Roasting treatments were investigated to remove arsenic from a nickel concentrate. The main arsenic minerals and their proportions in the concentrate were niccolite (NiAs)-50%, gersdorffite (NiAsS)-40% and arsenopyrite (FeAsS)-10%. Thermal analysis showed that gersdorffite and niccolite began decomposing when heated above 640 and 830°C respectively. The maximum roasting temperature was limited by agglomeration of the concentrate above 900°C. A small vibrated bed reactor was used to investigate the effects of temperature and gas flowrate, the latter to sweep away evolved arsenic. At 900°C, 24% of the original arsenic remained in the concentrate. SEM examination of the calcine showed that the residual arsenic was associated with the calcium in the gangue minerals. Additions of sulphur (either as elemental sulphur or from pyrite) facilitated the decomposition of the arsenic-containing minerals, decreased reaction with calcium in the gangue and produced calcine containing 4-6% of the original arsenic. Treatment with chlorine during roasting was effective in reducing the arsenic content to similar levels. Generation of chlorine in the bed by sulphation of CaC12 also produced encouraging results. Arsenic, Nickel Concentrate, Roasting, Chlorine, Sulphur, Gersdorffite, Niccolite

Jan 1, 2005

By Takahiro Miki

Soldering material widely used is Sn-Pb alloy, which have low melting point and excellent electrical, strength properties and wettability. However, Pb is one of the toxic elements, which is undesirable due to environmental and safety reasons, thus Pb-free alternative alloy is preferred for new soldering material. Sn-Ag and Sn-Zn based alloys have been viewed as very promising candidates, among many potential substitutes. Addition of third element to these alloys will decrease melting point of the alloys. Hence, Sn-Ag-In and Sn-Zn-Mg alloys are expected to be suitable for replacing Sn-Pb solder alloy. In order to design new Pb-free soldering materials, it is crucial to understand precise thermodynamic properties and phase diagrams of alloy systems. In the present work, ion current ratios of Ag to In and Mg to Zn were measured for Sn-Ag-In and Sn-Zn-Mg alloys by mass spectrometry, respectively. Also, the authors reviewed the thermodynamic properties of terminal binary alloys determined by other researchers and evaluated a thermodynamic functions to express the excess Gibbs free energy of each binary alloy. Thermodynamic functions to express the excess Gibbs free energy of liquid Sn-Ag-In and Sn-Zn-Mg ternary alloys were determined, utilizing the assessed Gibbs free energy of terminal binary alloys with the measured ion current ratios using mass spectrometer.

Jan 1, 2003

By Enrui Dai, Weibing Chen, Bin Yang, Wenhui Ma, Haisheng Fang, Hui Wang

LiMn0.8Fe0.2PO4/C composite was prepared by an improved solid-state method and the effect of calcination temperature on properties of the obtained materials was investigated. The results showed that increasing calcination temperature from 600 to 700 oC improved the performance of the LiMn0.8Fe0.2PO4/C due to enhanced crystallinity and increased conductivity, but further increase in calcination temperature to 800 oC led to degraded performance due to particle growth and decrease in porosity. Therefore, the LiMn0.8Fe0.2PO4/C composite prepared at 700 oC exhibited the best electrochemical performance, and could deliver a high capacity of 152 mAh g−1 at 0.1 C, 147 mAh g−1 at 1 C and 114 mAh g−1 at 10 C. In addition, the performance of the LiMn0.8Fe0.2PO4/C and LiMn0.8Fe0.19Mg0.01PO4/C was compared when they were obtained at the optimum calcination temperature.

