By J. W. Spretnak, V. Kandarpa

Stress -induced ordering of carbon atoms is studied in a series of Fe-Mn-C alloys. A prominent peak is found in the vicinity of 280°C at frequencies of the order of 1.0 cps, with an associated activation energy of 37 kcal per mole. The height of the peak is linearly rekzted to the concentration of carbon in solution. The distortion of octahedral holes by manganese atoms appears to be predominant over carbon-carbon pair interactions. RELAXATION by stress-induced ordering of point defects is expected whenever the introduction of these point defects produces distortions which have a lower symmetry than that of the lattice. Under zero stress, the isolated point defects occupy the crystallographic-ally equivalent positions in the lattice, as these represent states of equal energy. However, if the defect sites are asymmetric, application of an uniaxial stress will split the energy states, and a redistribution of the defects among various states will take place. This is the case of the internal friction peak called the Snoek peak,1 resulting from isolated interstitials in bcc metals. The interstitial sites in this case have tetragonal symmetry. In the case of fcc and hcp lattices, such an effect is not expected from isolated point defects because of the symmetrical nature of the interstitial sites. However, internal friction peaks arising from interstitial diffusion have been reported both in hcp2,3 and fcc4-8 lattices. These peaks are often explained on the basis of stress-induced ordering of interstitial solutes, caused by the deviation of interstitial sites from their cubic symmetry through the presence of nearby defects. In the case of fcc lattices, evidence for interactions of both the substitutional-interstitial4,6,13 and interstitial-interstitial types5'798'14 have been presented by various investigators. The purpose of the present investigation was to study the internal friction peak attributed to the diffusion of interstitial carbon atoms in high purity austenitic manganese steels and to account for the peak in the light of the existing models. MATERIALS The Fe-Mn-C alloys used in the present investigation were made in two different ways, designated as Type I and Type 11. Type I alloys were made from high purity Fe-Mn alloys obtained in the form of 0.04- in.-diam wires from Materials Research Corporation, Orangeburg, N.Y. These alloys were carburized to different levels using gas mixtures of H2 and CH4 at 1000°C. Type I1 alloys were made in this laboratory starting with zone refined iron, spectrographically pure manganese, and spectrographically pure carbon. They were melted in an argon arc melting furnace and drawn into 0.04-in.-diam wires. All the wires were annealed at about 900°C for 3 hr prior to the internal friction experiments. After the measurements of internal friction, the phases in the samples were identified by X-ray diffraction and the carbon determined by the combustion method. EXPERIMENTAL PROCEDURE In the present work, a classical Ke-type pendulum was used. The details of the equipment were described previously by D. T. Peters.9 Dry helium at 40 torr was used in all the experiments. The internal friction, measured as the logarithmic decrement of the torsion amplitude of vibration was determined as a function of temperature, from ambient to about 500°C. The background internal friction was assumed to have the form of the exponential of the inverse temperature and was subtracted from the raw data. The height of the peak was measured at the position of the maximum in the plot of the internal friction versus temperature. The activation energies of the peaks were measured by the peak shift method. The internal friction values for an alloy were obtained as a function of temperature at different frequencies of vibration. The position of the peak changes with frequency, the higher the frequency the higher the peak temperature. The activation energy of the process associated with the peak is obtained using the formula

Jan 1, 1970

By M. J. Marcinkowski, K. S. Raghavan, A. S. Sastri

A detailed transmission electron microscopy investigation was carried out in connection with a manganese Hadfield Steel. At small plastic strains, numerous individual intrinsic stacking faults are observed. With increased plastic deformation, the stacking faults thicken into twin lamellae which in turn subdivide the original austenite matrix into smaller domains. The twin boundaries act as strong barriers to subsequent dislocation motion and is in a sense equivalent to grain refinement. It is this "grain refinement" which is believed to be the cause of the very high work hardening rates in the Hadfield Steels. In many cases, especially where an hcp phase is the stable one at low temperatures, the stacking fault energy in fcc metals and alloys decreases with decreasing temperature.' Since stacking faults of the intrinsic type are precursors of both twins as well as the hexagonal close packed structure, both of these entities should become more frequent as the temperature of a fcc crystal is lowered. In the case of the twin, there is no chemical driving force for its formation and it is generally necessary to provide the required driving force by an applied stress, i.e., strain energy. In the case of the hcp structure the transformation from the fcc modification can occur spontaneously (marten-sitically) since a decrease in chemical energy does in fact occur; however, an applied stress will provide an even greater driving force toward complete transformation. Since the transformation products mentioned above occur in an inhomogeneous manner throughout the crystal and since these can act as potential barriers to further plastic deformation2 marked strengthening effects can be anticipated. Also because metal and alloy strenghening is in general proportional to the shear modulus, these effects should be greatest in steels of the austenitic type (y), i.e., the fcc types. Perhaps the two most important steels in this category are the austenitic stainless steels and the Hadfield manganese steels. Both may be quenched from elevated temperatures so as to retain the austenitic states characteristic of those temperatures. The effect of subsequent deformation at lower tem- peratures has a profound effect on the stress-strain curves of these alloys. In particular Fig. 1 shows the compressive stress-strain curves obtained with an 18-8 stainless steel which was quenched from 1850°C after annealing for 1 hr so as to produce all y. As the temperature is lowered, the work hardening rate increases markedly. Although some hcp or c mar-tensite can be generated by plastic deformation as the temperature is lowered,~ it is believed to be a transition phase4 and most of the martensite produced is of the bcc or a variety.3 It is this stress induced martensite which gives rise to the very low initial work hardening at 77°K as can be seen in the stress-strain curve in Fig. 1. Similar low initial work hardening rates have been observed in the stress induced Ni-Ti martensites.5 Fig. 2 shows that an even more rapid rate of work hardening occurs in the Hadfield steels treated in the same way as that described for the 18-8 stainless steels a; the temperature is lowered. It is this ability to work harden to such high stress levels that makes the Hadfield steels particularly suitable for armor plate and heavy construction equipment. However, unlike the case of Fig. 1, no initial low rate of work hardening is observed in any of the curves in Fig. 2. Thus the stress induced formation of any low energy martensite phase in any significant quantity must be ruled out. This observation is in accord with the X-ray findings of Otte.~ On the other hand, small quantities of the E phase have been observed by other investigators using transmission electron microscopy (TEM) above Even more significant was the fact that large numbers of deformation twins were observed in the deformed Hadfield steels,678 which were postulated to be one of the reasons for the high work hardening ability of this class of steels.8 It is the purpose in what follows to discuss a series of experimental observations pertaining to the stress induced transformation in a Hadfield steel and to formulate a dislocation mechanism which adequately accounts for the observed results. EXPERIMENTAL PROCEDURE The stainless steel used to obtain the curves shown in Fig. 1 was of the AISI Type 303 containing approximately 18.0 pct Cr and 8 pct Ni. On the other hand, the Hadfield manganese steel used to obtain the curves shown in Fig. 2 contained between 1.00 to 1.25 pct and 11.5 to 13.5 pct Mn. In all cases the samples were in the form of compression cylinders 0.220 in. in diam and 0.370 in. long. Prior to testing the samples were annealed for a hr at 1050°C and rapidly quenched into a brine solution. This treatment was sufficient to preserve the y phase for subsequent testing at lower temperatures. All samples were compressed in an Instron testing machine using a cross head speed of 0.02 in.

