By Chao Li, Lim Hongxu, Yuyue Wang, Xie Yang

"A intergrated process of sulfuric acid leaching, sodium chloride leaching, lead chloride crystallization, lead hydroxide synthesis and roasting was carried out for the recovery of lead, cadmium, copper and zinc from lead smelting dust containing various metals. The results showed that the separation of cadmium, zinc and copper from dust could be obtained after sulfuric acid leaching and corresponding leaching rate were 92.12%, 90.25% and 88.26% respectively. The subsequent sodium chloride leaching carried out for lead with optimized parameters as: sodium chloride concentration 250g/L, leaching temperature 90°C, leaching time 2h, pulp density 33g/L, 0.12mol/L CaCh; The lead compounds crystallization rate reached 86.67%, and then transferred into mPbO·nH2O, the product of 98.66% ß-PbO could be obtained through roasting under 502°C. In the end, a feasible method of ß-PbO preparation from lead containing dust was put forward.IntroductionThe pyro-metallurgy flue dust from smelting lead activities are often stockpiled and pose potential environmental risks due to the heavy toxic elements, such as Pb, Cd, As, Cu, Cl, and Zn which are contained in the dust. With the rapid depletion of rich ore resources in recent years, it has become increasingly more financially attractive to recover valuable metals from previously stockpiled dust, while simultaneously reducing the potential of environmental pollution from toxic elements contained in the dust. Nowadays, pyro-metallurgical and hydrometallurgical routes or both combined methods can be developed to treat secondary materials such as lead ash, leach residues etc. By comparison the hydrometallurgical processes are often considered more eco-friendly.Some chloride leaching processes for recovering lead have been employed using either NaCl, or MgC2 and CaCl2, or FeCl3 [1] The effectiveness of the brine leaching method is based on the formation of complex metal chlorides in concentrated chloride solutions [2] Similarly, Other metals such as zinc, cadmium and copper contained in the flue dust are often treated with sulfuric acid, hydrochloric acid, ammonium solution and sodium hydroxide etc. as lixiviants [3] The metals from leach solutions thus has been obtained by precipitation, ion exchange, solvent extraction or replacement [4]"

Jan 1, 2014

By Florian Aurelian, Mihai Popescu

"It will be tested four types of “geochemical barriers”. All those mixtures were contacted with mine waters containing uranium, radium and heavy metals. The loading capacity was determined. The optimum mixture was determined and its efficiency was tested within an uranium areal, where the activity was stopped. It was determined the possibility to recover the radioactive elements and the heavy metals from the investigated barriers.IntroductionThe paper presents the results concerning the performances of some “geochemical barriers” used for the decontamination of mine waters from uranium mining sites, which were tested in lab and in situ.ExperimentalThe research activity was carried out in lab and on the site.In the lab a module was constructed in order to follow up the uptake capacity of the “permeable reactive geochemical barriers” used to remove the radiolelements from the contaminated waters originated from the uranium mining industry. The barriers, which were used, are made of cheap natural materials, which can be easily got (wood chips, peat coal, sawdust, iron span, steel and zeolitic tuff). The following types of barriers were tested:•, 1st barrier: peat coal, sawdust, zeolite on weight ratio of 1/1/1;•, 2nd barrier: bentonite, sand, wood chips, peat coal on weight ratio of 1/1/1/1;•, 3rd barrier: iron span, steel, sawdust, peat coal on weight ratio of 2/1/1;•, 4th barrier: iron span, steel, sand, firry wood chips on weight ratio of 1/1/1.Lab researches concerning the uranium uptake capacity of the above described “reactive barriers” pointed out that the 3rd mixture (iron span, steel, sawdust, peat coal on a ratio of 2/1/1) didn’t reach the maximum uranium uptake capacity not even after eleven contact stages (the uptake capacity being of 70.6 mg U/ kg of mixture) and the mixture of peat coal, sawdust and zeolite has an uranium uptake capacity of 26.6 mg U/kg of mixture and becomes saturated after four contact stages.Each one of the components involved in physical-chemical processes of sorption, reduction and precipitation, will determine the diminution of uranium and other metals contents upstream the permeable reactive barrier."

