By M. A. Quader, D. Kuhlmann-Wilsdorf, R. A. Dodd

STACKING fault tetrahedra were first observed in quenched and aged pure gold by Silcox and Hirsch1 and identified as defects originating in the collapse of vacancy discs on {111} planes. It was supposed that sessile loops are the first product of the collapse, and that by a dislocation dissociation/glide sequence these are converted into tetrahedra. Although the tetrahedra can be mechanistically accounted for in this way, recent investigations indicate that their growth occurs by the absorption of individual vacancies on small nuclei involving perhaps as few as six vacancies.2-7 Besides stacking fault tetrahedra, triangular and crystallographic shaped Frank loops, although fewer in number, have always been observed in quenched and aged gold.19798 It is not known definitely whether these loops form from collapsed tetrahedra. The fact that the Frank loops are usually larger than the accompanying tetrahedra might indicate that the loops grow independently by absorbing vacancies, but this does not rule out the possibility of the collapse of tetrahedra into loops under all circumstances. Silcox and Hirsch1 have actually observed under the electron microscope tetrahedra collapsing into loops, probably due to stresses set up by the heating of the specimen by the electron beam. The energy residing in the stacking faults of a tetrahedron is proportional to the square of the edge length, while the energy of a triangular perfect dislocation loop depends on its edge length, L, as const L ln(L/ro). Therefore, beyond some critical size tetrahedra must become unstable with respect to collapse into triangular loops.1,3,8-11 However, it seems that in the absence of strong stresses tetrahedra usually decay by the

Jan 1, 1969

By Richards R. Vandervoot

T HE creep behavior of many polycrystalline metals at moderate stresses can be described by the empirical relationship: where Em is the minimum creep rate, A is a constant, a is the applied stress, E is the average elastic modulus at the test temperature, and D is the self-diffusion coefficient.&apos; This equation is generally applicable for strain rates of less than around 10-5 per sec and temperatures greater than about one-half the melting point in absolute units. Under these conditions atomic mobility plays an important role in the deformation process, and steady-state creep occurs when a dynamic equilibrium is reached between the generation and recovery of dislocation substructure. Although several theoretical mechanisms have been proposed to explain the creep of polycrystalline solids,2"4 the dislocation climb model2 is in accord with most experimental observations. The majority of creep data used to develop Eq. [1] came from metals with either the fcc or hcp crystal structures. However, on the basis of results for a and 7 iron as well as those for a and a thallium, Sherby concluded that the high-temperature deformation behavior of close-packed metals and bcc metals is probably the same.&apos; The greater creep resistance of fcc and hcp metals and alloys on a relative temperature scale was attributed to lower diffusivities in the close-packed structures. To further compare the creep properties of fcc, hcp, and bcc metals, creep data for all six bcc refractory metals were analyzed according to Eq. [I]. The results are shown in Fig. 1. The sources of information for the quantities used to prepare this figure are listed in Table I, except for high-temperature elastic moduli. The latter data were obtained from Refs. 28 and 29. The dashed lines in the figure represent the range and breadth of data analyzed by Sherby for fcc and hcp metals. In general, the deformation behavior of all of the refractory metals, ex- cept possibly that of tungsten, can be represented by Eq. [1]. This correlation is strong evidence of the similarity that exists between creep of pure close-packed metals and creep of pure bcc metals. At (Em/D) < 108, the results of Flagella and Tarr on tungsten (W-1 in Fig. 1) agree with the five-power stress law, while those of Green (W-5 in Fig. 1) show a seven-power stress dependence. Where (Em/D) > 108, the stress exponents for other data on tungsten were in the range 10 to 15. It is possible that the creep rate dependence on stress in this region is not a power law but exponential (i.e., Em - eßo). However, it was not feasible to differentiate between these two cases because of the steep slope and scatter in the data. Note the inflection point in the curve for the data of Flagella and Tarr (W-1 in Fig. 1). The slope of the line changes from 5 to around 10 at Em/D = 108. The breakdown of the fifty-power stress law at high stresses is not uncommon in other metals, and this phenomenon may result from nonequilibrium conditions in the material such as excess lattice vacancies produced by rapid straining.30 The mechanical strength of a polycrystalline metal is related to its microstructure. Attempts to establish the influence of grain size on the creep rate of metals and alloys have led to a wide variety of results. For example, the following effects have been observed: creep rate decreases as grain size increases;31&apos;32 creep rate decreases as grain size decreases;&apos;,33 creep rate is a minimum at some critical grain size and increases with either an increase or decrease in

