Jan 1, 1923

By W. Chubb

By measuring the hardness of metals at temperatures just above and just below their allotropic change point, it has been established that crystal structure has a real effect upon the strength of metals. The DPH of cobalt, iron, titanium, uranium, and zirconium have been measured at temperatures up to 1000°C. It was found that the body-centered-cubic crystal structure is always the softer structure when it is involved in an allotropic transformation. The close-packed and more complex structures are inherently harder, and may be expected, therefore, to be better base materials for high strength alloys. IT has been observed that for metals with nearly the same melting point (i.e., tin and lead, magnesium and aluminum) the metal with the more complex crystal structure has a higher tensile strength and hardness. It might be asked whether this effect is really caused by the difference in crystal structure; and, if so, just what is the contribution of crystal structure to the strength of these metals. A qualitative answer to these questions can be obtained by measuring the change in hardness produced by the change in structure in metals exhibiting allotropic forms. The evidence for changes in mechanical properties during allotropic transformations is rather meager. In 1909, Rosenhain and Humfrey' observed that "ß" iron showed much less deformation at the transformation temperature than a iron. By means of a torsion test, Lee found that iron bars were "critically plastic" at the a-7 transformation temperature. Sauerwald and Knehans have shown that the dynamic hardness of iron increases between 900" and 1000°C. In 1930, Albert Sauveur' presented data on the hardness, tensile strength, and torsional strength of pui-e iron up to 1000°C. He concluded, "At 900°C, the a iron transforms into y iron, and this is accompanied by increased strength and stiffness and decreased ductility." The same year, Schischokin" obtained data on the hardness of thallium at temperatures above and below its transformation temperature. His data are replotted on semilogarithmic coordinates as Fig. 1. The fact that his data fall on straight lines in this type of plot is believed to attest to the purity of his metal and the accuracy of his results. In 1941, Nadai and Manjoine" obtained tensile data on pure iron with an indicated increase in strength at about 900°C. These experiments make it quite evident that changes in mechanical properties occur when a metal transforms from one crystal structure to another; but, except for Schischokin's data on thallium, none of the measurements seem accurate enough to determine the relative magnitude of the mechanical property change. Materials The metals that have been examined for changes in hardness during transformation include l—as- deposited commercial electrolytic cobalt about 99.7 pct pure, 2—Armco ingot iron, 3—are-melted iodide titanium of a purity in excess of 99.8 pct, 4—uranium of a purity in excess of 99.5 pct, 5—are-melted iodide zirconium of a purity in excess of 99.8 pct, 6—annealed, 0.08 pct C, rimmed steel, and 7—commercially pure RC55 titanium. While the purity of the first five of these materials leaves something to be desired, it will be noted that the observed hardness discontinuities occurred at the accepted transformation temperatures. (These temperatures are indicated by vertical arrows in Figs. 1 and 3 through 7.) The last two materials are commercial alloys introduced to show the effect of minor alloying elements upon the hot hardness curve. Apparatus Hardnesses at elevated temperatures were determined by means of a vacuum hot hardness machine. A diagram showing the basic features of this machine appears as Fig. 2. This machine is essentially a deadweight hardness .machine in a furnace within a vacuum chamber. The sapphire-tipped indentor

