Search Documents

By A. T. Churchman

The deformation modes of rhenium have been identified as those typical of the hexagonal metals, titanium, zirconium, and beryllium whose c/a ratios, in common with rhenium, are less than ideal for close packing. Slip is observed on (1010), (1011), and (0001) planes and twinning on (1121), (1122), and (1012) planes. The very high rate of work hardening is believed to be associated with intersecting partial dislocations on two (1010) systems which can combine to form sessile barriers. If the stacking fault energy is low, as postulated by Seeger, these barriers should be strong and not easily bypassed by cross slipping. Such an explanation could also account for the very small temperature dependence of the yield stress which was observed. RHENIUM is interesting scientifically as a member of the group of high melting point hexagonal metals: titanium, beryllium, and zirconium with a c/a ratio less than that for ideal close packing. Unlike them, however, it work hardens at a very high rate. This rate is greater and continues to a much higher degree of deformation than for nickel, normally considered to have a high rate of work hardening. This paper presents experimental observations on the modes of deformation of rhenium and, by comparison with other hexagonal metals, some speculation on the cause of the high work hardening. MATERIALS Johnson, Matthey rhenium powder of both 99.9 pct and 99.5 pct purity, see Table I, was compacted at 10 tons per sq in., part sintered at 1350°C in vacuo, and finally arc melted in a "gettered" argon atmosphere arc furnace to produce small buttons. Little difference was observed in the as-cast hardness or working down behavior of the two purities suggesting that either silicon and potassium do not have a significant effect on the working properties of rhenium or they were lost during arc melting. SPECIMEN PREPARATION The cast structure was broken up by cold-rolling with inter-stage annealing at 1600o or 1800°C in a vacuum high-frequency furnace using a tungsten susceptor. Strip for tensile testing was taken from two thicknesses of material 0.011 and 0.064 in. The former with intermediate anneals at 1800°C had a grain size of 900 grains per sq mm, while the latter with inter-stage annealing at 1600°C had a grain size of 3600 grains per sq mm. A coarse grain size was obtained by secondary recrystallization in a half button cold-worked by 30 pct reduction. Annealing times of from half an hour to several hours at 2200° to 2600°C in a "gettered" argon atmosphere arc furnace1 resulted in grains of up to 2 mm diam.

Jan 1, 1961

By J. E. Dorn, L. A. Shepard

LOW and Gensamer' demonstrated a number of years ago that the yield point phenomenon in mild steels was associated with the presence of fer-rite soluble carbon or nitrogen. More recently the yield phenomenon in body-centered-cubic metals containing interstitials was rationalized by Cottrell' in terms of a simple dislocation model. Interstitial atoms interact with dislocations in two ways; they cause not only local expansions but induce local tetragonality in the lattice. Consequently, interstitial~ interact with the hydrostatic tension and shear components of the stress about dislocations. They tend to migrate toward the expanded regions of edge dislocations and to assume sites that relieve the shear stresses of screw dislocations. Thus, a dislocation saturated with solute atoms constitutes a lower free energy state than that obtained when the dislocation threads through the average composition regions of the matrix. A greater stress will be required to separate the dislocation from its atmosphere than to move the dislocation through the matrix. This factor gives rise to the upper yield stress, which is required to unleash a series of dislocations in a localized region. This local yielding is propagated across the specimen to form a thin band of plastically deformed material known as a Lueder's band, making an angle of about 45" to the stress axis. Once the band has formed, deformation continues at the lower yield stress by the spreading of the Lueder's band in the direction of the applied stress. Undoubtedly the spreading of Lueder's bands at the lower yield stress is accomplished by the high stress concentrations at the band fronts, which serve to induce continued unlocking of new dislocations in advance of the migrating band fronts. Cottrell and Bilby have shown that the dependence of the yield point on temperature can be deduced by assuming that thermal fluctuations aid the stress in unlocking small dislocation loops from their solute atmospheres. Once a loop that exceeds a critical size has been nucleated, the entire locked diqlocation is released and can migrate. Fisher4 simplified this analysis by assuming that the locking forces were short range, so that if the dislocation loop were displaced only one Burgers vector from its atmosphere, it would be unlocked. Applying his model to the special case of delayed yielding under a constant stress of the order of the upper yield strength, he demonstrated that the delay time 7 for yielding should depend on stress and temperature according to where A and B are constants, G is the shear modulus, and u and T are the resolved shear stress and absolute temperature, respectively. Cottrell and Bilby, Fisher, and Fisher and Rogers' have shown that the above deductions are at least in qualitative harmony with the experimental facts. A number of investigators5-0 have shown that the yield point phenomenon can also be induced in sub-stitutional alloys of face-centered-cubic metals. In general such yield points are not as pronounced as those encountered in body-centered-cubic metals containing interstitials. The yield point phenomenon in these materials is usually enhanced by prestrain-ing at low temperatures and aging at intermediate temperatures. Undoubtedly the yield point phenomenon induced by strain aging substitutional alloys also results from locking of dislocations. But the locking of dislocations in substitutional alloys of face-centered-cubic metals differs somewhat from interstitial locking of dislocations in body-centered-cubic metals. Substitutional elements in face-centered-cubic lattices cause only radial displacements of the adjacent lattice points. Consequently, only the edge components of dislocations can be locked by the mechanism suggested by Cottrell. Additional locking, however, can be obtained by the Suzuki mcchanism.10 In face-centered-cubic metals, dislocations exhibit lower energies when they are present in the

