Search Documents

By R. F. Mehl, A. H. Geisler, S. Barrett

The studies of the mechanism of pre= cipitation and of the resulting property changes in aluminum-silver alloysl-3 have presented some new concepts of the aging reactioxl—concepts that may be fundamental in establishing a complete quantitative theory of age-hardening. With both aluminum-copper and aluminum-silver alloys, thin platelike aggregates form parallel to the Widmanstätten planes of precipitation.l,4 These platelets grow in lateral dimensions and in thickness with aging time until they arc thick enough to produce an X-ray diffraction line pattern. Their structure is that of a transition lattice which is coherent with the matrix, since the atomic spacings in the matrix and the precipitate are the same on each side of their common interface.2,4 The equilibrium precipitate forms later from and at the expense of the transition lattice. Since age-hardening occurs during the formation and growth of the transition lattice, the major contributor to the hardening no doubt is the stress condition in the matrix resulting from the matrix holding the precipitate in the coherent condition. The development of these stresses also appears to be responsible for an increase in the electrical resistance superimposed on the normal decrease resulting from a change in the concentration of the matrix during aging.3 The two consecutive reactions constituting the aging process are accompanied by characteristic microstructural alterations. The initial precipitation process results in the formation of a Widmanstatten figure, while the later transformation of the transition lattice to the equilibrium lattice is accompanied by a coalescence, in the case of aluminum-copper alloys,5 and by the appearance of light areas at the grain boundaries with aluminum-silver alloys showing a structural rearrangement of matrix and precipitate.3 This latter reaction is similar microscopically to the so-called "discontinuoils precipitation." Possibly discontinuous precipitation is a process that often if not always follows true precipitation of a coherent lattice and during which the transformation of the coherent transition lattice to the equilibrium lattice takes place accompanied by matrix recrystallization.3 Expermental Procedure The alloys were made using 99.97 per cent A1 or distilled magnesium, with

Jan 1, 1943

By Lawrence K. Jetter, Robert F. Mehl

Some advances have been made recently in the theory of the kinetics of precipitation from metallic solid solution despite the complexities of the problem, but there is surprisingly little quantitative information available on rates of precipitation with which to test present theory or upon which to build new theory. Attempts to measure rates of precipitation have been beset with difficulties which originate both in the anomalies that attend the changes in the properties selectcd for measurement, as, for example, in electrical conductivity or mechanical properties, and also in the complexities in the structural changes in some systems, as in the aluminum-copper system. If the functional relationship between the quantity of precipitate and the value of the selected property is uncertain, measurements of that property are obviously of uncertain utility in determining absolute rates of precipitation. If the precipitating system passes through one or more transition stages, the interpretation of measured rates lacks definiteness; in such cases, it is necessary to measure the rate of reaction in each separate stage, if the rate measurements are to have any significance from the kinetic point of view.* These difficulties cannot be wholly avoided, for at least in some measure they are characteristic of the process of precipitation from solid solution, but they can be minimized both by the selection of a simple system and by the use of a method of measurement relatively free from anomalous behavior. The present paper reports dilatome tric measurements on the rate of precipitation of silicon from the aluminum-rich solid solution in the aluminum-silicon system—a study that approaches the desiderata of simplicity. The aluminum-silicon system offers advantages from these points of view: there are no known anomalies in the property changes accompanying precipitation; there are no known transition stages; the precipitate is an element, not a compound, and both matrix and precipitate are cubic, and while the structures are not identical (the solid solution is face-centered cubic and the precipitate is diamond cubic), the system at least approaches the ideal case of a crystal precipitating from a matrix of the same crystal type—the ideal case which Becker6 assumed in treating the precipitation process theoretically. The dilatometric method, while not free from disturbing effects, as the subsequent dis-

