Search Documents

By R. S. Wagner, C. E. Miller, H. Brown

A dc field was applied to liquid BI-Sx or Au-Ge alloys of eutectic composition. The liquid alloys were kept at a temperature slightly above the eutectic. The concentration changes due to electrodijfusion are large enough to cause nuclcation and growth of the primary phases at the respective electrodes. Nearly complete separation of Bi-Sn eutectic was obtained as well as substantial separation of Au-Ge eutectic. The effect of an electric field on the solute distrihn-tion was itluestignted itt tlirectiortally solidified rods of a dilute Bi-Sn (0.5 al. pc,t Bi) alloy. Field-freezing was carried out in small-diameter cupillay tubes to avoid cotuectice mixing -of the liquid. The relative sollcte corzcentratioi, Cs/Co , was rneusred by n radioac1il.e tracer netlod. Cs/Co can be made both largev than unity or srialler than the equilibiuwz distvibrrlion c.oejyicienl, k, , oiler a substattiul portion of the soliclifi&apos;erl rocls. A direct current, passed through a liquid-metal solution, can cause substantial concentration changes by electrodiffusion. The magnitude of the change depends on the difference in ionic mobilities of the atomic species in solution. Electrodiffusion has been studied in many binary and ternary liquid alloys.&apos;y2 It was found that the rate of material transport decreases with time for a constant applied field, as a concentration gradient is established in the solution. A steady-state concentration profile is achieved when electro-diffusion is compensated by chemical diffusion. This may seem to limit the use of electrodif fusion for metallurgical application. However, a way of utilizing the effect of electrodiffusion is to combine it with crystallization or controlled freezing. rakin was first to propose this as a new method of separating metal alloys of eutectic composition at temperatures slightly above the eutectic temperature. It was possible by this method to separate Bi-Sn and Bi-Cd eutectics into their component phases. Angus et al discussed the possibility that the effective distribution coefficient, keff, could be varied by proper application of an electric field during solidification. The combination of electrodiffusion and solidification, called field-freezing, was discussed in detail by Pfann and aner. It was shown that field-freezing can be used as a crystal-growth process, an efficient method for eutectic separation, and a new means of changing the effective distribution coefficient. k,ff, beyond the usual range of ko < k,ff < 1. The liquid layer adjacent to the solid-liquid interface can be either increased or depleted in solute due to

Jan 1, 1967

By G. G. Hancock, H. H. Johnson

Hydrogen gas at atmospheric pressure is shown to cause substantial embrittlement in a martettsitic high-stretzgth steel. Subcritical crack growth is observed at very lom stresses and with high growth rates. It is suggested that an adsorbed layer of hydrogen atoms at the crack-tip surface provides the damaging hydrogen. Oxygen in small quantity, as little as O.7 pct by volume, is shown to eliminate subcritical crack growth in gas environments caused by hydrogen or water vapor. However, dissolved oxygen in water has little or no influence upon crack-growth rates. Oxygen-stopped cracks may be restarted by water, or by hydvogen or water vapor if oxygen is removed from the environment. These observations are interpreted in terms of preferential adsorption of oxygen at the crack tip and the formation of an oxide barrier. RECENT investigations1-3 have demonstrated that environmental factors are frequently responsible for delayed failure in martensitic high-strength steels. The environment causes crack initiation from preexisting cracklike flaws at unexpectedly low stresses, often far below the uniaxial yield strength. The crack then propagates at a rate controlled by the environment and the crack-tip stress-field intensity; during this period crack propagation will cease if either the stress or the aggressive environment is removed, and this may be considered a definition of subcritical crack growth. Fracture occurs when the crack has grown to a critical length, such that the fracture toughness of the steel is exceeded. Several liquids are known to cause delayed failure, but water and water vapor are the most severely damaging of the environments investigated to date.&apos;-3 It has been suggested that hydrogen produced during corrosion reactions may be the actual embrittling agent2 The severe embrittlement caused by water vapor inevitably raises the question as to whether other gas environments are damaging. Previous work4&apos;5 has demonstrated that high-pressure hydrogen (2250 psi or greater) is an effective embrittling medium, as measured by such criteria as reduction in area, notch tensile strength, and time to failure. Moreover, the embrittlement was eliminated by the addition of small quantities of air or oxygen to the high-pressure hydrogen, but it was not influenced by additions of nitrogen or argon.4 In the present study attention is focused upon gas environments at atmospheric pressure, in particular hydrogen and oxygen. The influence of these constituents upon the initiation and growth of a crack from a pre-existing cracklike flaw in a high-strength steel was determined directly by the electric-potential method of monitoring crack growth. MATERIALS AND PROCEDURE The H-11 steel was supplied by the U.S. Naval Research Laboratory as 3 by 12 by 0.065 in. sheet specimens with 1-in. transverse center slots. The slot tips were finished by Elox machining to a radius of 0.001 in. or less. The yield strength was 230,000 psi; chemical composition and heat-treatment schedule are given in Table I. The experimental apparatus, precracking procedure, and incremental loading sequence have been described previously.3 In the only significant change, precracking was sometimes carried out by a hydrogen embrittlement and baking technique. All experiments were conducted at room temperature; the hydrogen gas environment was purified by a commercial palladium purifier. Crack initiation and propagation were followed by the electric-potential method,&apos;-3 using a calibration that has been recently dicussed. Stress-field intensities at the crack tip were computed by the conventional Irwin frmula; the plasticity correction was negligible and therefore not included. EXPERIMENTAL RESULTS A striking brittleness associated with molecular hydrogen at atmospheric pressure is demonstrated by the data in Table I1 and Fig. 1, which indicate that subcritical cracks in hydrogen initiate at lower stress-field intensities and propagate more rapidly than in fully humid argon. Ki and Kf are the crack-tip stress-field intensities at initiation and termination of subcritical crack growth, respectively. Termination, of course, corresponds to fracture. In both hydrogen and humid argon Ki is less than Kf

Jan 1, 1967

By R. F. Hehemann, Darrell W. Smith

The kinetics of alloying- in W-5 rot pct Re powder compacts were investigated at temperature about the upper limit for the formation of the x phase, such that a single intermediate phase was involved in the process. The rates and directions of motion of the a-o and o-b interface were assessed as functions of tinze at the sintering teri7peraticve by quantitative izetallog-ralhic techtziques. The iiotion 01 these interjuces could be specified approxitnate1.y by u Parabolic )-ate law and deviations from this ,rate law were attribuled to a complex interaction between surface dif&apos;fusion and volume diffusion during the initial stages of sintering. WHEN binary or more complex alloys are produced by sintering compacted blends of elemental powders, a complication is encountered which does not arise in the sintering of pure metals. In addition to concern for grain size and densification, the rate of inter diffusion of the component elements must be considered. The general problem of alloying during sintering has been treated by numerous investigators.&apos;-7 These investigations have been concerned only with systems that form continuous series of solid solutions and a concentric-sphere diffusion model4 provides a useful description of homogenization in these stems.&apos; Some controversy remains, however, over the contribution of surface and grain boundary diffusion to the homogenization process. Heckel% ePorts that homogenization can be described by volume diffusion at all temperatures, whereas other invetiators&apos;&apos; recognize the importance of surface and grain boundary diffusion, particularly at lower temperatures. Analysis of the homogenization process in partially miscible systems is complicated by the motion of the interfaces separating the individual phases. A simple analytical solution does not exist for such finite systems with spherical symmetry. It was the purpose of this work to examine the kinetics of the formation and dissolution of an intermediate phase in a binary system through an assessment of the motion of the interfaces separating this phase from the terminal solid solutions. PROCEDURE The W-Re system is an example of a partially miscible binary system and was selected for study because of its current importance in refractory-metal technology. The equilibrium phase diagram, Fig. 1, shows that the o phase will be formed by interdiffu-sion between tungsten and rhenium. At temperatures between approximately 2125" and 282O°C, the o phase will appear as the only intermediate phase in the diffusion system. In this work, a mixture of elemental powders containing 5 pct Re was employed. In such a mixture, the rhenium particles will be distributed randomly in a tungsten matrix. During sintering, a o-phase layer will form at the W-Re interface. The development and subsequent disappearance of the o phase are controlled by the relative rates and directions of motion of the 0-0 and a-p interfaces. The motion of these interfaces can be inferred from quantitative metallographic measurements of the average radii of the o shells surrounding rhenium particles. Elemental tungsten and rhenium powders of commercial purity were employed in these investigations. The rhenium powder was spheroidized from +200 mesh agglomerates by plasma-arc spraying and was then classified to yield a powder composed of essentially