Jan 1, 1957

By W. J. Helfrich, R. A. Dodd

Binary aluminum solid-solution alloys containing various amounts of silver, magnesium, and zinc were prepared by careful directional solidification, and the hydrostatic and X-ray densities were compared. With the exception of the Al(Ag) alloys, the X-ray densities were consistently greater than the hydrostatic measurements, in agreement with earlier observations by Ellwood. In contrast to Ell-wood's interpretation in terms of vacant lattice sites associated with Brillouin zone effects, a tentative explanation based on the existence of solidification microshrinkage was favored. This hypothesis was confirmed by an examination of Al(Zn) alloys prepared by vapor diffusion of zinc into aluminum. The hydrostatic and X-ray densities were now in very close agreement, and it was concluded that the filling of Brillouin zones in aluminum solid-solution alloys does not necessarily result in the formation of defect structures containing an excess of vacant lattice sites. ThE existence of defect structures of the vacancy type in alloys in which the excess vacancies have an electronic rather than a thermal or mechanical, and so forth, origin is well recognized. Examples of incomplete lattices of this type are to be found in the Ni-Al,1-3 Fe-Ni-A1,4 c~-Ni-Al,5 Fe-Cu-Al,= and Co-A17 systems. These defect structures are of a special kind in that the intermediate phases possess an ordered atomic arrangement or superlattice, and in some instances the vacancy concentration may be unusually large, e.g., at 45.25 at. pet Ni in NiA1, approximately 8.8 pet of the lattice sites are unoccupied. Ellwood8-10 has reported similar defect structures in the aluminum solid solution alloys of the Al-Zn and A1-Mg systems and in alloys of the Au-Ni system." In Al(Zn) the (apparent) vacancy concentration rose, somewhat irregularly, to a maximum of about 2 pet vacant sites at 25 at. pet Zn, while in Al(Mg) the (apparent) vacancy concentration increased continuously to 1.7 pet at 15 at. pet Mg. An explanation in terms of Brillouin zone overlap was attempted, although Pearson12 has pointed out the difficulty of reconciling the observations with zone theory. However, the possibility of the effect being caused by the Fermi surface just touching a plane of energy discontinuity inside a prominent Brillouin zone has, in general, been accepted. In fact, Massal-ski13 has interpreted Ellwood's8 observations as confirmation of Leigh's14 theoretically predicted zone overlap occurring at approximately 2.67 electrons per atom. Unfortunately, Massalski was apparently unaware that Ellwood9 had revised his earlier results considerably, and the revised data did not confirm Leigh's analysis. Ellwood's clata were reexamined by the present authors who noted a possible correlation between the percentage defects as a function of alloy composition and the temperature interval of solidification measured from the respective equilibrium diagrams. This suggested an explanation in terms of shrinkage porosity rather than vacant lattice sites, and pointed to the desirability of reexamining appropriate alloy systems using: both Ellwood's method of specimen preparation (casting followed by wrought fabrication) and alternativ'e methods, i.e., diffusion, which might be expected to minimize, or even completely obviate, microporosity. ALLOY PREPARATION 1) Cast Allolys and Aluminum Single Crystals. Al(Ag), Al(Mg;l, and Al(Zn) alloys of various compositions up to 20 at. pet silver, 13.5 at. pet mg, and 30 at. pet Zn were prepared by melting under helium and casting into graphite molds. In the first two systems, the maximum alloying addition was quite close to the limit of solid solubility, but the possibility of transformation to a' during quenching somewhat restricted the suitable Al(Zn) composition range. The alloys were prepared from high-purity aluminum, a lot analysis showing 0.002 wt pet Cu, 0.002 wt pet Fe, and 99.996 wt pet A1 by difference. The silver, magnesium, and zinc were of 99.99+, 99.98+, and 99.998 wt pet respectively. Each composition was analyzed chemically. The as-cast ingots measured 7/16 in. diam and 5 in. length. One in. was removed from the top of the ingot, and the bottom 3 in. was machined to 0.275 in. diam; a point was also machined on the smaller diameter end. The remainder of the original ingot served as a top riser during subsequent remelting and controlled solidification. The machined ingots were now remelted using a Bridgman soft-mold technique to ensure directional solidification and, therefore, a minimum of micro-shrinkage. Alumina powder was used as mold material contained in an alundum thimble, and this crucible was placed in a helium-filled Vycor tube. The assembly was lowered through a suitable temperature gradient at approximately 0.5 in. min-l, and the risered portion of the casting was subsequently removed by sawing.

Jan 1, 1962

By W. C. Leslie, R. M. Fisher, K. G. Carroll

J. S. Bowles and J. K. Mackenzie (Commonwealth Scientific and Industrial Research Organization, Mel- bourne, Australia)—The authors are to be congratulated for giving the first direct experimental proof that the observed macroscopic strain accompanying marten-site transformations is not necessarily a shear. We

Jan 1, 1953

By George Mah, Charles Wert

Internal-friction peaks caused by diffusion of oxygen and nitrogen have been observed in ytterbium. They are thought to be caused by the redistribution, under stress, of strain dipoles around an interstitial oxygen or nitrogen and a neighboring substitutional impurity. With the use of a simple geometrical model, diffusion coefficients for oxygen and nitrogen between special interstitial sites have been calculated. a) APPLICATION OF INTERNAL FRICTION TO MEASUREMENT OF DIFFUSION RATES IN DISSOLVED INTERSTITIAL ATOMS In bcc metals, the interstitial atoms occupy the centers of cube faces (0, 1/2, 1/2), or their equivalents, the center of the cube edges (0, 0, 1/2). An interstitial atom in this position causes an aniso-tropic distortion in the lattice. When stress is applied, mechanical relaxation can take place by the movements of the interstitial atoms. This relaxation has been used to obtain information concerning the movements of the interstitial atoms in the bcc metals. Data for these alloys have been compiled by Stanley and Wert. Other researchers have extended the investigation of interstitial diffusion to the close-packed metals. Gupta and weinig2 found an oxygen peak in a titanium, the height of which is linearly dependent on the oxygen concentration. They assumed, therefore, that they were dealing with movement of atomic ally dispersed oxygen in titanium. KG and wang3 determined that the diffusion coefficients of carbon in fcc steels and in nickel obtained by internal-friction methods were consistent with those obtained by macrodiffusion methods at much higher temperatures. Bisogni found oxygen and nitrogen peaks in hafnium by use of which he deduced the diffusion coefficient of these gases in hafnium. He observed further that the half-widths of these peaks corresponded almost exactly with those of a single-relaxation process; he assumed it to be caused by movement of atomically dispersed oxygen and nitrogen. From these studies, the deduction can be drawn that, in general, diffusion data can also be obtained for the interstitial diffusion in close-packed metals (or more precisely, in slightly impure close-packed metals). One group of such metals for which little data exist for the diffusion of dissolved oxygen and nitrogen is the rare earths. They have great affinity for gases, which enter solution interstitially. In this investigation results were obtained for the Yb-O and Yb-N interstitial solid solutions with traces of substitutional impurities; these solid solutions are of fcc structure. b) MECHANISM OF THE RELAXATION IN FCC CRYSTALS In the fcc structure, an interstitial gas atom is usually situated in the octahedral position (1/2, 1/2,

