Experimental analysis of diffusion samples covering the entire Cu-Ag-Au system at 725°C has been carried out. Experimental coefficients are computed at twenty-eight points in the lermary system. It is found that the direct coefficienl for copper is nearly independent of the silver, content for 1ow-silver alloys and that the cross coefficient for silver correlates with the ther-nzodynatnic properlies. This lalter observalion leads to the conclusion that the mobililies of copper and gold are nearly equal. Thermodynarmic actiuilies for Cu-Ag-Au were computed from binary data and adjusted to be consistent with neasured tie lines across the two-phase region which extends into the ternary diagram at 725°C. Application of these therknodynarnic calculaliorls to the dijftcsion data terifies the Onsager reciprocal relations to the extent that experimental uncertainlies will allow. It is jound that diffusion neav the critical point of the 1200-phase field in the isothermal section at 725°C causes the composition gradients for copper and silver to approach infinity while the direct and cross coeficients become equal. From the standpoint of experimental Procedures, it has been shown that microanalysis of ternary samples may be carried out using a simple expression for the conversion of X-ray zntensily to composilion. The accuracy of' this method has been demonstrated by the analysis of standard alloys and by the reproducibility of composition determinations using differed X-ray lines. DIFFUSION in a ternary alloy system is basically and significantly different from diffusion in binary alloys. When only two elements are present there is just one independent composition variable, and the diffusion profile of composition vs distance across a sample must change monotonically through all solid solutions bracketed by the terminal alloys. If two-phase regions are stable for compositions between the terminal values, these must appear as planar interfaces in the diffused sample, with the composition profile exhibiting sharp discontinuities. Adding a third element may alter this picture completely. Because of the additional degree of freedom in the composition, we may see composition profiles which do not change monotonically through solid-solution ranges, and stable, nonplanar phase interfaces. Even though two-phase regions may lie between the terminal compositions of a diffusion sample on the constitution diagram, they will not necessarily appear in the diffusion profiles. In binary diffusion only one coefficient is needed to describe the interdiffusion process. From Fick's law this coefficient relates the diffusive flux of one component to its own composition gradient. In ternary diffusion we must allow for cross interaction between the two independent species. By a linear extension of Fick's law we introduce "cross" or "off-diagonal" diffusion coefficients which relate the flux of one component to the composition gradient of the other independent constituent. Thus, we require four interdiffusion coefficients to describe the transport process in a ternary system. In its most general form,1,2 the rate equation for mass transport by isothermal diffusion in a system of s components states that the diffusive flux of component i, Ji, is a linear summation of all driving forces, Xk, each force being multiplied by an appropriate compliance coefficient:

Jan 1, 1968

By C. Laird, C. E. Feltner

An investigation into the effect of a material's slip character on its high strain fatigue properties has been carried out using copper and Cu-7.5 wt pct A1 as representative wavy and planar slip mode materials, respectively. In copper, the constant term and exponent in the Coffin-Manson equation, ?EpNf1/2 = const, are unaffected by the temperature of testing or the history of the metal. On the other hand, in Cu-7.5 wl pcl Al, while the exponent is invariant, the constant is increased with respect to copper and increased further with decrease in temperature. The life in Cu-7.5 wt pct A1 is double that of copper at room temperature and about four times at 78°K. Fractoflaphic studies indicate that these diffevences in life are associated with the early stages of cracking. In copper, severe surface rumpling provides crack nuclei at pain boundaries independent of' testing temperature or the history of the metal. In Cu-7.5 wt pct Al, the planar slip mode of deformation prevents grain boundary folding; crack nucleation is therefore mainly transgranular and the increase in life with respect to copper is associated with a prolonged linking-up stage of such transgranulay cracks. At the lower temperature the increased difficulty of cross slip inhibits multiplication of trans-granular cracks and retards the linking-up process, giving a further enhaancement in life. It is expected that such behavior will be found general in materials of wavy and planar slip mode, respectively. STAGE II crack propagation in high strain fatigue takes place by a repetitive process of crack tip blunting in the tension part of a fatigue cycle followed by resharpening of the crack in the compression part.1-3 This mechanism has come to be called the "plastic relaxation process".3 At very high strains (lives to failure less than 103 cycles), most of the life of a specimen is spent in crack propagation by the plastic relaxation process.4,5 Since the differences in the cyclic strain hardening behavior of metals and alloys are comparatively small in this strain range,6,7 the amount of blunting at a crack tip depends primarily on the applied strain amplitude. The rate of crack propagation in this life range is therefore nearly constant with respect to material and temperature of testing. In the longer life portion of the high strain fatigue range (l03 to 103 cycles to failure), a considerable fraction of the lives is spent in crack initiation and Stage I growth. Grain boundaries have frequently4,5,8 been found to be the sites for this growth which is also associated with a surface folding process.4'5 Such folding behavior may also be general in any material having a grain structure and capable of plastic deformation. It has therefore been suggested475 that the universality of the Coff in-Manson law,9'10 constant,* where ?Ep is the plastic strain range and Nf the number of cycles to failure, is reflected in the approximate invariance of both the crack initiation and propagation behavior. It happens that, in most investigations of the phenomena associated with failure,4,5,8 materials with a wavy slip mode have been used as vehicles for the studies, or else "normally" planar slip mode materials have been tested under conditions giving rise to wavy glide deformation, e.g., stainless steels cycled at high temperature.'' The purpose of the present investigation was to determine whether or not different cracking phenomena would occur when the slip mode of a material is planar and if the associated life to failure would be different than that of a wavy slip