Jan 1, 1970

By H. H. Podgurski, H. E. Knechtel

Annealed Fe-Al alloys do not react readily to form AlN when held at 500ºC in NH3-H2 gas mixtures, but do so upon the introduction of dislocatims. Nuclea-tion of the nitride phase occurs on dislocation sites. In turn, the growth of the aluminum nitride particles causes the ferrite phase to yield plastically, generating more dislocations for the nucleation process. The nitride phase extracted from an Fe-2 pct A1 alloy nitrogenated at 500°C was identified as stoichio-metric aluminum nitride with a hexagonal crystal lattice. THIS investigation reveals the role that dislocations play in initiating and sustaining the nitriding reaction in Fe-A1 alloys. As early as 1931 the work of Meyer and Hobrock1 suggested that the initiation of the nitriding reaction could involve a nucleation controlled process. Recently Bohnenka2 depicted the gas-phase nitriding process below 600°C as one of mixed control limited by nitrogen penetration through the surface, by nitrogen diffusion, by aluminum diffusion, and by nucleation of the nitride phase, Fig. l(a). In our research in a comparable alloy (0.57 pct Al) at 575ºC, we have observed a nitrogenation which we feel is better described by Fig. l(b). In the case of a 2 pct-A1 alloy partially nitrided at 500°C we propose the profiles shown in Fig. l(c). For a complete and accurate description of the process, a concentration profile of the dislocation density in the test specimen would be needed. EXPERIMENTAL Nitrogenization was conducted between 500" and 575°C in a variety of NH3-H2 gas mixtures on three Fe-A1 alloys: 1) zone-refined iron + 0.16 i 0.2 pct Al—levita-tion melt, 2) zone-refined iron + 0.57 0.02 pct Al— levitation melt, 3) plastiron + 2 pct Al—melted by induction heating. To demonstrate the effect of dislocations on reactivity, both cold-worked and annealed samples were investigated. All nitrogenation rate studies were conducted gravimetrically with a gold-plated invar balance4 contained in a gas-flow system. To avoid contamination of the specimens in the reaction zone of the system, the reaction chamber was constructed of high-purity dense alumina. The activity of nitrogen was fixed by specific NH3-H2 gas mixtures whose compositions were continually monitored by calibrated thermal conductivity gages and checked by chemical analysis. Variations of ± 0.1 pct NH3 could easily be detected by both methods. Throughout this paper the activity of nitrogen is defined as PN3 /PH23/2 , where PNH3, and Ph2 are partial pressures in atmospheres. Electron transmission, density measurements, and chemical analyses were made on specimens before and after nitrogenating in order to reveal structural and chemical changes. Similar studies as well as X-ray diffraction studies were conducted on nitride extractions from the nitrogenated 2 pct-A1 alloy. These extractions were obtained by the use of an anhydrous bromine-methyl acetate solution which dissolves the iron and leaves the insoluble nitrides as a residue. Hardness profiles were obtained on cross-sections of partially nitrided specimens to demonstrate the extent of nitriding through the thickness of the specimens. RESULTS AND DISCUSSION The nitrogen activity in the NH3-H2, atmospheres was never allowed to reach a level capable of producing iron nitride (Fe4N). Hence, the term nitriding as used in this paper refers only to the formation of aluminum nitride whereas nitrogenation refers to the total uptake of nitrogen regardless of how it is distributed throughout the alloy. The weight increases observed during the initial stage of a nitrogenating treatment are due primarily to the solution of nitrogen in the ferrite phase, particularly when starting with annealed specimens. Because this initial nitrogenation rate in the case of the 0.57 pct A1 alloy, see Figs. 2 and 3(a), was most rapid the weight change that occurred thereafter might be attributed to the nitriding reaction with the exception of a small weight increment due to the irreversible pickup of oxygen by aluminum. The oxygen (<70 ppm) came from traces of H2O and 0, in the hydrogen and ammonia gases. On the basis of discrepancies between total weight increase and the increase in the nitrogen content of the sample as determined by chemical analysis, it was estimated and later established by activation analysis, that as much as 200 ppm of oxygen were taken up by a fully nitrided Fe-0.57 pct A1 specimen at 575°C. Most of the oxygen could have been picked up from the nitriding atmosphere on the surface of the samples during cooling to room temperature. Even 50 ppm of water in the gas phase will become oxidizing to iron before the sample has cooled to room temperature. The lack of reactivity* of these alloys in the annealed

Jan 1, 1970

By M. B. Kasen

eralized strain equation appear quite different they are really identical. This identity can be shown in a simple mathematical rearrangement. Referring to Eq. [I], the substitution of ln(1 +?E) for ? (where ?E is the engineering strain) yields: a =s8- (s8?so)e?1/?c) ln(1 +s8??E) [4] or s =s8?(s8?so)(l +?E)-1 [5] Replacing (1 + cE) with its equivalent, (l/lo): s=s8?(s8?so)l/€c [6] Adding and subtracting the quantity (s8 - so) yields: s=s8?(s8?so)+ (s8-so) l-(^)l/£c [7] = s0+(s8?so)ri-(^0)1/^l [8] Letting n = 1/?c it follows that: This equation will be seen to be identical to the generalized strain expression in Eq. [3], the coefficients a and b being equal to so and (s8?so)/?c or n(s8?so), respectively. Confirmation of the relationship noted above was provided by fitting experimental stress-strain data5 for 304 stainless steel (total strain from 0.072 to 1.15) at room temperature at a true total strain rate of 4 x 10-3 sec-1 to Eqs. [I] and [3]. In this study nonlinear regression analyses were used to evaluate the equation constants. The results of this evaluation are presented in Table I. When these constants are used in Eqs. [I] and [3] the curves obtained are coincident. It will also be noted that the value of n is equal to YE,, the value of a is equal to so, and the value of b is equal to (s8 - so)/Ec. These equalities are illustrated in Table I where the Voce constants in parentheses were calculated from a, b, and n values. Excellent agreement is seen to exist. It is concluded, therefore, that the Voce equation is, indeed, identical to the linear expression involving generalized strain. In applying the generalized strain concept to stress-strain data, it has been noted3 that data within what was termed the transition region (first few points in the plastic flow region) must be excluded from the analysis in order to obtain the linearity in Eq. [3]. A similar exclusion applies in the use of the Voce equation since an expression which would describe the strain-hardening region would usually be found to be not too effective in the elastic-plastic fillet2 which connects the elastic line to the strain-hardening region. These considerations further substantiate that Eqs. [I] and [3] do indeed describe identical behavior. Note added in proof. Since this manuscript was submitted for publication, correspondence with Professor S. R. Davies, University of Edinburgh, (of Ref. 3) indicated that his associates have also confirmed the identity between the Voce equation and the generalized strain concept. It is sometimes desirable to obtain a small grain size in super-purity metals. Unfortunately, the absence of impurities, the low recrystallization temperatures, and the low activation energies for boundary motion result in rapid growth of relatively few grains when conventional recrystallization practices are used. For example, Arajs et al.1 were unable to obtain a mean grain diameter less than about 0.4 mm in iron containing 38 at. ppm of impurity. The <1 at. ppm purity range in many modern superpurity metals results in yet larger limiting grain sizes. It is the purpose of this communication to describe a technique by which mean grain diameters as small as 30 µ have been produced in aluminum having an impurity content < 0.5 at. ppm. The technique should be applicable to superpurity metals other than aluminum and has potential applications to grain refinement of commercial alloys. The necessary and sufficient requirements for production of a small grain size are as follows: a) a large number of potential nucleating sites must be created randomly within the cold worked material, b) sufficient thermal energy must be provided at a rate that will simultaneously activate a large fraction of the potential nuclei, and c) the grain growth must be stopped shortly after grain impingement.&apos; A high density of potential grain nuclei may be cre-

Jan 1, 1970

By R. L. Orr, J. D. G. Masse, Ralph Hultgren

The relative partial molar enthalpies of gold and tin in liquid Au-Sn alloys have been measured from Xsn = 0.474 to 0.510 at 696°K, slightly above the melting point of solid AuSn. Within an average precision of 6 cal per g-atom, the data are represented by two smooth curves, which satisfy the Gibbs-Duhem relationship and which do not show any anomalous behavior in the range of composition studied. The results give no support to the hypothesis that atomic associations in the equiatomic liquid alloy resemble those in solid AuSu. LITTLE has been firmly established as to the nature of atomic distribution in liquid metallic phases. A favored hypothesis assumes the existence of atomic groupings in the liquid phase which are similar to those in solid phases occurring at lower temperatures. Beginning with this hypothesis, it is often possible to adjust the values of certain parameters (such as degree of association) so that approximate agreement is achieved with certain features of the X-ray diffraction pattern of the liquid, even though many other possible structures might satisfy the data equally well. Thus, in this manner, the structure of liquid tin has been described as a dispersion of fragments of gray tin in a matrix of metallic tin.1 Four X-ray diffraction studies2"5 have been made of the liquid alloy of composition AuSn at temperatures slightly above the melting point of the solid. Each investigator concluded, on somewhat different grounds, that the liquid consisted to a large extent of arrays of atoms similar to the solid, with admixture of more disordered arrays. Solid AuSn has the nickel arsenide crystal structure: each tin atom has six nearest neighbors, all gold atoms; and each gold atom has six tin and two gold atoms as nearest neighbors. It remains highly ordered to the melting point. The liquid alloy has a large exothermic (?H700° K = -2700 cal per g-atom6) enthalpy of formation, favoring ordering and making the hypothetical molecular association not unreasonable. The possible existence of such solidlike arrays, or of a high degree of order that occurs preferentially at a specific composition in a liquid alloy, might also be revealed by thermodynamic behavior somewhat analogous to that in highly ordered solid alloy phases. The latter often exist over wide composition ranges, within which the highest degree of order occurs at the ideal composition for which the atomic fractions are equal to the fractions of sites which are "right" for each kind of atom. On departing from the ideal composition, the excess atoms occupy "wrong" positions, raising the internal energy and making it progressively easier for additional atoms to occupy "wrong" positions. Thus, on either side of the ideal composition, there should be a pronounced rise in the entropy and enthalpy, which would be shown particularly by the change in the relative partial molar enthalpies, ?Hi, since they depend strongly on d?H/dx. In the one case where accurate measurements have been made, the solid AuCu ordered phase, the structure becomes much less ordered as the composition deviates from the ideal, and relative partial molar enthalpies change sharply as shown by the data6 given in Table I. This suggests the possibility of finding similar pronounced changes in the relative partial molar enthalpies of gold and tin in liquid alloys near the composition AuSn if the postulated solidlike ar-

