By E. T. Turkdogan, J. H. Swisher

The solubility of oxygen in zone-refined iron was determined in the temperature range.from 881" to 1350°C. The solubility in a iron at 881°C ms found to be about 2 to 3 ppm; in y iron, the solubility was found to increase from about 2 to 3 ppm at 950°C to about 25 ppm at 1350°C. The permeability of oxygen in an iron -0.1 pct Al alloy was determined in the y iron range, using an internal oxidation technique. By combining the permeability and solubility data, the diffzisivity of oxygen in y and a iron was calculated. The oxygen diffusivity in solid iron may be s~immarized as follows: 8820 For 6 iron and IN a recent paper, Hepworth, Smith, and Turkdogan1 reported on the solubility, permeability, and diffusivity of oxygen in 6 iron, together with permeability data for oxygen in a iron. In the present investigation, similar measurements were made in the ? phase region. In addition, a solubility measurement was performed in the a phase region to permit calculation of the diffusivity of oxygen in a, iron. References to early work on this subject are given in the previous publication.' EXPERIMENTAL Solubility Measurements. The oxygen solubility was determined by equilibrating cylindrical samples 0.3 in. diam by 14 in. long of zone-refined iron in water vapor-hydrogen gas mixtures. The zone-refined iron was prepared by B. F. Oliver of this laboratory, using an apparatus and technique described elsewhere.2'3 Six zone-melting passes were used to achieve a total impurity level of about 30 ppm. Of this 30 ppm, the combined nickel and cobalt content was about 20 ppm, oxygen was 4 ppm, and all oxidizable impurities less than 1 pprn each. A vertical resistance furnace wound with molybdenum wire was used for the experiments. The temperature was measured before and after each experiment with a Pt/Pt-10 pct Rh thermocouple. In the gas train, flow rates of hydrogen and argon were measured with capillary flow meters, and the resulting mixtures were passed through a column containing 90 pct oxalic acid dihydrate and 10 pct anhydrous oxalic acid to obtain predetermined ratios of H2O to H2. The vapor pressure of H2O above this mixture as a function of temperature is well-known.4 The exit gas was ana- lyzed periodically for H2O, and good agreement (+3 pct) with the calculated composition was obtained. The zone-refined iron specimens were held in the furnace for a sufficient length of time for equilibration, e.g., 18 hr at 1350°C and 1 week at 881°C, then quenched in a brine solution. After removing the surface oxide from the samples by machining, duplicate analyses were obtained by a combined vacuum fusion-infrared method; oxygen analysis was reproducible within 2 ppm. Permeability Measurements. The permeability of oxygen in alloys containing about 0.1 pct A1 was determined by internal oxidation and measurement of the subscale thickness as a function of time. The experimental alloys were prepared by adding aluminum to electrolytic iron (grade 104A plastiron) that had previously been vacuum-carbon deoxidized. The resulting ingots contained about 20 ppm O, 100 pprn C, 40 pprn Si, 50 ppm Mo, 20 ppm P, 20 ppm S, and 20 pprn Zr as the principal impurities. After hot rolling the ingots to 1-in.-thick slabs, specimens were machined from the stock in the form of rectangular plates, 4 by 5 by 2 in. The general procedure for the permeability experiments was the same as those for the solubility measurements. The specimens were cooled in a reducing atmosphere rather than quenched, however, in order to maintain a clean surface for measurement of the sub-scale thickness. This measurement was made on a polished cross section of each specimen, using a microscope with a micrometer stage. The inclusions formed at the lowest temperature 1033°C were too small to be seen with an optical microscope. An electron micrograph showing the size and shape of individual particles is shown in Fig. 1. The dark band in the picture is a boundary between two subgrains. The subscale thickness in these samples was measured with an optical microscope after heavily etching in 2 pct nital, which gave contrast between the subscale and the unoxidized zone.

Jan 1, 1968

By R. D. Pehlke, J. V. Gluck

A study was made of' the effects of up to five additional solutes on the thermodynamic activity of zinc in dilute solution with molten bismuth in the range 450" to 650°C. The experimental measurements were made in a multielectrode galvanic cell apparatus employing fused LiCl-KCl as the electrolyte. The solute additions included indium, lead, tin, cadmium, copper, silver, antimony, or gold. A range of positice and negative interactiotls with zinc was covered. The experinzer~tal observations were cowlpared with the activity coefficients calculated usitlg either Wagner's first-order Taylor series rnodel or a proposed second-order solution itrteraction model. hi general, the truncated first-order Taylor series proposed by Wagner gaue good results for "dilute" solutions (XBi > 0.90) contaitzing up to six solutes. The second-order model, which includes a second-order cross-interaction term, produced a slight improvement in predictions for solutions with XZn = 0.015 and a significant improvement for solutions with XZn = 0.050 hear the limit of Henry's law region). Seveval of the quaternary solutions studied contained a total solute content of 0.215 mole fraction, and fairly good success was achieved in predicting the activity coefficient 01- zinc. ThE study of thermodynamic interactions between dilute solutes in liquid metallic solutions has occasioned much recent interest. It is useful to recall in this respect that Wagner's well-known expression for the activity coefficient' is a practical application of the problem of representing a given function, i .e., In ?, by means of a sequence of polynomials. No specific physical model of a solution is involved in its use. As suggested by Wagner, a Taylor Series is used to expand In ? about a point of infinite dilution with respect to all solutes. The partial differential coefficients of the series have been termed "interaction parameters". Various authors'-6 have proposed formalisms for parameters, the definitions being designed to meet some specific experimental or physical condition. A usual assumption is that terms above first-order in the Taylor Series may be neglected. In that case, the logarithm of the activity coefficient is expressed as a linear function of solute concentrations. The resulting expression is presumed valid for any number of additional solutes as long as the solution can be regarded as "dilute". This assumption can be termed "the hypothesis of additivity". However, experimental tests of that hypothesis for quaternary or higher-order solutions have been extremely limited. Primarily such tests have been confined to studies of effects of added metallic elements on either the activity of carbon or the solubility of gases in liquid iron.7-13 The only known previous study of an all-metal system is the limited work of Okajima and pehlke14 on the effects of multiple solute additions on the activity of cadmium in liquid lead. The present investigation is a portion of the work to determine the effects of various solute additions on the activity of zinc in dilute solution with molten bismuth in the range 450" to 650C It was shown for such ternary solutions that second-order Taylor Series terms could be evaluated at the same time as first-order terms, with no additional experimentation required. A second-order solution model was described which, under certain conditions, is a rigorous representation of solute activity in a ternary solution. (In the sense employed in this paper, the term "model", as distinguished from "equation", is taken to mean an empirical correlation or formalism, but not a hypothetical physical system per se.) Presumably such a model could be extended to produce a better representation of In ? in solutions of even higher order. The feasibility of a generalized Taylor Series approach to solution interactions and inclusion of second-order terms also has been discussed recently by Lupis and Elliott in independent work concurrent with the present investigation. In addition, they discussed empirical means of estimating certain second -order coefficients.17 The utility of such solution models rests on the ability of a truncated series to represent adequately the experimental facts in multicomponent solutions. Questions that arise include: Do the second-order terms really make a significant contribution? How far away from "dilute" solution may such models be applied? Are the types and varieties of the additional solutes important? among others. In order to provide some answers to these questions, an experimental study was made of the effects of two or more additional solutes on the activity of zinc in dilute solution with molten bismuth. Comparisons were then made with calculated activity coefficients obtained using the previously determined ternary interaction parameters. INTERACTION MODELS As an example of the approach to defining activities in multicomponent solutions, consider the Taylor Series expansion for a quaternary system, i.e., three dilute solutes. Writing terms through second order, the result is:''

