Search Documents

By N. A. Gokcen, J. Chipman

A revised treatment of the authors' published data eliminates the complex relation previously proposed between concentration of silicon and activity coefficient of oxygen in liquid iron. Revised values of the thermodynamic properties of the liquid solution are presented. IN a recent experimental study of the reaction SiO2 (s) = Si+ 2O; Kf, = [% Si] [% O]² [1] the authors' found a substantially constant equilibrium product in liquid iron at 1600°C of 2.8x10-5 They also reported extensive data on the reactions: SiO2 (s) + 2H2 (8) = Si- + 2H2O (g); K'2= [% Si] (H2O/H2 [2] and H, (g) + 0 = H2O (g); K'3 =( H2 O [31 (H2) [%O] From the results on reaction 3 and earlier data of Dastur² on this same reaction in the absence of silicon, they determined the activity coefficient of oxygen, f0, on the basis of the definition K3 = (H2O)/ (H2)f0 [% 0] where K, is the equilibrium constant and f0, is taken as unity in the pure Fe-0 system. Similarly values of fsi were deduced from results on reaction 2. In a more recent study" of analogous reactions in the system Fe-A1-0, it was found impossible to reconcile the results on reaction 3 with Dastur's data; accordingly the latter were ignored and the equilibrium results were extrapolated to find a value of K, at zero concentration of aluminum. This procedure failed to locate the cause of the discrepancy but it did yield reasonable values of activity coefficients. It also avoided introduction of the complex empirical relation between the oxygen activity coefficient and the concentration of the added element. The same type of discrepancy exists for system Fe-Si-0.' In the earlier paper an attempt was made to fit both sets of data by a single curved line (Fig. 6 of ref. l), the form of which is contrary to the theoretical requirement of a finite slope at infinite dilution. In the light of experience on the Fe-A1-0 system the discrepancy must be recognized as one which can be resolved only by more refined measurements. Accordingly Figs. 6 and 10 are retracted. It is pointed out also that until the discrepancy is resolved Figs. 7, 8, and 11 are subject to some uncertainty. Qualitatively the following conclusions still appear valid: 1—The activity coefficient of oxygen is reduced by addition of silicon. 2—In dilute solutions the activity coefficient of silicon increases with its concentration. 3—With respect to equilibrium in reaction 1, the above effects are approximately compensating. The discussion of K'1 in the previous paper requires no revision. It was pointed out that the constancy of the product [% Si] [% 0]² ndicated a compensating effect of the activity coefficients of silicon and oxygen. Therefore, as a very good approximation, K1 = K'1 and the following average values are suggested both for K, and K', at the temperatures 1550°, 1600°, and 1650", respectively, 1.0x10-", 2.8~10-" and 5.5 ~lo-'. Revision of the thermodynamic treatment is necessitated by the recent appearance of new data, based on a combination of combustion and solution calorimetry,' which yields for the heat of formation of low-cristobalite from the elements, the value —209,330 ±250 cal per mol at 25°C. This is about 4000 cal larger than the value previously accepted. The new value for cristobalite is used, together with Kelley's tables of high-temperature heat contents" and entropies and with Korber and Oelsen's' heat of fusion of silicon to obtain the following equation for the standard free energy of cristobalite in the temperature range 1700" to 2000°K: Si (1) + 02 (g) = Si02 (crist.); ?F° = -217,700 + 47.OT [4] The free energy of solution of 0, in liquid iron is:8 O2 (g) = 20 (in Fe); AF° = -55,860 - 1.14T [5] and these two equations are combined to give: Si (1) + 20 = SiO, (crist.); AF° = -161,840 + 48.14T [6] ?F°1873 = -71,700 cal. From the experimental value of K, = 2.8x10-5, Si + 20 = SiO2 (crist.); ?F°1873 = -39,000 cal. [7] The combination of Eqs. 6 and 7 yields the free energy change when liquid silicon dissolves in iron to form the dilute solution of unit activity (1 pct). Si (1) = Si; ?F°1873 = -32,700 cal. [8] The heat effect in this process according to Korber and Oelsen' is an evolution of 28,500 cal per gram

Jan 1, 1954

By Takashi Katsura, Avnulf Muan

Equilibrium relations in the system FeO-Fe2O3 Cr2O3 have been determined at 1300°C at oxygen pressures ranging from that of air (0.21 atm) to 1.5 x 10-11 atm. The following oxide phases have stable equilibrium existence under these conditions : a sesquioxide solid solution with corundum-type structure (approximate composition Fe2O3-Cr2O3); a ternary solid solution with spinel-type structure (approximate composition FeO Fe2O3-FeO Cr2O3) and a ternary wüstite solid solution with periclase-type structure and compositions approaching FeO. The metal phase occurring in equilibrium with oxide phase(s) at the lowest oxygen pressures used in the present investigation is almost pure iron. The extent of solid-solution areas and the location of oxygen isobars have been determined. ThE system Fe-Cr-O has attracted a great deal of interest among metallurgists as well as ceramists and geochemists. Metallurgists have studied the system because of its importance in deoxidation equilibria, ceramists because of its importance in basic brick technology, and geochemists because of its importance for an understanding of natural chromite deposits. Chen and chipman1 investigated the Cr-O equilibrium in liquid iron at 1595°C in atmospheres of known oxygen pressures (controlled H2O/H2 ratios). The main purpose of their work was to determine the stability range of the iron-chromite phase. Hilty et al.2 studied oxide phases in equilibrium with liquid Fe-Cr alloys at 1550°, 1600°, and 1650°C. They reported the existence of two previously unknown oxide phases, one a distorted spinel with composition intermediate between FeO Cr203 and Cr3O4, the other Cr3O4 with tetragonal structure. They also sketched diagrams showing the inferred liqui-dus surface and the inferred 1600°C isothermal section for the system Fe-Cr-O. Koch et al3 studied oxide inclusions in Fe-Cr alloys and also observed the distorted spinel phase reported by Hilty et al. Richards and white4 as well as Woodhouse and White5 investigated spinel-sesquioxide equilibria in the system Fe-Cr-O in air in the temperature range of 1420" to 1650°C, and Muan and Somiya6 delineated approximate phase relations in the system in air from 1400" to 2050°C. The present study was carried out at a constant temperature of 1300° C and at oxygen pressures ranging from 0.21 atm (air) to 1.5 x 10-11 atm. The chosen temperature is high enough to permit equilibrium to be attained within a reasonable period of time within most composition areas of the system, and still low enough to permit use of experimental methods which give highly accurate and reliable results. These methods are described in detail in the following. I) EXPERIMENTAL METHODS 1) General Procedures. Two different experimental methods were used in the present investigation: quenching and thermogravimetry. In the quenching method, oxide samples were heated at chosen temperature and chosen oxygen pressure until equilibrium was attained among gas and condensed phases. The samples were then quenched rapidly to room temperature and the phases present determined by X-ray and microscopic examination. Total compositions were determined by chemical analysis after quenching. In the thermogravimetric method, pellets of oxide mixtures were suspended by a thin platinum wire from one beam of an analytical balance, and the weight changes were recorded as a function of oxygen pressure at constant temperature. The data thus obtained were used to locate oxygen isobars. The courses of the latter curves reflect changes in phase assemblages and serve to supplement the observations made by the quenching technique. 2) Materials. Analytical-grade Fe2O3 and Cr2O3 were used as starting materials. Each oxide was first heated separately in air at 1000°C for several hours. Mixtures of desired ratios of the two oxides were then prepared. Each mixture was finely ground and mixed, and heated at 1250" to 1300°C in air for 2 hr, ground and mixed again and heated at the same temperature for 5 to 24 hr, depending on the Cr2O3 content of the mixture. A homogeneous sesquioxide solid solution between the two end members resulted from this treatment. A Part of some of the sesquioxide samples thus prepared was heated for 2 to 3 hr at 1300°C and oxygen pressures of 10-7 or 1.5 x 10-11 atm. Reduced samples (either iron chromite