Jan 1, 1967

By R. M. Waterstrat, E. C. van Reuth

BINARY- alloy phases having the A15-type crystal structure have been described as occurring at a simple and more or less invariant stoichiometric composition (A3B) which corresponds to the relative number of atoms occupying each of the two crystallographi lattice sites in this structure.1,2 It is frequently assumed, therefore, that each crystallographic site is occupied exclusively by one kind of atom. In most cases, however, there have been insufficient experimental data to establish whether atomic ordering is, in fact, complete. Recent studies have shown that binary A15-type phases are sometimes stable over an appreciable composition range3&apos;&apos;* and, occasionally, the composition range of stability does not even include the "ideal" A3B stoichiometric composition.5-7 We have observed the existence of nonstoichiometric A15-type phases in the binary systems Cr-Pt and Cr-Os. This has not been reported in previous work on these alloy systems.1,8-11 A series of alloys, each weighing approximately 30 g, was prepared by are-melting in an Ar-He atmosphere using 99.999 pct Cr, 99.999 pct Os, and 99.99 pct Pt as starting materials. Each alloy was melted four times with a total weight loss of less than 1 pct. The stoichiometric (A3B) alloys were sealed in evacuated quartz tubes and annealed at 1200°C for periods of time ranging from 3 days to 2 months. Examination of the alloy microstructures revealed that little change had occurred over this time interval and it was therefore assumed that the microstructures were fairly representative of equilibrium conditions. No evidence of contamination was observed although there was apparently some loss of chromium which was confined to a thin layer at the surface of the specimens. The quartz tubes were quenched from the annealing temperature into cold water. X-ray diffraction and metallographic examination of the stoichiometric alloys revealed an estimated 10 to 30 pct of second phases which were tentatively identified as phases previously reported in these binary-alloy systems.8-11 A second series of alloys was prepared by mixing -325 mesh metal powders having a nominal purity of 99.9 pct and compressing these mixed powders in a cylindrical die at a pressure of 43,000 psi. These alloys, each weighing 15 g, and some of the arc-melted alloys were annealed in a high-temperature vacuum furnace heated by tantalum strips at a pressure of 10-8 Torr and were rapidly cooled by turning off the furnace power. X-ray and metallographic examination of both series of alloys served to establish the composition ranges of the A15-type phases. Although some chromium losses occurred during the vacuum annealing, they were largely confined to a thin layer on the outer surfaces of the samples. It was established that the A15 phases occur in the Cr-Pt system at 21 ± 1 at. pct Pt after 1 week at 1200°C and in the Cr-Os system at 28 ± 1 at. pctOs after 1 day at 1400°C (see Table I). We also observed that an arc-melted stoichiometric (A3B) alloy in the Cr-Ir system was single-phase (A15-type) in the "as-cast" condition in agreement with previous work.8,13 In addition we obtained a sample of the Cr-Os A15-type phase from Argonne National Laboratory. This alloy contained less than 1 pct second phase12 and was submitted to a density measurement. The density measurement yielded a value of 11.14 g per cu cm in comparison to a theoretical value of 11.25 g per cu cm calculated using the observed lattice constant (4.6806Å) of this alloy. The uncertainty in measurement was 0.1 pct but the sample may have contained some cracks or minor imperfections which could account for the low experimental value. We have also studied the atomic ordering in these phases by means of integrated line intensity measurements using thick, flat, rotating powder samples and CuK a radiation in an X-ray diffractometer. We have obtained order parameters of 0.90 for the Cr-Pt phase, 0.89 for the Cr-Ir phase, and 0.64 for the Cr-Os phase using the formula: where s is the usual Bragg and Williams order parameter, ra is the fraction of chromium atoms in A sites, and FA is the fraction of chromium atoms in the alloy. The values obtained are estimated to be accurate within ±4 pct. If the unusually small value for the order parameter of the Cr-Os A15 phase were due to the existence of lattice vacancies on the "B-atom" sites, then a density of 10.04 g per cu cm would be expected in contrast to the observed value of 11.14 g per cu cm. We, therefore. conclude that the fraction of lattice vacan-

Jan 1, 1967

By N. N. Breyer

A specially built "hard" tensile machine with characteristics permitting the precise detertnination of the drop of the load at the yield point has been used to study the magnitude of the yield-point phenotnenon in prestrained martensitic 4340 steel. A new phenonzenon, the appearance of a secondary yield point, has been observed by holding the specimen at constant strain in the plastic region. Furthermore, it has been found that a series of yield-point drops could be introduced by successive constant strain holds in the plastic region. The isothermal kinetics of the development of the secondary yielding point lave been studied at four temperatures: 24° 0° -18°, and -79°C. From the results of the kinetic investigation, equations for the In a previous investigation1 it was shown that, contrary to generally held opinion, steels of medium carbon content, such as 4340, 4140, and 86B30, in the as-quenched martensitic condition, can be cold-drawn through a die with reductions in area of up to 10 pct without cracking. Tensile specimens of 4340 machined from bars quenched and prestrained in this manner exhibited tensile strengths of about 400,000 psi coupled with 30 pct reductions in area. In addition, it was found that each sample of such steels exhibited a yield point in the quenched, cold-drawn condition. Since these studies were conducted on a commercial hydraulic testing machine of a type which is not well-suited to detailed study of yield-point behavior, it was decided to study this phenomenon more thoroughly on a rigid straining machine. In this new investigation, use of such a "hard" machine not only allowed study of the magnitude of the yield-point drop but also revealed a new phenomenon—secondary yielding of the martensite introduced by stopping crosshead motion after plastic deformation of the sample had begun. The present paper is a report of these findings. MATERIALS AND PROCESSING The material used was a commercial 4340 steel of the composition shown below: 0.41 0.80 0.013 0.019 0.31 0.85 1.76 0.28 1 0.42 0.77 0.015 0.024 0.30 0.84 1.69 0.28 0.08 2 1 = Ladle analysis. 2 = Laboratory analysis. Bars of this steel were processed in the following way: 1) machined to predetermined diameters; 2) austenitized at 870°C for 1 1/2 hr; 3) oil-quenched; 4) cooled to -115°C for 1/2 hr; onset and increase in magnitude of the secondary yielding in this temperature region have been found to fit the relationship ?Ys = Atn where ?Ys is the magnitude of the secondary yield Point in psi, t is the time in seconds, and A and n are parameter characteris-tics of the material. Although the occurrence of the primary and secondary yield points could be rationalized qualitatively on the basis of stress-induced ordering of carbon atoms in the stress fields of dislocations, as postulated in an earlier paper, the kinetics of the secondary-yield-point development were interpreted to indicate that the ordering involves more than just single jumps of carbon atoms from high-energy to neighboring low-energy sites. 5) pickled and lime-coated; 6) drawn through a carbide die. The predetermined diameters were chosen so that drawing through the same die gave the various reductions desired. Tensile specimens of 0.252 in. diam with a 1 1/4 in. gage length were then prepared from the drawn bars and tested. In order to study the stress-strain behavior at the yield point in detail, a rigid tensile machine with a high spring constant was constructed. Columns of large cross section (relative to the specimen cross section) constituted the machine frame. A dc motor was used to drive a screw via a gear reducing train and a "crane" thrust bearing. In this relatively simple device small deformations could be observed un-blurred by the slow response and lower spring constant inherent in hydraulic machines.&apos; A strain-gage dynamometer permitted load changes as small as 8 lb to be read. RESULTS Tensile test samples machined from bars in the as-quenched condition with no subsequent drawing and samples from bars with 3.8 pct reduction after quenching gave stress-strain curves typified by those shown in Figs. I and 2. The time lapse between predrawing and tensile testing varied but usually ranged between 3 to 6 days at room temperature. The strain rate during testing was 0.003 in. per in. per min. The as-quenched curve is seen to have a broad serrated maximum whereas the stress on the specimen prestrained 3.8 pct rose linearly to point A, Fig. 2, fell abruptly to B, and then gradually to C. The abrupt drop to B was accompanied by evidence of incipient necking. The drop of the stress at the yield point in the prestrained samples (A to B in Fig. 2) changed with the percent prestrain, as illustrated on Fig. 3. Although the tensile strength increased continuously with the amount of previous cold drawing, the magnitude of the yield point drop first increased—up to about 6 pct prior reduction—and then decreased. Specimens from bars predrawn more than 8 pct broke in a brittle fashion in the elastic portion of the stress-strain curve.

