By Johan Sundström

Anhydrous DyC13 was prepared by dehydration of DyCl3?6H20 in a fluidized bed using both batch- wise and continuous feeding. A gas mixture with varied composition of argon and HCl was used. The productivity was high, reaching values of 0.25 mol H20/m2-st during the reaction step 6- 1 and 0.062 mol H2O/m2.s during the reaction step 1-0. The product was free from hydrolytic compounds, such as DyOCI, if control of inlet gas composition versus temperature was achieved. From the results of various experiments, some relations between HCI-concentration and temperature in order to avoid hydrolysis have been deduced. The fluidization process efficiency decreases drastically after the dehydration has proceeded down to about 10 mol% of remaining water. Therefore, in a final treatment the last traces of water were removed by slowly purging gas through a packed bed. The water content could thereby be reduced to less than 1 mol%.

Jan 1, 1997

By S. F. Cheng

Among the many extraordinary features of the rare earths are their magnetic and magnetoelastic properties. The rare earths, e.g. Tb, Dy, Nd, Sm, are known worldwide for their large magnetocrystalline anisotropy and magnetization, which has led to the importance of magnetic rare earths as vital ingredients of modem permanent magnets. In this paper, we focus on the strain dependence of these giant effects which gives rise to huge magnetostrictions, magnetomechanical couplings, and ?E effects. Magnetostrictions greater than 10-3 have been measured at temperatures as high as 500 K. At low temperatures magnetostrictions reaches -1%. ?E effects - 10. No other solid state material has matched these values. A proper balance of magnetic anisotropy and magnetostriction, plus a proper choice of crystal axes lead to alloys which can switch large quantities of energy between the internal (magnetic) and external (mechanical) states with the application of small triggering magnetic fields. In addition to the traditional use of these materials in transduction, they are particularly valuable for smart systems where reliability and robustness are needed such as active structure stiffening and active vibration control.

Jan 1, 1997

By Donald O. Voit

A BASIC language program has been written that simulates the performance of an integrated solvent extraction circuit consisting of an extractor, a reflux fed scrubber, and a stripper. The program is designed to simulate the performance of a circuit having an aqueous feed containing each of the lanthanides as well as yttrium. The Kremser equation is used to determine the separation occuring in each section of the circuit. The required input variables are the feed composition, the separation factors, the light key extraction factors and extractor feed zone distribution coefficient, the number of stages, and the reflux ratios. The program calculates the composition of the streams at each node in the circuit, the total loading, and the remaining distribution coefficients. User interaction with the program is essential. The program has no capability to determine if the calculated values are consistent with various real restraints. Knowledge of the physical, chemical, and equilibrium behavior is essential to successfully utilize the program. The number of iterations required to achieve steady-state provides insight to the circuit response times. With suitable supervision the program can be used as a simulator for operator training.

Jan 1, 1989

By Steven Wright

The extent and the rate of reduction of slags produced from the smelting of recycled lead batteries were investigated under laboratory conditions using graphite as reductant. Simultaneous reduction of PbO, Fe2O3, Sb2O3 and As2O3 occurred at temperatures of 1180 and 1200°C, with Sb and As reporting to the metal phase while the PbO content of the slag was above 2 wt%. Fuming of As from the metal occurred at lower concentrations of lead in the slag. Discard slags with low levels of As, Pb and Sb were produced. Arsenic levels were reduced to less than accurately measurable by ICP analysis, and Sb levels in the final slags were in the range of 0.1 to 0.2 wt%. The kinetic data obtained were analysed and compared with other measurements on lead oxide containing slags. The results showing a dependence of the reduction rate on the oxidation state and the basicity are consistent with other studies on well characterised industrial and. synthetic lead slags. These results indicate that when carbonaceous reductants are used, the rate of interfacial reactions play an important role in enabling the production of environmentally acceptable discard slags.