Jan 1, 1968

By I. R. Kramer

The stress associated with the surface layer was deter-minedfor iron and molybdcnum. These measurements show that the surface layer plays a very important role in the plastic deformation of bcc metals. From the relationship between strain arui the surface layer stress and the back stress imposed by the internal obstacles, it is Proposed that the term of of the Hall-Petch equation is related only THE large number of studies on plastic flow of bcc metals have failed to delineate clearly the nature of the obstacles influencing dislocation movement. Since there have been numerous articles which have reviewed the mechanisms proposed to explain various aspects of plastic flow of bcc metals (for example, conrad1 and Keh and weissmann2), no attempt will be made here to discuss their conclusions. However, it should be to the surface stress while the term Kfd is the stress required to move dislocations through internal obstacles. Further, it was possible to derive the well-known empirical equation C = , and it is shown that the terprz a is comprised of two terms: a term Cs associated with the surface layer stress and Ci related to internal dislocation obstacles. pointed out that in all of these publications it has been tacitly assumed that plastic flow occurred uniformly throughout the cross section of the specimen (except, of course, for the Luders band region), It has generally been further assumed that the nature and distribution of the obstacles opposing the motion of dislocations are of the same type throughout. The role of the surface layer in bcc metals has not, as yet, been considered even though its role in fcc metals has been shown clearly to be of primary importance.3-5 Investigations on fcc metals have shown that at the onset of plastic deformation a surface layer acts to

Jan 1, 1968

By R. W. Smashey, B. J. Piearcey

The structure, composition, and morphology of the carbide phases present in the nickel-base superalloy, Mar-M200, hare been determined and three carbide phases observed. The MC carbide is a solidification product, and the M23 Co and M6C carbides are both prod~icts of solid-state precipitation. The identity of each phase usas determined by both X-ray and electron-diffraction techn~ques. Compositions of all three carbides were studied using the electron beam micro-probe analyzer and by unalyszs of electrolytically extracted residues. Optical and electron microscopy were employed in order that the time/temperature -dependent behavior of the carbides might be observed. Supplementary studies were completed on thin foils and oriented single crystals to determine the mor-phology and orientation relationship of each phase with that of the matrix. MAR-M~OO* is a high-temperature, creep-resistant superalloy designed for use in the as-cast condition. The "as-cast" microstructure consists of a solid-solution matrix, referred to as gamma (y), which contains a general, coherent precipitate of the inter-metallic Ni3(A1,Ti) referred to as gamma prime (?). As a result of dendritic segregation during solidification, a degenerate, spherulitic ? -?' eutectic constituent is present at the grain boundaries and the in-terdendritic regions, which is nucleated by the y on the dendrite tips. A primary carbide phase, a solidification product, is also present at the grain boundaries and in the interdendritic areas, and an additional carbide appears at the grain boundaries as a fine discontinuous precipitate. The alloy is particularly susceptible to heat treatment. For example, the mechanical properties of the columnar grained mater- ial are substantially improved by solution heat treatment, followed by an intermediate temperature age. Metallographic examination of heat-treated material reveals, however, that exposure to elevated temperatures has a marked effect on the microstructure of the alloy; in particular, it is observed that precipitation of considerable amounts of various carbide phases occur. The following investigation was carried out to determine the morphology, composition, and behavior of the carbides in Mar-Ma00 as an aid to the determination of their effect on the mechanical properties and stability of the alloy. THE PRIMARY MC CARBIDE The MC carbide phase appears in the interdendritic interstices and the grain boundaries. In directionally solidified Mar-M200 the carbide appears as very small particles in the chilled region, Fig. l(a), whereas in material less affected by the chill, it becomes larger and develops a dendritic morphology, Fig. 1(b). Step polishing of metallographic specimens from this region shows that in directionally solidified material the individual carbide dendrites are connected in a dendritic network within the metallic interdendritic interstices, whereas in material from the chilled region and in conventional Mar-M200 they are discontinuous, isolated dendrites. No orientation relationship exists between the primary carbide and the matrix.

Jan 1, 1968

By J. F. Held

In a study of the influence of cold rolling on mechani cal properties of steel, it was found that the specific rolling procedure influenced crystallographic orientation. Properties developed by several rolling modes were determined and related to crystallographic orientation. Sanzples were cold-rolled various amounts on a laboratory mill. When palm oil was used as a lubricant, the crystallographic orientation was homogeneous throughout the thickness of the samples. Other samples were rolled without lubrication. Variations in intensity of the recrystallization texture components persisted throughout more than 50 pct of the volume of these samples. When the average plastic strain ratio, which is dependent upon crystallogvaphic orientation, was plotted as a function of percent reduction, a maximum was found at 40 pct in the samples which contained the observed texture variation. No maximum was found for the samples with the homogeneous texture distribution. Other mechanical properties, such as tensile strength and yield strength, were not influenced by the variation in crystallopaphic orientation. MECHANICAL properties of steel sheets depend, in general, upon the structural properties of the steel. For example, the Petch equation describes the relationship between yield strength and grain size. Other properties, such as hardness, vary with chemical composition. The plastic strain ratio, or R value, has been found to be dependent upon crystallographic orientation . In the course of investigating the effect of cold rolling on mechanical properties, it was found that a previously reported relationship between percent cold reduction and R value was not always observed. Published data had shown that the optimum cold reduction for best R values is 70 pct for aluminum killed steel.' However, by altering the rolling conditions, the optimum reduction can be shifted to much lower values, or it can be moved to very high values. This paper describes the rolling conditions that lead to shifting of the optimum cold reduction. The effect of rolling conditions on the various structure parameters and the resulting mechanical properties are evaluated. EXPERIMENTAL PROCEDURE Samples of three low-carbon aluminum killed steels were cold-rolled various amounts on a 9-in.-diam 2-high laboratory mill. Hot-mill thermal practice and steel chemistries are listed in Table I. Steel A was rolled with palm oil lubrication and heavy reductions on each pass; i.e., a total reduction of 75 pct was ac- complished with a maximum of five passes. Steel B was rolled without lubrication, and light reductions were given on each pass. After approximately 75 pct reduction, it was necessary to use a small amount of light oil to achieve any additional reduction in thickness. Following cold reduction, the samples were box-annealed at 1300°F for 10 hr. The heating rate between 800" and 1300°F was 50°F per hr, and the cooling rate following the soak period was 50°F per hr. Tensile specimens were machined from the annealed material and these were used to measure yield strength, tensile strength, and the plastic strain ratio (R value). Recrystallization textures were determined by an inverse pole figure technique.*'3 Integrated intensities of the (110), (002), (112), and (222) reflections were recorded for those planes lying parallel to the sheet surface. Examinations were made on both surfaces of each sample, and also at various levels beneath each surface to approximately 0.010 in. depth by etching techniques. RESULTS R Values. The R values obtained in steels A and B are shown as a function of percent cold reduction in Fig. 1. No optimum cold reduction was observed in steel A, rolled with palm oil lubrication. It is likely, however, that an optimum reduction would have occurred had higher reductions than 88 pct been employed. The optimum reduction in steel B occurred at 40 pct. The behavior in both of these steels is quite