Jan 1, 1964

By D. G. Westlake

The electrical resistance of a series of V-H alloys (0 to 3.5 at. pct H) has been measured over the temperature range G° to 360°. Interstitial impurities made contributions to the residual resistivity, but not the ideal resistivity. The contribution of hydrogen in solid solution is expressed by Ap = 1.12 microhm-cm per at. pct H; but the contribution of precipitated hydride was negligible. A portion of the so1vu.s for the V-H phase diagram is presented. The solubility limit is given by In N (at. pct H) = (5.828 i 0.009) - (2933 i 44)/RT. Comparison of critical temperatures joy hydride precipitation and published critical temperatures for hydrogen embrittlement suggests the two are related. ThiS study was initiated as part of an investigation of the mechanism by which small concentrations of hydrogen embrittle the hydride-forming metals at low temperatures. It has already been shown that, in the case of hcp zirconium, a reduction in ductility accompanies the strengthening resulting from precipitation of a finely dispersed hydride phase.''' Our attempts to detect a similar precipitation of a second phase at low temperatures in V-H alloys by transmission electron microscopy have been thwarted because we have been unable to prepare thin foils that are representative of the bulk material with respect to hydrogen concentrati~n.~'~ The present investigation establishes the solvus of the V-H system at subambient temperatures. Subsequently, we hope to be able to determine whether the embrittlement temperature is related to the critical temperature for precipitation of the hydride in a given V-H alloy. veleckis5 has proposed a partial phase diagram for the V-H system based on extrapolations of the pressure-composition relations he measured at higher temperatures. Kofstad and wallace' conducted a similar study of single-phase alloys but did not attempt to establish the phase diagram. Zanowick and wallace' and ~aeland' have studied a portion of the phase diagram by X-ray diffraction, but they investigated no alloys in the hydrogen concentration range 0 to 3 at. pct, the range of interest to us. EXPERIMENTAL PROCEDURE The vanadium was obtained from the Bureau of Mines, Boulder City, Nev., in the form of electrolytic crystals. The analyses supplied with them listed 230 ppm by weight metallic impurities, 20 ppm C, 100 ppm N, and 290 ppm 0. The crystals were electron-beam-melted into an ingot that was rolled to 0.64 mm. Strips, 60 mm long and 4.2 mm wide, were cut from the sheet, and both rolled surfaces were ground on wet 600-grit Sic paper to produce specimens 0.4 mm thick. They were wrapped in molybdenum foil, vacuum-encapsulated in quartz, and annealed 4 hr at 1273°K. The specimens were annealed in a dynamic vacuum of 2X lo-' Torr for 30 min at 1073°K for dehydrogenation, and charged with the desired quantity of hydrogen by allowing reaction with hydrogen gas at 1073°K for 2 hr and cooling at 100°K per hr. Purified hydrogen was obtained by thermal decomposition of UH3. Sixteen specimens were studied: two contained no hydrogen and the others had hydrogen concentrations between 0.5 and 3.5 at. pct (hydrogen analyses were done by vacuum extraction at 1073°K). Electrical resistances were measured by the four-terminal-resistor method on an apparatus similar to the one described by Horak.~ The specimen holder was designed so that both current and potential leads made spring-loaded mechanical contact with the specimen. The potential leads were 30 mm apart, and the current leads were 55 mm apart. The current was 0.10000 amp. We used the following baths for the indicated temperature ranges: liquid nitrogen, 77°K; Freon 12, 120" to 230°K; Freon 11, 230" to 290°K; and ethanol, 290" to 340°K. Temperatures lower than 77°K were achieved by allowing the specimen to warm up after removal from liquid helium. Temperatures above 77°K were measured by a calibrated copper-constantan thermocouple (soldered to the specimen holder) and below 77°K by a calibrated carbon resistor. The temperature of the bath changed less than 0.l0K between duplicate measurements of the resistance. RESULTS AND DISCUSSION Typical plots of resistivity p vs temperature T are shown in Fig. 1. In the interest of clarity, only five curves are presented and the data points have been

Jan 1, 1968

By Larry Kaufman, Martin Schatz

The effect of pressure on the extension of the ? loop in the FeSi system has been determined by means of metallogvaphic studies and hardness measurements performed on a series of high-purity Fe-Si alloys containing 7.5, 11.0, and 13.9 at. pct Si, respectively. These mensurements, performed at 42 kbar and temperatures up to 1200oC, indicate that the ? loop is expanded to about 10 at. pct Si at 42 kbar as opposed to a maximum extension of 4 at. pct Si at 1 atm. Comparison of the experimental results with thermodynamic predictions of the pressure shifts yields satisfnctory results. DURING the past few years, several studies have been performed in our laboratory1-' in order to determine the effect of high pressure on phase equilibrium in pure iron and iron-base alloys. The purpose of these studies has been to elucidate the effects of high pressure experimentally and to compare the observed results with predicted pressure effects derived on the basis of known thermody-namic and volumetric data at 1 atm. These studies have included work on pure iron2,5,7 as well as Fe-Ni,1,5 Fe-cr,l,5 and Fe-c4-6 alloys. In addition, Tanner and Kulin3 have reported results of pressure studies on two Fe-Si alloys containing 2.0 and 6.25 at. pct Si. At the time of this latter study, no detailed information was available concerning the difference in volume between the a (bcc) and ? (fcc) phases in the Fe-Si system as a function of silicon content. In order to compare their observations with calculated pressure shifts, Tanner and Kulin were forced to assume that silicon had no effect on the difference in volume between a and ? iron. The resulting discrepancy between their calculation of the a/? phase boundary at 42 kbar and the observed results led them to the conclusion that silicon additions probably decrease the difference in volume between a and ? iron. Recently: Cockett and Davis8,9 have reported de- tailed studies of the lattice parameters of a series of Fe-Si alloys at temperatures ranging from 20" to 1150°C. These measurements, performed on alloys in the bcc and fcc range, show that silicon does indeed decrease the difference in volume between a and ? iron. By correcting the calculations of Tanner and Kulin in line with the observed effect of silicon they were able to show improved agreement between computed and observed pressure shifts.' The present measurements were undertaken to provide additional corroboration of this effect, by extending the range of composition, in addition to exploring a situation where large extensions of a ? loop could result in impingement of the ? field with an ordered bcc phase (based on Feo.75Sio.25). I) EXPERIMENTAL PROCEDURES AND RESULTS The alloys investigated were obtained from Dr. F. Kayser of M.I.T. They were prepared at the Ford Scientific Laboratory by vacuum melting electrolytic iron and high-purity silicon. The melts were poured under an argon atmosphere into hot-topped steel molds. Subsequently the ingots were hot-worked down to 1/2-in.-diam rods. Three alloys containing 7.5, 11.0, and 13.9 pct Si were studied. Carbon, regarded as the principal impurity, analyzed at, or below, 0.001 wt pct for all of the alloys. Prior to pressure-temperature treatment, the rod was annealed for 24 hr in vacuum at 1000°C, water-quenched, and subsequently machined into 0.100-in.-diam by 0.100-in.-long specimens. Subsequent to machining, the specimens were again annealed and then examined metallographically. They were found to exhibit a clear coarse-grained ferrite similar to Figs. 10 and 110 of Ref. 1 and Fig. 2 of Ref. 3. Subsequently, specimens of each alloy were equilibrated at 42 kbar at various temperatures in supported piston apparatus.1,3,4,6 Three specimens, one of each alloy, were wrapped in platinum and exposed simultaneously. The pressure-temperature cycle consisted of increasing the pressure from ambient to 42 kbar at 25oC, heating rapidly to the desired temperature, holding for 15 min, and quenching to 100°C, followed by slower cooling to 25°C and pressure release. The temperature was measured with a Pt/Pt-13 pct Rh thermocouple which was not corrected for pressure effects. Subsequently, specimens were examined metallographically and by

