By B. Nowak

For sources with an iron-to-vanadium ratio of far above 1, it is proposed to leach in acid and to oxidize under autoclave conditions. During this oxidation process, it is experimentally shown that divalent iron contained in this solution will be oxidized to trivalent iron, whereas free acid contained will be consumed by this reaction. In case no acid is present or already fully consumed, a solid consisting of ferric compounds and an iron-vanadium-co-precipitate will form that can be filtered from the solution. If choosing the right reaction conditions, this filter cake has an iron-to-vanadium ratio of close to 1, whereas the liquid remainder is almost vanadium free. This precipitate, identified as FeVO4, 1.1 H2O, can be processed by conventional technologies such as caustic leaching, or probably salt roasting or reduction with aluminum, yielding common marketable products.

By R. S. Celmer

The distributions of cobalt, molybdenum, copper, and selenium between nickel matte and silica-saturated iron silicate slag have been determined in the region of the metallic saturation boundary, at 1523 K. Results are given as a function of the composition of the coexisting Fe-Ni alloy and the activity of iron in the system. Under strongly reducing conditions, these minor elements display a marked preferential accumulation in the sulphide phase. It is shown that the dissolution of cobalt and molybdenum in slag follows an oxidative mechanism, and distribution equilibria are correlated with the oxygen potential. From these data, the thermodynamic properties of cobalt in nickel matte are computed. Further, comparisons of minor element partitions are made between the nickel and copper matte smelting cases under metal saturation conditions.

Jan 1, 1988

By Mitsutaka Hino

The contents of gangue minerals, such as A1203, P205, crystalline water and so forth in the iron ore imported to Japan tend to increase year by year, Though the increments of such gangue contents are approximately 0.1-0.2 mass%, some problems for the blast furnace operation in ironmaking process have already been reported, In order to clarify the mechanism of harmful effect caused by the small increment of gangue minerals, mainly A1203, on the blast furnace operation, the dripping behavior of FetO-CaO-SiO2-AI2O3-MgO slag from the iron funnel, which simulated the micro-porosity in sinter ore, has been observed with the wide range of basicity, Al2O3, FetO and Mgo contents. The effect of MgO on the dripping behavior of slag has been summarized in this paper, It was found that the addition of 2mass% MgO resulted in large increase of hold-up on the most of the conditions. When FetO content was less than 20mass% and the basicity was lower than 0.8, MgO lowered the hold-up even if the slag contained 10mass% Al2O3. Every slag hold-up showed the minimum at the basicity of less than unity on the conditions of constant FetO and A1203 contents. This trend became remarkable when the slag contained 2 mass% MgO.

Jan 1, 2003

By R. J. St. Eloi

The Kidd Creek Copper Smelter has been expanded from its original design of 59,000 tonnes of copper per year to over 120,000 tonnes per year .. Modifications to the process gas handling system and acid plant have been made to accommodate this higher production rate and to .generally optimize the operation. The gas handling system associated with the continuous smelting process is discussed in terms of boiler accretions and modifications to minimize their impact on operations; design changes to effect reductions in high pressure drop duct configurations; material changes to overcome corrosion and plant additions to 'improve gas cleaning capability. The acid plant is reviewed with references to changes made to accommodate the increased S02 gas strength resulting from the higher smelting rates;

Jan 1, 1992

By Varadarajan Seshadri

A physical model based on similarity principles was constructed for simulating the RH degasser of CST (Companhia Siderurgica Tubarao, Vitoria, ES, Brazil) to evaluate the circulation rate of the metal which essentially defines the degree of exposure of the metal to vacuum in the chamber and thus of the refining rate. The circulation rate on the other hand will influence the decarburization rate and removal of dissolved gases like nitrogen and hence it is essential to optimise this parameter to get maximum refining efficiency with minimum refming times, thus improving the productivity of the secondary refining process. Mixing characteristics in the ladle is evaluated by pulse tracer addition using conductivity-meters located at the down leg as well as at several locations in the ladle. The influence of gas injection through nozzles in the upleg with simultaneous bottom injection of gas as well as nozzle blockage on the circulation rates were investigated. Also simulation experiments of kinetics of decarburization were carried out using C02 adsorption-desorption process in sodium hydroxide solution as circulating fluid and the effect of, bottom gas flow rate in this case was also evaluated. The results were carried over to prototype and to optimize the process.