Jan 1, 1968

By B. A. Cheadle, K. P. Steward

Axial tensile, ring tensile, closed end burst, and free end burst tests were done at room tempe.vature and 300°C on three batches of Zircaloy-2 sheathing zuith different textures. Knoop hardness tests were also done on all batches. The mechanical properties of the tubes were largely dependent on the percentages of cold work, but were also markedly affected by the textures, particularly with respect to deformation behavio'r. The deformation behavior observed confirmed Picklesimer's predictions, zuhereas Knoop hardness results could be correlated with texture and yield strength anisotropy after the ,method of Wheeler and Ireland. From the mechanical properties, and from efjectiue strain values deterrlzined at the fractures using a photoqid technique, it zuas concluded that tubing witlz a single preferred orientation of radial basal poles best combines strength and ductility for any given deqee of cold work. THE mechanical properties required in collapsible Zircaloy-2 fuel sheathing for water-cooled power reactors are strength to resist wrinkling deformation by coolant pressure and ductility to accommodate a small amount of deformation in service without rupturing. Zircaloy-2 tubing during fabrication develops pre- ferred orientations of the a Zr grains due to aniso-tropic deformation behavior, and these textures markedly affect mechanical properties. Picklesimer' had predicted the deformation behavior of tubes with various textures, but the texture required to provide the optimum strength and ductility for a given degree of cold work has not been reported. To investigate this problem, tests at three transverse to axial stress ratios were done at room temperature and 300°C on three batches of Zircaloy-2 tubing covering a wide range of textures and percentages of residual cold work. Knoop hardness values were also measured to correlate with preferred orientation and yield strength anisotropy after the method of Wheeler and relland.' 1) MATERIAL For this investigation, three batches of tube-reduced tubing were chosen from the Zircaloy-2 sheathing produced for the Douglas Point Reactor. Individual tubes were 191/2 in. long, 0.600 in. OD, and 0.0165 in. nominal wall thickness. The identities of the batches, together with their textures, are shown in Table I. The tubes had the normal Zircaloy-2 composition3 of 1.5 wt pct Sn, 0.3 wt pct Fe, Ni, Cr combined with the following oxygen concentrations: Batch VII 1140 to 1390 ppm 0 Batch VIII 1400 to 1750 ppm 0 Batch IX 880 to 1320 ppm 0

Jan 1, 1968

By R. L. Moment

The anisotropic elastic behavior of rolled beryllium sheet has been measured, using a pulse echo technique, and compared with X-ray diffraction data. Calculated elastic stiffness constants compared favorably with published values for beryllium single crystals which were attributed to the strong (0002) rolling plane texture. Variations of Young's modulus in the yolling plane could be associated with the velative distribution of (0002) planes out of their ideal position in the rollitzg pkule. WHEN a metal is subjected to cold working such as drawing, forming, or rolling, a crystallographic texture develops which can significantly alter its physical properties. One method for detecting this texture is X-ray diffraction, but Alers and Liu' have recently pointed out how the prediction of anisotropic physical properties from pole figures alone is not always accurate due to differences in interpretation. Variations in Young's modulus with orientation or, more completely, the values of the effective elastic constants of the worked metal, also serve to indicate the presence of a texture. In fact, as Alers and Liu' pointed out, calculated variations in Young's modulus for assumed orientations, when compared with experimental data, can be used to eliminate some of the uncertainty in interpretation of X-ray pole figures. Thus, elasticity measurements can serve not only to clarify any unusual elastic behavior of worked metal, but also to detect and in part determine the nature of its texture. X-ray determination of the texture of rolled beryllium has been reported by Smigelskas and Barrett,2 who found a strong texture of (0002) in the rolling plane with (1070) planes normal to the rolling direction. In the case of metal rolled at room temperature, they reported that [1010] directions also appeared at positions 60 and 120 deg from the rolling direction in the rolling plane, while in more recent work Keeler3 found these directions were also tilted towards the rolling plane. The texture for beryllium rolled at 80O0C, however, only showed (1010) planes normal to the rolling direction and the spread of (0002) planes out of the rolling plane was less. In looking for elastic anisotropy one might consider unidirectional rolling of a metal as introducing an or-thorhombic symmetry through reorientation of the grains, since the three deformations, compression, extension in the rolling direction, and extension in the cross direction, are orthogonal to each other and unequal in magnitude. Thus the rolled sheet could be treated like an orthorhombic single crystal and the nine stiffness constants of the elasticity tensor used to calculate the anisotropy of Young's modulus, the shear modulus and Poisson's ratio. In this case we could write: which is symmetric about its diagonal. Borik and Alers4 have recently used this approach on rolled die steel with very good results. They found, however, that instead of displaying orthorhombic elastic symmetry their specimens could be considered tetragonal in which case Cr1 = c22, c13 = Ca, and c44 =cjj. This conclusion was made solely on the basis of the measured tensor elements, and serves to point out the advantage of this method for studying the anisotropy of rolled metals. Their calculated values for Young's modulus as a function of angle in the rolling plane also checked very well with direct measurements made on different specimens using the resonance technique. In the present study, cross-rolled beryllium was used which had been unidirectionally rolled about 11 pct for the final reduction. This imparted a slight anisotropy in the rolling plane which was detected both by X-ray techniques and elasticity measurements. For purposes of discussion in this paper, the rolling direction is that direction in which the most reduction passes were made and cross direction is the normal to the rolling direction in the rolling plane. It was also decided to consider the rolled sheet as displaying orthorhombic symmetry for the purpose of obtaining elasticity samples with the direction defined as in Table I. Any change in the final symmetry attributed to the sheet would then be made on the basis of the measured elastic stiffnesses. The final data would then be compared with that expected from the X-ray study and that reported for beryllium single crystals. EXPERIMENTAL PROCEDURE Rolling Schedule. The samples used in this study were taken from a large sheet which, because of its size, had to be unidirectionally rolled for the final reduction. The resulting texture was that of cross-rolled metal with a slight unidirectional texture superimposed. A cast beryllium ingot, 9.500 in. sq by 3.325 in. thick, was cross-rolled to 81 pct reduction followed by unidirectional rolling for an additional 11 pct to give a total reduction of 92 pct. The thickness of the final sheet ranged from 0.265 to 0.280 in. Reduction up to 67 pct was done at 980°C and the final 25 pct at 870°C. Analysis for metallic impurities showed aluminum 0.06 pct, iron 0.19 pct, and silicon 0.11 pct, giving a beryllium purity of 99.64 pct.