Jan 1, 1964

By W. H. Smith

IN connection with some recent work on the effect of impurities on the ductility of chromium, it appeared desirable to know the solid solubility of carbon in chromium. A literature survey indicated that this information was not available. Although considerable work has been done on the Cr-C phase diagram,&apos;.&apos; previous investigators have been more concerned with the structure and phase boundaries of the carbide phases than with the terminal solid solution. The phase diagram shown in Fig. 1 is taken from the work of Bloom and Grant&apos; and represents the most recent determination. As indicated by the dashed line, the a solid-solubility limit was not determined. Experimental Procedure Alloys of chromium were prepared from hydrogen-treated and vacuum-degassed electrolytic chromium plus spectrographic grade carbon. The oxygen and nitrogen content of the alloys was <0.002 pct. After melting, analysis of the alloys showed them to contain 0.02, 0.08, 0.15, and 0.55 pct C. Pieces of the alloys were heated in a protective atmosphere to various temperatures and then quenched after holding for a time sufficient to insure equilibrium. Microscopic examination of the as-quenched alloys for the presence of a second phase was used as a measure of the solubility limit. The heats were made in a multiple hearth arc-furnace using a zirconium-gettered static argon atmosphere. A zirconium melt was made before each Cr-C heat. Triple melting was used to insure ingot homogeneity as shown by microscopic examination. The alloys were prepared by adding portions of a 4.5 pct C-Cr master alloy to high purity chromium. The carbon contents listed previously were those obtained by analysis. The nitrogen and oxygen contents after arc melting were both <0.002 pct. Sections 1/8X1/4X1/2 in. were cut from the 100-g ingots and a hole drilled in one end in order to suspend the sample from a molybdenum wire. After the surface was carefully cleaned, a sample of each melt was hung in a mullite tube heated externally by a platinum resistance furnace connected to a vacuum system. The lower portion of the mullite tube was sealed to Pyrex and closed off several inches below the furnace. This was filled with sili-cone oil kept cold by circulating cold water around the outside of the Pyrex. Quenching into the oil bath was achieved by melting a fuse wire supporting the sample. It required about 4 sec for the sample to cool from 1400" to 600°C. This severity of quench was considered satisfactory to freeze-in the high temperature equilibrium. For tests made at temperatures of 900" to 1200°C, heating was done in vacuum; for tests above 1200°C, an argon atmosphere was used. The holding time employed ranged from 12 hr at 900°C to 6 hr at 1400°C. Experiments were performed at temperatures of 900°, 1000°, 1100°, 1200°, 1300°, and 1400°C. Microscopic examination for evidence of a second phase was done at X1500. Experimental Result The microstructures of a 0.08 pct C-Cr alloy as-cast and after quenching from 1300°C are shown in Figs. 2 and 3. A 0.15 pct C-Cr alloy quenched from 1300°C is shown in Fig. 4. The data obtained from the quenching experiments is shown graphically in Fig. 5. If the Van&apos;t Hoff equation is obeyed, a plot on a logarithmic scale of the mol fraction of solute vs the reciprocal of the absolute temperature should give a straight line. For dilute solutions the weight percentage can be substituted for the mol fraction without introducing any appreciable error. The Van&apos;t Hoff equation can then be written as where H is the heat of solution in calories per mol. The slope of the straight line on the log pct C vs 1/T plot gives the value of AH. Assuming that the Van&apos;t Hoff equation is obeyed, which is probably justified for the dilute solution of carbon in chromium, the heavy straight line shown on Fig. 5 represents the best fit of the data. This line was obtained as follows. On Fig. 5 the results of the microscopic examination of all alloys following quenching were plotted and designated as to whether one or two phases were seen. Below 1100°C all alloys showed a second phase on quenching. The heavy vertical lines shown in Fig. 5 therefore represent the possible range of the ter-

Jan 1, 1958

By W. C. Smith, P. J. Hickey

After a short historical background of the process evolution, this article descvibes present-day plant facilities and operating techniques utilized for high-purity bismuth production. The plant is one of the world&apos;s largest, with an annual output of some one million pounds of refined bismutlz. PREVIOUS papers1 written by staff members of Cerro de Pasco Corp. have referred briefly to the production of refined bismuth. Since the Corporation is one of the world&apos;s foremost producers of high-purity bismuth, a detailed description of the process for extracting the metal may be of general interest. Following a short historical background of the development of the actual process, this presentation will trace the progress of bismuth from its entry into the primary smelting circuits to its concentration in electrolytic lead cell slimes. Our facilities for the treatment of anode muds will be described and the extractive methods given in some detail, with particular emphasis on the techniques which result in the production of refined metal. HISTORICAL BACKGROUND Shortly after Cerro de Pasco began smelting operations at Oroya, Peru in 1922, it became apparent that the dust carried by copper converter gas contained appreciable amounts of bismuth. Although dust collection efficiency was poor prior to building of the 550-ft stack and installation of the central cottrells in 1938, a large stock of dust was accumulated during the intervening years, having the following approximate composition: Oz. per ton Ag - 11.0 Pct Sn — 0.5 Pct Pb - 49.0 Pct Zn - 6.5 Pct Bi - 2.0 Pct Insol. - 1.5 Pct Cu - 0.7 Pct Fe - 2.3 Pct Sb - 3.0 Pct S - 10.0 Pct As - 7.5 In the mid-1920&apos;s, experimental crucible melts of this dust with carbon indicated that most of the bismuth and silver, and some of the lead, could be reduced to a fairly clean bullion. Other products were a small amount of leady copper matte and a slag high in zinc, arsenic, antimony, and lead; this slag contained some tin but only small quantities of silver, bismuth, and copper. After the laboratory results had been confirmed by operation of a small reverberatory, a dust reduction furnace was constructed. The ±10 pct Bi-Pb bullion produced from this operation was stocked until 1930, when an Oroya-designed converter type furnace3 was installed for the elimination of arsenic, antimony, and some lead from the bullion. This process concentrated the bismuth from 10 to about 60 pct. By means of the bismuth process developed4 by W. C. Smith at East Chicago (1909-1914) and the discovery of a method5 for separation of lead from bismuth with chlorine gas in 1929, it became possible to begin production of refined bismuth. Unfortunately, bismuth deleaded with chlorine always contained residual chlorides, and the removal of the chlorides by caustic soda left a lead content of 0.02 to 0.04 pct. This final problem was solved6 by substitution of air-blowing for the caustic treatment, which effectively removed all excess chlorine and gave bismuth which was practically lead-free. In 1934, a pilot electrolytic lead refinery began operations at Oroya. Lead smelting was resumed in 1935 and two years later a 100-ton-per-day lead refinery was put into service. In conjunction with the latter, the present-day Anode Residue Plant was constructed. Until 1940, the plant treated both lead anode slimes and dust reduction bullion. The dust reduction furnace was shut down in that year, and all cottrell dusts (with the exception of the product from the arsenic cottrell) were mixed with pyrite and treated in a Wedge roaster to eliminate all possible arsenic. Calcine from this operation joined the sinter plant feed; hence the bismuth from the copper and lead circuits was collected in the lead bullion and subsequently in lead anode slimes from the electrolytic lead refinery. The latter source has been the only bismuth-bearing material of any consequence entering the Anode Residue Plant from late 1940 to the present. A copper refinery began operating in 1948, and the cell mud from this plant is mixed with lead slimes and processed through the same circuit, though only a small quantity of bismuth is present in electrolytic copper cell residues. BISMUTH INTAKE Present-day routes which are followed by the new bismuth feed from its entry into the primary smelting circuits to its arrival at the Anode Residue Plant are traced schematically in Fig. 1. As illus-