Jan 1, 2003

By L. J. Lutz

The U.S. Bureau of Mines has developed an electrorefining process to recover Ni, Co, Cr, and other metals from mixed and contaminated superalloy scrap. The superalloy scrap is cleaned then directly electrodeposited as a Ni -Co deposit. The process recovers approximately 90 pct of the Ni-Co available from the scrap as a 99t pct pure Ni-Co alloy. During electrorefining the electrolyte undergoes a purification process which results in Cr and other refractory metals reporting to the purification residue. Operating data is given for a 3-L compartmented electrolytic cell. Techniques for the removal of Fe, Cr, and trace impurities from the recycled electrolyte are outlined. The economics of a facility producing 15 mt/d of a Ni-Co alloy are also discussed.

Jan 1, 1993

By Ilija Ilic

Recovery of tin from tinplate and production of good-quality detinned-plate for further processing in ironworks has been the subject of interest for many years. Tinplates are mostly used for production of tin containers for food industry and consumer goods. The research carried out so far included determination of the parameters of dissolution of tin from tinplates by alkaline solution of NaOH and electrochemical recovery of tin from the alkaline solutions. During leaching, NaNO3 and methanitrobenzoic acid (MNBA) as oxidants were studied. By leaching the waste tinplate which contains 0.31 % of tin with a solution of 1.12 mol/dm3 NaOH, 0.26 mol/dm3 Na2CO3 and 0.09 mol/dm3 MNBA at temperature of 70°C for 60 mm, a degree of tin leaching of 97 % was attained. MNBA facilitates oxidation of Sn2+ into Sn4+ suitable for obtaining compact, and not spongy, Sn cathode deposit, as it was the ease earlier. Recovery of tin by electrolysis from solutions obtained by leaching was studied to determine the effect of electrolyte composition on the quality of cathode deposit and the degree of electric current efficiency. Experimental results obtained at a laboratory level were checked on an enlarged laboratory set up where continuos leaching of tin from waste tinplate and its electrolytic recovery from the solution obtained were carried out. The experimental set-up -operated under semi-industrial conditions, and about 500 kg of waste tinplate was processed yielding about 1.160 kg of tin (99 % Sn).

Jan 1, 2000

By Huyang Xie, Rishi Raj, Vera A. Versteeg

"A new method for MOCVD has been developed in which a precursor solution is directly injected into a reaction chamber. The vaporization of short pulses of liquid is facilitated by atomization with a piezoelectrically-operated nozzle. The system has been used successfully to grow oriented, thin Ti02 (rutile) films on sapphire substrates with the crystalline relationship (101)[010]R I (1120)[0001]s. A growth rate of approximately 2 monolayers per pulse was achieved at 650°C for a reactant impingement rate of about 800 monolayers per pulse. Also, epitaxial LiTaO3 thin films were grown on (0001) sapphire from a single source, bimetallic precursor, lithium tantalum hexa-t-butoxide as the precursor. X-ray diffraction shows that the LiTaOa c-axis is normal to the sapphire surface. The x-ray pole figure and crosssection TEM diffraction show that the films were also in-plane oriented, with sapphire [1010] parallel to lithium tantalate [1010]. These films are shown to have extremely low optical attenuation, and refractive index that compares well with bulk values.IntroductionMetalorganic chemical vapor deposition (MOCVD) techniques have come into increasing use in recent years, due to the growing versatility and availability of precursors and improved environmental advantages over the halogenated compounds used for conventional CVD. Most commonly, the films are deposited by dissolving the metalorganic reactant (typically a metal alkoxide) in a carrier gas, which is carried through heated lines to a heated substratel . The metal alkoxides decompose by pyrolysis, leaving the films on substrates. While this method has been used to produce excellent epitaxial and heterepitaxial films, it has the disadvantages of complexity: the precursor must be heated to fix its vapor pressure, the gas flow rate carefully controlled, and the carrier lines heated to prevent condensation before reaching the reactor. Additionally, this conventional method cannot be used with certain low-volatility precursors that decompose upon heating."