Jan 1, 1968

By J. H. Swisher

In measuvements of the solubility of nitrogen in fer-rilic Fe-P alloys, tile nitrogen solubility is found to be Less in pIrospliorus-bearing alloys than in pure iron. The reduction in solubility is about 20 pct in a 1.0 wt pct P alloy at 1300°C and about 30 pct in a 0.23 wt pct P alloy at 440°C. Diffusion coefficient measurements at 1150 and 585°C show that phosphorus also decreases the nitrogen diffusivity in iron. In previous work on the Fe-P-N system, phosphorus was found to reduce the nitrogen solubility in liquid iron slightly.&apos; Indirect evidence for similar behavior in a Fe at low temperature was obtained by Dickenscheid and Brauner.&apos; These authors found that phosphorus reduces the height of the internal-friction peak due to dissolved nitrogen. The results of Dickenscheid and Brauner were confirmed by J. C. Swartz of this Laboratory in a single internal-friction experiment using the same specimen stock as in the solubility measurements described below. In the present investigation, the solubility of nitrogen in a fer rite-stabilized Fe-1.0 wt pct P alloy was measured in the temperature range from 800" to 1300°C. Additional experiments were performed in the temperature range from 440° to 585°C, using an Fe-0.23 wt pct P alloy and NH3-H2 gas mixtures. EXPERIMENTAL The experiments were performed in a vertical tube furnace wound with platinum wire. For experimental temperatures of 800°C and above, a mixture of 5 pct Hz in N2 was used as the reacting gas. The gas mixture was prepurified from oxygen by passage over platinized asbestos at 450°C, and subsequently over anhydrone to remove water. Flow rates of the gases were measured with capillary flow meters. The temperature was measured before and after each experiment with a Pt/Pt-10 pct Rh thermocouple. The specimens used for the high-temperature solubility measurements were in the form of rectangular plates, 0.534 by 1.6 by 3.8 cm. The specimens were cleaned in trichloroethylene and annealed for 2 hr in hydrogen at the beginning of each experiment. In measuring the nitrogen solubility, the specimens were held in the reacting gas until equilibrated, then cooled in a water-cooled copper block at the bottom of the furnace. The time needed for equilibration at 1150°C was determined by measuring the average nitrogen content of the 1.0 pct P alloy as a function of reaction time. As will be described, the nitrogen diffusivity in the alloy at 1150°C is only slightly less than its calculated diffusivity in pure iron. At temperatures other than 1150°C, the reaction time used in measuring the nitrogen solubility was about twice the calculated equilibration time for pure iron at the same temperature. With a few exceptions, the procedure for the low-temperature solubility measurements was the same as that described above. The compositions of the NH3-H2 gas mixtures were determined by collecting gas samples from the gas train and analyzing them for NH3 by titration with HC1. The specimen thicknesses were less than those used for the high-temperature experiments, eg., 0.124 and 0.051 cm for measurements at 585° and 440°C, respectively. Nitrogen concentrations were obtained by chemical analysis, using the Kjeldahl method. The Fe-P alloys were made by adding ferrophos-phorus to electrolytic Plastiron (Type 104 A). Commercial ferrophosphorus, containing 3 pct Mn and 0.35 pct Si as the major impurities, was first purified by melting under an FeO slag. In a separate heat, the electrolytic iron was melted and vacuum-carbon-deoxidized prior to making the ferrophosphorus addition. The principal impurities and their concentrations in weight percent in the 1.0 pct P alloy are as follows: Mn, 0.01; Si, <0.01; C, 0.01; 0, 0.003; and N, 0.0012. The impurity levels in the 0.23 pct P alloy are con-

Jan 1, 1968

By A. Hellawell

Specitlrens of the Al-Ge eutectic alloy have been frozen unidivectionally at rates between 2.5 x 10-6 and 2.5 x 10-4 cm per sec and the structure examined by optical and X-ray methods. There is no epitaxial relationship between phases, the aluminum having random orientation and the germanium a preferred (011) fiber textuve. Lamellar colonies which are BINARY eutectic alloys occur between either silicon or germanium with the metals aluminum or silver. common in this alloy are constructed from axial and nonaxial (111) plates of germanium which are related by a variety of twin configurations. Irregular or globular regions of the microstructure are composed of continuous single crystals of each phase, the germanium being heavily twinned. There is limited solid solubility in these systems, and the eutectic phases all involve diamond cubic with fcc crystal structures. In the microstructures of these eutectic mixtures the silicon and germanium crystals exhibit an almost infinite variety of shapes which are notably sensitive to

Jan 1, 1968

By D. M. Boulin, E. S. Greiner

Single crystals of vanadium were bent at 293" and 77°K to a maximum fiber strain of about 1 pct. Analysis of slip line and etch markings of- crystals deformed at either temperature show the slip planes are {112}. The slip directions at 298° and 77°K, deterwined from the asterism axes of rotation of crystals compressed in a {110} direclion, were (111). Etch pits, associated with dislocations, were observed in the plastically deformed vanadium. There was no evidence of mechanical twinning. THIS paper presents results on single crystals of vanadium plastically deformed by bending and compressing at 298° and 77°K. Bcc metals have been observed to slip on {110}, (1121, and (123) planes while the slip direction has invariably been found to be ( 111) 1 Lindley and smallman2 have studied the deformation intension of polycrystalline vanadium between 298° and 20°K and reported that at and above 77°K the deformation is predominantly by slip, but at 20°K the deformation is associated with twinning. Later, Edington and smallman3 found that single crystals of vanadium compressed in a (111) direction at 77°K deformed by twinning on { 112}( 111) systems. Clough and pavlovic4 have reported that mechanical twins were observed in vanadium loaded by impact at 77°, 173°, and 195°K, respectively. PREPARATION OF SINGLE CRYSTALS The vanadium single crystals were made from commercial vanadium reported to contain 0.03 pct C, 0.03 pct 0, 0.02 pct N, 0.0X* pct Ca, 0.0X pct Si, proximately 0.8 cm diam, 4 cm long and were grown in (100) and (110) directions. A crystal for studies of etch pits was gound to have a face parallel to a {l00} plane by the Bond crystal-orienting technique.7 In order to avoid straining, the crystals were placed on the steel mount with a low-melting organic compound (glycol phthalate) before grinding. Crystals for the bending experiments were ground to have the four side faces parallel to ( 100) planes. The crystals were electropolished8 in 10 pct H2So4 using a current density of about 3 amp per sq cm to remove the strained surface material. The crystals were bent slowly by three-point loading in a stainless-steel jig designed by Sylwestrowicz.9 The end rollers of the jig were 3.8 cm apart. DEFORMATION AT 298°K The bent vanadium crystal, after removal from the jig, had a radius of curvature of 20.4 cm over the 2-cm length close to the center loading roller, where the maximum bending moment occurred. This radius of curvature corresponded to a maximum fiber strain of 0.9 pet. The side faces contained slip bands as shown in Fig. 1. These bands are straight where the strain is high, top and bottom of micrograph, but are curved on either side of the neutral axis in the center. This curvature of the slip bands in the low-stress area may be due to cross slip. The plastically deformed crystal was subsequently electropolished and then electroetched in 10 pct H2SO4 solution, using a current density of 0.25 amp per sq cm. The structure is shown in Fig. 2. The directions of the traces on two adjoining faces were plotted stereo graphically, Fig. 3.* Since there were two sets of