Jan 1, 1943

By Lawrence K. Jetter, Robert F. Mehl

Some advances have been made recently in the theory of the kinetics of precipitation from metallic solid solution despite the complexities of the problem, but there is surprisingly little quantitative information available on rates of precipitation with which to test present theory or upon which to build new theory. Attempts to measure rates of precipitation have been beset with difficulties which originate both in the anomalies that attend the changes in the properties selectcd for measurement, as, for example, in electrical conductivity or mechanical properties, and also in the complexities in the structural changes in some systems, as in the aluminum-copper system. If the functional relationship between the quantity of precipitate and the value of the selected property is uncertain, measurements of that property are obviously of uncertain utility in determining absolute rates of precipitation. If the precipitating system passes through one or more transition stages, the interpretation of measured rates lacks definiteness; in such cases, it is necessary to measure the rate of reaction in each separate stage, if the rate measurements are to have any significance from the kinetic point of view.* These difficulties cannot be wholly avoided, for at least in some measure they are characteristic of the process of precipitation from solid solution, but they can be minimized both by the selection of a simple system and by the use of a method of measurement relatively free from anomalous behavior. The present paper reports dilatome tric measurements on the rate of precipitation of silicon from the aluminum-rich solid solution in the aluminum-silicon system—a study that approaches the desiderata of simplicity. The aluminum-silicon system offers advantages from these points of view: there are no known anomalies in the property changes accompanying precipitation; there are no known transition stages; the precipitate is an element, not a compound, and both matrix and precipitate are cubic, and while the structures are not identical (the solid solution is face-centered cubic and the precipitate is diamond cubic), the system at least approaches the ideal case of a crystal precipitating from a matrix of the same crystal type—the ideal case which Becker6 assumed in treating the precipitation process theoretically. The dilatometric method, while not free from disturbing effects, as the subsequent dis-

Jan 1, 1943

By G. D. Cremer, J. J. Cordiano

Aluminum powder is a well-known article of commerce and in various forms has been marketed widely for use in paint, for pyrotechnic purposes and for exothermic mixtures. For a number of reasons, however, aluminum powder has not been employed extensively in powder metallurgy, although a great many proposals along this line have been offered. Aluminum and alumiuum-alloy powders oxidize readily upon exposure to air and the thin film of oxide (or hydroxide) thus formed is highly refractory, in that ordinary gaseous reducing agents such as hydrogen or carbon monoxide do not reduce the oxide to metal at temperatures below the melting point of aluminum. It has been thought that the presence of these films of oxide on aluminum particles would interfere markedly in powder metallurgical work and a number of suggestions have been made, either for preventing the formation of the film through the production of the powders in inert or reducing atmospheres, or for the removal of the oxide by means of powerful reducing agents, including "nascent" or atomic hydrogen released from metal hydrides. A second and more serious difficulty in the use of aluminum and aluminum-alloy powders in powder metallurgy resides in the fact that during compression such powders tend to adhere or cold-weld to the die walls, thus interfering with the formation and ejection of a compact. A third difficulty, which has been encountered only with aluminum-alloy powders, is their hardness when compared with elemental aluminum. Certain of these powders are susceptible to age-hardening, which further hinders the formation of strong green compacts. These conditions are particularly true of atomized aluminum-alloy powders. Even in the annealed condition, plastic deformation of alloy powders under pressure is low when compared with unalloyed powders. This fact, coupled with the lower corrosion resistance of the alloy powders. is probably the significant factor in our failure to obtain strong sintered pieces. Methods of Puoducing the Powder Many methods have been proposed for manufacture of aluminum powder, only a few of which are used commercially. Several of the more important processes include: (I) atomization of the molten metal; (2) mechanical pulverization and other types of comminution; and (3) graining, in which molten aluminum is stirred during freezing. For pigment and certain pyrotechnic uses aluminum flake powder is desirable, because of its greater proportion of surface to volume; and large quantities of such material are made by a procedure that involves stamping or ball milling. In making flake intended for use as pigment,

Jan 1, 1943

By G. D. Cremer, J. J. Cordiano

Aluminum powder is a well-known article of commerce and in various forms has been marketed widely for use in paint, for pyrotechnic purposes and for exothermic mixtures. For a number of reasons, however, aluminum powder has not been employed extensively in powder metallurgy, although a great many proposals along this line have been offered. Aluminum and alumiuum-alloy powders oxidize readily upon exposure to air and the thin film of oxide (or hydroxide) thus formed is highly refractory, in that ordinary gaseous reducing agents such as hydrogen or carbon monoxide do not reduce the oxide to metal at temperatures below the melting point of aluminum. It has been thought that the presence of these films of oxide on aluminum particles would interfere markedly in powder metallurgical work and a number of suggestions have been made, either for preventing the formation of the film through the production of the powders in inert or reducing atmospheres, or for the removal of the oxide by means of powerful reducing agents, including "nascent" or atomic hydrogen released from metal hydrides. A second and more serious difficulty in the use of aluminum and aluminum-alloy powders in powder metallurgy resides in the fact that during compression such powders tend to adhere or cold-weld to the die walls, thus interfering with the formation and ejection of a compact. A third difficulty, which has been encountered only with aluminum-alloy powders, is their hardness when compared with elemental aluminum. Certain of these powders are susceptible to age-hardening, which further hinders the formation of strong green compacts. These conditions are particularly true of atomized aluminum-alloy powders. Even in the annealed condition, plastic deformation of alloy powders under pressure is low when compared with unalloyed powders. This fact, coupled with the lower corrosion resistance of the alloy powders. is probably the significant factor in our failure to obtain strong sintered pieces. Methods of Puoducing the Powder Many methods have been proposed for manufacture of aluminum powder, only a few of which are used commercially. Several of the more important processes include: (I) atomization of the molten metal; (2) mechanical pulverization and other types of comminution; and (3) graining, in which molten aluminum is stirred during freezing. For pigment and certain pyrotechnic uses aluminum flake powder is desirable, because of its greater proportion of surface to volume; and large quantities of such material are made by a procedure that involves stamping or ball milling. In making flake intended for use as pigment,

