By Victor A. Phillips

A series of specimens of a Cu- 3.23 pct Co alloy were prepared with particle diameters from zero to 590A. The samples were then cold-rolled 95 pct and the effects of the particle size on the behavior on annealing for hr at temperatures between 100" and 900°C were studied (by hardness, light, and electron metallography). Particles, particularly for d r 105 to 590A, greatly impeded softening and vecvystallizn-tion, and tended to give elongated grains. Particles deformed fairly homogeneously with the ,matrix, be- IN a previous study by the author,' the growth of cobalt-rich precipitates was followed electron microscopically in Cu-3.12 Co alloy as a function of aging, typically at 650°C. The coherent spherical precipitates grew to 520 + lOOA average diam before spontaneously losing coherency and developing (111) facets. Stretching a few percent after precipitation 2aused loss of coherency to occur sooner at about 220A average particle diam. The particles apparently retained their fcc structure after loss of coherency. coming lau2ellae. For d = 55 to 180A, these lamellae gave streak-contrast effects apparently due to coherency strains , and spheroidized on annealing at 600" to 650°C, forming coherent particles. Particles of d = 250 ov 320A lost coherency during t-olling, giving incoherent lamellae. Recrystallization apparently occured by growth of new grains into unrecrystallized (recovered) material at temperatures below that at which cobalt atoms had much mobility. The present study was undertaken to explore the effect of cobalt-rjch particles of various average sizes from 50 to 600A diam on the isochronal annealing behavior of copper after heavy cold rolling. The previous work' was used as a guide in preparing the two-phase series of prerolling structures. The solution-treated alloy was also rolled for comparison. A further question of interest in the present study was whether dislocation and particle hardening were additive, since the prerolling structures covered the full range unaged - peak aged — overaged, and further precipitation might occur on annealing after cold rolling. Although there have been exhaustive studies of the isothermal2"6 and is~chronal annealing behavior of

Jan 1, 1967

By D. T. Peterson, F. A. Schmidt, J. D. Verhoeven

The velocity of mig-ration of these solutes in thorium metal due to a high amperage dc current was measured at several temperatures. All three solutes migrated in the same direction as the electron flow. Diffusion coefficients were combined with the migration velocities to predict the steady-state concentration profile. Electrotransport was shown to be an effective method of removing carbon, oxygen, and nitrogen from thorium and resistance ratios several times larger than for crystal bar thorium were achieved. However, the maxirnum attained purification was well below the predicted values, apparently due to some form of contamination. THE migration of solutes in metals when a high current density dc current is passed has been known for many years. This phenomenon has been the subject of a number of reviews published in recent years.l~* Many of the earlier investigators of electromigration of interstitial solutes interpreted the direction and velocity of migration on the basis of a charge on the solute particle. This interpretation is unclear because, in a given experiment, one cannot separate the contributions to the force moving the solute which arise from the charge on the solute in an electric field gradient and the momentum transfer from the scattering of the electrons or holes. There have been only a few quantitative measurements of interstitial migration velocities and some of these have been characterized by poor accuracy or by errors in the analysis of the experiment. The electrotransport mobilities of carbon, nitrogen, and oxygen in thorium were determined by observing the rate of movement of a discontinuity in the concentration profile. This method was used by Carlson el a~.~ to determine the mobilities of interstitial solutes in yttrium and its advantages are discussed in that paper. The specimen is essentially a pair of semi-infinite, bar-type diffusion couples. The electro-transport velocity was measured by observing the displacement of the mean concentration point in a measured length of time. The diffusion coefficients were calculated by the Grube method from the concentration profile. The transport mobilities and diffusion coefficients can be used to predict the concentration profile in an electrotransport experiment of a given time, current density, and specimen length. At long times a steady state will be reached such that the natural logarithm of the concentration of each solute varies linearly along the bar with a slope which is equal to the velocity of the migrating solute divided by its diffusion coefficient. The estimation of the purification potential of electrotransport is discussed by ~erhoeven.' A comparison of the concentration profile and the purification which should be expected from known solute velocities and diffusion coefficients with that which is obtained in an experiment can be very useful in indicating whether the maximum possible purification has been achieved. EXPERIMENTAL METHOD The apparatus used in this study consisted of a sample chamber which was equipped with two electrodes, a sight glass, and a flange for mounting to a high-vacuum system capable of obtaining pressure of 2 x lo-? Torr. The chamber was made of stainless steel and was 4 in. in diam and 6 in. long. The seal between the electrodes and the chamber was made with "0" rings and compression bushings. The thorium specimens were threaded and screwed into tantalum "U"-shaped adapters attached to the ends of the electrodes. This arrangement is shown in Fig. 1

Jan 1, 1967

By W. C. Winegard, J. R. Carruthers, A. Plumtree, L. R. Morris

The unidirectional solidification of dendrites containing central twin planes was studied in A1-Ti alloys. Once nucleated, the twinned dendrites are a Twore ejficient form for solute redistribution and therefore grow in preference to the normal columnar dendvites. Comparison of these twinned dendrites to adjacent colunmar dendrites by means of decanting experinzents and electron-probe rnicvoarmlysis indicates that these special dendrites grow with less undercooling than normal dendrites. These findings are further supported by the effect of forced convection on the dendrite morphologies. COMMERCIAL semicontinuous cast ingots of most aluminum alloys frequently exhibit large grains which appear to be composed of hundreds of parallel, continuous, thin lamellae. This structure has been termed "basaltic",' "fiederkristall", or, commonly, "feathery grain". The lamellae are 'about 100 p thick, several inches long, and each lamella contains a central (111) coherent twin boundary. The feathery grain has been reported to have a (112) direction2 and a (110) direction4 in the twin plane parallel to the casting direction, in contrast with the usual columnar structure where a (100) direction predominates. Aust et uZ.~ proposed that the twin boundaries were growth twins nucleated by stacking faults on the octahedral planes. chalmers6 has suggested that feathery grain may grow by a re-entrant edge mechanism, as proposed by wagner7 for twinned dendritic growth in germanium. Cahn et ~1.~ have concluded that the occurrence of feathery grain is evidence of some form of lateral layer growth rather than the atomically continuous growth normally observed in metals. The postulates by Chalmers and Cahn would seem to be contradicted by the work of Nakao~"' who showed that feathery grain only occurs when growth rates are high and the aluminum contains some solute. Specifically, Nakao found that in order to obtain feathery grain, in small castings solidified unidirec-tionally upward, the rate of growth must be above 2.4 cm per min and a critical solute concentration must be present. Below this solute concentration the grain structure was totally columnar. The critical solute concentration was found to be approximately: 0.04 wt pct Ti, 2 wt pct Cu or Mg, and 8 wt pct Zn. As pointed out by Chalmers it is not obvious why a twin-plane re-entrant edge mechanism would occur in aluminum which is thought to have a diffuse solid-liquid interface. The present experiments were undertaken to determine the growth mechanisms in- volved and to study the solute segregation in more detail. EXPERIMENTAL PROCEDURES Alloys ranging in composition from 0.05 to 0.23 wt pct Ti* were prepared from 99.9 pct pure Ti and 99.993 pct pure Al. Two-hundred-gram samples of A1-Ti binary alloys were solidified unidirectionally and vertically upward from a water-cooled copper base, in a heated insulated mold. The 1-in.-diam, 6-in.-length mold was made of Marinite (manufactured by Johns-Manville Co.). The mold was attached to a 24-in. pivoted arm such that by dropping a weight the mold was rotated 180 deg, throwing the liquid metal from the solid. In this way, the solid-liquid interface was revealed by decanting. A sketch of the decanting mold is shown in Fig. 1. The alloy was poured into the mold at temperatures ranging from 680" to 750°C, partially solidified by water cooling from the base, and decanted after a measured time interval. Growth rates for each metal-pouring temperature were calculated from solidification-time vs length solidified curves. Temperature gradients in the melt were measured using four No. 34 gage thermocouples which protruded into the mold cavity. Grain orientations were determined by X-ray diffraction using Laue back-reflection techniques. Grain substructures were examined metallographically, using polarized light, by applying a thin epitaxial anodic film to polished sections after the method of Hone and pearson." Titanium micro segregation was measured by electron-probe microanalysis using a NORELCO AMR/~ with a mica crystal and proportional-flow counter. Several of the cast samples exhibited feathery and columnar dendrites growing in the same direction and