Jan 1, 1967

By J. Bruce Wagner, Roger L. Levin

Lattice-parameter measurements have been carrzed out at room temperature on undoped and on chromium-doped wustite as a function of oxygen concentration. Results may he expressed by for the undoped uustite. These data are in agreement with and extend the work of&apos; Jette and Foole. The present results are consistent with the cation vacancy model. for metal- deficil wuslite, both undopen and doped. SEVERAL investigators have made room-temperature lattice-parameter measurements on wustite as a function of composition. Jette and Foote used these measurements to determine the phase limits of wustite. Willis and Rooksby and Benard have also measured the lattice parameters of wustite at room temperature, but their values of a. vary considerably from those of Jette and Foote. In conjunction with Studies&apos; on the transition from surface-controlled heterogeneous reactions involving CO-C02 oxidation of metals, lattice-parameter measurements on undoped and chromium-doped wiistite have been performed. These studies are especially needed to clarify conflicting data of previous authors, to extend the data to the stability limits of wiistite as determined by Darken and urr,6 which include a larger range of existence than that found by Jette and Foote, and to test by X-ray means the role of chromium as a vacancy producer in wiistite.

Jan 1, 1967

By J. C. Yannopoulos, N. J. Themelis

Ah electronic thermogravirnetric balance was used to measure the veductioiz rule o single cirpric oxide particles suspended in a stream of hydrogen. Very jzne thermocouples embedded in lie center and at the surface of the sphere recorded the variation of terw perature during reduction. In contrast to iron oxide reduction, where in most instances the rate of interface reactiokl is controlling, the heat- and mass-transfer phenotnena play a predolrinant role in the reduction of cupric oxide. The correlation of experitnental data or tnass lransfev lhrough the boundary layer at Reynolds nunlber 0-4 50 was as jollocs: ThE reduction of cupric oxide by hydrogen is represented by the equation: It is a highly exothermic reaction and the amount of heat released varies only slightly with temperature (-21,430 cal per g-mole at 400°C). Most of the published studies on this system have been conducted at temperatures in the range of 34 to 280c.l-&apos; The concensus of opinion has been that at temperatures below 200°C the reaction is preceded by an induction period during which there is very little or no reduction. The length of this period diminishes as the temperature of the reaction is increased1l5 and aseawa found that at 280°C reduction starts practically immediately when the oxide is exposed to hydrogen gas. The existence of an induction, or incubation, period has led experimenters to believe that the reduction of CuO by hydrogen is catalyzed by metallic copper.&apos; Boldurev and rmolaev found that mechanical additions of powdered copper to oxide did not affect its reduction, although metallic copper produced during the reduction seemed to have a catalytic effect. At least three other authors2&apos;5&apos;7 have reported that addition of copper had no effect on the rate of reduction. Pease and alor&apos; observed that water vapor had a strong inhibiting effect on the reduction at 1503C, but its effect was greatly diminished at 200 C. Pavlychenko and Rubinchik5 studied this reaction at 159 to 235 C and found that, once the reaction had been initiated, there was no inhibiting effect due to the introduction of water in the hydrogen stream; at temperatures above 183°C there was no inhibiting effect due to water vapor, either before or during reaction. The same authors noted that the rate of reduction was independent of pressure in the range of 200 to 700 mm Hg. aseawa investigated the kinetics of the CuO-Hz system at 160 to 280°C and estimated the apparent activation energy at 14,000 cal per g-mole. A similar value (13,500 1200 cal per g-mole) was reported by ond&apos; in the temperature range 148 to 216°C. Bond also reported that there was no incubation period and that water vapor had no inhibiting effect on reduction at temperatures above 190 C. The above studies have been conducted at temperatures below 280°C and the physical configuration of the system under investigation has not been defined adequately. However, it is well-known that the mechanism of gas-solid reactions depends on a number of in series physical and chemical rate prcesses.&apos;&apos; It is, therefore, essential to include among the experimental factors the geometry of the solid system and the mass-transport characteristics of the reducing gas. Scott studied the reduction of packed beds of cupric oxide cylinders by Hz-He streams of very low hydrogen concentrations at temperatures 400 to 600 C, pressure of 10 to 30 atm, and gas velocity from 0.18 to 5.8 ft per sec (3 < Rep < 30). The reduction rate was found to be mainly controlled by diffusion through the boundary layer and through the pores of the reduced copper phase. The following correlation was proposed: Scott in an earlier work studied the reduction of fixed beds of cupric oxide wire and found that the rate of flow of the gas stream through the bed had a controlling effect on the rate of reduction. The same mass-transfer phenomenon was observed by Bond and clark13 on a similar reduction system. The analogy between mass and heat transfer through the boundary layer which exists between a solid surface and the bulk stream stems from the similarity of the differential equations representing these phenomena

Jan 1, 1967

By Robert E. Green, T. Hinton

Expressions are derived for tke orientation factors appearing in the Grana to -Lucke theory of dislocation damping, for fcc crystals. The factors are given as functions of the elastic constants, the direction cosines of the specimen axis, atld the direction cosines of the particle displacemeizts, for darnping due to dislocation motion on each of the twelve possible slip systems as ixell as lor simultaneous dislocation rnotion on all twelve systems. RECENTLY Green&apos; has outlined the general procedure for calculation of the modes of wave propagation in a single crystal possessing a given crystallo-graphic orientation. In addition he has suggested how the results of such calculations along with calculations of the resolved shear-stress factors for slip enable the orientation-dependent factors (orientation factors) appearing in the Granato-Lucke theory of dislocation damping to be calculated. However, reen&apos; assumed that the maximum stress on dislocations was in the direction of the particle displacement of the elastic wave giving rise to the dislocation damping. The present cal&apos;culations show that this is an oversimplified approach appropriate only to special cases of high crystallographic symmetry. The exact calculation of stress on the dislocations can only be obtained by resolving the nine components of stress associated with the elastic wave into the appropriate slip direction and then summing. In this paper the general expressions for orientation factors are derived for fcc crystals in terms of the elastic constants, the direction cosines of the particle displacements, and the direction cosines of the specimen axis, bearing in mind the point mentioned above. Equations are presented which give the orientation factors for damping due to dislocation motion on each of the twelve possible slip systems as well as for simultaneous dislocation motion on all twelve systems arising from elastic-wave propagation. These orientation factors are appropriate to attenuation measurements made by the pulse-echo technique, where the elastic wave is a traveling wave. They will be compared with those for the case of a standing wave as derived by Granato and Lucke which are appropriate to measurements of internal friction by the resonance technique. The expressions for the orientation factors are compared with the five values given by insruch,&apos; based on unpublished work of Granato and Liicke, for positions of highest symmetry in the stereographic triangle. The various equations derived for modes of wave propagation and orientation factors have been evaluated for the case of aluminum crystals at 1-deg intervals throughout the stereographic triangle. These results will be presented in the form of contour diagrams in a subsequent paper3 and their relevance to ultrasonic measurements discussed. ORIENTATION FACTORS The coordinate system used for the calculations is shown in Fig. 1 and all specimen axes are taken to lie in the shaded standard triangle. The twelve slip systems are indexed according to Table I. Following the suggestion of lers, we may define the orientation factor Ok in the Granato-Liicke theory5 by the equation