Jan 1, 1994

By Bengt T. Andersson

Outokumpu Consulting Engineers, Outokumpu Oy SF-02200 Espoo 20, Finland This paper describes experiences from some operating non-ferrous flash -smelters and focuses on the advances in smelter byproduct and gas treatment engineering design. In this context a summary is given of the specific technical and economic benefits achieved-by flash -smelting technology and oxygen enrichment. The paper will also briefly outline a few new process and equipment developments.

Jan 1, 1983

By F. T. Principe

In order for solvent extraction technology to be acceptable as an alternative to existing jarosite precipitation circuits, iron must be cleanly separated and concentrated into a feed stream suitable for downstream iron by-product recovery which meets market specifications and economics. Ten years ago, significant progress was made in a joint McCill University/CANMET project that involved iron extraction with mono(2-ethylhexyl) phosphoric acid and stripping with HCI. Our iron solvent extraction research was reactivated recently by looking into this and other members of the organophosphorus extractant family. Our research focuses on the mechanisms and control of anion (SO42/CI) transport across the various phases (Rafinate/Organic/Strip), iron build-up in the strip liquor, and extractant stability/selectivity. In this paper, these issues along with some other performance parameters are discussed using data derived from an extensive search of the two commercially available and best known members of the organophosphorus family, di-2-ethylhexyl (D2EHPA) and mono-2-ethylhexyl (M2EHPA) phosphoric acid. Further in this discussion, the challenges lying ahead in the development of sx systems that overcome the deficiencies of D2EHPA and M2EHPA are outlined. In particular, the necessity of considering secondary separation technologies that can further concentrate iron values in the chloride strip liquor to levels economically attractive for the production of saleable iron oxide by pyrohydrolysis is addressed.

Jan 1, 1998

By Claudio Parra De Lazzari

The determination of the governing step of the deoxidation rate and the effects of the hydrogen content of the mixtures (C), the diameter of the delivery orifice (4) and the Reynolds number of the orifice (Re.) on the product Av kjg were investigated. A,, is the total surface area of the interface between the bubbles and the melt and kjg is the mass transfer coefficient in the gas phase. The design of the experiments was based on a two level statistically fractionated, factorial planning. Oxygen in the melt was measured as a function of time. It was found that the governing step of the deoxidation rate was the transport of hydrogen in the gaseous phase and that {Ay kjg} increases with C, {o} and Reo.

Jan 1, 1997

By Zhucheng Huang, Yuanbo Zhang, Kecheng Zhang, Guanghui Li, Tao Jiang

"With rapid development of Iron and Steel industry, plenty of metallurgical dusts and sludges are generated, which have not been effectively utilized because of their poor hydrophilicity and bad ballability. Agglomeration and roasting of metallurgical dusts & sludges with a new-type composite binder are studied in this paper. The results indicate that the dosage of the new binders can be decreased to 2.5 wt% from 3.5 wt% when using the wet-grinding process. Under the optimal conditions of briquetting pressure 2070 N/cm2, briquetting moisture content 13 wt%, roasting temperature 1000 °C and roasting time 40 min, the qualities of the green, dry and roasted briquettes meet the requirements of the industry production. The finished products have the compression strength of more than 2000 N/cm2, which can be used as high-quality burdens for blast furnaces.IntroductionWith rapid development of Chinese Iron & Steel industry, there are more and more serious resource shortage and environmental pollution existing. Converter sludges, containing 30% ~ 40 wt% moistures, are typically difficult for recycling [1]. Foreign processing technologies for sludges treatment are relatively advanced including cold-bonded agglomerates for blast furnace, RHF reduction for the dusts and sludges with high content of Zn and Pb, smelting and reduction. Domestic iron and steel companies use a small amount of sludges in sintering. However, the sludges have the characteristics of high moisture and containing harmful impurities, which directly affect the sintering mixture permeability and product quality [2-5]. There are also other technologies such as production of metallized pellets, cooling agents for steelmaking, etc [6]. All of these deficiencies and applied are not in large-scale."