Jan 1, 1968

By S. K. Tarby, W. O. Philbrook

The rate of FeO and MnO reduction from silicate and aluminate slags by carbon-saturated iron is dependent on both slag composition and temperature. Owing to variable stirring rules during- the course of reaction, the reduction processes occur in two stages in stationary graphite crucibles. In the first stage the slirring caused by CO evolution results in forced convection conditions in the slag. As the boiling action subsides during reduction, the flow conditions within the system become those defined by natural convection. Analysis of the data by an unsteady-state penetration model indicates that the rate of reduction is controlled by the rate of cocur-rent flow of&apos; cations and anions from the bulk slag to the interface during both stages of reduction. The hearth reactions of the blast furnace have been extensively investigated from the viewpoint of equilibrium by deductions from controlled laboratory experiments. However, the literature contains relatively few studies that have been directed toward the area of slag-metal reaction kinetics, and the majority of these have been concerned with the rate and mechanism of sulfur transfer between iron and slag. More recently, attention has turned to the kinetic factors in the reduction of oxides from liquid slags. One of the first investigations in this field was conducted by Dancy1 on the reduction of pure liquid FeO and pure liquid Fe3O4 by carbon-saturated iron. The integrated form of the rate equation indicated that the reduction of FeO was of the first order up to 80 pct reduction. Over the initial 30 pct of reduction, the magnetite reaction was also interpreted as a first-order process. The rates of reaction were extremely rapid as indicated by a 30 pct reduction of the liquid magnetite in a time interval of about 1 to 2 sec. Phil-brook and irkbbride&apos; studied the reduction of FeO from a lime-alumina-silica slag by carbon-saturated iron and solid graphite in stationary crucible assemblies. With the use of the differential form of the rate equation, the rate of the reduction reaction was found to be proportional to the second power of the concentration of the reactant FeO for both the slag-metal and slag-graphite reactions. These authors presented a number of comments in an effort to explain the difference between the molecularity of the above reaction and the observed second-order relation. One such argument, recently extended by Wagner,3 was that the rate-limiting step may well be one of transport control. A complete discussion of the proposed mass-transport control mechanism of this reduction reaction will be presented in a later section of this paper. Kinetic studies of the reduction of other oxide species, namely chromous oxide, titania, and silica, have also been reported. McCoy and philbrook4 used rotating crucible assemblies to investigate chromium reduction from Ca0-SiO2-A12O3 slags. First-order kinetic law was obeyed for the slag-metal reduction reaction as determined by the integration method of data analysis. Due to scatter of the data, any dependence of the rate constant on temperature or slag composition was obscured. Concentration-time data for the reduction of titania from blast-furnace type slags under reducing conditions were obtained by Delve, Meyer, and Lander.&apos; The data were too few, however, for a formal kinetic interpretation. Kinetic data for the very slow reaction of silica reduction have been observed by McCoy and Philbrook6 and Fulton and chipman.7 The former experimenters found the reaction-rate constant for silica reduction by carbon-saturated iron to be 20 to 60 times less than the rate constant for chromium reduction. In their work on the reduction of SiO2 in mechanically stirred systems, Fulton and Chipman also found small values for the specific reaction rate and derived a high value for the energy of activation for the reaction. In both of these investigations, the reduction process was assumed to follow first-order behavior. schuhmann8 proposed that the rate-limiting step in this reaction is the diffusion of oxygen from the interface through a boundary-layer film to the bulk metal phase, and Rawling and Elliott9 have reported experimental confirmation of this hypothesis for temperatures below 1600°C. Turkdogan et a1.10 have also concluded that the rate of reduction of silica is a slow process and controlled by the diffusion of oxygen in the metal, but only in the absence of carbon monoxide bubbles at the slag-metal interface. In the presence of bubbles, achieved either by injecting carbon monoxide at the slag-metal interface or by blowing it through the metal and slag, these investigators found a rather rapid reduction of silica which appeared to be controlled by an interfacial reaction involving the de-sorption of silicate ions from the slag-metal interface to the metal phase as silicon and oxygen atoms. In view of the unresolved nature of the kinetics of FeO reduction and the lack of kinetic data for the manganese reaction,

Jan 1, 1968

By B. C. Allen

The solubility of chromium in liquid silver and that of molybdenum and tungsten in liquid tin have been determined by equilibrating Ike Liquid in a crucible of the solule metal. Generally the weight of solute in solulion was delermined both chemically and from crucible weight losses. The resulting weight percent solubilily of chromium in silver as a function of absolule temperature T is given by log w = -6660/T + 4.02 in the range 960° to 1445°C, and that of molybdenlttrl in tin by log w = —5050/T + 1. 79 in the range 1200° to 2200°C. The values appear unaffected by minor changes in solute composition. Calculations aye made of the parlial molar heal and excess entropy of mixing. The estimated solubility of tungsten in tin is 0.001 pct at 2000°C. Evidence is presented that molybdenwm dissolves in tin without compound for mation and that tungsten and tin form W10Sn. RECENT developments in coatings, heat transfer, and brazing require a knowledge of equilibrium solubilities in a variety of systems at elevated temperatures. Of particular interest are solid-liquid interactions in metal systems involving dilute solutions. This investigation was undertaken since little is known about the phase relations or solubility of chromium in liquid silver or of molybdenum and tungsten in liquid tin.1,2 EXPERIMENTAL WORK As indicated in Table I, high-purity metals or those of known impurity levels were used. Crucibles were machined from chromium, molybdenum, and tungsten bar stock 1.3 cm diam and 2.2 cm long. Chromium rod was prepared by arc melting and extruding iodide process crystals.3 The five chromium impurity alloys were in the form of 0.6-cm-diam swaged rod. A Cr-0.06N* alloy was prepared by exposure to NH3 at 1150°C in a closed quartz capsule for 24 hr. Because significant nitrogen was lost during annealing in argon at 1600°C,4 the estimated level was 0.01 pct N. Chromium and Mo,W crucibles were outgassed at 1200" and 1600°C, respectively, at 3 X 10-5 mm. The solvent was placed In crucibles of the solute metal- 6 g Ag in chromium, 0.4 g Ag in the five chromium impurity alloys, and 4 g Sn in Mo,W crucibles. The silver and tin series were outgassed at 900" and 110O°C, respectively, and held at the desired solution temperature in a tantalum resistance furnace under 1.05 atm 99.995 pct Ar. An equilibration time of 0.5 to 1 hr was chosen since 0.3-, I-, and 4-hr anneals at 1235°C for Cr-Ag yielded similar results. Temperatures were measured optically to +10°C under essentially black body conditions which were checked against the melting point of silver. The Cr-Ag and Mo-Sn,W-Sn series were respectively equilibrated at 990° to 1400°C and 1200" to 2000°C. Vaporization losses were generally held to <1 pct by the argon. In the 1800" and 2000°C anneals for 0.5 hr, the crucibles were placed in tightly sealed tantalum cans which kept tin losses to <5 pct. After the anneals, the specimens were furnace-cooled. One anneal was made on small Mo-0.02 C, Mo-0.5Ti-0.lZr, and tungsten crucibles containing tin at 2200°C. The metals were sealed in an electron-beam-welded tantalum can of minimum volume. After the anneal, tin was still present in each crucible, none of which was severely attacked. After equilibration, the saturated solvent metal was selectively removed from the crucible by acid leaching. Weight losses sustained by the crucibles were determined from the initial weight minus the final blank-corrected weight after acid leaching. Chemical analyses were performed on some of the samples. Hot 1:l HNO3-H2O removed silver from chromium with the blank running <0.1 mg or <0.002 pct on measured solubility. Tin was removed from molybdenum and tungsten by hot concentrated HC1 with the respective blanks amounting to -0.004 and -0.0004 pct in the presence of tin. The insoluble residues were weighed and checked for composition. The leaching solutions contained traces of the solute metals which were analyzed by colorimetric methods, Diphenyl Carbazide for chromium, Thiocyanate for molybdenum, and Dithiol for tungsten. The total of the two percentages found from the residue and leaching solution minus the blank gave the desired solubility values. On the basis of annealing empty molybdenum and tungsten crucibles, weight losses due to MoO3 or WO3 volatilization were found to be generally 10.4 mg and affect measured solubilities by <0.01pct. RESULTS AND DISCUSSION Chromium-Silver . Since no intermediate compounds are reported to form in the Cr-An system,&apos; crucible weight losses and chemical analysis of the entire melt should provide reliable measures of the chromium in solution. Values obtained by the two methods are in agreement as shown by the results for unalloyed chromium in Table II and plotted in Fig. 1. Furthermore, the results are consistent with those previously determined by melting equilibrated silver out of the crucible and analyzing calorimetrically for chromium.&apos; On the basis of limited thermal analysis data, the solubility of chromium in silver has been quoted as 8 pct at the monotectic temperature of -1445°C.1 This investigation indicates an extrapolated solubility of 1.38 pct which is believed to be more reliable. At the eu-