Jan 1, 1956

By A. R. Troiano, E. A. Steigerwald, F. W. Schaller

The kinetics of crack propagation in a hydrogenated high-strength steel at subzero temperatures indicated that cracking progressed in a discontinuous fashion. The delayed failure process thus involves a series of crack initiations rather than the continuous growth of a single crack. The incubation time required for the initiation of delayed failure was controlled by the diffusion of hydrogen. The activation energy for the process was 9120 cal per g-alom. As the test temperature was lowered the incubation time constituted a greater percentage of the total tinze to fracture, and al -50°F the incubation and fracture times were essentially coincident resulting in instantaneous, catastroplzic fracture. A unique feature of hydrogen embrittlement is the delayed failure process in which the material fails under the action of a sustained load even though it is capable of supporting a higher load for a finite period of time.')' Delayed failure of steel and titanium is characterized by an incubation time, preceding the initiation of a crack in a highly localized region, and the subsequent growth of the crack to ultimate failure.3-5 The kinetics of crack growth in hydro-genated high-strength steels have been studied through the use of resistance measurements and have an important bearing on the mechanism of delayed failure. Delayed failure is believed to be merely a facet of hydrogen embrittlement in which sufficient time is allowed during a test for hydrogen diffusion. The current theories employed to explain hydrogen em-brittlement can be grouped into two types. one6-8 explains the embrittlement on the basis of the pressure exerted by molecular hdrogen in lattice voids or defects while the other9-10 attributes the embrittlement to the influence of hydrogen in the lattice. The mechanism used to explain the nature of the crack kinetics in delayed failure is based on the stress-induced diffusion of hydrogen to the area of maximum triaxiality.3 When the hydrogen concentration in this region reaches a critical value, a crack is nucleated. This initial crack propagates instantaneously until stopped by the higher fracture stress of the adjacent material of lower hydrogen content. The continuation of cracking must then await the further diffusion of hydrogen to the new region of triaxiality near the base of the crack where another initiation will occur. From this mechanism it follows that crack propagation is nothing more or less than a series of initiations with limited fracture. The purpose of this investigation was to examine the kinetics of crack growth in an effort to determine whether or not the process was discontinuous. Studies of crack propagation were conducted at low temperatures to retard the diffusion of hydrogen which is presumed to be the rate controlling process in delayed failure. MATERIALS AND PROCEDURE Specimen Preparation—A commercial heat of air-craft quality SAE-AISI 4340 steel, designated as Heat G, was furnished by the Republic Steel Co. in the form of %-in. hot-rolled bars. The material had the following chemical analysis: Composition of 4340 Steel—G Heat C Mn Si Ni Cr Mo 0,395pct 0.82pct 0.29pct 1.76pct 0.85pct 0.25pct Notched tensile specimens with less than a 0.001 in. radius, Fig. 1, were used throughout the investigation. The specimens were heat treated to a 230,000 psi strength level according to the following sequence: a) Normalize bar stock at 1650°F for 1 hr, b) Stress relieve at 1200°F for 4 hr and furnace cool,

Jan 1, 1960

By R. W. Hyde, B. S. Old, S. E. Eaton

INTRODUCTION ONE of the most important problems facing the steel industry at the present time is that of maintaining at a minimum the sulphur content of many grades of steel where sulphur is known to have harmful effects on both quality and yield. The present outlook in this struggle to reduce the amount of sulphur in steel is rather gloomy since the sulphur content of the raw materials available in the United States is gradually rising, with little relief in sight. A flow sheet of sulphur in the steel process is shown in Fig I. The values used here were obtained by averaging coke oven and blast furnace data at No. 5 furnace in Cleveland and are considered typical for high top pressure practice. The sulphur evolved in the blast furnace top gas was obtained by difference and since the amount is relatively small, little significance should be attached to this particular value. From Fig I it is apparent, however, that coals used in the production of metallurgical coke represent by far the largest single source of sulphur in steelmaking. As an indication of the decrease in quality of these coals as regards sulphur content the weighed average annual sulphur analysis of the coals supplied to two different steel plants, since 1925, is plotted in Fig 2.1 The sharp rise since 1940 is strikingly apparent. Another indication of this trend is found in estimates of coking coal reserves. Thus in the case of Pittsburgh seam coals available in Allegheny, Fayette, Greene, Washington, and Westmoreland Counties in Pa. as of Jan. 1937 only 25 pct of the coal reserves would contain less than 1.50 pct sulphur after washing.2,3 Many of these lower sulphur reserves have been seriously depleted in recent years because of accelerated war demands. Still another demonstration of the increasing sulphur content of coals on a country-wide basis is found in a report by the Bureau of Mines4 which shows a steady increase in the sulphur content of coke made in the United States, It should be noted that this increase continues in spite of the wider use of coal washing in recent years. Sulphur occurs in coal in three forms, pyritic (FeS2), organic sulphur, and a small amount of sulphate sulphur (CaSO4), The sulphur is subsequently found in the coke in combination with carbonaceous material of unknown composition and as calcium and iron sulphides: In considering the general problem of sulphur elimination, the Republic Steel Corp. was interested in determining which, if either, of the two major forms of sulphur in coal contributes the greater portion of sulphur to the coke, Since the ratio of pyritic to organic sulphur varies widely in different coals, it was thought that if it could be shown definitely that the major part of the sulphur occurring in coke originates from one of the two major forms of sulphur in the coal, it would then be possible to select with confidence coal which, although high in total sulphur, would yield coke of fairly low sulphur content, Using the new