Jan 1, 1967

By P. Chaudhari, Michael B. Bever

The heat of solution at infinite dilution of selenium in bismuth, the heat of mixing of selenium and bismuth, and the limit of solubility of selenium in bis~rzuth have been determined at 573, 623; and 663°K by metal solution calorimetry. The heat of forrrzation of the compound Bi2Se at these temperatures has been determined from the heat effects associated with the precipitation of the compound from a saturated solution oj selenium and bismuth. The published information on the thermodynamic properties of the system Bi-Se is limited. The heat of solution at infinite dilution of selenium in bismuth at 623°K has been measured.&apos; The heat of formation at 273 K1 and room temperature2 and the heat capacity at 80 K3 of the compound Bi2Se3 have been reported. An estimate of the heat of formation of the compound BiSe at room temperature has been published.2 Information on the phase relations in the system Bi-Se is available.&apos; In the investigation reported here the following quantities have been determined at 573", 623", and 663°K: 1) the heat of solution at infinite dilution of selenium in bismuth, 2) the heat of mixing of selenium and bismuth in bismuth-rich solutions, 3) the limit of solubility of selenium in bismuth, and 4) the heat of formation of the compound BizSe. These quantities were determined by the addition of selenium to bismuth-rich solutions in a metal solution calorimeter. The determination of the heat of formation at the tem- perature of the calorimeter bath involved the precipitation of the compound from a saturated solution in the calorimeter. 5,6 This method differs from that commonly used which requires the addition of the compound and of a mechanical mixture of its components and yields the heat of formation at the temperature from which the additions are made (273 K EXPERIMENTAL PROCEDURE AND CALCULATIONS The solution calorimeter has been described in detail.&apos; Pure bismuth (99.999+ pct) was used as the bath at the start of a run. The calorimeter was calibrated with small amounts of bismuth added from 273°K; the differences of the heat contents of bismuth at 273°K and the temperatures of the baths are listed in Table I. After the calibration, additions of hexagonal selenium (99.999+ pct) were made. Loss of selenium by evaporation was negligible. No unusual experimental difficulties were encountered.9 The differences in the heat contents10 of selenium at 273°K and the temperature of the bath, listed in Table I, were subtracted from the measured heat effects to give the "adjusted heat effects". The methods by which the heat of solution at infinite dilution, the

Jan 1, 1968

By M. E. Wadsworth, K. C. Bowles, H. E. Flanders, R. M. Nadkarni, C. E. Jelden

The kinetics of precipitation of copper on iron of various purity were carried out under controlled conditions. The rate of reduction has been correlated with such parameters as copper and hydrogen ion concentration, geometric factors, flow rate, and temperature. The character of the precipitated copper as a function of flow conditions and rate of PreciPitation has been observed under a variety of conditions. ThE precipitation of copper in solution by cementation on a more electropositive metal has been known for many years. Basile valentine&apos; who wrote Currus Triumphalis Antimonii about 1500, refers to this method for extraction of copper. Paracelsus the Great2 who was born about 1493 cites the use of iron to prepare Venus (copper) by the "rustics of Hungary" in the "Book Concerning the Tincture of the Philosophers". Agricola3 in his work on minerals (1546) tells of a peculiar water which is drawn from a shaft near Schmölnitz in Hungary, that erodes iron and turns it into copper. In 1670, a concession is recorded4 as having been granted for the recovery of copper from the mine waters at Rio Tinto in Spain, presumably by precipitation with iron. Much has been published in recent literature on the recovery of copper by cementation, the majority of the articles being on plant practice.5-24 The rest include articles on investigation of the variables involved25-28 and a review of hydrometallurgical copper extraction methods." This literature has established: a) The three principal reactions in the cementation of copper are Cu + Fe — Fe+4 +Cu [ 11 One pound of copper is precipitated by 0.88 lb of iron stoichiometrically. In actual practice about 1.5 to 2.5 lb of iron are consumed. 2Fe+3 + Fe — 3Fe+2 [21 Fe +2H&apos;-Fe+2 + H2 [3] Reactions [2] and [3] are responsible for the consumption of excess iron. Wartman and Roberson&apos;28 have established that Reactions [ I] and [2] are concurrent and much faster than Reaction [3]. b) Acidity control is important in the control of hydrolysis and the excessive consumption of iron. he commercial workable range is approximately from pH = 1.8 to 3." c) Iron consumption is closely related to the amount of ferric iron in solution. Jacobi" reports that, by leaving the pregnant mine waters in contact wi th lump pyrrhotite (Fe7S8) for 3 hr, all the iron was reduced to the bivalent condition and scrap iron consumption was cut to 1.25 lb scrap per pound of copper precipitated. He also reported that SO2 has been used successfully to reduce ferric iron to the ferrous state. d) The ideal precipitant is one that offers a large exposed area and is relatively free of rust. e) High velocities and agitation show a beneficial effect upon the rate of precipitation, as it tends to displace the layer of barren solution adjacent to the iron and also dislodges hydrogen bubbles and precipitated copper to expose new surfaces. Little work, however, has been published on the reaction kinetics of copper precipitation on iron. Cent-nerszwer and Heller20 investigated the precipitation of metallic cations in solutions on zinc plates. They found the cementation reaction to be a first-order reaction. The rate constant was independent of stirring for high stirring rates and they concluded that the rate is governed by a diffusional process at low stirring speeds and by a "chemical" process at higher stirring speeds where the rate reaches a constant value. This conclusion has been challenged by King and Burger30 who could not find any region where the rate was independent of the stirring speed, although the rate constant they had obtained for high stirring speed was greater than the maximum value of the rate constant reported by Centnerszwer and Heller (by a factor of six). King and Burger, therefore, concluded that the rate of displacement of copper was controlled only by diffusion. Cementation of various cations on zinc has been summarized by Engfelder.31 APPARATUS A three-necked distillation flask of 2 000-mm capacity was used as a reaction vessel. A pipet of 10-mm capacity was introduced through one of- the side necks, the sample of sheet iron, mounted in a rigid sample holder, through the other, the stirrer being in the middle as shown in Fig. 1. The whole assembly was immersed in a constant-temperature bath. The stirrer was always placed at the same depth in the solution. EXPERIMENTAL PROCEDURE Reagent-grade cupric sulfate (J. T. Baker Chemical Co., N.J.) was used to make up a stock solution containing 10 g of copper per liter which was then diluted to various concentrations as required. Experimental data were obtained by measuring the amount of copper and iron ions in solution at successive time intervals. The initial volume of the solution was always 2000 ml, 10-ml aliquots being removed each time for chemical analysis. Because the total volume change of the solution was less than 10 pct, no correction was used for solution volume change. Nitrogen was bubbled through the solution before and