Jan 1, 1962

By S. T. Wlodek

The surface and subscale oxidation reactions were followed by means of continuous weight-gain and metallographic techniques over the range 1600" to 2200°F (871° to 1204 °C) for up to 400 hr. Full identification of all scale and subscale reaction products was obtained by electron and X-ray diffraction. At or below 1800°F (982°C) a linear rate of reaction (QL = 46.0 kcal per mole) governed the oxidation process, extending for up to 100 hr at 1600°F (871 "C). During linear oxidation the surface scale consisted of an amorphous SiO2 film overgrown with Cr 2O 3 and NiCr204. This initial linear process was followed, and above 1800°F completely replaced, by two successive parabolic rate laws (Qp = 60 and 57 kcal per mole). This parabolic reaction involved the formation of a complex scale consisting of Cr2 O3 and smaller amounts of NiCr2O4. Parabolic oxidation appeared to coincide with the disruplion of the silica film present during linear oxidation and was followed by subscale (internal) oxidation of crystobalite and NiCr2O4. The balance between the subscale and surface oxidation reactions controls the oxidation of this commercial alloy. The amorphous silica film appears to result in the linear rate and diffusion through Cr2O3 is the more likely rate-limiting step during parabolic oxidation. THE oxidation of a multicomponent composition is a complex phenomenon not presently amenable to a rigorous classical interpretation. Nevertheless, even a qualitative understanding of the scaling and subscale reactions that occur in a commercial composition can illuminate the reactions that limit its high-temperature stability in an oxidizing environment. This study of the oxidation of Hastelloy Alloy X presents the first of a series of studies with the above approach in mind. Hastelloy X exhibits one of the best combinations of strength and oxidation resistance available in a wrought, solution-strengthened, nickel-base alloy. Although during long time exposure some precipitation of M6C and M23C8 carbides as well as a complex Laves phase occurs, the amounts are probably small enough to have no appreciable effect on the chemistry of the matrix. Radavich has identified the oxidation products on Hastelloy X oxidized for 5 min to 10 hr at 1115°F as NiO and the NiCr2O4 spinel. Oxidation for 5 to 15 min at 1500°F produced a scale of spinel, NiO, and a rhombohedra1 phase, probably Cr2Os. Sannier et 2. have reported continuous weight-gain data for Hastelloy X at 1650" and 2010°F and internal-oxidation measurements after 150 hr at 2010°F. In addition, much of the data on binary Ni-Cr alloys recently reviewed by Kubaschewski and okins&apos; and Ignatov and Shamgunova4 as well as studies of binary Ni-Mo alloys5 are also pertinent to the oxidation of this composition. EXPERIMENTAL Continuous weight-gain measurements and metallographic measurements of subscale reactions were the main experimental techniques used in this study. X-ray and electron diffraction backed up by a limited amount of electron-microprobe analysis served to characterize the nature of the scale- and subscale-reaction products. Two heats of commercial sheet of the composition given in Table I and identified as A and B were used in the bulk of this study. Internal-oxidation measurements were made on a third heat of material in the form of a 0.5-in.-diam bar. In order to assure homogeneity, all heats were reannealed 4 hr at 2175°F prior to sample preparation. weight-Gain Measurement. All specimens (1.5 by 0.4 by 0.03 in.) were abraded through 600 paper, electropolished, and lightly etched in an alcohol-10 pct HCl solution. An electrolyte of 150 cu cm H,O, 500 cu cm HsPO4 (85 pct conc), and 3 g CrO3 at a current density of 0.9 amp per sq cm or a solution of 10 pct HaW4 in alcohol used at 4 v and 0.3 amp per sq cm was used for electropolishing. The resultant surface exhibited a finish of 3 ± 1 p rms. Continuous weight-gain tests were made at 1600°, 1700°, 1800°, 1900°, 2000", and 2200°F on auer&apos; type balances capable of recording a total weight change of 110 mg with an accuracy of k0.1 mg. All tests were made in air dried to a dew point of -70°F and metered into the 2-in.-diam reaction

Jan 1, 1964

By D. M. Waldorf

Steam permeability measurements have been made in the laboratory on several samples of natural reservoir materials. The steam temperatures and pressures were selected to simulate conditions which might exist in a reservoir during the injection of steam. For each sample tested, the experimental permeability to superheated steam was comparable to that measured with air and no evidence of plugging was detected. Some samples were exposed to water at various temperatures and plugging was found to occur in materials which contained significant quantities of monmorillonite clay. Temperature had little effect on the degree of plug-ning between 75 and 325 F. The measured pemeabilities tended to increase slightly with temperature, but the changes were small compared with the initial loss of per~neability on wetting. Sequential pemzeability measurements were made on two samples using air, water, steam, water and air, in that order. Both samples were water-sensitive and plugged extensively after the initial injection of water. Upon exposure to superheated steatm the samples dehydrated and their permenbilities to superheated steam were comparable to those initially measured with air. The remaining measuretnetzts with water and air confirmed that the water plugging was reversible and that the samples were not seriorrsly damaged during the tests. INTRODUCTION The swelling of water-sensitive clays during water floods has long been recognized as a potential source of reservoir damage. The recent extensive application of steam injection and stimulation has compounded this problem since both hot water and steam (as well as fresh water at reservoir temperatures) are, at sume time, in contact with the producing zone adjacent to the bore of a steam injection well. The purpose of this paper is to present data which compare the sensitivity of some natural sedimentary rock samples to water at various temperatures, and to super-heated steam. Some properties of montmorillonite clay are briefly reviewed, and comparisons are drawn between empirical data and the predicted behavior of the montmorillonite known to be present in the samples. PROPERTIES OF MONTMORILLONIT E CLAY Water initially adsorbs on dry N a -montmorillonite clay in discrete layers in the interlaminar space between clal platelets. The platelet spacing, which is 9.6 A (angstroms) for a dehydrated clay, has been observed to expand in discrete steps to 12.4, 15.5, 18.4 and 21.4 A spacings, indicating the formation of four discrete layers of regularly oriented water molecules.&apos; The first two layers are easily formed by hydrating a dry sample to equilibrium in an atmosphere with carefully controlled humidity. The formation of the higher layers is more difficult. The usual X-ray diffraction patterns of the more highly hydrated samples indicate a gradual increase in the average spacing betwcen 15.5 and 19.2 A, followed by a discontinuous expansion to 31 A when the weight ratio of water to dry clay is between 0.5 and 1.2.&apos; Platelet expansion above 31 A proceeds monotonically as the moisture is increased and no regular arrangement of the platelets ib observed. Water-sensitivity in sedimentary rocks is usually associated with Na-montmorillonite clay when it is in the noncrystal-line state. Mering3 found that the average lattice spacing of sodium montmorillonite hydrated at 68 F and 70 per cent relative humidity was 15.5 A, and that the spacing, at 92 per cent humidity was 16.5 A. The water adsorbed at the higher humidity has the same free energy as liquid water at 65.6 F. Kolaian and Low&apos; used a tensiometer to measure the thermodynamic properties of water in diffuse suspensions of montmorillonite clays relative to pure water. They observed that water in suspensions as dilute as 6 per cent clay became partially oriented when left undisturbed. The bonding associated with this orientation was not extensive because the free energy difference between the water in suspension and pure water was only a few millicalories per mole. They also found that the measured free energy difference decreased rapidly with temperature and became negligible above 100 F. This evidence indicates that montmorillonites contained in sedimentary rocks would dehydrate to a crystalline structure when exposed to superheated steam, and that the rock permeability measured with steam would be equivalent to that measured with air. The effect of elevated temperatures on the swelline of montmorillonite clays in aqueous suspensions has not been investigated. The Gouy-Chapman diffuse-ion-layer theory has been used to predict the swelling pressure of clay suspensions in dilute salt solutions at room temperature with reasonable success. theory also correctly predicts the direction of the thermal response of Na-mont-morillonite swelling pressures in dilute salt suspensions, 9 Over the temperature range of 33 to 68 F, an increase in

