By J. V. Happ

The investigation reported in this paper was prompted by the belief that vacuum processing of copper mattes could provide significant advancement to present-day copper smelting and converting technology. Specifically, vacuum distillation of copper mattes in a unit such as the R.H. vessel used in vacuum degassing of steel, can lead to improvements in: converter flue-gas-cleaning system, purity of acid (or liquid SO2), aisle hygiene, purity of electrorefined copper and smelter flexibility. In the study conducted, removal of Volatile impurities (arsenic, antimony, bismuth, lead and zinc) from liquid mattes, by vacuum distillation in a laboratory-scale equipment was performed. The conditions investigated covered a temperature range of 1123-1223K, absolute pressure of 6.5-0.5kPa (50 - 3 mm Hg) and with bleed gas consisting either of pure oxygen or argon. Six matte samples (four U.S. and two foreign) were tested. Under the "best" conditions arsenic and antimony were reduced to << 0.01% in the product matte. The removal of bismuth, lead and zinc was variable and appeared to be influenced by the matte composition of the sample. As might be expected, the rates of distillation of the various species were increased at higher temperatures and lower absolute pressures. The influence of a small flow rate of gas (02 or Ar) over the melt did not have a signifi¬cant influence on the extent of impurity removal. The magnetite content of the matte was reduced by up to 30% during vacuum treatment and was favored by a low partial pressure of oxygen over the melt. Substantial amounts of sulfur were also evaporated and an, overall increase in copper grade of the matte was realized. The paper concludes with an evaluation of industrial aspects of the process as applied to conventional smelters.

Jan 1, 1983

By Daojin Cao

The chemical components in the saturated aqueous solution of ammonium dimolybdate (ADM) were investigated at room temperature by comparative Raman spectroscopy. In order to explore the further detailed results, a new method of qualitative and half quantitative analyses, based on the main vibrant frequencies and the intensity ratio of the strongest peak to the second strongest peak recorded in Raman spectrum of saturated aqueous solution of ammonium heptamolybdate tetra hydrate (AHM), was put forward and attempted to analyze the chemical components of saturated aqueous solution of ADM. The results showed that there was obvious difference between Raman spectrum of saturated aqueous solution of ADM and that of ADM, but there were good relationships between Raman spectrum of saturated aqueous solution of ADM and Raman spectra of the three samples including AHM, the saturated aqueous solution of AHM and monomolybdate ion in aqueous solution. It was found that aggregated dimolybdate ion ({Mo2O72-}n)did not exist in the saturated aqueous solution, and was changed into heptamolybdate ion (Mo7O246-) and monomolybdate ion (MoO42-), which were in equilibrium each other, but the distribution ratio of heptamolybdate ion was larger than that of monomolybdate ion. In addition, Raman spectral pattern of saturated aqueous solution of ADM was reported.

Jan 1, 2006

By Yanlong Li, Lifeng Zhang, Ying Ren

In this work, a multiphase mathematical model for the fluid flow in argon-stirred steel ladles was established and validated by experimental measurement of wood's metal. Alloy dispersion in the molten steel was calculated. The melting and mixing of alloy was faster with smaller size of the alloy particles, larger superheat and bigger slip velocity. The current mixing time is approximately 300 s with 30 mm alloy diameter and 91.5 K superheat.

Jan 1, 2014

By James R. Myers

A source of clean gas containing sulfur dioxide and sufficient oxygen for conversion to sulfur trioxide is essential to the production of sulfuric acid. SO2 containing gases obtained from roasting sulfide ores are heavily contaminated with inorganic dust and volatile impurities. If not removed, these contaminants will reduce product acid quality, foul the catalyst beds and mist eliminators, and accelerate equipment corrosion. This paper reviews conventional gas cleaning systems for metallurgical acid plants, followed by a discussion of modern systems utilizing DynaWave Scrubber technology. This technology is based on a unique approach togas scrubbing that can concurrently accomplish several gas cleaning/processing tasks. Scrubbing liquid is injected into the gas stream to create a "Froth Zone". This is a region of extreme turbulence, with a very high rate of liquid surface renewal. It efficiently removes both particulate matter and gas contaminants, and is also a cost effective quenching device for gases as hot as 1250 o C.