Jan 1, 2015

By Yoshisada Michiura, Junko Umeda, Katsuyoshi Kondoh

Rice husks or straws, one of the main agricultural wastes in South-east Asia, have a large possibility to be employed as usefully renewable resources to produce energy and high-purity silica (SiO2), because they consist of about 70% organics such as cellulose or hemi-cellulose, and 20% amorphous SiO2. The former is utilized as bio-mass energy; for example, thermal or electric energy, and bio-mass ethanol. High-purity silica can be used as raw materials in the industrial uses. It would be possible to extract silica elements from rice husks and straws by burning them in air because their main contents are organics. In the previous studies, a strong acid leaching treatment on rice husks before burning was carried out by using H2SO4, HCl and HNO3 to prepare high-purity silica materials. This was available to accelerate the hydrolysis of celluloses and hemicelluloses contained in rice husks, and remove the above metallic impurities. A strong acid leaching treatment, however, is significantly hazardous to environment and human life, and causes an increase of the process cost. In this study, the environmentally benign, harmless to human and economically effective process to produce high-purity amorphous SiO2 materials from rice husks has been established without using strong acids. From a viewpoint of the harmless influence on human body, the carboxylic acids were used in the leaching treatment on rice husks. TG-DTA measurement and GCMS analysis indicated that the leaching was effective for the hydrolysis of celluloses and hemicelluloses contained in rice husks at 473K~873K, which produced the same results in using the conventional sulfuric acid. The metallic impurities could be also removed from the husks via a chelate reaction between carboxyl groups (-COOH) and the metal elements. In particular, it was clarified that cadmium (Cd) were completely removed from rice straws by this reaction. Concerning the burning conditions of rice husks after the acid leaching, it was necessary to supply a suitable amount of air to completely combust organics; for example it required air supplement of 50 ml/min. or more. The burning temperature should be less than 1273K to obtain amorphous structured silica. High-purity amorphous silica materials with 99% or more were prepared from rich husks by applying the citric acid leaching treatment and burning process at 1073K in air.

Jan 1, 2008

By Esther Carrera Martinez

Caraiba Metals is the sole brazilian copper custom smelter. The sulfur present in the various concentrates processed is recovered as sulfuric acid and oleum ,which are sold in the local market For quality assurance purposes, a study was carried out in order to determine how to control the arsenic content in the acid, allowing the continuous processing of concentrates with high levels impurity, The study was based on the process parameters of the washing towers and mist precipitators, Others process variables were investigated and their effects were used in support to confirm the results, After many analyses performed some interventions to improve the quality of the acid were implemented in the plant, which proved to be successful even by using a conventional purification system,

Jan 1, 1996

By Ralph H. Nafziger

The feasibility of smelting a Ni-Co-Cr-bearing laterite ore from southern Oregon was evaluated by the Bureau of Mines. The objective was to prepare a master alloy for subsequent stainless steel production. A mixture of the ore with suitable reductants and fluxes was smelted in a 50-lb-capacity single-phase ac electric furnace under sub- merged arc conditions. The smelting tests produced a metal in which most of the nickel was concentrated. High-chromium recoveries required an excess of carbon. The resulting metal alloys contain sufficient nickel for some stainless steels. Ferrochromium additions would be required to attain suitable chromium levels. This research was conducted under the Oregon Metals Initiative in cooperation with Walter B. Freeman.

Jan 1, 1993

By Robert G. Robins

Precipitation of ferric arsenate is an effective method for removing arsenic(v) from hydrometallurgical process solutions. The solubility and stability of this compound. FeAs04.2H20, has received some attention in recent years and the reported solubilities of amorphous and crystalline material have varied considerably. This paper reviews previous studies and reports some recent work with a consistent model to explain the variable results. Free energy data for ferric arsenate and its associated dissolved complexes are presented.

Jan 1, 1990

By Henrique Kahn

The Anitapolis alkaline massif in southern Brazil underlies a sub circular area of 6 km2. Bore-hole data show a concentric rock distribution, with mafic rocks in the central part and felsic rocks in the border zone. The rocks are covered by talus and weathered material, 30 m thick on average, and very inhomogeneous in composition. Phosphate mineralization associated mainly with two levels of the weathering mantle and with fresh rocks. A preliminary ore-type classification was based on distribution of apatite, feldspar, vermiculite, biotite-phiogopite, calcite, pyroxene, amphibole and analcime, determined by semiquantitative diffraction method. Technological tests performed on eluvial ore samples from three adits resulted in a subdivision of ore-types based on the difference in behavior due to mineral characteristics during mineral pr

Jan 1, 1991

A new technology for the treatment of copper nickel-containing concentrate after high-grade matte flotation to blister copper with the production of liquid silicate slags in a vertical autogenous unit with upper oxygen blow has been considered. The copper and nickel behavior in the process of sulphide copper concentrate interaction with silicate melt containing oxide copper has been studied. The general mechanisms of such interaction are found.