Jan 1, 1994

By Carlos A. Nogueira

Spent Ni-Cd batteries contain in the electrode materials heavy metals like Ni, Cd and Co, which must be recycled due to environmental problems. Pyrometallurgy is normally used for recycling these end-of-life products, but alternative processes by hydrometallurgy, integrating also physical operations, can be used. Hydrometallurgy seems to be useful, because metals can be efficiently recuperated in chemical forms with commercial value. The economical viability of this recycling process can be improved increasing the treatment capacity, through the application to different types of residues with similar characteristics like Ni-MH and domestic batteries, or other residues containing Ni/Co, like sludges, dusts or spent catalysts. Spent Ni-Cd batteries were first physically processed using shredding and wet sieving operations. Best results were achieved using an output of 6 mm in the shredder and 1.4-2 mm in the physical separation by wet sieving, resulting a fine fraction containing 70% of the initial electrode material and only 6% of the initial scrap. The acid leaching of the obtained material in the previous operation was studied, being the parameters like: temperature, H2SO4 concentration and the liquid/solid ratio (L/S) optimized. The values attributed to the factors which concerned the best results obtained on the leaching process were mainly influenced by Ni recovery. In opposition, Co and Cd were easily leached in a wide range of conditions. To attain an overall recovery, with minimum costs, of the three metals, the values of T~100ºC, [H2SO4]=2.3-2.7 M and L/S=8-10 L/kg were considered the most appropriate.

Jan 1, 2006

By K. Kashiwaya, N. Hiroyoshi, H. Furuya, N. Sumiya, M. Tsunekawa, M. Ito

"The number of hybrid vehicles is increasing and this is causeing an increase in waste nickelmetal hydride batteries. The cathode activating agent of batteries is made of nickel hydroxide and the anode activating agent is an alloy of nickel and rare earth elements. Conventional rotary kiln methods cannot recover the rare earth elements, and hydrometallurgical treatment of crushed product consumes large volumes of agent. The physical separation of the anode alloy from the cathode hydroxide would make it possible to reuse the alloy. The authors have reported separation of anode and cathode components in the large size fractions using a newly developed dry magnetic separation method. Wet magnetic separation has been applied to the powder fraction and about 90% anode purity was achieved. This paper reviews experimental results from previous publications and proposes an integrated treatment process for crushed nickel-metal hydride batteries.IntroductionEnvironmentally-conscious clean energy vehicles have attracted much attention in developed countries and particularly hybrid vehicles are increasingly mass-produced as low emission vehicles. Hybrid vehicles have both a gasoline engine and an electric motor to save on gasoline usage and a nickel-metal hydride battery is used to store electric energy. The battery contains Nihydroxide and Co as the cathode activating agent and an alloy of Ni and mischmetal (mM), a rare-earth element mixture consisting of La, Ce, and Nd, as the anode hydrogen adsorption component. In conventional recycling, the Ni and Fe are recovered with a rotary kiln-electric melting process and the Co and mM go to the slag component [1] and hydrometallurgical treatment of crushed product consumes large volumes of agent. Japan Oil, Gas and Metals National Corporation have proposed a low energy and low cost recycling treatment process combining the physical and chemical treatments and the authors are investigating the physical treatment process."

Jan 1, 2008

By M. Kane, O&apos

Operators and designers require a comprehensive model to predict performance of heap leach piles and provide input of reliable and defensible data for economic modelling. A conceptual, theoretical, or numerical predictive model addressing the required metallurgical, geological, biological, and operational considerations should be developed within the framework of the hydraulic performance of the heap leach pile. It is generally agreed that segregation, compaction, and consolidation are physical aspects which significantly affect recovery and in general hydraulic performance. Hydraulic performance of heap leach piles can be described through the application of unsaturated zone hydrology. Unsaturated zone hydrology describes the flow and storage of moisture and oxygen in a porous medium under conditions where the pore water pressure is less than atmospheric. The porous material is "unsaturated" if an air phase, in addition to the water phase and solid material phase, is present. These conditions describe the operation of a copper heap leach pile. This paper will focus on developing an understanding of hydraulic performance in segregated heap leach material and demonstrating that unsaturated zone hydrology can be used as the framework to improve understanding and prediction of heap leach performance.

