By Om P. Garg

During the period between 1970 and 1974 the Iron Ore Company of Canada had embarked on a detailed program to evaluate all aspects of mine design work for its open pit mines around Schefferville, located both in Quebec and Labrador, Newfoundland, Canada. One of the main conclusions was that the majority of the slope angles for the ultimate pit walls could be steeped. During the period 1975 and 1976,five (5) open pit iron ore mines were redesigned using the steeper slope angles up to 55 degrees. Initially these pits were designed at slope angles varying between 37 degrees and 45 degrees due to the generally fractured and leached nature of rocks in the area. During the active mining phase between 1976 and 1979, the stability of the steeper ultimate pit walls was monitored. The mining of ore was successfully completed in 1978 and 1979 in three pits. This of course, resulted in a significant savings due to a reduction in the quantity of waste that had to be removed. The successful pit slope redesign project was a co-operative effort between the Federal Government, Universities and the Iron Ore Company of Canada.

Jan 1, 1983

By H. C. Fiedler

THE development of the cube-on-edge secondary re-crystallization texture in Si-Fe strip depends upon the ability of inclusions to restrain normal grain growth. This ability is determined by the number and size of inclusions, which, for a given composition, is controlled by the thermal history of the material during the prior processing.' It has been shown2 that increasing the silicon content decreases the solubility of sulfur, and it is the purpose of this note to show the consequences of this decreased solubility for secondary recrystallization. Heats were made as previously described and cast into graphite molds.' The compositions are shown in Table I. Slabs 1 in. thick were cut from the ingots and either hot-rolled from 1000°C in the as-cast condition or after one of the heat treatments described later. The processing to the final gage of 12 mils followed the previous procedure.' To avoid cracking, the 5.2 pct Si alloy was cold-rolled at 150" to 200°C rather than at room temperature. The percent cube-on-edge texture developed by isothermal heat treatments was determined by dividing the maximum torque measured on disk sam-

Jan 1, 1968

By J. V. Gluck, Ping-Wang Chiang

The tellurium-rich region of the Sb-TI-Te ternary system was investigated by means of DTA, metallo-graphic, X-ray, and electron beam microprobe techniques on the sections Sb2Te3-T12Te3, SbTlTe2-Te, SbT1Te2-Sb2Te3, and SbTlTe2-T12Te3. The phase behavior of this region is summarized in terms of four ternary invariant reactions and a schematic reaction diagram is suggested. Isopleths for the sections SbT1Te2-Sb2Te3, Sb2Te,-T12Te3, and SbTlTe2-Te were constructed, and a schematic diagram of the projections of the liquidus lines and invariant planes is presented. No evidence was found to support the existence of the ternary compound "SbTlTe3", or pseudo-binary behavior of the section T12Te3-Sb2Te3, as reported by Borisova and Efremova. Electrical conductivity, Seebeck coefficient, and thermal conductivity measurements were made at room temperature on fully annealed samples. 1 HE phase relationships in chalcogenides are often complex and difficult to resolve, particularly since the approach to equilibrium is a rather slow process. For example, the phase diagram of the T1-Te binary system was in doubt until clarified by Rabenau et al.,1 the phase fields at compositions near Bi2Te3 in the Bi-Te binary system have only recently been satisfactorily elucidated by Glatz,2 and there may still be some question as to the extent of the Sb2Te3 field in the Sb-Te system.3-5 In ternary systems, the existence of the compound "AgFeTe2" was the subject of a number of conflicting reports6-8 and the stoichiometry of the composition "AgSbTe2" was in doubt for a period of time.9 Recently, questions have arisen regarding the existence of certain compounds in the ternary systems Bi-Tl-Te10-14 and Sb-Tl-Te.15 The impetus for studies of these latter systems stemmed from the report of Borisova et a1.10 of a congruently melting ternary compound, "BiTlTe3", which apparently had extremely favorable thermoelectric properties for room-temperature cooling applications. Attempts by other investigators to produce the compound or confirm the transport properties proved to be unsuccessful.12-14 Recently, Chiang and Gluck14 reported studies of the phase relations in the tellurium-rich region of the Bi-T1-Te system which indicated that the section T12Te3-Bi2Te3 was not pseudobinary as suggested by Borisova et a1.10 The contention of Spitzer and sykes12 was supported that the composition "BiT1Te3" was multiphase, with the primary constituent actually being BiTlTe2, a compound whose existence has been well demonstrated.16,17 The investigation reported in the present paper was prompted by a later report of Borisova and Efremova15 on a similar study of the section T12Te3-Sb2Te3 from the Sb-T1-Te system. They also claimed this section to be pseudobinary, and that a ternary compound "SbTlTe," was formed peritectically. Some "preliminary" crystallographic data were given for the compound and thermoelectric transport properties were presented. In view of the questions concerning the behavior of the Bi-T1-Te system and the existence of the compound "BiT1Te3" it was suspected that the Sb-T1-Te system might behave in a similar fashion, particularly in light of the known existence of a compound SbT1Te2, iso-structural with BiT1Te2.17 Consequently, an investigation was undertaken to clarify the phase relationships in the tellurium-rich region of the Sb-T1-Te system. It is the purpose of this paper to present the results of this study, including a representation of the phase relations, isopleths for various composition sections, and the determination of some phase compositions and transport properties. EXPERIMENTAL PROCEDURES Commercially available high-purity (99.999+ pct) elements, purchased from the American Smelting and Refining Co., were used for the sample preparation. All samples were made from thoroughly mixed powders of previously prepared master alloys: SbTlTe2, Te, Sb2Te3, and T12Te3. Stoichiometric quantities of the constituents for each 10-g sample were weighed into a specially cleaned fused silica tube and sealed under a vacuum of better than 5 x 10-5 torr. The sealed constituents were fused and reacted at 650° to 750°C for at least 4 hr under continuous agitation in a "rocking" furnace, and the resulting product was air-cooled. The tube was opened and the sample was ground to a powder. A portion of the powder was rebottled in a DTA tube under vacuum, and the rest of the material was similarly resealed in a separate tube, re-fused in the rocking furnace, and again cooled to make the ingots for electrical and microstructural studies. All samples were subjected to further heat treatments as discussed in the section on experimental results. Each DTA tube was made of 7-mm-OD fused silica tubing with a concentric 2-mm-ID depression about 4 mm long formed in the bottom to accommodate a thermocouple. The size of a DTA sample was 0.5 to 1.0 g. An Aminco Thermoanalyzer whose accuracy was within 2°C18 was used for the DTA measurements. The metallographic samples were prepared by conventional techniques. A solution of FeCL dissolved in a methanol-HC1 mixture was found to be the most satisfactory etchant. Electron beam microprobe scanning and point-count examinations were made on polished and unetched samples using an ARL Electron Microprobe at an electron beam voltage of 20 kv. The detectors were set to receive characteristic La1 radiation. Calibration standards of the pure elements were incorporated in each sample mount; quantitative point counts were calibrated by a method similar to Ziebold

