By E. O. Ávila-Davila, F. R. Barrientos-Hernández, I. A. Lira -Hernández, Miguel Pérez-Labra, M. Reyes-Pérez, J. Antonio Romero-Serrano

Slag from smelting reduction processes were characterized by chemical analysis, XRD, SEM-EDS and XRF. The results revealed Ag concentrations of 362 g/t of slag, the slag mineralogical characterization by XRD and SEM-EDS showed mineralogical species oxidized complex containing Pb, Zn, Ca, Si, Fe, As, S in its structure, silver was found in globules associated lead in the slag and the furutobeite specie. The leaching study was conducted to evaluate process variables such as NaCN concentration: from 7.8x10-3M - 1.26x10-1M, temperature: 25-50°C, particle size: +140 mesh to -400 mesh, stirring speed of 750 rpm - 900 rpm. All studies were performed with a NaOH concentration of 0.2 M. The optimal values of silver recovery encountered in conditions of 7.8x10-3M NaCN, agitation rate of 750 rpm, temperature of 35°C and with a treatment time of 240 min. We also observed that a particle size -400 mesh will have optimum recoveries compared to +140 mesh, +200, +270 and +325.

Jan 1, 2015

By Xiancong Zhao, Hao Bai, Qi Shi, Zhancheng Guo

Reducing electricity cost is important for energy intensive industries such as the iron and steel industry. With the implementation of time-of-use (TOU) electricity price, plenty of attention has been paid to the optimal management of byproduct gases. The time-of-use (TOU) electricity price is the practice of implementing different prices for different times of use. It is possible to reduce electricity cost by adjusting the amount of product gases stored or used for power generation throughout the day. In this paper, a novel mixed integer linear programming (MILP) model concerning the TOU electricity price is proposed to optimize byproduct gas use. Compared with previous models, this model considers the optimal load shift between gasholders and boilers under TOU electricity price. The case study of a steel plant demonstrates that the electricity purchase cost can be reduced by more than 30% after optimization.

Jan 1, 2016

By James W. Reeves

DuPont was the titanium metal pioneer who put the greatest effort into both R&D and commercial sponge and powder metallurgy production. This was concentrated in the period 1945 through 1963. The commercial results were development of the chloride process for TiCl4 using ilmenite, development and improvement of the Kroll process, development of a modified Hunter process to make titanium powder and commercial development of a direct powder process. The powder metallurgical process failed because of the inability to meet powder chloride specifications. All this work remained a trade secret until published in NMAB -392 by Mahla in 1983. There were other processes explored by DuPont, both improved sponge and powder processes. Much of this work has been continued by others but none, as of yet, resulting in new improved titanium metal capacity.

Jan 1, 2001

By Seiji Yokoyama

As a series of fundamental study on the gas evaporation method, a levitation-melted aluminum was evaporated in the gas mixture of argon and ammonia to synthesize ultrafine particles of aluminum nitride. When the ammonia partial pressure were more than 2kPa, the formation ratio of aluminum nitride was about 95%. The particles of aluminum nitride were mainly hexagonal. The mean size of the particles of aluminum nitride was about 57 nm, and it was constant without depending on the temperature of the levitated aluminum and the partial pressure pf ammonia. The aluminum nitride was formed by the reaction between ammonia and condensed liquid aluminum particle whose size was relatively small.