Jan 1, 1999

"Silver is traditionally recovered in base metal smelters (lead and copper), or as a by-product of other precious metals (gold and/or PGM's). This paper presents the results of non-conventional techniques to recover silver from complex materials. The PLATSOL® process has been developed to recover, in one step and without the use of cyanide, base metals (copper, cobalt, nickel) and precious metals (gold, PGM's) from sulphide concentrates too low in grade to enter the mainstream extraction processes. Silver is only partially recovered in solution with gold and the PGM's during the PLATSOL® process. However, the silver minerals are transformed into silver chloride, which can then be recovered from the PLATSOL® residue using conventional techniques. Some South American silver concentrates contain levels of impurity (mostly arsenic) so elevated that the penalties incurred significantly affect the process economics. The present results have shown that a low temperature calcination process transforms the concentrate into a product well suited for traditional recovery treatments. Metallurgical details will be provided, as well as the results of mineralogical studies that helped clarify the process mechanisms.IntroductionSilver occurrences in nature are very diversified, and, therefore, primary silver is produced as a by-product of many base metal and precious metal operations [1], as well as a co-product of most gold ores. However, difficulties can arise when high temperature processes are used for refractory gold ores or copper concentrates, or when the silver concentrate contains impurity elements such as arsenic that trigger high penalties."

Jan 1, 2012

By Roger Wilmoth

Exposed, open pit mine highwalls contribute significantly to the production of acid mine drainage (AMD) thus causing environmental concerns upon closure of an operating mine. Four innovative technologies were evaluated under the U.S. Environmental Protection Agency?s, Mine Waste Technology (MWTP), Prevention of AMD Generation from Open-Pit Highwalls Demonstration Project. This project is funded by the U.S. Environmental Protection Agency (EPA) and jointly administered by the EPA and the U.S. Department of Energy (DOE) through an Interagency Agreement. The objective of the field demonstration was to evaluate the technologies ability to decrease or eliminate acid generation from treated areas of the highwall in comparison an untreated highwall area. The field demonstration was performed at the Golden Sunlight Mine (GSM) a subsidiary of Placer Dome U.S., located near Whitehall, Montana. GSM is an operating gold mine. The highwall at GSM was divided into five plots measuring 15.24 by 15.24 metres (m) and each technology was assigned a plot with the fifth plot being used for comparison as a background control plot. The four technologies were spray-applied. The applied insitu treatment technologies included: 1) A modified, furfuryl alcohol resin sealant, utilizing wood and agricultural by-products to coat the rock surface. 2) EcobondTMARD, a phosphate based process that forms a stable, insoluble compound, coating the rock surface. 3) Two ARD passivation technologies, magnesium oxide and the Dupont technology developed to create an inert layer/coating on the pyrite, preventing oxidation. The technologies were evaluated using the following methods: 1) ASTM D 5744-96, Accelerated Weathering of Solid Materials using a Modified Humidity Cells, 2) mine wall residual wall rinse sampling, 3) microscopy, and 4) core drilling followed by water injection testing.

Jan 1, 2003

By Douglas Robinson

This paper describes technical work done to develop a Spouted Bed Electrode Cell into a commercially viable Electrowinning Cell; (a previous paper has been presented at the ECS meeting in Paris in May of this year, with a more general overview of the cell, [1]). The studies have included hydrodynamic tests to understand the criteria for the circulating flow of metallic beads in the cell, particularly in the region at the entrance to the draft tube, and electrochemical tests to find a suitable diaphragm for extended time electrolysis. Various patent pending features were developed including a double nozzle to allow for automatic stopping and restarting of the bed, an arrowhead shaped draft tube to control the flow of beads into the entrance to the draft tube, a roof-top shaped device to control the flow of beads out of the top of the draft tube, an overflow weir to allow the continuous recovery of beads from the cell, and a family of diaphragm fabrics for extended operation. Prior to the identification of the diaphragm material, short circuits would develop within a few hours. A pilot scale cell was operated for three days, with continuous operator attention, and then for ten days with operator attention only on day shift. The cell is currently advancing to the next stage of development which will involve continuous testing in a commercial copper electrowinning facility.