Jan 1, 2008

The 15m high Inco flash furnace uptake was designed as a reaction chamber with the objective of destroying the H2S contained in the furnace off-gas by combustion with oxygen at about 1300°C. Until recently, the oxygen required for this purpose was injected through afterburners located at the bottom of the uptake. An undesirable side effect of this practice was the formation of build up accretions on the inside walls of the uptake. This buildup had a negative impact on both the furnace on line time and the control of the flash smelting process. In late 200 I, the afterburners were relocated to the roof of the uptake. As a result, about 80% of the uptake accretion buildup disappeared with obvious beneficial effects for the operation of the furnace. This paper discusses key flash smelting aspects that affect the operation of the flash furnace uptake such as the dusting rate, the formation of H2S in the freeboard of the furnace, and the impact of using coke to supply some of the heat required by the process. The mechanism of buildup formation and its dependence 'on uptake afterburners location are also examined. Prof. Yazawa's sulfide smelting thermodynamic relationships proved instrumental in understanding the conditions that influence the formation and the elimination of H2S and uptake buildup.

Jan 1, 2003

By P. C. Chaubal

The overall kinetics of oxidation of single partic1es of chalcopyrite have been studied for temperatures up to 1273 K. The experiments were conducted in a stationary bed reactor using a non-isothermal technique. Any mass and heat transfer effects on the kinetics of oxidation were eliminated by using a high-enough gas flowrate. Up to temperatures of 873 K, pore-bl1ocking kinetics were applicable, whereas above 873 K, power-law kinetics gave a satisfactory fit of the data. The activation energy was 215 kJ/mol below 754 Kand 23.7 kJ/mol above 1,060 K. Predominance area diagrams were constructed at various temperatures and used in conjunction with X-ray analyses of partially oxidized samples to determine the intermediate phases formed during the reaction. The analysi1s also provides a justification for the kinetic models used. The results indicate that the reaction rate is first order with respect to oxygen concentration and inversely proportional to the square of the particle size throughout the ranges of temperature studied.

Jan 1, 1985

By Animesh Jha, Catherine Davey

"Carbothermic reduction and nitridation reactions using synthetic kaolinite mineral were investigated for the formation of silicon based nitrogen ceramics. The temperature dependence of the reaction rate and its effect on phases formed are reported. The effect of the reactivity of carbon on the kinetics of formation of AIN and ShN4 is discussed. Using the standard Gibbs free energy values for the formation of nitrides and oxides of aluminium and silicon, a log po2 verses I/T diagram is constructed. The experimental data results are discussed and compared with the predicted phase equilibria. We also report the influence of sub-oxide gaseous species on the microstructure of the ceramic phases produced.IntroductionSynthetic kaolinite is a clay containing alumina, silica and water of crystallisation, and has a chemical formula 3(Al2O 3.2SiO2.2H2O). This mineral is relatively inexpensive and, is therefore an ideal candidate for use in the production of ceramic powder mixtures for example silicon nitride and aluminium nitride for composite material formation, When the mineral is heated, the water of crystallisation from the crystal lattice is lost via the 3(Al2O 3.2SiO2.2H2O) = 3(Al2O3.2SiO2) + 6H2O reaction. It has been shown [1·2j that on further heating to 1673K, the anhydrous kaolinite decomposes to a mixture of mulllte and silica, 3(Al2O3.2SiO2) = 3Al2O 3.2SiO2 + 4SiO2 which is consistent with the alumina-silica phase diagram, shown in figure 1.The binary alumina-silica phase diagram has a well-defined sub-eutectic immiscibility dome and this characteristic dernixing behaviour is reflected in the thermal decomposition of anhydrous kaolinite consequently the microstructural features resemble the spinodal decomposition process. It is well established that the spinodal decomposition process raises the nucleation frequency due to their low free energy barrier, (?G). The small magnitude of this barrier consequently promotes the evolution of a very fine microstructure. The process of spinodal decomposition is therefore expected to be influential during the reduction-nitridation of kaolinite minerals."

Jan 1, 1996

By Hong Liang-shi

Olivine lithium iron phosphate (LiFePO4) is considered as one of the most promising materials for lithium-ion secondary batteries because of its high theoretical capacity, low cost, good safety, benign environment and good cycle performance. In this paper, carbon-free and/or carbon-coated olivine lithium iron phosphate composite ultrafine powders were successfully synthesized from aqueous precursor solutions of (NH4)2Fe(SO4)2?6H2O, H3PO4 and LiOH?H2O by co-precipitation method. The obtained LiFePO4 or LiFePO4/C powders were characterized by X-ray diffraction (XRD) and scanning electron microscope (SEM). Their electrochemical performance was investigated in terms of cycling behavior. As confirmed by X-ray diffraction and scanning electron microscope, the material obtained by co-precipitation within the temperature range of 60ºC to 100ºC and then followed by moderate heat treatment are a single-phase olivine LiFePO4with the particle size of about 300nm. An improved carbon-coated olivine LiFePO4/C material was prepared by adding conductive carbon materials, such as glucose, activated carbon and acetylene black, into the precursor. The carbon dispersed in the materials increases the electronic conductivity of LiFePO4/C composite, and consequently, leads to high rechargeable capacity of the material. The carbon-coated material with carbon amount of 7.64%wt obtained from glucose has the first discharge capacity of 150.3mAh/g at the rate of 0.1C and 129.3mAh/g at the rate of 1.0C, respectively. After cycled for 50 times, the capacity retention rate is 95.13% at the rate of 1.0C in the voltage range of 2.5 to 4.3 V vs. Li/Li+.