Jan 1, 1969

By William J. Gillich, Gerald L. Moss

PREVIOUS studies of the shock loading of randomly oriented polycrystalline aggregates have firmly established that, after rather short load duration, hydrostatic compression closely approximates the shocked state.&apos; However, McQueen deduced from pressure measurements with good time resolution that, during shock loading, metals begin to undergo a stress relaxation at the yield stress. He suggested that the relaxation is due to plastic deformation accompanying the change from a one-dimensional compression to a three-dimensional, hydrostatic, compression.&apos; Stress relaxation may occur faster as stress is increased above the yield stress, but the existence of unidirectionally compressed states for finite times suggests that the concept of a unidirectionally distorted lattice should furnish considerable insight into the mechanical behavior of materials subjected to shock loading. Here, a crystallographic analysis is presented for the hypothetical situation where atom motion may be considered as unidirectional which, as indicated above, is a useful extension of the macroscopic concept of shock loading to the microscopic domain. Only motion caused by the com-pressive forces is treated; i.e., lattice vibrations upon which this motion is superimposed, as discussed by Fitzgerald, are ignored.3 The purpose of the analysis to be presented is to develop a description for single crystals of the lattice rotations that occur for idealized uniaxial strain deformation. The usefulness of such an analysis in realistic deformation is to give a method of specification of those properties of an initially distorted lattice which would affect the subsequent deformation. Non-axial complications that arise experimentally, such as off-axis rarefaction waves, must be treated in proper context. Consider the material element shown in Fig. 1 and let the compression be uniform at all regions of the element. Then, any interior point of the element is displaced in proportion to its distance from the base of the element. Accordingly, if the top of a unit element is displaced by an amount, (-K), with respect to the base, a point P(X, Y) will be displaced by (-KY). Crystal planes are, therefore, rotated by the compression. Analysis of this rotation may be accomplished from the geometry shown in Fig. 1 where the line OP is the edge of the plane {hkl} and N is its normal. The orientation of the crystal plane with respect to the shock direction is specified by the angle, before deformation. After deformation the edge of plane {hkl}

Jan 1, 1969

By Charles R. Simcoe

The stress-strain curves in the microyield region for various Fe-C solid solutions shown by Davies and Ku are typical examples of parabolic curves defined by the expression a = kEn 111 These data, when replotted on log-log coordinates, as shown in Fig. 9, exhibit three essentially parallel straight lines. It is apparent that carbon increases the flow stresses, but does not affect the exponent n. In other words, the only factor in Eq. [1] affected by in in carbon content is the constant k. As Eq. [1] is written k is the stress at a strain of 1.0. This is unsatisfactory for examining data in the microyield region. Therefore, the equation can be altered to the form: to permit the use of the authors&apos; microyield stress at a strain of 10-6 as k. Extrapolating the curves in Fig. 9 to a strain of 10-6 gives stress values of 2000, 3200, and 5400 psi for 0.008, 0.014, and 0.02 pct C, respectively. These values do not agree exactly with the authors&apos; measured values, but this will not affect the following discussion. The effect of carbon content on the slopes of the stress-strain curves shown in Fig. 2 of the paper by Davies and Ku can be analyzed by differentiating Eq. [2] with respect to strain. Thus: where n is always less than 1.0. Since n is essen- tially constant as a function of carbon content for the data under discussion, the slopes of the stress-strain curves depend only on k and E. If the slopes are examined at various selected Plastic strains. i.e., 10-6, 10-5, and so forth, it follows from Eq. [3] that the dif-ferent slopes for the different carbon contents depend only on the different values of ke=10-6. Thus, the larger ke=10-6, the steeper the linear stress-strain curve will rise with increasing plastic strain. This