Jan 1, 2003

By David Dreisinger

The pressure oxidation of pyrite is an important hydrometallurgical technology, especially in the total oxidation of refractory gold ores and concentrates (gold is locked in the pyrite structure preventing direct cyanide recovery). It has been noticed in some commercial applications and benchscale studies that the leaching of pyrite may be slow and apparently can be inhibited by the presence of molten elemental sulfur in the leach pulp. The purpose of this study was to determine whether Ortho-Phenylene-Diamine (OPD) could be used as a surfactant or dispersant for sulfur in the pressure oxidation of pyrite. OPD has previously been shown to be useful for pressure leaching of zinc and copper sulfides at 150 C.In this work, the interfacial chemistry of sulfur was studied at temperatures of up to 190 C in the presence and absence of OPD and other surfactants. The contact angle between molten sulfur and pyrite was also measured. Finally, the impact of OPD on the kinetics of pyrite oxidation was measured in bench-scale pressure oxidation experiments. The essential finding of this study was that OPD lowers the interfacial tension between molten sulfur and acid solutions and increases the contact angle (reduces wetting) between molten sulfur and pyrite. The work of adhesion between sulfur and pyrite was reduced by more than an order of magnitude in the presence of OPD. In bench scale tests, addition of OPD was found to significantly accelerate the rate of oxidation of pyrite. Conveniently, it was found that OPD was also fully degraded during high temperature oxidation processes. No residual OPD was detected in solution or solid samples from the leach testing. OPD is recommended as a sulfur dispersant in the pressure oxidation of pyrite and/or elemental sulfur containing feeds.

Jan 1, 2003

By P. Chris Pistorius

Calcium treatment of alumina inclusions, to convert the alumina to molten or partially molten calcium aluminates, is a well-established treatment for steel, to improve the castability of aluminium-killed steel. However, the role of magnesium in calcium-treated steel is not fully clear, nor is the origin of the several percent of magnesium oxide that is often present in calcium-treated inclusions. To study this, steel was sampled after calcium treatment at an industrial steel plant, and the inclusions identified by energy-dispersive X-ray microanalysis (EDX) on polished sections of the samples (analysing the samples in a scanning electron microscope). The predicted fraction liquid in the inclusion was estimated from the ternary alumina-magnesia-lime phase diagram. Inclusions with higher CaO contents generally had lower MgO contents, indicating that the calcium wire is not the origin of the magnesium in the inclusions; this was also confirmed by wet chemical analysis of the calcium wire. Instead, it appears that magnesium-alumina spinel inclusions form during extended ladle contact after aluminium killing and before calcium treatment. While such spinels have been stated to cause poor castability (clogging the submerged-entry nozzle), it is clear that calcium treatment successfully modifies the spinel inclusions to mixed alumina-lime-magnesia inclusions, where the magnesia content contributes substantially to liquefaction of the inclusions: for typical MgO contents of around 10%, the range of Ca:O ratios which yield liquid (or partially liquid) inclusions is extended substantially to lower Ca:O ratios.

Jan 1, 2006

By Bruno Lebon, Koulis Pericleous, Georgi Djambazov, Mayur Patel

"High speed compressible jets are used in a number of steel-making applications. In the case of the BOF, a compressible oxygen jet reacts with a carbon-rich iron bath to reduce carbon levels and produce steel. The intensity of the process is governed by the speed of the jet and by the size and shape of the depression created in the metal and slag by the force of the jet, i.e. by the corresponding free surface. This is a difficult CFD problem, since there are compressible and incompressible regions in the flow domain, which need to be handled differently in a finite-volume (FV) pressure-correction scheme. Also, standard turbulence models do not account for compressibility, or the large difference in density between the cold oxygen jet and the hot reacting surroundings. Corrections are introduced to the k-E model to remedy this deficiency and the results are validated against experimental data. The compressible/incompressible boundary is handled through a transition region, based on Mach number.IntroductionThe deformation of a free surface by a compressible high speed jet is of paramount engineering interest, particularly for understanding the physical processes within a Basic Oxygen Furnace (BOF). In a BOF, a supersonic oxygen jet impinges on a molten iron surface, thereby creating a cavity. Oxygen penetrates the bath and removes carbon, resulting in low carbon steel [1].The challenges in modelling such a process lie in coupling a solution domain with distinct compressible and incompressible regions and in dealing with large density differences between the modelled gas and liquid. The modelling of compressibility within the jet is crucial, since the correct velocity profile in the jet is required to determine the cavity depth with accuracy."