Jan 1, 2003

By G. A. Irons, D. Guo, D. Angheiina

To produce low-carbon (<30 ppm) steel in the tank degassing process, a ladle of steel with an oxidizing slag is placed in a vacuum tank equipped with bottom bubbling. The kinetics of this process are slow compared to the more prevalent RH degassing process, providing the impetus for the present work. There are several aspects to this work: water models of the fluid flow in the ladle; simulation of the decarburization (CO evolution) with C02 desorption in water; pilot-plant (60 kg) studies of the decarburization kinetics; mathematical modelling of the fluid flow in the ladle; mathematical models for each of the kinetic sites (plume, top slag and auto-nucleation); and full-scale trials. The results show that during the refining cycle the contribution from each reaction site changes, suggesting avenues for reducing cycling time and final carbon contents.

Jan 1, 2000

By Pandey H. D.

The paper describes a fluidised bed ion exchange method for simultaneous removal of phenols and cyanide from the effluent. Use of an eluant enables regeneration of the resin in the continuous operation mode. The breakthrough experiments conducted both on the laboratory scale and on a pilot plant scale have shown that while the level of phenol can be brought down from 462 ppm to about 6 ppm, the free cyanide is almost totally removed. An examination of data indicates that the method can serve the twin objectives of pollution control and phenolic compounds recovery.

Jan 1, 1992

By Lztok Peruš, Goran Kugler, Matevz Fazarinc, Milan Tercel

"Hot deformability of M42 tool steel additionally alloyed with cobalt and molybdenum was investigated. Hot-compression tests were carried out in the temperature range 850 °C -1200 °C, at strain rates range 0.001--6s-l up to strain of0.9. Field-emission scanning electron microscope and optical microscopy were used for characterization of microstructure of deformed samples, which revealed a very complex precipitation of carbides that strongly depends on the soaking temperature, the soaking time, the stress state, the deformation temperature as well as on the strain rate. Gathered data was used to calculate the processing parameters such as process maps, apparent activation energies and strain hardening exponents. For better understanding of thermodynamical properties of the studied steel a simultaneous thermal analysis was conducted. Furthermore the analysis of phase equilibrium was calculated using Thermo-Cale software. On the basis of these studies the optimal soaking temperature and process windows were determined.IntroductionHot workability ofledeburitic tool steels is important economic factor. This means that for each tool steel individuallysafe range of hot working parameters should be revealed. Publications in the literature with regard to the hot workability of tool steels are rare and therefore more information from this research area is desired.The relatively low hot workability of ledeburitic tool steels, i.e. steels in which the solidification is completed by a eutectic transformation of the residual interdendritic liquid to austenite and various alloy carbides (ledeburitic carbides), is usually characterized by the production of surface and internal cracks during the hot deformation."

Jan 1, 2013

By Bingyi Bai, Wangjun Peng, Yanling Guo, Jieyu Zhang, Guoding Gao

The phase transformation of bayan obo ore with high concentration of iron and calcium was reduced at temperatures no more than 1000℃ were investigated in this study. The samples with insufficient carbon were treated at the temperature using a vertical furnace with a thermogravimetry (TG). The mineral phases and content were examined using Xray diffraction (XRD) and X-ray fluorescence spectroscopy (XRF) respectively. The complex phases of bayan obo ore transformed to some simple phases after treated with different content of carbon at the same temperature for 10 hours. The result of XRD、 XRF and TG showed that the reduction degree of Fe3O4 phase formation varied with the temperature and the carbon content of bayan obo ore.

Jan 1, 2015

By Walter E. Dean

Twenty six samples of carbonaceous gold ores and associated rocks from outcrop and mine localities in northcentral Nevada were analyzed for concentrations of major. minor, and trace elements, total sulfur, and organic carbon. Q-mode factor analysis was used to define six distinctive carbonate, organic, and detrital associations of elements, and to group samples based on these associations. The trace metals that have clearly enriched the organic-carbon-rich samples are V, Zn, Ni, Cu, Cr, and Mo, although few of the samples could be considered "metal-rich" when compared to other organic-carbon-rich black shales. Rock-Eval pyrolysis was used to evaluate thermal maturity and hydrocarbon yield of the samples. Unfortunately, most samples were too thermally altered to be suitable for routine organic geochemical characterization of organic matter. The 813C values of organic carbon in rocks from different deposits have a trimodal distribution, but there is no clear distinction between the three groups of deposits that can be related to age, thermal history, or depositional environment.