Jan 1, 1969

By S. W. Zehr, G. S. Murty, W. A. Backofen

AN observation by Squires, Weiner, and phillipsl has stimulated interest in a mechanism of deformation at high temperature (above -0.5 of the absolute melting point) that is not usually thought to be involved in the creep of metals. They found precipitate-free or "denuded" zones along grain boundaries normal to the stress axis in tensile specimens of a hydrided Mg-1/2 wt pct Zr alloy after slow straining at 450° and 500°C. Their suggestion that the zones were a result of directional diffusion of magnesium atoms was supported with calculations from Harris and Jones2 which also tended to identify the process as Nabarro-Herring (N-H) creep3,4—a process that is characterized by Newtonian viscosity, with stress (o) directly proportional to strain rate (C), and one that proceeds by lattice diffusion. Material transport by diffusion along grain boundaries is an alternative basis for Newtonian viscosity, as demonstrated by Coble,5 and is favored over N-H creep for fine grain size and lower temperature.6 In either case, the strain rate sensitivity of flow stress, defined as m = d log o/d log E (which commonly appears in the empirical a = KEW), is unity. The experiments to be described here gave metallo-graphic indications of diffusional creep which were no less clear than those just cited, but the associated m (as measured by the method of Ref. 7) was much more like that of a Bingham material. For true Bingham behavior, (a — ao) E, where oo is an initial yield stress. Therefore, even if flow after yielding should occur by diffusional transport, m must increase from 0 as < is raised to reach unity only in the limit as One result is that the resistance to tensile necking conferred by Newtonian viscosity is lost, which would become increasingly apparent through the formation of more sharply defined necks as 6 is lowered. That trend appeared in these experiments. Most of the work was done on an extremely finegrained alloy of magnesium with -6 wt pct Zn and ½ wt pct Zr (Mg ZK60); the initial mean-intercept grain diameter, L, was 0.55 µ. Shown in Fig. l(a) is a germanium-shadowed carbon replica of the surface of a specimen that was coated with silicone oil,* heated to 270°C under a helium atmosphere, and then stretched locally -200 pct at an initial E = 3.3 x 10-5 sec-1. Under

Jan 1, 1969

By W. C. Coons, E. H. Rennhack, R. A. Perkins

THE constitution of Ti-N alloys containing up to 17.5 wt pct N has been investigated by Palty, Margolin, and Nielsen.1 Their results, which confirmed earlier work

Jan 1, 1969

By H. A. McKinstry, F. F. Lange

A vector analysis of orientating single crystals using the Laue back-reflection X-ray technique is given. Briefly, the analysis involves using a few data taken from a Laue photography and defining the crystal co- ordinate axes in a reference coordinate system. After a few matrix multiplications, the proper goniometer angles can then be determined to orient the crystal coincident with the reference frame. This analysis is easily programed for a digital computer to provide a fast, precise, and efficient method of orienting many crystals which are identical. The general procedure is as follows. The crystal is mounted on a goniometer. Laue photographs are taken until an array of diffraction spots is observed that includes a Laue spot that represents a rotational axis of symmetry. The rotation angles of goniometer are recorded. These angles are defined as positive for a counterclockwise rotation. When the axis of symmetry is located on the Laue photograph, the crystal coordinate axes can be defined in the reference coordinate system* as follows. Two Laue spots are chosen, one of which corresponds to the rotational axis of symmetry and the other to a set of planes whose zone axis is a known crystallographic direction and normal to the rotation axis of symmetry. The Laue spots are used to determine these two crystal directions in the reference coordinate frame. This is done by placing the Laue photograph on a sheet of polar coordinate graph paper and determining the polar coordinates (r, o) of these two diffraction spots in the reference coordinate frame. Their third coordinate is the distance between the crystal and the film (-D). The coordinates Xni of the two crystal directions Nn, (n = 1, 2) in the reference frame are then calculated by the following equations: Xn1 = -D X2n = Ancos on X3n = A, sin on where -tan- 1 rn/D An =Dtan(tan-1rp/D/2) By taking the proper cross products of these two directions (normalized to unit vectors), the crystal coordinate axes 3 (i = 1, 2, 3) can be determined in the reference frame. This is illustrated in Fig. 1. The next step is to determine the relation between

Jan 1, 1969

By A. Tanaka, K. G. Carroll

The existence of local room-temperature plastic flow in germanium, which has been a subject of controversy for nearly two decades, has recently received renewed attention, albeit no more agreement than hitherto. Phenomenologically one major facet of the problem has been reduced to the question whether or not indentation can be effected in germanium without the introduction of cracks. That plastic flow can be induced at room temperature by fracture appears to have been rather convincingly demonstrated recently by Suzuki and Kamada and by Noble and Henisch.1 The literature contains both direct and incidental references to Vickers and Knoop indentations showing no cracks, within resolution of optical microscopy. Recently, however, following a controversy on the subject,2,3 johnson4 made a study of indentations produced by spherical indenters and concluded that these are accompanied by cracking. This study in-

