of a commercial heat of 17-4 PH under the conditions defined. Characteristically, 800°F exposure causes a rapid drop in Charpy V-notch impact strength. Tensile and yield strengths gradually increase and a gradual loss of elongation and reduction of area occur, accompanied by an increase in hardness. Notched tensile strength increases to 125 hr exposure and then sharply decreases after exposure for 500 hr. The notched vs un-notched tensile ratio remains virtually constant to exposure for 125 hr (1.67 to 1.56) but drops to 1.15 after 500 hr. Tensile ductility is not alarmingly affected even after much longer exposure times than these. For example, samples aged at 1100°F for 1 hr exposed at 800°F for 4000 hr showed a drop in elonga-tion of from 13 to 11 pct and in reduction of area of from 58 to 37 pct. Notched impact is the property SmIgth KSI 3JJ[/__________^UTS-Nrteh 260 ;/- 240 —^ 200 UTS-Smooth________._, o ioo mo Sob" m Too Hours Exposure Fig. 1—Effect of exposure at 800°F for various times on notched tensile strength and smooth tensile and 0.2 pct yield strength of 17-4 PH in the H 1100 condition.

Jan 1, 1970

By Hiroshi Oikawa, A. G. Guy

Recent experimental evidence has shown that it is often incorrect to neglect the reactions occurring at an interface with respect to the diffusion reactions. By introducing reaction-rate constants and k for the transfer of components 1 and 2 between the a and b phases, a phenomenological description has been devised for the coupled processes of diffusion and in-terfacial reaction. An illustrative example has been analyzed with the aid of a suitable computer program. The results indicate that for kab values on the order of 10&apos;1 cm per sec and Ð values of about 10¯10 sq cm per sec, the interfacial reactions are significant during the first 10 2 to l0 6 sec of a diffusion experiment. Among the observable effects of the interfacial reactions in this case appear to be the burying Kirkendall markers and an anomaly in the initial shifting of these markers. THE study of diffusion between two phases is especially important because of its direct connection to phase transformations. For example, the transformation of austenite to ferrite involves diffusion in the a and ý phases and also an interfacial reaction (trans formation) at the a/? interface. If ferrite and aus-tenite are the two members in a diffusion couple, the same two reactions occur during the diffusion process. The numerical values obtained for the diffusion coefficients and interfacial-reaction constants from diffusion experiments can then be employed to predict phase-transformation behavior. Refinement of the calculations of phase transformation is also suggested by the present method for treating two-phase diffusion. In the recent paper by Nolfi et al.&apos; only the solute com ponent is considered in the interfacial reaction accompanying a phase transformation. The present analysis demonstrates that both components must be considered. It is generally recognized that reactions of some kind must occur at the interface in a two-phase diffusion couple, but usually it is assumed that the interface reaction occurs so rapidly that its effect on the overall process is unobservable because the slower diffusion process determines the kinetics of the process. However, Seith and Heumann 2 pointed out that effects of the interfacial reaction should always occur in the early stages of diffusion, and recently Eifert et al. 3 have shown that interfacial reactions influence the composition and motion of the interface in a/ß Al-Cu diffusion couples during the entire course of prolonged, high-temperature treatments. A general procedure for handling the combined processes of interfacial reaction and diffusion in a binary, two-phase system is to introduce kinetic coefficients for the interface reactions and to develop the system of equations governing the interlinked processes of diffusion and interface reaction. The resulting equations, although not amenable to solution in closed form, can be usefully manipulated by a digital computer. INTERFACIAL REACTIONS IN TWO-PHASE DIFFUSION Consider the general case of diffusion between two solid solutions, a and ß, which are adjacent phases in a binary system, Fig. 1. Two semiinfinite bars having compositions c1 and c0ß are jointed at x = 0. If concentrations are expressed in volume fraction,4