Jan 1, 1948

By Edwin B. Johnson

The success of self-fluxed sinter in enhancing the operation of the blast furnace during the past few years has reasonably led to the assumption that the use of self-fluxed pellets might result in even greater furnace efficiencies. A great share of development work in agglomeration has been directed towards techniques related to the production of self-fluxed pellets, but no appreciable tonnage of self-fluxed pellets had been produced on a commercial scale until this past year when The Cleveland-Cliffs Iron Co. produced 35,000 tons of such pellets by the grate kiln system at the Republic mine during the period May 21-June 5, 1962.

Jan 3, 1963

By Harry K. Ihrig

Jan 1, 1947

By Harry K. Ihrig

Jan 1, 1947

Jan 1, 1898

NORTH AMERICA ALASKA Anchorage.-Strandberg, H. Tuck, R. Coal Creek.-Moore, E. G. Spencer, W. W. College.-Hance, J. H. Henricksen, R. Henton, H. M. Comet.-Albertson, F. E. Cordova.-O'Neill, W. A. Douglas.-Cahill, W. E. Fairbanks.-Crawford, J. D. Earling, R., B. Fowler. D. A.

Jan 1, 1937

By Harry E. Cross

Kiln Products commissioned a Waelz kiln 4 metres in diameter by 75 metres long, in South West Africa in March, 1969, to recover nine in a form suitable for the production of electrolytic zinc. The raw material consists of a mixture of zinc silicate concentrates and zinc rich tailings purchased from an adjacent zinc mine - the mixture containing 20% to 25% zinc. The chemical composition of the ore is tabulated and the initial test results are described. Due to the comparatively low temperature at which the ore starts softening the kiln has certain unusual features to enable the temperature to be controlled within the necessary limits. A detailed description of the kiln, the starting-up problems and present operating conditions and results are presented.