Jan 1, 2011

By Gordon A. Irons

"Powder injection for melt refining is widely practiced in the steel industry, and is gaining acceptance in the non-ferrous industries. In these commercially-important systems, the thermodynamics and kinetics may be very complicated. More than one element may be removed by refining, and often the refining agents are not just one compound. In this paper, the thermodynamic and kinetic aspects of these processes are reviewed. A number of examples are given, such as the desulphurization of iron with a variety of reagent mixtures, and selenium removal from copper with several different reagent combinations.IntroductionI am very pleased and honored to present a paper at this Symposium recognizing the many contributions of Professor Howard Womer. Even at the time I was an undergraduate student, the WORCRA process was part of the curriculum. I remember at the time that I was fascinated by the concept, and due to it and the many other rapid developments in Process Metallurgy, I chose it as my field of study. I think the Symposium is testimony that Professor Womer has touched the lives of many others as well.My original assignment was an overview of the basic aspects of gas and solids injection. However, I reviewed most of this material at the Savard/Lee Symposium [1]. In the present paper, I will present some of the basic issues related to refining with powder injection, using work that we have recently completed in both ferrous and non-ferrous systems."

Jan 1, 1996

By C. M. F. Vieira

Crushed fired brick waste, known as grog, screened at two different particle size, 840 (20 mesh) and 180 µm (80 mesh), was used in mixtures with clayey body to make typical red ceramics for bricks. The effect of the grog addition up to 20 wt.% on the properties of bricks fired at 700oC was evaluated. The results indicated that both the particle size and the amount of grog addition changed the fired properties of the clayey body. Additions above 5 wt.% of grog, with a coarser particle size, decreased the mechanical strength of both the dry body and the fired ceramic pieces. By contrast, grog with a finer particle size may be used up to 10% wt. without deteriorate the properties and corresponding microstructure of the clayey body.

Jan 1, 2009

By Michael A. Lllga

Electrically Switched Ion Exchange (ESIX) is an approach for ion separation that combines Ion exchange (IX) and electrochemistry by utilizing electro active IX films to provide a selective, reversible, and economical separation method that greatly reduces secondary waste generation compared with conventional ion exchange. Studies on the development of films with improved stability and capacity and their use in continuous flow systems for ion separations will be. reported. Both technical and economic evaluations demonstrate ,the viability of once-through or batch recycle waste processing with ESIX.

Jan 1, 1999

By Anja Pfennig, Thomas Böllinghaus, Marcus Wolf

During CCS components are exposed to a corrosive environment and mechanical stress which results in corrosion fatigue and is inevitably followed by the lifetime reduction of these components. The lifetime reduction of the cyclically loaded high alloyed stainless injectionpipe steel AISI 420C (X46Cr13, 1.4034) constantly exposed to highly corrosive CO2- saturated hot thermal water is demonstrated in in-situ-laboratory experiments (T = 60 °C, brine: Stuttgart Aquifer, flow rate: 30 l/h, CO2) in an environment similar to the on-shore CCS-site in the Northern German Bassin. In-situ tension-compression experiments were established simultaneously along with electrochemical measurements using a newly designed corrosion chamber in a resonant testing machine at a frequency as low as 30 – 40 Hz. In addition technical CO2 was introduced into the closed system at a rate close to 9 L/h. S-N plots, micrographic analysis and surface analysis of the fracture surface are demonstrated. X46Cr13 (surface roughness Rz = 4) reached the maximum number of cycles (12.5 x 106) at stress amplitude of 173 MPa producing a low scatter range of 1:3.5. Hydroxide and siderite layers were found on pits and crack surfaces. No typical fatigue limit exists. Pit corrosion prior to crack initiation may be identified as failure cause.