Jan 1, 1968

By Thomas L. Garrard, James A. Sprague, Rex B. McLellan, Samuel J. Horowitz

A simple rnodel for interstitial solid solutions has been devised in which each solute atom interacts with the solzlent lattice in such a way as to exclude an integral number of nearest-neighbor sites from being occupied by solute atoms. The vemaining interstitial sites ave not affected. In calculating the entropy of such a solution the increase in the number of interstitial sites available to solute atoms due to the ozlerlap of blocked sites is taken into account. The ther-modynamic functions and the solute activity fov the solution rnodel are calculated. It is shown that considevation of the overlap sues vise to a correction term of the order 8&apos; ( where 0 is the ratio of solute to solvent atoms) in the thevmodynamic functions of the solution and the solute activity. The theo,uetical equation for the solute activity was used to analyze the available data for the activity of carbon in austenite at three different temperatures. The use of a computer enabled many comparisons to be made between the experimental activity data and those predicted by both the complex blocking model and the simple, widely used blocking model in which the ozierlapping of blocked sites is not taken into consideration. Even though at the highest concentvations oj carbon the value of 0 is small it is shown that the best fit to the experimental data is found with the complex blocking model. RECENTLY it has been shown by analysis of gas-solid equilibriums that many interstitial solid solutions can be described by the quasi-regular solution model in which the partial energy of solution E, is independent of composition and, apart from a composition-independent term due to nonconfigurational factors, the partial entropy is that of an ideal solution. Dilute solutions of nitrogen in both bcc and fcc iron,&apos; dilute solutions of oxygen and silver,&apos; carbon in a Fe,&apos; and dilute solutions of carbon in ? Fe2 are all quasi-regular. In addition many hydrogen-metal solutions, both dilute and concentrated (with the notable exceptions of the H-Ni and H-Pd systems), can be described by this model.3 However, it has been shown that, at various temperatures, solutions of carbon in ? Fe begin to depart strongly from quasi-regular behavior at low concentrations. A plot of the activity of carbon in ? Fe relative to pure graphite vs atom fraction of carbon (Cc) calculated from Smith&apos;s data4 begins to depart from the (nonlinear) plot for a quasi-regular solution at about Cc = 0.02. Several statistical models have been proposed to account for the thermodynamic behavior of carbon in y Fe. Darken and smith4 set up a model in which a carbon atom in its octahedral site in the fcc lattice has either one or no neighboring carbon atoms in the twelve nearest-neighbor octahedral sites. It is assumed that the number of carbon atoms having more than one nearest neighbor is negligibly small and that a solute atom does not interact with another solute atom located at a greater distance than the first shell of interstitial sites. Thus this model contains two characteristic interaction energies. Darken and Smith showed that this model gives reasonable agreement with the measured variation of carbon activity ac with composition. It is noteworthy that Darken and Smith concluded from their analysis of the activity data using this model that there was a repulsive force between carbon atoms in austenite which reduces the concentration of C-C pairs below that corresponding to random mixing. Recently Aaronson, Domian, and pound5 have considered in detail the statistical model developed by Lachere and by Fowler and Guggenheim7 and have shown that it is compatible with the activity data for carbon in austenite. In Darken&apos;s model the energy of solution of carbon in austenite is dependent on temperature and concentration; the departure from Henry&apos;s law arises from the concentration dependence of the energy of solution. In Aaronson, Domian, and Pound&apos;s discussion of the Lacher, Fowler, Guggenheim model the interaction energy wy between adjacent carbon atoms in austenite is strongly temperature-dependent. Aaronson et al . suggested that this temperature dependence of wy and hence the energy of solution of carbon could be explained either by the formation of clusters of carbon atoms (despite the repulsive nature of wy) or by the dual occupancy of the octahedral and tetrahedral sites by the carbon atoms. However, a temperature-dependent heat of solution

Jan 1, 1968

By P. Gobin, J. Perez, P. Peguin

The strain-amplitude- dependent part of the internal friction of alluminum after several ther momechanical treatments has been measured in the I-cycle range and at the ambient temperature. The internal friction in the outer layer of the torsional specimen us stress is computed from the experimental data. The curues obtained are analyzed in tevnzs of u coirzbinntion of AH and p, which aye, respectively, due to the vecersible unpinning from weak pills and to the plastic strain. Considerirlg the notion of thermally activated unpinning and repinning, it is shown that in our experimental conditions tlze dislocation lines acl as in the H model of Granato and Liiclze. It is also seen that the internal friction p which appears at higher- strains call be described by a simple expression which is in good agreement with our results. A qualitative interpretatiorz is proposed by combining these new types of intelpnal fviction. We define the internal friction 6 as half the ratio of the dissipated energy aW during one cycle to the maximum supplied strain energy W of a material submitted to a periodic stress. Experiment and theory show that internal friction varies with stress above a critical value.&apos; Below this value the internal friction is strain-amplitude-independent and is often masked by an experimental background; so we shall call it AB. ~bove this critical value, the internal friction is strain-amplitude-dependent. This quantity is usually called aH:&apos; and it can be explained as a thermal unpinning of dislocations.3-6 Furthermore, at higher stresses, a rapid increase of internal friction appears. This phenomenon could be caused by the plastic strain,&apos; so we shall call it Ap. It seems interesting to us to study the influence of several t her momechanical treatments on the curve internal friction 6 vs strain E, in order to study the variation of AH and p with the concentration and the repartition of linear and point defects. In order to try to explain the results obtained, we shall propose and discuss models for H and hp and shall show that we obtain a combination of these two types of internal friction. 1) EXPERIMENTAL PROCEDURE 1) Preparation and Treatment of Specimens. We