Jan 1, 1964

By T. H. Alden

T. H. Alden (General Electric Research Laboratory)—This paper as well as earlier ones of Dr. Wood represent an important contribution to the experimental description of fatigue fracture. The mechanism of fracture proposed by the authors, however, is not established by this data nor supported by other data existing in the literature. Although taper section metallography provides a rather detailed picture of fatigue crack geometry, photographs so obtained must be interpreted with care. The narrow bands revealed by etching, frequently associated with surface notches, are labeled by the authors "fissures". Measurement shows, taking into account the 20 to 1 taper magnification, that the depth of these structures is at most 2 to 3 times the width. This distinction is important in the conception of a mechanism of crack formation. It is difficult, for example, to imagine a deep, narrow fissure arising from a "ratchet slip" model. A surface notch, on the other hand, may form easily by this mechanism. The notches observed in the present work are the subsurface evidence of the surface slip bands or striations in which fatigue cracks are known to originate.4-6 It is clear that an understanding of the structure of these slip bands is of key importance in understanding the mechanism of fracture. The evidence presented shows that these regions etch preferentially, possibly because they contain a high density of lattice defects, or as the authors state equivalently, because they are "abnormally distorted." However, it is not possible to conclude that the distortion consists of a high density of vacant lattice sites. The fact of a high total shear strain in itself does not assure a predominance of point defects as opposed to other defects, for example, dislocations. Other evidence in the literature which suggests unusual densities of point defects formed by fatigue7-' refers not to the striations or fissures, but to the material between fissures (the "matrix"). If a choice must be made, the preferential etching would seem to be evidence for a high dislocation density, since dislocations are known to encourage chemical attack in copper;g no such effect is known for the case of point defects. A third alternative is that the slip bands are actually cracked, but that near its tip the crack is too narrow to be detected by the authors' metal-lographic technique. In this case the rapid etching can be readily understood in terms of the increased chemical activity of surface atoms. Unless a vacancy mechanism is operative, the motion of dislocations to-and-fro on single slip planes will not lead to crack growth. Point defect or dislocation loop generation are the principal non-reversible effects predicted by this model. In any case, the nonuniform roughening of the surface in a slip band6 requires a flexibility of dislocation motion which is not a part of the to-and-fro fine slip idea. The same is probably true of crack growth by a shear mechanism. Either some dislocations must change their slip planes near the end of the band and return on different planes,'0 or dislocations of opposite sign annihilate." The mechanism by which these processes occur in copper at room temperature or below is that of cross slip. Thus cross slip appears to be essential to fatigue crack growth.6'10"12 The fact that a tensile stress opens the slip bands into broad cracks does not indicate the structure of the bands or the mechanism by which cracks form. The charactersitic concentration of slip into bands during fatigue shows a low resistance to shear strain in these regions. (This fact in itself may be inconsistent with a high concentration of vacancies.) The authors contend also that continuing shear produces an additional mechanical weakening so that the bands fracture easily (are pulled apart) under the influence of the superimposed tensile stress. It is equally possible that the only weakness is a weakness in shear, that the crack propagates by a shear mechanism, and that subsequently the tensile stress pulls the crack apart. Even the direct observation of bands opened by a tensile stress would not be conclusive since, as argued above, they may be fine cracks. The same argument applies to internal cracks, their existence in the presence of a tensile stress not indicating the mechanism of formation. Internal cracks originating in regions of heavy shear have also been seen following tensile deformation of OFHC copper,13 so that this mode of fracture is not unique to combined tensile and fatigue straining. The authors point out in their companion report14 that 90 pct of the cracks formed during pure tor-sional strain were within 8 deg of the normal to the specimen axis. If the tensile stress were an important factor in crack propagation, it is surprising that the cracks cluster about the plane in which the normal stress vanishes. Similarly, a study of zinc single crystals showed that for various orientations the life correlated well with the resolved shear stress on the basal plane,'= and was not dependent on the normal stress across this plane. W. A. Wood and H. M. Bendler (Authors' reply) -Dr. Alden's discussion emphasizes the essential point in the relation of slip band structure to

Jan 1, 1963

By W. C. Leslie

W. C. Leslie (Edgar C. Bain Laboratory for Funda mental Research)—This investigation, with its com bination of high-purity metal, calorimetry, and metallography, will serve as a model for annealing studies for a long time to come. The evidence for a competition between recovery and recrystalliza-tion is particularly convincing. The demonstration of edge-nucleated recrystallization was so clear that it may obscure the necessity for other types of "nucleation" sites; otherwise, single crystals of aluminum could not be recrystallized after cold work. At least three types of sites have been found to operate in iron: 1) high-angle boundaries, probably in the same manner as in aluminum, 2) matrix sites, 3) inclusions or second-phase particles. In each instance, the cells developed during cold work and perfected during recovery are the "nucle for recrystallization. Observations by ourselves and others of the dislocation structure of cold-worked metals and of the structural changes that occur during annealing have led us to doubt the validity of the basic assumption of the Lucke-Detert theory, and of the modification developed by Gordon and Vandermeer, that during recrystallization of a metal containing foreign elements in solid solution a high-angle boundary is ad vancing into a cold-worked matrix having a random distribution of solute atoms. We contend that an es sential part of the cold-working and annealing of solid solution alloys is the trapping of solute atoms by the low-energy "wells" afforded by individual dislocations and by dislocation arrays. If cells are formed during cold work, the cell walls are stabilized by this concentration of solute atoms. Thus, solutes inhibit recrystallization not only by decreas-ing the rate of high-angle boundary migration, but also by preventing the formation of high-angle boundaries by subgrain growth or coalescence, i.e., solutes can inhibit both "nucleation" and growth. In addition to stabilizing the dislocation Structure, the solute-dislocation interactions may produce clusters of solute atoms which are not as readily assimilated into the recrystallized grains as are individual solute atoms. There is an additional complication. The dislocation structure formed upon cold working a dilute solid solution may not be the same as that formed during cold working of the pure solvent metal. The solute can either enhance or minimize the formation of cells during cold working. Both effects have been observed in binary alloys of iron. The annealing process is inextricably connected with the mechanisms of strain hardening and solid solution hardening. Although the correlation between experimental boundary migration rates and the predictions made from the theoretical equations are impressive, it should be mentioned that in at least four other instances (Pb-Ag and pb-Au,15, Fe-Mn,16, Fe-Mo)17 the agreement was rather poor. In brief, while it is probable that the migration of high-angle boundaries is held back by solutes in the manner described, this is only a partial explanation of the total effect of solutes upon recrystallization of cold-worked alloys. Paul Gordon and R. A. Vandermeer (author's reply)— The authors first wish to thank Dr. Leslie for his compliments of this work. It is perhaps worth pointing out that some of Dr. Leslie's remarks are directed toward subject matter covered in two earlier papers in our work.18,19 We agree with Dr. Leslie's main contention that the exact nature of the metal structure in the vicinity of a boundary should have an effect on the boundary migration. The theory of Lucke and Detert does not take such detail into account, nor does it account for orientation effects on the migration rates. We assume that since our data checks the theory so well, the effects of detailed structure are statistically averaged out by the polycrystalline techniques used just as are the effects of orientation factors.