Jan 1, 1967

By H. H. Kellogg

A model of the slag-fuming process for recovery of zinc oxide fume from lead blast furnace slags, adapted to solution by a digital computer, is presented. The model incorporates the variaticm with time of the following: the fuming of zinc and lead, the change in the ferrous-ferric ratio in the slag, the transfer of sulfur to and from the slag, the temperature of the liquid slag, the temperature of the gases and fume which exit to the flue, the heat losses to the water jackets, and the amount of frozen slag on the water jackets. The assumptions which underlie the model-some of which are but crude approximations—are discussed. Despite some obvious shortcomings, the model simulates faithfully many of the important features of practical slag-fuming operations. The behavior of the model is compared with the operation of the American Smelting and Refining Co. fumzace at El Paso, Tex. The model is used to predict the effects on performance of changes in the coal rate, the temperature of the secondary air, and the composition of the coal. THE fuming of lead blast furnace slag for recovery of zinc oxide is standard practice today, and it has been the subject of several previous attempts at mathematical process analysis.'-' The mathematical process model described in this paper incorporates many of the features from the earlier studies, but it is a far more complete and realistic representation of the commercial process in that the following additional features have been included: the fuming of lead as well as zinc; the transfer of sulfur between slag and gas; the addition of slag feed in batches, over a period of time; tapping of the final slag over a period of time; the change of slag temperature with time. The additional features of the present model add greatly to the mathematical complexity, but this difficulty has been obviated by programming the model for solution by a digital computer. The IBM 7094 computer solves the model for one operating cycle of the fuming furnace in less than 1 min. It is doubtful if the same calculations could be completed with the aid of a desk calculator in less than a month. The computer program, written in the Fortran IV language, is too lengthy for presentation here.* Instead, this paper As shown in the sections which follow, it does simulate with remarkable faithfulness most of the known behavior of the industrial process. On the other hand, the model contains several gross simplifications of both the chemistry and heat balance, necessitated by the lack of more exact knowledge. In addition to these known weaknesses, it is not unlikely that those more intimately acquainted with industrial practice than the author will find other additions to or modifications of the model which will improve its utility and reliability. CHEMISTRY In brief outline, the present model treats the fuming furnace as two units, A and B, in series. In A the batch of slag reacts with the continuous stream of air (primary and secondary) and fuel injected at the tuyeres, to produce a stream of hot, reduced gases containing zinc vapor. The zinc content of both the slag and the product gas changes with time because of the batch nature of the process. Unit A is called the "lower furnace" in this paper; physically, it is considered to be that part of the fuming furnace which lies below the charge port. In B, the "upper furnace", the product gas from A is burned with the stream of "tertiary" air, to produce zinc oxide fume. The performance of B also depends on time because of the time dependence inherited from the product gas of A. The rate behavior in the lower furnace determines the important features of the process—the rate of elimination of zinc and lead from the slag, and the amount of fuel required for this purpose. Bell, Turner, and peters' published the first useful model of the lower furnace. They employed the assumption that, at any instant of time, the slag and reduced gas reach a state of equilibrium, according to the reactions: They cited only indirect evidence in support of their assumption of slag-gas equilibrium, yet several more recent laboratory studies of the activity of zinc oxide in slags4-8 have produced evidence which supports their view. On first acquaintance it seems unlikely that a high-output "rate" process like slag fuming would even approach an equilibrium state. The author, in an earlier study,' established, however, that the gas-slag interface in a fuming furnace was capable of such high mass-transfer rates that a close approach to equilibrium between gas and slag was quite probable. In devising the present model it was decided to assume a state of equilibrium between slag and gas at the outset, and then to modify this assumption as necessary in order to make the model agree with the be -havior of the actual process. Up to this time the assumption remains a part of the model, since no behavior

Jan 1, 1968

By D. G. Westlake

The electrical resistance of a series of V-H alloys (0 to 3.5 at. pct H) has been measured over the temperature range G° to 360°. Interstitial impurities made contributions to the residual resistivity, but not the ideal resistivity. The contribution of hydrogen in solid solution is expressed by Ap = 1.12 microhm-cm per at. pct H; but the contribution of precipitated hydride was negligible. A portion of the so1vu.s for the V-H phase diagram is presented. The solubility limit is given by In N (at. pct H) = (5.828 i 0.009) - (2933 i 44)/RT. Comparison of critical temperatures joy hydride precipitation and published critical temperatures for hydrogen embrittlement suggests the two are related. ThiS study was initiated as part of an investigation of the mechanism by which small concentrations of hydrogen embrittle the hydride-forming metals at low temperatures. It has already been shown that, in the case of hcp zirconium, a reduction in ductility accompanies the strengthening resulting from precipitation of a finely dispersed hydride phase.''' Our attempts to detect a similar precipitation of a second phase at low temperatures in V-H alloys by transmission electron microscopy have been thwarted because we have been unable to prepare thin foils that are representative of the bulk material with respect to hydrogen concentrati~n.~'~ The present investigation establishes the solvus of the V-H system at subambient temperatures. Subsequently, we hope to be able to determine whether the embrittlement temperature is related to the critical temperature for precipitation of the hydride in a given V-H alloy. veleckis5 has proposed a partial phase diagram for the V-H system based on extrapolations of the pressure-composition relations he measured at higher temperatures. Kofstad and wallace' conducted a similar study of single-phase alloys but did not attempt to establish the phase diagram. Zanowick and wallace' and ~aeland' have studied a portion of the phase diagram by X-ray diffraction, but they investigated no alloys in the hydrogen concentration range 0 to 3 at. pct, the range of interest to us. EXPERIMENTAL PROCEDURE The vanadium was obtained from the Bureau of Mines, Boulder City, Nev., in the form of electrolytic crystals. The analyses supplied with them listed 230 ppm by weight metallic impurities, 20 ppm C, 100 ppm N, and 290 ppm 0. The crystals were electron-beam-melted into an ingot that was rolled to 0.64 mm. Strips, 60 mm long and 4.2 mm wide, were cut from the sheet, and both rolled surfaces were ground on wet 600-grit Sic paper to produce specimens 0.4 mm thick. They were wrapped in molybdenum foil, vacuum-encapsulated in quartz, and annealed 4 hr at 1273°K. The specimens were annealed in a dynamic vacuum of 2X lo-' Torr for 30 min at 1073°K for dehydrogenation, and charged with the desired quantity of hydrogen by allowing reaction with hydrogen gas at 1073°K for 2 hr and cooling at 100°K per hr. Purified hydrogen was obtained by thermal decomposition of UH3. Sixteen specimens were studied: two contained no hydrogen and the others had hydrogen concentrations between 0.5 and 3.5 at. pct (hydrogen analyses were done by vacuum extraction at 1073°K). Electrical resistances were measured by the four-terminal-resistor method on an apparatus similar to the one described by Horak.~ The specimen holder was designed so that both current and potential leads made spring-loaded mechanical contact with the specimen. The potential leads were 30 mm apart, and the current leads were 55 mm apart. The current was 0.10000 amp. We used the following baths for the indicated temperature ranges: liquid nitrogen, 77°K; Freon 12, 120" to 230°K; Freon 11, 230" to 290°K; and ethanol, 290" to 340°K. Temperatures lower than 77°K were achieved by allowing the specimen to warm up after removal from liquid helium. Temperatures above 77°K were measured by a calibrated copper-constantan thermocouple (soldered to the specimen holder) and below 77°K by a calibrated carbon resistor. The temperature of the bath changed less than 0.l0K between duplicate measurements of the resistance. RESULTS AND DISCUSSION Typical plots of resistivity p vs temperature T are shown in Fig. 1. In the interest of clarity, only five curves are presented and the data points have been