Jan 1, 1968

By T. E. Scott, R. P. Zerwekh

The charactevistics of the deformatiotz of fcc thorium were examined between 78 and 473 K. Activation energy, actiuation volume, and the temperature dependence of the flow stress were determined and conlpared uith several theories for the rate-controlling mechnnistn of the tempemture-dependent component of the flou~ stress. It was established that the Cottrell-Stokes law does not hold, even approximately, for thorium. Through consideration of the above factors and other parameters, it was concluded that the vandom solute barrier theory proposed by Friedel demonstrates the best agreement with experimental observations of the deformation of thorium below ambient temperature. THORIUM, the first metal in the actinide series of rare-earth elements, is interesting and important from two points of view. In the more practical vein, it is a potential reactor fuel. As such, it is important to know its properties. Of specific interest here are the mechanical properties of thorium. Second, no detailed information concerning the deformation characteristics of the actinide elements has been gathered to date. In view of the interesting physical and chemical properties of these metals, their mechanical behavior might reveal characteristics which could improve our understanding of the mechanisms controlling deformation of the more common metals. For example, it has been shown1 that thorium exhibits a yield point which is greatly enhanced by interstitial solute elements such as carbon. This is not a normal occurrence in fcc metals. The goal of this investigation, therefore, was to characterize the deformation of polycrystalline thorium. MATERIAL AND PROCEDURES Thorium, made by the magnesium intermediate alloy process described by Peterson et al.,2 was rolled and swaged to 0.065-in.-diam wire. The metal analysis is given in Table I. After preparation, the oxygen and nitrogen contents had risen to 308 and 60 ppm, respectively. The 0.065-in.-diam wires were cut into 2-in. lengths and annealed in a vacuum of lo-&apos; Torr at 750°C for 1 hr, producing a grain size of 2735 grains per sq mm. The ends of the 2-in. sections were masked off so that a 1-in. gage length could be electropolished. Specimens were polished at 35 v in a solution of 6 pct perchloric acid in methanol which was maintained at 0°C . The gage diameters after polishing were about 0.0625 in. The tests were run on a screw-driven tensile machine at a constant crosshead speed corresponding to a strain rate of 0.005 min-&apos;. The strain rate was changed rapidly after each 0.01-in. extension between 0.005 min-&apos; and one of three higher strain rates which were selected in order to achieve strain-rate ratios of 5, 10, and 20. Tests were run at several temperatures from 78" to 473°K; most were tested at 423", 300°, 215", and 78°K. EXPERIMENTAL RESULTS Flow Stress vs Strain and Temperature. Typical true stress-true strain curves for thorium are shown in Fig. 1 for several temperatures over the range 473" to 78°K. The curves for 78", 215", 300") and 423°K were obtained from strain-rate change tests using the lower (0.005 min-&apos;) or base strain-rate values of stress. Additional tests, using the same base strain rate at different strain-rate ratios, gave curves which virtually superposed on those shown, indicating that strain-rate changes did not materially influence the work-hardening characteristics at the base strain rate. The curves for 273") 373") and 473°K were standard tensile tests at 0.005 min-&apos;. The behavior of the flow stress with temperature is

Jan 1, 1968

By C. N. Reid

Slip-line studies on deformed chromium single cvystals showed the usual bcc behavior. At room temperatuve, cross slip was prevalent—slip was not confined to a given plane, but the slip direction was (111). At -10O0K, slip occuvred on (110) planes, twins on(112) planes, and cleavage on (1001 planes. A single-crystal tensile specimen with an axis close to [011] showed a pronounced yield drop and high strain rate sensitivity which zclere used to derive relevant parame tevs in a dislocation dynamics treatment. Transmission electron microscope studies confirmed the existence of (110) slip planes and showed ecidence of loops punched out by precipitates and of grown-in dislocations promoting tangling. OF recent years experimental studies have been made of the deformation characteristics of single-crystal molybdenum and tungsten, but very little has been published on the behavior of single-crystal chromium. During a study of the mechanical properties of chromium, single-crystal studies were made which have already been partially described.&apos; However, additional information was generated which was not directly relevant to the main theme of Ref. 1, and, therefore, was not reported. In view of the need for complete documentation of deformation modes, the experimental observations made on the deformation of single-crystal chromium are summarized here, together with an electron-microscope study of the associated dislocation structures. It was found that, in terms of the deformation modes, chromium is a conventional bcc metal, showing a very pronounced yield-point phenomenon. Further, it was found that the flow strength of these crystals is very sensitive to the strain rate. Finally, the crystals were observed to contain many unidentified precipitates, which often were associated with prismatic dislocation loops. EXPERIMENTAL METHODS Single crystals were grown from rods of wrought chromium by the method of zone annealing. Rods of "1/4in.-diam were supported vertically in an argon atmosphere while an induction coil was moved up the rod at 1 in. per hr. The power was adjusted to just below that required for melting, and the process produced single crystals in about 30 pct of the rods used. The orientations of the crystals, in general, lay near [011] and are summarized in Fig. 1. Before this treatment, the wrought material contained 35 pprn C, 68 ppm O, and 12 ppm N.* An analyzed single crystal *Usual metallic impurities found in iodide chromium are: Al, 5 ppm; Ca, A ppm; Cu, 2 ppm; Fe, 75 ppm; Yg, 0.5 ppm; Yn, < 3 ppm; Mo, < 3 ppm; Ni, 4 ppm; Si, < 20 ppm; Ti, < 1 ppm; V, 4 ppm; Zr, < 3 ppm. contained 10 pprn C, 79 ppm O, and 50 pprn N. Tension and compression specimens were shaped from the crystals by mechanical grinding, followed by the electrolytic removal of about 0.010 in. from the surface in a perchloric/acetic acid bath. All specimens had a gage length of 0.75 in., and tension specimens had a diameter of 0.100 in., while that of the compression samples was 0.200 in. Mechanical tests were carried out at a rate of 1.3 pct per min, and temperatures below 0°C were attained by means of a nitrogen cryostat similar to that of Wessel.2 EXPERIMENTAL RESULTS Modes of Deformation. In addition to the tensile properties of these crystals, which are described in Ref. 1, deformation markings on the surface were studied. Crystals A and F, Fig. 1, were deformed in tension at 300°K to 10 and 16 pct strain, respectively. The surfaces contained visible slip lines, about 1 C( apart, composed of both straight and wavy segments. They did not define a single plane, and so determination of the slip plane was not possible. However, the slip direction was deduced by comparing the axial orientations of the crystals before and after deformation. Fig. 2 is representative, and shows that the axis ro-

Jan 1, 1968

By M. F. Burr, F. V. Lenel, G. S. Ansell

The mechanism of materials transport was studied in a model experiment in which a silver sphere was sintered to a silver plate under an applied external stress near 800° C. For this purpose the rate of growth of the neck between the sphere and the plate which is proportional to the strain rate of the creep process involved in a neck growth was determined by measuring the change in electrical resistance of the away. This rate of neck growth will depend upon the magnitude of the applied external stress. By measuring the rate just before and just after a change in the external load and therefore the applied stress, the relationship between strain rate and stress can be derived. For material transport by slip in a pure metal it is expected that the strain rate should be proportional to the 4.5th power of the stress, while for transport by diffusional flow the strain rate should be proportional to the first power of the stress. It was found that for stresses above 5 X 10&apos; dynes per sq cm (70 psi) the exponent in the stvain rate-stress relationship was near 4.5 while for a stress of 0.7 x 108 dynes per sq cm (10 psi) an exponent of 1.8 was determined indicating that under the conditions of the experiment the transport mechanism for creep in silver shifts from diffusional flow to slip in the region of 0.7 x 106 dynes per sq cm (10 psi). The importance of these findings for an understanding of the mechanism of material transport in conventional sintering (without an external load) is pointed out. In a paper by Early et al.,&apos; the mechanism of material transport during sintering was treated as a creep process. It was pointed out that two possible types of creep processes could operate during sintering. In one of these material transport takes place by vacancy diffusion due to a gradient in chemical potential. The vacancy sinks in this diffusion process may be either grain boundaries, as in Herring-Nabarro microcreep, or regions beneath a surface of small radius of curvature. The diffusive transport may be by volume, grain boundary, or surface diffusion. In the other mechanism, creep takes place by slip, i.e., dislocation motion with its rate generally controlled by dislocation climb. One method of distinguishing between these two modes of materials transport is to investigate the creep rate, i.e., the rate of material transport as a function of stress. For material transport by vacancy diffusion, the creep rate is proportional to the stress.&apos; For creep by slip, controlled by dislocation climb, the creep rate is proportional to a power of the stress. For pure metals this power is 4.5;374 for dispersion-strengthened material a fourth power relationship can be derived.5 This difference in the stress dependence of the strain rate is illustrated schematically in Fig. 1, in which the logarithm of strain rate is plotted vs the logarithm of the stress for material transport in a pure metal by vacancy flux and by dislocation climb. The stress range in which the two types of material transport overlap would be expected to be relatively small. In the experiments described by Early and coworkers compacts pressed from spherical copper powder were sintered isothermally under an applied axial external load in a dilatometer. During sintering the magnitude of the applied external load was changed and the rate of axial shrinkage of the compact before and after the load change determined. In order to find the stress dependence of the strain rate the magnitude of the stress acting on the neck area between the spherical particles before and after the load change had to be calculated. This stress is the resultant of the stresses due both to the externally applied load and to surface tension. The stress due to surface tension is a function of the geometry of the powder compacts. It can be determined, at least for simple geometrical arrays,&apos;76 but it is difficult to obtain exact values of the stresses for actual powder compacts when only average values of particle diameters and of neck diameters between particles are available. The calculation of stress and the strain rate-stress relationship is therefore only very approximate.