Jan 1, 1969

By A. C. Fraker, H. H. Stadelmaier

In the systems Mo-Fe-C, Mo-Co-C, and Mo-Ni-C the phase boumdaries of the cubic Ij carbides were determined at 1000°C and the variation of the lattice parameter with composition was measured. In the system Mo-Fe-C a single ternary carbide, Mo3Fe3C, was observed. In Mo-Co-C and Mo-Ni-C two new n phases of the type M12C were found: Mo6C06C and Mo6Ni6C. At 1000°C they coexist with the M6C phases MO3-4,CO3-2C and Mo3-4Ni3-2C, respectively. Mo3C03C and Mo4C02C are not separate phases but parts of a single M6C phase region, and the same is true of Mo3Ni3C and Mo4Ni2C. THE n carbide structure type has been known since it was determined by westgren' in 1933, yet reliable information on phase compositions of this type is ap-parently scarce. The following selection of suggested formulas illustrates the extent of the confusion con-cerning compositions: W2-3Fe4-3C,1W6Fe6C,2 W2_4Fe4-2C,3 (W,Fe)6C,4 Tj.-W4Co2C and nz-W6Co6C,5 n1-W3Co3C and n2-w4Co2C,5 W3C03C and w6Co3C2,7 MO3Fe3C,8n2-M04Fe2C,9 (MO,Fe)6C,4 MO3CO3C,8 n2-MO4CO2C.9 Many of these compositions obviously overlap, some disagree in carbon content. The use of the designations 77, and n2 is not consistent. There is uncertainty whether two carbides M6C coexist or whether there is only one M6C with a wide range of substitution of one metal for the other. The existence of M12C seems questionable altogether if one ignores the results of a neutron diffraction study of W6Fe6C supporting that particular metal to carbon ratio.'' More reliable information is available for the iso-typic oxides studied by Nevitt,11 Nevitt, Downey, and orris," and Meussner and carpenter.l3 That n car-bides and oxides are structurally identical, particularly with respect to the location of the metalloid atom, has been demonstrated clearly by Stadelmaier and Meussner14 and also by Parthe, Jeitschko, and sadagopan.15 Therefore the present paper, which attempts to establish the phase boundaries of n defini-tively for three carbon systems, has implications for the whole family of filled Ti2Ni types. EXPERIMENTAL PROCEDURE The samples were prepared in two stages. Pellets weighing 3 g were compacted from powders of the elements and presintered in a closed tube of fused silica that had been evacuated to lO-4 mm Hg. This was fol- lowed by arc melting the sintered samples under argon. Remelting the button once was sufficient to produce homogeneous specimens. The metal powders had the following minimum purities in wt pct: molybdenum 99.5, iron 99.0, cobalt 99.7, nickel 99.9, graphite 99.94. Carbon determinations by the gas volumetric method were obtained from thirty-one of the one hundred samples in the annealed condition. They were limited to compositions that were critical to placing a boundary line in the isothermal sections. The carbon losses were comparatively low and averaged less than 1.5 at. pct. For annealing, the samples were sealed in tubes of fused silica evacuated to 10-4 mm Hg. The annealing schedule was 20 hr at 1250°C followed by 150 hr at 1000" ±10°C. For the water quench the silica glass tubes were broken mechanically to speed the quench. The specimens were examined in the as-cast and annealed condition by standard metallographic techniques. Some of the as-cast and all annealed samples were studied by X-ray diffraction using a 114.6-mm powder camera with filtered Co radiation. The lattice parameters of the n phases were determined by graphic extrapolation to 8 = 90 deg on a plot against sin2 8. It is estimated that the maximum error in the lattice parameters is ±0.002A.. The phase fields were determined by the disappearing phase method, relying on X-rays for phase identification and on microscopy to detect small amounts of a phase. RESULTS Pertinent information on the binary side diagrams has been summarized by Hansen and Anderko16 and Elliott17 and will not be discussed further. Photomicrographs documenting the equilibria at 1000°C have been selected to avoid redundancy due to the similarity of the three systems. Thus there will be only one picture showing an equilibrium with Mo2C, and so forth. Molybdenum-Iron-Carbon. An isothermal section of most of the Mo-Fe-C system at 1000°C is shown in Fig. 1. No attempt has been made to distinguish between a and y iron or to determine their phase boundaries. A conspicuous absence is the phase Fe2 1Mo2C6 with the Cr23C6 structure, supporting the suggestion by Krainer4 that it decomposes by annealing at high temperatures. The only ternary phase is found in a narrow range around Mo3Fe3C (MO43Fe43C14). A microstructure with a two-phase mixture of Mo + n is seen in Fig. 2. The variation of the lattice parameter of n with the estimated composition is shown in in Table IA. The phase diagram does not agree with the results of Kuo9 who reported n2-Mo4Fe2C. Our lattice parameter Varies from 11.095A at the iron-rich end to 11.140Å at the molybdenum-richoend of the phase field whereas Kuo9reported 11.26Å for Mo4Fe2C. We are in agreement with the older work

Jan 1, 1970

By Richard L. Ashbrook, John F. Wallace

Several high-temperature eutectics of cobalt and nickel alloys were modified by small additions of selected elements. Thes-e alloys were compared to unmodified melts for microstructural variations. A few modified compositions were selected on the basis of structure and their tensile and stress-rupture behavior determined. The results of stress-rupture tests in air at 1800 F and room-temperature tensile tests of four high-temperature eutectics showed modification capable of producing substantial improvements in properties. The microstructures were altered and mechanical properties improved by: a.) dispersing a subordinate phase more uniformly throughout the matrix; b) replacing large continuous -network or platelike constituents with small equiaxed discontinuous phases; and c) by forming new, finely divided phases. tHE term "modification" is most commonly used to describe the refinement in microstructure of the Al-Si eutectic that occurs as a result of rapid cooling from the melt or on slow cooling after treatment with small amounts of sodium.1 "Modification" has also been used to describe the change from flake to spheroidal graphite in the austenite-graphite eutectic of cast iron.2 This change of graphite shape is accomplished by small additions of cerium or magnesium.3 Other systems have also been shown to be capable of modification, for example: Pb-Sn by copper;4 Al-Cu by sodium;5 Al-Mn by sodium;5 and Pb-Sb by aluminum.5 Although modification of Al-Si alloys and cast irons is usually accompanied by improved mechanical properties, a general definition of modification has been suggested to include the effect of small quantities of impurity elements on the microstructures of all eutectic alloys, regardless of the effect on the mechanical properties.6 In this paper, the term "modification" is employed in a broad sense to include the formation of third phases or even the supplanting of one of the binary eutectic phases by a third phase. The mechanism of modification, as for any solidification phenomenon, must be considered primarily in terms of nucleation and growth. Although both nuclea-tion and growth mechanisms are required to explain all the phenomena observed in connection with the solidification of modified eutectics, various investigators have usually favored one or the other.7"16 It has been shown that modification of a binary eutectic can be effected by addition of a solute element that has greatly different distribution coefficients or k values in the two phases of the eutectic. Under these conditions, differences in the temperatures at the solid-liquid interfaces of the two phases retard the growth of one phase with respect to the other.4 It has also been shown that increased undercooling favors a transition from a rodlike eutectic to a globular eutectic.17 A mechanism proposed for the transition from lamellar to rodlike eutectics depends on the concept of constitutional super cooling.18 The modification of eutectic alloys may be of interest for high-temperature service as well as at room temperature. Although "high-temperature eutectic alloys" may appear to be a contradiction in terms, many eutectic systems, including those studied in this work, have melting points in excess of 2400°F. One of the mechanisms by which high-temperature alloys are strengthened is dispersion of a relatively brittle phase such as an oxide, carbide, or an inter-metallic compound throughout a ductile matrix. For a given volume fraction of dispersed phase, strength is increased by decreasing the size and spacing of the dispersed particles.19'20 Furthermore, room-temperature ductility may also be increased by changing the shape of a brittle dispersed phase from platelike to equiaxed or spheroidal.8 Overaging and redissolving of the secondary phase limit the maximum temperature to which precipitation-hardened alloys can be used. However, in a binary eutectic system, both phases coexist up to the melting point. Although all eutectic structures are not completely stable,21 a dispersion-hardened cast high-temperature alloy might result if a fine distribution of one of the eutectic phases could be obtained during solidification. An additional reason for interest in eutectic alloys is their excellent castability.22 Since eutectic alloys, like pure metals, freeze at a single temperature rather than over a range of temperatures, their castability is superior to solid-solution alloys with long liquidus to solidus ranges. The purpose of this research was to study the effects of small solute additions on the microstructure and mechanical properties of a number of high-melting-point eutectic compositions.

Jan 1, 1967

By R. C. Gould, A. M. Skov, L. F. Elkins

Comparison of long term decline in oil production during cyclic waterflooding or pressure pulsing of part of the Driver Unit with steady injection-imbibition flooding in the Tex Harvey area led to large expansion of flood in the Driver Unit on the steady injection basis. While the flood has been successful, the major problem has been attainment of satisfactory oil production rates in most of the wells. Large volume fracture treatments of low capacity wells were unsuccessful in achieving sustained increases in production. A two-section area in the Driver Unit has already recovered 620 bbl of oil per acre by waterflood but other areas have not performed so well. Sun Andres water containing 300 to 500 ppm H,S is sweetened to 0.5 to 1 ppm H,S by extraction with oxygen-free flue gas. This prevents contamination of gas produced in the area and apparently it has reduced corrosion in minimum investment, thin-wall, cement-lined water dktribution systems. Cement-lined tubing in injection wells has mitigated corrosion as effectively as thick polyvinyl chloride films have, and at less cost. Introduction As reported in the literature the Spraberry field of West Texas has presented unusual problems for both primary production and waterflood ing. Earlier information from the Spraberry Driver Unit included conception and evaluation of cyclic waterflooding or pressure pulsing in a nine-section pilot test as an aid to extraction of oil from the tight matrix rock and as a boost to normal capillary imbibition forces An additional 5 years' operation in that area, and performance of expanded steady injection water-flood, now covering a total of 68 sq miles, are reported herein. In addition, since the Driver Unit is one of the largest waterfloods in areal extent in the U. S., many operating experiences are presented for the benefit of engineers concerned with operation of other Spraberry floods or with other waterfloods where this reservoir technology and/or water handling technology may be adaptable in part. These include: (1) attempts to improve producing well capacity through large volume fracture treatments, (2) long-term performance of water treating plants utilizing oxygen-free flue gas to extract H,S from sour San Andres water, (3) performance of thin-wall cement-lined pipe in water distribution systems including comparison between those sections carrying raw San Andres water and those carrying treated water, and (4) comparison of performance of various lining materials and subsurface equipment in water supply and water injection wells. These experiences are reported without regard to whether results are good, bad or indifferent. Since the operations reported are limited to the techniques, materials, and equipment actually used in the Driver Unit, no comparison is possible with results of other approaches used in other Spraberry floods or in waterfloods generally under different conditions. However, an attempt is made to quantify these experiences as much as possible in the space available to permit other engineers to select those parts applicable to eheir problems. Background The Spraberry, discovered in Feb., 1949, is a 1,000-ft section of sandstones, shales and limestones with two main oil productive members—a 10- to 15-ft sand near the top and a 10- to 15-ft sand near the base, having permeabilities of 1 md or less and porosities of 8 to 15 percent. Extensive interconnected vertical fractures permitted recovery of oil on 160-acre spacing from this fractional-millidarcy sandstone, but they made capillary end effects dominant. Primary recovery by solution gas drive is less than 10 percent of oil in place, with most wells declining to oil production of a few barrels per day when reservoir pressures are still in the range of 400 to 1,000 psi. Partial closing of the fractures with declining reservoir pressure is believed to be the cause of such low production rates at these relatively high reservoir pressures. In 1952 Brownscombe and Dyes proposed that displacement of oil by capillary imbibition of water from the fractures into the matrix rock might significantly increase oil recovery from the Spraberry, overcoming otherwise serious channelling of water through the fractures." A pilot test conducted by the Atlantic Refining Co. during 1952 through 1955 indicated technical feasibility of the process; but low oil production rates averaging I5 to 20 bbl/well/D failed to create significant interest in large-scale waterflooding at that time." Humble Oil & Refining Co. conducted a highly successful 80-acre pilot test during 1955 through 1958 with

