By Du Sichen, S. Seetharaman, Wei Liu

"The viscosities of two-phase mixtures are of great importance in the modelling of the fluid flow in metallurgical processes. For example, in steel making and refining, the intimate mixing of metal droplets in the slag phase requires a consideration of the effective viscosities for the mixture. The present work was aimed at an understanding the phenomena underlying the viscous flow in a two-phase mixture with widely differing viscosities.Emulsions of silicone oils of known viscosities (345mPa.S and 1010mPa.S at 293K) with small amounts of water evenly distributed in the same were prepared by subjecting the mixture to uniform stirring using a magnetic stirrer. The viscosities of these emulsions were measured at constant temperature by rotating cylinder method using Brookfield Digital Rheometer. The uniformity of the preparation of the emulsions was confirmed by the reproducibility of the results. Th7 measured viscosities were generally found to be independent of the torque under the experimental conditions so that the two-phase mixture could be considered as a Newtonian liquid. The variation of viscosities with temperature and the effect of addition of a surface-active substance were also studied in this work.The measured viscosities were found to be· higher than those of both pure water and silicone oil. The experimental viscosities were found to increase with increasing concentration of water. The influence of surface tension on the viscosities was examined by adding surfaceactive agent to the mixtures. The result is discussed and compared with theoretical models developed by Einstein, Taylor and Oldroyd."

Jan 1, 2000

By Lucas Lopes da Costa, Sergio Neves Monteiro, Rômulo Leite Loiola

"Composites with DGEBA/TETA epoxy matrix reinforced with thinner and continuous bamboo fibers stripped from culms were mechanically characterized by tensile tests. Specimens with up to 30% in volume fraction of aligned fibers were tensile ruptured at room temperature. The results showed a steady increase in both the ultimate strength and the elastic modulus of the composites with the amount of incorporated bamboo fibers. The fractographic analysis by scanning electron microscopy showed evidence of moderate adhesion between the bamboo fiber and the epoxy matrix. This fiber/matrix adhesion by interaction mechanism apparently justifies the improved tensile properties of the composites.IntroductionIn recent years polymer composites reinforced with natural fibers, mainly those lignocellulosic obtained from plants, have been subject to extensive research works [1-5]. Environmental, economical, societal and technical advantages of these composites are motivating their substitution for similar polymer composites reinforced with synthetic fibers. In particular, R & D efforts have been conducted aiming to replace glass fibers composites that are comparatively more abrasive to equipments, non-recyclable, more expensive, heavier and toxic [6]. Among the many lignocellulosic fiber composites being investigated, those fabricated with bamboo stripped fibers, i.e., fibers longitudinally cut from the culm, still need information to support possible industrial applications. Several works, however, have been dedicated to bamboo stripped fibers as possible reinforcement of polymer composites [7-17]. These works reported mechanical properties that could markedly vary with the type of polymer matrix, the fiber disposition (if continuous, aligned, short-cut, mat interlayered, etc) and the test condition."

Jan 1, 2011

By Mariola Saternus

The quality of the liquid metal has the biggest influence on the quality of the final products. In the metallurgical industry, and especially in aluminium production the refining process is the important technological stage. Today the most popular are refining reactors with impellers like URO ? 200, which can generate small gas bubbles. A rotary impeller also makes the metal bath to be stirred well. There are two basic hydrodynamic parameters: the flow rate of refining gas and the mixing of refining gas (impeller rotation) that influence metal stirring and generating small gas bubbles. The paper presents the influence of the flow rate of refining gas on the hydrogen removal process from aluminium (final hydrogen concentration), taking into consideration the refining process of AlSi7Mg alloy and using URO - 200. The mathematical model of this process is also presented. The equation needed for calculation of the final hydrogen concentration as a function of the equivalent bubble diameter is shown. Basing on this equation the calculations of bubble diameter and optimal refining time are done. This paper presents the physical model (the water one) of aluminium refining process and the gas dispersion taking into account the fact that the gas flow rate is changing from 2,5 to 17,5 l/min and the impeller speed is changing from 0 to 400 rpm. Schemes of gas dispersion in liquid metal in comparison with the model data are shown and the optimal values of the gas flow rate and the impeller speed are chosen.