Jan 1, 1963

By Kenneth A. Moon

Kenneth A. Moon (U.S. Army Materials Research Agency)—The authors are to be congratulated for a very interesting and valuable paper. Their discussion of the structural implications of the results shown in their Fig. 5, however, requires a small correction. The model of Speiser and Spretnak with 0 = 1 and z' = 2 is perfectly reasonable for the Ti-O a phase, but Eq. [3] is valid only for solutions sufficiently dilute that the number of empty sites excluded by more than one filled site is negligible. The composition at which intrinsic saturation occurs therefore cannot be deduced from Eq. [3], but but must be decided by consideration of the structural details of the phase in question. In this case, intrinsic saturation is expected not at the composition Ti3O but at Ti2O, because Ti2O has the anti-Cd structurel4 for which each filled octahedral site has two nearby empty sites, one in the hexagonal plane immediately above it, and one in the similar plane below it. The other two models, with ?=1/3 and 1/2, imply a distinction between octahedral sites in pure titanium which is not easy to justify. The problem of extending Speiser's and Spretnak's treatment in a general way to more concentrated solutions will be the subject of a forthcoming publication by the writer. M. T. Hepworth and R. Schuhmann, Jr. (authors' reply)—The authors wish to thank Dr. Moon for calling to their attention the paper by Holmberg which presents the results of X-ray studies of Ti-O solutions ranging from 0 to 33 at. pct 0 and quenched from various annealing temperatures between 400" and 1800°C. Within these ranges, Holmberg found three types of phases: 1) At high oxygen contents (above 25 at. pct) and low annealing temperatures, he found the anti-Cd(OH)2 structure referred to by Dr. Moon. In this structure each titanium atom is in contact with 3 oxygens and each oxygen is in contact with 6 titaniums, the "available" oxygen sites corresponding to every other layer of octahedral sites in the titanium matrix. The limiting composition is Ti2O. However, this anti-Cd(OH)2 structure was not observed for samples containing 25 at. pct 0 or less. 2) For the specimen containing 25 at. pct 0 annealed at 400°C an ordered Ti3O structure was observed. This structure is related to the anti-Cd(OH)2 structure but differs from it by providing only two oxygens adjacent to each titanium atom and thus is consistent with the model represented by Eq. [5] in our paper, with 6 = 1/3, z' = 0. 3) For dilute solutions and for more concentrated solutions annealed at higher temperatures, the structure corresponds to that of the metal with random distribution of oxygens among all the octahedral sites. Thus, it is interesting to observe that the thermo-dynamic indications of ordering in the vicinity of Ti3O can now be supported qualitatively at least by Holmberg's X-ray evidence of the existence of an ordered phase of the composition Ti3O. That is, for solutions with oxygen contents close to that of Ti3O, both the thermodynamic data and the X-ray data are more consistent with models based on the ordered structure of Ti3O than they are with the model which Dr. Moon suggests corresponding to "intrinsic saturation" at Ti2O.

Jan 1, 1963

By J. D. Meakin, H. G. F. Wilsdorf

Using a combined decoration and etching technique the dislocation structure of annealed and deformed a brass has been studied. Annealed crystals revealed a low density forest and well-developed subboundaries; lightly deformed crystals contained discrete groups of dislocations. The dislocation density and the number of dislocations in a group were obtained from the micrographs. Using slip-line data, the mean path of a dislocation and the configuration of groups along an active slip plane have been deduced. Observations on secondary and cross-slip are reported. It has been the aim of many investigations to obtain detailed knowledge of the dislocation patterns which are present in metals before and after their deformation. The "decoration" of dislocations with impurity atoms has been considered as one of the promising experimental approaches, and much work has been done to develop this technique for revealing dislocation sites in metals. Following the early work by Castaing,' Castaing and Guinier,' and Lacombe and Berghezan~ on aluminum-rich aluminum-copper alloys, dislocations in this material have been studied extensively by others.+' In these alloys the dislocation sites act as nuclei for the precipitation of the second phase. The main results of the investigations on aluminum with copper are: i) the confirmation of the earlier contention that subboundaries consist of dislocation walls, ii) that many more dislocations are found in slip bands than in regions where less glide had taken place, iii) the observation of individual dislocations, lying nearly parallel to the surface investigated, and iv) that parts of dislocation loops, apparently emitted from a dislocation source, could be made visible. Recently, Jacquet, Weill, and Calvert have succeeded in revealing nearly concentric dislocation loops in quenched A1-4 pct Cu and thus indicated directly the existence of dislocation sources in a fcc metal specimen of normal dimensions. Another decoration method developed by Dash10'11 and applied to silicon crystals makes use of diffusing copper to the dislocations from a surface deposition. The dislocation pattern can then be observed by an infrared technique. His results include evidence for symmetrical and spiral Frank-Read sources, and for arrays of dislocation loops which follow simple crys-tallographic directions. Recently Low and Guard" have studied the dislocation structure of silicon-iron using carbon for the