Jan 1, 1966

By J. E. Flinn, S. A. Duran

The steady-state creep behavior of poly crystalline cad mi inn was studied over a temperature range of (1.56 to 0.94 Tm. Two distinct mechanisms were found to occur over this temperature range. They were described by: where and represerqt the minimum strain rates corresponding to the low- and high-temperature regions, respectirely. The two regions of constant acti11ation energy were connected by a transition region where the strain rate was controlled by both mechanisms acting in parallel. At temperatures below a transition temperature of about 0.7 Tm the agreement between the activation energy value for creep and that for self-diffiision suggests a rate-controlling mechanism of dislocation climb. For cadwzium, steady-state creep at temperatures above 0. 7 Tm appears to be controlled by another mechanism, perhaps involving the behavior of dislocation jogs. FRENKEL et al.1 studied the high-temperature creep of polycrystalline cadmium and reported an activation energy of 21 kcal per mole for the 0.5 Tm < T < 0.8 Tm range. Based on observations of creep rate at only two temperatures, a value of 22.1 kcal per mole was determined by Medbury. These two investigations were for the purpose of showing agreement between the activation energy for creep and that for self-diffusion, reported3 as 18.2 and 19.1 kcal per mole, respectively, for diffusion parallel and perpendicular to the hexagonal axis. Gilman4 investigated prismatic glide in single crystals of cadmium over a higher-temperature range of 0.72 to 0.93 Tm, and found an activation energy of 29 kcal per mole. He also reported5 an activation energy higher than that of self-diffusion for prismatic glide in zinc single crystals deformed at temperatures near the melting point. This value was in good agreement with those found for an equivalent temperature range by Flinn and Munson6 and by Tegart and sherby7 for polycrystalline zinc. These two independent studies also disclosed at lower temperatures another value of activation energy near that for self-diffusion. It would be expected from the creep results on zinc and single-crystal cadmium that creep studies on polycrystalline cadmium, extended to temperatures near the melting point, might yield an activation-energy value higher than the 22 kcal per mole value found in earlier studies. The purpose of this paper is to report the steady-creep behavior of polycrystalline cadmium over a temperature range of approximately 0.5 to 0.9 Tm EXPERIMENTAL METHOD The cadmium used in this study was obtained in the form of as-cast rods, 0.5 in. diam, through the courtesy of the Bunker Hill Mining Co. The material was of 99.995 pct purity, as determined by spectro-chemical analysis. The creep specimens, which were 0.250 in. diam by 0.400 in. long and annealed at 300°C for 45 min to produce a stable average grain diameter 0.25 mm, were tested in compression using an apparatus similar to that described by Sherby.8 The specimen temperature was controlled to within ±0.5°C with the help of appropriate constant-temperature baths. The applied stress was maintained within 1.0 pct of the desired value by the additions of lead shot at fixed strain increments. No barreling was observed over the strains encountered during testing. Isothermal creep tests9 were used in the study with only a few differential temperature tests10 run for comparison purposes. Steady-state creep data were obtained over a temperature range of 60 to 287°C (0.56 to 0.94 Tm) at five stress levels ranging from 28.1 to 140.6 kg per sq cm. RESULTS The minimum or steady-state creep rate may be described by an equation of the following form:" where i is the minimum strain rate, S is the structure factor, F is a stress function, Qc is the energy of activation, T is the absolute temperature, and R is the gas constant. The minimum strain rates obtained in this study for cadmium were recorded on a semilogarithm plot as a function of the reciprocal absolute temperatures for the various stress levels, as shown in Fig. 1. This figure shows a characteristic transitional behavior" with a parallel interaction of two mechanisms. It is obvious that the activation energies corresponding to the individual processes are insensitive to stress because the curves are parallel. The discrete activation-energies values for the low- and high-temperature regions for the various stress levels are reported in Table I, and were determined by the least-mean-square method. For the low-temperature region, an activation energy of 20.7 ± 0.6 kcal per mole was obtained, and for the

Jan 1, 1967

By F. Claisse, R. Angers

Self-diffusion in iron has been measured during rapid a-r transformations using a variant of the Kryukou and Zhukhovitskii diffusion method. The study was performed by thermally cycling iron foils (1 to 6 cpm) through the transformation (=910°C). Some foils have been subjected to over 1000 cycles and some have spent more than 15 pct of their total diffusion time in the process of transformation. The experimental results show that the a-r transformation has no measurable effect on self-diffusion in iron. The study is completed by a quantitative analysis of mechanisms which can affect the diffusion rate during the transformation. The analysis confirms the experimental results. SINCE diffusion is an important factor in many solid-state transformations, it is of interest to study how it is affected by the stresses generated during these transformations. Clinard and Sherby1&apos;2 were the first to make a study along these lines. They measured diffusion coefficients in Fe-FeCoV couples subjected to slow thermal cycling (1.5 cph) through the a-r transformation range. They found an enhancement of diffusion by a factor of about two. The purpose of the present paper is to report measurements of the self-diffusion coefficient of iron during much more rapid thermal cyclings (1 to 6 cpm) through the a-r transformation (-910°C). These more rapid cyclings produce higher strain rates during the transformation and should emphasize any possible influence of transformation upon diffusion. EXPERIMENTAL Iron foils, 25 to 35 µ thick, were cold-rolled from 99.92 pct pure iron and annealed in pure helium for 2 hr at 870°C; the resulting grain diameter was about 150 µ. Specimens 0.5 by 8 cm were cut from the foils and I7e55 was vapor deposited on one of their surfaces. A 38 gage alumel-chrome1 thermocouple was spot welded in the middle of one of the specimen long edges, Fig. 1. Two 38 gage chrome1 wires were also spot welded along the same edge on each side of the thermocouple; they were placed 2.5 cm apart and used for electrical resistance measurements. In order to prevent twisting and crumpling, the specimens were pinched between two quartz plates 0.1 by 1 by 7 cm and the assembly was close fitted into a 1 cm ID quartz tube. Four holes were drilled through the tube to let the 38 gage wires out: these were connected to the recording equipment by means of extension wires. 20-gage nickel wires fixed at both ends of the specimens were used to thermally cycle the foils by Joule heating. The above described device was placed in a 2.7 cm ID quartz tube which in turn was placed in a tubular furnace. Either a pure helium atmosphere or circulating hydrogen was used during the experiments. Specimens were subjected to thermal cycles between a minimum temperature To and a maximum temperature Tm at rates ranging from 1 to 6 cpm. This was obtained by maintaining the furnace at a constant temperature near the minimum temperature To and periodically passing an electric current through the specimen. Cooling was achieved by heat losses to the surroundings. The forms and periods of cycles were varied from one specimen to another; however, each specimen was subjected to one type of cycle only. The temperature and electrical resistance variations of the specimens were recorded as a function of time. The temperature curves were used for diffusion calculations while the electrical resistance curves were used to monitor the transformation and to determine its starting point and its approximate duration. Diffusion was measured by the method developed by Kryukov and zhukhovitskii3 and modified by Angers and Claisse.4,5 In this method a metallic foil is coated on one side with a radioactive isotope and the activity is measured periodically on both sides during the diffusion anneal. The following equation then holds: where: I1 Activity on the surface on which the deposit is made. I, Activity on the opposite surface. t Diffusion time. B Constant. D Diffusion coefficient. d Foil thickness including the deposit. G(t) A function of time; it is a second order correction term which is given graphically in Refs. 4 and 5. The diffusion coefficient D is found by plotting ln[(Il - I2)/(I1 + I,)] -G(t) against t; the resulting slope m leads to an accurate calculation of D through Eq. [2]. The effect of the a-r transformation on diffusion is expressed by the ratio DT/DU where:

Jan 1, 1970

By R. O. Williams

Analytical representation of the thermodynamics of solutions is highly desirable from the standpoint of accuracy, compactness, and numerical manipulations. In particular, computer calculations are greatly implemented. Mathematical considerations show that previous expressions have one or more serious defects. This investigation shows a Fourier series to be satisfactory but that it is also possible to derive a new series which fits certain additional conditions. Included examples show the value of analytical expressions in giving a simple characterization of each system using some two to five parameters, the elimination of the Gibbs-Duhem integration, and the es timation of the error for the experimental function as well as derived functions. It is further shown that the present characterization provides easy comparison between systems. IN the past, thermodynamic calculations have depended to a considerable extent on tabular and graphical methods. As the volume and precision of such data increase such methods become less satisfactory. Specifically, the selection of the optimum representation and the estimation of errors require statistical methods which in turn require analytical representation. The utilization of such data require further manipulations which are best done analytically for maximum precision. For example, phase equilibria are determined by common tangents to free-energy curves: a graphical determination is normally of low accuracy. As computers are increasingly used analytical representations become almost mandatory. Insufficient mathematical consideration has been given previously to the selection of empirical expressions. Those expressions having some theoretical justification are generally too inflexible and mathematically unattractive. We consider the problem in some detail and show that a Fourier series can be effectively used. Also a new series is defined which has certain advantages. ANALYSIS We wish to consider the analytical representation of the heat of mixing, AH, the excess free energy, ?Gxs, and the excess entropy, ?sXS, as a function of composition, X, for binary solutions relative to the pure components in the same state. When a distinction is not required, we use W to denote any one of the above functions. One may use a Taylor expansion around X = 0 to generate a power series. As the derivatives are un- known we represent the series as W = A + BX + CX2 + DX3 + EX4 + ... [l] where the constants A , B, C , ..- are to be selected to provide some optimum fit. For the extremes of composition W is necessarily zero so it follows that A = 0 [2a] B +C + D + E +••• = 0 [2b] Nonelectrolytes, which we are considering, appear to satisfy the condition that d3W/dx3 = 0 [3] in the terminal regions. This is the basis of the a, ß, and Q functions used by Hultgren et al.&apos; and others. While this condition does not have a strong theoretical basis it does appear desirable that any analytical relation should satisfy this condition. Darken2 and Turk-dogan and Darken3 have shown that many systems exhibit this behavior over an extended range from each terminal region, departure being restricted to a limited intermediate region. Since we have no a priori knowledge as to where this transition occurs we can require that this condition be satisfied only as a limit at the extreme compositions as a general condition. We will show later how more restricted conditions can be included in specific solutions. Darken2 has called this behavior the quadratic formalism; we call our application the limiting quadratic formalism, LQF. This condition applied to the above power series requires that D = 0 [4a] 4-3-2E +5-4-3_F + 6 • 5 . 4G + ••• =0 [4b] The form of the power series normally used, due to Margules,4 is W=X(1-X)(A + BX + CX2 + DX3 + EX4 + •••) [5] where A, B, C, --. are a new set of constants. (Guggenheim5 has given a variation of this expression in a more desirable form. Since, however, it is contained in the above expression it does not require separate consideration.) This form is precisely what results by incorporating the conditions in Eq. [2] into the power series and regrouping the constants. The LQF requires that B =C [6a] and 4.3.2(D-C) +5-4-3(E-D) + ••• =0 [6b] Thus, the correct form of the Margules expression with two adjustable parameters is w =X(1-X)[A + B +X2-2/3x3)] 171 and the EX4 term must be included before three adjustable parameters are permitted.