Jan 1, 2006

By Bowen Li

Copper vermiculite is a special nanomaterial with excellent antibacterial and antifungal performance. By means of ion exchange, copper vermiculite containing up to 5.8wt% copper was prepared. The chemical and mineralogical characterization of the material was investigated in this study based on the XRD, AAS, TEM and EDS analysis, as well as the calculation of crystalline parameters and crystal chemical formula. Cu2+ and Mg2+ have similar atom radius and same electrovalence. Correspondingly, the structure character of copper vermiculite is very close to that of standard Mg-vermiculite. Most of the CU21 may have occupied the interlayer cationic positions in the form of hydrate in vermiculite. However, some may have entered into octahedral coordinate positions. The values of au and bo of the copper vermiculite crystal cell have no obvious change compared to that of original vermiculite micropowder, but the Co value decreased slightly, which is desirable for the stabilization of the Cu2+ in copper vermiculite.

Jan 1, 2003

By Cesimiro Fabian

The crystallite size of copper electrodeposits was determined by X-Ray powder diffraction analysis using a General Area Detector Diffraction Solution (GADDS) diffractometer. Crystallite size was calculated for copper thin films which were deposited on a 316 stainless steel rotating cylinder electrode (RCE) in the presence and absence of additive ?A?. The crystallite size was calculated from a corrected full width at half maximum (FWHM) of the [110] peak profile using the Scherrer equation. The test of significant difference on crystallite size was derived using Kruskal-Wallis method. It was found that in the absence of the additive the median crystallite size was 426, which decreased to 364 in the presence of the additive. As the additive degraded, the crystallite size increased to a size similar to that observed in the absence of additive.

Jan 1, 2003

By I. Mc Dougall

"The matte/slag tidal zone in a platinum smelting furnace is subject to severe process conditions which can often lead to premature failure of the lining. The MgO-FeO-Si02 slag is aggressive to refractory bricks, whilst the Ni-Cu-Fe-S matte is aggressive to water-cooled copper cooling elements, and can penetrate and sulphidize refractory bricks, particularly at the high matte temperatures often experienced in the PGM industry. A novel approach to the lining design was taken at Lonmin's new 10MW Furnace 2. An indirectly-cooled graphite ring was applied in the matte/slag tidal zone, with refractory bricks on the hot face. Thermal Finite Element modeling was conducted to determine the optimal lining design in this region of the furnace. The resistance of two graphite grades to damage by slag and matte was evaluated experimentally. The graphite lining is not wet by the matte, and is resistant to slag attack at operating temperatures. In comparison to water-cooled copper in various configurations, cooled graphite shows promise as an indirect refractory cooling system in the tidal zone area of furnaces.IntroductionIn South African Platinum Group Metals (PGM) smelting operations, the PGMs are associated with nickel-copper sulphides in magmatic rocks. After ore is mined, it is concentrated by means of a flotation process prior to smelting. Both rectangular 6-in-line and circular 3 electrode AC submerged arc furnaces are used for this purpose. A new 10 MW round furnace is currently under construction by Tenova Pyromet at Lonmin's Marikana Smelter Division. An overview of Lonmin's smelting operations and Lonmin's approach to smelting high chromite containing PGM concentrates is given by Eksteen et al. [1]"