Jan 1, 1992

By WenCai Li, Yong Ren, Shuai Niu, Xin Hong

"Temperature measurement is very important in metal smelting process. Many devices are used to realize non-contact temperature measurements. Compared to conventional thermocouple, infrared temperature measurement has it's unique advantages. However, using an infrared temperature measurement at the top of the furnace can not obtain the desired optical signal because of disturbance from slag layer, high-temperature gases and other effects. A real time thermometry system with dual-wavelength radiation was presented to get optical signal emitted from molten metal through bottom-blowing nozzle. Taking into account the advantages and disadvantages of bottom-blowing devices, a MHP (Multiple Hole Plug) bottom-blowing device was used, through which the optical signal was transferred to the infrared thermometer by use of optical fiber. After conversion and analysis in real-time, the result was displayed and recorded in computer. After calibration, it could be a good predictor of temperature trend in a metallurgical process. IntroductionAt the refining stage of steelmaking, in order to achieve predetermined chemical composition and temperature, high-temperature molten steel is refined in a furnace such as converter. Because the refining process involved with chemical components and reaction velocities in the furnace rely on the temperature of steel, it is necessary to know the temperature accurately in real time during the process. And temperature measurement is also helpful for the end-point judgment. The temperature in the refining process changes quickly, for instance, in a converter, 300t molten steel is processed in only about half an hour.At present, traditional way of temperature measurement is using a thermocouple probe mounted on a lifter called a sub-lance. The thermocouple is immersed in molten steel and its temperature is measured during the short period until the thermocouple is fused. Accurate and reliable temperature can be obtained by this method, but in consideration of the discontinuous measurement and the costs, missing the end-point temperature may sometimes occur.According to the above background, a method in which a temperature-sensing element such as a thermocouple is immersed directly in molten steel is not suitable for the continuous temperature measurement because materials having such stability are not available. Therefore, radiation thermometry is promising. There have been some reports on radiation thermometry through an observation nozzle through the bottom or side of a refining furnace [1, 2]."

Jan 1, 2014

By A. von Röpenack

A forecast of the consequences of our techniques and goods produced, at least a technical assessment will be demanded from us as an industry. The hydrometallurgical winning of zinc is therefore at a crossroads. New processes promise not only better economics, better maintenance of resources and simpler operation, but also more harmony with nature. Pressure leaching promises to eliminate roasting and thus one complete process step. The hematite process solves a difficult and always costly iron problem. HOA opens a possible road to a totally new ,generation of electrolysis. Zinc has a long tradition behind it. Its? importance is as great as ever-. There is still room for new production developments. In my estimation there are good chances for successful new techniques? which will benefit our whole industry. Zinc is a modern and forward-looking metal.

Jan 1, 1990

By Liangying Wen, Xuewei Lv, Yuelin Qin, Feng Zhu, Guibao Qiu, Chenguang Bai, Meilong Hu, Shengfu Zhang

"The COREX process is the first reduction ironmaking technology with coal and pure oxygen to get high quality hot metal, which consumes a lot of high quality lump coal and some coke. In order to increase the utilization of fine coal, reduce coke consumption and enhance the competitiveness of the technology, the combustion behavior of pulverized coal injection in melter gasifier is studied experimentally. The results show that the combustion rate of PCI increases with the increase of temperature. And the combustion rate increases with decreasing coal particle size. Compared bituminous coal with anthracite, the former’s burning ratio is higher than the latter in the same granularity. The combustion effect is remarkable when coal blend of bituminous coal and anthracite with the smaller particle size is pulverized in COREX process.IntroductionThe COREX process is the first reduction ironmaking technology with raw coal and pure oxygen to get high quality hot metal, which consumes a lot of high quality lump coal [1-3]. However, the proportion of lump coal in raw coal is very small, and it is avoidless to produce fine coal because of mechanical coal cutter and storage and transportation process, so it is important to resolve utilization of fine coal in COREX ironmaking process in order to energy conservation and reduce the cost of hot metal [4]. Currently, Coal briquetting technology is adopted to utilization of fine coal in COREX process [5], but coal briquetting system has high investment cost and requires feasible adhesive agent. The pulverized coal injection (PCI) into a blast furnace is being used on a global scale to improve the stability and reduce the cost of blast furnace operations [6]. The successful development of PCI in blast furnace is contributed to pulverized coal in COREX melter gasifier. However, it is different in PCI process between COREX melter gasifier and blast furnace, and the differences are as follows: firstly, The air is injected into blast furnace, which temperature is about 1200 ?, but in COREX melter gasifier the normal temperature oxygen is blasted, so PCI in blast furnace begin burning in blowpipe, but the combustion of PCI in COREX melter gasifier is only in raceway. Secondly, the racway of COREX is smaller than that of blast furnace of the same size. So, the combustion behavior of PCI is complex in COREX melter gasifier, which is not use for reference."