Jan 1, 1970

By Luc Delaey, Horace Pops

The structure and morphology of thermoelastic and burst type martensitic phases that form upon cooling in Cu-Zn-Si p phase alloys have been studied by transmission electron microscopy. The martensitic phases are composed of a lamellar mixture of two close-packed structures with different stacking sequence, namely ABCBCACAB (orthorhombic) and ABC (fcc). Striations within thermoelastic martensite are most likely produced during interaction with impinging burst-type martensite and not as a consequence of secondary shears. In a study of the martensitic transformation in ternary Cu-Zn based 0 phase alloys1 the dependence of the martensitic transformation temperature, M,, with composition shows variations for elements within a constant valence subgroup and between different subgroups. Such variations are not reflected in a change in habit plane, which is approximately the same for each ternary alloy, namely in the vicinity of (2, 11, 12 Ip. The fact that the habit plane remained constant, despite large differences in M, temperature and electron concentration, suggested2 that the crystal structures of the martensitic phases could be nearly the same. Crystal structures of ternary Cu-Zn based martensites have been determined recently for alloys containing the three-valent elements gallium3, 4 and aluminm. The present studies have been made to examine the structures and morphology of the martensitic phase in ternary Cu-Zn based alloys containing a four-valent element, silicon. I) PROCEDURE Two alloys were prepared by melting and casting weighed quantities of the component high-purity metals in sealed quartz tubes under half an atmosphere of argon. They were subsequently remelted by levitation under a protective atmosphere of argon. After allowing for losses of zinc as determined by the difference in weight before and after casting, the compositions in atomic percent of both alloys were established to be Cu-33.5 Zn-1.8 Si and Cu-27 Zn-5.0 Si. These alloys were homogenized in the P-phase field for 2 days at 800" C. Bulk samples consisted of a martensite phase at room temperature, the M, temperature being approximately 30&apos; and 200" for the 1.8 and the 5 pct Si alloys, respectively. Thin disks were cut from the ingots using a spark machine, and they were heated for 5 min at 800&apos; and quenched into water in order to obtain martensite. These slices were thinned chemically at room temperature in a solution consisting of 40 parts HN03, 50 part H3PO4, and 10 parts HC1 and thinned further electrolytically by the Window technique, using a voltage of 15 to 25 v and a mixture of 1 part HN03 and 2 parts methanol, which was kept at a temperature near -30° c. Foils were examined by transmission electron microscopy using a Philips EM 200 electron microscope. 11) RESULTS AND DISCUSSION 1) Structure and Morphology. Fig. 1 shows the martensitic phase in the alloy containing 1.8 at. pct Si. This phase is composed of contiguous platelets, each containing striations. The direction of the striations changes at the boundary between individual platelets. These internal markings resemble the striations that are usually identified as stacking faults, as for example in Cu-A1 martensites6-a or the lamellar mixture of two close-packed phases in Cu-Zn-Ga marten-sites.3p &apos;9 lo In the present alloys, selected-area diffraction experiments have been obtained in order to determine the nature of the striations. Figs. 2(a), (61, and (c) are electron diffraction patterns of an area inside a single martensite plate. Fig. 2(a) contains diffraction spots which correspond to two close-packed structures with different stacking sequences, namely ABCBCACAB (orthorhombic) and ABC (fcc). Spots belonging only to the fcc structure are indicated by arrows. By tilting the foil either the orthorhombic structure, Fig. 2(b), or the cubic structure shown in Fig. 2(c) may be obtained. When the foil is oriented so that only the diffraction spots of the orthorhornbic structure are present, bright-field illumination shows small lamellae, as seen in Fig. 3. In this figure the lamellae that belong to the fcc structure are bright bands inside the dark extinction contours of the orthorhombic structure. The boundaries of the lamellae are parallel to the basal planes of the orthorhombic structure and to the {Ill} planes of the cubic structure, the close-packed directions of both structures being parallel. The 5 pct Si alloy shows similar features as those described for the 1.8 at. pct Si alloy.

Jan 1, 1969

By A. F. Crawley

The density and viscosity of 1iquid thallium have been measured by absolute methods to temperatures of about 200° and 150°C, respectively, above the melting point. These new data reported, especially density data, do not closely confirm previous work. Density p, in g per cu Cm, is shown to vary linearly with temperaluve t, in °C, according to the equation p = 11.658 - 1.439 X l0-3t. The viscosity data obey the well-known Andrade equation nv1/3 = A exp C/vT , the constants A and C for thallium having values of 2.19 x A and 79.648, respectively. This paper reports some new data for the density and viscosity .of liquid thallium. Measurements of these fundamental physical properties were undertaken as part of a continuing research program at the Mines Branch, Department of Energy, Mines and Resources, Ottawa. Canada. A literature search has revealed that data are so scarce that there could not be a consensus on the true values of the density and viscosity of liquid thallium. To be more specific, there exists only one set of viscosity data&apos; and only two acceptable sets of density data,273 one of which is limited in scope.3 In Liquid Metals Handbook,3 another density study is reported but indications of impurities in the thallium render the results suspect. In this situation, further careful experimentation was required to realize the true density and viscosity of thallium. EXPERIMENTAL METHODS Density. Densities were determined using a graphite pycnometer. The technique and its accuracy have been discussed in earlier papers.4&apos;5 It is considered that experimental data can be obtained which are accurate within +0.05 pct, all sources of random and systematic errors having been evaluated. Density results for thallium were identical whether measured under an atmosphere of argon or a vacuum of 5 x 10-6 torr and, for the most part, the argon atmosphere was used. Viscosity. Viscosity measurements were made in an oscillational viscosimeter by an absolute method—the liquid metal being held in a closed graphite cylinder. Design and operation of the apparatus, constructed in this laboratory, have previously been discussed.6 For thallium, runs were made under a vacuum of about 2 x 10-6 torr. To evaluate viscosity coefficients from the various experimental parameters, the mathematical analysis of Roscoe7 was used. Measurements of the necessary parameters and the accuracy of these measurements have also been discussed.6 The cylinder dimensions were corrected for the anisotropic expansion of graphite, as discussed for density measurements.4,5 It is well-known that thallium oxidizes rapidly and hence a newly machined surface quickly tarnishes in air. The oxide film, however. is nonadherent and is easily removed by rubbing or by solution in water. Hence, immediately before use, both density and viscosity charges were immersed in water, wiped dry, and quickly transferred to the apparatus which was then rapidly evacuated. Specimens removed after determinations were only slightly tarnished and there was no other evidence that tarnishing affected the results. For example, the sharpness of the specimen edges from the containing vessels indicated complete filling by the liquid metal. Thallium of 99.999 pct purity was used in this investigation. Because of its high toxicity care was exercised in handling this material. For example, the melting procedure to prepare machinable ingots was carried out in an open, well-ventilated area, while protective gloves were always worn when handling the solid metal. RESULTS AND DISCUSSION Density. Measurements were made over a tempera-ture range of about 200°C above the melting point. The results are listed in Table I and plotted in Fig. 1. From the graph it is evident that the relation between density and temperature is linear. Such a relation has been observed before in this program for other metals and alloys475 and elsewhere by other workers. A least-squares analysis of experimental data gives the equation: pT1 = 11.658 - 1.439 x 10-3t where p = density in g per cu cm and t = temperature in "C. In Fig. 1, together with the present results, the data of Schneider and Heymer2 in the corresponding temperature range have also been plotted. Evidently, the two sets of data do not agree well, the results of Schneider and Heymer being about 0.6 pct higher. Viscosity. Viscosity data were obtained from the melting point, 303.5°C, up to 457.5"C. The data are listed in Table I and in Fig. 2 the plot of these results demonstrates a smooth curvilinear relation between