Jan 1, 1961

By R. I. Jaffee, F. C. Holden, H. R. Ogden

Alpha solutes increase the strengths of Ti-Mn alloys through solid-solution strengthening. The substitutional a addition, aluminum, decreases, and the interstitial solutes, carbon and nitrogen, increase the rate of nucleation and growth of a from ß. The best combinations of properties of a-ß alloys are obtained when there is a sufficient quantity of a phase in the structure to dissolve the a solutes. OF the many different titanium-base alloy systems, the predominant alloy type is the a-ß alloy. The properties of the a-ß alloys are dependent on solid-solution strengthening and heat-treatment effects involving the a-ß ratio and transformation reactions. Another variable which influences the mechanical properties of a-ß alloys is the a-stabilizer content of the alloy. An a solute may be present as an intentional addition, such as aluminum, or as an impurity element, such as carbon, oxygen, or nitrogen. It is known that these a stabilizers, when added to titanium, form single-phase alloys which are not heat treatable but which obtain their strength from solid-solution strengthening. Thus, it would be expected that a additions to a-ß alloys would increase the strength of the alloys by solid-solution strengthening of the a phase. In addition, they would affect the transformation kinetics of the ß-to-a reactions and other processes based on the instability of the ß phase. The effects of heat treatment and structure on the mechanical properties of Ti-Mn alloys have been shown in a previous paper.6 This system offers a good base to demonstrate the effects of typical a solutes on the properties of a-ß alloys. The three a solutes described in this work are aluminum, representative of a substitutional a solute, nitrogen, representative of an interstitial a solute, and carbon, representative of an interstitial compound-forming element. The effects of heat treatment and microstructure on the properties of a alloys containing these three elements are described in concurrent publications. Some of these data are used for base-line points in several of the curves used for illustration herein. Experimental Procedures Iodide titanium was used as the base for all of the alloys studied in this work. The alloys were prepared as ½ lb ingots by double arc melting in an argon atmosphere. The ingots were forged to ¾ in. rounds, vacuum annealed for 6 hr at 900°C at a pressure of 10 ' to 10-5 mm of Hg to remove hydrogen, and hot swaged to 1/4 in. diam rod. After me- chanical descaling, test specimens were prepared for heat treatment. The alloys used in this study together with the fabrication temperatures are given in Table I. Heat treatments were done in argon. For the most part, the specimens were sealed in Vyeor capsules under a partial pressure of argon. Quenching was accomplished by breaking the capsule under water. Other cooling methods used included oil quench, argon cool (simulated air cool in an argon atmosphere), and furnace cool. The times for the various heat-treating temperatures are given in Table 11. The tests performed on the alloys consisted of tensile tests on ? in. diam specimens, hardness tests, and microimpact tests. Specimen sizes have been adequately described in a previous publication.' The micrographs presented in this paper were taken from specimens cut from the shoulders of broken tensile specimens. Final polishing was done with Linde B on a slow-speed wheel, and the specimens were etched with a 1½ HF — 3½ HNO, solution. Ti-N-Mn Alloys The transformation diagram and microstructures of the Ti-0.1 pct N-Mn alloys used in this investigation are given in Fig. 1. The effect of small nitrogen additions on the binary Ti-Mn diagram is to raise the ß-transus temperature with little effect on the a solubility of manganese. Also, as has been noted previously,' high manganese-content alloys containing nitrogen, when quenched from temperatures high in the ß field, contain a subgrain boundary phase which appears to be nitrogen-rich a. Marten-site is formed when alloys containing less than about

Jan 1, 1956

By R. E. Ogilvie, H. C. Gatos, R. E. Hanneman

The ejj-ect of high pressures on chemical inter-diffusion in the Fe-V system was determined by analyses of concentration vs distance profiles of atmospheric and high-pressure diffusion couples. Diffusion data were obtained as a function of tern -perature and composition. Activation energies, activation volumes, and frequency factors were determined at 1 atm, 20 kbars, and 40 kbars as a function concentration in the a and y phases. The A great deal of research has been carried out in the measurement and understanding of binary chemical inter diffusion in solids. Studies of the effects of high pressure on interdiffusion in binary systems, however, have been virtually nonexistent until the present work. This paper gives a detailed account of the effect of high pressure on interdiffusion and the Kirkendall effect in the Fe-V system. The present data are compared to existing theo- Kirkendall effects were measured at 1 atm and 40 kbars. At 1 atm Dy > DFe at the marker concentration; however, Dv approaches DFe under pressure, and at 40 kbars the values are approximately equal. The high-pressure and atmospheric diffusion data are evaluated on the basis of theoretical models. Chemical analyses of the diffusion -couple profiles were made using an electron microbeam probe. retical treatments of pressure dependence of diffusion which are based upon self-diffusion studies. THEORY The rates of atomic migration in metals and alloys are regulated by the repulsive forces exerted on an atom during its motion from one equilibrium lattice site to another and by the availability of a jump site. Application of high pressure is expected to decrease diffusion rates because it decreases interatomic distances as well as defect concentrations. A number of theoretical treatments have been focused on the problem of calculating self-diffusion coefficients in solids under atmospheric pressure. In general, the vacancy mechanism of diffusion appears to be dominant at high temperatures in most metallic systems. The migration of an atom by this

Jan 1, 1965

By C. G. Dunn, E. F. Koch, K. T. Aust

Strain-induced grain boundary migration was studied in a series of silicon-iron (3% pct Si) bicrystals of controlled orientations. Each bicrystal was given a 7 pct cold-rolling strain rind annealed at 1100°C. The direction of boundary migration was found to depend on orientation; results for several orientations related by a common [110] axis are given. Analysis of the micrographic and X-ray data is made in terms of the residual strain-energy densities within the crystals (energy per unit volurne) and a driving force on the boundary due to an energy density difference across the boundary. Relative strain energies were obtained for the various orientations investigated. A CHROME-acetic acid electroetching method for revealing dislocation sites in silicon iron was previously applied to clarify the structural features and the energetics involved in strain-induced grain boundary migration.',' The present paper is a continuation of this study, but is primarily concerned with the influence of crystal orientation. Sperry, as reported by Beck,3 attempted to determine the factors that influence the preferred growth of one grain over another in aluminum due to strain-induced boundary migration. He found that the particular grain of a pair which work hardened more was invaded, although exceptions to this correlation were noted. The index of work hardening was determined from microhardness measurements of each grain before and after cold-rolling. In the present study, orientation itself was taken as a useful variable for studying the behavior of individual grains in a bicrystal and the direction of boundary migration, since the extent of work hardening is orientation dePendent." The effect of strain on boundary migration is evident from a consideration of driving forces. Thus, in the absence of inclusions, the driving force (per unit area of boundary) for growth of grain A into grain B when a bicrystal is strained and annealed may be expressed as follows:2

Jan 1, 1960

By K. P. Gupta, P. A. Beck, N. S. Rajan

By determining the a phase boundaries in the following ternary systems: V-Fe-Si (at 1175oC), V-Co-Si (at 1175°C), V-Ni-Si (at 1175oC), Cr-Mn-Si (at 1000°C), Cr-Co-Si (at 1175°C), Cr-Ni-Si (at 1175°C), V-Fe-A1 (at 1175°C) and Cr-Co-A1 (at 1175°C), it was found that Si exerts a stabilizing effect on these a phases, while A1 tends to destabilize them. Si atoms in solid solution occupy sites D in the a structure, The co/ao ratio increases with increasing Si-, Mn- or Fe-content. The volume of the unit cell decreases with increasing Si-content. THE stabilization of certain metal silicides (the Nowotny phases) by the addition of relatively small