Jan 1, 1968

By Donald T. Hawkins, Ralph Hultgren

The lorsion effusion method has been used to measure the vapor pressure of lead over pure lead and eight Pb-Sn alloys ranging from 9.1 to 87.9 at. pct Pb in the temperature range 950° to 1125°K. The resulting ?H°y 298 = 46,630 ± 200 cal per g-atow for pure lead is in excellent agreement with previous work. Deriued ?Gph values for the alloys were smoothed and correlated with previous heat of formation data to obtain entropies for the liquid alloys. values for the tin component were calculated by Gibbs-Duhem integmtion. Surfhce depletion of these liquid alloys was found to be absent, as shown by the fact that the measured pressure remained substantially constant with time in contrast with previous measurements on iron-rich solid Fe-Mn alloys. The activities and Gibbs (free) energies of the liquid Pb-Sn system are not well known although the heats of formation have been accurately determined by K1eppa.l Vapor pressure determinations of the activity of lead by Voronin and Evseev2 disagree with those of Predel.3 Elliott and chipman4 measured activities by the electromotive -force technique in the ternary Pb-Sn-Cd system. From the resulting values of the activity of cadmium, they were able to calculate the activities of lead and tin for the binary Pb-Sn system at the compositions xsn = 0.33 and 0.67. Atarashiya, Uta, Shimoji, and Niwa5 determined the activity of tin from Hz-H2O equilibrium measurements, but their results are subject to question due to uncertainty in the final state of their samples. To resolve these differences, measurements of the activity of lead were made using a torsion-effusion apparatus. Among other advantages, this apparatus rapidly detects errors caused by surface depletion, which tends to reduce the apparent vapor pressure of the more volatile component. If the measured torques remain nearly constant with time, only bulk depletion is occurring. This contrasts with the rapid decrease in torque found in solid Fe-Mn alloys at high temperatures and low manganese contents.6 EXPERIMENTAL 99.999+ pct Pb was obtained from the American Smelting and Refining Co. and 99.999 pct Sn from Vulcan Detinning Co. Eight Pb-Sn alloys were prepared by melting together weighed amounts of the pure metals in evacuated Pyrex tubes and quenching the melts in water. Loss of weight in preparation was less than 0.02 pct in all cases. The effusion cells were made from high-purity, nonporous graphite. Graphite was chosen because of its resistance to reaction with lead and tin and because it can be accurately machined with precision orifices. Two cells were used with overall dimensions as shown in Fig. 1. The orifices of cells 1 and 2 were, respectively, 1 and 1.5 mm in diam.

Jan 1, 1968

By Mark J. Klein

The precipitation of nitrogen in quenched and aged CY-35 at. pct Re was followed by internal-friction and electrical-resistivity measurements. It is shown that the precipitation kinetics of nitrogen from solution are many orders of magnitude lower in this alloy than in chromium. The reluctance of nitrogen to precipitate from sol~ction can be attributed to the composilional r-eadjustnzents required in the z.icinity of a chromium nitrade particle for gowth to occur. AS part of an investigation of the mechanism by which rhenium increases the low-temperature ductility of chromium and other Group VI-A metals, it was of interest to compare the concentration of interstitial elements retained in solution in chromium with that of a ductile Cr-Re alloy. The presence of certain interstitial elements in chromium has been shown to decrease its ductility1-5 and, of these interstitials, nitrogen is believed to have the most detrimental effect on mechanical properties. Thus, a comparison of the disposition of nitrogen in chromium with that in a ductile Cr-Re alloy might provide information about the mechanism whereby rhenium enhances the ductility of chromium. In previous internal-friction studies it was shown that the equilibrium solubilities of nitrogen in chromium and Cr-35 at. pct Re did not differ greatly.= However, results indicated that the actual concentration of nitrogen retained in solution at ambient temperatures is likely to be considerably greater in the alloy than in chromium because the precipitation kinetics of nitrogen are greatly retarded by the addition of rhenium. The objective of this investigation was to study the kinetics of nitrogen precipitation in Cr-35 at. pct Re in greater detail and to obtain information concerning the mechanism of nitrogen precipitation in this alloy. The properties studied were internal friction and

Jan 1, 1967

Jan 1, 1967

By J. E. Flinn, S. A. Duran

The steady-state creep behavior of poly crystalline cad mi inn was studied over a temperature range of (1.56 to 0.94 Tm. Two distinct mechanisms were found to occur over this temperature range. They were described by: where and represerqt the minimum strain rates corresponding to the low- and high-temperature regions, respectirely. The two regions of constant acti11ation energy were connected by a transition region where the strain rate was controlled by both mechanisms acting in parallel. At temperatures below a transition temperature of about 0.7 Tm the agreement between the activation energy value for creep and that for self-diffiision suggests a rate-controlling mechanism of dislocation climb. For cadwzium, steady-state creep at temperatures above 0. 7 Tm appears to be controlled by another mechanism, perhaps involving the behavior of dislocation jogs. FRENKEL et al.1 studied the high-temperature creep of polycrystalline cadmium and reported an activation energy of 21 kcal per mole for the 0.5 Tm < T < 0.8 Tm range. Based on observations of creep rate at only two temperatures, a value of 22.1 kcal per mole was determined by Medbury. These two investigations were for the purpose of showing agreement between the activation energy for creep and that for self-diffusion, reported3 as 18.2 and 19.1 kcal per mole, respectively, for diffusion parallel and perpendicular to the hexagonal axis. Gilman4 investigated prismatic glide in single crystals of cadmium over a higher-temperature range of 0.72 to 0.93 Tm, and found an activation energy of 29 kcal per mole. He also reported5 an activation energy higher than that of self-diffusion for prismatic glide in zinc single crystals deformed at temperatures near the melting point. This value was in good agreement with those found for an equivalent temperature range by Flinn and Munson6 and by Tegart and sherby7 for polycrystalline zinc. These two independent studies also disclosed at lower temperatures another value of activation energy near that for self-diffusion. It would be expected from the creep results on zinc and single-crystal cadmium that creep studies on polycrystalline cadmium, extended to temperatures near the melting point, might yield an activation-energy value higher than the 22 kcal per mole value found in earlier studies. The purpose of this paper is to report the steady-creep behavior of polycrystalline cadmium over a temperature range of approximately 0.5 to 0.9 Tm EXPERIMENTAL METHOD The cadmium used in this study was obtained in the form of as-cast rods, 0.5 in. diam, through the courtesy of the Bunker Hill Mining Co. The material was of 99.995 pct purity, as determined by spectro-chemical analysis. The creep specimens, which were 0.250 in. diam by 0.400 in. long and annealed at 300°C for 45 min to produce a stable average grain diameter 0.25 mm, were tested in compression using an apparatus similar to that described by Sherby.8 The specimen temperature was controlled to within ±0.5°C with the help of appropriate constant-temperature baths. The applied stress was maintained within 1.0 pct of the desired value by the additions of lead shot at fixed strain increments. No barreling was observed over the strains encountered during testing. Isothermal creep tests9 were used in the study with only a few differential temperature tests10 run for comparison purposes. Steady-state creep data were obtained over a temperature range of 60 to 287°C (0.56 to 0.94 Tm) at five stress levels ranging from 28.1 to 140.6 kg per sq cm. RESULTS The minimum or steady-state creep rate may be described by an equation of the following form:" where i is the minimum strain rate, S is the structure factor, F is a stress function, Qc is the energy of activation, T is the absolute temperature, and R is the gas constant. The minimum strain rates obtained in this study for cadmium were recorded on a semilogarithm plot as a function of the reciprocal absolute temperatures for the various stress levels, as shown in Fig. 1. This figure shows a characteristic transitional behavior" with a parallel interaction of two mechanisms. It is obvious that the activation energies corresponding to the individual processes are insensitive to stress because the curves are parallel. The discrete activation-energies values for the low- and high-temperature regions for the various stress levels are reported in Table I, and were determined by the least-mean-square method. For the low-temperature region, an activation energy of 20.7 ± 0.6 kcal per mole was obtained, and for the