Jan 1, 1969

By Walter Knox, J. D. Doherty

IN 1939, at the request of The Koppers Coal Co., the Koppers Company Research Department established a Stoker Coal Research Laboratory for the purpose of investigating the performance characteristics of stoker coals in typical domestic stoker installations. Fig. I is a photograph of part of the laboratory. The material in this paper deals with the performance of one coal in a single installation. Presented are details of this installation, mechanical characteristics of the stoker, and the results of a series of burning tests in which adjustments were systematically varied. SUMMARY OF RESULTS Mechanical Features I. A large percentage of the total power consumed by a domestic stoker is used to operate the gear case and motor (Fig. 3). 2. The power consumption per ton goes down with an increase in rate of coal feed (Fig. 4). 3. The automatic air control in this stoker showed advantages over manual control (Fig. 5). 4. The air velocities through the retort tuyeres were uniform around the retort, but varied between the rows of tuyere rings (Fig. 6). 5. The crushing of coal with this stoker increased the minus 1/8-in. from 1 1.6 per cent to 19.2 per cent. There was a noticeable segregation of coal as it came from the retort and distribution was not uniform (Fig. 7). 6. Measurement of air entering over the fire showed that with some not uncommon adjustments this air may he a high percentage of the total air supply (Fig. 8 and Table I). Operating Performance I. The removal of clinker was shown to give a period of poor performance characterized by a high fuel-bed resistance and a high percentage of carbon monoxide in the flue gases (Fig. 10). 2. The fuel-bed resistance was found to decrease as the fuel bed built up in a normal response to heat demand after a prolonged hold-fire (Fig. II). 3. With intermittent operation the burning rate was almost always less than the feeding rate. The wide variations were found to be greatly dependent upon the length of the On period and the length of the intervals between On periods (Fig. 12). 4. The maintenance of a low furnace draft led to less fly ash, better clinker formation, and higher efficiencies (Fig. I3). 5. The maintenance of a minimum of excess air also resulted in less fly ash, better clinker formation, and higher efficiencies (Fig. 14). GUIDING PRINCIPLES In planning the investigations, the following principles were adopted: Selection of Healing Equipment.-Use only standard models of stokers and furnaces representative of those widely used.

Jan 1, 1942

By T. R. Graham, J. R. Long

This report is concerned with part of a series of investigations carried on by the Federal Bureau of Mines on alloys, particularly nonferrous alloys, made with electrolytic manganese. A broad general program instituted after commercial quantities of electrolytic manganese became available was necessary in order to compare the effects of electrolytic manganese with those of the ordinary commercial grades. Representative analyses of these two materials show the commercial manganese metal to contain up to 2 per cent iron, a maximum of I per cent silicon and 0.06 per cent carbon, while the electrolytic manganese rarely exceeds 0.01 iron, 0.02 sulphur, with no silicon or aluminum. In the literature, the emphasis has been largely on high-strength casting alloys containing up to 5 per cent manganese, and few data are available on wrought manganese alloys. These factors, coupled with the strategic position of copper and zinc, have given impetus to the Bureau&apos;s War Research Program for the development of alloys containing nonstrategic manganese for the purpose of supplementing or providing alternates for the more strategic metals. The alloy reported here was studied, along with several other ferrous and nonferrous alloys, as possible cartridge-case material, and was chosen after a review of the properties of the ternary alloys of copper-manganese-zinc. Preliminary Work In a cursory survey of this system, alloys ranging from 60 to 95 per cent copper, o to 50 per cent manganese, and 5 to 40 per cent zinc were investigated. The alloys containing 60 per cent copper were found to fall into the two-phase alpha plus beta region of the system, and since those containing 70 per cent would not permit a saving, only alloys containing 65 per cent copper were considered. The tensile properties of these 65 per cent alloys are plotted in Fig. I as a function of manganese content for annealed material and for four conditions of cold-work In the annealed condition the increases in strength and decreases in elongation are minor up to 15 per cent manganese; beyond this, the changes become more significant. In the cold-worked condition, the first 5 to 10 per cent of manganese appears to have the greatest strengthening effect, the rate of increase dropping off as the manganese increases beyond this amount. These effects are more pronounced with moderate than with severe cold reduction. It is also interesting to note that while the elongation of annealed material drops regularly with increasing manganese, the elongation in the cold-worked state is relatively little affected by increasing manganese content, particu-

Jan 1, 1944

By J. R. Long, T. R. Graham

This report is concerned with part of a series of investigations carried on by the Federal Bureau of Mines on alloys, particularly nonferrous alloys, made with electrolytic manganese. A broad general program instituted after commercial quantities of electrolytic manganese became available was necessary in order to compare the effects of electrolytic manganese with those of the ordinary commercial grades. Representative analyses of these two materials show the commercial manganese metal to contain up to 2 per cent iron, a maximum of I per cent silicon and 0.06 per cent carbon, while the electrolytic manganese rarely exceeds 0.01 iron, 0.02 sulphur, with no silicon or aluminum. In the literature, the emphasis has been largely on high-strength casting alloys containing up to 5 per cent manganese, and few data are available on wrought manganese alloys. These factors, coupled with the strategic position of copper and zinc, have given impetus to the Bureau&apos;s War Research Program for the development of alloys containing nonstrategic manganese for the purpose of supplementing or providing alternates for the more strategic metals. The alloy reported here was studied, along with several other ferrous and nonferrous alloys, as possible cartridge-case material, and was chosen after a review of the properties of the ternary alloys of copper-manganese-zinc. Preliminary Work In a cursory survey of this system, alloys ranging from 60 to 95 per cent copper, o to 50 per cent manganese, and 5 to 40 per cent zinc were investigated. The alloys containing 60 per cent copper were found to fall into the two-phase alpha plus beta region of the system, and since those containing 70 per cent would not permit a saving, only alloys containing 65 per cent copper were considered. The tensile properties of these 65 per cent alloys are plotted in Fig. I as a function of manganese content for annealed material and for four conditions of cold-work In the annealed condition the increases in strength and decreases in elongation are minor up to 15 per cent manganese; beyond this, the changes become more significant. In the cold-worked condition, the first 5 to 10 per cent of manganese appears to have the greatest strengthening effect, the rate of increase dropping off as the manganese increases beyond this amount. These effects are more pronounced with moderate than with severe cold reduction. It is also interesting to note that while the elongation of annealed material drops regularly with increasing manganese, the elongation in the cold-worked state is relatively little affected by increasing manganese content, particu-