Jan 1, 1968

By John F. Elliott, John P. Hager

The standard free energies of formation of the lowest stable sulfides of chromium, molybdenum, and tungsten in equilibrium with the corresponding metal hazle been determined by reacting the sulfide and metal with H2(g)/H2S(g) mixtures. The reaction is A method for estimating the standard ~nolav entropies and standard entropies of formation at 298°K of the sul-fides of refractory metals is presented. The standard free energies of formation of the lowest sulfides of the metals in group VIa of the periodic table are probably best determined with the reaction* is known with greater accuracy than is that property for any other sulfur-bearing compound or solution which might serve as a reference phase to establish the chemical potential of sulfur for the essential re- However, there still remain significant problems to the use of Reaction [I] in studying these sulfides. First, the equilibrium gas ratios (Ph2S/PH2) are very small, and with the most stable sulfides in the series the ratios tend to be at the limit of the range for precise chemical analysis (10-4); and second, the reaction rate for the formation or reduction of these sulfides appears to be relatively slow. A primary reason for the latter problem is that the gas phase near the equilibrium concentration has very little capacity for transport of sulfur. It is to be noted that the thermo-dynamic properties obtained from the experimental results by Eq. [I] apply for 1 g-atom of sulfur in the metal-saturated compound even though the exact composition of the compound has not been determined. The work reported here is a study of the standard free energies of formation of the lowest sulfides of chromium, molybdenum, and tungsten, and of copper, by Reaction [I]. In planning the experimental program, it was decided that the technique that has been used previously3"' could be used with modification and that an improved analytical method was needed for determining H2S in the gas phase. THE EXPERIMENT The once-through flow of gas was selected in preference to recirculating the gas, a) because of the low sulfur capacity of the gas, b) because of the relatively slow rate of reaction and the danger of the

Jan 1, 1968

By Klaus Detert

Fifteen and 18 pct Ni maraging steel and several binavy and ternary alloys of the iron-rich corner of the Fe-Co-Ni system have been studied. After annealing in the austenite range, these alloys were deformed slightly by cold rolling and subsequently aged. Compavison of experimental measurements at various processing stages indicates that small degrees of deforn~ation (5 to 10 pct reduction in thickness) do not influence hardness and strength or the aging kinetics. Electrical resistivity and ductility are somewhat redu]ced and the coercive force is substantially lower when compared to identical samples which were not deformed. The results are explained in terms of retained austenite which transforms into martensite with the small amount of deformation. RECENTLY there has been increasing interest in maraging steel for applications in electric power generators requiring a high ratio of power to weight.' Fifteen pct Ni maraging steel has been investigated to evaluate its properties and performance for application as high-strength magnetic rotor steel,' and a thorough investigation of the precipitation and transformation processes in this alloy has been conducted in this laboratory.3 The influence of deformation, which preceded the aging treatment, was also studied. It was found that a small deformation in the order of 5 pct has a rather striking effect in reducing the coercive force. Other interesting effects on the properties caused by such deformation have led to the more detailed studies reported herein. EXPERIMENTAL METHOD The methods used to produce the samples from 15 pct Ni maraging steel have been described elsewhere.3 The general procedure of hot forging and cold rolling to sheet has been followed. The composition is included in Table I which also contains the composition of the 18 pct Ni maraging steel grade 250 studied. More data about the material and the processing of the 18 pct Ni maraging steel have been recently reported.4 The experimental alloys of binary and ternary Fe-Ni-Co alloys were made by levitation melting in an argon atmosphere and casting into rod-shaped ingots 7 mm thick weighing 20 g. From these ingots 25-mm-long rods were machined to study the phase transformation by a dilatometer. These rods were then cold-rolled to strips, 2.4 mm thick. Annealing for austenitizing was done in tube furnaces in an argon or helium atmosphere followed by cooling in the water-cooled portion of the tube. Aging was done in a salt bath containing a neutral blend of Alkali nitrates and nitrites. Vickers hardness was measured using a load of 50 kg for 15 sec. Tensile tests were carried out on a hard beam tensile tester at a strain rate of 5 X lo-' per sec using flat samples with a gage length of 37.5 mm and a cross section of 1.25 by 6.25 mm. Estimated sensitivity was 5 K x strain and 0.35 kg per sq mm stress. Magnetic saturation was determined on small cylindrical samples, 2.5 mm in length and diameter, by measuring the force exerted by the gradient of a magnetic field of 1000 oe per cm in a mean field of 11,500 oe. The measured values could be reproduced within *1 pct. Coercive force was measured by a precision-type magnetic field probe in a magnetic coil as described by Foerster.5 The magnetizing field was 1300 oe. The samples were 5 cm long, 1 cm wide, and 2.4 mm thick. he coercive force was measured to within +0.1 oe. Electrical resistivity was measured by using a potentiometer on flat strips with a gage length of 100 mm and a cross section of 2.5 by 0.5 mm. The accuracy of the measurement was 0.1 pct but the reproducibility of the measured specific resistivity among different samples was in the order of 1 pct. The method used to prepare the samples for electron transmission has been reported elsewhere.3 RESULTS Fig. 1 shows the influence of deformation after annealing on the resistivity, hardness, and coercivity. The samples were annealed for 30 min at 1000"C,