Jan 1, 1969

By R. D. Nelson

The purpose of this technical note is to briefly present some data on a phenomenon—recrystallization with concurrent deformation—that has been found to occur in a plutonium. This phenomenon is unusual because a plutonium is considered brittle, not easily deformed, and not easily recrystallized; the a phase is simple monoclinic having 8 atoms per unit cell and it is stable below about 115°C. The properties of the recrystallized metal were different from the as-cast metal. Even though a plutonium is difficult to deform, Ianniello successfully rolled it&apos; and he also observed some recrystallization at 120°C.2 Pavlick and Hanson3 detected some recovery at 109°C but they observed no recrystallization. Gardner4 and Bronisz5 studied the compression properties up to 100°C but they did not report having seen recrystallization. In the present deformation studies of electrorefined plutonium pronounced recrystallization took place concurrently with plastic deformation in compression between 24" and 115°C. The metal contained less than 300 ppm total impurities with the major impurities being 100 ppm Am, 30 ppm C, 40 ppm W, and 25 ppm U; all other impurities totaled less than 100 ppm. The compression specimens were machined to dimensions of 1.2 cm long and 0.8 cm diam from as-cast rods having a density of 19.65 g per cu cm. They were heated to the test temperature in a high-temperature silicone fluid that was evacuated to 10-4 Torr. With this procedure the specimens oxidized a negligible amount, and the temperature was maintained within ±0.2°C for times up to 3 weeks. Deformation and recrystallization

Jan 1, 1969

By A. E. Dwight, A. F. Berndt

ThE published U-Ru equilibrium diagram indicates the existence of six intermetallic compounds in this system.&apos; The structure of only two of the compounds, u2Ru2,3 and URU3,4 have been identified. This communication reports on the crystal structure and density of Uau3, which is formed by a peritectoid transformation at 1025° ± 5°C: U3Ru4 + U3Ru5 = U2Ru3. An alloy with the stoichiometric formula U2Ru3 was prepared by arc melting electrolytic uranium and ruthenium of 99.9 pct purity on a water-cooled copper hearth under an argon atmosphere. After homo-genization at 1000°C for 3 days, a metallographic examination revealed that the peritectoid transformation was complete and less than 5 pct of a second phase was present. A powdered sample, obtained by crushing the brittle compound, was annealed for 1 hr at 1000°C and air-cooled. Debye-Scherrer patterns were obtained with filtered CrKa, FeKa, CoKa, or CuKa radiation. The X-ray patterns of U2Ru3 weFe indexed as an fcc structure with a. = 12.895 0.00lA. The unit-cell constant and its standard deviation were calculated by a computer program described by Mueller, Heaton, and Miller.5 The density, measured by an immersion method, was 14.45 g cm-3. A calculated density of 14.48 g cm-3 was obtained on the assumption that twenty-four formula units (120 atoms) comprise a unit cell. The space group is either oh7 Fd3m, or the less symmetric, T4h, Fd3, since reflections indexed as hk0 with h + k + 4n are absent. All values of h2 + k2 + 12 permitted by both space groups are listed in Table I together with dc, do, and I. values. The calculated d spacings were obtained by the computer program of Mueller, Meyer, and simonsen.6 The observed d spacings above 0.77A were obtained from X-ray" patterns prepared with CuKa radiation, above 0.90A with CoKa radiaaion, above 0.98A with FeKa radiation, and above 1.16A with CrKa radiation. An attempt was made to identify the crystal structure of U2Ru3 by comparison with published data on other A2B3 compounds. A recent compilation7 of intermetallic compounds lists thirty-two structure types with the A2B3 stoichiometry. Only two of the structure types are fcc and they are Sb2O3(r), senarmontite, with 16 Sb2O3 per unit cell, and In2Te3 for which several structures have been proposed.8 However, the two cases cited do not have twenty-four formula units in the unit cell. We therefore, cannot identify UPRU3 with any of the other known A2B3 compounds. Ternary alloys were made in which 5 at. pct Os, Rh, or A1 were substituted for 5 pct of the Ru in U2Ru3. The osmium substitution increased the unit cell constant to 12.899 * .001A, which is to be expected since the atomic volume of osmium is slightly larger than

Jan 1, 1969

By J. S. Blakemore, E. O. Hall

SERRATED yielding, commonly called the Portevin-Le Chatelier effect, is known to occur in a wide range of alloys where the moving dislocations are considered to be locked by the diffusion of solute atoms to them. From the work of Cottrell,1 an approximate relationship between strain rate, E, dislocation density, p , and solute diffusion coefficient, D, giving rise to serrated yielding is: e =Dp