Jan 1, 1987

By Kafui Nyavor

Acid mine drainage (AMD) is presently the biggest single environmental problem facing the mining industry. New and expanding metal mines in most parts of the world have to demonstrate their ability to contain this problem to obtain operating permits. Conventional methods of controlling acid mine drainage have primarily been limited to collecting the drainage and neutralizing with alkaline materials which do not provide a permanent solution to the AMD problem. Since acid mine drainage results from the oxidation of sulfides in the presence of oxygen, water and iron-oxidizing bacteria, controlling any of these three factors contributing to pyrite oxidation provides a potential at-source remedy for reducing or preventing acid mine drainage formation. Physical properties such as hydrophobicity also play an important role in the attachment of bacteria, adsorption of oxygen, water, and other ions that subsequently lead to the oxidation of pyrite. In this communication, the suppression of pyrite oxidation by treatment with fatty acid amines (FAA) was investigated. The FAA treated pyrite samples were tested at various conditions of temperature and pressure. At an elevated oxygen pressure of 500 psi and a temperature of 600 C, less than 0.2% oxidation was obtained for the FAA treated pyrite samples, while over 1.2% oxidation was obtained for the untreated samples in 10 hours of oxidation time. Accelerated column oxidation tests at ambient condition showed that FAA mated samples reduced pyrite oxidation by at least 75% in 81 days.

Jan 1, 1994

By J. J. Kim

In a study of buildup in a green-feed reverberatory furnace, it was determined that approximately half of the crucible area has a moderate buildup of 25 in. or less, and that the area extending 45 f t from the burner end of the furnace has only a slight buildup. The false bottom, averaging 6 in. in thickness, was found to cover the entire crucible area. The stratification of Cr2O3, A12O3, and SiO2 occurs throughout the slag layer; this phenomenon is the principal reason for the formation of the false bottom in the green-feed reverberatory furnace. The false bottom is caused primarily by the settling of FeO*(A1,Cr),03 aggregates, which are derived mainly from returned converter slag. The false bottom can be transformed to a solid permanent buildup in the furnace, particularly when the matte is completely withdrawn. From the material balance of Al2O3 and Cr2O3 around the furnace, It is estimated that the average rate of aluminum chromite accumulation is approximately 0.3 ton per day or less.

Jan 1, 1976

By J. K. Brimacombe, I. V. Samarasekera, B. G. Thomas

"Mathematical models have been developed for the processing of static cast steel ingots and are app1ied to investigate the mechanisms for the formation of panel cracks. Panel cracking is an intermittent but persistent defect that causes affected steel ingots to be scrapped. A two-dimensional, finite-element, heat-transfer model was formulated and employed to calculate the temperature distribution in both large and small steel ingots during the various processing stages from initial casting to the start of rolling, including solidification, cooling in the mold and in air, reheating in the soaking pit, and subsequent air cooling. The stress state in the ingot arising from the calculated temperature variations was then determined. This involved the development of a transient, elasto-visco-plastic, finite element, thermal stress model, including the effects of phase transformation volume changes and kinetics creep, and temperature-dependent, mechanical properties. The results of the mathematical model predictions of temperature and stress were then used to determine the mechanisms and to suggest solutions for two different types of panel crack formation. Mid-face panel cracks apparently form during air cooling when the mid-face surface temperature is between the Arl and 500~C. Off-corner panel cracks appear to initiate internally during the early stages of reheating but do not propagate to the surface until much later. IntroductionPanel crack formation in static-cast steel ingots is a defect that has been plaguing the steel industry for several decades. Although the problem is intermittent, it is also serious since affected ingots must be scrapped. Panel cracks are manifested as two distinct types of cracking problems. ""Mid-face"" panel cracks are found exclusively in small, 2 to 6 ton, medium carbon steel (0.3 to 0.7% C) ingots and usually exhibit a single, continuous, longitudinal crack down the center of one of the ingot faces as shown in Fig. l (l). ""Off-corner"" panel cracks often form roughly oval, discontinuous crack patterns on the wide faces of large, 20 to 30 ton ingots as seen in Fig. 2 (2). They affect only low carbon steels (0. l to 0.2% C) with high manganese content. Both defects affect only aluminum-treated steels and are caused by a combination of intermediate temperature ductility loss involving aluminum-nitride precipitation and thermal stress generation. The ductility problem has received a good deal of attention which was the subject of a recent review (3). The present study was undertaken to investigate the thermal stress aspects of the problem through the development of mathematical models of heat transfer and stress generation in static-cast steel ingots. The ultimate objective was to elucidate the mechanisms of formation for both types of panel crack and to evaluate possible solutions to the problem."