Jan 1, 1968

By John Chipman

The concentration of a solute in a dilute ),zetallic solution may be measured by any of several parame- ters including weight percent, atom fraction, atom ratio, and lattice ratio. The ratio of filled to unfilled interstitial sites is useful for interstitial solutes. A variable 2 proportional to this ratio is used as a measuve of concentration. For component 2 irz a bitzary solution z2 = n2/Ym - nz/b) where b is the numberber of interstitial sites per lattice atom. For a t~lul-ticortzporzent solution this becomes zz = n2/(nl + Cvjnj) in which Vj = - l/b for an interstial solute and +1 for a substitulional solute. In the infinitely dilute solution the activity of an interstitial solute 2 is proportional lo z2. At finile concentration the departure from this limiting law is expressed us an activity coefficient, his coefficient is a function of concentra1io)z expressed as tevactiolz coeffcient 8; is analogous to the jark~iliar e£ bul is found to be independent of concentvation in certain solutions for which data are available. It is found that the same equations may be used to express the activity of a nonmetallic solute, sulfur, in liquid solutions of iron containing other solutes, both metallic and nonmetallic. For a nonmetallic solute or for one which strongly increases the actiuity of sulfur, it is convenient to assign arbitvarily a value vj = — 1. When this is done the derivative is found to be constant in each of the ternary solutions studied. The activity coefficient of sulfur in a complex liquid iron solution may be expressed as where nk is a second-order cross product determined in the quaternary solution Fe-S-j-k. The equation is used to calculate tlze activity of sulfur i)z three sevetl- component solutions. IN thermodynamic calculations concerning dilute solutions it is unnecessary to invoke laws and relations which extend across the concentration range to include concentrated solutions. In most binary metallic systems, as arkeen&apos; has recently pointed out, there exist two terminal composition regions of relatively simple behavior, connected by a central region of much greater complexity. When the solute is a nonmetal there is only one such region and in many systems the concentration range is extremely limited. It is the purpose of this paper to suggest a method for the calculation of activities in such a terminal region in which one or more solutes are dissolved in a single solvent of predominantly high concentration. HENRY&apos;S LAW In the usual textbook statement of Henry&apos;s law, concentration is stated in mole fraction. This has the advantage that it makes Henry&apos;s law thermodynamically consistent with Raoult&apos;s law. Since all measures of concentration at infinite dilution are related by simple proportion it follows that mole fraction, molality, atom ratio, weight percent, or any other unit of concentration can be used with the appropriate constant. At finite concentrations, however, calculations based on the law depend upon the unit employed. Deviations from Henry&apos;s law at finite concentrations depend upon the composition variable employed. They are evaluated in terms of activity and interaction coefficients2 which have become familiar features of metallurgical thermodynamics. It is the purpose of this paper to propose a measure of concentration for metallic solutions containing interstitial or nonmetallic solutes by means of which the calculation of activities in complex solutions may be simplified. The discussion will be restricted to free-energy interaction coefficients3 typified by Wagner&apos;s c|a BINARY SOLUTIONS The several measures of concentration which are to be considered are shown in line a of Table I. The corresponding activity coefficients are in line b and the deviation coefficients, sometimes called self-interaction coefficients, are in line c. Henry&apos;s law simply states that the activity coefficient approaches a constant value at infinite dilution. By adoptihg the infinitely dilute solution as the reference state and defining the "Henrian" activity as equal to the concentration in this state, the activity coefficient is always unity at infinite dilution. This convention is far sim~ler and more useful in dilute solution than emploiment of the &apos;Raoultian" activities and it will be used in the following discussion. The several definitions and equations of Table I will be referred to by means of their coordinates in the table. Early observations of deviations from Henry&apos;s law in metallic solutions were shown graphically4 rather than analytically. For the case of sulfur in liquid iron5 the slope of a plot of logfs vs (%S) was constant in the range 0 to 4.8 pct S, indicating constancy of eh2&apos; in Ic. He was proposed by wagnerz and has been widely adopted. The a function of IIIc recently employed by ~arkenl was designed specifically for dilute solutions. Darken has shown that the value of a12 remains essentially constant for many binary solutions within a substantial range of compositions. The atom ratio is directly proportional to the molalitv.<, a conventional measure of concentration. IVb and C served as the basis for smith&apos;s6 classic studies of

Jan 1, 1968

By J. Clair, H. Mirabel

The determination of the temperature and electrical potential distributicms in the cathodes of aluminum electrolytic cells is difficult. The reascms come from the various nature and the intricate three-dimensional geometry of the materials; besides thermal and electrical phenomena react upon each other. A method of calculation using a computer program applied to a mathematical model, figuring the cathode, is developed. Both of the thermal and electrical phenomena are simultaneously considered. Temperature and electrical potential distributions are finally obtained by successive iterations. Results are compared with measurements on industrial cells. Theoretical and practical applications of these studies are given. Up to the present time the study of the distribution of the temperatures and electric potentials in the electrodes, anode and cathode, of the electrolytic cells used for the production of aluminum was limited to one of the two aspects of the phenomena because of lack of a simultaneous method of calculation. For example, the anode or cathode drop was studied assuming that the temperatures in the iron and carbon are known, a method that obviously is very approximate since iron resistivity, in particular, greatly varies with temperature, which in turn depends on current density. Consequently we tried to find a method of calculation simultaneously taking into account both thermal and electrical phenomena. We proceeded to the study of the cathodes as an initial approach to the problem. Although the cathode and surrounding materials may have varied forms and particularly very heterogeneous characteristics, their structures are simpler than that of the Sijderberg anode and boundary conditions are more easily represented than in the case of anodes even though they are prebaked. The study was in two parts: a) development of a model schematizing the true geometry of a cathode and defining the thermal and electrical boundary conditions, and b) working out a method of calculation of the temperatures and potentials by means of an electronic computer. To facilitate solution of the problem, a model was used initially much simplified in comparison with an actual cathode. This model permitted development of the method of calculation. In a second phase, this model was adjusted to the study of actual cathodes and applied to different types of cells: low- or high-intensity cells, cells set up at ground level or above ground level, cells with cathodes more or less heat-insulated. Simultaneously measurements were made with cells equipped with cathodes of the types studied to compare the values resulting from calculation. The initial model was also used for general studies, in particular for studying the effects of current density in the carbon and iron. The results were confirmed or made precise by the model of the true cathodes. This report successively describes: a) the manner in which the model representing a cathode was worked out, with the simplifications and/or the hypotheses used, b) the method of solution of the problem by means of the electronic computer, and c) an example, stating the extent to which the results obtained may be realistic. Further the possibilities offered by such a study are examined. 1) CATHODE REPRESENTATION The purpose of this phase is to represent the cathode in the form of a so-called "mathematical model", that is with a simplified geometrical configuration, in order to meet the subsequent calculation requirements, while keeping to the true facts as closely as possible. This model further includes the thermal and electric conductivities with regard to temperature for the varied materials composing the cathode, as well as the thermal and electrical conditions at the model boundaries. 1.1) Guiding Principles. For calculating the temperatures and potentials the model is divided by trior-thogonal planes into a network of small elementary parallelepipeds. At the summit of these parallelepipeds&apos; so-called mesh points, the temperatures and potentials are computed. The number of mesh points is of course limited by the capabilities of the computer, since 1) the number of equations to be solved depends on the number of mesh points selected, and 2) the amount of time spent by the computer considerably increases with increasing this number. These conditions call for the following requirements as concerns the model: a) Dimensional requirements: the calculation will be all the more accurate as the network is more closely meshed. Since the number of mesh points is limited in practice, it is necessary to restrict the dimensions of the model. b) Geometrical requirements: so as to make things easier in working out the network, the model must be given a simple geometry. In particular, it will be convenient to have the cathode so constituted that the surfaces limiting the cathode and the surfaces within the cathodes separating the different materials consist of triorthogonal planes. 1.2) Schematization of the Cathodes. After the tech-