Jan 1, 1970

By Harry C. Gatos, Frank J. Bachner

It was shown through high-pressure experiments that tin loss by volatilizatim is necessary for the degrada-tion of the superconducting transition temperature of Nb,Sn associated with high-temperature annealing. Crystallochemical analysis of the degraded Nb3Sn showed that it constitutes a new phase with ordered niobium-site vacancies, created by the migration of niobium atoms to vaccnt tin sites. This new phase was found to form when 4 pct Nb-site vacancies were present. It has a transition temperature of 6'K and a lattice parameter of 5.283A. A similar degradation effect was observed in Nb,Al. Its superconducting transition temperature dropped from 16.5" to 8" K following a high-temperature annealing. The superconducting temperature degradation in these 0-tungsten structure compounds is attributed to the disruption of the interchain d bonding by the periodic interruption of the niobium atom chains. By annealing the degraded Nb, Sn at 1000 C in nitrogen its normal superconducting behavior is restored most likely due to the incorporation of nitrogen atoms causing the elimination of the ordered vacancies. HANAK et al.' have observed low superconducting transition-temperature values (T, - 9"K) in some NbsSn samples deposited from the vapor phase. They attributed such low T, values to disorder in the 0-tung-sten structure. Much lower T values (down to 5.6"K) were reported by Reed et al.zC for NbsSn samples annealed at high temperatures. These authors also attributed this degradation effect to disorder (random occupation of the A and B sites by niobium and tin) but pointed out that such disorder could be brought about (by high-temperature treatment) only in samples containing niobium in excess of the stoichiometric composition NbsSn. Both groups reported that the normal superconductivity behavior could be rever-sibly restored by appropriate heat treatment. Courtney et al., also found that degradation in NbsSn requires excess niobium brought about by the loss of tin during the treatment. However, these investigators proposed that the degradation is due to niobium-site vacancies resulting from the migration of the niobium atoms to the vacated tin atom sites. They did not consider the reversibility of the effect. The present study attempts to establish the nature of the above degradation phenomenon. EXPERIMENTAL PROCEDURES All compounds prepared for this investigation were made from the powders or filings of the elements which were intimately mixed, cold-pressed into a cylindrical pellet at approximately 50,000 lb per sq in., and then submitted to the desired heat treatment. The samples annealed under high pressure were placed in a MgO sample container which was mounted in a pyrophyllite tetrahedron designed for a tetra-hedral-anvil press. Details of the experimental arrangement are given elsewhere. This setup allowed heating at 1800°C or above under pressures in excess of 30kbars for 3 hr. The samples annealed in a vacuum were prepared in a high-temperature vacuum furnace which could reach temperatures up to 2400°C under a pressure of 2 x lo-' Torr. For annealing in a reactive atmosphere, a quartz tube was placed in a clamshell furnace and the desired gas ambient passed through the tube. Lattice parameters were determined using a Debye-Scherer 114.6-mm camera. Cohen's method, programmed for the IBM 7094 computer, was used to calculate the lattice parameter from the measured d spacings. X-ray integrated intensity measurements were made on several samples. These samples were ground to -400 mesh and the powder mixed with a solution of collodion in amyl acetate. The mixture was poured into a depression milled in a bakelite disc. When the mixture dried, the surface of the disc was ground flat leaving a diffraction surface defined by the face of the disc. The disc was mounted in a Philips rotating specimen holder which allowed the rotation of the sample in the plane of the diffraction surface and the integrated intensity measured using a scintillation counter and a pulse-height analysis sys-tem. The superconducting transition temperatures were determined by means of self-inductance techniques.' EXPERIMENTAL RESULTS AND DISCUSSION The Role of Tin Loss in the Degradation of Super-conductivity. The loss of tin during high-temperature annealing can be effectively suppressed by annealing under high hydrostatic pressures. Accordingly, a series of experiments were performed under pressures of approximately 30kbars. This pressure was the minimum under which high-temperature experiments could be safely performed in the particular pressure apparatus employed. Experiments were also designed to test high-pressure effects on the superconductivity behavior of NbJSn. The results of the high-pressure annealing experi-ments are summarized in Table I. All samples were prepared as described earlier. They were reacted and homogenized at 1000°C for 24 hr under argon at-

Jan 1, 1967

By A. A. Bauer, M. S. Farkas, F. A. Rough

An investigation of the d-phase relationships between the uranium-zirconium and uranium-molybdenum systems was conducted. A ternary cut joining U-31.5 at. pct Mo to U-74 at. pct Zr is presented on the basis of differential thermal analysis, metallographic and X-ray diffraction data. HyDothetical isothermal ternary sections, inferred from the determined d-phase relationships, are presented for the uraniztm-zirconium-molybdenum system. A ternary eutectoid, at 454ºC, was found in zirconium-rich alloys. Its composition, based on metallography and electron-beam micro-analysis, is estimated as U-61.7 at. pct Zr-7.1 at. pct Mo. URANIUM binary systems have been studied extensively in the past to supply basic information needed in reactor-fuel development. Alloys of uranium with zirconium, molybdenum, and titanium are of particular interest because, in these binaries, extensive or complete solid solubility between the body-centered-cubic forms of these elements and y uranium exists. In addition, an intermediate phase of limited solid solubility forms in each of these systems by transformation of the high-temperature ?-uranium phase. Previous investigation of the phase relationships existing between the intermediate 6 phases in the uranium-zirconium-titanium and the uranium-molyb- denum-titanium ternaries have already been reported.1,2 The results of an investigation of the phase relationships existing between the 6 phases in the uranium-zirconium-molybdenum system is reported here. The phase equilibria that occur in the solid-state portions of the pertinent binary systems are shown in Fig. 1. Phase nomenclature appearing throughout the report is as shown in these diagrams. The crystal structure of the phases in this system are given in Table I. EXPERIMENTAL PROCEDURES Alloys were cast and fabricated to 1/4-in.-diam rod. Specimens were heat treated and examined by metallographic and X-ray techniques. Thermal-analysis data were obtained.