Jan 1, 1943

By C. H. Mathewson, P.W. Bakararian

The greatcr part of the literature on the plastic behavior of magnesium dates back to that active period of research in crystal mechanics immediately following the widespread preparation of isolated metallic crystals large enough for the application of conventional methods of mechanical testing. These investigations, performed on single crystals, revealed an analogy between zinc and magnesium with respect to their fundamental mode of deformation. in the operation of glide and twinning, respectively, on crystallographically similar planes. Mathewson and Phillips (1928)' by geometrical analysis identified the plane in magnesium as the twinning plane. Schiebold and Siebel (1931) confirmed this twinning planc, established the basal plane as the plane of slip, and a digonal axis I as the slip direction. They also rcported twin formation in a secondary role on the {IOI} plane. Schmid (1931)³ summarized and discussed the earlier evidence and presented the results of his own experiments on the effect of temperature and small amounts of soluble elements. From X-ray studies on extended wire single crystals, he concluded that slip along the basal plane in the direction of the digonal axis I closest to the stress direction was the sole slip system operating at atmospheric temperature. This conclusion was based on experiments with crystals of many different orientations relative to the stress axis. Special attention was directed to the basal plane and the digonal axis I, as the plane and direction of greatest atomic density. Determinations of resolved shear stress at the onset of plastic yielding-—i.e., the critical resolved shear stress—were also made; the average of these calculations showing 82.9 grams per sq. mm. This value varied only slightly up to 300°C. at which temperature it was found to decrease to 70.5 grams per sq. mm. The extension of his crystals at temperatures above 225°C. further disclosed the presence of new slip systems. After the origince specimens of circular section had been

Jan 1, 1943

By C. H. Mathewson, P. W. Bakararian

The greatcr part of the literature on the plastic behavior of magnesium dates back to that active period of research in crystal mechanics immediately following the widespread preparation of isolated metallic crystals large enough for the application of conventional methods of mechanical testing. These investigations, performed on single crystals, revealed an analogy between zinc and magnesium with respect to their fundamental mode of deformation. in the operation of glide and twinning, respectively, on crystallographically similar planes. Mathewson and Phillips (1928)' by geometrical analysis identified the plane in magnesium as the twinning plane. Schiebold and Siebel (1931) confirmed this twinning planc, established the basal plane as the plane of slip, and a digonal axis I as the slip direction. They also rcported twin formation in a secondary role on the {IOI} plane. Schmid (1931)³ summarized and discussed the earlier evidence and presented the results of his own experiments on the effect of temperature and small amounts of soluble elements. From X-ray studies on extended wire single crystals, he concluded that slip along the basal plane in the direction of the digonal axis I closest to the stress direction was the sole slip system operating at atmospheric temperature. This conclusion was based on experiments with crystals of many different orientations relative to the stress axis. Special attention was directed to the basal plane and the digonal axis I, as the plane and direction of greatest atomic density. Determinations of resolved shear stress at the onset of plastic yielding-—i.e., the critical resolved shear stress—were also made; the average of these calculations showing 82.9 grams per sq. mm. This value varied only slightly up to 300°C. at which temperature it was found to decrease to 70.5 grams per sq. mm. The extension of his crystals at temperatures above 225°C. further disclosed the presence of new slip systems. After the origince specimens of circular section had been