Jan 1, 2016

By N. Kanari

The thermal decomposition studies of two zinc basic carbonate samples were carried out up to 400 "C by thermogravimetric analysis, boat experiments and differential scanning calorimetry measurements 'DSC'. The initial samples and the solid decomposition products were analyzed by scanning electron microscopy, x-ray diffraction and laser particle size analyzer. The thermal decomposition of both samples started at about 150 "C and the rate of decomposition became significant at temperatures higher than 200 "C. The apparent activation energies 'Ea' in the temperature range 150-240 "C for sample decomposition were between 132 and 153 kJ1mole depending on the sample origin. The XRD analyses of the intermediately decomposed samples and the DSC results up to 400 "C suggest that the decomposition reaction probably occur in a single step.

Jan 1, 2002

By Anja Pfennig, Axel Kranzmann, Sabrina Schulze

The CCS technique involves the compression of emission gasses in deep geological layers. To guarantee the safety of the site, C02-corrosion of the injection pipe steels has to be given special attention when engineering CCS-sites. To get to know the corrosion behaviour samples of the heat treated steel 1.7225 42CrMo4, used for casing, and the stainless injectionpipe steel 1.4034 X46Cr13 were kept at T=60 °C and ambient pressure as well as p=lOO bar for 700 h - 8000 h in a C02-saturated synthetic aquifer environment similar to possible geological on-shore CCS-sites in the northern German Basin. The isothermal corrosion behaviour obtained by mass gain of the steels in the gas phase, the liquid phase and the intermediate phase gives surface corrosion rates around 0.1 to 0.8 mm/year at ambient pressure and much lower about 0.02 to 0.2 mm/year at 100 bar where the C02 is in its supercritical state. Severe pit corrosion with pit heights around 4.5 mm are only located on the 42CrMo4 steel. Main phase of the continuous complicated multi-layered carbonate/oxide structure is siderite F eC03 in both types of steel.

Jan 1, 2013

By Yury Kapelyushin

Formation of cementite in the reduction of hematite by CO–CO2 gas was studied in situ using high temperature XRD (HT XRD) analysis. Reduction of hematite was examined in the temperature range 873–1173 K by CO–CO2 gas mixture with high carbon activity. When carbon activity in the system was 1.5, cementite was formed only at 1023 K; it was not observed in experiments at 973, 1073 and 1123 K. Formation of cementite was observed at 923–1073 K when carbon activity increased to 3–5; and at 873 K when carbon activity was 10. Formation of cementite at 973–1073 K proceeded through metallic iron; however, in the reduction of hematite at 873 and 923 K, iron was not observed; cementite apparently was formed directly from wüstite. XRD spectra were used to estimate concentration of carbon in austenite in the process of cementite fromation.

By M. El Ganaoui, P. Bontoux

"A computational model to investigate solid/liquid phase change transitions for binary alloy under directional solidification is presented. Conservation equations are developed by using an homogeneous formulation. A second order accuracy method of time and space based on finite volume approximation has been evaluated by comparing results to spectral solution for time-dependent solutal convection developping in a melted alloy. For extended model to solid/liquid interface effects time amplification of solutal perturbation injected near the interface is described before considering solutal convection is melt.IntroductionThe enthalpy method gives a front fixing approach for energy equation without introducing coordinate transformation. The interfare position is recovered a posteriori [1]. A number of authors have extended this approach so as to include the convection phenomena within the two phase 'mushy region' [2, 3, 4, 5, 6].We have developed a time-dependent enthalpy-porosity formulation for directional solidification [4, 6, 8]. The interaction between solid and liquid phases is modelised by a Darcien type force in the phase change area. The behaviour of the melt is similar with the flow of an incompressible fluid in a porous medium. This force is proportional to the relative phase velocity. It corresponds to a damping force depending on the anisotropic permeability of the 'mushy zone'. The permeability depends on the liquid fraction and on the size of·solidification microstructures. An informative discussion of a new slant on the general approach of continuum mechanics needed to analyze the formation of mushy zone is given in [12]. The method is extended to the presence of species diffusion: the solutal Stefan condition which expresses the solute incorporation or rejection across the interface is accounted implicitly in a species equation valid in all the domain [14, 15]."

Jan 1, 2001