Jan 1, 2006

By Wayne Bell, Matthew Andriese, Shuqian Xie, Jiann-Yang Hwang, Zhiwei Peng

"Pyrolyzed carbons are generally known as good microwave absorbers and their dielectric properties still remain to be fully explored. In the present study the dielectric properties and dielectric polarization-relaxation phenomenon of a typical activated carbon was investigated. The experimental results indicate the complex permittivity is highly dependent on temperature and frequency. The decrease of permittivity with increasing temperature from room temperature to ~100 °C is probably ascribed to the release of the water vapor adsorbed on the surface of activated carbon, and the variations of permittivity with temperatures between 100 °C and 450 °C in the frequency range of 300 MHz to 3000 MHz are mainly attributed to the decreased relaxation time of dielectric polarization.IntroductionPyrolyzed carbons have been identified as excellent microwave absorbers owing to their high dielectric and electrical loss under microwave irradiations. Among them, activated carbon continues to attract more and more attention from researchers. Due to its special physical properties, the production, modification and regeneration of activated carbon with the assistance of microwave have been widely studied over the last few decades [1-6]. However, only few attempts have been applied to explore the dielectric properties of such materials due to the complexity and variability of their organic precursors and activation processes [7,8]. In order to shed a light on this problem, a typical sample, Norit® A Supra USP powdered activated carbon, was adopted to perform dielectric characterization, which may provide useful information for its wide application in the fields of purification, energy (hydrogen) storage and so on."

Jan 1, 2011

By T. Iriyama, Y. Fujita, R. Omatsuzawa, T. Nishio, N. Okochi

Sm-Fe-N hard magnetic materials are good candidates for high performance bonded magnets. Rapid-quenching method should be highly favorable for the fabrication of isotropic magnet powder with high coercivity. We report here the magnetic properties of Sm-Fe-N powders produced by a few kinds of rapid-quenching processes. Sm2Fe17 powders were prepared by gas-atomization (GA), rotating-disk atomization (RDA), or melt-spinning (MS) method. The Sm2Fe17 GA powder had dendritic solidification structure, while the RDA powder had micro crystalline structure with size of 3-5 µm. Coercivities (HcI) of their nitrides were 56 (for GA) and 217 ka/m (for RDA). The H cI of nitrided Sm2Fe17 MS powder with wheel velocity (V5) of 5-20 m/s, which had also microcrystalline structure, was 53 to 509 Wm. These coercivity values are not sufficient for bonded magnet applications. From the study of additive effects, it was found that C, C-Si, C-Ga, or C-Al addition decreased the crystal size of quenched Sm2Fe17 powder. Consequently, high coercivity was obtained; the HcI of nitrided Sm2Fe1C1Si1 MS powder with V5 of 10 m/s was 898 kA/m, and 708 kA/m for the nitrided Sm2Fe15C1Si1 RDA powder. The compression-molded bonded magnet made from Sm2Fe18Si0.1Nx MS powder showed a high (BH)max of 82.7 kJ/m3.

Jan 1, 2000

By Daniel A. Norrgran

Grinding ball fragments discharging from SAG mills and ball mills causes extreme wear to downstream processing equipment. These ball fragments, recirculating in a milling circuit, will cause excessive wear to sumps, pumps, hydrocyclones, and interconnecting piping. A magnetic separation system to remove grinding ball fragments from the mill discharge has been developed and successfully applied in the milling circuit. This magnetic separation system - termed Trammel Magnet - was first applied at the Escondida copper concentrator in Chile. The Trommel Magnet consists of an arc of permanent magnets mounted at the discharge end' of the tommel screen. The magnetic arc attracts the ball fragments and removes them from the process stream. This retrofitted magnetic separation system removed 126 metric tons of ball fragments from the circulating load of a. single ball mill in the initial 24 hour period. The mill has since stabilized and the magnetic separator is currently removing 7 metric tons per day of ball fragments. The retrofit of the Trommel Magnet has: 1. Extended the pumpp life and the hydrocyclone life approximately 300 percent. 2. Provided a 5 percent increase in the throughput of the mills by removing grinding ball fragments that contribute very little to the grinding process. Variations of the Trommel Magnet have also been developed for removing grinding ball fragments directly from the mill discharge without the use of a trommel screen. In each case, permanent magnets are used to collect the ball fragments from the mill discharge stream prior to reporting to the sump. These other systems have been designed and fabricated for in-plant test work.