Jan 1, 1969

By A. Mitchell, T. Bagshaw

A recent paper by Thomas1 has presented new data on the solubility of hydrogen in solid silver at 1 atm pressure in the temperature range 600° to 963°C. However, no data is reported in the literature on hydrogen solubility in liquid silver. The Sieverts technique which has been described previously2,3 was used in the present work. Charges of approximately 160 g were melted in Morgan "purox" recrystallized alumina crucibles and purified helium was used for the determination of the "hot volume" during each experiment. A chemical analysis of the silver indicates that the impurity content (Cu + Al) is less than 0.02 wt pct. Hydrogen solubility in the temperature range 963° to 1200°C was investigated. The results of three experiments are shown in Table I. Fig. 1 shows an Arrhenius plot of the present work together with the solid-state data of Thomas, Steacie, and johnson,4 Eichenauer et al.,5 and Siegelin et al.6 The following expression has been derived from the Arrhenius plot of the present data: log (solubility of hydrogen, cm3 per 100 g) = 2.154-3512.0/ToK The heat of solution derived from Fig. 1 is 31,150 cal per g mole H2 compared with the value of 33,020 cal per g mole H2 obtained by Thomas and 12,000 cal per g mole H2 obtained from the data of Steacie. It was observed that hydrogen evolution took place when the silver melts were solidified under 1 atm of hydrogen, which would not be expected from an extrapolation of the results of Steacie. Schenck and Lange7 have observed that, for several transition metals at their melting points, the ratio of the hydrogen solubility in the liquid to that in the solid lies in the range 2.1 to 3.1. The present results and those of Thomas are in accord in this respect having a ratio of 2.8. &apos;C. L. Thomas: Trans. TMS-AIME, 1967 vol. 239, pp. 485-96. 2T. Bagshaw and A. Mitchell: I. Iron Steel Inst., 1966, vol. 204, p. 87. &apos;M. Weinstein and J. F. Elliott: Trans. TWS-AIME, 1963, vol. 227, p. 382. &apos;E. W. R. Steacie and F. M. G. Johnson: Proc. Roy. Soc. (London), Ser. A, 1928, vol. 117, pp. 662-79. &apos;W. Eichenauer et al.: Z. Metallk., 1958, vol. 49, pp. 220-25. 6W. Siegelin et al.: Z. Elektrochem., 1957, vol. 61, pp. 359-66. &apos;H. Schenck and K. W. Lange: Arch Eisenhuettenw., 1966, vol. 37, no. 9, pp. 739-48.

Jan 1, 1969

By W. A. Oates, J. S. Blakemore, E. O. Hall

AS part of an investigation into the effect of hydrogen on the serrated yielding of Ni-Cu alloys,&apos; it was necessary to determine the solubility of hydrogen in the alloys of interest. With the exception of the work by Fukusima and Mitui2 who investigated the solubility of hydrogen in solid Ni-Cu alloys at 20 wt pct intervals at 1050°, 700°, and 350°C, the information in the literature is limited.3-10 Alloys were prepared from deoxidized Analar Copper and Mond Nickel pellets.&apos; Wire samples were hydrogenated at 7.8 atm in an autoclave consisting of 5 ft of thick-walled Inconel 600 tube with a resistance furnace around the middle portion. The top end, at room temperature, was fitted with a safety valve, a calibrated pressure gage, and a sample inlet, while the bottom end, again at room temperature, was filled with water. After reaching equilibrium samples were quenched by dropping from the high-temperature region of the autoclave into water. They were then quickly transferred to liquid nitrogen where they were stored until analyzed for hydrogen using an Exhalograph.11 The results, which are shown in Fig. 1, represent the mean of two separate determinations on each sample. Because of the lower level of hydrogen at the high copper end of the series, the results here are of poor precision using this method. Fortunately, the results of Himmler9 using the Sieverts technique are available for these copper-rich alloys (>80 at. pct Cu)

Jan 1, 1969

By M. Oka, C. M. Wayman

It has been known for some time1 that (110)b twinning is possible in bct martensite.* Any plane of the form (110) not parallel to the fourfold axis of tetra-

Jan 1, 1969

By A. Coskun, J. F. Elliott

The activity of aluminum in liquid Al-Fe alloys .has been measured by an improved version of the transportation method in which the metallic vapor has been collected by its solution in a metallic condenser. The results can be represented by the equation: log yAl = -3.0(1 - xAl2) (0.6 < XAl < 1.0) This equation applies at 1315°C. MORRIS and zellarsl adapted the transportation method for measuring the vapor pressure of a com- ponent of an alloy at high temperature. We have modified their technique further2 for use with metals that are strong oxide formers. In the present case the method has been applied to the Al- Fe system to obtain the activity of aluminum in the liquid region at 1315°C. Dried ultrahigh-purity hydrogen (Matheson) is the carrier gas. The operations, Fig. 1, of deoxidizing the gas, equilibrating the gas with the sample at 1315";, and then collecting the aluminum vapor are all accomplished within a single, continuous alumina tube to avoid contamination of the system by leaks. De-oxidation to a very low level of PO2 (<10-25 atm) is Obtained by passing the hydrogen through a tightly packed bed of aluminum powder. The temperature of this bed increases to approximately 550°C in the direction of the gas flow. The boat containing three pellets of the alloy is supported on the end of a