Jan 1, 2006

By M Philip Schwarz

"This paper reviews the status of computational modelling of a variety of common metals reduction processes, namely the blast furnace, rotary kiln and fluidised bed, and one new process not yet commercialised, namely smelting-reduction as in the HIsmelt Process. In each case, the last decade has seen the emergence of the capability to simulate the processes using multi-phase reacting computational fluid dynamics techniques. In some cases this capability is still in the process of being developed, and the next few years will see the maturing of the modelling techniques. As they become established, it will be possible to apply them to further refine the older technologies such as blast furnaces and rotary kilns, and assist in the optimisation, commercialisation and acceptance of the newer technologies such as fluidised bed and molten bath reduction. The development of a computational fluid dynamic model of bath smelting-reduction is described in some detail to illustrate how a large number of complex and interacting phenomena can be successfully simulated within a CFD framework. IntroductionPyrometallurgical reduction processes, such as the iron blast furnace, have become increasing more sophisticated through the centuries, so that today they are often highly efficient. There are continuing pressures, however, to refine existing processes and develop new ones. The imperatives are often economic, given that the long-term trend in the price of metals is always downward. In recent times, there has been the additional need to improve the environmental impact of metal production. Given that they almost inevitably require the use of carbon, metal reduction processes are large sources of greenhouse gases, and even a relatively small improvement in efficiency can be valuable in reducing CO2 production. Local environmental issues, such as the need to control of particulate emissions, are also driving incremental improvements in equipment.In addition to the economic and environmental drivers mentioned above, new process development is also being driven by the need to process new ores, and the need to produce unrefined metal in a form more compatible with alternative routes for downstream processing. An example of the latter is the production of DR! (Direct Reduced Iron) as a feed for EAF Electric Arc Furnace) in mini-mills.Further improvement of processes that have already been honed by continual plant experimentation over many years is not an easy task. To deliver further gains in efficiency, throughput, or product quality requires a highly sophisticated tool: one such tool· is computational modelling."

Jan 1, 2001

By Evgueni Jak

Pyrometallurgy is an important sector of modern industrial society actively participating in solving current environmental, economic, materials scarcity and other challenges. Recent advances in analytical methods, experimental techniques, thermodynamic, phase equilibria and process modelling tools provide new opportunities to increase the productivity of pyrometallurgical reactors, the treatment of complex feeds and metal recoveries. Fundamental theoretical models can now be used to make a significant next step towards the development and implementation of computerised models describing real industrial processes—Virtual Reactors, and computer-aided smart-decision-making systems that may be called Pyro-GPS by analogy to GPS; these developments can facilitate knowledge-based improvement and optimisation strategies. The implementation of these improvements require ongoing collaboration between researchers, industry and government.

By Jürgen Antrekowitsch, Thomas Griessacher

The recovery of valuable metals from residues like dusts and sludges is nowadays state of the art. Depending on the complex constitution, a recovery of different metals can – in the majority of cases – only be performed with considerable energy input in high temperature processes together with insufficient yields and newly generated residues. Often, the behavior of the dust or sludge in the process during melting or reduction is unknown. In this work, a detailed characterization of selected residues like steel mill filter dusts, cupola furnace dusts and leaching residues is done. The different steps of getting from solid particles into a homogenous liquid phase were investigated. Although high temperature processing leads to high reaction speeds, the complexity of residues keeps the system away from thermodynamic equilibrium. With this research program, some basics are generated to understand smelting and reduction and the gap between thermodynamical calculations and real behavior can be explained.

Jan 1, 2008

By Ricardo Ponce

In recent years, ENAMI implemented modernisation plans at its two smelters in order to meet the government's environmental regulations introduced in the early 1990s. The modernisation plans defined the new SO2 and particulates emission targets, deadlines for compliance, and the revised treatment capacities of the smelters. At Las Ventanas smelter, the principal process change consisted of eliminating the reverberatory furnace. All the smelter feed is currently processed in a 4m diameter, 14m long Teniente Converter, using up to 34% oxygen enriched air. Dry concentrate is injected into the bath through tuyeres. A fuel oil burner compensates for any process heat deficiency. The Teniente Converter high copper content slag is cleaned in an electric furnace. This furnace is also used to melt internal reverts. This paper will discuss the successful operation of the slag cleaning electric furnace.

Jan 1, 1999

By Du Sichen

The present paper presents the modeling of gas-solid reactions in the case of the decomposition of CaCO3, describing the reaction kinetics on the basis of heat-transfer concepts which could be compared with thermogravimetric results. In the case of solid-solid reactions, the present paper describes the model developed for describing solid-solid reactions from dynamic X-ray diffraction technique, developed by the present team. The model has been successful in explaining the formation of spinel from MgO and Al2O3.