Jan 1, 1968

By J. H. Bucher

The effect oj strengthening by the precipitation of CbC on the toughness offerrilic steel (0.11 pct C, 0.74 pct Mn, 0.02 pct Cb) was stlrdierl. A g-veater degree of pvecij~itatiotz strengthning is ohtaznable by aging the so11ution-treated steel rtt velaticely Low temperature was (1050" to 1l0O3F) than at higher temperatures (I150" to 1200°F). Tlzis ),eslrlts because a finer dispersion of CbC is obtained. However, the ductile-brittle transition te~ripertltlo.e is raised approximately tlzjeee tirues as IFLIIC~ perv a given yield stress increase) by aging in the lower tempareture range, as opposer1 to the Irigher temperaturee range. This is proposed to result pl-iir~avily because different precipitation distributions ar-e associated with the different aging -treaments. For tile steel aged at 1050" and 1100 F, heavy: precipitation on disloccctions occurs resulting in a high degree of rlislocution pinningh tl~us lowevirzg- the toilguiess. in tll c(.rise of the steel aged at 1150 'a?zd 1300"F, Pvecipitatiol~ is irzove g-enerally distributed throughout the matrix rather limn preferentially on dislocations.; and Ike detlsitj, oj mobile dislocations is not sttyong-ly affected. THE most effective means of strengthening hot-rolled ferritic steels are grain refinement and precipitation hardening. It is well-known that grain refinement increases both the strength and the toughness. However, the upper limit of yield strength obtainable by grain refinement alone is about 60,000 psi,'12 i.e., without the formation of acicular structures of lower toughness. The most economical means of obtaining higher strengths is the addition of small amounts of elements such as columbium, vanadium, and titanium which form carbonitrides. These precipitates are very effective in increasing the strength, but the ductile-brittle transition temperature is is Although it is agreed upon that precipitation decreases the toughness, there has been little effort to isolate the causative aspects of embrittlement. The purposes of this research are to assess quantitatively the embrittlement associated with different precipitate distributions and morphologies, and to correlate the degree of the embrittlement with the microstruc-ture. In this manner, a more fundamental insight into the mechanism of embrittlement may be gained. The steel selected for this purpose was a low-carbon, columbium-bearing steel which, after solution treatment, was aged in various time-temperature cycles while attempting to hold all other microstructural variables constant. MATERIALS AND PROCEDURE The composition of the steel used in this investigation is given in Table I. Starting with commercially hot-rolled material 0.074 and 0.280 in. thick, tensile blanks were cut from the thinner material and sub-size Charpy blanks from the thicker stock. The steel had been rolled using a low finishing temperature and rapid cooling after hot rolling to produce grain refinement. Also, chemical-extraction analysis and electron-microscopic examination revealed that the cooling was rapid enough to suppress any significant precipitation of CbC. Therefore, the as-rolled steel is essentially in the solution-treated condition in terms of the precipitation reaction, and it was used as the base material in this investigation. The room-temperature tensile properties of the as-rolled steel aged at 1100", 1150", and 1200°F for various time intervals were determined, see Table 11. The ductile-brittle transition behavior was studied for smooth and notched tensile specimens, and longitudinal half-size (0.200 in. thick) Charpy V notch specimens aged at 1100" and 1150°F for various times, also Table 11. In addition, tensile specimens aged for single times at 1050" and 1200°F were evaluated with respect to their ductile-brittle transition. Only one 1050°F treatment was used because of the extremely slow kinetics of precipitation at this temperature and because no significant difference between 1100°F aging was observed. Only one treatment at 1200°F was used because aging at this temperature alters the shape of the grain boundary cementite particles present in this steel and complicates analysis. The design of the tensile specimens is given in Fig.1.

Jan 1, 1968

By E. Miller, J. M. Eldridge, K. L. Komarek

The thermodynamic properties of- liquid Mg-Pb allojs have been determined by an isopiestic method from 18 to 42 at. pct Pb and by a thevmodynumic analysis of the phase diagram frofiz 0 to 100 at. pct Pb. In the overlapping composition range the magneszupn activity values derived by the two methods are in excellent agreement, thus mutually supporting the correctness of the Mg-Pb phase diagram previously determined by the authors and of the acticitzes deriz~ed isopiestically. SEVERAL studies have been made of the thermody-namic properties of liquid Mg-Pb alloys. Wagner and Engelhardt,1 Lantratov,2 Knappwost,3 Sryvalin et al.* and Wilson5 used the electromotive-force method, Scheil and Wolf8 and Schmahl and Sieben" applied the transpiration technique, and the present authors8 utilized the phase diagram to determine the activity of magnesium in the Mg-Pb system. The results of these studies are not in very good agreement and could not be incorporated into a general systematic analysis of the thermodynamic properties of the homologous series of the Mg-Group IV B systems Mg-Pb,8 Mg-Sn,° Mg-Ge,10and Mg-Si.11 The thermodynamic properties of the Mg-Pb system were therefore re investigated by an isopiestic technique which has been developed for similar studies in the Mg-SnB and Mg-Ge10 systems- Lead specimens, contained in iron or graphite crucibles, were heated in a temperature gradient in an evacuated and sealed titanium reaction tube and equilibrated with magnesium vapor of known vapor pressure to form alloys of compositions which depended on their temperatures, the temperature of the magnesium vapor source, and the thermodynamic properties of the system. EXPERIMENTAL PROCEDURE Magnesium (Dominion Magnesium Ltd., Toronto, Canada) of 99.99+ pct purity and lead (American Smelting and Refining Co.) of 99.999 pct purity were used. In the early experiments, Runs 2 and 3, the alloys were contained in uncovered high-purity iron crucibles. Alloys formed in the uncovered iron crucibles had to be chemically analyzed owing to the slight volatility of lead under the imposed experimental equilibration conditions. The compositions of these alloys were determined by a gravimetric analysis of lead as lead chromate. To avoid this problem, the remaining runs were made in covered graphite crucibles machined from high-density (1.92 g per cu cm) graphite rods (Basic Carbon Corp., Sanborn, N.Y.) which had a maximum ash content of less than 0.04 pct. The non- i reactivity of graphite with lead and magnesium has been previously established,' and the experimental procedure has been described in full detail.' In the runs using covered graphite crucibles it was found that the weight increases of the crucibles and their contents after equilibration equaled the magnesium contents of the alloys within the accuracy of the chemical analysis (i0.3 at. pct Pb). Clearly, the small lid openings of the graphite crucibles prevented significant lead losses during a run, and the weight increase was therefore taken as the magnesium content of the alloys. EXPERIMENTAL RESULTS At thermodynamic equilibrium the magnesium partial pressure of the specimens equaled that of the reservoir. Since the magnesium reservoir was always maintained at the temperature minimum of the system, the activity of magnesium of any specimen was given by the ratio of the magnesium reservoir pressure to the vapor pressure of pure magnesium at the specimen temperature. The standard state was chosen as liquid magnesium and the vapor pressure of liquid magnesium