Jan 1, 2012

By Li. Jiarong, Zuojian Liang, Qingyan Xu, Baicheng Liu, Shizhong Liu, Hailong Yuan

Single crystal solidification of turbine blades is a key technology for the production of reliable and high efficiency gas turbines. The solidification process of single crystal investment castings causes a number of problems that have to be solved such as the increase of casting defects and complexity of production process. Computer modeling and simulation is helpful to predict the defects and improve the process design. In the paper, a mathematical model for three dimensional simulation of solidification and single crystal growth of investment castings was developed based on CA, mechanism of crystal growth and basic transfer equations such as heat, mass transfer equations. Many factors including constitutional undercooling, curvature undercooling and anisotropy, which had vital influences on microstructure evolution, were considered in the model. Temperature, crystal growth interface and structure defects of investment castings of single crystal superalloy were investigated at withdrawal rates of 4.5mm/min and 7mm/min. Simulated results showed that microstructure evolution and structure defects were predicted reasonably and calculated results were coincident with experimental ones. The study indicated that three dimensional solidification simulation technique is a powerful tool for understanding the fundamental of solidification and the formation of structure defects in single crystal investment castings and finally for optimizing process design.

Jan 1, 2004

By Girley Ferreira Rodrigues, Crocce Denise Romano Espinosa, Victor Bridi Telles, Eduardo Junca, Jorge Alberto Soares Tenorio

"Steel sector is responsible for the generation of solid waste, liquid and gaseous effluents. The Solid waste are mainly composed of slag, dust, sludge and scrap. The industry generates approximately 650kg of solid waste per tonne of steel. Approximately 10% of this waste is in the form of dust and mud. The basic oxygen furnace dust is a waste generate by steel sector. Each tonne of produced steel generates 10 to 20 kg dust. Thus, the aim of this paper is study the reduction of pellets made with BOF dust using hydrogen and study kinetic during the reduction. The tests were performed in a netzsch thermobalance to obtain the data of lost mass. This loss mass is coming from iron oxides present in the BOF dust.IntroductionThe generation of solid waste is a problem for many companies in the steel sector. The main solid wastes generated are slag, dust, sludge and scrap [1]. Beyond solid waste liquid and gaseous effluents are also generated.The basic oxygen furnace is responsible for 60% of all steel produced. This sector is the second largest generator of solid waste from an integrated steel mill, contributing with 27% of solid waste generated in a plant ( 5-7 million tons of waste generated annually worldwide) [2,3,4]."

Jan 1, 2013

By C. A. Morais

The present work describes the development of an efficient and relatively simple process to obtain high grade CeO2 from a mixed rare earth chloride solution. The process involves cerium oxidation and precipitation by addition of a KMnO4-NaCO3 solution. The experiments were carried out at room temperature (25 1° C). The results indicated that the major parameters affecting cerium recovery are the molar ratio of KMnO4/Ce, the initial acidity of the chloride feed solution and final pH of Ce(OH)4 precipitation. In strong acid solutions (pH < 1), the oxidation of Cl to Clo took place in addition to the oxidation of Ce(III) to Ce(IV), so increasing the permanganate consumption. Conversely, low acidity (pH >3) led to coprecipitation of the other rare earth elements. Under the selected conditions, cerium was selectively precipitated as ceric hydroxide, together with some manganese dioxide. Further purification was carried out by the dissolution of Ce(OH)4 in HCl, followed by precipitation as cerium carbonate. The filtrate was neutralised with a Na2CO3 solution in order to recover the associated rare earth elements for further separation. The final product, assaying 99.7 % CeO2, was obtained with a recovery of nearly 100%.

Jan 1, 2003

By S. Fitzel

The Betts process for electrorefining of lead has been in operation since 1902 in the Trail Operations Metallurgical complex. The Betts process allows production of high purity lead in a single electrochemical step. Process improvements and plant expansions have taken place over the many decades of operation of this process which has proven to be robust, flexible, and capable of successfully treating a large range of anode bullion compositions. This paper reviews the history of the Betts lead electrorefining process, the innovations and quick industrial adoption of new discoveries that took place at the end of the nineteenth century. The process was first implemented in Trail Operations and integrated very well with metallurgical needs then and now.