Jan 1, 1969

By R. W. Jordan, J. Winter, A. J. Goldman

Kirkendall diffusion of copper and nickel atoms across the bond interfaces, as well as oxygen diffusion in the core to the interfaces, are the mechanisms which control the variation in bond strength with annealing time at 1600°to 1800°F in the cupro-nickel clad copper Mint composite. The unequal mass transfer resulting from the high diffusion rate of copper in cupro-nickel compared with that of nickel in copper caused void formation in the core. Small voids also formed in the cladding after short annealing times. These may have been nucleated by nickel oxide particles which are formed by the dissociation of the cuprous oxide in the core and the movement of oxygen to the cupro-nickel interfaces. The bond strength drops to very low values for annealing time up to 3 hr when the void density is greatest. The increase in bond strength after 16 to 72 hr at 1600°F is a result of the decrease in the void density in the cupro-nickel cladding and the growth of grains across the interface. The void density decrease is attributable to grain boundary diffusion of vacancies to the surface. The abnormally large grains in the copper preclude a similar process from taking place in the core. THE solution to many engineering materials problems that cannot be satisfied by using a single metal or alloy is often attained by combining two or more metals in such a way that each component performs a different function, while the composite meets the overall requirements. The Coinage Act of 1965 authorized a changeover from the traditional 90 Ag-10 Cu dimes and quarters to a bimetallic laminate of 75 Cu-25 Ni clad on a copper core. Economic considerations as well as physical, chemical, and mechanical properties provided a basis for the selection of this composite as a substitute for the silver-bearing alloy. An extensive survey of alloys suitable for use as coinage was prepared by Battelle Memorial Institute for the U.S. Mint.1 It was found that the cupro-nickel/cop-per/cupro-nickel composite satisfied the required color, density, mechanical properties, corrosion resistance, electrical properties, and magnetic properties to make it completely acceptable to the general public and the vending machine industry. This investigation is part of a program to determine the feasibility of reclaiming composite scrap by thermally degrading the bond strength of the cupro-nickel clad copper laminate. The composite exhibits bond degradation and subsequent bond improvement during annealing in the temperature range 1600" to 1800°F. A study of the operative diffusion processes and the resultant structural changes was made in order to explain the observed variations in bond strength with annealing time. EXPERIMENTAL PROCEDURES AND RESULTS Bond Degradation. A measurement of the forces required to peel the cupro-nickel cladding from the

Jan 1, 1969

By T. Leffers, A. Grum-Jensen

The development of texture in copper and brass (15 pct Zn by weight) rolled at room temperature and in copper rolled at -196°C has been followed by determination of pole figures for various degrees of reduction. The concurrent development in microstructure has been investigated by transmission electron microscopy. For low deformations, the texture in brass, and in copper rolled at -196°C, is the same as the texture in copper rolled at room temperature. The difference in texture does not show until 50 pct reduction. At the same reduction at which the difference in texture appears, mechanical twinning starts in brass and low-temperature rolled copper. Nevertheless, Wassermann&apos;s twinning theory is found to be incompatible with the present resulls. All fcc metals and alloys develop, by heavy rolling, one or the other of two types of texture, classified for convenience as copper type and brass type, or possibly a &apos;(mixed" texture representing an intermediate stage between the two types. The pure fcc metals, except silver, develop copper-type texture by rolling at room temperature. Silver and many alloys, including brass with more than 10 pct Zn, develop brass-type texture.&apos; By rolling at low temperatures a transition in texture from copper type to brass type has been observed for copper of commercial purity.2&apos;3 It is generally accepted that there is a correlation between the type of texture developed and the stacking fault energy. Metals and alloys having fcc structure develop brass-type texture when rolled at room temperature if the stacking fault energy is low, whereas those with higher stacking fault energies have copper-type texture.2 Thus, the difference in stacking fault energy must cause a difference in deformation mechanism responsible for the difference in texture. Of the numerous theories advanced concerning the nature of this difference in deformation mechanism, four seem to be of current interest. Smallman and Greeen,2 Dillamore and Roberts,4 and Dillamore5 refer to the fact that cross slip more easily takes place in a material with a higher stacking fault energy and suggest that the copper-type texture is developed by deformation with extensive cross slip whereas the brass-type texture is developed by deformation without cross slip. Haessner6 has advanced the theory that the copper-tye texture is developed by a combination of normal {111} slip and slip on other planes, mainly 1100). Thus his theory, like the theory above, proposes an additional deformation mode for the formation of the copper-type texture. Contrary to this, wassermann7 and Ahlborn et al.8 believe that the copper-type texture is obtained by normal slip. In their opinion mechanical twins will change a copper texture into a brass texture. For this reason it is suggested that the brass-type texture is developed when, in addition to normal {111}(110) slip, mechanical twinning is present. None of these theories are, however, supported by direct experimental evidence. In a recent experiment Hu et al.9 have followed the development of rolling texture in copper and brass. The texture of copper and brass was found to be es-

