By G. B. Kasik, George Sachs, George Espey

IT has been reported frequently that the hardness and strength vary over the cross section of cold-worked, particularly cold-drawn, material. Brass rod and wire usually have been found to possess a maximum strength and hardness near the surface.1,2 According to Sachs,' the center fiber has about the same strength as a wire stretched by the same amount in a tensile-test machine, the strength increasing toward the surface (Fig. I). These differences are particularly large for wire given a small reduction on drawing through a die with a wide opening. However, with increasing reduction and hardness, a tendency to form a thin soft surface skin becomes apparent. On the contrary, copper wire has usually been found to possess a soft surface skin3-5 and it has been reported by Harris3 that during the cold-drawing of hot-rolled wire the surface layer becomes increasingly softer than the core, while the layer of maximum strength moves toward the core, it being found near the surface at first. The increase of strength and hardness from the core to the skin is readily explained by the observation that, in addition to the stretching, the layers of a rod or wire are sheared more the closer they are to the surface.1,6-8 However, the presence of a soft surface layer can be attributed only to an annealing effect. The source of such a softening might be the extremely high temperature that originates from the friction between

Jan 1, 1942

By Harrison Schmitt

During the past decade the writer has studied and mapped certain ore deposits and their structural associations in the states of Chihuahua, Durango, New Mexico and Arizona, and he believes that these deposits, with the exception of the manto-chimney, are representative of the principal types in the area of the states named. In this paper the deposits are described; then generalizations are drawn so far as seems appropriate. Hanover, New Mexico The Hanover, New Mexico, zinc deposits were briefly described by Lindgren and others,' Paige2 and recently in more detail by Schmitt. These, the kind ordinarily called contact metamorphic, border the southern end of an oval area of granodiorite intrusive ¾ mile wide and 2 miles long (Fig. I). The granodiorite has intruded, folded, and metamorphosed sedimentary and igneous rocks, which range in age from pre-Cambrian to Upper Cretaceous. About 90 per cent of the ore has replaced coarse, recrystallized, pure, fossiliferous, lower Mississippian, nonmagnesian limestone (Hanover limestone) 110 ft. thick;4 about 75 per cent of it occurs in the upper 50 ft. of this horizon just below an 18-ft. lower Pennsylvanian shale bed, which lies on a locally inconspicuous unconformity representing upper Mississippian time. The orebodies show five shapes or attitudes, each dependent on a special structural situation: 1. Most of the ore occurs as podlike, thick lenslike or other "three-dimensional" shoots extending from top to bottom of the Hanover limestone and lying adjacent to the outer contact of a silicate zone largely of andradite, which follows the intrusive contact (Figs. 1 and 2).

Jan 1, 1935

By Harrison Schmitt

During the past decade the writer has studied and mapped certain ore deposits and their structural associations in the states of Chihuahua, Durango, New Mexico and Arizona, and he believes that these deposits, with the exception of the manto-chimney, are representative of the principal types in the area of the states named. In this paper the deposits are described; then generalizations are drawn so far as seems appropriate. Hanover, New Mexico The Hanover, New Mexico, zinc deposits were briefly described by Lindgren and others,' Paige2 and recently in more detail by Schmitt. These, the kind ordinarily called contact metamorphic, border the southern end of an oval area of granodiorite intrusive ¾ mile wide and 2 miles long (Fig. I). The granodiorite has intruded, folded, and metamorphosed sedimentary and igneous rocks, which range in age from pre-Cambrian to Upper Cretaceous. About 90 per cent of the ore has replaced coarse, recrystallized, pure, fossiliferous, lower Mississippian, nonmagnesian limestone (Hanover limestone) 110 ft. thick;4 about 75 per cent of it occurs in the upper 50 ft. of this horizon just below an 18-ft. lower Pennsylvanian shale bed, which lies on a locally inconspicuous unconformity representing upper Mississippian time. The orebodies show five shapes or attitudes, each dependent on a special structural situation: 1. Most of the ore occurs as podlike, thick lenslike or other "three-dimensional" shoots extending from top to bottom of the Hanover limestone and lying adjacent to the outer contact of a silicate zone largely of andradite, which follows the intrusive contact (Figs. 1 and 2).