Jan 1, 1943

By G. H. Anderson

During an investigation of the copper-rich portion of the copper-silicon-iron system as part of an extensive research program on P.M.G. alloys, which was begun in 1937 in the research laboratory of the Phelps Dodge Corporation, it became apparent that the binary copper-silicon system below 7 per cent Si needed revision, therefore an investigation was undertaken. Both X-ray methods and microscopic technique were employed. Despite the many investigations that have the clarification of this system as their object, no two successive reports on the system have agreed in placement of the alpha-phase solubility limit, and uncertainty about the secondary phase first to appear has been voiced several times.3,4,5 It was therefore not surprising, when T. Isawa's6 and M. Okamoto's7 works were reported at the time we were finishing up our experimental work, to find essential disagreement between their results and ours. But when C. 5. Smith's latest work on the copper-silicon systema was published just as we were finishing our laboratory report, it was indeed gratifying to find that the latter's diagram and ours checked in all essential features, except the temperature of the peritectoid line above 830" C. Many attempts were made to retain the beta phase during the present investigation, but none was successful. Isawa,6 however, reports that he has been able to obtain X-ray photograms of the beta phase. The structure, he states, is body-centcrcd cubic with a lattiee constant of 2.848 ,&. at 7.2 per cent Si. Okamoto7 and Smith8 both use the designation Kappa for the hexagonal phase, and to avoid confusion this designation will he adhered to in the present paper. Preparation of Samples The alloys were melted in vacuum in a high-frequency furnace. from copper cathodes containing 99.98 per cent Cu, and specially refined silicon supplied by The Electro Metallurgical Co. This silicon is stated

Jan 1, 1940

By G. H. Anderson

During an investigation of the copper-rich portion of the copper-silicon-iron system as part of an extensive research program on P.M.G. alloys, which was begun in 1937 in the research laboratory of the Phelps Dodge Corporation, it became apparent that the binary copper-silicon system below 7 per cent Si needed revision, therefore an investigation was undertaken. Both X-ray methods and microscopic technique were employed. Despite the many investigations that have the clarification of this system as their object, no two successive reports on the system have agreed in placement of the alpha-phase solubility limit, and uncertainty about the secondary phase first to appear has been voiced several times.3,4,5 It was therefore not surprising, when T. Isawa's6 and M. Okamoto's7 works were reported at the time we were finishing up our experimental work, to find essential disagreement between their results and ours. But when C. 5. Smith's latest work on the copper-silicon systema was published just as we were finishing our laboratory report, it was indeed gratifying to find that the latter's diagram and ours checked in all essential features, except the temperature of the peritectoid line above 830" C. Many attempts were made to retain the beta phase during the present investigation, but none was successful. Isawa,6 however, reports that he has been able to obtain X-ray photograms of the beta phase. The structure, he states, is body-centcrcd cubic with a lattiee constant of 2.848 ,&. at 7.2 per cent Si. Okamoto7 and Smith8 both use the designation Kappa for the hexagonal phase, and to avoid confusion this designation will he adhered to in the present paper. Preparation of Samples The alloys were melted in vacuum in a high-frequency furnace. from copper cathodes containing 99.98 per cent Cu, and specially refined silicon supplied by The Electro Metallurgical Co. This silicon is stated

Jan 1, 1940

By W. A. Mudge, Paul D. Merica

One of the most prominent features of our present-day industrial development is the ever-increasing demand put upon materials of construction. Engineering ingenuity, within the past 25 years, has been unusually active, and in some fields at least engineers frankly say that engineering design has progressed as far as the limitations imposed by the properties of the present materials of construction will permit. Consequently, they are today demanding improvement in their working materials and seeking new ones, through the aid of which the present limitations of design may be overcome. The activity of this search is evident in all fields, but it is particularly so in that of structural materials required to be resistant to corrosion. The corrosion resistance of metals and alloys is never absolute and all-inclusive; a particular alloy will withstand some corrosive conditions well and fail utterly under others. Furthermore, other properties, physical and mechanical, required in conjunction with corrosion resistance vary considerably for different commercial applications. One wants a soft, ductile sheet metal resistant to atmospheric corrosion; another, a high-strength alloy resistant to sulfuric acid. The last decade has witnessed active and definite progress in the development of high-strength, corrosion-resisting alloys. In June, 1924, a symposium by the American Society for Testing Materials, on Corrosion-resistant, Heat-resistant and Electrical-resistance Alloys, disclosed no less than 60 commercial alloys the properties of which were described as being suitable for industrial service where corrosion resistance was a feature. Today the number of these alloys has been doubled, at least. In addition, economy in design and construction through decreased weight has given considerable impetus to the improvement of alloys of which the mechanical propprties may be improved by heat-treatment.