Jan 1, 1999

By Lucas L. da Costa, Sergio N. Monteiro, Romulo L. Loiola, Tammy G. Rodrigues Portela

"The fibers extracted from the petiole of the buriti palm tree are relatively strong as compared to other lignocelluloses fibers, with a potential for composite reinforcement. In this work, polyester matrix composites incorporated with these fibers were investigated for their flexural behavior. Specimens with up to 40% in volume of continuous and aligned buriti petiole fibers were bendtested until rupture. The results showed an increase in both the composite mechanical strength and the stiffness with incorporation of these fibers. A fractograph analysis by SEM disclosed a moderate adhesion mechanism between the buriti petiole fiber and the polyester matrix. This mechanism is apparently responsible for the improved performance of the composites.IntroductionIn recent years, the substitution of energy-intensive synthetic materials for natural ones is being considered in many industrial sectors including automobile, packing and textile [1]. A typical case is that of natural fibers, mainly those obtained from cellulose-based plants also known as lignocelluloses fibers. They have being investigated in the past two decades, aiming to replace synthetic fibers, particularly the glass fiber, commonly used as polymer composite reinforcement [2-8]. From the engineering point of view, lignocellulosic fibers present today important environmental, economical, societal and technological advantages already discussed [7-8]. Moreover, several lignocellulosic fibers are known since the beginning of our civilization and still cultivated or naturally extracted all over temperate and tropical regions of the world. According to Kalia et al [1 ], these fibers can be classified by their origin, as shown in Table 1."

Jan 1, 2011

By Truan-Sheng Lui, Li-Hui Chen, Hao-Wen Hsueh, Fei-Yi Hung

"Since Ag wires have similar hardness and bonding properties to Au wires, they can be applied in some pads. In the present study, the annealing effect (at 225°C~275°C for 30min) on the tensile mechanical properties of silver wires with f=23µm was investigated. In addition, the micro-structural characteristics and the mechanical properties before and after an electric flame-off (EFO) process were also studied. Experimental results indicate that with annealing temperatures of more than 250°C, the silver wires possessed a fully annealed structure, the tensile strength and the hardness decreased, and the elongation was raised significantly. Under the thermal effect of EFO, the necks of the Ag balls underwent recrystallization and grain growth was induced, and the annealed Ag wires had a shorter zone of HAZ (220µm). The bonding strength and the neck-strength of the Ag wires were more than 7gf and possessed excellent bonding properties.IntroductionThermosonic ball bonding is one of the preferred processes for electronic packaging to connect a semiconductor chip and a lead frame by a thin metal wire. At present, gold wire and copper wire are the preferred interconnect materials to bond with the aluminum metallized wafer pads [1, 2]. Since gold is expensive and the reliability of copper is poorer [3], the study of silver wire has attracted a lot of attention already. In addition, the inherent properties of high ductility and low hardness of silver as well as its workability effectiveness compared to gold, have made it a preferred alternative .[4, 5]"

Jan 1, 2012

By Alwin Frei, Aldo Steinfeld, Peter G. Loutzenhiser, Enrico Guglielmini

"Using concentrated solar radiation as the energy source of high-temperature process heat, the carbothermal reductions of Al2O3 to Al and SiO2 to Si were examined thermodynamically and demonstrated experimentally at vacuum pressures. Reducing the system pressure favors Al(g) and Si(g) formation, enabling their vacuum distillation and avoiding contamination by carbides and/or oxycarbides. Exploratory experimentation in a solar reactor was performed with mixtures of charcoal with alumina and silica in the ranges of 1300-2000 K and 1997–2263 K, respectively, at 10-3 bar by direct exposure to concentrated thermal radiation. Distilled samples contained up to 19 wt% of Al in Al-Al2O3 mixtures and 79 wt% of Si in Si-SiO2 mixtures. When the reducing agent is derived from a biomass source, the solar-driven carbothermal processes are CO2 neutral.IntroductionMetallurgical extractive processes for producing Al1-2 from Al2O3 and Si3-6 from SiO2 are characterized by their high specific energy consumption and concomitant emissions. Alternatively, concentrated solar energy can be used as a high-temperature heat source to drive the carbothermal reductions and, thus, avoid greenhouse gas emissions and other pollutants derived from fossil-fuel-based processes7-12. When the reducing agent is biomass charcoal, the solar-driven carbothermal reduction is CO2 neutral. The carbothermal reductions of Al2O3 and SiO2 are represented by the simplified overall stoichiometric reactions:"