Jan 1, 1961

By J. A. Snyder, W. L. Finlay

G. Edmunds—Solid solubility is considered to be of either the interstitial or the substitutional type. Is it possible, in a binary alloy as the simplest case, that some of the solute atoms are present in the normal lattice sites (substitutionally or filling lattice vacancies) while simultaneously others are in interstitial positionss One might even ask whether a distribution of the two types may be the normal situation. H. M. Meyer—Metastable states of interstitial atoms occupying vacant lattice sites possibly occur as well as of substitutional atoms squeezed in between regular matrix positions. However (as we know since Hume-Rothery), the solute atoms choose between the two kinds of solutions; consequently, every solute will be unequivocally either substitutional or interstitial in the equilibrium state of the solid solution. M. Balicki—In view of the fact that the authors apparently correlate the analysis of the alloys at the ingot stage with the properties exhibited at the testing stage, I would like to ask whether this is a fully justifiable procedure. In other words, how good are their determinations of solute concentration for correlating them with the mechanical properties. The answer to this question may explain some of the divergencies. Assuming good enough homogenization of the samples and exact determination of mechanical properties the position of the plotted experimental points will depend solely upon the accuracy of composition determination. If this is not accurate, say due to loss or pickup of elements during processing from the ingot to the testing stage, or due to a systematic error in the method employed for obtaining solute concentration data, the points will deviate from their true position and may align themselves along a different curve than the one expected. H. V. Kinsey—We have been studying the creep-rupture properties of titanium-base alloys at 1000°F. In the course of this work, anomalies in behavior of the alloys that would suggest that the material under test was becoming stronger as the test progressed have been observed. If this was so, the most likely explanation that we could think of was that the test bars were absorbing oxygen and nitrogen from the air during the test and were thereby becoming strengthened. In an attempt to determine the strengthening effect of absorbed oxygen and nitrogen the following experiment was conducted. A length of cold-rolled titanium was supplied by the E. I. du Pont Co. Two test bars, having a 1/4 in. diam gauge length, were prepared from this material. One bar was tested in the as-received condition. The second bar was heated in air at 1550°F for 100 hr and subsequently air cooled prior to testing. A testing temperature of 1000°F was employed. The results of these tests are tabulated in table 11. In the author's opinion, is it reasonable to assume that the bar that was exposed to air at 1550°F for 100 hr was stronger because it absorbed oxygen and nitrogen from the air during this heat treatment? W. L. Finlay (authors' reply)—Direct experimental evidence for or against Mr. Edmunds' interesting suggestion will probably never be available. It seems possible, however, that mixed interstitial-substitutional solid solution might well occur with interstitial elements. The less likely possibility of interstitial solution of a normally substitutional element like copper in aluminum was recently discussed at length by the

Jan 1, 1951

By W. R. Hibbard

THE classical work on the electrical conductivity of alloys was carried out by Matthiessen and his coworkers1 in the early 1860's. He attempted to correlate the electrical conductivity of alloys with their constitution diagrams, but the information regarding the latter was too meager for success. Guertler2 reworked Matthiessen's and other conductivity data in 1906 on the basis of volume composition (an application of Le Chatelier's principle with implications as to temperature and pressure effects), and obtained the following relationships between specific conductivity and phase diagrams (plotted as volume compositions) : 1—For two-phase regions, electrical conductivity can be considered as a linear function of volume composition, following the law of mixtures. 2—For solid solutions, except intermetallic compounds, the electrical conductivity is lowered by solute additions first very extensively and later more gradually, such that a minimum occurs in systems with complete solid solubility. This minimum forms from a catenary type of curve. Intermetallic compound formation with variable compound composition results in a maximum conductivity at the stoi-chiometric composition. Landauer" has recently considered the resistivity of binary metallic two-phase mixtures on the basis of randomly distributed spherical-shaped regions of two phases having different conductivities. His derivation predicts deviations from the law of mixtures which fit measurements on alloys of 6 systems out of 13 considered. Volency (Ionic Charge) Perhaps the first comprehensive discussion of the electrical resistivity of dilute solid-solution alloys was presented by Norbury' in 1921. He collected sufficient data to show that the change in resistance caused by 1 atomic pct binary solute additions is periodic* in character. The difference between the period and/or the group of the solvent and solute elements could be correlated with the increase in resistance. Linde5-7 determined the electrical resistivity (p) of solid solutions containing up to about 4 atomic pct of various solutes in copper, silver, and gold at several temperatures. He reported that the extrapolated"" increase in resistance per atomic percent addition is a function of the square of the difference in group number of the solute and solvent as follows: ?p= a + K(N-Ng)2 where a and K are empirical constants and N and Ng are group numbers of the constituents. This empirical relation was subsequently rationalized theoretically by Mott,8 who showed that the scattering of conduction electrons is proportional to the square of the scattering charge at lattice sites. Thus, the change in resistance of dilute alloys is propor-t,ional to the square of the difference between the ionic charge (or valence) of the solvent and solute when other factors are neglected. Mott's difficulty in evaluating the volume of the lattice near each atom site where the valency electrons tend to segre-gate: limited his calculations to proportionality relations. Recently, Robinson and Dorn" reconfirmed this relationship for dilute aluminum solid-solution alloys at 20°C, using an effective charge of 2.5 for aluminum. In terms of valence, Linde's equation becomes ?P= {K2 + K1 (Z8 -Za)2} A where K1 and K2 are coefficients, A is atomic percent solute, Z, is valence of solvent, and Zß, is valence of solute. Plots of these data for copper, silver, gold, and aluminum alloys are shown in Fig. 1. The values of K1 and K2 are constant for a given chemical period (P), but vary from period to period. The value of K, increases irregularly with increasing difference between the period of the solvent and solute element (AP), being zero when AP is zero. The value of K, appears to have no obvious periodic relationship. All factors other than valence that affect resistivity are gathered in these coefficients. Because of the nature of the coefficients, Eq. 1 is of limited use in estimating the effects of solute additions on resistivity unless a large amount of experimental data are already available on the systems involved. It is the purpose of the first part of this report to investigate the factors that may be included in the coefficients of Linde's equation. On this basis, it is hoped that the relative effects of solute additions on resistivity can be better estimated from basic data, leading to a more convenient alloy design procedure. It is well 10,11 that phenomena that decrease the perfection of the periodic field in an atomic lattice, such as the introduction of a solute atom or strain due to deformation, will also increase the electrical resistivity. Thus, in an effort to relate changes in electrical resistivity to alloy composition, it appears appropriate to consider the atomic characteristics related to solution and strain hardening