Jan 1, 1968

By G. Y. Chin, W. L. Mammel

The problem of selection of the active slip systems for a crystal undergoing an arbitrary strain has been analyzed by Taylor and by Bishop and Hill. The Taylor analysis is based on a principle of&apos; virtual work, and involves finding, among numerous cotnbinalions of slip systems that satisfy the imposed strain, the combination in which the sum of the glide shears is a minimum. Previously, Taylor has treated the case of axisymmetric flow when slip occurs on (111)(110) (or {110)(111)) systems only. His analysis has now been extended by computer methods to the cases of slip on {112}(111) and {123)(111) systerns and of mixed slip on {110), {1 12), and (123) planes with a common (111) slip direction, all of which are important in the deformation of bcc crystals. The results are computer-plotted as contours of the ratio of the floe strength to the critical resolved slzea-r stress for slip, for axial orientations distributed throughout the standard stereographic triangle. Implications of the computer results to texture develop,merit, texture hardening, and dislocation theories oj work hardening are discussed. WhEN a single crystal is extended in the usual tension test, the lateral dimensions can change relatively freely. In this case, the glide shear produced by slip on a single slip system is sufficient to accommodate the (tensile) deformation. Since slip is governed by a critical resolved shear stress law (the Schmid law&apos;), the single active slip system is one for which the stress, resolved on the slip plane and in the slip direction, is the highest among the several equivalent slip systems. This amounts to saying that a value M = U/t = y/~ is a minimum among the equivalent systems, where M is the inverse of the familiar Schmid factor (a and E refer to tensile stress and strain, and T and y refer to resolved shear stress and shear strain). A grain embedded in a polycrystalline aggregate, on the other hand, cannot freely change its shape due to constraint from its neighbors. In this case, slip from five independent slip systems (to accommodate five independent strains) is generally required.&apos; Based on the principle of virtual work and assuming that the critical resolved shear stress for slip is the same for all systems, Taylor hypothesized that, among all combinations of (five) slip systems which are capable of accommodating the imposed strain, the active combination is that one for which the sum of the absolute values of the glide shears is a minimum. Again, this is equivalent to saying that the value of M = CjlyjI/ is a minimum, in analogy to the single slip case. Taylor aminimum,analyzed the case of {111)(110) slip for fcc metals, and applied the analysis to crystals undergoing axisymmetric flow, that is, the same macroscopic shape change as the poly crystalline aggregate under uniaxial tension (or compression). For the twelve equivalent {111}( 110) slip systems, there are 384 independent combinations of selecting five systems to satisfy the five independent linear equations of imposed strain.4 Taylor calculated the value of M for each combination* and obtained the active com- *A number of the independent combinations were omitted from consideration in Taylor&apos;s original work (see Ref. 5). bination (minimum M) for a number of axial orientations distributed throughout the standard stereographic triangle. Later work by Bishop and Hill*&apos;8 showed that Taylor&apos;s least-shear hypothesis was equivalent to a maximum work principle which they advanced. Using the simplified Bishop and Hill method for {111)(110) slip, Hosford and Backofen&apos; obtained detailed contours of constant minimum M for the same axisymmetric flow case. In contrast to {111}(110) slip in fcc metals, slip in bcc metals is generally described as occurring on {ll~)(lll), {112)(111), {123) (111) systems as well as mixed slip composed of all three. Since the direction cosines of the slip plane normal and the slip direction enter as a product in the Taylor analysis, the Taylor solutions of ,M for {110)(111) slip are identical to those for { 111} 110) slip. The other three cases of slip, however, have not been solved. In view of the numerous combinations of slip systems involved in the calculations, the Taylor analysis is clearly oriented toward computerized solutions. THE TAYLOR ANALYSIS In order to obtain the active combination of (five) slip systems by solving for the minimum value of M = we first express the (small) strain components E,, with respect to the cubic axes 1, 2, 3 ([loo], [010], [001], respectively) of the crystal, in terms of the sum of the glide shears yj from slip systems j: where n, and n,j refer to direction cosines of the slip plane normal, and dri and dsi to direction cosines of the slip direction, of slip system j, all referred to the cubic axes. In practice, the strain components are given with respect to the specimen axes X, y, 2. These components are readily converted to ers through the tensor transformation where irk and 1,~ are the direction cosines between the two sets of coordinate axes.

Jan 1, 1968

By P. R. Schmidt, N. J. Themelis

A study zvas made of the deoxidation of copper at 1170°C by injecting a jet of carbon monoxide vertically upwards into the melt. The effects of submersion depth (2 to 20 cm), orifice diameter (& to 5 in.), and gas velocity (100 to 3650 ft per sec) were examined. In the oxygen range 0.1 to 1.0 pct 0, the overall rate was conlrolled by gaseoLcs mass Lransfer. The results were interpreted in terms of a rate coefficient per unit depth which was found to be constant with distance along the jet axis and nearly proportional to the orifice Reynolds number in the range 1000 < NReo < 9100. AS the gas flow rate through an orifice submerged in a liquid is progressively increased, at least three regions of bubble formation may be distinguished. At very low rates, the formation of bubbles is practically a static phenomenon, depending on the orifice diameter, the liquid surface tension, and the densities of the two phases. In this region, the bubble size is constant while the frequency of bubble formation increases with gas flow rate.&apos;-3 At higher flows (500 < NR~, < 2100), the frequency of bubble formation reaches a steady value and the bubble size increases with gas flow rate; when the bubbles issuing from the orifice become so large that they start coalescing to form larger bubbles, the turbulence induced in the liquid by the passage of previous bubbles shatters them into small bubbles of varying size. Finally, for gas velocities in the intermediate and turbulent regions of flow (NR,, > 2100) a tangential separation surface is created around the jet and momentum transfer takes place between it and the surrounding liquid medium. The entrainment of liquid and the resulting deceleration of the gas-liquid dispersion causes the jet to expand forming a characteristic jet cone. The large velocity and density differences between the jet and the liquid result in a high degree of instability and the jet envelope fluctuates rapidly.The characteristic jet cone can be observed by means of time exposure photographs such as those shown in Fig. 1 for an air jet introduced vertically upwards in a water bath. High-speed photography has showns that the gas-liquid dispersion within the cone consists of small bubbles the size of which depends mainly on the jet orifice diameter and Reynolds number. In the laminar region of flow, the following correlation was obtained by Leibson: The results of Liebson et a1.&apos; are plotted in Fig. 2. It can be seen that the region 2000 < NReo c 10,000 is not well-defined experimentally. In the entrance to the fully turbulent region of flow (NR,, = 10,000), the mean bubble diameter decreased to about 0.4 cm and varied only slightly from there on according to the correlation:

Jan 1, 1968

By E. L. Raymond

The effect of heat treatment on the microstructure and resultant notch-bar rupture life of ZNCONEL alloys X- 750 and 718 was studied. It was found that the primary effect of heat treatment in rendering these alloys notch-ductile is the elimination of any y&apos; denuded zone adjacent to the pain boundaries. The mechanisms by which such a denuded zone can arise and be eliminated by heat treatment are discussed. InCONEL Ni-Cr alloy X-750 and INCONEL Ni-Cr alloy 718 are age-hardenable austenitic materials. Alloy X-750 is used for its corrosion and oxidation resistance and high creep-rupture strength up to 1500°F. Alloy 718 is used most effectively up to 1300°F. One of the most important areas in their development has been establishment of consistently good rupture properties, especially in the presence of a stress concentration, such as imposed by a notch. A desire to improve these properties has led to extensive studies of the effect of heat treatment on the micro structure of these alloys and their performance in stress-rupture tests. In earlier investigations"~ of INCONEL* alloy X-750, *INCONEL i s a Registered Trademark of The International Nickel Co., Inc. grain boundary carbide morphology was linked with stress-rupture properties. If, during heat treatment, the carbide MZSC was precipitated in the grain bound-ary in a cellular form, poor rupture properties re-

Jan 1, 1968

By J. E. Hanlon, S. R. Butler, R. J. Wasilewski

It is known that stoichiometric NiTi transforms to a structure of lower symmetry near room temperature. The present investigation deals primarily with the changes in the electrical and magnetic properties which occur at the transformation. The effects of composition and various heat treatments on electrical properties are also discussed. In recent investigations by Purdy and Parr,&apos; Wang et a1.,2 Dautovich and Purdy,~ Dautovich et a1.,4 and the authors, ~,&apos; NiTi has been observed to undergo a martensitic phase transformation from the ordered CsCl (B2) structure to one of lower symmetry. The crystal structure of the low-temperature modification is still not completely worked out. This transformation occurs near room temperature for the stoichiometric composition. The thermodynamic, elastic, crystallographic, and microstructural characteristics of this transformation for some compositions have been previously reported.&apos;-= In the present investigation, the changes in the electrical transport properties and magnetic susceptibility of NiTi when it undergoes the martensitic phase transformation have been measured. The approximate composition range covered is 48 to 52 pct Ti.* *All compositions are given in atomic percent._____________________ EXPERIMENTAL PROCEDURES AND RESULTS 1) Sample Preparation. The NiTi alloys were prepared from iodide titanium (>99.92 pct Ti) and vacuum-premelted carbonyl nickel (>99.95 pct Ni) by repeated arc melting under gettered argon and casting in a water-cooled copper mold. After the cast buttons were hot-forged at 800" to 950°C, the oxidized surface was removed by grinding and etching. Samples were cut from the worked polycrystalline buttons. After fabrication, the samples were annealed 1 hr at 900°C and water-quenched. The composition of the alloys was assumed to be the same as in the initial feed. This assumption was supported by material balance checks on 100-g arc-melted buttons which demonstrated quantitative recovery to within k0.02 pct. The oxygen content of the alloys was &apos;150 ppma (weight) and the carbon content was 30 to 50 ppm. 2) Electrical Resistivity and Hall Effect. The electrical resistivity was measured over the composition range 48 to 52 pct Ti for temperatures varying from 4.2"K to 900°C. The high-temperature and many of the low-temperature experiments were carried out using conventional 4-probe dc techniques.7 The Hall coefficient and ac resistivity were measured at 20 cps using the apparatus shown schematically in Fig. 1. The equipment is basically an ac potentiometer: The resistive or Hall voltage of the sample is balanced by a comparison voltage provided by a dividing network across a standard series resistance. The off-balance signal is amplified by a Tektronix 122 amplifier and detected by a Princeton Applied Research (PAR) phase-sensitive detector. The precision of the resistivity and Hall coefficient measurements is i0.1 and i3 pct, respectively. The uncertainty in the data is increased by i2 pct from the precision limits because of uncertainty in dimensions and possible end effects. The temperature dependence of the electrical resistivity and Hall effect for a stoichiometric (50.0 pct Ti) NiTi sample are illustrated in Fig. 2. Above 75"C, this sample has essentially the B2 structure, while below about 0°C it is completely in the low-tempera-

Jan 1, 1968

By V. Koump, R. H. Tien, W. J. Kim

This paper presents an approximate solution of the problem of freezing of a binary alloy. he alloy is in the form of a one-dimensional slab of finite thickness. The surface temperature of the slab is assumed to be constant and lower than the solidus (or eutectic) temperature. The densities of the liquid and the solid are assumed to be equal. For a given binary alloy system, initial concentration of solute and surface temperature, the solution yields a) the temperature distribution in the solid skin, b) the temperature, concentration, and solid fraction distribution within the solid-liquid region, and c) the positions of the liquidus and the solidus (or eutectic) fronts as a function of time. The results of calculation for Fe-C and Fe-P systems are presented. In this investigation we are considering the problem of solidification of a binary alloy. The alloy is in the form of a one-dimensional slab of finite thickness. The molten alloy is initially at liquidus temperature. At time zero the surface of the slab is reduced to a temperature T, < Te,, where Te, is the solidus (or eutectic) temperature and T, is a constant. The densities of solid and liquid alloys are assumed to be equal and independent of temperature and composition. A qualitative picture of solidification of an alloy, under these conditions, is illustrated in Fig. 1. During the initial stage of solidification, before liquidus front reaches the center of the slab, freezing proceeds by propagation of two isothermal fronts, the liquidus front and the solidus (or eutectic) front. The fraction of solid at the liquidus front is zero; the fraction of solid at the solidus front is unity, The solid fraction and the temperature distribution between the two fronts and the width of the solid-liquid region change with time. During the later stage of freezing, after the liquidus front reaches the center of the slab, the liquidus front disappears. The solid fraction and the temperature at the center of the slab, as well as throughout the solid-liquid region, are now changing with time. The solidification is completed when the fraction of solid at the center of the slab reaches unity. In solution of this problem we seek to determine a) the temperature distribution in the solid, b) temperature, concentration,