Jan 1, 2012

By Onuralp Yücel, Mehmet Bugdayc, Murat Alkan

"In this study, iron based alloys (Fe-Mo, Fe-Cr-Ni, etc.) were produced by using aluminothermic methods starting from Mill Scales obtained continuous casting processes. Mill scales are an oxidised layer of steel alloys containing iron oxide, which includes + 2, + 3 values, on the surface of slabs and billets occurring during annealing in heating furnace at integrated iron and steel milling plant, and continuous casting unit. In the metallothermic experiments, different ratios of starting mixtures and addition of the oxide powders (Alz03, Si02, CaO, MgO) were examined, and their effects on the metal recovery and alloy compositions were carried out. The samples were characterized by using chemical analysis (AAS), XRD, XRF and SEM/EDS techniques.IntroductionSelf Propagating High Temperature Synthesis process (SHS) has many favour compared to the furnace applications, such as low energy requirement, low cost, very short processing time and simple operation, [l, 2]. In a SHS process, the ignition starts the combustion and propagates throughout the reactant mixture yielding the desired product. However, the disadvantages of the process such as inhomogeneous or unreacted products due to undesirable reaction rates needs to be overcome by changing some parameters such as ignition temperature, particle size, additive, atmosphere etc. [3, 4]. Mill scale is a layer of iron oxide which forms on ferrous materials cooling after being processed in hot rolling or continuous casting plants. Mill scale contains iron (II) and iron (III) oxides, which result in a 70% total iron content in oxide form. Not being able to reuse this material will prevent the raw material entering the production plant from being fully utilized [5]. This study aimed to produce Fe-based alloys via SHS (Self Propagating High Temperature Synthesis) metallurgy which is attractive process technique regarding fast and low-cost production ability of cast alloys by using high metallic iron content by reducing continuous casting mill scale."

Jan 1, 2013

By Joo Hyun Park, Soo Sang Park

The distribution behavior of Pb between molten copper and FetO-SiO2 (-CaO, Al2O3) slags was investigated at 1473 K (1200 oC) and p(O2)=10-10 atm in view of the reaction mechanism of Pb dissolution into the slag. The distribution ratio of Pb (LPb) decreases with increasing CaO content (~6 mass pct) irrespective of Fe/SiO2 ratio (1.4~1.7). However, the addition of alumina into a slag with Fe/SiO2=1.5 linearly decreases the LPb, whereas a minimum value is observed at about 4 mass pct Al2O3 at Fe/SiO2=1.3. The log LPb continuously decreases with increasing Fe/SiO2 ratio, and the addition of Al2O3 (5 to 15 mass pct) into the silica-saturated iron silicate slag (Fe/SiO2 < 1.0) yields the highest Pb distribution ratio. The log LPb linearly decreases by increasing the log (Fe3+/Fe2+) value. The Pb distribution ratio increases and the excess free energy of PbO decreases with increasing Cu2O content in the slag. However, from the viewpoint of copper loss into the slag, the silica-saturated system containing small amounts of alumina is strongly recommended to stabilize PbO in the slag phase at a low Cu2O content.

Jan 1, 2014

By Fabio J. Esper, Guillermo R. Martín-Cortés, Francisco R. Valenzuela-Díaz, Cassio P. Carvalho, Giorgio Grotti, Reginaldo B. Santos

"Rejected sands from smelting metallurgical process because contain lead and others heavy metals are a problem to dispose as waste in all the countries. A procedure that is being proposed for it is to incorporate it on common clay bodies in the fabrication of structural ceramic products as bricks, blocks and roof tiles. The main goal of this paper is to present the results obtained with mixtures of sands from smelting metallurgical process with common clay from Jundiaí, São Paulo, Brazil. Preliminary incorporation tests (1,0% in weight) were made with hand formed spherical samples. With the higher compression strength of the spheres after drying and firing (950ºC) experiments on bricks production were made for quality technological test. Seven hundred hallow blocks containing 1,0% waste were produced and presented ceramic properties similar to those without sand incorporation. Introduction In last the fifteen years the LMPSol - Raw Materials & Non-metallic Solids Laboratory – Metallurgic Eng. & Materials Depto. – Polytechnic School - University of São Paulo comes studying the possibilities of incorporate industrials waste materials to the production of bricks and other products of construction aiming at to remove pollution products of the environments and to user the properties of the same ones in the structural ceramics products. Examples are the study of the influence of rejected steel furnace dusts in structural ceramic [1], another example is the main subject of the present paper: use of rejected sand from smelting metallurgical process in the production of bricks an other products of structural ceramics. Antecedents More or less one year ago, specialist and members from the direction board of METALÚRGICA GROFE LTD. Company contacted researchers and professors of the LMPSol – PMT – EPUSP seeking for a solution to their concern with the disposal of rejected sand from smelting metallurgical process."