Jan 1, 1969

By M. Schwartz, S. K. Nash, R. Zeman

Knoop hardness in the rolling plane and in the longitudinal plane of hot-rolled and cold-rolled sheets of sublimed magnesiu?w was measured as a function of the angle between the long axis of the indenter and the rolling direction. These measurements were correlated with similar data taken on the (0001) and (1010) planes of a single crystal of magnesium where the hardness was measured as a function of the angle between the long axis of the indenter and the [1120] direction. The results were analyzed for compliance with the hypothesis of Daniels and Dunm to account for slip, and with a similar hypothesis to account for twinning. Some hardness anisotropy data are also presented for magnesium-indium and magnesium-lithium solid solution alloys. It is well known that the hardness of a crystalline specimen is different for its different surfaces, and also that the hardness is a function of direction within a single surface. Variations in hardness for single crystals have been found to be much larger than those for polycrystalline materials. Also, materials having low crystal symmetry were found to have a greater anisotropy of hardness than those of high symmetry. 0'Neill1 and Pfeil,2 using a 1-mm Brine11 ball, studied single crystals of aluminum and iron, respectively; and they found a variation of hardness of about 10 pct between readings taken along the principal crystallographic faces. Daniels and Dunn3 found that the Knoop hardness number varied about 25 pct as the long axis of the indenter rotated on the basal plane of a zinc single crystal. The variation on the (1450) plane was about 100 pct, and the average hardness on this plane was about twice that of the basal plane. They also studied the variation of hardness within the (loo), (110), and (111) faces of a single crystal of silicon ferrite and found variations of about 25 pct although the average values for these planes were almost identical. Single crystals of zinc were also studied by Meincke.4 He found that the Vickers hardness numbers varied about 30 pct depending on whether the axis of the indenter was parallel or perpendicular to the (1010) and (1110) planes. Mott and Ford,5 using a Knoop indenter, found a 25 pct variation in hardness on the basal plane of zinc. Crow and Hinsley6 studied heavily cold-rolled bronze, steel, brass, copper, and other metals. They found that the difference in hardness numbers based on the difference in the length of the diagonals of the Vickers indenter was from 5 to 12 pct. Some minerals and synthetic stones show a very large anisotropy of hardness. Robertson and Van Meter7 found the Vickers hardness of arsenopyrite to vary from 633 to 1148 kg per mm2. stern8 using the double-cone method on synthetic corundum found the hardness number to vary from 950 to 2070. And winchell9 reported a variation of hardness number from 184 to 1205 in kyanite. The variation of hardness as a function of direction in a given crystallographic plane in single crystals possesses a periodicity which is related to the symmetry of the lattice. Daniels and Dunn3 found a six-fold periodicity of hardness in the (0001) plane of zinc. They found that the hardness curves of silicon ferrite had a four-fold symmetry in the (100) plane, a two-fold symmetry in the (110) plane, and a six-fold symmetry in the (111) plane. Mott and Ford5 also reported a six-fold symmetry of hardness in the basal plane of zinc. And vacher10 found two-, four-, and six-fold periodicities of hardness in copper on the (110), (100), and (111) planes, respectively. The purpose of this paper is to report the results of an investigation on the anisotropy of hardness as a function of orientation in single crystals of mannes-ium, and samples of rolled magnesium, magnesium-indium, and magnesium-lithium solid solution alloys. The anisotropy of hardness of pure magnesium which had been hot rolled, and then cold rolled various amounts to fracture, was studied by means of Knoop indentation hardness numbers; and the results were correlated with the preferred orientation as determined by quantitative X-ray pole-figure data. A comparison was made of the hardness data obtained from the rolled sheets and those of single crystals of magnesium. In order to obtain a more fundamental understanding of the variation of hardness and of Knoop hardness testing, the data were analyzed by

Jan 1, 1962

By D. V. Edmonds, C. J. Beevers

Tensile tests were carried out on a! titanium containing 850, 1250, and 2700 ppm 0, and up to -500 ppm H. The tests were performed at -196", -78", 20°, 150°, and 300°C at a strain rate of -1.0 x 10??3 sec-1. Increasing oxygen content, increasing grain size, and decreasing test temperature resulted in enhanced embrittlement of the a titanium by the hydrogen additions. Metallographic observations showed that this can be correlated with the influence of these parameters on the introduction of cracks into the a! titanium by fracture of titanium hydride precipitates. CRAIGHEAD et al.1 reported that the hydrogen content normally found in commercial-purity a! titanium (60 to 100 ppm) was sufficient to cause a substantial lowering of the impact strength, and they attributed this embrittling effect of hydrogen to the precipitation of titanium hydride. Lenning et al.&apos; found that in commercial-purity a titanium there is an almost complete loss of impact strength at about 200 pprn H, which is approximately half the value needed to eliminate the impact strength of high-purity a titanium. They also showed that the presence of 3000 ppm hydrogen reduces the room-temperature tensile ductility of commercial-purity material to a value of the order of 10 pct; the corresponding hydrogen concentration for high-purity titanium is over 9000 ppm. It thus appears that the detrimental effect of hydrogen on the mechanical properties of commercial-purity titanium becomes evident at much lower hydrogen contents than for high-purity titanium. The main difference between the two types of a titanium might be expected to be the higher level of interstitial impurity in the commercial-purity grade. Jaffee et a1.3 studied the influence of temperature and strain rate on the hydrogen embrittlement of high-purity and commercial-purity ! titanium. In general, the behavior was the same for both materials; embrittlement was enhanced by decreasing temperature and increasing strain rate. Recent results from tests on commercial-purity a titanium containing 850 ppm O and varying amounts of hydrogen up to -500 ppm showed that the degree of embrittlement by hydrogen is intimately related to the fracture characteristics of titanium hydride precipitates.4 The present paper considers the interrelationship between the mechanical properties and micro-structural features of commercial-purity a! titanium containing 850, 1250, and 2700 ppm 0 and varying amounts of hydrogen up to -500 ppm. 1. EXPERIMENTAL PROCEDURE Three types of commercial-purity titanium supplied by IMI* were used in the investigation, and for the *Address: Witton, Birmingham 6, United Kingdom. purpose of this paper are designated Ti 115, Ti 130, and Ti 160. The principal impurity elements are given in Table I. The material was received in the form of 12.7 mm diam bars having a fully recrystallized structure. Tensile specimens with a round cross-section of 4.5 mm diam and a gage length of 15.2 mm were machined from the bars. In order to develop the same grain size (mean linear intercept of grain boundaries) in each of the three types the specimens were annealed under a dynamic vacuum of <10?5 mm Hg, Table 11. Specimen hydriding was carried out in a modified Sieverts apparatus;&apos; hydrogen was taken into solution at 450°C and after holding the specimens at this temperature for 24 hr they were furnace-cooled to room temperature at an average rate of -100 C deg per hr. By this method nominal hydrogen contents of 0, 50, 100, 250, and 500 ppm were introduced into specimens of Ti 115, Ti 130, and Ti 160 (100 ppm (wt) -0.5 at. pct). The actual hydrogen contents were calculated from the weight differences obtained by weighing the specimens before and after the hydriding treatment. Tensile tests were carried out at temperatures of -196", -78", 20°, 150°, and 300°C on a 10,000 kg In-stron machine at a nominal strain rate of -1.0 x 10-3 sec-1. Fractured specimens were sectioned in planes parallel to the tensile axis, mechanically polished to 0.25 µm grade of diamond paste, and then attack polished using a solution containing by volume 99 parts H2O, 1 part HF, and 1 part HNO3. Although the latter treatment unavoidably opened out cracks and voids visible after mechanical polishing, it did reveal the grain structure, titanium hydride morphology, and deformation twinning structure.