Jan 1, 1935

During the past decade the writer has studied and mapped certain ore deposits and their structural associations in the states of Chihuahua, Durango, New Mexico and Arizona, and he believes that these deposits, with the exception of the manto-chimney, are representative of the principal types in the area of the states named. In this paper the deposits are described; then generalizations are drawn so far as seems appropriate. Hanover, New Mexico The Hanover, New Mexico, zinc deposits were briefly described by Lindgren and others,' Paige2 and recently in more detail by Schmitt. These, the kind ordinarily called contact metamorphic, border the southern end of an oval area of granodiorite intrusive ¾ mile wide and 2 miles long (Fig. I). The granodiorite has intruded, folded, and metamorphosed sedimentary and igneous rocks, which range in age from pre-Cambrian to Upper Cretaceous. About 90 per cent of the ore has replaced coarse, recrystallized, pure, fossiliferous, lower Mississippian, nonmagnesian limestone (Hanover limestone) 110 ft. thick;4 about 75 per cent of it occurs in the upper 50 ft. of this horizon just below an 18-ft. lower Pennsylvanian shale bed, which lies on a locally inconspicuous unconformity representing upper Mississippian time. The orebodies show five shapes or attitudes, each dependent on a special structural situation: 1. Most of the ore occurs as podlike, thick lenslike or other "three-dimensional" shoots extending from top to bottom of the Hanover limestone and lying adjacent to the outer contact of a silicate zone largely of andradite, which follows the intrusive contact (Figs. 1 and 2).

Jan 1, 1935

During the past decade the writer has studied and mapped certain ore deposits and their structural associations in the states of Chihuahua, Durango, New Mexico and Arizona, and he believes that these deposits, with the exception of the manto-chimney, are representative of the principal types in the area of the states named. In this paper the deposits are described; then generalizations are drawn so far as seems appropriate. Hanover, New Mexico The Hanover, New Mexico, zinc deposits were briefly described by Lindgren and others,' Paige2 and recently in more detail by Schmitt. These, the kind ordinarily called contact metamorphic, border the southern end of an oval area of granodiorite intrusive ¾ mile wide and 2 miles long (Fig. I). The granodiorite has intruded, folded, and metamorphosed sedimentary and igneous rocks, which range in age from pre-Cambrian to Upper Cretaceous. About 90 per cent of the ore has replaced coarse, recrystallized, pure, fossiliferous, lower Mississippian, nonmagnesian limestone (Hanover limestone) 110 ft. thick;4 about 75 per cent of it occurs in the upper 50 ft. of this horizon just below an 18-ft. lower Pennsylvanian shale bed, which lies on a locally inconspicuous unconformity representing upper Mississippian time. The orebodies show five shapes or attitudes, each dependent on a special structural situation: 1. Most of the ore occurs as podlike, thick lenslike or other "three-dimensional" shoots extending from top to bottom of the Hanover limestone and lying adjacent to the outer contact of a silicate zone largely of andradite, which follows the intrusive contact (Figs. 1 and 2).