Jan 1, 2008

By Hiroyuki Sano, Chikabumi Yamauchi, Mitsuru Tanahashi, Toshiharu Fujisawa, Shin-ya Iwahori

"Pyrometallurgical process using Cu2O-based slag was proposed as a recycling process for copper scrap. However, it is difficult to remove nickel from copper by oxidative refining. Therefore, it is necessary to reduce the concentration of nickel in copper before the oxidative refining. In the present work, the copper enrichment stage in this recycling process, where copper scrap melt is separated into the Fe-C-Cu melt and the molten copper, was taken up and the compositions of both melts were measured. Based on the above results, the distribution ratios of nickel between the Fe-C-Cu melt and the molten copper were calculated. Furthermore, the optimum condition of copper enrichment stage was discussed from the viewpoint of nickel removal and copper recovery. The possibility of recovering 4N-purity copper by using this recycling process was confirmed.IntroductionRecycling is well known as a method for saving resources and reducing environmental damage. More than 99% of copper is used in metallic form - as metal or copper alloys[l]. High-grade copper scrap is directly re-melted and reused, while low-grade copper scrap is transported to copper smelters to be pyrorefined and electrorefined. Nevertheless, a great amount of copper is being stockpiled in the cities and should be recycled in the near future. At that time, the current recycling process will face new problems due to the increases in the recycling rate to the smelters. This includes insufficient combustion heat to melt copper scrap and ·almost no benefit in electrorefining because the scrap does not contain gold and silver. Thus, an alternative pyrometallurgical method for copper scrap refining will be required."

Jan 1, 2000

By Anette Mueller, Thomas Schnellert, Sérgio C. Angulo

"The use of automatically sorting technique, to separate gypsum components from recycled material of processed construction and demolition waste (C&DW), is motivated by environmental and economical aspects. Only if the gypsum can be separated the aggregates can fulfill the environmental requirements and also the structural characteristics according to the standards. Furthermore, the separation of red brick can also improve the quality of the aggregates.This paper aims at analyzing the separation of gypsum components and red brick by using the color sorting technique. The impacts on the composition and the envelope density of recycled aggregates are described. Depending on the gypsum content the application of two processing stages (rougher-cleaner) can be necessary to produce aggregates with sufficiently low gypsum content. Additionally, the separation of red brick and concrete is successful. So, the color sorting may be a promising technique to upgrade the quality of mixed C&DW aggregates.IntroductionConstruction and demolition waste (C&DW) is a mixture of different materials. Such mixtures can be used only in low grade applications. If the material is used as certified material for road construction or as aggregate in concrete the concrete particles must be separated from the other building materials. This paper aims at analyzing the separation of gypsum components and red brick by optical sorting. The needed stages of sorting for getting a product quality according to the German Standards are deduced.Gypsum is a building material that is increasingly used for interior works in Germany like it is shown in figure 1 [1]. At present the content of gypsum in C&DW is estimated at about 1 %. Assessments on the basis of material streams of gypsum and concrete and their life spans show that higher gypsum contents of about 3 % must be expected in future [2]. Also in other countries the use of gypsum has grown considerably in the last decades. From the characterization of C&DW available in some cities in Brazil, 4 to 15 % of total amount of C&DW that may arrive at the recycling plant to be processed is excessively contaminated by gypsum. In one of these cities, the average content of gypsum in the C&DW before processing was as high as 2.1 % [3]."

Jan 1, 2008

By Daniel Adolfsson, Ryan Robinson, Fenwei Su, Jelena Blagojevic

"Cold bonded briquetting of steel plant by-products has proven to be a viable recycling alternative concerning technology, economy and environment in both the traditional blast furnace route and the direct reduction process. A critical parameter in cold bonded briquettes is the type and amount of binder used during production. The binder material must meet certain quality requirements concerning low and high temperature strength, chemistry and economy. Currently, SSAB Tunnplåt uses ordinary Portland cement (OPC) as binder in their cold bonded briquettes. In order to improve binder quality and possibly decrease OPC dependency, a binder feasibility study has been conducted concerning an internal by-product, ladle slag, as a supplement and/or partial substitute for OPC. Several characterization techniques have been used to study the behaviour of ladle slag, these include: XRD, XRF, SEM, glass content analysis, calorimetric analysis, particle size distribution and thermochemical stability considerations concerning the CaO-Al2O3-SiO2 system.IntroductionRecently, a project was initiated at SSAB Tunnplåt AB, in Sweden, which aimed at reducing the amount of ordinary Portland cement (OPC) as hydraulic binder in cold bonded briquettes by partly replacing it with ladle slag. OPC is traditionally used within civil engineering, and widely accepted as a hydraulic binder in a number of different applications. OPC consists of four major crystalline phases, i.e. C3S, C2S, C3A and C4AF. Tricalcium aluminate as well as the ferrite phase in OPC reacts very quickly with water, for this reason gypsum is added to the clinker in order to retard these reactions. The fact that gypsum is present in the system limits the recycling of briquettes to the BOF, since the presence of gypsum during steelmaking results in a significant amount of sulphur emissions. The latter along with the expense that follows, makes it worthwhile to consider alternatives for OPC as binder in cold bonded briquettes."