Jan 1, 1970

By S. F. Frederick, G. F. Pittinato

The deformation mechanisms operating in Ti-5Al-2.5Sn at 20°K under uniaxial and biaxial stress fields were determined by using both optical and electron microscopy. In the uniaxially stressed specimens, de-fu~rnation twins were found only in the immediate vicinity of the fracture. Twinning was, however, established as a deformation mechanism under biaxial stress conditions. The same slip systems were opera-tiz,e under both uniaxial and biaxial stress. Prismatic slip was identified as the major slip syslem; however, basal and first-order pyramidal slip also occurred, but to a lesser degree. The interaction of moving dis-locations on intersecting slip planes resulted in the formation of jogs and dipoles. Hexagonal dislocation networks were formed only under biaxial stress conditions. A discussion is given on the formation of hexagonal dislocation networks. IT has been shown that titanium alloys can exhibit unusually high strengths when tested in a biaxial stress field.&apos;-" The high biaxial strengths are a consequence of a strong basal plane sheet texture which results in distinctly anisotropic flow properties. This texture strengthening appears to decrease with decreasing temperature2 and would seem to indicate a change in deformation modes. For example, in a uniaxial tensile test, Ti-5A1-2.5Sn yields isotropically at 20°K but is strongly anisotropic at room temperature. The increase in biaxial ultimate over uniaxial strength at 20°K is also much less than at room temperature. It is known that titanium car] form deformation twins more readily at cryogenic temperatures than at room temperature.4 Since the formation of deformation twins will reduce the degree of basal texture in sheet material,&apos; an accompanying decrease in texture strengthening would be expected. To investigate more fully the nature of texture strengthening at cryogenic temperatures, the deformation modes of Ti-5A1-2.5Sn tested in uniaxial and 1:1 biaxial tension at 20°K were studied by optical and electron transmission microscopy. EXPERIMENTAL PROCEDURE The uniaxial and biaxial stress test specimens were prepared from 0.020-in. thick sheets of Ti-5A1-2.5Sn ELI having the composition shown in Table I. Uniaxial stress conditions were obtained by using flat tensile specimens machined from the sheet material. The longitudinal axis of the tensile specimens was aligned perpendicular to the rolling direction of the sheet. Tile biaxial test specimens were prepared by rolling precut, 19-in.-lengths of sheet into 4-in.-diam cyl- inders. Following longitudinal butt welding, the cylinders were stress relieved at 1000°F for 4 hr. A 9-in. sq "window" was then chemically milled into each cylinder&apos;s surface reducing the wall thickness in the milled area to approximately 0.006 in. The testing procedure consisted of pressurizing the cylinders while simultaneously applying a tensile load. Using this technique, a 1:l axial to hoop stress was obtained. Complete details of the specimen and testing procedures are given in Refs. 1 and 2. The biaxial and uniaxial stress specimens were all tested in liquid hydrogen. Specimens for electron transmission microscopy were prepared by first chemically milling to a thickness of about 0.001 in. followed by electrolytic polishing to electron transmission thickness. The chemical milling solution, consisting of 800 ml of water,

Jan 1, 1970

By J. D. Defilippi, E. M. Gilbert, K. G. Brickner

FCC chromium-manganese-nitrogen (Cr-Mn-N) steels differ from most other fcc materials in that these steels undergo a ductile-to-brittle transition. Transformation to martensite is considered to be responsible for this behavior in some metastable Cr-Mn-N steels. However, very stable Cr-Mn-N steels also exhibit a ductile-to-brittle transition. The results of this study indicate that deformation faulting is the probable cause of the brittle behavior of stable Cr-Mn-N steels. Deformation faulting accounts for the ductile behavior of these steels in a tension test at -320°F and brittle behavior in an impact test at -320°F. Deformation faulting also accounts for the toPological features observed on the fracture surfaces of impact specimens of these steels. FACE- centered- cubic chromium-manganese-nitrogen (Cr-Mn-N) steels differ from most other fcc materials in that these steels undergo a ductile-to-brittle transition. Many Cr-Mn-N steels transform to martensite during deformation,l-5 and several investigatorsl-3 have suggested that the brittle behavior of these steels is caused by martensite formation. However, very stable Cr-Mn-N steels also exhibit brittle behavior. Schaller and Zackeyl reported that a very stable Cr-Mn-N steel (less than 3 pct martensite formed at -320°F) exhibited a transition temperature higher than that for steels in which large volume fractions of martensite formed during testing. The explanation given by Schaller and Zackey for this observation was that in the very stable steel the martensite, because of its higher interstitial content, was more brittle than that formed in their other steels. This explanation was questioned by Tisinai and samans4 and Baldwin.6 Moreover, because the toughness of stainless martensite at cryogenic temperatures is generally very low, this explanation does not account for Thompson&apos;s7 observation that small additions of nickel (1 to 3 pct) greatly improve the toughness of high nitrogen (0.35 pct) Cr-Mn-N steels. The present paper summarizes the results of an investigation of the low-temperature brittleness in very stable Cr-Mn-N steels. The importance of the mode of deformation on the toughness of these steels is discussed. Table I. Compositions of the Steels Invertigated, Pet Steel C Mn P S Si Ni Cr N - A 0.09 14.70 0.018 0.011 0.47 0.22 18.40 0.54 B 0.12 14.90 0.001 0.008 0.48 0.14 17.80 0.38 C 0.12 14.95 0.004 0.005 0.62 3.95 18.43 0.38 MATERIALS AND EXPERIMENTAL WORK The compositions of the steels investigated are shown in Table I. Steels A and B had compositions within the limits of a proprietary Cr-Mn-N stainless steel,* whereas Steel C was similar in composition to the proprietary steel except for its 3.95 pct Ni content. All steels were hot-rolled to 1/2-in. thick plate. The plates were subsequently annealed for 1 hr at 2000°F and water-quenched. Standard longitudinal and transverse Charpy V-notch impact specimens were machined from the annealed plates. Duplicate longitudinal and transverse impact specimens were tested at 212", 80°, 32", 0°, -100°,-160°,-200°,-256", and -320°F. Longitudinal tension-test specimens were also machined from the plates and tested at a crosshead speed of 0.05 in. per min at the aforementioned temperatures. The fractured impact and tension-test specimens of all three steels were examined to determine whether martensite had formed during testing. Magnetic, X-ray, electron-diffraction, and electron-microscopy techniques were used to detect the presence of martensite in the highly deformed areas of these specimens. Metallographic examination of highly deformed areas of impact and tension-test specimens revealed the presence of dark-etching bands, such as those shown in Fig. 1. These bands were observed only in deformed samples and were thought to be associated with the low-temperature brittleness of the Cr-Mn-N steels. Accordingly, a sample 1 in. wide by 3 in. long was cut from the 1/2-in.-thick plate of Steel C. This sample was surface-ground to a in. and then cold-rolled 60 pct at -320°F. Thin foils were prepared from the cold-rolled sample and examined in a JEM electron microscope. Brightfield, dark-field, and selected-area diffraction techniques were used to determine the cause of the dark-etching bands. Fractographic experiments were also performed. Impact specimens Of Steels A, B, and C were broken at -320oF, and the fracture surfaces of these specimens were immediately shadowed with carbon. The carbon replicas were examined in a Siemens electron microscope, and attempts were made to correlate the topological features of the fracture surfaces with the deformation mechanisms that could be occurring during an impact test of these steels.