Jan 1, 2006

By Joel K. Witt

San Manuel Oxide operations of BHP Copper, located in Southeastern Arizona, operates a leach-solvent extraction/electrowinning (SXEW) facility that produces high quality cathode copper from low-grade oxide ores. Permanent heap leaching and in-situ leaching methods accomplish the dissolution of copper from the oxide ores. Open pit mining and heap leach construction took place from 1985 to 1995. Run-of-mine oxide ore from the pit was hauled to the heap dumps and leached by the soaking cure and continuous irrigation method. Solution application to the heaps still continues and acid soluble copper recovery has reached 86%. This paper presents and discusses the current operating practices and innovations applied to the leach facilities to maximize copper recovery from the heap leached residue. Factors such as irrigation methods, solution chemistry, sideslope treatment, post curing, lixiviant acid strength, and "rice paddies" irrigation, will be discussed. Heap leach solution control and sampling methodologies will be also presented.

Jan 1, 1999

By P. K. Narasimhargahavan

This paper discusses briefly the major reasons associated with the growth and its impact on the energy requirement and Environmental imbalance. A projection based on the present global Alumina and Al requirement indicate a substantial further growth of at least 30% over the next 10 years. It is indicated that the main factors which are likely to influence investments are the environmental factors such as the Climate Change and global response to the growing energy prices and sustainable development. Each of the developed / developing nations must find response to the GHG emissions which will encourage the Al Industry to make an effective contribution to global warming while preserving the international competitiveness of the industry - a challenging task. The efforts shall concentrate on improving energy efficiency in the industry possibly of the order of 25% over the next 10 to 20 years. The developments in this line are discussed.

Jan 1, 2010

By Rak-lun Choi

Plasma-induced damage of InGaN/GaN multiple quantum well (MQW) light-emitting diodes (LEDs) has been studied in terms of forward turn-on and reverse breakdown voltages, together with etch rate and surface morphology. The physical degradation of sidewall along with rough surface morphology of n-GaN caused by increased ion scattering induced the deterioration of the forward and reverse voltages. It was found that the turn-on voltage is sensitive to the surface roughness of the etched n-GaN and the breakdown voltage is strongly affected by the sidewall contamination. Annealing under nitrogen after the mesa etching improved the electrical properties of the InGaN/GaN MQW LEDs. Efficient blue light-emitting diodes (LEDs) were fabricated using InGaN/GaN triangular MQWs. The LEDs with triangular QWs showed a lower operation voltage and 2.4 times higher light output power than those with the rectangular MQW LEDs at 20 mA and 20 °C. The intensity of electroluminescence (EL) at 20 mA was almost independent of ambient temperature in the triangular QW LED, but decreased substantially in the rectangular one.

Jan 1, 2003

By Ko-ichiro Ohno

It is recently recognized that the iron reduction and melting as well as the slag separation of a composite of granular iron ore and coal are completed in a very short period of about IO minutes when the composite is rapidly heated up to approximately 1673K. These phenomena are expected to be applied to a new iron-making process. The mechanism of iron ore reduction and iron-slag separation during rapid heating has not yet been revealed and the fundamental research has just started. Carburization of the reduced iron is regarded as one of the most important steps in this process. In the present work, the composite was prepared from four kinds of coal or graphite as a carbon source and electrolytic iron powder as a completely reduced iron ore. The temperature at which the liquid formation and iron carburization occurred was monitored. Direct observation of smelting reduction behavior was made by a confocal laser-scanning microscope combined with the infrared image-heating furnace to clarify the effect of molten ash on iron carburization. It was found that the meltdown temperature of composite became lower as the melting temperature of coal ash decreased. From the observed result, it was presumed that the liquid slag would act as an important media for the carbon transfer from coal to iron. The carburization mechanism during the smelting reduction was estimated as follows. When slag containing iron oxide melted down and contacted carbon, iron oxide in the slag was reduced and the formation of the metallic iron particle as well as the its carburization occurred simultaneously at the slag-carbon interface. Carburized iron particle was carried from slag- carbon to slag-iron interfaces due to the slag convection flow caused by the difference of the interfacial tension between the carbon-slag and iron-slag interfaces. Carburization of reduced iron could proceed with a repeat of the above-mentioned process.