Jan 1, 1935

By Paul D. Merica, W. A. Mudge

One of the most prominent features of our present-day industrial development is the ever-increasing demand put upon materials of construction. Engineering ingenuity, within the past 25 years, has been unusually active, and in some fields at least engineers frankly say that engineering design has progressed as far as the limitations imposed by the properties of the present materials of construction will permit. Consequently, they are today demanding improvement in their working materials and seeking new ones, through the aid of which the present limitations of design may be overcome. The activity of this search is evident in all fields, but it is particularly so in that of structural materials required to be resistant to corrosion. The corrosion resistance of metals and alloys is never absolute and all-inclusive; a particular alloy will withstand some corrosive conditions well and fail utterly under others. Furthermore, other properties, physical and mechanical, required in conjunction with corrosion resistance vary considerably for different commercial applications. One wants a soft, ductile sheet metal resistant to atmospheric corrosion; another, a high-strength alloy resistant to sulfuric acid. The last decade has witnessed active and definite progress in the development of high-strength, corrosion-resisting alloys. In June, 1924, a symposium by the American Society for Testing Materials, on Corrosion-resistant, Heat-resistant and Electrical-resistance Alloys, disclosed no less than 60 commercial alloys the properties of which were described as being suitable for industrial service where corrosion resistance was a feature. Today the number of these alloys has been doubled, at least. In addition, economy in design and construction through decreased weight has given considerable impetus to the improvement of alloys of which the mechanical propprties may be improved by heat-treatment.

Jan 1, 1935

By Thomas C. Wilder

The activities of both components and the partial and integral molar thermodynamic properties of mixing for the liquid Al-Ge system at 1200°K and for the gertnanium-rich Al-Ge liquidus have been determined from data for eighteen alloys of compositions in the range 0.0593 < 0.880 using the reuersible gal-vanic. cell in the temperature interval 9320 to 1258°K. The liqui-dus compositions above 93 2 °K loere also ve determined by observing the discontinuities in the C us T plots for the high-melting alloys. This system shows moderate negative deviation from ideality throughout, the values for y° being 0.212 and 0.189 for aluminum and germanium, respectively, at 1200°K. Pavtial molar Properties of aluminum on the germanium-rich solidus and at infinite dilution in Ge(s) oboue 932°K were estimated from the foregozng measurements and the equlibrium data of previous investzgators. RECENT compilations of data1" have shown an increasing demand for knowledge of the thermodynamic properties of mixing of metallic alloy systems. In the case of binary-liquid systems where one of the components is a semiconductor this information is useful because, primarily, properties of the second (dopant) component on the liquidus, solidus, and at infinite dilution may be determined more accurately than from calculations based on the phase diagram. In this investigation a reversible galvanic cell was used to determine the chemical potential of aluminum in the two-phase region, liquid + [Ge], on the germanium-rich side of the A1-Ge system in the temperature range 932" to 1193°K. In addition, similar measurements for homogeneous liquid A1-Ge alloys for the entire composition range were obtained for the temperature interval 932" to 1258°K. The cell used was: The experimental technique and the treatment of the data were essentially the same as described earlier394 and are elaborated upon only briefly here. Each cell consisted of a liquid aluminum anode and three A1-Ge alloy cathodes of different composition which were held in Morganite alumina crucibles. The alloys were made up from aluminum and germanium weighed to the nearest 0.1 mg to a total weight of 5 to 10 g. Aluminum was a gift of Aluminum Co. of America and had a purity of 99.995+ pct. Germanium of transistor grade was a gift of Bell Telephone Laboratories. The four electrodes were contained in a larger alumina crucible which also held the prepurified fused chloride electrolyte. Contact to the electrodes was made by tantalum wire leads sheathed in alumina. The tantalum leads were centered in the electrodes by suitable positioning of an alumina radiation shield which fitted on the top of the - alulnina crucible. Two chrome l-alumel thermocouples, sheathed in quartz wells, completed the internal cell arrangement. The entire assembly was enclosed in an alumina tube, fitted with a water-cooled copper head so the system could be evacuated and then flushed with purified argon. *