Jan 1, 2011

By L. W. Beckstead

In a conventional zinc refinery plant, zinc concentrates were roasted at 950°C. The calcine was ground and leached in a series of leaching vessels using sulfuric acid. The pH in the first leaching vessel was maintained at 2.5, while the pH of the solution exiting the last vessel was about 5.4. The leached residue typically contained (in percent) 0.1 Ag, 0.2 As, 0.7 Cd, 2 Cu, 15 Fe, 10 Pb, and 15 Zn, and it was classified as hazardous material according to the EP-toxicity test. In order to make the residue non-hazardous, and to recover most of the metal values from the residue, a brine leach process was developed. The process consisted of leaching the zinc leach residue in CaCI, brine solution at pH 2 for 1 hour at 90°C. Silver extraction was about 95 percent, while lead, copper, cadmium, zinc, and iron extractions were about 80, 50, 50, 30, and less than 0.5 percent, respectively. More extreme conditions of acidity could have been used in the leaching stage to increase zinc dissolution, but iron dissolution would have significantly increased which would have complicated subsequent recovery steps. The leached and washed residue passed the EP-toxicity leach test and could be disposed as non-hazardous. Silver, copper, and lead in the leach solution were recovered by zinc cementation, while zinc and cadmium were recovered by sulfide precipitation. The resulting solution can be recycled in the process after magnesium precipitation.

Jan 1, 1993

By Jorge A. S. Tenorio, Chuanwei Zhuo, Joner O. Alves, Yiannis A. Levendis

"Reduction of combustion-emitted greenhouse gases, which are associated with global warming, may be achieved by use of CO2-neutral alternative fuels, such as bio-ethanol. Distillers Dried Grains with Solubles (DDGS) are the main co-products of the com-grain-based ethanol industries. In 2009, the North American production of ethanol from com was about 38 billion liters, which generated approximately 31.5 million tons of DDGS. Samples of DDGS were pyrolysed at temperatures of 600-1000 °C in a two-stage laminar-flow horizontal furnace, and a catalyst system was used to synthesize nanomaterials. This work presents a microstructural characterization of these nanomaterials by scanning electron microscopy (SEM) and transmission electron microscopy (TEM). Results showed that the nanomaterials produced from pyrolysis of DDGS were in the form of long, entangled, rope-like structures with rugged walls, lengths in the tens of microns, and axially non-uniform diameters in the range of 100-300 nm.IntroductionThe interest in ethanol has increased considerably worldwide due to the necessity of finding renewable and cleaner energy resources [1, 2]. According to the Renewable Fuels Association (RF A), the world ethanol production in 2008 was approximately 65.7 billion liters (17.3 billion gallons), which figure represented a 24% increase in the production over that in the previous year [3]. The major producers of ethanol are the USA and Brazil, which together account for 90% of world production. The main feedstock for ethanol in USA is com grain, whereas sugarcane predominates in Brazil [2-4]."