Jan 1, 1967

By E. T. Turkdogan, W. L. Worrell

The rate of reaction of hydrogen sulfide with ferrous sulfide was studied by measuring the initial rates of sulfidation of iron strips in hydrogen sulfide-hydrogen-argon mixtures at 670°, 800°, and 900" C. The time-dependent surface sulfur activity is derived from the instantaneous rate of sulfidation with the assumption that diffusion in the sulfide layer is in a pseudo-steady state with the gas-sulfide chemical reaction. The rate of sulfur transfer from hydrogen sulfide to the surface of iron sulfide is proportional to the partial pressure of hydrogen sulfide and inversely proportional to the activity of sulfur at the surface of the sulfide layer. The derived rate equation is based on the assumption that most of the surface sites on the chemisorbed layer of iron sulfide are occupied by sulfur atoms and that the slow rate-controlling reaction is the dissociation of hydrogen sulfide on the chemisorbed layer. The experimental results are in reasonable accord with this reaction model. 1 HE slow approach to parabolic growth rate in the sulfidation of iron in hydrogen sulfide-hydrogen mixtures is a manifestation of slow approach to surface equilibrium between the gas and the surface of the sulfide layer. For example, at 800°C and Fig. 7 in Part I, the parabolic growth rate begins after approximately 1 day of sulfidation time. With decreasing temperature and decreasing partial pressure of hydrogen sulfide, the time necessary to reach gas-sulfide surface equilibrium is much longer. These observations are similar to those reported previously by Turkdogan et al.&apos; on the oxidation of iron to wustite in hydrogen-water vapor mixtures. The slow approach to gas-sulfide equilibrium is well-demonstrated by the results in Fig. 1 where the square of the weight gain per unit area, ( g S per sq cmI2, is plotted against time for gas mixtures having PH g//>H = 1.0 with 0, 25, 50, and 67 pct Ar at 800°C. The value of 1.5 X lo-&apos; (g S per sq cm)&apos; corresponds to almost complete sulfidation of the iron strip (- 0.05 cm thick) to iron sulfide. The points fall on S-shaped curves. If the inflection parts of the curves are considered to be linear, thus indicating parabolic growth rate and the establishment of gas-sulfide equilibrium, their slopes would have to be the same for a fixed ratio in the gas mixture. Such is not the case, and the slopes for the "linear" parts of the S-shaped curves are lower than the value when gas-sulfide surface equilibrium is established. The subject matter of this paper is the kinetics of the surface reaction of hydrogen sulfide with iron sulfide during the early stages of sulfidation of an iron strip. EXPERIMENTAL RESULTS The apparatus and materials used were the same as those discussed in Part I. In the present experiments of relatively short duration, a purified iron strip, 5 by 2 by 0.05 cm, which was suspended in the uniform hot zone of a vertical zircon tube, reacted with a flowing gas mixture of hydrogen sulfide-hydrogen-argon. The sample was suspended from a gold chain attached to a calibrated silica spring. The amount of sulfur picked up by the iron, which formed a layer of iron sulfide, was determined by measuring the displacement of a reference point on the silica spring, using a cathetom-eter. In all cases, the degreased sample was first annealed in a stream of oxygen-free dry hydrogen for several hours to remove any impurities such as oxygen, nitrogen, or carbon which might have been present on the surface of the sample.&apos; The rate measurements were carried out at 670°, 800°, and 900° C in hydrogen sulfide-hydrogen-argon mixtures with pH2 s/Ph2 ratios from 4 to 0.1. In a few experiments of short duration no sulfur deposition was observed in gas mixtures with (comments concerning sulfur deposition at high pH s/ph ratios were made in Part I.) Typical examples of the results obtained are shown in Fig. 2 for two temperatures and two gas compositions. With the present experimental technique, reproducible rate data could be obtained only after a uniform

Jan 1, 1969

By H. E. Cook

The Ising model for the internal energy of a binary alloy has been used to obtain a general equation for the critical resolved shear stress of partially ordered crystals. The equation expresses the stress in terms of the Warren "alphas " and can be used to estimate the variation in strength with order without the assumption, present in the original formulation of this problem in terms of domain size, that order is complete within each domain and that the domains are of ungorm size and shape. In addition, it is the general equation, according to the Ising model, for strengthening by short-range order. Two applications of the equation are considered: One is an estimate of the variation in strength of CkAu with long-range order. The other is an estimate of the variation in strength of FeCo with quench temperature. Reasonable agreement is found with the variations reported in the literature. When the internal energy of an alloy crystal depends upon the distribution of solute, the strength of the crystal will also depend upon it because a portion of the applied stress for plastic deformation will be: where V is the volume of the crystal and E(E) is the energy change associated with the solute redistribution caused by the plastic strain, E. We expect T to equal zero for a crystal having a random arrangement of solute because the arrangement would remain random after plastic deformation. Likewise, we expect it to equal zero when the crystal is perfectly ordered because the motion of paired dislocations found in such crystals does not disrupt order. However, when short-range order exists or when long-range order is incomplete, plastic deformation will decrease the amount of order and additional work, proportional to the ordering energy, will be expended. Fisher&apos; estimated T for crystals having short-range order by assuming an interaction energy between neighboring atoms and estimating the change in the number of unlike neighbors as a dislocation moved through the crystal. (His analysis was limited and several workers2"6 have since given more complete ones.) Fisher minimized the importance of a strengthening mechanism of this type for paired dislocations in a structure having long-range order. ~ottrell,&apos; however, pointed out that T could be appreciable for ordered crystals having antiphase domains. He attributed the strengthening to the increase in surface energy of the domains as they were cut by paired dislocations. Ardley,&apos; in his test of Cottrell&apos;s theory, found that r for Cu3Au crystals obeyed the equation: for 1 > t where 1 is the domain size, t is the domain wall thickness, and y is the surface energy of an antiphase boundary. His experiments represent the classic confirmation of the strengthening mechanism proposed by Cottrell. However, the assumptions involved in using Cottrell&apos;s theory are valid only for large domain size in CU~AU,~"~ i.e., when Eq. [2] reduces to: For small domains, ~linn~ has questioned Ardley&apos;s assumption that order was complete, and, indeed, Stoloff and ~avies" fpnd it incomplete until a size of approximately lOOA was reached. Even when the order within a domain is complete, it is not obvious how one determines the appropriate value for I in a structure where domains vary in size and are irregularly shaped. The purpose of this paper is to estimate T without restrictions upon the degree of order and domain shape. Our major assumption will be the use of a generalization of the model proposed by Bethe" (the Ising model) for the internal energy. This will in fact allow us to combine the theories for strengthening by short-range order and by antiphase domains into a single, general formalism. We will use the results to estimate the variation in strength of Cu3Au crystals with long-range order8 and the variation in flow stress of FeCo crystals with quench temperature.12&apos;13 INTERNAL ENERGY For simplicity, we restrict our considerations to those binary solid solutions which can be described as an arrangement of atoms on a Bravais lattice. An atom site will be indexed by three numbers (PI, pz, p3) determined by the vector: from the origin fixed at atom (0, 0, 0) to the atom site where a&apos;, an, and a, are the lattice translation vectors. We write: For the energy of the crystal where pi(p) is the probability (either zero or one) of finding an atom of type i (i = 1, 2) at site (p), which is shorthand for (pl, pz, p3) and pj(p + r) is that for an atom of type j (j = 1, 2) at the site (p + r), which is shorthand for (pl + rl, The coupling parameter, resents the energy associated with the pair Pi(p), Pj(p + r). The crystal is assumed large enough so that surface effects can be neglected; therefore, trans-lational and inversion symmetry require the coupling parameters to obey the relations

Jan 1, 1969

By C. L. Magee, H. W. Paxton

PREVIOUS workersl&apos;% ave found that as-quenched ferrous martensites can be plastically deformed at low stresses. They have also found that the stress to obtain small strains can be significantly increased by aging at temperatures up to 150°C. This behavior has been interpreted in two ways: 1) that the deformation at low applied stress is due to internal stresses and thus the aging phenomenon is due to relaxation of the internal stresses;&apos; 2) that the microdeformation arises through the motion of unpinned dislocations and the aging process is the diffusion of carbon to the dislocations to pin them.293 In a recent paper,4 we have shown that under certain conditions the dominant microdeformation mechanism of as-quenched Fe-31Ni marten-site-austenite aggregates is the transformation of retained austenite. Our results on resistance changes during deformation and temperature dependence of the deformation also established that, at temperatures above 300° K, the microdeformation was not due to this transformation. The purpose of this note is to report results of experiments which indicate that explanation 1 is appropriate for this deformation. All results presented here are from conditions where transformation does not make a measurable contribution to the microplastic deformation, in Fe-31Ni-0.002C, or in Fe-29Ni-0.02C-0.25Ti. The experimental techniques that were used for measurement of the plastic deformation are described4 and analyzed5 elsewhere. Fig. 1 shows the microplastic response of 100 pct austenite at 300" and 350° K. The microplastic response of an austenite-martensite aggregate is also given in Fig. 1 and it is seen that, after formation of martensite, the initial plastic deformation occurs at lower stresses. Thus, the softness is not entirely due to retained austenite—the quenched structure can be deformed at lower stresses despite the fact that the macroscopic strength is significantly higher. A result which allows a distinction to be drawn between the alternative explanations for this behavior is derived from aging experiments on the low-carbon alloy containing titanium. We have previously shown4 that the presence of titanium in this alloy reduced the free carbon to a sufficiently low level that thermal stabilization of the austenite-martensite transformation was not detected. Despite this, Fig. 2 shows that the microplastic response is decreased by aging treatments. A similar aging effect in Fe-ZONi, with some titanium, has previously been reported by . Thus, carbon is not necessary for the aging process and explanation 2 is at best incomplete. Since internal stress relief can occur independently of carbon (any temperature dependence of the flow stress can result in decreased internal