Jan 1, 1967

By D. L. Albright, R. W. Kraft

High-purity materials have been used in producing as-cast, controlled, colony, and degenerate solidification structures in the Fe-FeS eutectic. Experiments disclosed that this eutectic can be classified as normal and has a natural morphology composed of rodlike iron particles dispersed in a matrix of iron sulfide. The metallography of the various structures was studied, and a preferred crystallography was revealed in the controlled specimens produced by unidirectional solidification. The orientation effects found in these latter specimens are an [001] fiber texture in the -mowth direction of the bcc iron bhase and a texture corresponding to bicrystalline behavior in the hexagonal iron sulfide, with the growth direction near to (2111) poles. The observed texture of the iron phase is considered as indirect evidence that the alloy un-dercooled by at least 75°C before solidification. The unidirectional solidification of binary eutectic alloys has produced materials which exhibit a structure and properties markedly dependent upon the solidification process. In many cases a controlled microstructure with pronounced metallographic and crystallographic anisotropy can be experimentally achieved by proper regulation and balance of the growth rate of the alloy, the chemical purity of the starting materials, and the thermal gradient in the liquid at the liquid-solid interface. The purposes of this investigation were to produce various micro-structures in the Fe-FeS eutectic for subsequent study of their magnetic properties and to correlate the different structures with the solidification conditions in order to obtain a better understanding of the structure of eutectics. The Fe-S equilibrium diagram exhibits a eutectic composed of nearly pure iron and stoichiometric iron sulfide (FeS1.00), with the eutectic reaction occurring at 988°C and 31.0 wt pct S.1 Calculations indicate that this eutectic should solidify with about 9.5 vol pct Fe and 90.5 vol pct FeS, which in turn suggests2 that the micros tructure will consist of a rodlike iron constituent dispersed in a matrix of FeS. This characteristic has in fact been revealed some years ago.3 Thus, controlled solidification of this alloy might yield a material whose micromorphology would consist of very small ferromagnetic iron particles, rod-like in shape and aligned parallel to one another, supported in a matrix of antiferromagnetic FeS. Such specimens, because of the magnetic characteristics of the two phases, would be interesting subjects of study as magnetic materials. Hence the magnetic properties were considered in detail and are reported elsewhere.4 EXPERIMENTAL PROCEDURE The specimens of Fe-FeS eutectic were prepared from ultrapure iron (99.99+ pct) and high-purity sulfur (99.999+ pct). The iron was estimated to contain 60 ppm impurities (99.994 pct Fe) after zone purification.5 The ingots of iron were cut into chips, and the lumps of sulfur were ground into powder. In order to redice any nometallic impurities which might have accumulated during handling, the iron chips were annealed for 5 hr at 750° ± 10°C in a dry hydrogen atmosphere. Immediately after this treatment the chips were blended with the sulfur powder in eutectic proportions; the mixture was tamped into transparent fused quartz tubing and then vacuum-encapsulated under a pressure of 40 to 60µ of Hg. Because FeS expands upon solidification it was necessary to re-encapsulate the initial capsules so that oxidation reactions would be avoided when the inner tube cracked during solidification. For purposes of homogenizing the blended mixtures before solidification, the double capsules were heated to 750° ± 20°C and held for 20 hr; after this treatment the reacted product was weakly agglomerated. Each sample was then loaded into an apparatus for very rapid melting and freezing; this was accomplished by passing a molten zone through the specimen, using induction heating and a traverse mechanism. The resulting specimens solidified in the shape of the quartz tubing. Two sizes of specimens were used in this work, 18 mm diam by 100 mm long and 5 mm diam by 30 mm long. Metallographic examination of several ingots of both sizes after the above consolidation indicated no lack of compositional homogeneity and a random "as-cast" structure, because the travel rate was so rapid that unidirectional solidification was not achieved. Unidirectionally solidified specimens were resolidified in the apparatus shown schematically in Fig. 1, This equipment consisted of a kanthal resistance furnace mounted on the carriage of a zone-melting unit so that the heating element could traverse the length of the sample at a selected rate of speed. Large specimens were solidified with the mechanism tilted at ap-

Jan 1, 1967

By John F. Elliott, David L. Schroeder

SURFACE depletion can be a significant source of error in the use of the effusion method for determining the thermodynamic properties of alloys, particularly in the case of solid alloys.&apos; However, as yet this problem has not been treated quantitatively by experimentalists in the field.1-3 The method necessitates diffusive transport of material out of the source alloy to obtain a relevant measurement. The general character of the system is shown in Fig. 1. The diffusive flux (nD) at the alloy surface is equal to the effusive flux (nE): where D is the diffusion coefficient of the diffusing substance, C is its concentration, X is the distance from the surface into the source alloy, p is the density of the alloy, and AS is the actual available surface of the alloy. The concentration of the diffusing substance at the surface is CS, and Here fE is the Clausing factor, AE is the area (sq cm) of the orifice, y is the activity coefficient of the substance in the alloy, PO is the vapor pressure (Torr) of the pure substance, M is the molecular weight of the effusing species, and T is the absolute temperature. The differential equation for diffusive transport in the source alloy is Fick&apos;s second law. Its solution is dependent on the geometry of the source alloy. Two boundary conditions must be established to obtain the proper solution, the first being Eq. [1], or its equivalent. The solutions for several important forms of the source alloy are considered below.