Jan 1, 2012

By Bo Yan, Jiaquan Zhang, Haibo Sun

"Based on the validation of steady-state isothermal mathematical model by a 0.4-scale water model for the single-strand slab casting tundish, the effect of varying pouring temperature on the flow, temperature field, and residence time distribution(RTD) of the liquid steel was studied by a transient hydrodynamic model. Due to the decreasing temperature of ladle stream over a casting period of 50 min, the direction of vortex flow at the downstream side of dam changes to clockwise from the anticlockwise at 4 min after the new teeming, and reverts to anticlockwise direction again at 43 min. Meanwhile, the melt flow state in the dam hole is also varying with time. For conventional isothermal water modeling, the RTD parameters obtained are much different as compared with the non-isothermal ones. For the flow control devices(FCD) design, however, the identical optimal scheme can be concluded from the point of view of isothermal modeling.IntroductionOriginally, tundish was adopted as a buffer and distributor to hold and allocate molten steel for sequence casting upon ladle exchange and to provide a desired steel flow rate to the mould below. With the increasing demand to strand quality, the tundish has become a critical metallurgical reactor to enhance inclusions removal, avoid reoxidation of molten steel, and prevent slag entrapment. The general trends to obtain these metallurgical effects are to optimize steel flow pattern and to extend the residence time of molten steel in the tundish through increasing the volume of tundish and/or using FCDs in the interior of the tundish."

Jan 1, 2012

By Tiruttani Munikamal, Suresh Sundarraj

"A numerical model of the induction hardening process of steel cranks has been developed and the predicted results of temperature and phase distribution during this solid state phase transformation process are verified with experimental data from the literature. This heat treatment process involves heating the crank to the austenitic temperature range followed by rapid quenching in water to harden the surface of the crank. The model has been developed using ABAQUS, commercial FEA software. The formation of martensite, pearlite, and retained austenite phases are modeled and implemented through a user defined function in ABAQUS. A sensitivity study on the various process parameters affecting the amount of phase distribution has been carried out.IntroductionThe type of surface and sub-surface microstructure as well as the residual stresses that are present in a component after manufacturing, significantly affects it fatigue performance. The wear resistance of the automotive components such as crankshaft, gears, camshaft and bearings depends on the surface hardness. In order to achieve the surface hardness, these steel components are subjected to a type of quench hardening heat treatment process. There are several heat treatment processes available for the industrial application to improve the mechanical properties of the final part. Case hardening using induction heating is one of the widely used industrial techniques for improving the surface microstructure of a steel component. It consists of two stages i.e. induction heating cycle, followed by quenching in a fluid medium (usually water or oil)"

Jan 1, 2012

By Alex Moyano

Due to very demanding environmental rules, and to the incrementing impurities contents in the processed concentrates, Codelco Norte smelter permanently faces new demands for planning the production program with the present fulfillment of the environmental regulation. Accordingly, the CN smelter along with IM2, developed an impurity distribution simulation model, M-DICE, which predicts the impurities behavior for each of the process units of the smelter under different process configurations and concentrates quality. The development of the M-DICE included the gathering of operational data for the process units of the CN smelter, including temperature, oxygen enriched air, matte grade, etc. Then based on a mass balance for each of the process units involved in the smelter a thermodynamic evaluation was done to derive the arsenic fractional distribution among the condensed (matte/white metal/copper/slag) and gas phases. Then, the validated M-DICE was able to predict the arsenic behavior in the Teniente converter processing complex concentrates with high arsenic content, among others. At present, M-DICE is in its last stage of development, and is expected to be a suitable environmental and process management?s tool for the Codelco-Chile?s smelters.

Jan 1, 2006

By Cam T. Nhan

The potential use of coal fly ash as a construction material has been recognized for many years,. In this work, an admixture of the ash residue is investigated for use as a landfill liner. In particular, its performance as a chemical barrier to the leachate from the municipal solid waste (MSW,) is determined. The test specimens are a water compacted admixture of class F fly ash, low in calcium content, which is blended with lime dust and calcium bentonite. MSW is passed through the compacted fly ash specimens under a gravitational head. The. diffusion of elements in the leachate through this material is monitored as a function of time. The distribution profiles of the retained elements in the compacted admixture provide prediction of the long term performance of the compacted admixture directly affect the leachate diffusion rate, hence, the mobilities of the retained elements.