Jan 1, 1935

By Harrison Schmitt

During the past decade the writer has studied and mapped certain ore deposits and their structural associations in the states of Chihuahua, Durango, New Mexico and Arizona, and he believes that these deposits, with the exception of the manto-chimney, are representative of the principal types in the area of the states named. In this paper the deposits are described; then generalizations are drawn so far as seems appropriate. Hanover, New Mexico The Hanover, New Mexico, zinc deposits were briefly described by Lindgren and others,' Paige2 and recently in more detail by Schmitt. These, the kind ordinarily called contact metamorphic, border the southern end of an oval area of granodiorite intrusive ¾ mile wide and 2 miles long (Fig. I). The granodiorite has intruded, folded, and metamorphosed sedimentary and igneous rocks, which range in age from pre-Cambrian to Upper Cretaceous. About 90 per cent of the ore has replaced coarse, recrystallized, pure, fossiliferous, lower Mississippian, nonmagnesian limestone (Hanover limestone) 110 ft. thick;4 about 75 per cent of it occurs in the upper 50 ft. of this horizon just below an 18-ft. lower Pennsylvanian shale bed, which lies on a locally inconspicuous unconformity representing upper Mississippian time. The orebodies show five shapes or attitudes, each dependent on a special structural situation: 1. Most of the ore occurs as podlike, thick lenslike or other "three-dimensional" shoots extending from top to bottom of the Hanover limestone and lying adjacent to the outer contact of a silicate zone largely of andradite, which follows the intrusive contact (Figs. 1 and 2).

Jan 1, 1935

By H. E. McKinstry

Movement on a fracture of irregular shape can cause local widening of the fissure and thereby offer freer channelways for circulation of ore-depositing solutions. This influence: coupled with large areas of wall rock available for reacting with ore solutions in brecciated and shattered ground can account for locally active deposition of metals and the resulting ore shoots. Such irregularities in the fracture system may be caused by local variations in the strength of rocks and by pre-existing lines of weakness, especially if these stand at favorable angles to certain components of the fracturing stress. Therefore correct interpretation of the mechanics of fracturing should permit deductions as to structurally favorable places on unexplored portions of the vein system. Introduction It has long been recognized that movement on a curved or irregular fault surface is capable of separating the walls in certain portions of the fault, but until very recent years the importance of this mechanism as a factor in localizing ore shoots has escaped proper recognition. A short time ago W. H. Newhouse' presented a careful analytical study of displacements and their corresponding open spaces. For reasons that will be discussed later, it frequently happens that portions of the vein which are favorably oriented are not merely wider but also richer than the average. In many cases the widening with its accompanying richness coincides with very minor changes in the dip or strike of the vein, irregularities that commonly escape notice unless the vein is mapped in detail and a careful geometrical analysis made. While the relationship between the width of the vein and the changes in dip or strike has been recognized as a matter of observation, the irregularities have been accepted as more or less the result of accident. There has been very little effort except in isolated cases to find out the causes of these changes in dip or strike. Yet it is clear that if the causes can be recognized and expressed in terms of geologic structure the geologist will know where to look for repetitions of these favorable conditions either on extensions of the same vein or on adjoining veins. Any lack of understanding of the causes is due to the limitations of our ability to interpret our observations and not to the sheer capriciousness of

Jan 1, 1941

By H. E. McKinstry

Movement on a fracture of irregular shape can cause local widening of the fissure and thereby offer freer channelways for circulation of ore-depositing solutions. This influence: coupled with large areas of wall rock available for reacting with ore solutions in brecciated and shattered ground can account for locally active deposition of metals and the resulting ore shoots. Such irregularities in the fracture system may be caused by local variations in the strength of rocks and by pre-existing lines of weakness, especially if these stand at favorable angles to certain components of the fracturing stress. Therefore correct interpretation of the mechanics of fracturing should permit deductions as to structurally favorable places on unexplored portions of the vein system. Introduction It has long been recognized that movement on a curved or irregular fault surface is capable of separating the walls in certain portions of the fault, but until very recent years the importance of this mechanism as a factor in localizing ore shoots has escaped proper recognition. A short time ago W. H. Newhouse' presented a careful analytical study of displacements and their corresponding open spaces. For reasons that will be discussed later, it frequently happens that portions of the vein which are favorably oriented are not merely wider but also richer than the average. In many cases the widening with its accompanying richness coincides with very minor changes in the dip or strike of the vein, irregularities that commonly escape notice unless the vein is mapped in detail and a careful geometrical analysis made. While the relationship between the width of the vein and the changes in dip or strike has been recognized as a matter of observation, the irregularities have been accepted as more or less the result of accident. There has been very little effort except in isolated cases to find out the causes of these changes in dip or strike. Yet it is clear that if the causes can be recognized and expressed in terms of geologic structure the geologist will know where to look for repetitions of these favorable conditions either on extensions of the same vein or on adjoining veins. Any lack of understanding of the causes is due to the limitations of our ability to interpret our observations and not to the sheer capriciousness of