Jan 1, 2011

By Naixiang Feng, Shaohu Tao, Zhihui Wang, Yuezhong Di

"A novel vacuum aluminothermic reduction lithium process was developed in present work which used lithium carbonate, alumina and calcium oxide as raw material. The process mainly contained three steps. The first step is that LiA102 clinker is prepared in ambient environment, then metal lithium is vacuum extracted from LiAl02 clinker with aluminum power as reducing agent, and the last step is that alumina is leached from the reduction residue with a mixture of sodium hydroxide and sodium carbonate. The results show that the lithium reduction ratio can be over 95% under the conditions of reduction temperature 1423K, reduction time 3h, and aluminum excess 20%. The main components of reduction residue are CaO· Al203 and 12Ca0·7Alz03. The alumina leaching rate of calcium aluminate in residue is over 80%. High-whiteness aluminum hydroxide can be obtained by carbonation precipitation of the reduction slag leaching solution.IntroductionWith a density about half of water, lithium is with the lowest density of all solids, mere 0.5 g/cm3 at 20 °C [l]. Lithium is widely used in aerospace, aviation, nuclear-generated power and electric battery industry. Nowadays, over 90 % of the world's primary lithium is produced by molten salt electrolysis [2-4]. But the development of molten salt electrolysis will be effected by some factors: cost, environment, and so on. Vacuum thermal reduction may be used extensively in future because of its low-energy consumption, high-purity and short-cycle."

Jan 1, 2013

By Guohua Bai, Mingjun Rao, Jianchen Lim, Guanghui Li, Tao Jiang

"By using thermogravimetry, optical microscope and chemical phase analysis, the solid-state reduction of carbon-burdened chromite pellets in the absence and presence of additives were investigated. The effects of reduction temperature, reduction time and additives on the metallization of chromite pellet were studied. The results indicate that the pre-reduction ratio of carbon-burdened chromite pellets is improved with the increase of reduction temperature and the addition of additives. The metallization of chromium is increased from 63.9% to 92.8% at 1300 °C for 4h with the addition of 2 wt.% of sodium borate. Investigation suggests that the reduction of carbon-burdened chromite pellets is diffusion controlled. The apparent activation energy without additive is 192.1 kJ/mol, while it decreases to 170.4 kJ/mol in the present sodium borate.IntroductionFerrochrome is used to produce high strength, corrosion resistant, wear-resisting, high temperature resistant and oxidation resistant special steels, and it is becoming one of the most important alloy materials for the production of stainless and high alloying ferritic steels [1-5]. Demand for ferrochrome is steadily on the rise due to the growth of stainless steel industry. Nowadays, more than 80% of the world's ferrochrome is utilized in the production of stainless steel [6-7].Ferrochrome is mainly produced in submerged-arc furnaces (SAF) with chromite lump ore. However, lump ore merely accounts for 20% of the chromite ore output, while fine ore (< 8 mm) accounts for about 80% [8]. Therefore, agglomeration of chromite fine ore is necessary before charging into SAF."

Jan 1, 2011

"Hematite pellets were electro-deoxidized to iron in molten sodium hydroxide to produce iron containing about 10-wt % oxygen. The anodic reaction was the evolution of oxygen on an inert nickel anode. Before the electrochemical reaction, there is a reaction between sodium hydroxide and ferric oxide to form sodium ferrite and, in order to compensate for the reduction in sodium oxide content, 1 wt % sodium oxide is added to the melt. In a laboratory cell, the cell voltage was 1.7 V with a current density of 5000 A m-2, a current efficiency of 90% and an energy consumption of 2.8 kWh kg-1.Introduction The iron and steel industry contributes about 2.3 bn tonnes/annum of the carbon dioxide to the atmosphere, which is about 10% of the total, and some believe that, in order to prevent a catastrophic rise in the earth’s temperature, carbon dioxide emissions must be reduced by 50% come 2050. However, by 2050, it is likely that the iron and steel industry would have grown significantly so that the production may have risen to 2 or 3 bn tonnes/year so in order to meet the 50 % reduction on today’s figure, the carbon dioxide may have to be reduced to 25% or less, which is a very demanding requirement. There are probably three ways of reducing the carbon dioxide output:1. By capture and sequestration, but this may be technically very demanding.2. Reduction using hydrogen in place of carbon."