Jan 1, 1960

By G.A. Moore, C. E. Sims

In previous publications of the writers4-7 it has been shown that vacuum extraction of steel can be carried as close to quantitative completion as desired provided the steel is in the austenitic state and sufficiellt time is allowed. For precise work, the method claims preference because the equipmelit for holding and heating the sample can be made simple, and because crucibles, boats, and other unnecessary materials can be eliminated and the blanks thus made very small. It is well known that the evolution rate of hydrogen is smaller just above the trans. formation than immediately below, as would be expected from the increase in solubility when passing into the gamma state. Many attempts have been made to obtain analyses by extraction just below the transition, using times of approxi. mately 2 hr. while it is true that the rate of evolution drops nearly to zero under these conditions, it has repeatedly been shown that the process is incomplete since on raising the temperature into the austenitic range, evolution will be resumed, usually after a, considerable induction period. The low-temperature evolution process appears to be useful in some cases for comparative tests where the residual crror may be more or less constant between samples, For general use, however, there is no guarantee that the error caused by incomplete extraction is constant; hence, the more laborious but more reliable high-temPe'atu'e Process must be used. At high temperature, an original flash evolution, similar to that at lower temperature, is first observed. After not more than an hour, the flash subsides and cvolution settles down to a regular first-order reaction rate for which the half-life* is usually of the order of a few hours for the 5/8-in. diam cylinder at 1050°C. The regular evolution may be followed for whatever period appears justified, after which the residual gas may be estimated as equal to that which was evolved in the last observed half-life period. Tests have shown that the composition of the evolved gas does not vary greatly during the progress of evolution; therefore the residual gas may safely be taken to have the same composition as the portion col-

Jan 1, 1949

By C. E. Sims, G. A. Moore

In previous publications of the writers4-7 it has been shown that vacuum extraction of steel can be carried as close to quantitative completion as desired provided the steel is in the austenitic state and sufficiellt time is allowed. For precise work, the method claims preference because the equipmelit for holding and heating the sample can be made simple, and because crucibles, boats, and other unnecessary materials can be eliminated and the blanks thus made very small. It is well known that the evolution rate of hydrogen is smaller just above the trans. formation than immediately below, as would be expected from the increase in solubility when passing into the gamma state. Many attempts have been made to obtain analyses by extraction just below the transition, using times of approxi. mately 2 hr. while it is true that the rate of evolution drops nearly to zero under these conditions, it has repeatedly been shown that the process is incomplete since on raising the temperature into the austenitic range, evolution will be resumed, usually after a, considerable induction period. The low-temperature evolution process appears to be useful in some cases for comparative tests where the residual crror may be more or less constant between samples, For general use, however, there is no guarantee that the error caused by incomplete extraction is constant; hence, the more laborious but more reliable high-temPe'atu'e Process must be used. At high temperature, an original flash evolution, similar to that at lower temperature, is first observed. After not more than an hour, the flash subsides and cvolution settles down to a regular first-order reaction rate for which the half-life* is usually of the order of a few hours for the 5/8-in. diam cylinder at 1050°C. The regular evolution may be followed for whatever period appears justified, after which the residual gas may be estimated as equal to that which was evolved in the last observed half-life period. Tests have shown that the composition of the evolved gas does not vary greatly during the progress of evolution; therefore the residual gas may safely be taken to have the same composition as the portion col-

Jan 1, 1949

ALABAMA Alabama City.-Eddy, L. Altoona.-Cain, J. America.-Foreman, J. T. Anniston.-Foster, R. N. Ashland.-Sturdevant, J. C. Bessemer.-Ball, E. M. Calhoun, F. W. Maschmeyer, W. L. McKenzle, W. C., Jr. Birmingham.-Abbott, C. E. Aldrich, T. H. Aldrich, T. H, Jr. Ashton, J J.

Jan 1, 1923

By O. D. A. Pease, C. D. Young, C. H. Strand

In an effort to employ cast steel of a stronger structure than that found in the annealed steel casting, the possibilities of heat treatment which will increase the strength without materially decreasing the ductulity may be resorted to.