Jan 1, 1967

By V. B. Kurfman

The temperature, strain rate, and orientation deDendence of defbrnzation of single-crystal MgAg has been examined. The crystals exhibit a tendency to single glide and little or no hardening at 25°C for many orientations. A much higher hardening rate is observed when multiple glide occurs, such as can be initiated by surface defects. The tendency for easy glide becomes less dependent on surface preparation and orientation as T — 100°C and bars so tested often fail after one-dimensional necking-. At T > 200°C (transition temperature for single-crystal notch sensitivity and poly crystalline ductility) single glide diminishes and two-dirnensionul necking begins. The crystals do not strictly obey a critical resolved shear stress law, but show the influence of {loo) cracks in determining the slip mode. The results are correlated with the difficulty of sciperdzslocation intersection and semibrittle behavior of this compound in single-crystal and poly crystalline form. Comparisons are made with the slip selection mode observed in tungsten, with the reported observations of easy glide in bee metals. and with the mechanical behavior of poly crystalline MgAg. PREVIOUS work on tensile deformation of polycrys-talline MgAgl and bending deformation of single-crystal MgAg2 has shown that the compound is semi-brittle (i.e., notch and grain boundary brittle). If this semibrittleness is supposed to result from the difficulty of multiple glide (associated with the problems of superdislocation intersection) one might expect single crystals deformed in tension to show pronounced single glide and strong orientation dependence of hardening rate. These experiments were done to examine this supposition and to study the tensile deformation of a highly ordered system which may be considered bcc if the difference between the two kinds of atoms is ignored (actual structure: CsC1). EXPERIMENTAL Single-crystal ingots were grown by directional freezing as previously described.&apos; These ingots were sliced into a by a by 2 in, rectangular bars by electric discharge machining, then round tensile bars were conventionally machined to 1/8-in.-diam by 1-in.-long reduced section. The bars were typically tested without an anneal because of the problem of magnesium vapor loss and they were typically tested as mechanically polished. The analyses are within the same limits as those reported earlier; i.e., the average composition for each specimen is within 0.5 at. pct of stoichiometry, while the total range from end to end in a given specimen varies from 0.7 to 1.4 at, pct. There has been no indication in the results of any variation in slip or fracture mode attributable to the composition fluctuations. The slip systems were determined by two-surface analysis of the bars after testing to failure at room temperature. Single glide was so dominant that there was little difficulty in identification of the dominant slip system even though the tensile elongation to failure often approached 7 to 8 pct in room-tempera- ture tests. Elevated-temperature testing was done in a silicone oil bath and low-temperature testing was done in liquid Np or a dry-ice bath. All stress measurements are reported as engineering stress unless otherwise specified, and crosshead travel is used as the strain measurement. RESULTS The tendency toward single glide is best seen in the pictures, Figs. 1, 2, and 3, which depict deformation at fracture as a function of test temperature. While it is possible to find regions of secondary slip by careful microscopy, such regions are very small. The development of a ribbon-shaped configuration from an initially round section bar pulled at 100°C is typical, occurred by single glide, and illustrates the degree to which such glide continues. At temperatures =100°C the bars typically show elongation of 20 to 50 pct by predominently single glide. Despite the large elongation, fracture even at 150°C occurs in a brittle mode, Fig. 2, in the sense that it is an abrupt failure which shows no discernible necking in the second dimension of the bar&apos;s cross section (i.e., there is no appreciable action of any slip modes which would decrease the broad dimension of the cross section). Near 200°C the fracture mode changes slightly. Although most of the sample extension is by single glide, after the bar develops the characteristic ribbon shape it begins to neck in the second (i.e., broad) cross-sectional dimension. The bar becomes very thin in the "necked down" region, Fig. 3, and the reduction in area approaches 100 pct. Often there oc-

Jan 1, 1967

By George A. Roberts

The development of an alloy system, high-speed steel, is used as an example of the progress of physical metallurgy. Tracing the history of men and their thoughts as they studied and invented and modified these materials, the story of high-speed steel since the 1890&apos;s is seen to be a long, slow, but steady progression of achievements. Today&apos;s multiplicity of high-speed steels are the result. Data are presented on quantitative metallography of carbides in high-speed steel with high vanadium content using the QTM instrument. Grindability as well as mechanical properties are related to the content of excess MC and M6C carbides in a series of high-speed steels and the newer matrix steels. These emphasize the present state of knowledge and show the current stages of thought that may affect the development in succeeding years. It is a great thrill for me, an ex-research metallurgist and ex-practicing metallurgical engineer, to speak to an audience currently engaged in both pursuits on the occasion of the 43rd Howe Memorial Lecture before the Iron and Steel Division of the AIME. I shall not review Henry Marion Howe&apos;s distinguished career, so adequately reviewed in Maxwell Gensamer&apos;s contribution in the 1965 AIME History of Metallurgy, except to point out that, while leading the life of an intellectual, he worked as a practicing research metallurgist and a practicing metallurgical engineer for significant periods of time and contributed greatly in both areas. For those of you who believe, as I do, that in the intellectual activity of metallurgy we are blessed with an intimate mixture of science and engineering (see Mehl&apos;s 1960 Howe Lecture), we might recall that Howe, while pursuing a life of writing and teaching in later years, served as the first Chairman of the Division of Engineering of the National Academy of Sciences. That metallurgists were called upon then to lead an engineering recognition movement is perhaps related to the strong part played by the AIME and its members in the recent establishment of a National Academy of Engineering and to the fact that a metallurgist is its head, 47 years after Howe served. I stress these engineering aspects for I wish to talk about a metallurgical engineering subject today. Alloy systems, physical metallurgy, and steel blended with an historical perspective and a report on new techniques to improve the old will, I trust, be of sufficient interest to bring these lectures back to the physical-metallurgy banner from which they have departed for 4 years. Those process metallurgists, open-hearth fiends, and physical chemists among you will just have to be patient. The development of an alloy system is the engineering application of scientific thought and fact. There are many interesting alloy systems, developed to a high degree of technology and sophistication over the past 40 to 70 years. These systems are bound together and related by a similar set of characteristics. For example, stainless steels are a system in which the members are related by a high chromium content which gives a corrosion-resistant characteristic. A subfamily in this system would be austenitic steels