Jan 1, 1968

By A. E. Jenkins, A. Jostsons

Isothermal sections of the Ti-0-H phase diagvam at 600°, 700°, and 800°C have been constructed from equilibrium hydrogen pressure measurements over a range of Ti-0-H alloys containing up to 34 at. pct 0. Oxygen reduces the hydrogen solubility at fixed hydrogen pressure but increases the terminal solubility in the a solid solutions at the a/(a + P) phase boundary. Metal-lographic studies of alloys annealed below the eutectoid temperature show that oxygen also increases the ter-ninal solubility of hydrogen in the a solid solution in equilibrium with the hydride phase. The effect of oxygen on hydrogen solubility is discussed in terms of the electronic and geometric structure of interstitial solid solutions. THE isothermal solubility of hydrogen in a Ti-0 alloys at 800°C has been measured by Hepworth and ~chuhmann&apos; who subsequently used ternary Gibbs-Duhem integrations to calculate oxygen activities in binary Ti-0 alloys. The present study aims to extend Hepworth and Schuhmann&apos;s measurements to alloys richer in oxygen and to a range of temperatures. This paper presents the results of hydrogen equilibrium pressure/concentration measurements in Ti-0 alloys as well as observations on the effect of oxygen on the terminal solubility of hydrogen in a titanium. The thermodynamic properties of binary Ti-0 alloys, derived from these measurements, will be published separately.&apos; EXPERIMENTAL METHODS Specimen Preparation. Ti-0 alloys were prepared from iodide-refined titanium and titanium dioxide obtained by hydrolysis of redistilled titanium tetrachlo- ride. Specimens containing up to 16 at. pct 0 were prepared by electromagnetic levitation3 whereas a conventional tungsten arc furnace with a water-cooled copper hearth was used to melt oxygen-rich alloys. The specimen homogeneity was indicated by the constancy of lattice parameters of samples from various parts of the ingot as well as by the sharpness of the reflections on X-ray powder patterns. Oxygen-rich specimens in the composition range (20 to 34 at. pct), where ordering has been ~bserved,~ were annealed for 300 hr at 600°C prior to use in hydrogen solubility measurements. Apparatus. The hydrogen pressure/concentration measurements were made with a modified Sieverts apparatus shown diagrammatically in Fig. 1. Specimens were placed in a clear silica tube and impurity pickup by direct reaction with silica was prevented by lining the heated end of the silica tube with thin molybdenum sheet. A double silica tube was required to eliminate loss of hydrogen by diffusion through silica at high temperatures and high hydrogen pressures, the space between the tubes being maintained at a hydrogen pressure equal to that above the specimen. Hydrogen was purified by diffusion through a Ag-Pd tube.= Hydrogen pressures were measured with a mercury McLeod gage in the range 0.001 to 4 Torr

Jan 1, 1968

By M. C. Flemings, G. E. Nereo

General expressions are given to describe macro-segregation in castings and ingots which results from mass flow of solute-rich liquid to feed solidification and thermal contractions. Analytical solutions are given for solidification with planar isotherms (unidirectional and bidirectional heat flow). These solutions describe inverse segregation and centerline segregation. Numerical examples are given for A1-4.5 pct Cu alloy. In 1540, Vannoccio Biringuccio published one of the first references to macrosegregation, describing the problem of exudation and inverse segregation in the manufacture of bronze gun barrels.&apos; Since then, a great many studies of macrosegregation have been reported. Recent work of particular engineering interest includes that of Marburg 2 and others:" on centerline segregation and other types of segregation in large steel ingots, and work of Adams,5 Scheil, 6 and Kirkaldy and youdelis7 on inverse segregation in nonferrous ingots. In most studies on this subject, the various types of macrosegregation have been treated as separate phenomena. For example, quite different mechanisms have been proposed for formation of centerline segregation, negative cone of segregation, inverse segregation, banding, and so forth. In this, and in several papers to follow, it is proposed that these as well as other types of macrosegregation result from the same basic mechanism and can be quantitatively described by the same basic equation. It has often been suggested that some types of segregation (such as centerline segregation and banding) occur as a result of buildup of solute at the tips of growing dendrites.2-4 ,8-10 As example, banding can be induced in centrifugal castings by mechanical vibration, and Northcott 10 suggests this might be due to the influence of the vibration on the boundary layer at the dendrite tips of the growing dendrites. However, in view of the extremely small boundary layer known to exist at the tips of the dendrites,11,12 any interpretation of macrosegregation based on this boundary layer is clearly incorrect. Note that experiment has shown that significant buildup of solute does not occur at dendrite tips in ingot solidification, but even if such buildup occurred the thickness of the enriched zone would only be the order of D/U where D is liquid diffusion coefficient and U is dendrite tip velocity. For usual casting or ingot solidification this solute-enriched layer is 10"3 cm, far too small to account, for example, for centerline segregation.11&apos;12 It has also been suggested that convection in the bulk liquid (ahead of the advancing dendrites) might cause segregation by sweeping away the solute-rich boundary layer in front of the dendrites.3 However, since there is no significant boundary layer, this explanation must be incorrect. The convection might directly cause segregation by penetrating between the dendrite arms, and presumably in a rimming steel ingot it is sufficiently vigorous to cause some segregation in this way. Centerline segregation, however, cannot be interpreted as resulting from this convection since a sharply segregated zone is usually found near the centerline, with the bulk of the ingot being nearly of nominal composition. If convection in the bulk liquid were the direct cause, a gradual change in ingot composition over the entire cross section would be expected. It is known that sudden changes in convection of the bulk liquid during solidification can result in banding,14 but it is not clear that the banding results directly from the effect of convection on solute distribution. Changes in convection also affect thermal conditions in the liquid-solid region of a solidifying ingot. It will be seen later in this paper, and in a paper to follow, that macrosegregation is strongly influenced by these thermal changes. Recognizing that in some cases of ingot solidification (as in solidification of rimming steels) convection in the bulk liquid may have a direct effect on solute distribution, we neglect it in this paper and in the several to follow. We then derive general expressions describing macrosegregation which results from the mechanism of interdendritic flow of solute-rich liquid

Jan 1, 1968

By Klaus Schwerdtfeger

In order to test the performance of ZrO, (CaO) and Tho,(Yz03) electrolytes in the electrochemical determination of oxygen activities in liquid metals at steel-rrzakitng temperatures , electromotive force measurements have been made with the following cells: The oxygen-- activities are calculated from the electmrnotive forces for the investigated systems. The standard free energy of- formation of MnO and the activity of manganese in Fe-Mn melts are derived. Indications are that the Zr 0z(Ca0) electrolyte exhibits little electronic conductivity at oxygen pressures as low as 10&apos;a atnz at 1600°C; however, the partial electronic conductivity may become noticeable at lower oxygen activities. The Tho,(Yz03) electrolyte is found to be an ionic conductor at the oxygen pressure as low as that for the Mn + MnO equilibrium, but exhibits partial electronic conductivity at oxygen pressures higher than 10"1 atm (1500°C). fi. better control of oxidation and deoxidation reactions in steelmaking may be facilitated if the oxygen activity in the steel is known during various stages of the process. In the present work oxygen activities have been measured in liquid iron, manganese, and iron alloys with galvanic cells using ZrOz(CaO) and s solid electrolytes with the object of establishing the range of oxygen pressure in which these materials can be used as electrolytes at steelmaking temperatures. Calcia-stabilized zirconia and Tho2-Y203 solid solutions are oxygen ion conductors. Such electrolytes were first used by Kiukkola and Wagner1 and Peters and ~ann&apos; in galvanic cells for the determination of thermodynamicquantities of oxide systems in the temperature range 700" to 1200°C. At these moderate temperatures calcia-stabilized zirconia has been found to exhibit predominantly ionic conductivity at oxygen pressures as low as those for the Cr + Crz03 equilibrium,394 but at lower oxygen pressures elec- tronic contribution to conductivity becomes significants4 The Th02-Y203 solid solutions are ionic conductors at oxygen pressures lower than those applicable to zirconia base electrolytes.5&apos;6 At high oxygen pressures Thoz base electrolytes exhibit significant p-type semiconduction. At the time the present experiments were carried out several papers1&apos;-* were published on the electrochemical determination of oxygen activities in liquid iron using the ZrOz(CaO) electrolyte. The results of different authors do not agree well. For instance, according to Fischer and ~ckermann" stabilized zirconia can be used to measure oxygen contents in liquid iron larger than 0.02 wt pct, but according to Baker and west1&apos; ZrOz(CaO) cannot be used for the determination of oxygen content in liquid iron because of high electronic contribution to the conductivity. Fig. 1 is a schematic diagram of the apparatus used. About 500 g of liquid metal is contained in a crucible into which a stabilized zirconia or Th02(Y203) tube is immersed. A platinum contact wire is pressed (with a spring mechanism) against the inside bottom wall of the electrolyte tube. The tube is flushed continuously with a stream of air, CO-CO, (or Hz-C02) (at 0.96 atm and at a rate of about 300 cu cm per min), via an alumina tube inserted inside the electrolyte tube. This alumina tube also contains the Pt-Pt/10 pct Rh thermocouple. A capillary alumina tube shielding the other contact wire is immersed in the melt. The molybdenum contact wires were used mostly; in some cases platinum wire was employed. Molybdenum has the advantage that it dissolves more slowly in the melt than platinum. The whole cell was contained in the alumina reaction tube of a resistance furnace with molybdenum winding. The reaction tube was closed gas tight at both ends and flushed continuously with argon. Because of the poor thermal shock resistance of the electrolyte tubes the cell had to be assembled in the cold furnace. The electrolyte tube and alumina sheath