Jan 1, 1969

By R. G. Vardiman, M. R. Achter

Observations of dislocation structure in niobium are presented using two techniques. Triangular pits developed by electroetching are confined to orientations in the stereographic triangle between the (111) pole and planes of the (1ll) zone and require the presence of carbon. Some unusual electroetching phenomena at other orientations are noted. A chemical etch of dislocations decorated by the addition of carbon to 50 ppm reveals the complete dislocation line structure in a surface layer up to 30 p deep, with a resolution of less than 1 p. This effect is independent of surface orientation. The structure of subboundary nets may be resolved for misorientations up to about 1&apos;. Dislocation structures found in strain anneal grown crystals, such as helices, prismatic loops, and high-density areas, are observed. The measurement of dislocation density is discussed and values obtained in different ways are compared. IN the course of some work on the response of refractory metals to thermal-mechanical treatments, it was desired to examine the defect structure of relatively low dislocation density crystals of niobium in bulk form. Surface and bulk methods for the observation of dislocations have been reviewed by ~melinckx,&apos; and include etch pitting, decoration, and various X-ray techniques. The dislocation line structure has been developed by decoration in a few metals, although observations were limited to certain orientations, or by the coarseness and nonselectivity of the precipitate. The most commonly used technique is etch pitting. In niobium, etch pits have been developed chemically&apos;0," in material of high impurity content and electrolyti-cally&apos;&apos; in relatively pure material. In this paper, etch pits developed electrolytically, and the dislocation line structure of a surface layer developed by decoration and chemical etching, are examined, and observations are presented from both techniques. EXPERIMENTAL METHODS Our starting material was electron-beam-melted niobium, swaged to 4 or -in.-diam rod. Chemical analysis is given in Table I. Single crystals were grown by a strain anneal technique using 1 to 2.5 pct of strain and growth temperatures of 1700" to 2300"~.&apos;~ Some crystals grown by zone melting were also examined. The desired surface orientation was exposed either by spark machining or by sectioning with a cut-off wheel and prepared for etching by electro-polishing.