Jan 1, 1968

By P. Chiotti, R. J. Hecht

Vapov pressure data of solid and liquid alloys along with phase diagram data WERE employed in calculating the thermodynamic properties for the Ca-Zn system. The relative excess partial molal free energy for zinc in the liquid alloys was fitted to the relation wnvre i is we tvmpvrutiirc in ucgrees neivtu ana in is the tr~ole fvaction. Relations for the standard free energy of fortnation for the eight cornpounds were developed. ThE phase diagram for the Ca-Zn system as determined by Messing et a1.' is reproduced in Fig. 1. Earlier work on the phase diagram has been summarized by Hansen and Anderko2 and the very limited thermodynamic information for this system has been reviewed by Hultgren et a1.3 The heat of fusion for the compound CaZn2 has recently been determined to be 9260 cal per mole.4 Solubility data for calcium in zinc for the temperature range of 650" to 725°C were fitted by the relation and reported by Johnson and Dilloon5 In the present investigation zinc vapor pressure data were obtained by both the dewpoint and Knudsen methods in order to calculate the thermodynamic properties for liquid and solid alloys. The dewpoint method as employed in this work requires that only one of the components be significantly volatile, in this case zinc, and that the vapor pressure of pure zinc be known. For calculation purposes the vapor pressure data for pure zinc3 were fitted to the relations; for temperatures below 692.7K, the melting point of zinc. The corresponding free-energy relations for vaporization and sublimation of pure zinc are respectively. Some of the calculations also required knowledge of the free energy of fusion of zinc and calcium and the free energy for the 721°K allotropic transformation of calcium. The free energy of fusion of zinc was taken to be the difference between Eqs. [4] and [5], or The free energy of fusion and transition for calcium were based on the enthalpy values of 2040 and 222 cal per g-atom, respectively, as reported by Chiotti et al. 4 and the heat capacity data given by Hultgren et a1.3 and are represented by the relations, In the latter expression the difference in heat capacity between the a and 0 forms of calcium was neglected. MATERIALS AND EXPERIMENTAL PROCEDURES The metals used in preparing the alloys were Bunker Hill slab zinc, 99.99 pct pure, and Ames Laboratory calcium. The average impurities in the calcium in parts per million by weight, ppm, were N-17, H—77, Ba—216, Mg-15, Si—7, C—157, and Fe—9. The zinc was cleaned in dilute nitric acid and the calcium was used as received. The calcium was stored and handled in an argon-filled glove box and when removed from the dry box it was kept in an argon-filled desiccator. Tantalum was found to be a suitable alloy container. The alloy components were contained in a 1-in.-diam cylindri-

Jan 1, 1968

By D. E. Peacock, B. Harris

Thermal-expansion and electrical-resistivity measurements have been carried out below 400°K on niobium and two niobium alloys containing tungsten. For anonaly in the expansion us temperature curve below aboct 300°K. This reslt is consistent with an earlier obsercation that Young's modilus joy Cb-132 lms an unusiully strong -tenperati-e dependence below roon temperature. No anonulous behavior was observed in the resistiuity vs temperature curve for either alloy or in the magnetic susceptibility us tenperature curve for Cb-132. These results are disclssed in terms of various electronic and bonding theories of the transition metals and their alloys, but it has not been possible to reach any definite conclusion as to the cause of the results obtained. ALONG with investigations of the low-temperature mechanical behavior of niobium and its alloys, some of the physical properties of these materials have also been studied. In the work described here, thermal expansion and electrical resistivity were measured below 400°K for niobium and two of its alloys, Cb-132 and D-43. In addition, the magnetic susceptibility of Cb-132 was measured over the same temperature range. The alloys are representative of two distinct tion-hardened alloy such as might find service as a turbine blade, while D-43 (Nb, 5.3 at. pct W, 1.1 at. pct Zr. and 0.08 at. pct C) is a solution- and dispersion-hardened alloy, of considerably lower strength than Cb-132. which is a potential vane material. Their significant common feature is the presence of tungsten as the principal source of solution hardening. EXPERIMENTAL TECHNIQUES Thermal-expansion measurements were made with a quartz-tube dilatometer using baths of liquid nitrogen, liquid bromoethane, and a liquid polyalkylene glycol derivative to cover the range 80 to 400 K. Results are recorded as expansion relative to that of quartz, and the probable maximum error in any value of relative expansion. All, is about il pct. The metallurgical condition of the specimens, which were in rod form. will be discussed in the section dealing with experimental results. Resistivity was measured on recrystallized wires 0.030 in. in diam using a potentiometric technique. The same baths were used for temperatures between 80' and 400°K as were used for the expansion measurements. and in addition the resistance of D-43 and Cb-132 was measured at 4.2 K by immersion in liquid helium. The maximum expected experimental error in any resistivity value is about 3 pct and that in any change in resistivity about i0.05 pct. Temperatures in both sets of experiments were measured with liquid-in-glass thermometers with an accuracy usually better than 1°K. EXPERIMENTAL RESULTS 1) Thermal Expansion. In Fig. 1 is shown the relative linear expansion of recrystallized niobium. D-43. and Cb-132. The curve for Cb-132 is composed of results from several runs on three different samples. Two of the samples were annealed for an hour at 1500°C to cause recrystallization and the third was annealed for an hour at 2000'C to remove some mi-crosegregation of tungsten which was known to be present in the wrought alloy received from the manu-

Jan 1, 1967

By L. R. Woodyatt, H. J. Beattie, C. T. Sims

Theories correlating the formation of u and related intermetallic compounds to the electron-per-atom density of binary and ternary alloys have appeared regularly in recent technical literature. These same principles can be modified and applied to complex precipitation-strengthened alloys such as the iron-, cobalt-, and nickel-base superalloys and the stainless steels. Since these complex alloys contain carbides and other phases that normally precipitate before the U-type phases, the nature and amount of the precipitated phases must be calculated first. The following general formula is then applied to the residual matrix composition of the alloy: element. The magnitude of the resulting number is indicative of whether the alloy will form a a -type phase. When these calculations (which are computerized) are systematically applied to alloys of knoun phase analysis, a breakoff in average electron-vacancy number is noted between U-free and U-prone alloys. Alloys with an average electron-vacancy number higher than the breakoff form a-type phases, while those with lower ones do not form these phases. This method could then be used to eliminate from consideration all experimental compositions that would precipitate undesirable phases. It also is useful in evaluating analyzed heats of alloys where minor heat-to-heat variations determine whether the alloy is o-free or o-prone. THE highly significant development of strong, ductile superalloys to provide reliable construction materials in the 1000" to 2500° F temperature range has been due principally to unremitting application of Edisonian techniques and logic by the dedicated physical metallurgists who have shouldered this responsibility. Tools such as the electron microscope, phase analysis, and computers to accomplish regression analyses have been used heavily, but the effort has been essentially practice of an art, rather than a science. The objective of this paper is to describe and illustrate application of some relatively fundamental principles to certain of these alloy systems in an attempt to remove some of the empiricism from the technology. Specifically, the work presented here deals with the use of periodic-group relationships to predict the formation of intermetallic phases which can occur in primarily austenitic (fcc) structures. Calculations that have been developed might be applied in the design of new alloys and the evaluation of known alloys, and thus have the potential of eliminating vast areas of unnecessary alloy preparation and evaluation. ALLOYING CONCEPTS AND STRUCTURAL FEATURES OF SUPERALLOYS Strength is produced in austenitic superalloys by three principle mechanisms: 1) precipitation of y'; 2) formation of carbides; 3) solid-solution hardening by soluble refractory metals. The first mechanism requires the addition of aluminum and titanium, the second requires carbon and carbide-forming elements, while the third calls for the addition of molybdenum and/or tungsten. A considerable concentration of chromium is usually maintained to resist oxidation/corrosion, but it is also an important carbide-forming element. Fig. 1 shows a sketch and electron micrograph of the structure of a typical wrought nickel-base super-