Jan 1, 1970

By F. M. d’Heurle

Films of molybdenum have been prepared by sputtering onto oxidized silicon substrates. The resistivity. lattice parameter, orientation, and grain size were studied as a function of substrate temperature and substrate bias. Under normal sputtering conditions, the resistivity of the films was found to be quite high (600 x 10 ohm-crn). However, with the use of the negative substrate bias of 100 v and a substrate temperature of 350°C, films weve produced with a resistivity of ahout twice that of bulk molybdenum. The lattice parameters measured in a direction nornzal to the surface of the films weve found to be gveatev than the bulk value. This was interpreted as being at least partly due to the presence of compressive stresses. The effects of annealing in an Ar-H atmosphere were studied in terms of diffraction line width, lattice parameter, and resistivity. BECAUSE of its relatively low bulk resistivity (5.6 x 106 ohm-cm)&apos; molybdenum is potentially interesting as a thin-film conductor in integrated circuits. An additional feature which makes it attractive for this purpose is its low coefficient of expansion (5.6 x KT6 per "c),&apos; which is fairly well matched to that of silicon (3.2 x 10 per c). It is possible to deposit molybdenum films by evaporation but generally films produced in this manner have a high resistivity. In order to achieve resistivities close to bulk value, Holmwood and Glang found it necessary to operate in a vacuum of about 107 Torr and to maintain the substrates at 600 C during film deposition. Sputtered molybdenum films have been examined by Belser et a1.7 and, recently, by Glang et al.&apos; This paper describes the results of an attempt to extend some of that work and examine the effects of annealing and getter sputtering on the physical and structural properties of the films produced. SPUTTERING APPARATUS AND PROCEDURE The apparatus used for most of the film sputtering work described here consisted of two "fingers" serving as anode and cathode, respectively, which were mounted within an 18-in.-diam glass chamber. A liquid nitrogen-trapped 6-in. diffusion-pump system was used to achieve a vacuum of about 1 x 107 Torr within the chamber prior to sputtering. The essential features of the equipment are shown in Fig. 1. Cathode and anode fingers are stainless-steel tubes isolated from the top and bottom plates by Teflon collars. In order to limit the discharge to the space between anode and cathode, each finger is surrounded by an aluminum hield, at ground potential, having an internal diameter 18 in. larger than the outside diameter of the finger. The cathode and anode fingers are 6 and 4 in. in diam, respectively. A 116-in.-thick sheet of molybdenum is brazed with a 10 pct Pd, 58 pct Ag, 32 pct Cu alloy to a copper disc which is mounted by means of screws and a large 0 ring onto the lower end of the cathode finger. The disc is cooled during sputtering by water circulation inside the finger. The use of several feet of plastic tubing for the water input and outputg reduces leakage to ground to less than 1 ma when the cathode potential is raised to 5 kv. The upper end of the anode finger is terminated by a brazed-on copper block. A variety of specimen holders can be easily mounted on the upper face of this block. Substrate heating or cooling is achieved by use of an appropriate unit attached to the lower face of the same block. Heating is achieved by means of cartridge-type heaters and cooling by copper coils fed with forming gas under pressure. The inner chamber of the specimen finger constitutes a small vacuum chamber of its own which is evacuated by an auxiliary mechanical pump in order to limit heating element oxidation and heat transfer by convection currents. An advantage of the finger arrangement is the absence of cooling and heating coils and wires within the main chamber. The stain less-steel shutter is useful to establish a discharge for cleaning the cathode at the beginning of each sputtering run. Water cooling of the shutter reduces heating and the out-gassing of impurities which might condense on the nearby substrates. Unless otherwise specified, the substrates used in these experiments were 1-in.-diam oxidized silicon wafe:s, 0.007 in. thick, having an oxide thickness of 6000A. The substrate holders were large copper discs onto the surface of which a number of molybdenum discs, 116 in. thick and 78 in. in diam, were brazed. The wafers were clamped to the molybdenum discs

Jan 1, 1967

By R. A. Wolfe, H. W. Paxton

Self-diffilsion coefficients for cr51 and Fe55 in 12 pct Cr-Fe and 17 pct Cr-Fe for Fe55 in chromium, and for Cr51 in vanadium have been measured. The results are compared with other values for the Fe-Cr system, and with the various theories of diffusion in hcc metals. Some empirical correlations are discussed between Do and Q in hcc systems, or, expressed differently, the constancy of ?G*/T solidus for seveval bcc metals and alloys is noted. It appears very probable that a vacancy mechanism is operative in bcc metals, hut this cannot he stated with certainty. THE great bulk of work on diffusion in metals, both experimental and theoretical, was for many years concentrated on those with close-packed and, in particular, fcc lattices.1,2 There appears to be little doubt that the mechanism of diffusion in these solids is vacancy migration, leading to mass transfer and in substitutional solid solutions to a Kirken-dall effect.3,4 For bcc metals, the picture is much less clear. The Kirkendall effect certainly occurs in several alloys.5-10 However, attempts to understand the factors contributing to the pre-exponential in the usual expression for the diffusion coefficient D =D, exp {-Q/RT) by extension of ideas useful in close-packed lattices have not always been successful. Zener,11 Leclaire,12 and Pound, Paxton, and Bitlerl3 have suggested that various forms of ring diffusion may be important in some bcc metals. For close-packed metals, Do is usually about 1 sq cm per sec and Q - 35Tm kcal per mole (Tm = melting temperature in OK). The theory of Pound et al. suggests for ring diffusion that Do may be about 10-4 and Q, although difficult to calculate with any precision, would be significantly less than 35 T,. The experimental results on self and solute diffusion in ? uranium14,15 and ß zirconium,10 and for solutes in 0 titanium,17 and possibly for self-diffu- sion in chromium below about 0.75 T,," gave some credence to this theory. However, not all bcc materials display low values of DO and Q, and the exceptions were not predicted by any theory. Furthermore, it has recently become apparent that, in bcc materials, log D is not always linear with T-l if a sufficiently wide range of temperature is studied.16,18 This variation may be such that Q may increase18,19 or decrease20 with increasing temperature. The present work was undertaken in an attempt to provide further diffusion data on bcc metals, and to try to understand the factors which contribute to differences in behavior between the various elements. For part of this work, the Fe-Cr system was chosen since it is of considerable technological importance, and data on 12 pct Cr and 17 pct Cr alloys appeared well worthwhile to supplement that existing for the remainder of the stern.18,22 The diffusion of Fe55 in chromium was studied as an example of a more or less "normal" tracer element in a possibly abnormal host lattice. Finally, no data were available for vanadium, the neighbor of chromium in the periodic table, because of lack of a suitable isotope so cr55 was used as a tracer in a few preliminary experiments. For convenience, we shall refer to elements whose Do and Q are low compared to those predicted by Zener&apos;s theory as "anomalous". PROCEDURE This investigation determined self-diffusion rates by means of radioactive tracers and the integral-activity method first utilized by Gruzin.23 In this method a thin layer of radioisotope of the diffusing element is plated or coated onto a planar surface of the diffusion sample, which is then given an isothermal-diffusion annealing treatment. The determination of an activity-penetration curve involves measuring the residual activity of the specimen after each successive layer or section has been removed parallel to the original planar surface. The method used here is essentially the same as that used by Gondolf18 and Kunitake.21 Two radioactive tracers, cr51 and Fe55, were used in this investigation. Diffusion coefficients were determined for the diffusion of one or both of these tracers in four different materials, viz., Fe-12 wt pct Cr alloy, Fe-17 wt pct Cr alloy, chromium, and vanadium. The diffusion samples had nominal dimensions of 1.5 cm diameter and 0.5 cm thickness. The grain size was several millimeters for the Fe-Cr alloys and at least 1 mm for the chromium and vanadium samples. Accurately planar surfaces

Jan 1, 1964

By G. Krauss, W. Pitsch

The fine structure of the bcc martensite formed in an Fe-33 wt pct ATi single crystal of arrstenite is sho~on by transmission electron microscoPy to consist of combinations of transformation twins, stacking faults, deformation twins, and regular arrays of parallel screw dislocations. These structures constitute evidence for the multiple lattice-invariant deformations which operating during the formation of martensite could produce the real habit-plane scatter measured by a two-surface analysis of the plates formed in the single crystal of this investigation and reported in the literature for other Fe-Ni rnartensites. CRYSTALLOGRAPHIC theories1,2 of martensitic transformation show that the habit plane of martensite in a parent lattice is dependent in part upon an inhomogeneous distortion or lattice-invariant deformation which takes place on a fine scale within a martensite plate during its formation. Several recent theoretical papers3,4 have addressed themselves to an analysis of a wide variety of conceivable lat-tice-invarient deformations and the habit planes which they produce, while experimental investigation have been concerned with either the measurement of habit planes or the description and identification of the martensitic fine structure which reflects the nature of the lattice-invariant deformation operating during transformation. In Fe-Ni alloys with subzero Ms temperatures, the group of alloys with which this paper concerns itself, habit planes have often been found to scatter an amount greater than might be expected from possible experimental errors,5-7 and fine twinning has been identified as a major constituent of the fine structure of martensite.8-11 It has been suggested3,4 that more than one type of invariant shear occurs during martensitic transformation. This possibility has been experimentally supported12,13 by the observation of both dislocation configurations and twinning in a single martensite plate. The purpose of this paper is to report additional evidence for multiple lattice-invariant deformations in martensite and so to account for the real scatter in the habit planes of the martensite plates formed in Fe-Ni alloys. EXPERIMENTAL PROCEDURE The Fe-Ni single crystal was produced by pulling a high-purity iron and nickel charge through a single-crystal vacuum furnace in an alumina crucible. The crystal was double-melted to promote homogeneity and to increase its size by further additions on the second pass. In its final form the crystal was 4 cm in diam and 5 cm long. The nickel and carbon contents were analyzed at 32.9 and 0.006 wt pct, respectively. The austenite of this alloy first transformed to martensite by bursts at about -120°C, and, to preserve as much of the austenite as possible, all transformation was performed just below -120°C. Some observations were made on transformed samples which had been heated for 2 min at 340°C. It is assumed that the features of the martensite of these samples, Figs. 1 and 4, are the same as those of the as-quenched martensite. Orientation of the crystal by X-ray diffraction established 10.735 0.609 0.3161? as the axis of the crystal, an orientation that was checked within 2 deg by neutron diffraction. Further checks by electron diffraction of samples cut normal to the axis confirmed this orientation within the larger limits of error inherent in electron diffraction of thin foils. The X-ray orientation was the one used for the two-surface analysis of the martensite habit planes. A two-surface analysis was performed on the quadrant of the single crystal which had been oriented by both X-ray and neutron-diffraction techniques. Photomicrographs at X50 were made on two surfaces along an edge 2 cm long. Fiducial marks and the fact that many of the plates were almost completely surrounded by retained austenite made good matching of individual plates on two surfaces possible. The habit-plane trace on a surface was taken as the best line parallel to the long axis of a plate. A measure of the accuracy afforded by this criterion was provided by a family of very large plates which appeared at intervals along the entire 2 cm length of the edge. The plates all had habit-plane traces within 2 deg of one another. Many of the plates did not show midribs and, therefore, the use of midribs7 to represent habit-plane traces was not feasible in this investigation. The over-all experimental accuracy is estimated to be better than ±2 deg. Samples for transmission examination in a Siemens Elmiskop I at 100 kv were prepared by cutting 2-mm-thick discs from the single crystal, removing about 0.5 mm by chemical polishing,14 trans-