Jan 1, 1967

By R. A. Harrington, H. R. Nelson

The: structure of anodic films formed on aluminum and other metals under varied conditions is not well known despite the wide use of such films both as protective coatings and as the dielectric medium in electrolytic condensers. The present work was undertaken as a survey of the possibilities of electron diffraction in the investigation of anodic films, especially in comparing the properties of anodic films formed under different sets of conditions and subjected to various subsequent treatments. In addition, an effort has been made to compare surface films formed on aluminum by anodic treatment with surface films formed by heating, immersion in chemicals, etc. The elcctron diffraction method in many cases has been successfully applied to the study of thin surface films. Its principal advantage is that it can be used without removing the films from the base material upon which they have been formed. The low penetrating power of electrons, in the "reflection" diffraction method which has been used in this work, prevents the appearance of diffraction patterns from substances at depths greater than about 100 Angstrom units (lop6 cm.). Different investigations of the structure of anodic films have showll widely varying results, depending on the methods used in preparing the films. Apparently under some conditions these films are crystalline and under other conditions they are amorphous, and it has been difficult to say which type of structure will be found in any particular case. Schmid and Wassermann&apos;s1 X-ray diffraction patterns of eloxal‡ films show two broad, diffuse bands, which these investigators attribute to finely divided cubic y-Al2O3.§ Burgers, Claassen, and Zernicke³ obtained sharp X-ray

Jan 1, 1940

By R. A. Harrington, H. R. Nelson

The: structure of anodic films formed on aluminum and other metals under varied conditions is not well known despite the wide use of such films both as protective coatings and as the dielectric medium in electrolytic condensers. The present work was undertaken as a survey of the possibilities of electron diffraction in the investigation of anodic films, especially in comparing the properties of anodic films formed under different sets of conditions and subjected to various subsequent treatments. In addition, an effort has been made to compare surface films formed on aluminum by anodic treatment with surface films formed by heating, immersion in chemicals, etc. The elcctron diffraction method in many cases has been successfully applied to the study of thin surface films. Its principal advantage is that it can be used without removing the films from the base material upon which they have been formed. The low penetrating power of electrons, in the "reflection" diffraction method which has been used in this work, prevents the appearance of diffraction patterns from substances at depths greater than about 100 Angstrom units (lop6 cm.). Different investigations of the structure of anodic films have showll widely varying results, depending on the methods used in preparing the films. Apparently under some conditions these films are crystalline and under other conditions they are amorphous, and it has been difficult to say which type of structure will be found in any particular case. Schmid and Wassermann&apos;s1 X-ray diffraction patterns of eloxal‡ films show two broad, diffuse bands, which these investigators attribute to finely divided cubic y-Al2O3.§ Burgers, Claassen, and Zernicke³ obtained sharp X-ray

Jan 1, 1940

By T. Suzuki

LABOR. conditions have finally caused rock-drilling machines to supplant hand drillers in the Japanese mining industry, and have encouraged this study. During a period of three years 25,000 tests were made on 67 different American, Japanese, and European rock drills, using, respectively, the Paynter testing machine, and drilling in granite and limestone. Recorded were: air consumption, speed of rotation, torque of rotation, foot-pounds of striking energy, air pressures, input horsepowers, and speed of rock penetration. The author expresses his views on the interrelation of these factors and offers theoretical support, as well, by formulas based upon the mechanics of impact. He discusses the different designs of the valves, cylinders, piston hammers and rotation devices involved in the different types of rock drills, with respect to their merits and defects and offers conclusions about the factors that should be considered in the new design of a superior rock drill. The author&apos;s mathematical demonstrations and arguments for a value of "best feed clearance" of the drill bit from the rock are based upon the hand-operated screw-fed type of hammer drill. Automatic feeds have not been considered in this paper except for the tests on one drifter with air feed, 10 air-feed stopers, and some hand-held blockholers. The following classes of drills, with one of each model, size, or type, were tested: 23 heavy drifters, 34 light drifters and hand-held drills, and 10 stopers. They represented the following makes and models: 40 from the United States—namely, Ingersoll-Rand 18, 148, L-74, 24-70, N-72, N-75, R-72, 26, BAR-33, BCR-430, DCRW-23, RA-12, CA-31, CC-11; Denver 7, 107, WT-21, WT-31, WT-331, WT-337 (models WT with motor rotation, screw feed), 11, Waugh 93, 95; Waugh 16; Sullivan DR-6, DW-64, T-3; DP-321, DP-331; DA-21, DT-44, DT-421; Gilman AX-321 (motor rotation and air feed); Cleveland D-5; AIBQ, 44-SWR,