Jan 1, 1967

By V. Koump, T. F. Perzak, R. G. Olsson

The vate of dissolutioz of carbon in molten Fe-C alloys urns studied by votating- cylindrical g-vaphite sairlples in a stationary crucible containing the melt. The rate of dissolltion was determdined from the change in the bnth co)npositiorz. Alccss-tvansfev coeffi'cients, calcilated with the assurlption that the inte)yacial liquid ulas saturated with carbon, were found to be in agreement with an existing Correlation fov mass transfer jroni votating cylinders. It is corzcllrded tlat, itz the wnge of- Reynolds' numbers itzvestigated (790 to 18,000), the vate of dissolutio of carborz in Fe-C alloys is controlled by tile rate of carbon difirsion from the interface. The dissolution of carbon in molten Fe-C alloys has been the subject of a number of investigations. Most of these investigations have been inconclusive because of poorly defined experimental variables. Two of the more sophisticated studies are summarized below. Dahlke and Knacke' studied the phenomenon by, in part, immersing graphite rods into 0.5 pct carbon-steel for different lengths of time. Since the experiments were conducted in air or in CO atmospheres, the melt was strongly agitated by gas evolution. It was concluded that the change in bath composition as a function of immersion time was in agreement with the assumption that the dissolution process was transport-controlled. The hydrodynamic conditions in these experiments, however, were not well-defined and gave no indication of the nature of the dissolution process at higher fluid velocities. In a recent study Shurygin and ruk investigated the dissolution of carbon in molten Fe-C, Fe-Si, Fe-P, and Fe-Ni alloys. Small graphite disks were rotated in a crucible containing molten alloys under such conditions that only the lower face of the disk was exposed to the melt. The results of this investigation indicate that, over the range of velocities (100 to 1000 rpm) and bulk liquid concentrations (0.7 to 4.5 wt pct C) considered, the dissolution of carbon in the iron alloys is limited by the diffusion of carbon from the interface to the bulk liquid (a transport mechanism). For the particular geometry used by these authors, exact analytical solutions of hydrodynamic and diffusion problems are aailable. Hence the experimental results obtained by Shurygin and Kryuk permit the evaluation of diffusion coefficients of carbon in the four systems investigated. In the present investigation a series of experiments were conducted in which the rate of dissolution of carbon in Fe-C alloys was measured under conditions which permitted wide variation of the fluid velocity and the carbon concentration of the bulk liquid. Graphite cylinders were rotated at different speeds in a stationary concentric crucible containing various molten Fe-C alloys. THEORETICAL DEVELOPMENT In general, the resistance to mass transfer from a solid interface to a turbulent liquid is assumed to reside in a laminar boundary layer adjacent to the interface. If it is also assumed that the diffusion coefficient is independent of concentration, the steady-state rate of dissolution for the case of arbitrary liquid and solid densities can be obtained from the integration of the equations of continuity. The derivation is similar to that used by Lommel and chalmers4 for the case of pl = ps. The solution, expressed in terms where N = rate of diffusion of the solute from the interface. Exact analytical solutions of the hydrodynamic equation for the boundary layer thickness are available for only a limited number of geometries. Consequently, a mass-transfer coefficient, k, is usually

Jan 1, 1967

By Jack L. Taylor

Single crystals of tungsten grown from powder -metallurgy swaged rod by high-temperative annealing were deformed in tetzsion at temperatures from 2500 to 5000 OF. Orientation of specittzen tensile axis, strained ratrix, and defortnation bands was determined optically by reflections from {110} etch pits. Slip traces meve analyzed and slip directiorz determined. Results indicate that {110}(111) , {112){111}. and {123}{111} type slip occur in tungsten over the terpe,atuve rutge investigated. Slip is orientation-dependent occuvring on tCuzt cowzbitzation oj slip plane and direction which has the highest critical resolved shear stvess. Overshooting appears to be a general occurrence between 2500' and 5000°F. Dejornatiotz bands show rotation in a directiorz opposite to the yotation of tire tensile axis. DEFORMATION in bcc metals has been reviewed by Maddin and Chen,' Keh and eissman,' and most recently by Nabarro, Basinski, and olt. From these reviews it is apparent that some disagreement exists concerning the crystallography of plastic deformation in bcc metals. There is evidence of noncrystallo-graphic slip, the crystal slipping on or near a noncrys-tallographic plane in the (111) zone for which the resolved shear stress is greatest. There is also evidence to indicate that crystallographic slip occurs in the planes of the same zone. On the other hand, there is agreement that the close-packed direction ( 111) is the slip direction in bcc metals. Further, in pure bcc metals4 and alloys the operative crystallographic slip systems are strongly dependent on temperature. Both crystallographic and noncrystallographic slip have been reportede8 in tungsten, a group VIA bcc metal. The number of slip families which operate in the case of crystallographic slip, however, has been in question. The earliest study by oucher' of single-crystal tungsten tested at temperatures of 1800 to 5000°F led to the conclusion that only {112)( 111) type slip operated. Raymond and eumann recently reached the same conclusion studying deformation by rolling of plasma-flame single crystals at 1800°F; however, only [loo] and [110] orientations were studied. Work at high temperatures by Leber and Pughs on tungsten and Chen and Maddin9 on molybdenum suggests that conjugate slip on nonparallel (110) planes may account for the slip on (112) and (123) planes found by others working with bcc metals. The present paper presents evidence of three families or modes of slip in tungsten in the temperature EXPERIMENTAL PROCEDURE Material. Standard microtensile specimens, 0.160 in. diam by 0.640 in. gage length, were ground from commercial powder-metallurgy swaged tungsten rod, type MK. Specimens were heated for 10 min at 5150°F or 6 hr at 5400°F in vacuum of 1 x 105 Torr or less to produce single crystals. At the lower temperature an average of two out of seven specimens heated in a group developed single crystals throughout the specimen length as shown in Fig. 1, the rest remaining wholly poly crystalline. At the higher temperature, three or four out of seven specimens became single crystal. Other than to note that Laue X-ray photographs generally showed sharp, well-defined spots, no attempt was made to assess crystal perfection or measure dislocation density. Two tungsten single crystals grown from the melt by the plasma-arc process were also used for this study.