Jan 1, 1941

By Thomas L. Kesler

The Cartersville mining district, 35 miles northwest of Atlanta, Ga, has been of varying but continuous importance in the southern mineral industry during the past century. Noted chiefly for its production of brown iron ore, manganese oxide ores, barite, sienna, and magnesian limestone, the district and its environs have produced brick and tile clays, slate, gold, bauxite, and graphitic schist. Minor deposits of serpentine, sericite schist, copper ore, and red iron oxide have been prospected. The obvious deposits of brown iron ore, together with some associated specular hematite, were mined out years ago, although a little ore was left in the workings. Moderately steady production of sienna reached a peak about 1930, then declined rapidly. Manganese mining passed through a relatively active period from the World War to 1931, but has subsided to a small but rather constant output for the Birmingham market. However, the White Manganese Corporation has prepared for possible increased production by constructing a new washer capable of handling about 300 tons of ore per day. Principal activity in the district proper has centered for some years in the production of barite and magnesian limestone. General Geology Geologic relations of the ore deposits of this district are more or less similar to those of many Appalachian districts. The lowermost Cambrian formation, heretofore called Weisnerl in this region, supposedly partly or. wholly equivalent to the Erwin and Hesse quartzites as recognized to the northeast, is overlain conformably by the Shady† formation, also of Lower. Cambrian age. In the Cartersville district, the sedimentary rocks of these formations were folded with increasing intensity eastward, and were recrystallized.

Jan 1, 1941

By Thomas L. Kesler

The Cartersville mining district, 35 miles northwest of Atlanta, Ga, has been of varying but continuous importance in the southern mineral industry during the past century. Noted chiefly for its production of brown iron ore, manganese oxide ores, barite, sienna, and magnesian limestone, the district and its environs have produced brick and tile clays, slate, gold, bauxite, and graphitic schist. Minor deposits of serpentine, sericite schist, copper ore, and red iron oxide have been prospected. The obvious deposits of brown iron ore, together with some associated specular hematite, were mined out years ago, although a little ore was left in the workings. Moderately steady production of sienna reached a peak about 1930, then declined rapidly. Manganese mining passed through a relatively active period from the World War to 1931, but has subsided to a small but rather constant output for the Birmingham market. However, the White Manganese Corporation has prepared for possible increased production by constructing a new washer capable of handling about 300 tons of ore per day. Principal activity in the district proper has centered for some years in the production of barite and magnesian limestone. General Geology Geologic relations of the ore deposits of this district are more or less similar to those of many Appalachian districts. The lowermost Cambrian formation, heretofore called Weisnerl in this region, supposedly partly or. wholly equivalent to the Erwin and Hesse quartzites as recognized to the northeast, is overlain conformably by the Shady† formation, also of Lower. Cambrian age. In the Cartersville district, the sedimentary rocks of these formations were folded with increasing intensity eastward, and were recrystallized.