Jan 1, 1967

By J. A. Bailey, J. H. Tundermann

The dihedral angles of the solid-liquid interfaces were measured at various temperatures above the solidus and the interfacial energies calculated when small additions of copper, indium, lithium, magnesium, antimony, and silicon were made to an aluminum alloy containing 3 pct Sn. When the results were compared with those of the Al-Sn alloy some differences were found which could be interpreted in terms of the ability of the added element to enter into solution or form intermetallic compounds with the aluminum and tin. It was shown that in some cases considerable changes in the shape of intergvanular liquid films can be brought about by comparatively small compositional changes in the alloy. DURING the melting or solidification of an alloy a temperature range is usually found where the presence of a liquid phase may be detected at the grain boundaries of a solid. It is believed that the presence of this liquid phase is responsible for hot tearing in castings and welds and hot shortness in the working of some alloys at elevated temperatures. Rosenberg, Flemings, and Taylor1 in a study of the solidification of aluminum castings have indicated the importance of intergranular liquid films and shown that their shape and distribution at the end of solidification effect the hot tearing characteristics of the material. The shape of such intergranular liquid films are determined largely by the ratio between the solid-liquid interfacial energy (yLS) and the grain boundary energy (ySS). A measure of this ratio (yLS/ySS , relative interfacial energy) is the dihedral angle 8. The dihedral angle 0 is related to the relative interfacial energy by the following expression: Rogerson and Borland 2 have also suggested that the shape of the intergranular liquid is an important factor in determining the susceptibility of a material to hot shortness. They showed that on a comparative basis materials having the lowest dihedral angles at a given temperature gave the greatest severity of cracking. They stated that liquid in the form of globules should be less harmful than liquid in the form of extensive films as more intergranular cohesion should be possible. Rogerson and Borlland 2 also showed that the susceptibility of an A1-Sn alloy to hot cracking can be reduced by small additions of cad- mium. It was found that the cadmium gave an increase in the dihedral angle at all temperatures. Ikeuye and smith3 investigated changes in the dihedral angle and relative interfacial energy with temperature for a number of ternary alloys formed when small additions of bismuth, cadmium, copper, lead, and zinc were made to an A1-Sn alloy. They found that in most instances changes in the dihedral angle were caused by compositional changes in the liquid phase; as the composition of the liquid approached that of the solid the dihedral angle decreased. They noted that the addition of a third element which was soluble in both the liquid and solid phases at a given temperature may decrease the dihedral angle (e.g., the addition of copper or zinc) but otherwise the ternary alloys formed exhibited dihedral angles between those of the A1-Sn binary alloy and those of the binary alloy of aluminum with the added element. Dwarakadasa and Krishnan4 investigated the changes in dihedral angle and relative interfacial energy with temperature when small additions of magnesium, iron, silicon, manganese, sulfur, cobalt, and silver were made to a copper alloy containing 3 pct Bi. They found that in all cases the added elements gave an increase in the dihedral angle and relative interfacial energy when compared with the values obtained for the simple binary alloy at the same temperature. It was noted that an increase in temperature gave a decrease in dihedral angle and relative interfacial energy in each of the ternary alloys studied. Similar results have been obtained by Ramachandran and Krishnan5 for the addition of small quantities of lead. This paper describes the application of dihedral angle measurement to the determination of the shapes of liquid phases at various temperatures above the solidus when small additions of copper, indium, magnesium, lithium, antimony, and silicon are made to an aluminum alloy containing nominally 3 pct Sn. An attempt is made to correlate the measurements with the relative solubility of the added elements in tin and aluminum. The work was undertaken to provide more data concerning the effects of temperature and composition on the shape of liquid films above the solidus. EXPERIMENTAL PROCEDURE In the present work ternary aluminum alloys containing nominally 3 pct Sn and small additions of high-purity copper, indium, lithium, magnesium, antimony, and silicon were made. The alloys were melted in a graphite crucible under an inert atmosphere of argon and cast into ingots 6 in. long by 0.5 in. diam. The ingots were then cut into rods 1.5 in. long, given a 50 pct cold reduction, and machined into test pieces 0.5 in. long by 0.5 in, diam for heat treatment. The alloy samples were annealed at the various test temperatures between the liquidus and solidus for approxi-

Jan 1, 1967

By J. C. Uy, A. A. Burr

A quantitative relationship between the allotropic phase boundaries of zirconium-base binary systenzs and the solute metallic valence is shown through an intermediate thermodynamic parameter. A simplified equation relating this parameter to the phase boundaries is briefly reviewed, and data from the literature are used to show the relationship of this parameter to the solute metallic valence. It has been reported that the solute metallic valence can be used as an index of phase stabilization in zirconium-base binary alloys.&apos; It was shown that the algebraic sign of the slopes of the hcp/bcc phase boundaries of zirconium alloys correspond to the algebraic sign of the metallic valence of zirconium minus the metallic valence of the solute, or, in other words, a solute whose metallic valence is higher than that of the solvent tends to stabilize the high-temperature phase while one whose metallic valence is lower than that of the solvent tends to stabilize the low-temperature phase. Further analysis of the zirconium binary systems has revealed a quantitative relationship between the solute metallic valence and the relative slopes of the two-phase allotropic boundaries. This relationship involves a thermodynamic quantity whose significance can be seen in the following section. PHASE-STABILIZATION PARAMETER Let Qb be the difference between the partial molar heats of mixing of a given solute in the two allotropic phases of the solvent which are in equilibrium with each other at a given temperature, thus A relationship between this term Qb and allotropic phase boundaries has been employed by several au-thors&apos;-= in the evaluation of phase diagrams, and can be briefly derived as follows. Referring to Fig. 1, consider the general case of two allotropic phases, each having a small mole fraction (Xa,Xb) of the solute, in equilibrium at temperature T and atmospheric pressure as represented by the reaction. solute in ß phase =solute in a phase If now a reaction occurs such that an infinitesimal amount of the solute is removed from the ß phase and added to the a phase, there would be a partial molar

Jan 1, 1967

By C. E. Lundin

The Ce-H system was investigated in the temperature range, 573° to 1023°K, and the pressure range, 10-3 to 630 Torr, as a function of &apos;composition up to 72 at. pct H. Families of isothermal arid isopleth curves were plotted from the pressure-terr~perature-composition relationships. From these curves the solubility relationships were determined for the system. The isopleths are analytically represented by equilibrium dissociation pressure equations. The relative partial molal enthalpzes and entropies of solution of hydvogen in the systerrz were calculated fronz the dissociation pressure equulions and are tabulated. The integral free energies, enthalpies, and entropies of mixing in the Ce-H system were determined from the relative partial quantities and are also tabulated. The standard free energy, enthelpy, and entvopy of reaction of the dihydride phase at kcal per kcal per mole H2, and ?S° = -34. 1 cal per deg mole H2, respectively. The equilibrium dissociation pressure equation in the two-phase region is: UNTIL recently very little was known of the detailed solubility and thermodynamic relationships of the Ce-H system. Two previous investigations1,2 are noteworthy. However, significant discrepancies and omissions exist on analyzing them. The work of Mulford and Holley1 on cerium did not clearly delineate the boundaries of the two-phase region, Cess - CeH2-x. The plateau partial pressures were not thoroughly defined and were considerably displaced in pressure compared to those from the work of Warf and Korst.2 These latter authors concentrated their studies primarily from 823° to 1023°K in the pressure range of 1 to 760 Torr. No data were determined to outline the regions of primary solid solubility and the hydride phase. Also the establishment of the plateau partial pressures was rather limited in scope. In neither work was a treatment conducted of the relative partial molal enthalpies and entropies of solution of hydrogen in the single-phase regions and the integral thermodynamic quantities of mixing throughout the system. Therefore, it was the objective of this research to determine the complete equilibrium solubility relationships and thermodynamic data for the system by pressure-temperature-composition studies. EXPERIMENTAL PROCEDURE The cerium metal for this study was donated by the Reno Metallurgy Research Center of the Bureau of Mines. Total impurity content was 0.13 pct with only 60 ppm O. The metal was checked metallographically and contained only minor amounts of second phase compared to cerium from other sources. Specimen preparation was done in a dry box flushed with argon gas. The surface of a small rectangular piece of cerium (about 0.2 g) was filed with a clean, mill file. Final weighing was done in a tared enclosed vial containing argon gas. The specimen was then loaded quickly into the reaction chamber which was purged several times with high-purity hydrogen gas and then allowed to pump to about 10-6 Torr. The furnace was heated to the reaction temperature and the run started. The equipment used to conduct the hydriding was a Sievert&apos;s-type apparatus. Basically it consisted of a source for pure hydrogen, a precision gas-measuring burette, a heated reaction chamber, a McLeod gage, and a mercury manometer. Pure hydrogen was supplied by the thermal decomposition of uranium hydride. The 100-ml precision gas burette was graduated to 0.1-ml divisions and was used to measure the quantity of gas and admit it to the chamber. The reaction chamber was a quartz tube. Prior to each run, the cerium specimen was wrapped in a tungsten foil capsule to prevent reaction of the cerium with the quartz. Control of the temperature was achieved within ±1°K. Pressures in the manometer range were measured to ±0.5 Torr and in the McLeod range (10-3 to 5 Torr) to ±3 pct. The compositions of hydrogen in cerium were calculated in terms of hydrogen to cerium atomic ratio. These compositions were estimated to be ±0.01 H/Ce ratio. The technique used to study the equilibrium pressure-temperature-composition relationships of the Ce-H system was to develop experimentally a family of isothermal curves of composition vs pressure. The range of pressure through which each isotherm was developed was from 10-9 to about 630 Torr in the temperature interval, 573° to 1023°K. RESULTS AND DISCUSSION The hydriding characteristics of cerium are iso-morphous with those of the elements of the light-rare-earth group (lanthanum, cerium, praseodymium, and neodymium) wherein the region from the dihydride to trihydride is continuously single phase.&apos; The structure of this phase is fcc.3 The heavy rare earths form a trihydride,2 which is hcp, separated by a two-phase region from the fcc dihydride phase. The Ce-H system is represented by the family of experimental isotherms in Fig. 1. Due to the small scale required to draw the curves, the experimental points are omitted; however, a total of 240 experimental data points were taken to prepare these curves. The solubility relationships can be deduced therefrom. Three distinct regions of partial pressure and composition can be seen. The region of cerium solid solution is represented by the rapidly rising isotherms in the dilute composition range. In accordance with Gibbs Phase Rule only one solid phase, the cerium solid so-