Jan 1, 1968

By G. R. St. Pierre, L. M. Adelsberg, R. Speiser

The rate of scale fot&apos;~I~ti0n on tantalum held in H20-Hz-Ar gns mixtures at temperatures between 840" and 1250°C is related to gas composition and ternpevature. It is found that water vapor partial pressure determines the oxidation rate at a given temperature and that the oxygen potential as fixed by the water vapor to hydrogen ratio Ins no significant effect on the oxidation rate. The Ta205 scale formed during oxidation is composed of an inner lattice-dijf~ision barrier and an outer layer of- cracked/porous oxide 1 HE oxidation of tantalum at temperatures less than 800°C is characterized by solution of oxygen into the metal,&apos;-&apos; the formation and growth of suboxides into the metal,&apos;)2~10-15 and the delayed nucleation of the highest oxide, Above 800°C, Ta205 is found to nucleate rapidly10, 11, 15, 16 except at low oxygen pressures:15 however, there is uncertainty regarding which does not retard the oxidation process. For each gas con~position and temperature investigated, the oxidatioz rate becomes constant after a short adjustment period. It is shozm that a constant oxidation rate nzay pre~?ail even though the tlzickness of the inner lattice-dijjitsion layer of Ta205 is clanging. TFze initial czcrz!ature of the typical &apos;Paralinear" oxidation curve may result froprz causes other than an increasing thickness of tlze inner protective layer. the detailed mechanisms of the high-temperature oxidation. Peterson, Fassell, and wadsworth17 observed linear oxidation behavior for tantalum in oxygen at temperatures between 600" and 1000°C. They reported that equilibrium adsorption of 0, occurs on a surface prior to the rate-deter mining step of the reaction. Cowgill and stringer1&apos; confirmed the observations of Peterson and his coworkers. They stated that the rate-determining step of the reaction could be either the incorporation of adsorbed oxygen into the anion lattice or the dissociation of 0, at the gas-oxide interface. The relative rates of the two surface reactions were proposed to be dependent upon the reaction temperature and the oxygen pressure. stringerlo subsequently reported that the reaction surface is located somewhere

Jan 1, 1968

By David L. Sikarskie

The measurement of residual stress fields using X-ray diffraction techniques requires the removal of successive layers of material from the specimen. In the process of removing these layers, the underlying residual stress field is altered; hence, if the original stress field is desired, corrections must be made to the measured stresses. Although these corrections already exist for a number of cases, an alternate procedure is outlined herein whereby the corrections are presented in series form. This form is numerically more convenient within certain ranges of correction depths and in its simplicity gives additional insight into the factors affecting the corrections. It, further, readily permits determining the proper slice depth to remove and the effect on the correction of both specimen thickness and magnitude and form of the measured residual stress itself. ONE of the techniques currently being used to determine residual stress fields is X-ray diffraction. Since X-rays are diffracted essentially from the layers of atoms near the surface of the specimen, of the order of 0.0001 to 0.001 in. depending on conditions, the method can only determine stresses* in this very thin surface region. Therefore, if the residual stress field at some depth into the specimen is required it is necessary to remove successive layers of material taking measurements after each cut. In the process of removing a thin surface layer of stressed material, however, the over-all equilibrium of a cross section of the specimen is disturbed with the result that the internal residual stress which existed before the slice of material was removed is altered. This alteration of stress occurs after each slice and its effect is cumulative. Thus, if the original stress distribution is desired, corrections must be applied to the measured stresses. These corrections can be found by satisfying equilibrium on each new cross section. These corrections have been derived in detail for a number of cases, e.g., cylinders, bars, plates,&apos; and also are given in Appendix VI of Ref. 2. In each of the above cases the correction terms require the evaluation of definite integrals of the measured residual stress distribution. In general, this is indeed the way one would proceed with the corrections. There are a number of instances, however, where the integrals can be replaced by a series form of correction which is considerably more convenient numerically and, also, gives added insight into the factors which influence the corrections. Such a form of the correction is particularly useful, for example, if one is interested in designing a test such that stress corrections will be small. Also, the question of what depth of slice to use in relation to both specimen thickness and residual stress distribution itself must invariably be answered. Questions of this type can be readily answered using a series form of correction. In addition, if the correct residual stress distribution is needed only for limited depths into the specimen the series correction provides numerical results which are equivalent to the integral correction. I) DERIVATION OF THE SERIES CORRECTION The problem to be considered here is that of a bar or plate,* i.e., either one or two dimensions of the specimen is large compared with the third. Also, the residual stress distributions considered depend only on z, see Fig. 1. In view of this it can be shown&apos; that a stress correction, based on simple beam theory, satisfies all conditions of "elasticity theory" and hence is the correct (and only) solution. The integral form of the correction (this assumes that the measured residual stress is a piecewise continuous function) as given in Ref. 1 is:

Jan 1, 1968

By W. A. Tiller, S. O’Hara

Grain refinement in stirred melts has previously been shown to arise from dendrite segmentation. The present work discusses experiments capable of distinguishing between remelting and mechanical effects which result from fluid motion. Nucleation of still un-dercooled Sn-1 pct Pb melts with a single-crystal seed shows that the grain size of the resulting ingots decreases as the undercooling at nucleation increases up to about 1Z0C, then increases again for larger undercoolings. Pure melts exhibit little refinement as a result of nucleation at any undercooling up to 12°C. The presence of fluid motion gives rise to grain multiplication in pure melts, but the magnitude of this effect is partly obscured by solid-state pain growth. The results indicate that two grain-multiplication pvocesses can operate, one which involves dendrite remelt ing, and another associated with fluid motion. Small ingot experiments indicated that an equiaxed transition can be caused by fluid motion. THE presence of forced convection during recales-cence of undercooled Sn-1.3 pct Pb melts has been shown to give rise to extensive grain refinement during solidification of small ingots of this alloy.&apos;&apos;2 In Ref. 2, this refining was shown to result entirely from dendrite fragmentation and not from any nucleation mechanism. The purpose of the present work is to establish what processes lead to dendrite segmentation. Experiments were therefore carried out to determine the resulting structure of both pure tin and Sn-1 pct Pb melts, nucleated at various undercoolings by single-crystal seeds in the absence of forced or natural convection. By comparing the information obtained from these experiments with the results of Refs. 1 and 2, the effects of fluid motion on the ingot structure, and the details of the segmentation mechanisms, should become clear. The results of these experiments should also be helpful in understanding the solidification structures of larger ingots since natural convection, which is known to play an important role in determining ingot structure13 differs only in degree from the fluid-motion effects studied here. I) EXPERIMENTAL PROCEDURE The apparatus shown in Fig. 1 was constructed to permit controlled nucleation of stirred or unstirred supercooled melts using a seed oriented in the tin dendrite growth direction. Because the melts, in all cases, were capable of larger supercoolings than the one used in each experiment, the structure observed always resulted from a single nucleation event at the surface. The sequential procedure was as follows: Tin was melted under purified hydrogen and the oxide removed at a temperature of 450°C . Electromagnetic stirring was then used to clear the surface completely and during this time the guide tube was lowered underneath the melt surface. A pointed Czochralski-like crystal was then propagated from a specially prepared tin dendrite seed4 inside the guide tube while the temperature of the bulk melt was held just above the melting point, ensuring a perfectly clean seed which was epitaxial with the original dendrite. The dendrite and epitaxial seed, still in the guide tube, were withdrawn from the melt which, in turn, was undercooled to 2C° below the temperature at which the nucleation experiment was to be performed. The melt was held there for several minutes, both in stirred and in still-melt experiments. The temperature was next raised to the required value and the melt nucleated by the carrot seed inside the guide tube, the heater power being shut off just after nucleation. In experiments where quenching after nucleation was required, a high-density graphite crucible was used, but otherwise the procedure was as described above. The temperature gradient in the melt before nucleation was kept below 1C° per cm by carrying the experiment out just below the center of the heater shown in Fig. 1.

Jan 1, 1968

By Larry Kaufman, Joan B. Berkowitz-Mattuck, Edward V. Claugherty

The oxidation characteristics of hafnium and zirconiunr diboride were measured between 1200 and 2200&apos;K by a thermal- conductivity method which continuously ttzeasures the rate of reaction of oxygen with the diboride and by a metallographic air oridation method zuhich provides a measure of the total arr7ount of bovide conuerted to oxide for a given time interval. The oxidized specimens obtained from the tl~eritaal-coi~ductitrity method were also examined by quantitatire metal-lographic procedares. The significant results obtained in this investigation reveal that metal-rich compositions of lzafi~iutil diboride proride the most oxidation-resistatzt material up to 2000°K; hafnium diboride is tmre oxidation- resistant titan zirconium diboride at all tempevatures examined; the morphology of the oxide formed on H/B2 and Llie temperature coefficient qi. the oxidation rate constants change at the temperature of ttze monoclinic to tetragonal phase transition] in HfO2; the oxidation of neither HfB2 nor ZrB2, results iN catastrophic Jazlure at lorc. oxygen pressures; and pvefevetztial gvaLti boundary oxidation was not obsevued for either HfBi or ZYB, A comprehensive study of the high-temperature characteristics of refractory transition-metal di-borides is currently in progress. This program has included investigation of the physical, thermal, and thermodynamic properties of TiB2, ZrB2, HfB2, NbB2, and TaB2. In addition, aspects of the synthesis and fabrication of such materials have been studied. In view of the diverse nature of this research, a number of other laboratories have actively participated and contributed specific capabilities for analysis and characterization of these materials. As a consequence, an extensive description of the relevant properties of these compounds has emerged which is central in evaluating their high-temperature (1200" to 2500°K) performance. To date, information on thermodynamic stability, specific heat, and vaporization characteristics,1 hot hardness and electrical resistivity,1, 3 therma1 expansion:&apos;4 and thermal conductivity 1, 5 has been presented. This information has been generated on materials of the highest purity (98.5 to 99.9 wt pct Me + B) and density currently available. Samples fabricated by zone melting6 and high-pressure hot pressing"3&apos;7 techniques have been used to generate suitable specimens for all of the aforementioned studies. dation characteristics of the most oxidation-resistant of these materials, hafnium and zirconium diboride, is presented and a description of the synthesis and the experimental procedures used to prepare and characterize specimens is given. The high-temperature range under consideration (1200" to 2200°K) and the known dependence of oxidation characteristics on sample chemistry, density, and oxidation conditions required a close coupling of the synthesis, fabrication, and evaluation procedures.8 This was accomplished by continual surveillance of chemical composition of starting materials before and after specimen fabrication and by evaluation of density, phase constitution, and microstructural features prior to and after oxidation exposure. I) PROCUREMENT AND CHARACTERIZATION OF STARTING MATERIALS In view of the current state of the art in fabricating refractory boride materials, the methods used in preparing samples for the present study are given in detail as follows: starting materials were purchased in high-purity powder form and fabricated by high-pressure hot pressing into 0.40 by 1.00 in. bars from which oxidation specimens were obtained. The hafnium diboride used in this study was purchased from Wah Chang Corp.; the zirconium diboride from U.S. Borax and Chemical Co. These powders were routinely characterized by quantitative chemical analyses for metal, boron, carbon, oxygen, nitrogen, and iron, by qualitative emission-spectrographic analysis for trace impurities, by X-ray procedures for extraneous phase identification, and by powder densitometry for comparison with X-ray (theoretical) density. Hafnium and zirconium metal and elemental boron were also purchased as high-purity powders and characterized for impurities by emission-spectrographic analyses. The hafnium diboride was procured in three shipments which were designated as HfBl.g7(1), HfB1.88(2A), and HfB2.12(2). The indicated stoichiometry is based on the atomic ratio of total boron to total hafnium; the number in parentheses identifies the shipment number. Shipment 1 was 5 1b, shipment 2A, 1 1b, and shipment 2, 8 1b. The zirconium diboride was procured as a 20-1b shipment and designated as ZrB1.89(1). A small quantity of purified zirconium diboride was also supplied and designated ZrB1, 9(P). The averaged results for chemical analyses which were generally performed according to the procedures set forth in the compilation by KrieGe9 are presented in Table I. Qualitative spectrographic analyses indicated that Ca, Cr, Ti, Si, Zr (in H~B~), and A1 were present at levels between 0.01 and 0.10 wt pct. Other metallic elements were found to be less than 0.01 wt pct. Since it is virtually impossible to purchase these materials in the desired quantities (5 to 20 lb) as single-phase compounds it is necessary to obtain