Jan 1, 1941

By L. W. Eastwood

The structure of eutectics has been studied by a number of investigators, and the complexity of the structural relationship of the components has been agreed upon, especially that of the "eutectic colony," type III of Portevin's1 classification. This paper does not attempt to alter the present classifications of eutectics; rather, it discusses the relationship between the macrostructure and the microstructure of the copper-cuprous oxide eutectic, and describes in detail the mechanism of the formation and the structure of the eutectic. Further, throughout the entire discussion it attempts to point out certain misconceptions in regard to the interpretation of the observed structure of the copper-cuprous oxide eutectic, one of the so-called "eutectic colony" types, and to correlate as much as possible the work done by the writer with that done by other investigators. Of the three types of eutectics listed by Portevin,2 the eutectic colony type has presented the greatest difficulty in interpretation. Although the copper-cuprous oxide eutectic is typical of the eutectic colony type in appearance, it may not be truly representative because the copper forms about 96 per cent of the eutectic and the cuprous oxide about 4 per cent. The interpretation of the origin and structure of the "eutectic colony" given here is strictly limited, therefore, to the copper-cuprous oxide eutectic. Macrostructure Fig. 1 shows the macrostructure of the eutectic at 3 diameters, the melt having been chill-cast into an iron mold, the resulting specimen sawed into two parts and the section polished and etched with the usual mixture of hydrogen peroxide and ammonium hydroxide. This specimen contains 0.48 per cent oxygen and is only slightly hypereutectic. If such a melt is allowed to cool slowly, large macrograins will form without the columnar structure of Fig. 1 and the well-known phenomenon of liquation will occur, forming copper oxide dendrites at the top and copper

Jan 1, 1934

By J. W. Spretnak, G. Sachs

The: iron-rich iron-nickel alloys have attracted considerable academic interest in recent years. The carbon-free alloys are of minor practical importance, but they are the base of many alloys with various outstanding properties. The iron-nickel alloys, therefore, have been investigated extensively regarding both their structures and their properties. The researches on these alloys up to 1938 have been collected and critically reviewed by J. S. Marsh,l and will be discussed in some detail in the sections of this paper dealing with specific subjects. These numerous investigations have not succeeded in establishing the equilibrium conditions in this system. Alloys containing more than a certain amount of nickel (8 to 10 per cent Ni) undergo the allotropic transformation extremely sluggishly, both on heating and cooling, showing a large hysteresis," which is not dependent upon the rate of cooling and persists even with very slow rates of cooling.3 Honda4 and Merica4 have therefore resigned themselves to proposing a diagram (Fig. I) for practical use, illustrating the structural relations under commercial conditions instead of attempting to establish the true equilibrium diagram. Marsh is less pessimistic and suggests an equilibrium diagram (Fig. 2) which conforms approximately to the facts known about this system. Recent X-ray investigations by Owen-Sully5 and Bradley-Gold-schmidt6 on powdered alloys indicate that the previous work on the iron-nickel system yielded very incomplete results. These investigators agree (Figs. 3 and ,+) that alloys in the powdered form containing more than 8 per cent and up to about 35 per cent Ni decompose into a stable heterogeneous mix-

Jan 1, 1941

By G. Sachs, J. W. Spretnak

The: iron-rich iron-nickel alloys have attracted considerable academic interest in recent years. The carbon-free alloys are of minor practical importance, but they are the base of many alloys with various outstanding properties. The iron-nickel alloys, therefore, have been investigated extensively regarding both their structures and their properties. The researches on these alloys up to 1938 have been collected and critically reviewed by J. S. Marsh,l and will be discussed in some detail in the sections of this paper dealing with specific subjects. These numerous investigations have not succeeded in establishing the equilibrium conditions in this system. Alloys containing more than a certain amount of nickel (8 to 10 per cent Ni) undergo the allotropic transformation extremely sluggishly, both on heating and cooling, showing a large hysteresis," which is not dependent upon the rate of cooling and persists even with very slow rates of cooling.3 Honda4 and Merica4 have therefore resigned themselves to proposing a diagram (Fig. I) for practical use, illustrating the structural relations under commercial conditions instead of attempting to establish the true equilibrium diagram. Marsh is less pessimistic and suggests an equilibrium diagram (Fig. 2) which conforms approximately to the facts known about this system. Recent X-ray investigations by Owen-Sully5 and Bradley-Gold-schmidt6 on powdered alloys indicate that the previous work on the iron-nickel system yielded very incomplete results. These investigators agree (Figs. 3 and ,+) that alloys in the powdered form containing more than 8 per cent and up to about 35 per cent Ni decompose into a stable heterogeneous mix-