Jan 1, 2008

"Injection technology has been an important subject from the early days of ladle metallurgy until the present. During the last decade, there have not been many publications in the area of injection technology. It is the author's opinion that with the challenge to find new solutions especially to environmental and energy related problems as well as better understanding of phenomenas from computer modelling, a new era of inventive injection technology developments is at hand. This is illustrated in the article with examples from six different areas where MEFOS is or have recently carried out R&D work related to issues from the injection technology field. IntroductionThe boom in injection technologies came with the introduction of ladle metallurgy treatment during the '70s and '80s. Since then, the theories and principles have been thoroughly laid down by a number of scientists and also published at several early SCANINJECT conferences.Not many new technologies/applications have been presented during the last ten years. This might lead one to believe that everything is known and done. Those, like MEFOS, who are challenged to find technological solutions to a number of environmental problems and energy saving issues in the pyrometallurgical field are, however, continuously faced with the task of developing new injection technologies.Especially, the call for sustainable technologies to solve environmental problems is a challenge for metallurgists all over the world and it will surely induce a revival of injection technologies. So, in order to encourage all injection experts, let us share some new experiences and let us encourage each other's creativity to solve some of the demands of the future society.The following show some examples of technologies under development, or recently tested."

Jan 1, 1996

By Sang Han Son

The vapor pressures of FeCI2 and ZnC12 in the FeCl2-ZnCl2 system were measured by the transpiration method at 873K and 917K. The vapor pressure data were interpreted to indicate the formation of complex ions in the FeCl2-ZnCl2 melts. It is presumed that the complex molecule FeZnCl4 as well as FeCI2 and ZnCI2 exists in the vapors in equilibrium with molten FeCl2-ZnCl2 mixtures. The activities in the FeCl2-ZnCI2 system are shown a negative deviation from Raoult&apos;s law. These results suggest the formation of complex ions such as ZnCl42- in molten FeCI2-ZnCI2 mixtures.

Jan 1, 2003

By Sang Han Son

The vapor pressures of FeCL2 and ZnCL2 in the FeCL2?ZnCL2 system were measured by the transpiration method at 873K and 9I7K, The vapor pressure data were interpreted to indicate the formation of complex ions in the FeCL2?ZnCL2 melts, It is presumed that the complex molecule FeZnCl4 as well as FeCL2 and ZnCL2 exists in the vapors in equilibrium with molten FeCL2-ZnCL2 mixtures, The activities in the FeCL2-ZnCL2 system are shown a negative deviation from Raoult&apos;s law. These results suggest the formation of complex ions such as ZnCL14 in molten FeCI2?ZnCL2 mixtures.

Jan 1, 2003

By Zhang Hengzhong

Based on thermodynamics of surfaces and a proposed two-dimensional state equation for surfaces, the relationship between the surface tension (Y) of a solution and the activity (a1) of its component (i) was derived: (1/Y)r2-.¬E (ai/Yl) The derived equation was verified with reported experimental data of water-alcohol systems and water-acetone system, the calculated results showed astonishing coincidence with experimental. Applications of the equation to the five matte systems Cu2S-FeS, Ni3S2-FeS, FeS-PbS, Cu2S-PbS and FeS-Cu22S-PbS also demonstrated that at given matte compositions the calculated surface tensions agreed with experimental fairy well.

Jan 1, 1993

By G. A. Brooks

Increasing interfacial area through gas injection is one of the main methods for accelerating reaction between slag, metals, and gases in modern pyrometallurgical reactors. In slag-metal reactors, the generation of a large number of metal droplets into the slag phase through high gas velocity has a much larger effect on the overall kinetics compared to the enhanced mass transfer through mixing. Top blowing technology generates large interfacial areas (>300 m2/tonne) through high impingement gas velocity at short distances between the exit of the injection lance and the metal-slag interface. Phase separation may become a limit at the case of very high interfacial areas, though there is still only limited understanding of the trajectories of metal droplets in slag-metal-gas emulsions.

Jan 1, 2003