Jan 1, 1969

By J. J. Frawley, W. J. Childs

The dynamic nucleation of supercooled bismuth and Bi-Sn alloys has been studied over a frequency range of 15 to 20,000 cps. For low-frequency vibration, a minimum vibrational energy was required for enhancement of nucleation. Above this critical energy, the dynamic supercooling was less than static supercooling showing that vibration promoted nucleation. The amount of dynamic supercooling continued to decrease with increasing vibrational energy until a minimum or threshold value was reached. This minimum value of supercooling for nucleation remained constant joy all further increases in vibrational energy. For higher frequencies, similar results were observed. This behavior has been related to the necessity of cavitation for dynamic nucleation. When a liquid is cooled to a temperature below its equilibrium melting point, the solid phase is more thermodynamically stable. However, for solidification to occur, a two-step process, nucleation and subsequent growth of the solid phase, must occur. When a liquid is supercooled, that is cooled below the equilibrium melting point, the controlling process for solidification to begin is the rate of nucleation. Once nucleation has occurred, the solidification process is controlled by the rate of growth. Nucleation can be induced by two factors: either by a catalyst or by the use of mechanical shock. Numerous investigators1-4 have studied the effect of nucleation catalysis but much less systematic study has been made of nucleation by mechanical shock waves. The influence of vibrations on grain size in castings and ingots has been studied by many authors but no clear understanding of the mechanism or accurate prediction of the effect has been presented.5 It would be intuitively expected that the further the departure from equilibrium (i.e., the greater the supercooling), the easier it would be to induce nucleation. This has been quantitatively demonstrated both by walker6 and later by Stuhr,7 that the greater the degree of supercooling the easier it is to nucleate by a shock wave. Stuhr also attempted to obtain the mechanical energy required for nucleation of bismuth as a function of supercooling. He vibrated a crucible containing supercooled metal at low frequencies and various amplitudes and noted the corresponding dynamic supercooling obtained. The amount of supercooling was inversely proportional to the mechanical energy applied. Limitation of his experiment was the problem of the confinement of the liquid in the crucible without splashing and minimizing other unwanted modes of vibration. Tiller et al.8,9 did similar work on tin and Sn-Pb alloys using an electromagnetic stirring device. Their conclusions were that the magnitude of the magnetic field strength did not affect the amount of undercooling at which nucleation was initiated. While conclusive experimental results have been lacking to explain this effect of mechanical vibration on inducing nucleation, a number of theories have been proposed. Two of these theories are discussed below. 1) The Change in Melting:- Point Locally Due to the Change in Pressure (Clapeyron Equation). According to Vonnegut10 the most plausible explanation for the nucleation of a supercooled melt by cavitation is the effect of changing the melting point by a change in pressure. For materials where the volume decreases on solidification, an increase in pressure raises the melting point; for materials which expand on solidification, the melting point is raised for a decrease in pressure, i.e., rarefaction. Using the Clapeyron equation, the melting point of a metal can be calculated as a function of pressure. If it is assumed that the equation can also be used to calculate the temperature of nucleation of a supercooled melt as a function of pressure (i.e., the temperature of heterogeneous nucleation will increase with pressure at the same rate as the melting point), the amount of supercooling required for nucleation will be constant at all pressures as shown in Fig. 1. It is obvious that an isothermal change which results in an increase in melting point results in an equal increase in supercooling. This increase in supercooling may now be sufficient for nucleation. A pressure of 80,000 atm was calculated, using the Clapeyron equation, as the pressure required to increase the temperature of nucleation of nickel by 200°C. According to Lord Rayleigh,11 this very large pressure could be generated for a very brief period of time by the collapse of a cavity. This pressure wave is radiated in all directions from the collapsed cavity. If the temperature of the melt is slightly below its equilibrium melting temperature at atmospheric pressure, stable growth can follow; that is, once nucleation occurs, growth becomes the main driving force of the solidification process. This proposal has been extended to water which expands on freezing by assuming that nucleation occurs during rarefaction following the pressure pulse. This negative pressure pulse should follow immediately after the positive pressure pulse with its magnitude approaching the critical tensile strength of the liquid. The negative pressure developed during this period would raise the melting point of water and thus promote nucleation. Hunt and jackson12 have suggested this for water. Similarly, it could be postulated that bismuth which also expands on freezing could be nucleated during the negative pressure pulse. 2) Nucleation by a High-pressure Phase. An extension of the Clapeyron equation to systems where density decreased on freezing at atmosphere pressure has been proposed by Hickling.13 The phase diagram for water initially shows the well-known decrease in

Jan 1, 1969

By R. E. Reed, C. J. McHargue

Poly crystalline aluminum specimens having random and diffuse (001) initial orientations were reduced 90 pct in area at room temperature by drawing, extruding, and swaging. Although each procedure produced the duplex (001)- (111) texture, there were marked dqferences in the relative amounts of each component. This also produced variations in the tensile properties of the aluminum rods. It is generally agreed that the fiber texture found in aluminum rods consists of a strong (111) and a weak (001) component after reductions in area of 90 pct or more. An examination of data summarized in recent reviews&apos;-3 shows much spread in the values for the relative amounts of the two components reported by different investigators. That the initial orientation has a marked influence on the final texture even after reductions in area greater than 90 pct is well-documented.4-7 Another factor which may influence the relative amounts of the two components is the method of fabricating the wires or rods. Barrett and ~assalski&apos; state that the center of wires formed by rolling, swaging, and drawing have the same textures. The data cited in support of this conclusion came from qualitative X-ray techniques. In recent years there has been renewed interest in correlating the type of preferred orientation with such parameters as stacking fault energy and onset of mechanical twinning.&apos;&apos; Since these analyses have often used many sources of data, it is essential that the data be evaluated for the effect of fabrication variables. In this study we have produced aluminum rods by drawing, swaging, and extruding and have quantitatively determined their textures. All specimens had the same purity and fabrication temperature, and the amount of deformation and the starting textures were determined. We have compared our results with published studies on similar materials and fabricating parameters. We have also compared results from the same three fabricating procedures for single-crystal specimens in three instances. EXPERIMENTAL PROCEDURE The aluminum was 99.99+ pct with the only detected impurities being (by weight) 0.002 pct Cu, 0.001 pct Si, and 0.001 pct Mg. Cylinders a in. in diam by 1 in. long with a fine-grain random texture were made by the following method. Cubes 1+ in. on a side were machined from 2-in.-diam ingots. These cubes were slowly pressed about 30 pct in each of the cube directions. The material was recrystallized by annealing 1 hr at 350°C. Three deformation-anneal cycles produced the desired material. Polycrystalline specimens with a diffuse (001) texture were made by casting into a graphite tube 1 in. ID, li in. OD, by 8 in. long which had been preheated to 900°C. One end of the tube was placed on a water-

Jan 1, 1969