Jan 1, 1941

By L. H. Levenson, Charles S. Barrett

Since 1925, when the preferred orientations in compressed aluminum were first determined1,2 the orientations have been described as a fiber texture in which a face diagonal, [110], of the face-centered cubic lattice is parallel to the compression axis. Subsequent experiments have seemed to confirm this texture,3-5 and a number of theories (recently summarized in references 6 and 7) have been proposed to explain it and to relate it to the behavior of single crystals during compression.3,8-11 The experiments reported in this paper prove that the orientations are not adequately described as quoted above—i.e., as a [110] fiber texture—although this is a first approximation to the actual texture. They also show that the texture cannot be thought of as a stable orientati011 that is reached and maintained after a sufficient amount of deformation. The actual texture, when studied in detail at successive stages of compression, indicates that a hitherto unsuspected range of orientations is present, both in the polycrystalline metal as a whole and in various individual grains in its interior, and that a state of dynamic equilibrium exists within this range. The reasons for the failure of previous theories to predict the actual texture become obvious when the heterogeneous nature of the flow is considered. In addition to the deformation texture, the manner of its development, and its theory, this paper presents data on the following related subjects: the identity of strain markings in aluminum; the orientation changes in aluminum single crystals during compression and a comparison of these with the conditions in individual grains of a polycrystalliile specimen; the origin of asterism ill deformed single crystals, which heretofore has been regarded as a distortion localized at the surfaces or slip planes; and the relation of plastic strain in individual grains ill all aggregate to the strain of the whole.

Jan 1, 1940

By Charles S. Barrett, L. H. Levenson

Since 1925, when the preferred orientations in compressed aluminum were first determined1,2 the orientations have been described as a fiber texture in which a face diagonal, [110], of the face-centered cubic lattice is parallel to the compression axis. Subsequent experiments have seemed to confirm this texture,3-5 and a number of theories (recently summarized in references 6 and 7) have been proposed to explain it and to relate it to the behavior of single crystals during compression.3,8-11 The experiments reported in this paper prove that the orientations are not adequately described as quoted above—i.e., as a [110] fiber texture—although this is a first approximation to the actual texture. They also show that the texture cannot be thought of as a stable orientati011 that is reached and maintained after a sufficient amount of deformation. The actual texture, when studied in detail at successive stages of compression, indicates that a hitherto unsuspected range of orientations is present, both in the polycrystalline metal as a whole and in various individual grains in its interior, and that a state of dynamic equilibrium exists within this range. The reasons for the failure of previous theories to predict the actual texture become obvious when the heterogeneous nature of the flow is considered. In addition to the deformation texture, the manner of its development, and its theory, this paper presents data on the following related subjects: the identity of strain markings in aluminum; the orientation changes in aluminum single crystals during compression and a comparison of these with the conditions in individual grains of a polycrystalliile specimen; the origin of asterism ill deformed single crystals, which heretofore has been regarded as a distortion localized at the surfaces or slip planes; and the relation of plastic strain in individual grains ill all aggregate to the strain of the whole.