Jan 1, 1965

By F. I. Grace, L. E. Murr

The mechanical responses and residual defect structures in 70/30 brass and type 304 stainless steel following explosive shock loading and cold reduction by rolling have been studied. A distinct relationship was observed to exist between the residual mechanical properties and micro structures observed by transmission electron microscopy. Shock-loaded brass deformed primarily by the formation of coplanar arrays of dislocations and stacking faults at lower pressures, and twin-faults (deformation twins and €-martensite bundles) at higher pressures (> 200 kbar). The micro -structures of cold-rolled brass were characterized by dense dislocation fields elongated in the rolling direction. Stainless steel was observed to deform by the formation of dense arrays of stacking faults at lower shock pressures and twin-faults at high shock pressures (>200 kbar). Lightly cold-rolled stainless steel deformed similar to low Pressure shock-loaded stainless steel, but transformed to a&apos; martensite in heavily cold-rolled stainless steel. Discontinuous yielding was observed for the heavily cold-rolled stainless steel, and stress reluxution in the weyield region for cold-rolled and shock -loaded stainless steel was interpreted as an indication of the ability of twin-faults and stacking faults to act as effective barriers to dislocation motion. A simple model for the formation of the planar defects and a&apos; martetnsite is presented based on the propagating of Shochley partial and half-partial dislocations. A considerable effort has been expended over the past decade in an attempt to elucidate the response of metallic-crystalline solids to the passage of a high velocity shock wave (e.g., smith,&apos; Dieter,2 and zukas3). While it has been possible to obtain relevant information pertaining to the residual defect structures and mechanical properties, there have been few rigorous attempts to draw a direct comparison between these structures and properties. In addition, numerous investigators have recently observed the occurrence of deformation twinning in shock deformed fcc metals (e.g., Nolder and Thomas,4 and Johari and Thomas5), but little attempt has been made to elucidate the mechanisms of formation of these defects. Comparative data for metals deformed by shock-loading and the same metals deformed by more conventional modes of deformation such as cold-reduction by rolling is also generally lacking. The present investigation therefore has the following objectives: 1) to examine the mechanical properties of some explosively shock loaded and cold-rolled fcc metals of low stacking-fault energy as a function of their residual substructures; 2) to present a simple model for the formation twin-faults and related defect structures in the low stack-ing-fault energy materials of interest (70/30 brass, ySFg= 14 ergs per sq cm; and 304 stainless steel, ySF = 21 ergs per sq cm); 3) to make some deductions with regard to the residual characteristics of dislocation and planar defect substructures in cold rolled and shock loaded 70/30 brass and type 304 stainless steel. In particular, it was desirable to characterize the residual hardening effects of particular deformation substructures. I) EXPERIMENTAL PROCEDURE Sheet samples of 70/30 brass (0.005 and 0.15 in. thick; annealed at 659°C for 2 hr) and type 304 stainless steel (0.007 in. thick; annealed 0.25 hr at 1060°C) of nominal compositions shown in Table I were cold-rolled in one direction only to produce reductions in thickness of 15, 30, 45, 60, and 75 pct in the brass; and 5, 15, 25, 35, and 45 pct in the stainless steel. Identical sheet samples in the annealed (unrolled) state were subjected to plane compressive shock waves to various peak pressures ranging from 0 to 400 kbar in the brass and 0 to 425 kbar in the stainless steel; and with a constant peak pressure duration of approximately 2 microseconds. A detailed description of the shock loading technique has been given previously.6 Tensile specimens 1.0 in. in length and 0.125 in. in width were cut from the cold-rolled sheets (tensile axis parallel to the rolling direction), and the shock-loaded sheet specimens. Stress (load)-strain (elongation) measurements on the tensile specimens were made on a Tinius-Olsen load-compensating tensile tester using a strain rate of 2.7 x 10-3 sec-1. Tensile tests were repeated at least twice, giving essentially the same results. Stress relaxation measurements in the preyield region were also made using an initial strain rate of 5.4 x 10-4 sec-1. In addition to tensile and stress relaxation measurements, Vickers microhardness measurements were made on all samples. A total of 100 microhard-ness readings were obtained for each specimen following a light electropolish to ensure uniform surface conditions for all tests. The hardness averages ob-

Jan 1, 1970

By Clarence O. Babcock

Model pillars of limestone, marble, sandstone, and granite, with length-to-diameter (LID) ratios of 3, 2, 1, 0.5, and 0.25 (0.286 for granite), were broken in axial compression to determine to what extent an increase in end constraint increased compressive strength. Radial end constraints of 13 to 23% of the average axial stress in the pillar, produced by solid steel rings bonded with epoxy to the ends of dogbone-shaped specimens, increased compressive strength somewhat above that of cylindrical pillars without ring constraint. However, when the results were compared with those obtained by other investigators for straight specimens of several rock types taken collectively, with LID ratios greater than 0.5, the resulting strengths were not significantly different. Thus, the amount of end constraint produced by the solid steel rings was about the same as that produced by the friction from the steel end plates. In other tests, a radial prestress of 3000 or 5000 psi was applied prior to axial loading by adjustable hardened steel rings to increase the constraint above that obtained for the solid rings. The average radial constraint stress, expressed as a percentage of the average axial pillar stress at failure for the 3000 psi prestress, was 54.3% for limestone, 40.3% for marble, 44.7% for sandstone, and 23.4% for granite. The average radial constraint stress, expressed as a percentage of the average axial pillar stress at failure for the 5000 psi prestress, was 74.2% for limestone, 51.2% for marble, 61.6% for sandstone, and 29.7% for granite. These constraints increased the compressive strength significantly above the strength of straight specimens and solid-ring constrained specimens. These results suggest that large horizontal stresses in orebodies mined by the room-and-pillar method should increase the strength of the pillars and allow an increase in ore recovery by a reduction of pillar size when major structural defects are absent. One important objective of the U.S. Bureau of Mines (USBM) mining research program is the rational design of mining systems. In the design of room-and-pillar mining operations, pillar strength is a fundamental variable. It is customary to estimate this strength from uniaxial compression tests of rock samples and to correct this value for the length-to-diameter (LID) ratio of the in-situ pillar. This method of estimating pillar strength corrects for pillar shape but does not consider the effect of a large horizontal in-situ stress field that sometimes exists in underground formations. The purpose of the work covered in this report was to determine to what extent the compressive strengths of model pillars of relatively brittle rock loaded in axial compression were affected by lateral end constraint. In previous work, Obert l used solid steel rings bonded to the ends of dogbone-shaped specimens to study the creep behavior of three quasi-plastic rocks -salt, trona, and potash ore - during a test period of 1000 hr. These rings provided radial constraint during the loading cycle of 20 to 50% of the axial stress for specimens with LID ratios of 2, 0.5, and 0.25. He concluded that (1) "for a quasi-plastic material the end constraint strongly affects the specimen strength, and (2) as D/L increases (length-to-diameter decreases), the specimens lose their brittle characteristics and tend to flow rather than fracture." He also concluded that model pillars constrained by rings were better for use in predicting the strength of mine pillars than either cylindrical or prismatic specimens. This conclusion appears to be valid where mine pillars, roof, and floor are a single structural element. In the present study, 460 specimens of four relatively brittle rocks — limestone, marble, sandstone, and granite - were tested to failure. The study consisted of two parts: (1) the effect on the compressive strength of end constraint produced during the axial loading cycle by solid steel rings bonded with epoxy to the ends of the specimens, and (2) the effect on the compressive strength of increased end constraint produced in part by a prestress applied prior to axial loading and in part by lateral expansion of the specimen during the loading cycle. The first part of this study was reported in some detail earlier.2 EXPERIMENTAL PROCEDURE AND EQUIPMENT Model rock pillars of the sizes and shapes shown in Fig. 1 were broken in axial compression when the ends were constrained as shown in Fig. 2. he straight specimens were broken without ring constraint. The specimens of dogbone shape were broken with (1) solid