Jan 1, 1955

By C. A. Bruch, W. E. McHugh, R. W. Hockenbury

Commercially pure molybdenum specimens were irradiated in the Materials Testing Reactor for an estimated exposure of 1.9 to 5.9x10 20 thermal nvt. Prior to irradiation, the material was ductile in the tension test; whereas after irradiation, it was brittle. The results of tension tests conducted at various temperatures revealed that the transition temperature for this material had been increased from —30' to +70°C as a result of the radiation exposure. From metallographic studies, it is concluded that the embrittlement is due to submicroscopic changes which raise the flow stress-temperature curve of the material. PRIOR to ten years ago, the bombardment of metals with high speed heavy particles such as protons, deuterons, a particles, and neutrons was primarily of academic interest. These particles existed in extremely small numbers in a few laboratories and only under very special conditions. With the introduction of the nuclear power reactors, these particles are now available in enormous quantities and it has become important from a practical standpoint to learn how well metals withstand severe reactor radiations. The principal radiations of concern in reactors are neutrons and y rays, since the heavier charged particles exist only in limited regions of reactors. Seitz,' in a theoretical approach, has shown that all of these high energy particles, except y rays, have enough energy to knock atoms from lattice sites and that these knocked-on atoms have enough energy to cause additional displacements of neighboring atoms. The result of this process would be a lattice containing many imperfections in the form of interstitial atoms and vacancies. Hence, it would be expected that the properties of metals can be changed by reactor radiations, and such has been found to be the case. Only a limited amount of data have been published in the open literature,2,3 and these data have been for relatively low integrated-neutron-flux exposures. In general, one effect of reactor radiations on the mechanical properties of metals has been to increase strength and decrease ductility. It is now possible to irradiate specimens in the Materials Testing reactor at much higher fluxes and to higher integrated exposures than previously possible.' The data which are being presented here describe the effects of a relatively high exposure on some mechanical properties of molybdenum. Experimental Procedures Material: The molybdenum used in this investigation was obtained from the Climax Molybdenum Co. The two heats from which the material originated were melted under a vacuum of 5 to 30 microns and cast in 7 in. diam water-cooled copper molds. One ingot contained 0.061 pct C and the other 0.066 pct. Both ingots were hot worked by extrusion and rolling into % in. diam rods, after which they were annealed and straightened. The rods were subsequently heated to 1100°C in a hydrogen atmosphere and swaged to ½ in. diam rods at the Research Laboratory of the General Electric Co. The resulting material had an average hardness of 264 VPN, or 99.2 Rb, and had an average of 5000 grains per sq ml in the transverse section, Test Specimens: Substandard-size tensile specimens were prepared according to the specifications shown in Fig. 1. These specimens were used also for hardness measurements. The metallographic specimens were small disks which were polished, etched, and photographed at X1000 prior to irradiation. The field studied was

Jan 1, 1956

By H. Warlimont

Precipitation of cementite plates from carbon-rich austenite gives rise to localized formation of martensite in the matrix next to the precipitate upon quenching. The growth of this martensite is urmsually restricted. A distinct lattice relationship is found between this martensite and the cementite phase. It is concluded that the martensite is nacleated in the region of lowest carbon concentration at the austenite-cementite integace, with low-energy matching to the cementite lattice. The restriction of the growth of the martensite phase to the vicinity of the cementite plates can be explained by misfit in the austenite -martensite glissile interface and the uphill carbon gradient in the austenite. The investigation was carried out by light- and electron-microscopy and by electron-diffraction of thin foils. THE precipitation of cementite from carbon-rich austenite gives rise to a localized formation of martensite in the matrix next to the precipitate upon quenching. This behavior has been described previously by A. B. Greninger and A. R. Troiano1 for a 1.78 pct C steel ("pseudomorphic martensite"), and by A. Hultgren2 for a Fe-0.99 pct C—5.20 pct Mn steel. By measuring the axial ratio of the martensite phase,' it was found that the carbon content of this martensite was lower than that of the martensite which formed without prior partial transformation to cementite. Therefore, it was concluded that lowering of the carbon concentration in the matrix next to the precipitate raised the M, temperature locally and thus led to nucleation of martensite at the ce-mentite-austenite interface. However, the restriction of the growth of the martensite phase to the vicinity of the cementite plates cannot be explained by localized carbon impoverishment alone. Under ordinary conditions a martensite plate which has been nucleated in a favorable site can continue to grow until it encounters a physical barrier, or until it encounters a compositional barrier in the matrix, where the total free-energy change for the reaction is not negative, since it has been shown by numerous experiments that the activation energy for growth of ordinary martensite is virtually zero.' An investigation was conducted by transmission electron microscopy and electron diffraction to study this extraordinary martensite. It was expected that crystallographic in addition to compo- sitional conditions caused this abnormal mode of martensite formation. MATERIAL AND PROCEDURE An Fe-C-Mn alloy containing 1.15 pct C and 5.1 pct Mn was used for most of the experiments. For metallographic work, specimens 15 by 15 by 3 mm were used. For preparation of thin films, the initial specimen size was 15 by 15 by 0.7 mm. The heat treatment of each specimen consisted of austenitizing for 1/2hr at 1100'~ in an argon atmosphere, subsequent isothermal holding in a lead bath at one of a series of different temperatures, and, finally, quenching into brine at room temperature. For metallographic examination, the specimens were mounted in bakelite (slight tempering effects resulted from the heat in the mounting press) ground, polished, and etched in nital. Thin films for transmission electron microscopy and electron diffraction were obtained by grinding the specimens to approximately 0.2 mm thickness and subsequent electrolytical thinning. The orientation relationships were evaluated from sets of electron micrographs and selected-area electron diffraction patterns of single units of the transformation products and the adjacent matrix. RESULTS In the alloy which was used for the experiments, proeutectoid carbide precipitates over a wide tem-

Jan 1, 1962

By John J. Gilman

F many years it has been suspected that a correlation existed between pits produced by etching and the density of dislocations in crystals. In 1953, the interest in this correlation was greatly stimulated when Vogel et al' demonstrated a 1:l correlation between etch pits and dislocations in low angle grain boundaries of germanium. About two years ago, the author began attempts to produce etch pits at dislocation sites in zinc mono-crystals. These attempts met with success a year or so ago,' and since that time a survey has been made of the etch pit patterns that are associated with various modes of deformation in zinc monocrystals. Unfortunately, the etching technique that will be described is too delicate for use as an accurate quantitative tool. Nevertheless, it has been of considerable assistance in clarifying the structure of plastically deformed crystals. Technique Many attempts were made to produce etch pits in high purity zinc crystals. It was found that several techniques would produce surface grooves at grain boundaries that had misorientation angles greater than about l°, but no technique was successful for boundaries with smaller angles. Among the things that were tried were: electrolytic CrO, (both etching and polishing concentrations), HNO, in various water and alcohol solutions, dilute HC1, many 0-0,-Na,SO, solutions, Cr0,-HC1 solutions, picral, electrolytic Na,S,O,, and electrolytic NaOH and KOH. A few attempts to use cathodic sputtering and thermal etching were also made.