Jan 1, 1969

By A. D. LeClaire

This paper claims to provide a description of diffusion processes in solids which is said to be a reformulation of Fick&apos;s Laws and therefore, presumably, is supposed to be as general as those laws. In fact, it appears to provide no more than an atomic model of a rather restricted type leading even to results in conflict with experiment. The restriction lies in the assumption, carried throughout the paper, that even in a chemical gradient the jump frequency i of an atom of species i is a function only of the composition on the plane from which it jumps, i.e., ?i = ?i(cl, c2 ...). This means that atom jumps in opposite directions from a site would occur with equal probability. There would then be no tendency for atoms to migrate preferentially in one direction along the gradient, so the model is incapable of accommodating the well established phenomenon of atom drift in a chemical gradient.10-" A more general model that does not suffer this difficulty was discussed in a paper13 I wrote in 1958, and the results therein already contain as a special case those given by Dr. DeHoff. The simplest sufficiently general assumption is to suppose that ?i is a function ?i(a1 a2,...; wl, w2, ..-) of the concentration aj and ? ?j at the site from which and to which, respectively, a jump is made. Any such function can always be expressed as a function of the sum and difference of its arguments. Thus d is the jump distance and g a geometrical constant. Obviously this is zero, i.e., no drift, if ??ri/??j = 0. X is written in this form, revealing two components of the total drift, because it can be shown that only the second component, depending on ??&apos;i/???(?j -aj), actually contributes to the net diffusion flux Ji. This component can be shown,13 by a straightforward ther-modynamic transcription, to be responsible for the so called "thermodynamic factor" in the Darken approximation for a chemical diffusion coefficient is the activity coefficient of i. Because the jump rate ?i in DeHoff&apos;s approximation has no dependence on the concentration gradient it does not seem possible to derive the Darken equation from his Eq. [6] without the further rather arbitrary assumption that ?i = const ri. It is to be noted too that the author&apos;s derivation of Eq. [12] is only valid when ?i is in fact a function only of the cj at the plane from which the atom jumps—for only then is ci?i a unique function of position and therefore of A. Author&apos;s Reply R. T. DeHoff I am indebted to Dr. LeClaire for his penetrating discussion of my paper, "A Reformulation of Fick&apos;s First Law". I concede that it does appear initially that the relationship presented in my paper could be derived from the detail atomic model of random walk and atom drift presented in Dr. LeClaire&apos;s approach. However, there are some important differences in concept and viewpoint which deserve further amplification. Dr. LeClaire&apos;s description is penetrating, detailed, and fundamental. His approach describes an extremely complex phenomenon, the displacement of atoms in a multicomponent gradient, at a sophisticated level. For precisely these reasons, his analysis has not proved to be useful for experimental studies that have practical objectives. For example, in order to obtain the information required to complete the analysis of the jump frequency distribution in a ternary system, the following series of experiments would, I believe, be required: 1) chemical (gradient) experiments, covering the composition range;

Jan 1, 1970

By S. N. Singh, M. C. Flemings

Results are presented of a study on the combined influences of ingot dendrite am spacing and thermo-mechanical treatments on the fracture behavior and mechanical properties of high purity 7075 aluminum alloy. The most important single variable influencing mechanical properties was found to be undissolved alloy second Phase (microsegregation inherited from the original ingot). Ultimate and yield strengths were found to increase linearly with decreasing amount of alloy second phase while ductility increased markedly. At low amounts of second phase, transverse properties were approximately equal to longitudinal properties. In tensile testing, microcracks and holes were invariably found to originate in or around second phase particles. Fracture occurred both by propagation of cracks and coalescence of holes, depending on the distribution and amount of second phase. IN most commercial wrought alloys, second phase particles are present that are inherited from the original cast ingot. These include, for example, non-equilibrium alloy second phases such as CuAl2 and impurity second phases such as FeA13 and Cr2A1, in aluminum alloys. A previous paper1 has dealt with the morphology of these second phases in cast and wrought aluminum 7075 alloy, and with their behavior during various thermomechanical treatments. In this paper we discuss the influence of the particles on mechanical properties and fracture behavior of the alloy. Previous experimental work indicating a direct and major effect of second phase particles on mechanical properties (especially on ductility) includes the work of Edelson and Baldwin on pure copper.&apos; Also relevant are the many studies demonstrating the important effect of nonmetallic inclusions on the fracture of. steel.3&apos;4 Work on aluminum includes that of Antes, Lipson, and Rosenthal5 who showed that a dramatic improvement in ductility of wrought aluminum alloys of the 7000 series is achieved by eliminating second phases. It now seems well established that included second phases play a dominant role in controlling ductility (as measured, for example, by reduction in area in a tensile test) of a variety of materials. There is, therefore, considerable current interest in the mechanisms by which second phase particles affect ductile fracture. Experiments done by various workers have shown that second phase particles or discontinuities in the microstructure are potential sites for nuclea-tion of microcracks and of holes,6-l3 which then grow and cause premature fracture and the loss of ductility. Theoretical attempts have been made to explain the observed phenomena; most are able to explain observations qualitatively, but lack quantitative agreement. Much experimental work needs to be done to aid extension of theoretical models. A recent review article by Rosenfield summarizes work in this general area.14 PROCEDURE Material used in the previously described study on solution kinetics of cast and wrought 7075 alloy1 was also used in this study. Procedures for ingot casting, solution treating, and working were described in detail in that paper. Test bars were obtained for material of 76 initial dendrite arm spacing (11/2 in. from the ingot base) and 95 µ initial dendrite arm spacing (51/2 in. from the ingot base) for the following thermomechanical treatments (solution temperature 860°F; reduction by cold rolling). a) Solution treated 12 hr, reduced 2/1, 4/1, and 16/1. b) Solution treated 12 hr, reduced 16/1, solution treated approximately 5 hr after reduction. c) Same as a) except solution treated 24 hr prior to reduction. d) Same as b) except solution treated 24 hr prior to reduction. e) Same as d) except solution treated 20 hr after reduction. Test bars were taken both longitudinally and transverse to the rolling direction. Transverse properties are in the long transverse direction; since the final product was sheet (0.030 in. thick), properties in the short transverse direction could not be obtained. Test bars were flat specimens, of gage cross section1/-| in. by 0.030 in. and 1/2 in. gage length. After machining the test bars, they were given an additional 1/2 hr solution treatment of 860°F and aged 24 hr at 250°F. Three bars were tested for each location and thermomechanical treatment, after rejection of mechanically flawed bars. The average results of these three bars are reported. Elongation was measured using a $ in. extensometer and reduction in area was determined using a profilometer to measure the area after fracture. INFLUENCE OF THERMOMECHANICAL TREATMENTS AND SECOND PHASE ON MECHANICAL PROPERTIES Results of mechanical testing are presented in Figs. 1 to 4 and in tabular form in the Appendix. A general conclusion from results obtained is that details of the thermomechanical treatments studied were important only insofar as they influenced the amount of residual second phase. Figs. 1 and 4 show the longitudinal properties obtained (regardless of thermomechanical