Jan 1, 1940

By F. W. Steadman, Charles S. Barrett

Deformation bands of surprising regularity are found in large-grained poly-crystalline copper after cold-rolling (Fig. I). Individual bands frequently are large enough to permit a determination of their orientation by means of etch pits and an optical goniometer. Measurements have been made on 21 areas in seven different grains, and these, combined with X-ray studies of nine single crystals that had been cold-rolled after mounting in a polycrystal-line block, have contributed to a better understanding of the preferred orientations in rolled copper just as similar studies have for rolled iron1 and brass.2,3 Particular attention was given to determining orientations that are stable during rolling and to the manner of fragmentation and rotation of unstable grains. The possible role of twinning was also carefully investigated. The texture of polycrystalline copper after cold-rolling is well established by the pole figures that have been plotted by Schmid and Staffelbach,4 Iweronowa and Schdanow,6 and Brick and Williamson,8 all of which are in substantial agreement. There has been some divergence in the list of individual "ideal" orientations that have been used to describe the texture by these observers and others," although the orientation (110) [II2]—that is, (110) parallel to the rolling plane and [TIP] parallel to the rolling direction—is generally recognized as the most prominent orientation and (112) [III] one of the lesser orientations. Other orientations have been given by some observers as (236) [535], (100) [00I], and (110) [00I]. The texture of copper has also been described as (I35) [533].6,7 The sum of these orientations provides a reasonable approximation to the complete pole figure, but it does not follow that these specific orientations are necessarily of fundamental significance, for the choice of indices is arbitrary, within limits. Furthermore, a detailed investigation of the ideal orientations in cold-rolled iron discloses continuous ranges of equally favored positions rather than definite positions of high stability,' and similarly Brick's observations in a single crystal of a brass2 suggest that all orientations in the range between (110) [II3] and (110) [II7] are about equally stable. Materials and Methods The material used was vacuum-cast electrolytic copper kindly supplied by L. L. Wyman, of the General Electric Co.* Slicec 1/2 in. thick and 21/2 in. square, cut from the ingot, were rolled with 50 per cent reduction per pass to final thicknesses between 0.02 and 0.04 in., and etched to develop cube-face etch pits suitable for goniometric work.8 The etch was light on some strips and deep in others.

Jan 1, 1942

By Charles S. Barrett, F. W. Steadman

Deformation bands of surprising regularity are found in large-grained poly-crystalline copper after cold-rolling (Fig. I). Individual bands frequently are large enough to permit a determination of their orientation by means of etch pits and an optical goniometer. Measurements have been made on 21 areas in seven different grains, and these, combined with X-ray studies of nine single crystals that had been cold-rolled after mounting in a polycrystal-line block, have contributed to a better understanding of the preferred orientations in rolled copper just as similar studies have for rolled iron1 and brass.2,3 Particular attention was given to determining orientations that are stable during rolling and to the manner of fragmentation and rotation of unstable grains. The possible role of twinning was also carefully investigated. The texture of polycrystalline copper after cold-rolling is well established by the pole figures that have been plotted by Schmid and Staffelbach,4 Iweronowa and Schdanow,6 and Brick and Williamson,8 all of which are in substantial agreement. There has been some divergence in the list of individual "ideal" orientations that have been used to describe the texture by these observers and others," although the orientation (110) [II2]—that is, (110) parallel to the rolling plane and [TIP] parallel to the rolling direction—is generally recognized as the most prominent orientation and (112) [III] one of the lesser orientations. Other orientations have been given by some observers as (236) [535], (100) [00I], and (110) [00I]. The texture of copper has also been described as (I35) [533].6,7 The sum of these orientations provides a reasonable approximation to the complete pole figure, but it does not follow that these specific orientations are necessarily of fundamental significance, for the choice of indices is arbitrary, within limits. Furthermore, a detailed investigation of the ideal orientations in cold-rolled iron discloses continuous ranges of equally favored positions rather than definite positions of high stability,' and similarly Brick's observations in a single crystal of a brass2 suggest that all orientations in the range between (110) [II3] and (110) [II7] are about equally stable. Materials and Methods The material used was vacuum-cast electrolytic copper kindly supplied by L. L. Wyman, of the General Electric Co.* Slicec 1/2 in. thick and 21/2 in. square, cut from the ingot, were rolled with 50 per cent reduction per pass to final thicknesses between 0.02 and 0.04 in., and etched to develop cube-face etch pits suitable for goniometric work.8 The etch was light on some strips and deep in others.