Jan 1, 1970

By Nicholas J. Grant, John S. Benjamin

A series of composite alloys containing a high volume of NiAl, Ni3Ah or CoAl, bonded with 0 to 40 vol pct of a ductile metal phase, were prepared by powder blending and hot extrusion. The binder metals were of four types: pure nickel or cobalt, near saturated solid solutions of aluminum in nickel and cobalt, type 316 stainless steel, and niobium. Sound extrusions were obtained in almost all instances. Studied or measured were the following: interaction between the alunzinides and the binders, room-temperature modulus of rupture values, 1500° and 1800°F stress rupture properties, hardness, structure, and oxidation resistance. Stable structures can be produced for 1800°F exposure, with interesting high-temperature strength and good high-temperature ductility. Oxidation resistance was excellent. A large number of experimental investigations have been made of the role of structure on the properties of cermets and composite materials. Gurland,1 Kreimer et al.,2 and Gurland and Bardzil3 have indicated the preferred particle size in carbide base cermets to be about 1 µ, with a hard phase content of 60 to 80 vol pct. The optimum ductile binder thickness was noted to be 0.3 to 0.6 µ.1 Complete separation of the hard phase particles by the binder is important in reducing the severity of brittle fracture.&apos; The purpose of the present study was to produce structures comparable to the conventional cermets, using a series of relatively close-packed intermetal-lic compounds rather than carbides as the refractory hard phase, and to study the effects of binder content and composition on both high- and low-temperature properties. The selected intermetallic compounds were particularly of interest because of the potential they offered in yielding room-temperature ductility. The highly symmetrical structures are known to possess high-temperature ductility and room-temperature toughness. Based on a ductile binder, the alloys were prepared by the powder-metallurgy route to avoid melting and subsequent alloying of the matrix, and were extruded at relatively low temperatures. It was expected that the composite alloy would retain useful ductility. In contrast, infiltration and high-temperature sintering led to alloying of the matrix and to decreased ductility. The systems Ni-A1 and Co-A1 were selected for this study. In the Ni-A1 system the compounds NiA1, having an ordered bcc B2 structure, and Ni3Al(?1), having an ordered fcc L12 structure, were chosen. In the system Co-A1 the intermetallic compound CoAl with an ordered bcc B2 structure was used. ALLOY PREPARATION The intermetallic compounds, see Table I, were prepared by using master alloys of Ni-A1 and CO-A1, with additions of either cobalt or nickel to achieve the desired compositions. The master alloy in crushed, homogenized form, was melted with pure nickel or cobalt in an inert atmosphere, cold copper crucible, nonconsumable tungsten arc furnace. The resultant intermetallic compounds were homogenized at 2192°C in argon, crushed, and dry ball-milled in a stainless mill to -100 and -325 mesh for the Ni-A1 compounds and to -325 mesh for the CoAl compound. Finer fractions were separated for some of the composite alloys. Several ductile binders were utilized. These included Inco B nickel, 5µ ; pure cobalt, 5 µ, from Sher-ritt Gordon Mines, Ltd.; fine (-325 mesh) niobium hydride powder; fine (15 µ) type 316 stainless-steel powder; and near-saturated Ni-A1 and Co-A1 solid-solution alloys, also in fine powder form. The niobium hydride was decomposed above about 700°C in processing of the compacts in vacuum to produce niobium powder. The Ni-7.1 pct A1 and the Co-5.3 pct A1 solid-solution alloys were prepared from pure nickel or cobalt and pure aluminum by nonconsumable tungsten arc melting under an inert atmosphere. The ingots were homogenized, lathe-turned to fine chips, and dry ball-milled in air to -325 mesh powder. These solid-solution alloys are designated NiSS and CoSS; see Table I. Subsequently the hard and ductile phases were dry ball-milled as a blend. Experiments clearly established the need to coat the hard particles with the ductile binder to optimize subsequent hot compaction by extrusion. Ordinary dry mixing usually resulted in nonhomogeneous alloys which were quite brittle. Conventional cermets are consolidated by liquid phase sinteiing or infiltration, which resulis in undesirable and uncontrolled alloying of the binder phase. For this study, a loose (unsintered) powder-extrusion process was emploved, minimizing reactions between binder and hard particle, thereby permitting much greater control of composition and structure. The constituent powders were first mixed in the desired

Jan 1, 1967

By George B. Clark

Many basic engineering principles of all four phases of mining operations, namely, prospecting, exploration, development, and exploitation, can be analyzed better in terms of quantitative geology. Geological data from both field and laboratory will also complement scientific methods now being developed. THE geological data emphasized so successfully in prospecting for new deposits, that is, structural controls, strength of solutions, and type of mineralization, are basically those required for successful exploitation. In the mining of newly discovered deposits the most economical methods should be employed as early as possible to keep the overall cost per unit produced at a minimum and to permit maximum extraction of valuable minerals. A crucial question is: How can geological data be translated into useful quantitative results which will aid in achieving this end? H. E. McKinistry&apos; has suggested that a solution may be reached in one of two ways: 1—the usual approach, use of judgment based on experience; or 2—mathematical calculations and tests on models, both subject to certain limitations. He also suggests that in addition to better use of geology more case data and theoretical data are needed on which to base sound judgment. Further research, therefore, is necessary. Perhaps in this field the emphasis should be on more specialization in mining methods and ground movement by men with thorough training in physics, engineering, geology, and underground mining. These specialists would be equipped to point out the most economical and scientific methods of exploitation. Selection of a stoping method is governed by the amount and type of support a deposit will require in the process of being mined, or by the possibility of employing the structure of the deposit to advantage in mining the ore by a caving method. In addition to these factors there are others which almost invariably influence the choice of an economical method of mining:&apos; 1—strength of ore and wall rocks; 2—shape, horizontal area, volume, and regularity of the boundaries of the orebody, and thickness, dip and/or pitch of the deposit and individual ore shoots; 3—grade, distribution of minerals, and continuity of the ore within the boundaries of the deposit; 4—depth below surface and nature of the capping or overburden: and 5—position of the de- posit relative to surface improvements, drainage, and other mine openings. In the final analysis it is usually necessary to disregard the less important of these factors to satisfy the requirements of the more important. Because of the variation of geological conditions throughout and surrounding the deposit, no mining method will be everywhere ideally applicable to the conditions encountered in one ore deposit. The immediate problem is to interpret the above physical characteristics of deposits in terms of geological characteristics. Very few quantitative geological data are available on the factors related to a choice of mining methods. However, there are many descriptive data in mining and geological literature which collectively show how important an effect details of geology have upon all phases of mining operations. The following categories of basic mining methods were investigated to establish the geological factors that have affected their successful application: 1— open stopes with pillars; 2—sublevel stoping; 3— shrinkage stoping; 4—cut-and-fill stoping; 5— square-set mining; 6—top slicing and sublevel caving; and 7—block caving. It should be noted that the first five of these methods are listed in the order of increasing support requirements. Mines were selected as examples only where geological descriptions were complete enough to warrant their use. A study of the geological factors involved in mining operations led to a choice of the following classifications, employed in Table I: 1—structural type of orebody; 2—dimensions (geometry); 3— country rock (type); 4—faulting, folding, and fracturing; 5—alteration of ore and rock; 6—type of mineralization; and 7—geological factors determining mining method (summary). Of these factors only one yielded results that can be defined from available data in a quantitative manner, i.e., dimensions of the deposit. These are the most reliable guides that can be used in selection of suitable mining methods. They are, in general, the properties of geologic structure most difficult to evaluate by studies of models, pho-toelastic studies, and other laboratory methods, all of which are at present more limited in their applications than the geologic method. Application of geology has proved a reliable guide in other phases