Jan 1, 2009

By Jun Li, Lin Chen, Tian-zu Yang, Wei-feng Liu, Wan-da Bin

"The Chinese bismuth production accounts for more than 80% all over the world in 2011. The main raw materials of bismuth smelting are bismuth concentrate and by-products of Cu or Pb smelting process. Many traditional methods of bismuth smelting in china was reviewed in this paper, such as reverberating furnace smelting, blast furnace smelting, fire-refining, ferric chloride leaching-hydrolysis, slurry electrolysis, and so on. But all the traditional pyrometallurgy or hydrometallurgy process have such shortages of low recovery, poor environment, and high cost. Therefore new technologies are introduced into the smelting process of bismuth concentrate, such as low-temperature alkaline smelting and side-blown bath smelting with oxygen-enrichment. These technologies have got great progress on energy saving, emission reduction, and friendly environment. Finally the development direction of new technology on bismuth smelting was prospected.IntroductionAs a green metal, bismuth has a wider applications, just extending from the traditional medicine, metallurgical-chemical engineering, low-melting alloys, solders, catalyst, and electronics to cosmetics, flame retardant, storage battery, semiconductor, supper conductor and nuclear energy etc[1,2,3,4,5,6,7]. This will increase the production of bismuth and promote the development and progress of bismuth smelting technology. At present, The major bismuth-product countries are China, Mexico, Peru, KZ, Bolivia and Canada etc, and China are dominating. A survey from the USGS[8] showed that Chinese bismuth production were 12,500 tonnes and got 80% of the world's in 2011. Thus the technology of Chinese bismuth smelting have a great representativeness."

Jan 1, 2013

By Tiejun Chun, Jian Pan, Deqing Zhu, Zhiyong Ruan

"In this paper, the desulfuration of pyrite cinder pellets was carried out. Phase analysis shows that most sulfur of pyrite cinder exists in the form of elementary sulfur. Most sulfur was removed in preheating stage. 81.25% sulfur was removed and the average SO2 concentration of exhaust gas was 1365ppm when the pellets were preheated at 950oC for 9 min. The final product, assaying 62.42wt%Fe and 0.02wt%S content at 96.88% desulfuration was achieved under the conditions of preheating at 950? for 9 min and roasting at 1200? for 15 min, which can be used as the burden for blast furnace.IntroductionPyrite cinder, as a subsidiary product of sulfuric acid production by roasting of pyrite ores, was solid waste in sulfuric acid enterprises. According to the statistics, the annual production of pyrite cinder is about 15 million tons in China. Besides, there is lots of pyrite cinder deposited for many years [1-3]. The pyrite cinder consumed in the cement and other industries as auxiliary additives only accounts for less 30% of its total discharge and the left is stored in waste pond, occupying much land and polluting environment in China [4-5]. Moreover, pyrite cinder contains iron between 30-63% which can be utilized as a cheap raw material for ironmaking by sintering or pelletizing processes, which can not only prevent pollution but also provide cheap raw materials for ironmaking [6-7]. However, compared to traditional iron ore concentrate, pyrite cinder possesses higher sulfur content."

Jan 1, 2012

By M. H. Lin, S. Kou

"Czochralski pulling has been a very widely used process for growing single crystals for electronic and optical applications. Dopant segregation can significantly degrade the quality and yield of single crystals. We have used the floating-crucible technique for segregation control in Czochralski pulling, our floating crucibles being unique in that the melt passageway is very long. As such, dopant back diffusion is suppressed, even when the cross-section of the melt passageway has to be relatively large to help the melt go through or when the pulling rate is very low. Single crystals of model materials K-doped NaN03 and Pb-doped Sn have been grown with very uniform dopant concentrations. IntroductionSingle crystals of electronic and optical materials are often doped with a small amount of impurities to develop required physical properties, e.g., P and B in Si for n-type and p-type semiconductors, respectively, and Nd in YAG lasers. Dopant segregation can result in nonuniform physical properties, thus degrading the quality and yield of the resultant crystals.Figure 1 is an illustration of the conventional Czochralski process for crystal growth. Several techniques have been developed to control dopant segregation in Czochralski pulling, including the push-pull technique (1,2), the drop-pull technique (3-7) and the floating-crucible technique (8-13). The first two techniques require precise sensing devices and feedback control systems to keep the feeding rate equal to the pulling rate. The last technique is simple since the feeding rate is automatically equal to the pulling rate."