Jan 1, 2003

By C. Schwandt

Recent research work has led to the development of a new electrochemical hydrogen sensor, which is based on a proton conducting solid electrolyte in conjunction with a self-contained solid hydrogen reference standard and is operated at elevated temperatures. The incorporation of the internal hydrogen reference renders the sensor versatile and user-friendly and makes it attractive for practical exploitation. The present article focuses on the utilisation of the sensor as the integral part of a probe for the quantitative determination of hydrogen in molten aluminium and aluminium alloys. The main features of the sensor and the probe as well as the measuring technique are discussed. Experimental results obtained with the novel analyser in trials under industrial conditions are presented and highlight the good performance of the device.

Jan 1, 2003

By R. I. Rodriguez

Since the 1973 energy crisis, high fuel oil costs have been eroding the economics of the Nicaro and Punta Gorda Plants that employ the Caron Process for laterites processing. Since 1995, Cuban crude oil production has growth dramatically, with progressive utilization in power generation, cement and nickel plants. This paper shows how Nicaro and Punta Gorda plants have been able to shift from expensive Bunker C Fuel Oil to heavy but cheaper Cuban Crude Oil of high Sulfur content and achieve a significant reduction in operating cost. Problems related to the high sulfur content of the Cuban crude oil have demanded extensive investigations of the process chemistry and novelty solutions are proposed, with corresponding changes in process conditions. Innovative options are shown that will allow further cost reductions in the future. Keywords: Cuban Crude Oil, Sulfur, Ammonia.

Jan 1, 2004

By Flavio Begazo, William A. Enrico

"Southern Peru Copper Corporation's Ilo Refinery, the largest in Peru, began operations in 1975 with a production capacity of 165,000 stpy. Southern Peru bought the Refinery from the state owned Minero Peru SA on June 1, 1994.The Refinery processes blister from Southern Peru's I/o Smelter. Blister copper is processed in an anode plant equipped with two 365 st tilting reverberatory furnaces, a 26 mold casting wheel and an anode press machine. Copper is electrorefined in a tank house equipped with 768 commercial cells, 44 stripper cells, and 40 liberator cells, utilizing two electrolyte circuits and a 21,000 Ampere rectifier.During 1989 through 1994 a program for improving productivity was carried out by increasing the number of cells and increasing current density to the total rectifier capacity. As a result, a capacity 215,000 stpy of refined copper, 2 million tr. oz silver and 6,000 tr. oz gold per year was achieved. In 1994 Southern Peru announced plans to increase capacity to 250,000 stpy of cathode with a US$ 18 million investment and a US$ 2 million investment in environmental improvement projects, as part of the purchase agreement with the Peruvian government.This paper outlines the scope of the SPCC lio Refinery modernization and environmental program. It describes the implementation of the Electrolytic Plant expansion based on instaliation of polymer concrete cells, a new rectifier, a new selenium roaster and a Precious Metal Plant upgrades."

Jan 1, 1997

By Jun Zhu, Jilai Xuel, Tao Li

"Coal gangue is industrial waste containing Al2O3 and SiO2 with great recycling and reuse values. This work is aimed at extracting Al2O3 content in the coal gangue by a process of carbonthermal reduction - alkaline leaching. The Al2O3 and SiO2 contents first became a mixture of SiC and Al2O3 in the process of carbonthermal reduction, and then Al2O3 was separated by leaching in NaOH solution, thus producing the sodium aluminate solution for Al(OH)3 precipitation. The products generated at various stages in the process were inspected using XRD and chemical analysis. The effects of parameters such as reduction temperature, carbon ratio, NaOH concentration, leaching time, leaching temperature, stirring speed, etc were investigated in details.IntroductionCoal gangue is an industrial residue resulted from the process of coal mining and washing, accounting for 100 - 150 kg with 1 ton raw coal mined. The existence of coal gangue in large quantities has become a serious problem for environment pollution. On the other hand, the chemical compositions of coal gangue are Si02 and Ah03 primarily. In China, the accumulation storage capacity of Ah03 in coal gangue is not less than 600 million ton at a rough estimate, which should be considered as an abundant second resource [1]. If the alumina can be recycling and reused effectively from coal gangue, it will not only reduce the imperilments caused by coal gangue, but also yield good economic returns.Generally, the processes of extracting Al2O3 from coal gangue can be divided into acid leaching (vitriol or hydrochloric acid) and alkaline leaching (mostly NaOH) [2]. The acid leaching processes have many problems, such as lower leaching ratio, corroding the equipments, recycling the spent acid hardly, etc. The primary matter of alkaline leaching process is silica dissolving with alumina, which brings perplexing desilication process, alumina loss seriously and higher energy consumption."