Jan 1, 1970

By G. L. F. Powell

g samples of Cu-20 wt pct Ag alloy have been mdercooled to a maximum of 197°C by melting under a slag of commercial soda-lime glass in a vitreous silica crucible. No grain refinement of the primary copper was observed in samples undercooled to the maximum of 197°C. When the samples contained a small amount of oxygen, the copper dendrites were partially recrystallized at undercoolings greater than 97°C. In previous papers&apos;-3 reporting the grain structure of undercooled silver and copper, it was observed that grain refinement was dependent on both undercooling and oxygen content. Grain refinement occurred in undercooled silver when the degree of undercooling exceeded the range 153" to 175"C, while in Ag-0 alloys (0.12 wt pct) fine equiaxed grains were exhibited when undercooling was greater than 50°C. Similarly, copper samples undercooled as much as 208°C displayed fan-shaped growth from a single nucleation site, while the grain structure of Cu-O alloys (0.08 wt pct) was fine and equiaxed at undercoolings larger than 150°C. Thus the presence of oxygen greatly reduced the undercooling at which grain refinement occurred. It was also observed that the change in grain size resulted from recrystallization and was not due to an enhanced nucleation rate in the liquid-solid transformation. It is possible that the influence of oxygen on recrystallization is due primarily to its presence as a solute element. walker4,&apos; reported that, although a grain size change did not occur in pure nickel until the undercooling exceeded 150°C, small grains were observed in samples of Ni-Cu alloy solidified at small and large degrees of undercooling. Jackson et al.6 suggested that the fine grained structure of the Ni-Cu alloy resulted from the melting off of dendrite arms during recalescence. This remelting process may occur in alloys as a result of segregation during freezing which causes a variation in liquidus temperature from point to point within a dendrite. It was therefore decided to undercool copper with a metallic alloying element to ascertain whether the presence of a metallic solute would have a similar effect to oxygen in inducing grain refinement. A Cu-Ag alloy was chosen, since both metals had been shown to behave similarly on undercooling. The alloy Cu-20 wt pct Ag was selected since the eutectic constituent outlines the initial growth form of the primary copper, so that the as-frozen grain structure is not obscured if subsequent recrystallization occurs. This paper describes the results of undercooling experiments carried out with Cu-20 pct Ag samples undercooled to a maximum of 197°C and the effect of oxygen content on the grain structure of the undercooled samples. EXPERIMENTAL Melting was carried out in a small cylindrical resistance furnace using "fine" silver granulate and oxygen-free high conductivity copper. The procedure adopted was to melt the required quantity of silver in air in a clean vitreous silica crucible for approximately 15 min, freeze, and add granulated commercial soda-lime glass to form a complete surface slag cover, after which the sample was melted and frozen several times to reduce the oxygen content. The glass slag cover was approximately 3 in. thick. Pieces of copper (=50 g) were added to the crucible until the required quantity to make 350-g samples of alloy had been charged. Each piece was added quickly to the crucible which was held at a temperature slightly above the melting point of silver. The piece was quickly pushed beneath the glass to minimize oxidation and any oxide coating usually decomposed before the piece had settled down into the silver. After the full quantity of copper had been added, the melt was stirred with a silica rod to hasten homogenization and a Pt/Pt 13 pct Rh thermocouple enclosed in a vitreous silica sheath inserted for temperature measurement. Heating and cooling curves were recorded on a potentiometric chart recorder fitted with a zero suppression unit. The milli-voltage range of the recorder was adjusted so that temperatures could be read to 1°C. Heating and cooling curves were taken every hour until three consecutive readings gave the same solidus-liquidus range, consistent with the solidus-liquidus range for this alloy composition by reference to Hansen and Anderko.7 Metallographic examination of samples frozen at this stage, failed to show any variation in composition from bottom to top of the ingot. Consequently, it was considered that the melt was homogeneous at this stage and undercooling experiments were then car-

Jan 1, 1970

By C. S. Yust, C. S. Morgan

ThIS note reports the observation of masses of dislocation etch pits around the weld necks of small single-crystal particles of calcium fluoride sintered to a cleaved face of a larger CaFz crystal. Crystal particles in the -50 +I00 mesh size range were placed on freshly cleaved CaFz surfaces and heated at 1250°C for 30 min in a tantalum container in an argon atmosphere. The sintered specimens were then etched at room temperature for 40 to 50 min in a 2 pct sulfamic acid solution which is a selective etch for dislocations in caF2.&apos; Figs. 1 through 3 show the masses of dislocation etch pits observed around weld necks after etching. In some cases, particles were gone after removal of the specimens from the furnace although weld necks were readily visible. In other instances, no etch pits formed around a weld neck. A possible cause of concentrations of dislocations on the crystal surface is mechanical deformation of the base crystal when particles are dropped on it. If such a deformation does occur, it would be much smaller than that caused by the light punching of a crystal with a sharp instrument which results in large concentrations of etch pits. However, crystals deformed by punching with the sharp instrument and annealed at the conditions of these experiments (1250°C for 30 min) before etching showed no concentrations of dislocation etch pits. It is obvious that dislocations from the much smaller deformations, possibly created when particles are placed on the surface, would also anneal out. Etching of large crystals which had particles placed on them in the usual manner but which were not heated showed no dislocation concentrations such as shown in Fig. 1. The magnitude of dislocation etch-pit concentrations did not vary with extensive variation of the cooling rate. The appearance of many of the etch-pit clusters is typical of a well-annealed condition, indicating that the dislocation concentrations formed before the specimen temperature was lowered. Therefore, it is evident that thermal stresses in the neck area did not create the deformation indicated by the presence of the dislocations. The possibility exists that the etch-pit concentrations at places where particles had been removed may be the result of deformation accompanying the fracture of the sintered bond. That this is not so was demonstrated by breaking off particles around which no etch pits occurred. Re-etching never resulted in the large concentrations observed at sintering sites. The stress available to effect material movement during sintering of two particles will depend on the geometry at the contact point but can easily exceed the macroscopic yield stress in CaFz systems. It appears that the plastic deformation observed results from sintering or simply from the weight of the small particles. It has been previously argued that plastic flow makes an important contribution to the initial densification of oxides having the fluorite crystal structure.2p3 If plastic deformation occurs, it would begin as soon as the temperature is sufficiently high

Jan 1, 1967

By R. Gibala

Internal-friction measurements on hydrogen-charged iron over the temperature range 4° to 300°K are reported. Two relaxation peaks, the hydrogen Snoek peak at 48 °K and the hydrogen cold-work peak in the range 145" to 2200K, are observed at 80 kc per sec. The effects of hydrogen-charging, aging, and deformation on the internal-friction results are determined and are used to show evidence of partitioning of hydrogen between solid solution and dislocations. The hydrogen-dislocation binding energy is estimated from the behaviors of the relaxation tiwzes and relaxation strengths of the Snoek peak and the cold-work peak. Its value is approxi,mately 6400 cal per mole. MANY investigators have demonstrated the usefulness of internal-friction measurements in determining the manner in which interstitial impurities interact with dislocations in bcc metals. Part of this success has resulted from the existence in bcc interstitial alloys of two anelastic relaxation peaks—the Snoek peak&apos; and the cold-work or Koster peak2 (designated hereafter by SP and CWP, respectively). The SP has its origin in the redistribution of interstitials in solid solution among sites made energetically nonequivalent by an applied stress. The rate at which the redistribution occurs, measured by the relaxation time for the process, is related in a simple way to the diffusion rate of the interstitial in the free solution. The relaxation strength is proportional to the concentration of interstitial in solid solution. The CWP appears to have its origin in the relaxation of an interstitial-dislocation complex for which the relaxation time at a given temperature is much longer than that for the SP. The relaxation strength depends strongly on the concentration of interstitial and the amount of deformation at relatively low concentrations and deformations.2-8 From the dependence of the relaxation strength on interstitial concentration, the SP and CWP may serve as measures of the concentrations of interstitials in free solution and bound at dislocations, respectively. Thus their behaviors have been used to investigate interstitial-dislocation interactions in Fe-C, Fe-N, and several refractory metal systems.&apos;-&apos; However, the Fe-H system has not been studied extensively,? even though disputes in recent years over the mechanism of hydrogen embrittlement in steels involve argument over the extent to which lattice hydrogen and hydrogen-dislocation interactions play an important role.?-&apos;&apos; Previous work on Fe-H indicates the internal-friction behavior to be qualitatively consistent with that for other systems. Apparently, both a SP and a CWP are observed in the temperature ranges 30" to 50°K and 100°to 140°K, respectively (at 1 cps). However, there is neither sufficient nor accurate enough information to identify convincingly these peaks with their supposed counterparts in other systems. Nor have there been any attempts to make quantitative use of these peaks to study hydrogen diffusion, aging, or interaction processes. In this paper, an attempt is made to obtain more complete information on internal friction of hydrogen in iron than presently available. Internal-friction measurements in the range 4° to 300°K on hydrogen-charged iron show that the two peaks discussed above are in fact the hydrogen SP and CWP. Several effects of hydrogen charging, aging, and deformation on these peaks are observed and are used to determine the partitioning of hydrogen between solid solution and dislocation sites in iron. EXPERIMENTAL Materials. The starting material for this investigation was a high-purity iron supplied by National Research Corp. as a 1-in.-diam rod. The following analysis was given (inwt pct): C, 0.004; N, 0.0003; 0, 0.007; P, 0.002; S, 0.005; Si, 0.006; Mn, 0.001; Cu, 0.002; Ni, 0.005; Cr, 0.001; Mo, 0.001. After an initial vacuum anneal (-5 XTorr) at 700°C, the rod was cold-