Jan 1, 1986

By F. F. Aplan, G. Simkovich

"A review is given of the effects of solid state point imperfections upon a number of mineral benefication processes and a metal extraction process. It has been found in numerous flotation studies that small amounts of aliovalent impurities (dopants) in binary compounds may show major effects upon flotation behavior. Both semiconducting and ionic conducting compounds are affected. These effects are also seen in hydrometallurgical studies as well as in electrostatic operations. Additionally, de-copperization of lead melts appears to be strongly influenced by similar defects. It is hypothesized that the effects observed in these studies are present in actual operations and should be considered in designing processes. A few speculations concerning future efforts are advanced. IntroductionImperfections [point (e.g., vacancies, interstials, quasi-free electrons, electron holes, impurity ions), line (e.g., dislocations), two dimensional (e.g., grain boundaries) and three dimensional (e.g., 2nd phases) defects] are generally present in solid materials and these imperfections may, and often do, have important effects upon a variety of properties and processes. In general, one may, in most cases, attain elimination of three dimensional defects by a separation process of one type or another (e.g., gravity, electrostatic, magnetic, flotation, hydrometallurgical etc.,). Thus, this type of defect has rarely been investigated in a systematic fashion. Two dimensional defects are always present in non-single crystal materials but have also escaped systematic studies in processes primarily because the control of such defects is not easily attained. Line defects are non-equilibrium entities which are present in ill-defined quantities so that they present a variable that cannot be easily controlled although through careful systematic experiments one can attain some reproducible relations pertaining to this type of defect.Contrary to the lack of studies concerned with the effects of 1, 2 and 3 dimensional types of defects there has been some activity concerned with point defects and their effects upon a number of mineral/metallurgical processes, especially flotation processes. Thus, this article will present a review primarily of point defects in relation to their effects upon flotation although other processes and defects will also be mentioned."

Jan 1, 1988

By Musa Karakus

The sedimentary iron ores of Alsace-Lorraine, France have very high phosphorous contents that average 0.7% and are as much as 2.19% P. Ores from the Tucquegnieux and Joeuf mines have been studied by cathodoluminescence microscopy, X-ray diffraction, scanning electron microscopy, and electron microprobe analysis in order to fully characterize the mineralogy, size, shape, and distribution of the deleterious phosphate grains. The phosphorous occurs as collophane, a carbonate fluorapatite, in ten morphological forms, most abundantly as microcoprolites, but also as intraclasts, concentric layers, and cortices in ooids, phosphate replaced ooids and bioclasts, phosphatiC shells, fossil infillings and internal molds, fish teeth, phosphatiC laminae, and cements between the goethite ooids. About 95% of the phosphate grains are sufficiently large that relatively fine grinding fol&apos;lowed by reverse flotation would be expected to be effective in significantly diminishing the phosphorous content of the concentrates.

Jan 1, 1989

By Mukesh K. Agarwala

Alloy composite parts were made from powders by Selective Laser Sintering (SLS). SLS is a rapid prototyping process that uses data from CADICAMICAE systems to guide a laser beam and rapidly form 3-D prototype parts from powders without any part specific tooling. In this study, Bronze-Nickel parts made by SLS were studied for their mechanical properties. To make the parts structurally sound, SLS parts were further processed by conventional isothermal sintering, without loss of shape. The resultant densification and mechanical properties were studied and related to microstructures and P/M densification models. These results were then correlated to the SLS processing parameters.

Jan 1, 1994