Jan 1, 1915

By Harrison R. Cooper

The key to concentrator automation is practical means for obtaining continuous assay data from concentrator streams. The technique most successfully used is x-ray fluorescence analysis. The practical reality of on-stream x-ray analysis has been achieved through effort over the past twenty years, marked by an occasional breakthrough, but more typically a step-by-step development to which many individuals and organizations have contributed. The net result of this progress is the present capability to install on-stream x-ray analyzer systems on a turn-key basis. It is now possible to provide all components of an x-ray analysis system as a completely engineered unit which can be put into immediate use, minimizing needs for specialized application knowledge to benefit from continuous assaying in process control. The economic factors which influence the choice of system and limitations of the x-ray fluorescence technique for slurry analysis are reviewed.

Jan 1, 1976

ALABAMA Anniston.-Carrington, F. G. Auburn.-Brown, R. L. Bessemer.-Abbott, C. E. Dobbs, G. G. Ferguson, V. Salmon, H. S. Schaber, C. F. Birmingham.-Aldrich, T. H. Aldrich, T. H., Jr. Allen, A. W, Ball, E. M. Bonnyman, J. Bowron, J. Bush, M. W. Crawford G. G. Crockard, F. H. Ellis, E. E. Fairbairn, C. T. Gallacher, J. Geisiner, H. S.

Jan 1, 1917

By E. H. Dix

All commercial aluminum contains small percentages of copper, iron, and silicon as unavoidable impurities. The purest metal obtainable commercially, special grade high purity ingot, contains a maximum of 0.50 per cent. impurities of which the usual minimum amount of copper is 0.01 per cent.; silicon, 0.12 per cent.; and iron, 0.20 per cent. This grade is too costly for most purposes. The two standard grades, Nos. 1 and 2, containing a minimum of 99.0 and 98.0 per cent. aluminum, respectively, are more generally used. Other grades of secondary aluminum often contain as high as 3 or 4 per cent. of impurities, which include 1 per cent., or more, of zinc. Specifications for high-grade aluminum-casting alloys generally allow a maximum of 1.7 per cent. for total impurities. The S. A. E. Specification No. 33, which is intended to cover alloys made from secondary aluminum ingot, gives the iron maximum as 1.5 per cent. and the maximum for silicon (including manganese and tin) as 0.75 per cent. The effect of even relatively small amounts of impurities on the physical properties of ingot aluminum is shown by the following cornparison of two lots of aluminum, which may be taken as representative of special grade and grade No. 2 ingot, respectively. AnalysEs Special Grade, Gbade No. 2, Per Cent. PeR CBnt. Copper................................. 0.01 0.32 Silicon................................. 0.12 0.32 Iron................................... 0.42 0.82 Aluminum.............................. 99.45 98.54

Jan 1, 1923

By E. H. Dix

All commercial aluminum contains small percentages of copper, iron, and silicon as unavoidable impurities. The purest metal obtainable commercially, special grade high purity ingot, contains a maximum of 0.50 per cent. impurities of which the usual minimum amount of copper is 0.01 per cent.; silicon, 0.12 per cent.; and iron, 0.20 per cent. This grade is too costly for most purposes. The two standard grades, Nos. 1 and 2, containing a minimum of 99.0 and 98.0 per cent. aluminum, respectively, are more generally used. Other grades of secondary aluminum often contain as high as 3 or 4 per cent. of impurities, which include 1 per cent., or more, of zinc. Specifications for high-grade aluminum-casting alloys generally allow a maximum of 1.7 per cent. for total impurities. The S. A. E. Specification No. 33, which is intended to cover alloys made from secondary aluminum ingot, gives the iron maximum as 1.5 per cent. and the maximum for silicon (including manganese and tin) as 0.75 per cent. The effect of even relatively small amounts of impurities on the physical properties of ingot aluminum is shown by the following cornparison of two lots of aluminum, which may be taken as representative of special grade and grade No. 2 ingot, respectively. AnalysEs Special Grade, Gbade No. 2, Per Cent. PeR CBnt. Copper................................. 0.01 0.32 Silicon................................. 0.12 0.32 Iron................................... 0.42 0.82 Aluminum.............................. 99.45 98.54

Jan 1, 1923