Jan 1, 1968

By David Kramer, Cecil G. Rhodes

Critical transport currents were measured as a function of perpendicular external magnetic field in Ti-22 at. pct Nb wire samples. These samples were heat-treated to yield w Phase precipitates at denslties ranging from 10 to 10 17cm-3. The Precipitates are ellipsoids of revolution with major axes of 50 to 1300A. Flux-Pinning by w precipitates is responsible for the high critical transport currents that were ob- ThE ability of a type II superconductor to sustain a zero-resistance transport current (Jc) in an external magnetic field (H) is due to the presence of micro-structural features which can impede the motion of magnetic flux penetrating the superconductor under the influence of a Lorentz force. Such features are referred to as pinning sites. The pinning strength is tained. A sample cooled from 800°C and annealed 1 hr at 450°C carried a critical tramport current of 10 amp per sq cm at 30 kG. Variations in the current-carrying ability of this alloy are due to changes in its pinning strength which is a function of precipitate density and composition and of the composition of the matrix. the reaction of the bulk superconductor to the Lorentz force and depends on the efficiency of the individual pinning sites and on their volume density. The super -current density increases with pinning strength, other things being equal. The above concepts are discussed in detail in a comprehensive review by Livingston and Schadler.&apos; In Ti-Nb alloys, as in other binary titanium alloys, the metastable hexagonal w phase usually forms below the p/a + p phase boundary near the titanium side of the phase diagram. Stiegler et a1.&apos; have summarized much of what is known about w phase in titanium and zirconium binary alloys. The present work deals with

Jan 1, 1968

By J. W. Downey, A. E. Dwight, M. H. Mueller, H. Knott, R. A. Conner

Sixty new ternary equiatomic compounds are reported with a hexagonal crystal structure that is isostructural with or very similar to Fe2P, D3h-P62m. HoNiAl is a typical example, with a, = 6.9893 ± 0.0003Å, C, = 3.8204 ± 0.003Å, and c/a = 0.54 7. Three holmium atoms occupy (g): x,0,1/2 three aluminum atoms occupy (f): x,0,0; one nickel atom occupies (b): 0,0,1/2; and two nickel atoms occupy (c): 4, + , 0. The nonequivalent 1(b) and 2(c) sites give rise to two sets of unequal interatornic distances (i.e., Ho-Ni and Al-NL in the case above), which account for the prevalence of Fe2P-type tertmry compounds and the scarcity of binary examples. Unit-cell constants are presented for the sixty compounds and density measurements on the compounds HoNiAl and UFeGa confirm that three formula weights are present per unit cell. Neutron and X-ray powder diffraction intensity measurements were made on CeNiAl and HoNiAl, respectively. The atomic posiLiotml parameters in CeNiAl were determined from neutron data to be x = 0.580 5 0.001 for cerium and 0.219 5 0.001 for aluminum. An investigation of the quasibinary section between the binary compounds CeNi2 and CeA12 revealed a new ternary compound CeNiAl. The compound has a hexagonal structure and is isostructural with the prototype compound Fe2P. Additional examples discovered or confirmed in this investigation provide a total of sixty ternary compounds that are isostructural with or closely related to Fe2P. Previous investigators1&apos;2 reported the unit-cell constants for the hexagonal compounds UFeA1, UCoAl, UIrA1, ZrNiAl, ZrNiGa, HfNiAl, and HfNiGa and the present investigation has confirmed that the compounds are isostructural with Fe2P. Independently, Steeb and petzow3 reported the same structure type for UCoAl, UIrA1, and UNiA1. However, the present results suggest a different atomic site occupancy for the component atoms in the three compounds. A detailed investigation of the relative positions of the three kinds of atoms in the compounds CeNiAl and HoNiAl will be discussed. EXPERIMENTAL PROCEDURE The equiatomic alloys were prepared from elements of 99.9+ pct purity by arc melting under a helium-argon atmosphere. After homogenization at temperatures from 700" to 900&apos; C, a metallographic examination was performed by conventional methods, and density measurements were carried out by the immersion method in CCl4. A powder sample was prepared for diffraction studies by crushing a portion of the annealed button. X-ray diffraction patterns were obtained with a Debye-Scherrer camera, in which the annealed powder was glued to a quartz filament, and indexed with the aid of a Bunn chart. Unit-cell constants were calculated from the computer program of Mueller, Heaton, and Miller4 and d spacings were obtained by the program of Mueller, Meyer, and Simonsen.5 The intensity values were calculated from the relation I, ~ (m)(L.P.)F2 by a computer program written by Busing, Martin, and Levy.6 The absorption and temperature correction factors were neglected. An X-ray study of HoNiAl was carried out to take advantage of: large differences in atomic scattering factors for holmium and aluminum, X-ray patters free of background darkening, negligible oxidation at room temperature, and negligible weight loss in the preparation of this alloy. The neutron diffraction studies were made on a powder sample of CeNiAl contained in a -in. diam V tube and a pattern was obtained with neutrons of wavelength The neutron scattering factors employed (x 10-12 cm). In contrast to the scattering amplitude for X-rays, cesium does not have the largest cross section, however, there is a sufficient difference in the neutron scattering amplitudes to distinguish between the atomic species. The neutron transmission was high, 86 pct; therefore, absorption corrections were not necessary for the cylindrical sample. Most reflections could not be observed individually, because of the relatively large unit cell (a = 6.9756 and c = 4.0206Å) and relatively short neutron wavelength; therefore, the intensity of grouped reflections was considered. The Kennicott modification7 of the Busing-Martin-Levy program6 was employed to determine the identity of the atoms at the various lattice sites and the positional parameters. RESULTS A structure for the prototype compound Fe2P was first reported by Hendricks and Kosting;8 however, the structure was in error. The correct structure, as reported by Rundqvist and Jellinek,9 is as follows. The unit-cell constants and volumes per formula weight (V/M) are given in Table I for the sixty compounds examined in this investigation and classified as Fe2P-type compounds. The structure type was determined initially from a comparison of the unit-cell constants of HoNiAl with other known examples of this structure type1&apos; and from the density of HoNiAl, given in Table 11. The density indicated that three formula weights comprised a unit cell, as in the prototype compound Fe2P. The assignment of the three species to lattice sites was made initially on the basis of atomic size. The large holmium atoms were assigned to the 3(g) sites that have a relatively large interatomic distance to nearest neighbor positions, the small nickel

Jan 1, 1969

By R. E. Miner, J. K. Jackson, T. L. Wilson

A study has been made of the transformation kintetics and morphology in gas-quenched Fe-5 pct Ni alloys. Massive ferrite or nlurtensite was found to form at temperatures in agreement with earlier results. Surface Preparation appeared to have the greatest effect in determining the type of transformation Product formed. Grain size change, subgrain morphology, and dislocation densities of massive ferrite were essen-tinlly invariant functions of cooling rate. The mar-tens~tic structures were typical of transformation in austenite grains of the order of the sample thickness. BY introducing the idea of a massive transformation in dilute iron-base alloys, Gilbert and Owen in 1962 served to stimulate a closer inspection of phase transformations in ferrous systems.&apos; A wealth of literature has followed concerned with the morphology,2-5 transformation mode,2&apos;3&apos;6-8 and thermodynamics of transformations.2,5,9 interesting controversies have resulted from the experimental observations; closer attention has been paid to the definition of massive transformations and still to be resolved is the Ms temperature of pure iron. The purpose of this note is to report some observations made in a detailed kinetic and metallographic examination of the transformations that occur in gas quenched Fe-5 pct Ni. The results are pertinent to the Ms extrapolations that have been made for pure iron and the observed substructure of massively transformed alloys. PROCEDURE The material used in this investigation was cast as a 5 lb vacuum induction melted, carbon deoxidized heat. The ingot was hot worked to a strip 0.10 in. thick, decarburized, and cold rolled to final thickness. Specimens were punched to sample shape and decarburized in wet hydrogen at 600°C. The chemistry of test specimens is indicated in Table I. Samples 1 by $ in., by thickness were resistance heated and rapidly cooled in an apparatus as illustrated in Fig. 1. Similar helium quenching apparatuses have been described previously;2,6&apos;10 the distinguishing feature of this apparatus is the nozzle geometry. Twin nozzles with three convergent-divergent, sonic ports were mounted perpendicular to the specimen for quenching purposes. The specimen temperature was monitored with an intrinsic 3 mil chromel-alumel thermocouple spot welded to the specimen and con- nected to an oscilloscope. A single switch stopped the current flow through the specimen, opened a gas flow solenoid valve, and initiated an oscilloscope sweep. Cooling rates were read directly from a photograph of the oscilloscope trace and the quenching rates quoted later were made at a point immediately prior to transformation on the trace. All quenching studies were conducted either under a vacuum of 10"-5 torr or a helium atmosphere. The sample geometry was chosen large enough to permit optical and electron microscopy to be performed on samples. The samples were electropolished for both types of examination in a perchloric-acetic solution. Electron microscopy was conducted on a HU 11A microscope operated at 100 kv. Dislocation densities were determined at the same general operating reflection (110) on foils thick enough to produce Kikuchi patterns. RESULTS AND DISCUSSION Transformation Temperature Observations and OD-tical Microscopy. The quenching results of this study are illustrated in Fig. -2(a). Samples which were treated in the as-decarburized condition transformed in a manner similar to that reported previously—a decrease in transformation temperature occurred as the quenching rate increased until a plateau region was reached. Within the scatter of the results obtained here, there was no break in the transformation temperature-quenching rate plot. This suggests no change in transformation mode. Further metallographic examination confirmed this observation. A martensitic transformation was obtained for similarly treated samples except that the surface was first electropolished. The Ms temperature was approximately 85°C below the plateau determined for the unpolished samples and cooling rates as slow as 2000°C per sec were adequate for producing marten-site. The transformation temperatures are in gen- / STRIP SAMPLE / COPPER I SAX/-/}&apos; / CONNECTOR-----A f, SON|C poRTS AC LEADS 3j ]j"I rofe[ \ Mf/yinK/iKj&apos;&apos;^ THERMOCOUPLE X-(^—iie"s*c? &apos; LEADS 1 INCH Fig. 1-—Schematic scction of gas quenching apparatus