By Liang Li

Thermodynamic analysis and experiments were conducted in order to verify the feasibility of preparing crude titanium tetrachloride (TiCl4) via the carbochlorination of low-grade titanium slag in molten salt. Titanium slag, assaying 74.6 wt% TiO2 with high calcium and magnesium oxide impurities, was treated by an optimized carbochlorination process in NaCl molten salt. These impurities in the titanium slag were chloridized simultaneously, and chlorination products FeCl2, MnCl2, MgCl2, CaCl2 and CrCl3 were collected in the furnace slag. XRD and SEM/ EDS analysis of residue shown that SiO2 and Al2O3 in titanium slag were difficult to chlorinate completely. Theoretical calculations and industrial-scale experimental studies reveal the content of TiCl4 in the products was more than 98.8 wt% and thus proved the feasibility of utilizing low-grade titanium slag for TiCl4 preparation by molten salt chlorination technology.

By Masayoshi Matswnoto

The Kosaka Smelter and Refinery produces copper and lead, and has a history of more than 100 years as a metallurgical department of Dowa?s Kosaka Mine. The Smelter treats complex sulfide concentrates which are difficult to smelt. Valuable metals are recovered using various processes developed by Kosaka Smelter and Refinery. Effluent waters from the smelter contain large quantities of heavy metals. This paper describes how Kosaka Smelter and Refinery recovers valuable metals from various effluent waters and handles overall waste waters in order to meet strict environmental standards.

Jan 1, 1993

By Xiang Sun, Zheng Zhang, Jiann-Yang Hwang, Zhiwei Peng

"Nickel oxide nanoparticles were synthesized using sodium dodecyl sulfate as the surfactant and urea as the hydrolyzing agent and different calcination temperatures and time were selected for preparation. Nitrogen adsorption (BET), X-ray diffraction (XRD) and scanning electron microscope (SEM) were subsequently used to characterize the prepared samples. The effect of an external electric field on hydrogen adsorption over a prepared nickel oxide was carried out. The electric filed was introduced by a piezoelectric element, which is capable of autogenously generating charges under hydrogen pressure. Increased hydrogen adsorption was obtained from this study, which indicated a stronger interaction between the adsorbent surface and hydrogen.IntroductionMetal oxide has attracted great attention for adsorption because of their wide application in catalysis [1-7], gas storage [8,9] and sensors [10,11]. However, with respect to the usage in hydrogen adsorption, few research outcomes have been reported [12,13], since there remains the difficult task of synthesizing highly porous metal oxides with unsaturated metal centers, which account for the strong interaction with hydrogen [14,15]. Nickel oxides are polar materials with an intrinsic dipole moment. The external applied electric field could further enhance the dipole moment so that the hydrogen could be more strongly adsorbed."

Jan 1, 2012

By Shinya Hodoshima

A catalysis pair of tetralin dehydrogenation / naphthalene hydrogenation has been proposed in the present paper as a liquid organic hydride for operating stationary fuel cells. Catalytic naphthalene hydrogenation, having been commercialized since the 1940s, proceeds to generate decalin via tetralin as an intermediate. The storage capacities of tetralin (3.0 wt%, 28.2 kg-H2 / m3) are lower than decalin (7.3 wt%, 64.8 kg-H2 / m3) but both tetralin dehydrogenation and naphthalene hydrogenation are much faster than the decalin / naphthalene pair. Moreover, existing infrastructures such as gas stations, chemical tankers and tank lorries are available for storage, transportation and supply of hydrogen. With respect to the stationary fuel cells with large space for hydrogen storage, tetralin as a hydrogen carrier is superior to decalin in terms of fast hydrogen supply or power density. Rapid hydrogen supply from tetralin under mild conditions was only accomplished with the carbon-supported metal catalysts in the ?superheated liquid-film states? under reactive distillation conditions. In contrast to the ordinary suspended states, the catalyst layers superheated in the liquid-film state gave high catalytic performances at around 250OC. As a consequence, both serious coke formation over the catalyst surface and excessive consumption of exergy were prevented simultaneously.

Jan 1, 2006

By Ping Long, Bin Yang, Jian Wu, Xiumin Chen, Wenli Zhang

In this study, the analysis method of trace element in pure indium using glow discharge mass spectrometry (GD-MS) has been established by correcting the analysis result, which was obtained from non-standard quantitative method of GD-MS. The effect of instrument operating parameters, the resolution and isotopes and the pre-sputtering time on the determination results were investigated respectively. The optimized operating parameters of the instrument were obtained as follows: the discharge current was 37.5mA and discharge airflow was 475ml/min. Mass spectral interferences have been eliminated using selected resolution and isotope. The pre-sputtering time was 30 min. 4 trace elements in two pure samples were determined for 6 times. The RSD were less than 20%. The content of trace elements in indium samples was determined by GD-MS and Chemical Analysis Method of Indium which is tested by inductively coupled plasma atomic emission spectrometry, respectively. The results were consistent with each other.