Jan 1, 1970

By Byoung Whie Lee

In order to investigate the change in surface energy as a function of cold work ad environment, the contact angles between a liquid and the surface of elec-tropolislzed aluminum with various degrees of cold work were measured. Specinlens cut from aluminum rod (99.99 pct Al) were annealed at 600°C for 24 hr and then cold compressed parallel to the drawing di-rectzon of the rod in increments of approximately 10 pcl from 0 to 70 pct. The sections, taken transversely to the drawing direction, were mechanically and electro chemically polished. Contact angles between the sessile drop of distilled water, glycerin, and glycol and the specimen surface were measured optically. The differences in interfacial energy were calculated from the contact angle data. The effects of chemical washing and surface roughness of the specimen on the contact angle were also studied. The liquid contact angle was a linear function of the degree of cold working (D) ad changed markedly with differed liquids. THE plastic deformation of polycrystalline metals induces a preferred orientation in crystal structure. A preferred orientation changes the atomic density of a metal surface. This change in surface atomic density brings about the changes in surface interactions of the metals."&apos; Also, the plastic deformation of metals raises the internal energy by increasing the stored energy.&apos; Consequently, the total Helmholtz free energy of the metal increases and, in turn, the surface free energy of the metal. In order to study the effect of plastic deformation on solid surface phenomena, the liquid contact angle of a sessile drop made on cold compressed and elec-trochemically polished aluminum was measured. The preferred orientation in aluminum, due to uniaxial compression, is known to be [110] direction parallel to the compression axis. However, this description is only a first approximation of a rather complex orientation. In actuality, half the crystallites are more than 10 deg from this orientation, regardless of the amount of compression." For randomly oriented fcc crystals, the average surface atomic density can be calculated as follows: The number of atoms in a unit volume is 4/a3, where a is a lattice constant. Hence, the number of atoms per unit surface area is about (4/a3)2/3 = 2.52/a2 However, when the preferred orientation took place along [110] direction, the surface atomic density is as follows: The area of (110) plane of a unit cell, considering ridges and valleys, is BYOUNG WHlE LEE, Member AIME, is Research Metallurgist, Atomic Energy Research Institute of the Republic of Korea, Seoul, Korea. Manuscript submitted May 29, 1968. IMD 2 x J2- a x Ga = 6a2 Since this plane contains 4 atoms, the surface atomic density is 4i6a2 = 2.3/a2 Upon changing from random to preferred orientations, the surface atomic density decreases about 10 pct. The increase in the stored energy and the change in surface atomic density due to plastic deformation would certainly alter the surface tension of a metal. EXPERIMENT High purity aluminum rod of 6-mm diam (99.99 pct Al, obtained from Johnson, Matthey & Co., Ltd, London, England) was cut into sections approximately 1 cm long. The transverse cross section was mechanically polished. Then, the specimens were annealed in air at 600°C for 24 hr. Thus, eight annealed specimens were uniaxially compressed at room temperature from 0 to 70 pct of cold working with an increment of 10 pct. The extent of cold working was determined by the percentage of reduction in axial length to the original length. The specimens were further polished mechanically and, then, electrochemically with the Modern Battelle Type 1 electropolishing solution with a current density of 0.3 to 0.4 amp per sq cm and an electrode potential of 8 to 12 v at the solution temperature of 78" to 82°C for approxirr~ately 5 min. The Modern Whlte Diffusing Screen \t/ --------------- re Goniometer for Mercury Lamp ^-^ Sessile Drop ¦=• Condenser c=> Microscope l_*~_i bJ Mlcromster Filer with Protmcter Fig. 1—Schematic diagram of apparatus set-up for liquid contact angle measurement.

Jan 1, 1970