Jan 1, 1970

By M. C. Flemings, T. Z. Kattamis

Dendrite morphology and grain size were studied in bulk samples of iron and nickel base alloys under-cooled up to 300°C. In the alloys studied, dendrite morphology gradually changes with increasing undercooling from the usual dendritic structure to a structure composed of cylindrical dendrite arms. At a critical undercooling of approximately 170°C in these alloys there is an abrupt transition to a fine-grained structure of spherical morphology. Final dendrite-arnz spacing of melts nucleated at less than the critical undercooling decreases with increasing undercooling and with decreasing distance from a chilled surface. Grain size of melts nucleated at greater than the critical undercooling decreases similarly with these factors. It is concluded that structure coarsening, with reduction of surface area as driving force, is the principal mechanism determining final dendrite-arm spacing in melts nucleated at small undercoolings and grain site in melts nucleated at large undercoolings. IN solidification of highly undercooled melts, nuclea-tion and growth of the solid is accompanied by a rapid release of latent heat of fusion. The heat release is sufficiently rapid in bulk specimens that it takes place essentially adiabatically with respect to the surroundings; hence the specimen heats up ("recalesces") to some maximum recalescence temperature. For bulk liquid metals and alloys, a simple thermal balance shows the undercoolings obtainable in bulk samples are not sufficient to lower the maximum recalescence temperature below the equilibrium solidus temperature. Hence, some liquid always remains at the end of recalescence; this liquid must solidify by rejection of heat to the surroundings. Metals, including iron and nickel base alloys, normally freeze with only a few degrees of undercooling. In general, nucleation begins on impurity particles present in the metal, at a "heterogeneous nucleation temperature" that is quite close to the equilibrium liquidus temperature. Very small droplets of metal can be undercooled considerably before nucleation occurs,1-4 presumably because subdivision of the liquid reduces the probability of solid impurity in a given droplet. Following early work on metal droplets,&apos; a series of studies has shown that it is possible, without great difficulty, to undercool bulk samples of many metals and alloys. Undercoolings obtainable are approximately two tenths of the melting point for nickel, iron, copper, and other metals and alloys.5-9 Specimen sizes have generally been in the range of 50 to 500 g. Studies on undercooling to date have been concerned primarily with techniques of undercooling and with nucleation and growth kinetics. Only limited consideration has been given to dendrite morphology in under- cooled alloys. One such study, in bulk Cu-Ni alloy,8 showed that at small undercoolings a typical dendritic structure was obtained. At undercoolings the order of 175°C the structure of a Cu-40 pct Ni alloy became "ray or starlike", and a dense network of subbound-aries appeared. At still larger degrees of undercooling, of the order of 250°C, the structure became more random and included an ensemble of globular forms. Comparable results were obtained by walker10 on Cu-Ni alloys, and by Kamenetskaya et al.11 in research on Cu-Ni, Sb-Bi, Fe-Ni, and Fe-Cr alloys. In this work, study was made of the processing parameters influencing dendrite morphology and grain size in undercooled alloy melts. Experiments were specifically designed to show the effects of coarsening ("ripening") during solidification on final casting morphology. EXPERIMENTAL PROCEDURE Apparatus used was patterned after that of Walker,10 Fig. l(a). Melting was by induction under reduced pressure of helium. Two different types of crucible materials were used; there was no difficulty in obtaining substantial undercooling in both types of materials. Alumina crucibles were used for the bulk of the runs made, with a glass coating separating the metal from the crucible walls. Other runs were made using fused silica crucibles with or without slag coating. A graphite susceptor was employed around the crucible to aid in melting and to reduce melt stirring. The major portion of the experimental work was on

Jan 1, 1967

By G. E. Pellissier, P. H. Salmon Cox, B. G. Reisdorf

Banding that occurred in plates rolled from the early production heats of 18Ni(250) maraging steel is described and related to the segvegation of certain alloying elements (nickel, molybdenum, titanium), the extent of which was quantitatively evaluated by means of electron-microprobe analysis. The effect of banding on mechanical properties is discussed, with particular reference to observed directional differences in plane-strain fracture toughness of plates. It is shown that banding originates as interdendritic segvegation during ingot solidification and persists in some degree through normal soaking and hot reduction to plate. The results of the study showed that heating sections of small laboratory-cast ingots at 2200°F for 4 hr was sufficient to markedly reduce microsegregation and to considerably improve mechanical properties. Hot rolling of 7-in.-thick ingot sections to 1/2-in.-thick plate effected a similar reduction of microsegregation, but resulted in even greater increases in ductility and toughness than that obtained by homogenization treatment alone. DURING the past few years, considerable attention has been directed towards the low-carbon, high-alloy maraging steels and in particular towards the 18Ni-8Co-5Mo-0.4Ti alloy. The steels of this group, having an excellent combination of high strength and toughness, have a number of advantages over their more conventional medium-carbon low-alloy, quenched-and-tempered counterparts. In the annealed condition, the maraging steels are in the form of a ductile marten-site; aging at a relatively low temperature, typically 900°F for 3 hr, increases greatly the strength through the precipitation of intermetallic compounds. One problem in the early production heats of maraging steel was that the finished plate frequently displayed a banded structure. Previous work on other steels1-&apos; had established that banding in wrought products is either a direct or an indirect consequence of chemical segregation, which occurs during solidification and persists to some extent through normal thermal and mechanical treatments. For example, Smith and others: in a study of low-alloy steel, were able to correlate the severity of banding in the wrought product with the degree of interdendritic segregation of nickel and chromium in the as-cast ingot. The effect of banding on the mechanical properties of steels is usually considered to be detrimental, although there is only limited evidence to suggest that a marked improvement in properties can be obtained with less heterogeneous structures. Comparison of the longitudinal and transverse tensile properties of banded and of homogenized 4340 steel showed that only the transverse ductility was improved by homogenization, but even then the improvement was not commercially significant.&apos; Conversely, homogenization of through-the-thickness tension specimens of quenched-and-tempered steel plate, containing 1.47 pct Mn, increased the strength by as much as 10 pct and the tensile ductility by at least a factor of twos5 This improvement was related to the elimination of manganese-rich bands, which also are one of the factors responsible for cold cracking in the heat-affected zone of metal-arc welds.7 In the present study the nature and severity of banding in early commercial 18Ni(250) maraging steel plate and in laboratory-melted 18Ni(250) maraging steel plate was determined. The effects of banding on plane-strain fracture toughness and the effects of thermal homogenization treatments on the strength, tensile ductility, and toughness of 18Ni(250) maraging-steel as-cast ingots and rolled plate were evaluated. In addition, the effects of hot deformation by rolling on the mechanical properties of ingots were determined. 1) STUDIES OF BANDING IN EARLY PRODUCTION PLATE The chemical composition of the steel (A) used in this part of the investigation is shown in Table I. Banding was not clearly evident in either as-rolled or annealed* plate, but annealed and agedc** plate had a banded structure. The typical banded condition, Fig. 1, consists of layers of unetched austenite (white) and dark-etching martensite in a light-etching martensitic matrix. X-ray diffraction measurements showed that this steel contained more than 6 pct austenite. An electron-probe X-ray microanalyzer (using a focused beam of electrons) was used to determine the composition of the bands and of the material between the bands with respect to the main alloying elements— nickel, molybdenum, titanium, and cobalt. The recorded X-ray intensities were converted to concentration values with the use of a standard of similar composition. To facilitate probe positioning, all analyses were conducted on specimens that had been given a light etch. The influence of this etching on the analytical results was negligible; analyses made on the identical area before and after etching yielded essentially the same concentration values. The results of the electron-microprobe analyses at selected points revealed that the layers of austenite and adjacent dark-etching martensite contained greater amounts of nickel, molybdenum, and titanium than did the surrounding matrix, Table 11. The austenite layers

Jan 1, 1968