Jan 1, 1942

By Charles S. Barrett

The experiments reported in this paper have been fruitful in disclosing the mechanism of the deformation of iron in compression. They have established the nature of "deformation bands," "etch bands," or "X-bands," that have been a recognized but little understood feature in the structure of cold-worked metals since the early days of metallography, and have shown the role of the bands in the development of preferred orientations by cold-working. The work has also shown the relation of the orientation of individual grains to the preferred orientation of the aggregate. Some of the methods previously used in the determination of the indices of slip planes and slip directions are shown to be untrustworthy in the presence of deformation bands. The conclusion is reached that many slip planes and slip directions must operate during each stage in the compression of a single crystal, and that theories failing to take account of this require revision. In conducting the experiments a method of compression has been used by which extreme reductions can easily be reached, even to the limit set by the metal's capacity to deform without fracture. The work is a portion of a research program on the plastic properties of iron and steel. It is being used as a foundation for studies of orientntions resulting from recrystallization and is being extended to other metals and other types of deformation. Previous Work The previous experiments are few and have given confusing results Onol compressed a polycrystalline alpha-iron specimen between two flan plates of a testing machine and found that severe deformation oriented the crystals into a duplex preferred orientation, one set of crystallites having a cube diagonal of the body-centered cubic lattice parallel to the compression axis, and another set having a cube axis parallel to the compression axis. We shall speak of this structure as a double fiber texture of the type [111] + [100]. Wever2 also made an X-ray determination of the texture

Jan 1, 1939

By Charles S. Barrett

The experiments reported in this paper have been fruitful in disclosing the mechanism of the deformation of iron in compression. They have established the nature of "deformation bands," "etch bands," or "X-bands," that have been a recognized but little understood feature in the structure of cold-worked metals since the early days of metallography, and have shown the role of the bands in the development of preferred orientations by cold-working. The work has also shown the relation of the orientation of individual grains to the preferred orientation of the aggregate. Some of the methods previously used in the determination of the indices of slip planes and slip directions are shown to be untrustworthy in the presence of deformation bands. The conclusion is reached that many slip planes and slip directions must operate during each stage in the compression of a single crystal, and that theories failing to take account of this require revision. In conducting the experiments a method of compression has been used by which extreme reductions can easily be reached, even to the limit set by the metal's capacity to deform without fracture. The work is a portion of a research program on the plastic properties of iron and steel. It is being used as a foundation for studies of orientntions resulting from recrystallization and is being extended to other metals and other types of deformation. Previous Work The previous experiments are few and have given confusing results Onol compressed a polycrystalline alpha-iron specimen between two flan plates of a testing machine and found that severe deformation oriented the crystals into a duplex preferred orientation, one set of crystallites having a cube diagonal of the body-centered cubic lattice parallel to the compression axis, and another set having a cube axis parallel to the compression axis. We shall speak of this structure as a double fiber texture of the type [111] + [100]. Wever2 also made an X-ray determination of the texture

Jan 1, 1939

By L. H. Levenson, Charles S. Barrett

Plastic flow in metal crystals and the changes in orientation resulting from it are generally understood to take place by the following fundamental mechanisms: (1) slip on crystallographic planes, (2) homogeneous crystal rotation resulting from the slip, (3) bending of the 1attice between the planes of slip, and, under certain circumstances, (4) twinning. This paper and a preceding one on iron subjected to uniaxial compression1 concern two additional processes that must now be added to this list: (5) the formation of deformation bands, and (6) the bending and rotation of these bands. The present investigation yields a new understanding and definiteness to the common terms so loosely used when speaking of cold-worked metals —('grain fragmentation," "elongated grains," and "deformation twins," "deformation bands," "etch bands," or "X-bands." Bands have been noted on the polished and etched surfaces of cold-worked metals by various investigators for more than 25 years, ‡ yet their nature and their significance have been so little understood that they are not treated in the most comprehensive modern texts on the deformation of crystals. The experiments in this series show that they are one of the fundamental processes in the deformation of metals, of importance in the development of preferred orientations, in work-hardening (since they have the effect of reducing the effective grain size and interfering with slip), and in the recrystallization process. The present experiments were performed on the same stock of material that was used in the earlier compression experiments1—hydrogen-purified mild steel in which the carbon content had been reduced to the limit detectable under the microscope and in which single crystals could be grown by a strain-anneal treatment.2

Jan 1, 1939