Jan 1, 1968

By Fred H. Perfect

The thermite process, now approximately 80 years old, has heretofore been practiced in ceramic vessels. This paper outlines the successful production of several million pounds of alloy produced in zuater-cooled copper vessels. THE high temperatures necessary to produce fluid high-alumina slags have probably discouraged earlier workers from attempting to utilize water-cooled vessels. The following is a report of the successful application of this method, together with a report of the physical and chemical problems which had to be solved to make the process practical. About 1955, when Reading Alloys was more concerned with the production of ferrotungsten than with most other types of alloys, it was found to be exceedingly difficult to predict the reaction rate that one would experience from one tungsten ore to another . This difficulty was increased for two reasons: the physical state of the ore as received was seldom uniform, and the size of the mass to be reduced is a very important factor in developing the proper mix for the final reaction rate and temperature. For example, the reduction of ferric oxide with aluminum would theoretically produce temperatures of about 2600°C, and, in spite of the losses due to radiation, the energy is quite sufficient to produce a very fluid slag and iron effecting a very clean separation. On the other hand, the reduction of ferrous oxide with aluminum, while it is not as energetic as the first reaction, nevertheless should give temperatures above 2000"C, which should cause separation of alumina and iron, but, in practice, this is not the case and good fluid slag is not obtained. The heat of reaction, calculated from the thermo-dynamic heats of formation of the constituents of the reaction, offers a convenient guide to the feasibility of a thermite reaction. Thus, the values listed in Table I can be used as an approximate guide for estimating the results which may be expected in the reduction of various oxides and combinations of oxides using aluminum as the reducing agent. As a generalization, those reactions releasing approximately 600 cal per g of total mass represent the lower limit at which to expect separation of slag and metal. On the other hand, those reactions which release 1100 to 1200 cal per g are too violent to be used successfully without the addition of considerable inert material, such as lime, fluorspar, and so forth. Reaction rate is also a very important factor. This, of course, is governed very largely by the sizing and intermingling of the oxidant and reductant and by the starting temperature of the reactants. This is why those figures shown in Table I can only be a general guide. Further, it must be understood, that by adding powerful oxidizing agents, such as nitrates, chlorates or metallic oxides, such as molybdenum trioxide or chromium trioxide, certain problems respecting low temperatures are not necessarily solved. This is true in the addition of oxidants, such as sodium chlorate. By adding too high a concentration of sodium chlorate as a booster for a particular reduction, explosions are generated. Generally, they are of an intermittent type so as to give a Roman Candle effect to the reduction itself; with each surge resulting from a minor explosion more and more material is thrown

Jan 1, 1968

By F. S. Pettit

The oxidation of Ni-3 to 25 wt pd Al alloys has been studied in 0. 1 atm of oxygen at temperatures between 900° and 1300°C. These alloys have been found to oxidize by three different mechanisms which depend on the temperature of- oxidation and the alloy composition. Two of the three mechanisms do not permit a continuous layer of Al,0, to be formed on the alloy surface and the oxidation rates are greater than that for pure nickel. The third mechanism results in the formation of an external A1203 scale and lke oxidation rates are about three orders of magnitude smaller than those for pure nickel. The minimum amount of aluminum required for the formation of external scales of A L,0, has been determined. NICKEL-base alloys are currently the main source of materials for use at elevated temperatures in gas turbine engines. These alloys are usually coated to obtain oxidation resistance. Coatings on nickel-base alloys are frequently formed by reaction of the alloy with aluminum whereby alloyed nickel aluminides are formed. The alloyed nickel aluminides provide protection to the nickel base alloy because external scales of A1203 (alumina) are formed during oxidation and mass transport through A120, is slow in comparison to mass transport through most other oxides. In view of the protective properties of A1203, it is important to know how much aluminum is required in these alloys in order to form external scales of AlzO,. The present paper is concerned with the oxidation kinetics and the oxidation mechanisms of Ni-A1 alloys and the minimum amount of aluminum required in these alloys for the formation of external scales of Alz03. THEORETICAL CONSIDERATIONS When a Ni-A1 alloy is heated in oxygen at elevated temperatures, the following reactions can take place on the surface of the alloy where the oxide phases are assumed to be virtually pure: These oxide phases are in the form of nuclei scattered over the surface of the alloy and, in view of their rapid formation, they need not be in equilibrium with the alloy. As the oxidation process continues, equilibrium between the alloy surface and the oxide phases is approached and the stability of the oxide nuclei is determined by the composition of the alloy at the alloy/oxide interface because of the following reactions: 3NiA1204 + 2A1 (alloy) = 4AlzO3 + 3Ni (alloy) [41 4Ni0 + 2Al (alloy) = NiA120, + 3Ni (alloy) [ 5 1 Application of the mass-action law to Eqs. [4J and [5J yields the following equilibrium conditions for these reactions: where aA1 and aNi are the activities of aluminum and nickel, are the standard free energies of formation of NiO, A1203, and NA1204, respectively, R is the gas constant, and T is the absolute temperature. If the composition of the alloy at the alloy/oxide interface is such that (akl/ahi) is greater than the equilibrium values defined by Eqs. [6] and [7], then Reactions (41 and [5] will go to the right as written. Conversely, if the alloy composition is such that the activity ratio (aLl,/aki) at the alloy/oxide interface is less than the equilibrium values, then Reactions [4] and [5] will proceed to the left. The equilibrium activity ratios in Eqs. [6] and 171 can be calculated since values for the standard free energies of formation of the oxide phases are available. Standard free energies of formation for NiO and A1203 have been tabulated by Elliott and ~leiser.&apos; The standard free energy of formation for NiA1204 can be obtained from the data of Tretjakow and Schmalzried.&apos; The results of these calculations are tabulated in Table I. Table I shows that the following inequality is valid over the temperature interval 900" to 1300°C: (Reaction [5]) (Reaction [4]) « 1and therefore the aluminum activity for these compositions can be taken as equal to the square root of the activity ratios (i.e., aNi = 1). If equilibrium is estab-