Jan 1, 1955

By W. S. Hyler, L. W. Berger, R. I. Jaffee

Hydrogen additions of 390 ppm to A-55 titanium and 368 ppm to Ti-8 pet Mn have no deleterious Hydrogenadditionseffect on the unnotched and notched rotating-beam fatigue properties of these materials. &apos;These amounts of hydrogen, however, are sufficient to cause severe notch-impact thesematerials.embrittlement in A-55 titanium and pronounced loss of tensile ductility in Ti-8 pet Mn. The lack of embrittling effect in fatigue in the latter alloy is consistent with the postulated strain-aging mechanism of hydrogen embrittlement in a-ß alloys. There is a significant strain-agingincrease in the unnotched endurance limit of A-55 titanium with the addition of hydrogen. This increase may be explained as the result of internal heating effects which would dissolve the hydride and cause solid-solution strengthening. TITANIUM and its alloys may be seriously embrittled by relatively small amounts of hydrogen. The form which this embrittlement takes has been shown to vary with alloy type. The a alloys, for example, suffer most strongly from loss of notch-bend impact toughness&apos; when sufficient hydrogen is added, and this effect has generally been associated with the presence of hydride phase in the micro-structure. In a-ß alloys, on the other hand, hydrogen is most detrimental to tensile ductility in slow-speed tests,2-1 and the embrittlement may be detected in a most convincing manner by means of rupture tests at room temperature. This particular kind of embrittlement has not been associated with a change in microstructure, but has been classified rather generally as associated with a strain-aging type of mechanism.&apos; In the present paper, the effect of an embrittling amount of hydrogen on the rotating-beam fatigue properties of both an a and an a-ß titanium alloy is covered. For this study, annealed commercially pure (A-55) titanium was chosen as an a alloy, and equilibrated and stabilized Ti-8 pet Mn as representative of a typical a-ß alloy. Nominal hydrogen levels of 20 and 400 ppm were evaluated, the latter amount having been shown previously to be severely detrimental to the impact toughness of commercially pure titanium and to cause pronounced strain-aging embrittlement in the Ti-8 pet Mn alloy. The only report of the effect of hydrogen on the fatigue properties of titanium is given by Anderson et al.,° in which a push-pull type of fatigue test was conducted on as-received commercial-purity titanium sheet. Much scatter was found in the results, but generally the presence of hydrides slightly decreased the fatigue strength of unnotched specimens in the longitudinal direction. The results of notched tests were masked too greatly by scatter to be significant. Experimental Procedure Preparation of Materials—Analyses of the A-55 titanium and the Ti-8 pet Mn alloy used in this investigation are given in Table I, which indicates the 8 pet Mn alloy to be more nearly a 6 pet Mn alloy. This alloy will be referred to as Ti-8 pet Mn, however, since this is the commercially designated composition. Both alloys were received in the form of5/8-in. diam rod and, after suitable surface preparation, 5-in. lengths were vacuum annealed at 820°C. Half of the rods for each material were then hydrogenated at 820°C to a nominal hydrogen content of 400 ppm. The hydrogenated and vacuum-annealed A-55 rods were hot swaged at 700°C from 5/8-in. diam to 1/4-in. diam, and then annealed 1 hr at 800°C and air cooled prior to preparation into test specimens. Fabrication of the Ti-8 pet Mn alloy was by hot swaging to 3/8-in. diam at 760" and then 1/4-in. diam at 704°C. This material was then annealed 1 hr at 704", followed by furnace cooling to 593"C, and finally air cooling to room temperature. Evaluation—In order to examine more completely the effects of hydrogen on the particular materials studied, slow-speed tensile and notch-bend impact properties were determined in addition to fatigue data. Tensile specimens were of the standard ASTM type with a reduced section of 1/8-in. diam and a gage length of 1/2 in. A subsize cylindrical Izod specimen was used for impact tests. These specimens had a 45" notch with a 0.005-in. radius and a 0.150-in. root diam, and the stress concentration factor of this notch in bending was Kr = 3. Both the ten-

Jan 1, 1959

By Charles F. Hickey, Eric B. Kula

Thermomechanical treatments applied to the maraging steels include a) cold working in the austenitic condition at 650°F, followed by transformation to martensite and aging, b) cold working in the murtensitic condition and aging, and c) cold working in the aged condition with and without subsequent reaging. The strength increases in these steels are very small compared to the increases observed in conventional carbon and alloy steels. The changes that are observed are compatible with the strengthening mechanisms operative during thermomechanical treatment of conventional steels, however. Differences are caused by the absence of a carbide precipitate and the low work-hardening rate in both the solution-treated and the aged conditions. ThE 18 pct Ni maraging steels represent a class of steels which are finding great interest for high-strength applications.1~2 They are essentially carbon-free, and contain 7 to 9 pct Co, 3 to 5 pct Mo, and 0.2 to 0.8 pct Ti. Although austenitic at elevated temperatures, they can be air-cooled to room temperature to form a martensite, which because of the absence of carbon is relatively soft. On subsequent reheating age hardening occurs and strength levels of 250 to 300 ksi yield strength can be attained. These steels appear to be particularly suitable for studying the response to various thermome-chanical treatments for additional reasons other than the obvious one of attempting to improve their already attractive properties. Thermomechanical treatments can be defined as treatments whereby plastic deformation, generally below the recrystal-lization temperature, is introduced into the heat-treatment cycle of a steel in order to improve the properties. With an absence of intermediate transformation products on air cooling the maraging steels have good hardenability and hence can readily be cold-worked in the austenitic condition prior to transformation to martensite. Further, they can be worked in the martensitic condition prior to aging, and even can be deformed in the fully aged condition. Finally, it is of interest to compare their re- sponse to that of the more conventional alloy and carbon steels, where the role of carbides is important in the strength increase by thermomechani-cal treatments. The thermomechanical treatment of conventional steels has been the subject of a recent review.&apos; I) MATERIALS AND PROCEDURE The steel used in this investigation was a commercially produced vacuum-melt heat, which had been rolled to 0.090 in. and mill-annealed. The composition of the alloy was as follows: 0.02 C, 0.08 Mn, 0.10 Si, 0.009 P, 0.009 S, 18.96 Ni, 7.34 Co, 5.04 Mo, 0.29 Ti, 0.05 Al, 0.004 B, 0.01 Zr, and 0.05 Ca. Unless otherwise stated the heat treatments used were the standai-d solution treatment at 1500°F for 1 hr, air cool, followed by a 900°F, 3 hr age. In this condition, the material exhibited 232 ksi yield strength and 239 ksi tensile strength. Mechanical properties were determined by Vicker&apos;s hardness measurement (20 kg) and by tensile tests on standard 1/2-in.-wide, 2-in.-gage-length sheet tensile specimens. Notch tensile tests were run using the 1-in.-wide NASA type, edge-notched specimen.4 Fracture-toughness determinations were made on 3-in.-wide, center-notched, fatigue-cracked specimens, following the recommendations of the ASTM Committee on Fracture-Toughness Testing.4 An electric-potential technique was used for measuring the crack size at the onset of rapid crack propagation5 which is necessary for calculations of Kc, the critical stress-intensity factor under plane-stress conditions. The critical stress-intensity factor under plane-strain conditions KI, was also calculated, using the stress at which the first observable crack growth occurred. 11) RESULTS A) Cold-Worked in the Austenitic Condition. The reported M, temperature for the 18 pct Ni maraging steel is about 310°F.1 Therefore, a temperature of 650°F was selected as suitable for rolling in the austenitic condition. Specimens were solution-treated at 1500°F for 1 hr, air-cooled to 650°F, and rolled varying percentages from 0 to 60 pct, at 20 pct reduction per pass. Tensile and hardness properties after aging at 900°F for 3 hr are shown in Fig. 1. The tensile strength increases from 253 to 271 ksi and the yield strength from 247 to 265 ksi as a result of a reduc-

Jan 1, 1964

By R. W. Bartlett

The rates of oxidation of tungsten have been determined at temperatures between 1320" and 3170°C and oxygen pressures to 1 amn using a surface -recession measurement technique. Above approximately 2000°C and 10-6 atm the rate is independent of temperature and can be calculated from gas collision theory assuming a constant reaction probability, e, of 0.06. Oxygen molecules react at surface sites where oxygen atoms have previously chemisorbed. This provides a direct pressure dependence at low pressures but at high pressures tungsten oxide molecule s form an adjacent gas boundary layer which lowers the PO2 at the tungsten surface. A correction for this effect using free-convection theory fits the rate data over the entire oxygen-pressure range from 10-8 to 1 atrn as well as data using O2-A mixtures. Below 10-6 atrn and above 2000°C, e decreases with increasing temperature because of desorption of oxygen atoms. Below 2000°C the rate decreases with decreasing temperature at all oxygen pressures following an apparent activation energy of 42 kcal per mole and depending on (Po2)n with n varying between 0.55 and 0.80. MOST of the previous tungsten oxidation studies have employed gravimetric methods and have been limited to temperatures below 1000°C where the weight loss associated with evaporation of tungsten oxides is negligible compared with the weight gain from oxidation.&apos; At higher temperatures, oxygen-consumption rates have been determined from pressure measurements, usually at constant flow rates, by Langmuir,2 Eisinger,3 Becker, Becker, and Brandes,4 and Anderson.5 The sensitivity of this method decreases with increasing pressure and, with the exception of Langmuir&apos;s work, these investigations were confined to pressures below 10-6 atm. Above approximately 1300°C, depending on the oxygen pressure, the rate of oxide evaporation is greater than the oxide-formation rate and the recession of the tungsten surface can be measured optically without interference from an oxide layer. This was first done by Perkins and crooks6 who heated tungsten rods in air pressures from 1 to 40 torr at temperatures between 1300" and 3000°C. The present investigation of the oxidation kinetics of tungsten at high temperatures emphasizes oxygen pressures from 10-6 to 1 atm. This is the range of interest for earth atmosphere re-entry applications of tungsten for which little data were previously available. APPARATUS The apparatus is a modification of the type used by Perkins and crooks.&apos; Ground tungsten seal rods, 6 in. long by 0.125 in. diam, were mounted vertically between two water-cooled electrodes, one fixed and the other having free vertical travel. The movable counter-weighted electrode is prevented from undergoing horizontal displacement by three sets of runners mounted at 120-deg intervals. Electrical contact is made by means of a water-cooled mercury pool. A 24-in. vacuum bell jar having a volume of approximately 267 liters was used as the reaction chamber with the sample holder mounted in the middle of the chamber. Power was supplied from an 800-amp dc variable power supply. Temperature readings were made by means of a Latronics automatic two-color recording pyrometer. With this instrument, corrections for emissivity are not necessary provided the spectral emissivi-ties at two closely spaced wavelengths are equal. Supporting measurements were made with a micro-optical pyrometer corrected for emissivity of bare tungsten and window absorptivity. The micro-optical pyrometer was calibrated against a National Bureau of Standards calibrated tungsten lamp and both pyrometers were periodically checked against the melting points of tungsten and molybdenum using the oxidation apparatus. Above 10-6 atm, pressures were measured with an Alphatron gage calibrated against a McCleod gage. At 10-6 atm, a hot-filament ionization gage was employed. A magnified image of the self-illuminated tungsten rod was formed using a 360-mm objective lens mounted outside the bell jar. When the experiment exceeded 1 hr, the image was focused on a ground-glass plate about 10 ft from the tungsten rod at about X8 and the recession of the thickness of this image was monitored with a Gaertner cathe-tometer. When faster rates were encountered, a 35-mm time-lapse cinecamera with a telephoto lens and bellows extension was substituted for the ground-glass plate and cathetometer. Diameter recession rates were determined from the photograph image projected on the screen of an analytical film reader. EXPERIMENTAL PROCEDURE After installing the rod in the apparatus and cleaning it with acetone, the system was evacuated to 5 1 x 10-5 torr. Before oxygen was introduced,