Jan 1, 1992

By Laurentiu Nastac

"This paper describes the development and validation of a comprehensive multiscale modeling approach capable of predicting at the mesoscopic scale level the ingot solidification structure and solidification-related defects commonly occurring during the vacuum arc remelting (VAR) process. The approach consists of a coupling between a fully transient macroscopic code and a mesoscopic solidification structure code. The predictions from the multiscale model, including grain morphology and size, primary and secondary dendrite arm spacings, Laves and NbC phases, tendency for freckling and columnar-to-equiaxed transition, were validated against experimental measurements for a 20-inch diameter VAR alloy 718 ingots. The validated model was then used to investigate the effects of melting rate and ingot diameter on the solidification structure of VAR processed 718 ingots.IntroductionThe objective of this work was to develop a fully transient multiscale modeling approach to get an insight into the effect of processing parameters on the cast micro- and macro-structure during VAR processing. The developed model assists in achieving better control of the ingot solidification structure and to determine trends in the macrosegregation in these ingots. Another objective of this work was to analyze the transient effects of production rate and ingot size on the resultant ingot microstructures. This objective was met by first understanding the effects of the full range of processing parameters typically used in the VAR process. Processing parameters such as power input and heat extraction rate significantly influence the ingot liquid pool size and shape as well as the ingot structure, which in turn will greatly impacts the final ingot quality."

Jan 1, 2012

By Carlos Schvezov, Eliana Agaliotis, Alicia E. Ares, Mario Rosenberger

"The interaction between a solidification front and a spherical particle was modeled and simulated in order to study the phenomenon of ""pushing"". Finite element methods were employed in axisymetric domains. The drag force is calculated from the calculated fluid flow field and the repulsion force is the Lifshitz-Van der Waal force. The thermal field is decoupled from the force field. The model is applied to a metallic matrix containing particles with similar, lower or higher thermal conductivities than the matrix, resulting in planar, convex and concave interface shapes, respectively.The results show that the critical velocities for pushing for concave and convex interfaces are about one order of magnitude larger and one order of magnitude lower than the critical velocity for flat interfaces, respectively. The simulated results were in very good agreement with reported experimental results.IntroductionThe solidification interface of materials containing spherical particles in some cases can push the particle ahead the interface. This phenomenon generally occurs during the solidification of different materials such as, metallic alloys containing native particles, metal matrix composites containing particles or fibers as reinforcements and crystallization of semiconductor, optical, optoelectronic or biological materials. In all cases the interaction strongly determines the distribution of particles and the resulting physical and physic-chemical properties of the resulting material. The phenomenon has been investigated for many years both experimentally and by mathematical modeling [1-21]. The process is complex due to the variety of phenomena involved during pushing. In all cases, the physical problem depends on the properties, nature, and morphology of the interacting media; the particle, melt and solid; and external fields such as gravity, thermal and electromagnetic fields."

Jan 1, 2012

By Mari Naess, Jan Erik Olsen, Gabriella Tranell

"Fume, also known as dust, is produced during metal refining. Exposure to fume is damaging to the health of plant operators. A mathematical model has been developed to study the different factors governing the fuming mechanism. It is shown that natural convection is the main driving force of the phenomenon, and that the fuming rate is highly sensitive to the area of the exposed metal surface. A new feature introduced in the modeling concept is the ability to include a gas flux of unconsumed process gas flowing up through the metal surface. This reduces the fuming rate, and should normally not be neglected.IntroductionFormation of fume from the ladle in which metal is refined into its final specifications is an environmental issue of importance for the working environment in the production plant. In layman-term fume is often known as dust. It is formed when metal reacts with oxygen. As an example of a fuming process, we will focus on ladle refining of silicon. Note that many of the principles and conclusions will apply to other metal refining processes. For silicon production, silica fume (S1O2) is produced when silicon metal (Si) reacts with oxygen (O2).Silicon is produced in a submerged arc furnace. The metal is tapped from the furnace into a ladle for refining. The refining is conducted by injecting a mixture of air and pure oxygen at the bottom of the ladle. The oxygen reacts with the metal and the impurities, and the amount of impurities is reduced according to product specification. At the ladle surface, metal also reacts with oxygen present in the air surrounding the ladle. This reaction produces silica fume as illustrated in Figure 1."

Jan 1, 2012