Jan 1, 1940

By T. Suzuki

LABOR. conditions have finally caused rock-drilling machines to supplant hand drillers in the Japanese mining industry, and have encouraged this study. During a period of three years 25,000 tests were made on 67 different American, Japanese, and European rock drills, using, respectively, the Paynter testing machine, and drilling in granite and limestone. Recorded were: air consumption, speed of rotation, torque of rotation, foot-pounds of striking energy, air pressures, input horsepowers, and speed of rock penetration. The author expresses his views on the interrelation of these factors and offers theoretical support, as well, by formulas based upon the mechanics of impact. He discusses the different designs of the valves, cylinders, piston hammers and rotation devices involved in the different types of rock drills, with respect to their merits and defects and offers conclusions about the factors that should be considered in the new design of a superior rock drill. The author&apos;s mathematical demonstrations and arguments for a value of "best feed clearance" of the drill bit from the rock are based upon the hand-operated screw-fed type of hammer drill. Automatic feeds have not been considered in this paper except for the tests on one drifter with air feed, 10 air-feed stopers, and some hand-held blockholers. The following classes of drills, with one of each model, size, or type, were tested: 23 heavy drifters, 34 light drifters and hand-held drills, and 10 stopers. They represented the following makes and models: 40 from the United States—namely, Ingersoll-Rand 18, 148, L-74, 24-70, N-72, N-75, R-72, 26, BAR-33, BCR-430, DCRW-23, RA-12, CA-31, CC-11; Denver 7, 107, WT-21, WT-31, WT-331, WT-337 (models WT with motor rotation, screw feed), 11, Waugh 93, 95; Waugh 16; Sullivan DR-6, DW-64, T-3; DP-321, DP-331; DA-21, DT-44, DT-421; Gilman AX-321 (motor rotation and air feed); Cleveland D-5; AIBQ, 44-SWR,

Jan 1, 1940

By J. S. Vanick

An extremely hard, tough, and strong, white or chilled cast iron has been applied for the past several years to industrial and mining services in which its unusual properties have been confirmed by its ability to deliver in many instances much better performance than plain chilled iron, or other wear-resistant materials. It is being produced regularly by alloying a good base composition of chilled or white cast iron with essentially 4 to 6 per cent of nickel and 1 to 2.5 per cent of chromium. Such a material can attain a hardness exceeding 600 to 750 Brinell as against 380 to 530 for corresponding grades of plain chilled iron. The strength is approximately doubled and the toughness significantly increased. These properties make it especially useful for many applications requiring a high hardness for resistance to wear, abrasion, attrition, deformation; to some extent to high compressive loading and to a lesser but important degree to corrosive action. A wide variety of commercial castings is being successfully produced from this iron, ranging in size from the small grain-grinding plates or burrs through medium-sized castings such as sand pumps up to large, heavy castings such as rolls for metal rolling or cement grinding. The composition of this white cast iron may be roughly bracketed within the range shown in Table 1.

Jan 1, 1933

By G. R. Gardner, D. H. Davis

Increasing realization of the importance of dust control, and the recommendations of various agencies, have led the mining industry to become actively concerned with this problem. The background and necessity for adequate dust-suppression measures have been discussed in a number of publications, including those of the U. S. Bureau of Mines, and the use of spray water to reduce dust at the face and on roadways has been recommended. The problem resolves itself into obtaining adequate dust reduction at a reasonable cost. Inasmuch as the term "adequate dust suppression" has never been clearly defined, nor have permissible limits of dustiness (in terms of dust count) been established, it is apparent that any method selected may be required to meet additional demands. Until the industry has been given some indication of permissible limits of dustiness, no permanent solution is possible. Progress will be somewhat handicapped until such information is available. In addition, dust reduction must be obtained without the addition of any excessive moisture to the coal, since consideration must often be given to: I. Quality standards, particularly reduction in heat value. 2. Handling characteristics, particularly in regard to unloading from railroad cars and bins. 3. Application of dry methods of coal cleaning. 4. Necessity for fine screening within specified limits of oversize and undersize. Little detailed information is available as to the advantages and disadvantages of the several methods of water distribution, the location and protection of sprays, operating data on pressure, quantity of water, and so forth, and results obtained. In 1940 an investigation was undertaken to determine and evaluate the principal factors involved. This paper constitutes a progress report on this work and cannot in any way be regarded as complete on any one of the several phases. Classification of Dust Sources The various sources of underground dust may be classified as primary or secondary. A primary source is one associated with appreciable degradation of size, that is, where the greater part of the actual fines capable of becoming air-borne dust are produced. A secondary source may be considered as one in which the greater part of the fines have been produced at some previous operation and are in such condition that they can be dispersed as air-borne dust. These conceptions appear to be of practical significance, as experience indicates that when dust is controlled at the primary sources the importance of secondary sources is minimized. For these reasons, investigations to date have been concerned principally with the primary sources of dust, and this paper is concerned particularly with one of these—namely, undercutting. In accord with the foregoing definitions, the sources to which the following opera-