Jan 1, 1967

By D. A. Munro, G. P. Contractor

Fourteen 50-lb laboratory melts were investigated to determine the effect of uranium on the tenpering characteristics of loo-carbon (0.06 to 0.1 pct C) steels. It was found that uranium additions, particularly in the range 0.30 to 0.45 pct, enhanced the hardness and both ultimate and yield strength of the experivzental steels in the quenched and tempered condition. The structural and morphological chazges indicated that uranium retarded tempering of the tnartensite, thereby hindering the normal formation of polygonal ferrite formed in the late stages of tempering. The effect of this was to make possible the re-tension of the acicilar ferritic structure in the uranium-bearing' steels. The iraniuin-bearing steels also showed IVidnzanstatten-type growth of ferrite plates and had large prior austenite grains containing assenzblies of fine ferrite grains, mainly acicular in geometry. The fine-grained ferrite structure and the presence of more numerous and apparently smaller precipitates in the uranium-bearing steels are thought to he principally responsible for the itnproved tensile strength and hardness of the experinzental uranium-bearing steels. At ternperirzg temperatures above 455% (850'F) the ferrite in the higher-uraniun steels nzaintained acicularity and, hence, its strength and resistance to tempering. Uranium did not produce a secondary hardening peak. However, it retarded softening during the third stage of tempering because of its effect of inhibiting the grouth of cementite particles and of retaining the acicularity of ferrite plates. The resistance to coalescence accounted for the slow grocth of the ferrite grains in the uranium-modified steels and, hence, fov the persistence of the acicular ferrite structure. IT had been found previously1 that uranium additions up to about 0.45 pct had no significant effect on the tensile properties of low-carbon steel (0.06 to 0.10 pct C) in the as-rolled and normalized conditions, Fig. 1. On the other hand, it was observed that uranium in excess of about 0.30 pct had an embrittling effect as revealed by Charpy V-notch impact results. It was also noted that, as the uranium content increased, the morphology of pearlite changed from lamellar to feathery and the ferrite grains showed an etching effect resembling striated or dashed markings, suggestive of precipitation. The sharp drop in the impact properties shown in Fig. 2 warranted an assumption that the uranium content of about 0.30 to 0.45 pct may produce some secondary hardening reaction on tempering, analogous to that associated with a Cr-Mo-V steel, which shows very poor CVN toughness at the secondary hardness peak in the tempering curve.1' With this background and the reported findings of Hasegawa and noda that low-carbon uranium-treated steel showed signs of secondary hardening, the present investigation was undertaken to determine the effect of uranium additions on the mechanical properties of 0.10 pct C steels. No attempts were made to investigate in detail the mechanisms of hardening, although some suggestions based on the experiments are made. MATERIALS AND PROCEDURES A series of 50-lb induction-furnace melts was made using AISI 1008 rimming steel billets as the melting stock. The melting, forging, and rolling techniques proven satisfactory in previous projects'-3 were employed as a guide for this investigation. The steel was deoxidized with aluminum (2 lb per ton) prior to the addition of high-purity uranium. The analysis of each melt is given in Table I. Properties were evaluated as a function of heat treatment and are presented in terms of hardness and tensile strength vs tempering temperatures. The variation of hardness with the tempering temperature was studied on the quenched and tempered specimens, some of which measured 0.50 by 0.25 in. diam and the others 0.40-in. cubes. Before quenching, the specimens were vacuum-sealed in glass tubes and normalized at 900°C (1650°F) for 20 min. Following this treatment, the sealed specimens were hardened by austenitizing at 955°C (1750°F) for 20 min and water quenching, and then tempered for 1 hr in the range 150 to 730°C

Jan 1, 1967

Jan 1, 1967

Jan 1, 1968

By Y. C. Liu, G. A. Alers

The anisotropy of Young's modules has been measured in a series of Cu-Zn alloys containing from 1 to 28 wt pct Zn and cold-rolled to 97.5 pct reduction in thickness. These modulus data show a transition in texture as a function of zinc content. In alloys containing 3 pct Zn or less, the texture is essentially that of copper. A transition is clearly seen to develop in 5 and 8 pct Zn alloys, and to have been completed in a 12 pct Zn alloy. Increasing the proportion of zinc to 28 pct does not produce any further changes in texture. The ease and clarity with which this texture transition can be seen in the modulus data is in great contrast with the inccertainty in the visual detertiination of the range of texture transition from a series of pole figures. It is also shown that the rolling texture of the high zinc content alloys cannot be a one-COIIIponenl texture, characterized by the (110)(112) ideal orientations, as usually assumed. A second, quite important component must also be present. Furthermore, the present data are inconsistent with matrix orientations on which the "oriented growth" hypothesis of the Formation of recrystallization textures is based. THE rolling textures of binary fcc alloy systems have generally been considered to lie between two terminal textures. One of these terminal textures is the copper type and the other is the 70:30 brass type. Alloys of intermediate solute content exhibit a texture which is said to be a transition between the two terminal textures. On the basis of efforts to correlate rolling and recrystallization textures, two concepts have been advanced in the literature on the nature of these transition textures. One school1 suggests that the addition of alloying elements, e.g., zinc, causes a gradual rotation about one of the (111) poles from the (358)( 523) ideal orientation of the copper-type rolling texture to the terminal {1 10)( 112) ideal orientation used to describe the rolling texture of 70:30 brass. This concept is depicted in Fig. 1 with the angle of rotation corresponding approximately to the zinc content and is designated here as the "rotational concept", since the ideal orientation of the transition textures varies continuously with alloy content. The other concept,' the "mixture concept", suggests that the copper-type rolling texture is a two-component texture. {358) (523) and {110)(112). The addition of alloying elements affects only quantitatively the relative amounts of these two components—a decrease in the amount of material in the {385}(523) orientation and an increase of that in the {110)(112) orientation with increasing solute content. An experimental distinction between these two concepts is essential to a better understanding of both the mechanism of formation of rolling textures and the subsequent formation of recrystailization textures in fcc metals. Because of the lack of resolution inherent in pole figures, it has not been possible to differentiate between the two concepts on the basis of this data. Both concepts, in fact, make use of the same set of pole figures but interpret them in a manner acco-rding to the view held.'" Experimental results obtained from inverse pole figures or selected-area electron diffraction3j4 simply -yield more refined pole figures but do not eliminate the ambiguity of interpretation. Quantitative measurement of an entirely different, orientation-dependent property must thus be considered

Jan 1, 1967