Jan 1, 2016

By Helfried Nafe

"For about a century thermodynamically absurd facts have been propagated in conjunction with the iron-carbon phase diagram. These facts concern fundamental relationships of chemical thermodynamics. Attention is turned here to the discussion of only one of the relevant aspects of the subject, i.e. the definition of the thermodynamic activity of the solute and its implications for the iron-carbon solution.IntroductionThe view on the iron-carbon solution is characterized by the assumption that the solute may appear in two different forms, i.e. graphite and cementite. Accordingly, two carbon solubilities are differentiated, on the one hand for graphite and, on the other hand, for cementite. As a consequence, two versions of the phase diagram exist simultaneously, the application of which depends on the prevailing conditions, (i) the so-called stable phase diagram with graphite as solute and (ii) the metastable one that is based on the cementite-in-iron solution. These diagrams are joined together in the double phase diagram that originates from Heyn [l ], with the first ideas mainly going back to Stansfield [2] and Charpy [3].Thermodynamically, the most inadequate implication of the Fe-C double phase diagram is that the carbon activity may take values larger than unity. With the standard state of the activity being that of the pure substance, i.e. the Raoultian one, such a value implies the nonsensical existence ofa state purer than pure. The explanation of this physical state, ifthere is any, vaguely refers to supersaturation and, in the wider sense, to the physico-chemical phenomenon of metastability. Other aspects of chemical thermodynamics are likewise involved. Therefore, the comprehensive investigation into the present subject requires more topics to be considered than only one separate issue. Not only should the criticism of the present view be in the focus but also the discussion of new ideas capable of reconciling the experimental facts, known about the F e-C system, with the fundaments of chemical thermodynamics. All this, however, cannot be provided here because of the limited space available. As a consequence, in what follows only a part of the whole problem is under scrutiny, i.e. the definition of the thermodynamic activity and its role for the interpretation ofrelevant experimental facts."

Jan 1, 2014

By Minh H. Pham

This paper presents a technique for imaging the extent of solidification of molten metal flowing in a cooled pipe based on the concept of eddy currents. A 3D mathematical model, which relates the geometry of solidification to the scattered field induced in a solenoid external to the pipe, is derived. The model is described by a set of integral equations which are solved numerically using the moments method. An iterative algorithm is developed to reconstruct the solidification distribution image. Experimental measurements have shown that the eddy current technique is sufficiently sensitive for practical purposes.

Jan 1, 2001

By C. J. Newman

In January 1999, a redesign of the Kennecott Flash Converting furnace settler was initiated to enhance furnace integrity and extend furnace life. This furnace uses Kennecott-Outokumpu Flash Converting technology to produce copper directly from copper matte. A detailed assessment was made of all technology available around the world before making a decision on the design features to be incorporated in the new design. The new design includes the following: redesign of all sidewall cooling elements to include the latest cooling element technology; redesign of the furnace hearth to include a stadium hearth at the reaction shaft end of the furnace; redesign of the furnace hearth to include a stepped hearth design adjacent to the furnace sidewalls; addition of flat settler roof cooling elements .around the reaction shaft; replacement of reaction shaft transition elements with an improved design and improvements to the furnace cooling element monitoring systems. The Flash Converting furnace was shut down on a planned basis in July 2001 to implement these improvements after 29 months of operation, converting more than 1,000,000 tonnes of matte. During the 30 day shut down, the improvements were successfully completed, with furnace start up in August 2001

Jan 1, 2002

By T. Lezhava

A new reactor model with rotating cathodes has been developed where various forms (dendrite, spongy) of metal depositions and their uninterrupted removal are accomplished by the realization of high current densities and low energy consumption. At the same time in contrast with the existing methods a high quality metal powder may be obtained from concentrated electrolytes without any specific organic or inorganic additives, which allows raising the intensity of the process. The reactor can be used for electrowinning of metals with low adhesive capacity (Pb, Ag, Cu, Zn, Ni, Co, etc.) and the powders. The obtained products may be utilized in general metallurgy as well as in powder metallurgy.

Jan 1, 2006