Jan 1, 1967

By T. R. Ingraham

The thermal decomposition of Nickel (II) sulfate was examined by determining the total pressure of SO3, SO2, and O2 developed over a sample when it was heated in an evacuated system fitted with a Pyrex-bellows mercury manometer. The equilibrium pressures were combined with previously published data on the oxide and sulfide systems to establish a predominance volume diagranz for the Ni-S-O system over the normal range of roasting temperature and gas composition used in the treatment of nickel minerals. The protective coating of NiSO4 which forms on the oxide during roasting, and which causes the sulfation reaction to almost cease, may be disengaged readily by temperature cycling. When nickel sulfide is roasted in air, either nickel sulfate or nickel oxide may be formed by altering the experimental conditions. Because of the differing stabilities of various metal sulfates and oxides, possibilities exist for separating some of the constituents of mineral mixtures by the technique of selective sulfation and oxidation roasting. The experimental information required to make reasonable predictions of the possibilities of this technique is incomplete and, in some cases, in conflict. As part of a general program of providing some of the required information, a study EXPERIMENTAL Materials, Apparatus, and Procedure. Fisher certified reagent-grade nickel sulfate hexahydrate was used in the source material for both nickel sulfate and nickel oxide. The manufacturer&apos;s analysis indicated: 0.001 pct Fe, 0.005 pct Cu, 0.003 pct Co, 0.001 pct C1, other 0.15 pct. The material was dehydrated, before use, by heating at 420°C for 5 hr. The oxide was prepared by roasting the sulfate in an open tray in a muffle furnace for 10 hr at950°C. Preliminary experiments which were made by thermogravimetric analysis and X-ray diffraction analysis established that only one crystal form of nickel oxide and one of nickel sulfate were involved in the equilibrium shown in Eq. [I]. The apparatus used in the experiments was described previously.1,3 The main feature is a corrosion-resistant, flexible Pyrex bellows which is used to protect the mercury in a u-tube manometer. Before a run was begun, the apparatus was washed thoroughly with hot hydrochloric acid and water and dried by heating under vacuum. The mixed sulfate -oxide sample was contained in a platinum bat rest-

Jan 1, 1967

By G. T. Hahn, C. N. Reid, A. Gilbert

An evaluation is made of the possible cautsal relationship between twinning and fracture in molybdenum. For both single and poly crystalline material no instance of twin-induced fracture was observed. Instead brittle fracture was found to be slip-induced at heterogeneities. For single-crystal material, the yield stvess in compression and the fracture stvess in tensiow obey a similar angular- relationship which follows approximately a 1/cos2 ? law. where 0 is the angle between the specimen axis and the nearest (100) plane. This sittlilarity between yield and fracture behavior casts doubt on the interpretations made previoltsly that a 1/cos2? relationship supports a critical normal fracture stress criterion. SINCE fracture in brittle materials takes place at stresses an order of magnitude lower than the theoretical strength of the lattice, it must be postulated that some stress-concentrating effect is operative during the fracture-initiation process. Several mechanisms have been proposed whereby the necessary stress concentrations could be produced. The well-known Cottrell mechanism1 describes a dislocation interaction which can lead to the formation of an incipient cleavage crack on a cleavage plane, and both zener2 and stroh3 have discussed models which predict the stress concentration at the intersection of a slip band with a grain boundary. When twinning occurs twin/twin intersections and twin/grain boundary intersections represent another possible means of fracture initiation. Although still controversial, the concept of twin-induced fracture is supported by a weighty mass of evidence, which has been reviewed in a recent paper.4 This investigation was conducted in order to assess the extent to which the brittleness of molybdenum can be ascribed to this cause. Emphasis was placed on seeking direct metallographic evidence for twin-induced fracture such as arrangements of twins located at the fracture origin. EXPERIMENTAL PROGRAM Materials. The experimental materials are described inTable I. From the chemical analyses and estimates of the amounts of interstitials likely to be retained in solution,5 it is concluded that all were mul-tiphased systems. X-ray diffraction experiments6 showed no evidence of preferred orientation in the polycrystalline materials. Single crystals were grown from Molybdenum X and Y using the floating-zone technique,&apos; in a vacuum of better than 3 x 10-5 Torr. However difficulties were experienced with Molybdenum X due to violent gas evolution from the molten zone, and additional crystals (Crystals 3 to 6) were produced by annealing for 5 1/2 hr at 2300°C under a vacuum of 10-4 Torr. Techniques. A series of tension, compression, and bend tests was conducted. Tension tests were used to demonstrate brittle behavior, to measure brittle-fracture stresses, and to provide fractured specimens for metallographic inspection. Compression tests were employed in order to obtain some ductility and a measure of the yield stress. Furthermore, it was considered that compression loading would permit the study of crack nucleation in the absence of propagation. The bend tests were conducted to facilitate identification of the fracture origin, which would be expected to be at, or near, the tensile surface of the sample. Tests were carried out at temperatures between 78" and 298°K attained by means of a liquid-nitrogen evaporator of modified Wessel design.&apos; Specimens were fashioned by mechanical grinding, and, prior to heat treatment, were electropolished at 10 v in a 3:l mixture of ethyl alcohol and sulfuric acid, using a stainless-steel cathode. Except where noted, a strain rate of 4 pct per min was used. All specimens had a gage section 0.75 in. long; diameters of 0.10 and 0.20 in. were adopted for the tension and compression specimens, respectively, the former of single shoulder design, the ends being gripped in split collets with a conical bearing surface. In the bend test, electropolished specimens measuring 0.080 by 0.25 by 1.25 in. were deformed at 78°K by four-point loading. The bending device had spans of 1 in. between the outer and 4 in between the inner fulcra; it was stressed between the compression anvils of the Instron machine at a constant deflection rate. EXPERIMENTAL RESULTS Polycrystals. Tension and Compression Tcsls. It is apparent from Fig. 1(a) that above 170°K fracture of Molybdenum X takes place at stresses equal to or greater than the compressive yield stress whereas

Jan 1, 1967