Jan 1, 1944

By R. B. Adamson

The fatigue behauior of irradiated copper single crystals is compared to that of unirradiated crystals. Proton or electron irradiation did not substantially change the fatigue-lzj.e, fatigue-hardening-, or slip-line characteristics, while neutron irradiation did appear to alter these parameters. Postfatigue transrrzission electron microscopy did not reveal any marked structural differazces between irradiated and unirradiated specimens. Possible dislocatio~a mechanisnzs to explain the observed behavior are discussed. A LTHOUGH considerable work has been done to ascertain the effects of radiation on the tensile properties of metals (e.g., Refs. 1 and 2), little work of a basic nature has been reported on the effect of radiation on fatigue properties. Since it is known that fatigue properties are sensitive to conditions at the surface of the metal, it was felt that charged particle irradiation, whose penetration into metals is very small, might influence the fatigue behavior. To investigate this surface effect, irradiations with 10 mev protons and 1.5 mev electrons were conducted. The range of 10 mev protons in copper is about 0.236 mm; which is very small compared with the thickness of the specimens used (1.53 mm). The range of 1.5 mev electrons is somewhat larger, on the order of 0.665 mm.4 On the other hand, irradiation with reactor neutrons produces damage throughout the entire specimen, so neutron irradiation can be used to study the effects of bulk damage. The damage introduced by proton and neutron irradiation is expected to con!ist of large interstitial dislocation loops,5 tiny (<25A) vacancy loops," and/or various vacancy-rich regions called depleted zones.&apos; In the case of electron irradiation at about -173°C the damage is expected to consist of isolated Frenkel pairs.&apos; The effect of radiation damage on the fatigue properties of some engineering materials has been reported,g,10 but the results are not clear-cut or consistent. SPECIMEN PREPARATION Zone-refined copper was used to grow single crystals by a modified Bridgeman technique in an inert helium atmosphere. Using a seeding method, single crystals were obtained as bars about 6 in. long with a cross section of 3 by $ in. Immediately upon removal from the split-mold graphite boat in which they were grown, the very soft bars were embedded in a room-temperature setting plastic. They could then be cut into specimen lengths without introducing any long-range damage. Generally, four or five specimens plus one seed were obtained from each bar. The plastic material was dissolved away in acetone and the orientation of each sample was checked by the standard Laue X-ray

Jan 1, 1968

By R. M. Brick

SEGREGATION can occur only in cast alloys that solidify over a range of temperatures with a difference in composition of liquid and solid phases within this range (ignoring monotectic systems and chemical reactions as in rimming. steels). Thus a pure binary eutectic alloy should show no segregation unless undercooling occurs for one of the solid constituents of the eutectic; e.g., chill-cast Al-12 per cent Si alloys. The phasial condition implicitly described above-solidification over a range of temperatures with a compositional difference between solid. and liquid-is found in nearly all solid solutions or combinations of solid solutions and eutectics. Metastable conditions of solidification of these types of alloys cause coring; i.e., a difference in composition between the center of a dendrite and its periphery. This composition gradient can be detected usually only by microscopic examination of etched structures; it is a "micro" effect. The gradient of more immediate industrial concern is that between the center of a cast section and the surface layers. This gross (macro) effect is usually determinable only by sampling of the casting at different points, with chemical analyses of each sample. If the compositional difference is of the same type as in coring, the first parts to freeze being enriched in higher-melting-point constituents, and vice versa, the effect is called normal segregation. When what is apparently the first part of the casting to solidify shows a higher concentration of low-melting-point constituents, the effect is called inverse segregation. These macro effects are quite separate from the micro effect, coring, yet the latter must be. described first because it is an essential part of the picture. CORING Solid Solution, Ni-Cu The nickel-copper phase diagram is reproduced in Fig. Ia, in which the solid lines represent the equilibrium liquidus 1, 3, 7 and solidus 2, 5, 8, and where the vertical 1, 4, 8 represents a 55 per cent Cu alloy. Upon moderately rapid solidification, the first dendritic axes of composition 2 (see Fig. 1b) start to form at a temperature somewhat under I. Solidification continues by growth of the dendritic nuclei, but at temperature 4 the increment solidifying is of composition 5. The rapidity of this crystal growth prevents diffusion of nickel and copper atoms from adjusting the composition of the entire dendrite at 5, which it would be under equilibrium conditions. The average composition of a specific dendrite, or the entire solid phase, at temperature 4 might be that indicated

Jan 1, 1944

By Alfonso W. Ovalle, Héctor R. Albornoz

INTRODUCTION The El Teniente Mine of Codelco-Chi le has extracted 588 mil lion tons of ore in its 77 year history for a total copper output of 8.800.000 tons. The mine production has been obtained mainly by traditional block-caving where grizzlemen using a hand held lever send ore through long-raises to load trains. At present the mine is about to introduce mechanized block-caving using LHD equipment to extract the primary rock. This paper describes this method which will be tested starting next month by caving an 11.000 square meter block. THE PRIMARY ROCK PROBLEM The secondary enrichment sulfides of the El Teniente ore body have characteristics which makes a standard unmechanized block-caving practice very successful. In the 60&apos;s parts of blocks encountered primary ow in the Teniente 1 and Sub-13 levels which proved to be extremely hard to extract. These foretold the obstacles that arised in the central part of the Teniente 4 level. Preparation of a completely primary 8.100 square meter block started in 1970. Its undercutting was completed by the end of 1972 and by 1973 the problem of mining the primary rock was clearly visualized. The numbers below describe the difficulties in mining this block: -Long-hole drilling rate is 90 m (270 ft) per shift in secondary rock and 37 m (110 ft) in primary. - Undercutting which is completed in 9 shifts in secondary took 180 shifts in the primary block. - Average grizzlymen productivity in secondary is 250 tons per shift while in primary it is only 25-30 tons, both at 343 mm (13 1/2 in. ) grizzly opening. - Powder consumption for secondary blasting increased from 8 grams per ton in secondary to 84 in primary. - The protection pillar between the under- cutting and the production levels was 60% broken in primary while 20% is usual for secondary. - Extraction advanced 5 cm per day in primary while a 50 cm per day rate is the aver- age in secondary. This is the main reason that after 8 years this primary block has a 20% extraction. Secondary blocks take 1.5 to 3 years to complete their extraction. - 80% of the boulders in primary rock are larger than 343 m (13 1/2 in.) with 10-20 % of them larger than 3 meters. -Direct cost of production (preparation, undercutting, extraction and haulage), using the traditional block-caving design for secondary rock, increased 3.5 to 4 times when used in primary rock. The following indicators of Table 1 show the rock characteristics differences.

Jan 1, 1981

By Pol Duwez, Paul Pietrokowsky

The crystal structure of the compound TisGeS has been determined from X-ray powder diffraction data. Related silicon and tin compounds have been found to be isomorphous. Unit cell dimensions, axial ratios, and parameters for equivalent atomic positions are given. THERE is, at present, only meager information pertaining to the solid state reactions of titanium with the elements in group 4B of the periodic table (silicon, germanium, tin, and lead). The only two compounds whose crystal structure has been established are TiSi² and TiGe² (references 1 and 2 respectively). These two compounds are isomor-phous and have an orthorhombic symmetry D242h— Fddd. The titanium-rich regions of the constitution diagrams of titanium-silicon, titanium-tin, and titanium-lead have been investigated by Craighead et al.³ While valuable information concerning the alpha solid solubility of these three elements in titanium was obtained, no light was shed on the existence or nature of the titanium-rich compound in these systems. The present study is concerned with the crystal structure of the intermediate phases Ti5Si ?, Ti³Ge³, and Ti5Sn³, which were found to be isostructural. The alloys were prepared by mixing the pure metal powders in the desired proportions, pressing the mixture into pellets, and melting them in an electric arc furnace in the presence of a helium atmosphere.& After melting, the specimens, weighing approximately 5 g, were sealed in evacuated quartz vials, homogenized at 1038°C for three days, and quenched from that temperature. Powder diffraction patterns were made with a 143.2 mm diam Debye-Scherrer X-ray camera in which the Ievins and Straumanis film arrangement was utilized. Filtered copper radiation was used throughout the entire investigation. A study of the powder patterns of a series of alloys of various compositions indicated the presence of a compound around a composition corresponding approximately to a ratio of 3 titanium to 2 silicon, germanium, or tin. From a visual examination of the diffraction patterns, it was evident that the silicon and germanium alloys were iso- morphous. For small angle reflections, the powder pattern of the tin compound was analogous to that of the silicon and germanium compounds, but after the first ten reflections, the similarity was no longer clear. The powder pattern of the germanium compound was selected for indexing, since it exhibited a weak small angle reflection and clearly resolved doublets in the back-reflection range. Good agreement between observed and calculated values of (1/d)² was found by indexing the pattern on the basis of hexagonal symmetry. For the hexagonal system:

Jan 1, 1952