Jan 1, 1957

By R. M. Rose, D. P. Ferriss, J. Wulff

Single crystals of tantalum, tungsten, and the binary alloys thereof were grown by electron-beam zone melting and tested in tension between 77° and 373°K. The ductile-to-brittle transition temperature increased sharply with solute concentration, for both tungsten-rich and tantalum-rich alloys; apparently, the maximum transition temperature exists near the 50 pet concentration. Twinning was observed to be a consequence of cleavage-crack propagation. Cleavage occurred on(100)planes, and extensive tearing and "river markings" were present. The onset of brittleness could not be associated with any change in deformation mode, the yield point phenomenon, or the large rise in yield stress with decreasing temperature. Cleavage was observed to initiate at either the specimen surface, or subgrain boundaries. The observation was made that the grain boundaries of Polycrystalline materials are probably even better as nucleation sites for fracture, and are responsible for brittleness at high temperatures and lower solute concentrations than those of the corresponding single crystals. TUNGSTEN and tantalum, the two high-melting neighbors in the third transition period of the periodic table, present striking contrasts. Although both are bee, tungsten has far higher elastic moduli, and the highest ductile-to-brittle transition (DBT) of all the pure metals.' Tantalum, however, is ductile at liquid helium temperatures. Large strain aging and yield point phenomena are observed in tantalum,2,3 but only to a lesser extent in tungsten.4 Tungsten work-hardens at a high rate,5 whereas this effect is negligible in tantalum.' Since the mutual solid solubility of these two metals is complete,7 and no ordering has yet been reported in the binary system, the possibility of depressing tungsten's DBT by tantalum additions was considered. Also, tungsten additions to tantalum could produce hard, high-melting alloys which might be ductile at room temperature. Such alloys offered excellent bases for complex alloy development, particularly with regard to the effect of rhenium on Group VI metals.8"10 In addition, there was the opportunity to examine flow and fracture modes in the vicinity of the DBT, with particular emphasis on the correlation between brittleness and fundamental deformation mechanisms. Myers11 has reported that recrystallized alloys with up to 10 pet W in tantalum are ductile at room temperature, but alloys with 20 pct W could not be swaged at temperatures as high as 500°C. The whole spectrum of Ta-W alloys has been surveyed by Braun, Sedlatschek, and Kiefferl2 using sintered powder compacts. In addition to some physical properties they reported a maximum hardness at about 50 at. pet W, dropping to much lower hardness levels for the pure components. They were able to cold work tantalum-base alloys with as much as 30 pet W and to warm work tungsten-base alloys with up to 20 pet Ta by procedures similar to those used for pure tungsten. EXPERIMENTAL In order to study deformation modes and to keep the impurity concentrations at a minimum, electron-beam zone melting was used to prepare single crystals of high purity. The electron-beam zone melting apparatus is similar to that described by Calverley, Davis, and ever" and incorporates a grid control rectifier to maintain control of emission current. Pure metals were refined by making three zone passes at 4 mm per min up the rod. Alloys were prepared by melting together wire of one constituent on a previously melted rod of the major constituent. Subsequently, two zone passes were made in opposite directions to level the composition after the manner suggested by pfann.14 Purification of the starting materials was accomplished by evaporation of the several impurities, and the degree to which this was accomplished is indicated in the chemical analyses of Table I. The uniformity of composition along a zone levelled rod was within the i 1 pet accuracy of the fluorescent X-ray technique used to determine composition. Crystallographic orientation of the

Jan 1, 1962

By R. W. Hertzberg, R. W. Kraft

A study of the fracture behavior of unidirectwn-ally solidified Cu-Cr eutectic alloy was performed. Fractured whiskers, grain boundaries, and the interface between proeutectic Cr dendrites and the Cu matrix were the predominant failure initiation sites where grain size was larger. Strain induced void formation was restricted at lower solidification rates. This was attributed to a lack of adequate plastic constraint and a probable preferred orientation. A modification of the Crussard et al. model is presented to explain the appearance of "elongated dimples" on the shear fracture surface. A Cu-Cr alloy containing about 1.8 at. pct Cr solidifies by a eutectic reaction forming filamentary crystals of chromium within a continuous copper solid solution matrix.' Webb and Forgeng2 have shown by bend tests that the extracted chromium filaments, which are ordinarily curved and branched (due to random solidification), have the high strengths associated with whiskers. If an ingot of the eutectic alloy is unidirectionally solidified and appropriate control exercised over the thermal gradient, growth rate, and impurity level, the chromium fibers can be forced to solidify as fibers which are substantially parallel to the growth direction, Fig. 1. Uniaxial tensile tests on these straight chromium fibers extracted from controlled ingots3 have confirmed the earlier bend test results on curved fibers. Combining the facts that the strength and modulus of the chromium filaments are higher than the more ductile copper matrix and assuming that a "good bond" exists between the two phases, the Cu-Cr controlled eutectic system fulfills the requirements for effective fiber reinforcement of ductile matrices as established by studies on fiber glass reinforced plastics and other two-phase systems.4 Therefore, it was decided to study the fracture characteristics of morphologically simple specimens of chromium fiber reinforced copper (i.e., specimens of the controlled eutectic with substantially parallel reinforcing fibers) with the objective of establishing the dominant aspects of fracture. PREVIOUS WORK Comparatively little work has been done to understand the manner in which ductile alloys fail be- cause of the limited demand for this kind of information. Ordinarily ductility is specified for safety or similar reasons and when a part deforms plastically its useful life is terminated. In recent years, however, a number of investigators have begun to

Jan 1, 1963