Jan 1, 1994

By Luben Xie, Lin Hu, Qiang Wang, Min Gan, Tao Jiang, Wenqi Li, Yi Wang, Xiaohui Fan

"The mineralization behaviors of typical fluxes are studied by investigating the microstructures with optical microscope. The results show that the reactions begin with between iron ore and lime, limestone with small particle to form primary liquid. Then coarse limestone, dolomite and serpentine take part in reaction under the action of primary liquid. Limestone is the easiest to mineralization, next dolomite, and the last is serpentine. The higher basicity and smaller fluxes size favor the mineralization process of dolomite and serpentine.IntroductionThe purposes of adding fluxes into sintering are that:(1) to increase the basicity of sinter, so as to reduce even eliminate addition fluxes into BF(blast furnace) and decrease the coke ratio of BF[1,2]. (2) to decrease the melting point of sintering mixture to ensure sintering can be carried out at a lower temperature and reduce the energy consumption. (3) to improve the qualities of sinter by forming binding phase with iron ore fines [3].Flux is another significant component for sinter besides iron ore, especially for high basicity sinter[4]. The proportion of flux is usually higher than 10% in sinter mixture(excluding return mine).There were many reports about the influence of the flux types on sintering, such as limestone, dolomite, lime and so on[5-7]. It is very important to choose suitable fluxes for iron ore sintering. Although the effect of flux size on sintering also has been researched, the mineralization behaviors of the fluxes in the sintering process has not been illuminated. The paper will study the mineralization behavior of fluxes in sintering."

Jan 1, 2011

Steel Ladle in Bhilai Steel Plant, SAIL, India, passes through VAD & LF-RH route and this exposes refractory lining to a severe operating conditions. Ladles are lined with in-house manufactured MgO-C refractories. Lining life used to be 35 heats, out of which 18-20 heats were through VAD/LF-RH, hence, ladle availability had become a constraint. Laboratory studies were carried-out to optimize granulometry and composition. Granulometry was developed by adopting Andearssen packing model. A suitable plasiticiser was identified to eliminate inconsistency caused due to variation in resin quality and weather condition. It reduced variation in green bulk density from 6 to 1.3%. Abrasion and slag erosion studies were conducted, which shows that with increase of carbon, abrasion resistance decreases and corrosion resistance improves. Based on these studies, graphite in slag zone was increased from 10 to 12.5% and in metal zone it was reduced to 7.5%. Different process parameters of brick making were optimized to make MgO-C bricks of maximum bulk density with reduced coke porosity. Modified bricks have bulk density of 2.99-3.02 g/cc and coke porosity of 9.5-10.5%. Further, shape of the bricks were changed from side arch to mini keys and thickness was increased from 80 to 100 mm. Mini key bricks are pressed from sides, thus eliminating variation in thickness which is critical dimension for dry joints. These modifications improved average lining life of steel ladles to 64 heats, which includes 37-40 secondary heats. Maximum life obtained is 87 heats.

Jan 1, 2006

By Peng Peng, Ouo Cheng, Guodong Lai, Lijuan Chu, Zebiao Zhang

"The pressure acid leaching residue of zinc concentrate contains a large quantity of sulfur. The present study attempts to leach sulfur using a mixture of ammonium sulfide and water solution at 25°C. Effects of three leaching variables: ammonium sulfide concentration, leaching time, liquid/solid ratio on the sulfur leaching rate were investigated. The process conditions were optimized using response surface methodology based on the central composite design. From the analysis of variance (ANOVA), the significant factors on response were identified. The optimum conditions for leaching elemental sulfur from pressure acid leaching residue of zinc concentrate were obtained using an ammonium sulfide concentration of 2.5 mol/L, leaching liquid-solid ratio of 6.5:1 and leaching time of 7 min. Under the optimum experimental conditions, a maximum of 98.50% of total sulfur was extracted. The experimental results obtained agreed satisfactorily with the model predictions, with a correlation coefficient (R2) of 0.99.IntroductionSulfur is widely used in agriculture, medicine, rubber, building materials, gunpowder, wine and sugar, and other fields [1]. Currently the world sulfur production is 40Mt, out of which more than 90% is recovered from industrial processes, and 10% is natural [2], This highlights the importance of sulfur recovery. As the pressure leaching technologies [3] continue to mature and are increasingly applied to refining, a large quantity of high-sulfur residue is produced [4-5]. It is desirable to recover sulfur from this residue, so that it is economically advantageous, and reduces environmental pollution [6]."

Jan 1, 2012