Jan 1, 1968

By J. E. Hanlon, S. R. Butler, R. J. Wasilewski

The temperature, orientation, and strain-rate dependence of tensile flow in single-crystal NiA1 of equiatomic composition have been investigated up to 800°C. Compression tests at room temperature have also been carried out. Optical and replica electron microscopy and X-ray diffraction methods were used to investigate the slip mechanisms. NiAl exhibits {110)(001) slip and cube slip {l00)(010) was also observed. This results in very high strength of single crystals in cube orientation. The implications of this slip mode, with the resultant small number of possible slip systems and three mutually perpendicular slip vectors, are discussed. ThE CsCl structure compounds represent a class related to the bcc elements, but their behavior is affected by three additional variables: composition (within the stability range of the compound), extent of long-range order perfection, and bonding energy. Very little data are available on the effects of these variables on mechanical properties. Rachinger and ~ottrell&apos; suggested slip to occur along (111) in compounds of low ordering energy; in compounds of higher bond strength (>0.06 ev), they observed (110) (001) slip. As pointed out by copley,&apos; only three in- dependent slip systems are available in the latter case; hence general deformation is impossible. Brown3 carried out a theoretical calculation of the yield-point variation with the degree of long-range order in the CsCl structure, based on the assumption of superdislocations. More general approaches, based on considerations of superlattice dislocations and antiphase domain boundaries in ordered structures, were carried out by Flinn~ and by Vidoz and Brown.&apos; These, however, give no information on changes in the slip structure—if any—between the ordered and the disordered compounds. This aspect was investigated experimentally and theoretically by Stoloff and Davies&apos; and by Marcinkowski and chessin7 in FeCo. The latter workers proposed the deformation behavior of the ordered FeCo to be essentially the same as that in many other bcc metals. Investigations of polycrystalline A~M~&apos;-&apos;O indicate considerable variation in mechanical properties with composition and test temperature. The existence of {123)(111) slip was reported in AgMg.&apos;9&apos;9&apos;0 (The formation energy of this compound, presumed to be ordered at all temperatures below melting, is 4.38 cal per g-atom," i.e., 0.024 ev per bond.) The yield strength has been reported as relatively independent of temperature below 0.45 T, (where T, is the absolute melting temperature). Tensile deformation of single-crystal AgMg was also investigated by Kurf-man," who observed marked tendency to single glide on{112}(111) and {110)(111). From observations of slip lines in deformed poly-crystalline NiA1, Westbrook et a1.I3 suggested the

Jan 1, 1968

By W. A. Backofen, B. C. Wonsiewicz

The Plasticity transition in magnesium was studied by plane-strain compression of single crystals and polycrystalline material at temperatures from about 20" to 307°C. Reduction of single crystals along the c axis was accommodated by twinning on {1011) and retwinning on (10 12}, followed by basal shear in the doubly twinned volume. Deformation in that mode can result in sufficient independent shears for arbitrary shape change. Fracture in c axis compression, below about 100°C, has been related to excessive shear caused by unloading from the stress for {1011} twinning (-50 ksi at 20°C) to that for slip within the twin (-3 ksi); ductility follows from heating because the stress difference is lowered and the twin volume, in which elastic strain energy is dissipated on unloading, is increased. The stress for (1011) twinning is strongly temperature-dependent but not given by a critical resolved shear stress law. The latter is attributed to the influence of stress concentration from prior intersecting shear on nonbasal planes, the former to the temperature dependence of the preliminary slip. THE basic symmetry of hcp crystals has the effect of limiting the number of independent slip systems and making twinning an important deformation mechanism. The general result in wrought polycrystalline aggregates is a more or less sharply developed texture (or preferred orientation) which underlies a strong anisotropy in mechanical behavior. Knowing how the one influences the other is essential background for the use of such materials. Magnesium was of interest in this work because of the unexplained plasticity transition that it undergoes somewhere in the neighborhood of 200°c.&apos;&apos;~ At lower temperatures plastic deformation before fracture in polycrystalline material is limited, while at higher temperatures extensive deformation is possible. The transition temperature commonly determines the lower limit of the range in which magnesium is worked. The limited ductility can be traced to a lack of independent crystallographic shears. A minimum of five are required for arbitrary shape change.&apos; Around room temperature, however, slip on all known systems provides only four.&apos; In each case, the slip direction is in the (0001) basal plane so that slip does not allow strain along the c axis. With increasing temperature, more slip occurs on the ( 1011) pyramidal plane and the ( 1010) prism plane but without change in direction.&apos;?&apos; Thus, that development alone cannot explain the transition temperature.

Jan 1, 1968

By L. J. Kashar

By means of a continuum-mechanics approach, the following equation for calculuting the pressure for axisymmetric cold forging has been derived: where P is the extrusion pressure; K and n are the strength coefficient and the strain-hardening exponent of the steel, respectively; a and b are strain factors, primarily dependent on the die design; and R is the extrusion ratio. Data from compression and backward-extrusion tests performed at a crosshead speed of 0.5 in. per min on a nonwork-hardening material pure lead) and on a work-hardening material (1018 steel) indicate that the predicted extrusion pressures obtained from the derived equation agree very closely with the actual extrusion pressures. Therefore, the equation can be used to predict backward-extrusion pressures from standard mechanical-test data. The decision to cold-forge a part is based on several considerations, most of them related to economics. However, the production feasibility is usually determined by the pressure needed to extrude the part and the availability of tooling that can repeatedly sustain this pressure for over several hundred thousand cycles. A major contribution to the cold forging of steel would result from the development of steels that could be forged at reduced pressures and from the development of techniques that permit the accurate prediction of the pressure necessary to cold-forge the part. The ability to predict extrusion pressures is necessary to properly design the tooling required for the cold-forging process. Attempts to theoretically predict the cold-forging pressure, especially for work-hardening materials, have been unsuccessful in previous investigations of the cold-forging process.1-3 Many empirical relations have, therefore, been proposed relating the extrusion pressure to the chemical composition,&apos; the extrusion ratio,2 the tensile strength,273 and hard- ness, 2 and the yield strength3 of the material being extruded. However, these empirical relations are valid only for the specific conditions used in their development, and, in some cases, the empirical relations had a scatter band greater than * 10 pct. A study of the extrusion process was undertaken with the objective of developing predictor equations for extrusion pressure by using a continuum-mechanics approach to the problem of metal flow. The derivation of such an equation is summarized in this paper, and data are presented that confirm the validity of the derived equation. DERIVATION OF THE EXTRUSION EQUATION If the extrusion of a material through a die is considered in terms of a work balance, it has been shown that it is possible to derive an equation relating the work necessary to move the material through the die to the deformation work undergone by the material. The work done, W, in moving the material is given by where F is the extrusion force, I, is the distance the material was moved, A, is the original cross-sectional area of the material, P is the extrusion pressure acting on A,, Ap is the cross-sectional area of the extrusion punch, and Pp is the punch pressure acting on Ap. The deformation work, WD, is given by where V is the volume of metal deformed, ay is the flow stress of the metal, and E is the total strain undergone in the extrusion. If there are no frictional losses, the work done, W, is equal to the deformation work, WD; therefore, Since the volume of a metal does not change during deformation,

Jan 1, 1968