Jan 1, 2011

By Gudrun A. Saevarsdotti

For decades tile aluminium industry has been practicing gas treatment of aluminium melts. This treatment is of great importance because of its influence on 'impurity" and inclusion removal from the melt. The gas-melt interaction is greatly influenced by the gas composition, melt temperature etc. This paper gives an overview of the interaction between argon-chlorine gas mixtures and the aluminium melt. It covers the thermodynamics of the reaction between the chlorine and a number of different elements commonly found in liquid aluminium, and discusses the behaviour of reaction products in the melt. The paper reports an experimental study of the behaviour of the chlorine-molten aluminium interface, using sodium contaminated aluminium melt with and without the addition of grain refiner.

Jan 1, 1996

By Keith Rozenburg, Ivar Reimanis, Jesus Chapa

"Experiments in conjunction with finite element analysis (FEA) are used to better predict crack propagation in ductile/brittle graded composites. Cu/W graded composites were fabricated by stacking discrete layers of powders and hot pressing. Crack propagation was studied by loading a notched beam in four point bending and examining the subsequent crack deflection. The notch was placed within a particular composition of material, oriented in a direction perpendicular to the gradient direction. Elastic and plastic mismatch between different constituents in the graded composite induce shifts in the phase angle of loading, thereby causing the crack to deflect. FEA indicates that thermal residual stress has a negligible ""influence on the crack path. The combined FEA and experimental results suggest that elastic mismatch is the single most important material property-related factor in controlling crack deflection.IntroductionMany 'applications would benefit or may even require materials whose performance or functionality must vary spatially. While the concept of functionally graded materials has existed for nearly one hundred years, it is only within the last fifteen years, that research efforts have focused on generic issues in processing, properties and performance of functionally graded materials. This generic research effort has brought together scientists and engineers from traditionally different disciplines to address common issues with graded composites. The current work focuses on issues in structural joining. A wide variety of applications require some type of joining between dissimilar materials. Examples include thermal barrier coatings for turbine engines, wear resistant coatings for tools, ceramic engine parts, and microeiectronic devices, as well as many traditional applications involving metallic welding. The joints may either be discrete, involving a single interface, or they may· be spatially graded in composition. Extensive theoretical and experimental information exists on discrete bimaterial and trimaterial joints, but relatively little exists for graded joints or composites"

Jan 1, 2000

By B. S. Terry

Experiments have been conducted to assess the feasibility of capturing bearing emissions arsenic with CaO during the roasting of enargite (Cu3AsS4). Enargite/CaO mixtures have been heat treated in air, nitrogen or oxygen for various times and the products of reaction analysed by X-ray diffraction and cleaned analysis. The results show that substantial capture of arsenic can be achieved via the formation of calcium arsenates and/or calcium arsenides. In addition significant capture of sulphur is achieved by the formation of calcium sulphate andlor sulphide. Complete conversion to copper sulphide with total removal of arsenic can be achieved within 30 minutes at 700°C. Further heat treatment in air or oxygen leads to the formation of copper oxide and copper oxysulphate. Without optimisation of reaction conditions, it has proved possible to achieve retention of in excess of 85% of the arsenic content of enargite in the form of calcium arsenates.

Jan 1, 1994