Jan 1, 1942

By G. R. Gardner, D. H. Davis

Increasing realization of the importance of dust control, and the recommendations of various agencies, have led the mining industry to become actively concerned with this problem. The background and necessity for adequate dust-suppression measures have been discussed in a number of publications, including those of the U. S. Bureau of Mines, and the use of spray water to reduce dust at the face and on roadways has been recommended. The problem resolves itself into obtaining adequate dust reduction at a reasonable cost. Inasmuch as the term "adequate dust suppression" has never been clearly defined, nor have permissible limits of dustiness (in terms of dust count) been established, it is apparent that any method selected may be required to meet additional demands. Until the industry has been given some indication of permissible limits of dustiness, no permanent solution is possible. Progress will be somewhat handicapped until such information is available. In addition, dust reduction must be obtained without the addition of any excessive moisture to the coal, since consideration must often be given to: I. Quality standards, particularly reduction in heat value. 2. Handling characteristics, particularly in regard to unloading from railroad cars and bins. 3. Application of dry methods of coal cleaning. 4. Necessity for fine screening within specified limits of oversize and undersize. Little detailed information is available as to the advantages and disadvantages of the several methods of water distribution, the location and protection of sprays, operating data on pressure, quantity of water, and so forth, and results obtained. In 1940 an investigation was undertaken to determine and evaluate the principal factors involved. This paper constitutes a progress report on this work and cannot in any way be regarded as complete on any one of the several phases. Classification of Dust Sources The various sources of underground dust may be classified as primary or secondary. A primary source is one associated with appreciable degradation of size, that is, where the greater part of the actual fines capable of becoming air-borne dust are produced. A secondary source may be considered as one in which the greater part of the fines have been produced at some previous operation and are in such condition that they can be dispersed as air-borne dust. These conceptions appear to be of practical significance, as experience indicates that when dust is controlled at the primary sources the importance of secondary sources is minimized. For these reasons, investigations to date have been concerned principally with the primary sources of dust, and this paper is concerned particularly with one of these—namely, undercutting. In accord with the foregoing definitions, the sources to which the following opera-

Jan 1, 1942

By M. G. Corson

Until recently, the characteristics of cast copper have seldom been studied and such study as has been made has been inadequate. The prevailing idea seems to be that since pure copper is infrequently used in the cast stlate, there is no reason for trying to establish precise data regarding the properties of the metal in that condition. On the other hand, wrought copper either in the shape of sheets or wire rarely fails in service, except as a result of the action of reducing gases at the annealing temperatures, so there is little incentive to study the properties of the cast shapes —cakes, bars, ingots and billets—for the sake of tracing the causes of failures of the wrought metal to the cast stock. However, about a decade ago, wirebars of American origin often cracked badly while being hot-rolled in mills in Germany. This Icd to four investigations: by E. Seidl and E. Schieboldll by P. Siebe12 by 0. Bauer and G. Sachs,3 and by G. Welter.4 These authors came to the conclusion that failures in hot-rolling were due essentially to the presence of a wide zone of columnar crystals between t&apos;he thin layer of fine crystal5 near the surfaces of the bars and the large but more nearly equiaxed grains of the central core. This macrostructural defect was explained in turn by the probable upward deviation in the temperature of the metal while it was being poured into the molds of the castling machine. More recently, cast shapes of copper were investigated by X. 1&apos;. Allenh and by C. Blazey. Allen examined vertically cast wirebars and hori-zontally cast wedge cakes of electrolytic tough-pitch copper, but only for the distribution of densities; i.e., porosity. Blazey was interested mainly in the mechanism of the variations in electrical conductivity due to cold-work and anneal, but gave introductively an account of the composi-tion and average densities of the tough-pitch horizontally cast Wirebars used. As far as the present writer can tell, no investigation mas under-taken for the sake of presenting a picture of the distribution of mechanical characteristics in the wirebars of copper, or otherwise.

Jan 1, 1938