Jan 1, 1968

By P. Chiotti, J. T. Mason

Ther?nal, X-ray, metallographic, and vapor pressure data were obtained to establish the phase diagram and standard free energy, enthalpy, and entropy of formation for the compounds in the Sw-Zn system. Four compounds, SmZn, SmZn2 , SmZn4.s, and SmZn8.5, melt congruently at 960°, 94Z°, 908°, and 940°C, respectively. The cornpounds SlnZns, Sm3Znll, and SnzZn7.3 undergo peritectic decomposition at 855", 870°, and 890C, respectively. Another compound of uncertain stoichiometry, SmZn11, undergoes peritectic decomposition at 760°C. Four entectics were observed with the following compositions in weight percent zinc and eutectic tenzperatures in degrees Centigrade: 12 pct, 680°C; 36 pct, 890°C; 58 pct, 850°C; and 72 pct, 900°C. An allotropic transformation and a composition range were observed for the SmZnz compound. The transfor)nation varies from 905" to 865°C as the zinc content increases from 16.0 to 48.5 wt pct, respectively. The free energy of formation of the compounds at 50PC varies between -15.9 kcal per mole for SmZn to -51.1 kcal per mole for SmZn,.,. Corresponding enthalpies vary between -19.2 to -78.3 kcal per mole. The ther-modynamic properties for the liquid alloys are described by the relations: A search of the literature revealed very little information on the Sm-Zn system. Chao et al.&apos; as well as Iandelli and palenzonai have reported the structure of SmZn to be cubic B2 type and Kuz&apos;ma et al3. have reported the structure of -sm2zn17 to be of the Th2Ni17 type. The purpose of this work was to establish the phase diagram of this system, to determine the zinc vapor pressure over the solid two-phase regions of the SYstem, and to calculate the thermodynamic properties of the compounds. MATERIALS AND EXPERIMENTAL PROCEDURES The metals used in this investigation were Bunker Hill slab zinc 99.99 wt pct pure and Ames Laboratory samarium. Analysis of the samarium by chemical, spectrographic, and vacuum-fusion methods gave the following average impurities in ppm: Nd, <200; Eu, <100; Gd, <100; Y, <50;Ca, 225; Ta, 400; Mg, 10; Cu, ~50; 0, 175; H, 20; and N, 15. The elements Fe, Si, Cr, Ni, Al, and W were not detected. The samarium was received as sponge metal and was kept under argon except when being cut with shears and when being weighed. Tantalum was found to be a suitable container for alloys with zinc contents up to the Sm2Znl, stoichio-metry. At higher zinc contents the grain boundaries of the tantalum containers were penetrated by the alloy and the containers failed during prolonged annealing. About 25 g of massive zinc and samarium sponge were sealed in tantalum crucibles equipped with thermocouple wells. These crucibles were in turn sealed in stainless-steel jackets. All closures were made by arc welding under an argon atmosphere. The samples were equilibrated in an oscillating furnace and in some cases were given various heat treatments in a soaking furnace. After appropriate heat treatment the steel jackets were removed and the alloy subjected to differential thermal analysis. The apparatus was calibrated against pure zinc and pure copper and found to reproduce the accepted melting points within 1°C. Alloys were subsequently subjected to metallographic examination and those of appropriate compositions were used for X-ray diffraction analysis and for zinc vapor pressure determinations. The vapor pressures were determined by the dewpoint method. Both the differential analysis and dewpoint measuring apparatuses have been described in earlier papers.4, 5 All alloy samples were etched with Nital (0.5 to 3 pct nitric acid in alcohol) except the samarium-rich alloys. These more reactive alloys were electro-polished in a 1 to 6 pct HClO4 in methanol solution at -700c at a potential of 50 v. EXPERIMENTAL RESULTS Phase Diagram. The results of thermal analysis are indicated by the points on the phase diagram, Fig. 1. Eight compounds and four eutectics were observed. The composition of the compounds and their melting or peritectic temperatures are given on the phase diagram. The four eutectic compositions in wt pct zinc and eutectic temperatures in % are: 12 pct,- 680°C; 36 pct, 890°C; 58 pct, 850°C; and 72 pct, 900°C. The stoichiometry of the most zinc-rich compound is still uncertain, but is very likely either SmZnll or SmZnlz. However, to simplify the presentation which follows it will be referred to as SmZnll. As shown on the phase diagram the phase regions for some of the samarium-rich alloys have not been unambiguously established. A sample of pure samarium was observed to transform at 924°C and to melt at 1074"C, in good agreement with corresponding val-

Jan 1, 1968

By A. D. Zunkel, A. H. Larson

Equilibrium antimony contents of pb-sb alloys in contact with PbO-Sb2O3 slags containing less than 45 mole pct Sb203 uleve determined at 650&apos;, 700°, and 750°C in an inert atmosphere. In this ten~pevature range, the antimony contmzt of the alloy increased with increasing temperature at all slag compositions. The PbO-Sb203 phase diagram below 28 mole pct Sb2O3 was determined by thermal analysis and by application of a log sbZ4/y$b0 us plot determined from the equilibrium-activity data. The resulting phase diagram showed a eutectic at a temperature of 604°C and a comfiosition of 21.6 mole pct Sb2O, with a maximum terminal solid solubility of Sb203 in PbO of 5.6 mole pct. These results are compared with existing data in the literature. In the past three decades, only a small amount of experimental work has been done on the slag-metal equilibria in the Pb-PbO-SbaO3 or the analogous arsenic and tin systems. These systems are important in commercial lead-refining processes such as softening and dross fuming since it is impurities such as antimony, arsenic, and tin in lead bullion and Sb2O3, As2O3, and SnOz in lead drosses which must be re-

Jan 1, 1968

By Charles L. Thomas

A novel, highly sensitive, and reproducible nzetlzod for the determination of hydrogen in solid materials is presented. The procedure requires equilibration of the specimen with hydrogen gas, rapid quenching, and hot vacuum extraction of the dissolved gas with subse-quent quantitative analysis by mass spectroscopy. Good linearity is obtained for the Arrl~enius plots of the investigated metals. The advantages in the use of this method over that of Sieverts aye discussed. The solubility data for copper are in reasonable agveewzent with a considerable number of other inuestigations, wllile those fov silver are considerably lower than previously reported. The first known solubility data for gold are presented. Solubility equations and heats of MUCH of the data which are available on the solubility of hydrogen in various metals and alloys have been obtained by the classical Sieverts method.&apos; The method involves the measurement of a decrease in pressure of a gas in a calibrated system, and the calculated contraction in volume is attributed to the solubility of the gas in the metal sample. The procedure requires several corrections, such as the solubility of the gas in the container walls and the diffusion of the gas through these walls, as noted by Steacie and .Johnson2 and others. In addition, errors may be incurred due to reactions between metal surface impurities, such as oxides, and the saturating gas. The precise calibration of the measuring system where large thermal gradients exist can present additional difficulties. Also, accurate volumetric measurements of small quantities of gas are difficult. Many of the objections to the Sieverts method were overcome on solid materials by Ransley and ~eufeld,~ who first saturated the metal with hydrogen and performed a subsequent extraction and measurement of the gas by chemical means. Eichenauer and pebler4 and Eichenauer, Kiinzig, and pebler5 measured the diffusion coefficient and solubility by following the degasification of a sample as a function of a rate of increase in pressure in a previously evacuated system. Here again, however, the procedure involves many of the corrections of the Sie-verts method. The present investigation deals with the solubility of hydrogen in solid copper, silver, and gold by a technique which eliminates many of the aforementioned corrections and possible errors. This procedure requires equilibration of the specimen with gas, rapid quenching, and hot vacuum extraction of the dissolved gas with subsequent quantitative analysis by mass spectroscopy. EXPERIMENTAL Two completely separate systems were employed to accomplish first, the equilibrium saturation of the sample and second, the extraction of the dissolved gas. Saturation Apparatus. The saturation apparatus, illustrated in Fig. l, consisted of a vertically mounted quartz tube with a three-way valve for vacuum or hydrogen near the top and an outlet near the bottom leading to a butyl phthalate seal. The bottom end of the tube was terminated with a joint accommodating an O-ring sealed "Asco Stirring Gland" (The Emil Greiner Co.). This gland facilitated movement of the thermocouple without introduction of air into the system. The upper portion of the tube (above the furnace) was water-jacketed. A Welsh 1405-B mechanical pump provided the necessary system evacu-

Jan 1, 1968