Jan 1, 1964

By Marius S. Darrow, William B. White, Rustum Roy

The PbS-PbTe systen has been studied by quench-ing and D.T.A. techniques f?om 400&apos; to 1150°C. Runs were made in evacuated silica tubes so that all equilibria are at the vapor pressure of the system. Lattice parameters of the quenched salnples , measured by X-ray diffraction, show a complete crystalline-solution series existing over a narrow temperature range between approximately 805" and 871°C. An exsolution dome extends from a maximum of about 805"C (approximately 30 mole pct PbTe) to 1 and 96.5 pet PbTe at 400°C. A narrow melting region, deternined by D.T.A., extends form 918c (mp PbTe), The shapes of the liquides and solidus curves imply the existence of a minimum at 871°C at approximately 65 pct PbTe. THe exact composition of the minimum could not be established due to the very narrow two-phase region. At compositions containing less than 50 pet PbTe, liquidus temperatures begin to increase, while the solidus remains almost flat to about 15 mole pet PbTe before beginning to vise toward the mp of PbS (1075 C). LEAD sulfide and lead telluride are isostructural (NaC1 type) semiconductors whose electrical and optical properties have been extensively studied and used in recent years. If appreciable crystalline solution exists between these compounds, the variation of physical properties with composition could be of interest. The purpose of this investigation was to determine the extent, if any. of crystalline solution, and to obtain the phase diagram for the system. To the knowledge of the authors, only three studies of the system PbS-PbTe have been reported, and, in chronological order, each investigation found an increasing amount of crystalline solution. In 1956, Yamamoto reported finding no evidence of crystalline solution between the compounds. Sindeyeva and Godov-ikov,&apos; in 1959, found very limited crystalline solution. but only under conditions of excess tellurium concentration. Finally Melevski s3 investigation in 1963 indicated that one solid phase exists in the region from PbS to 7 pct PbTe and from 82 pct PbTe to PbTe at 886&apos;C, with an eutectic at 55 pct PbTe at that temperature. Detailed data on the solvus boundary were not given. EXPERIMENTAL EQUIPMENT AND MATERIALS Commercially produced PbTe and PbS powders were used as starting materials. Batches of specific mole percent composition were accurately weighed and mixed in a plastic bottle, in a shaker mill. An analy- sis of impurity content is given in Table I for pure PbS and PbTe and for two randomly selected batches after the powders were mixed. Individual samples, ranging in weight from 0.2 to 0.5 g, were sealed in evacuated silica tubes which had been thoroughly washed and rinsed with acetone and distilled water. Thus all data taken were at the pressure of the system. Subsolidus relations were studied down to 400°C by heating the samples in a vertical tube furnace for 24 hr. The sealed tubes were quenched in water with quench time from the hot zone not exceeding 1 sec. Temperatures were measured by a chromel-alumel thermocouple and controlled to 53°C for most runs. The number and composition of phases present were determined from powder X-ray diffraction patterns taken at room temperature on a Norelco diffractome-ter, using silicon as an external standard. Above 850°C quenching techniques were, in general, found to be unsatisfactory, and differential thermal analysis (D.T.A.) was used to determine melting relations. The evacuated tubes were recessed about 1 cm at one end to accommodate the differential thermocouple. Al203 was used as the reference material in a similar tube containing the other side of the differential couple. For temperature measurements, a separate thermocouple was placed in the recess of the tube containing the sample to be measured, thus providing an opportunity to obtain thermal, as well as differential, analysis. All thermocouples for these measurements were Pt-Pt 10 pct Rh. Temperature and differential curves were recorded separately on synchronized strip-chart recorders. Thermocouples and recording equipment were calibrated using NaCl and gold standards, using the melting points 801" and 1063 C, respectively, which span most of the temperature range of interest. Heating and cooling rates generally were from 4 to 7°C per min. It was found, in fact. that rates ranging from 1.5 to 25°C per min did not significantly change the data obtained.

Jan 1, 1967

By Edna A. Dancy, Gerhard J. Derge

The specific conductance of FeOx,-CaO melts in contact with iron was found to decrease from 200 ohm-1 cm-1 for FeO, to 40 ohm-1 cm-1 for a melt containing 26.3 pct CaO at 1400°C. The temperature coefficient was positive at all compositions, but became smaller at high CaO contents. Current efficiencies for electrolysis increased from 2.5 pct in FeOx to 17.3 pct at the high CaO composition, indicating a change from predominantly electronic conduction to conduction with a substantial ionic contribution. It was shown that Ca++ ions as well as Fe++ ions carry the ionic current. A subsidiary investigation on the apparent effect of atmospheres of argon, helium, and nitrogen on the electrical conductivity showed that this could be correlated with surface temperature losses, which varied with the thermal conductivities of the gases and resulted in precipitation of metal by the reaction 3 Fe++ = 2 Fe+++ + Fe. The work described in this paper is offered as a contribution to the general fund of knowledge concerning metallurgical slags. Measurement of electrical conductivity and electrolysis are comparatively trouble -free methods for investigating molten materials, but, although these methods had been used for complex slags, it was not until the work of Bockris et al.1 that the approach of examining simple binary slag systems was employed, and CaO-SiO2, MnO-SiO2, and Al2O3-Si9 were studied. Two groups have performed work of particular relevance to the present investigation. Inouye, Tomlinson, and chipman2 studied the conductivity of wustite as a function of temperature and of the addition of 5 mol pct of a number of oxides, including CaO. They concluded that molten FeOx in equilibrium with iron is a semiconductor. Simnad, Derge, and ceorge3 demonstrated the ionic nature of liquid iron silicate slags and also concluded that, although the conductivity of FeOx in equilibrium with iron is predominantly electronic in nature, there is a small ionic contribution. The work reported here on FeOx,-CaO slags consists of three main parts, namely, the determination of the specific conductance over a wide composition range, an investigation into the nature of the conductivity through current-efficiency measurements over the same composition range, and an attempt to identify the current-carrying ions, as well as a subsidiary investigation on the apparent effect of the nature of the inert atmosphere on the conductivity. EXPERIMENTAL Materials. The slags, varying in composition from FeOx to 27 pct CaO, were prepared by heating reagent- grade Fe2O3 in an ingot iron crucible with a suitable amount of CaCO3 and, in some cases, powdered iron, in air. This prefused material was then used for the runs. At the end of each run the cell was removed from the furnace and quenched by immersing the bottom half in water. After crushing, the slags were analyzed for calcium and total iron by the usual wet methods. The oxygen content was obtained by difference. Specific Conductance: Apparatus and Method. Fig. shows the experimental setup, with the conductivity cell and leads of ingot iron. The standard four-probe method for measuring high conductivities was used. In this, the potential drop across the unknown resistance is compared with the potential drop across a known resistance connected in series, i .e., same current through both resistances. Thus there are both current and potential leads to the center electrode and to the crucible, which acts as th other electrode. Both ac and dc circuits were available for the measurements; they have been described in earlier work performed in this laboratory.4,5 The geometry of the cell was such that the center electrode was equidistant from the bottom and sides of the crucible. This ensured that the current path was the same irrespective of the magnitude of the conductivity of the material in the cell. Cell constant were measured with KC1 or NaCl solutions, which have considerably lower conductivities (0.0013 to 0.25 ohm-&apos; cm) than the slags, and this precaution in design made sure that the determined cell constants applied to the cells with contents of any conductivity. The cell-constant determinations were made with the ac measuring circuit to prevent polarization. The four-probe method eliminates lead resistance but not the resistance of those parts of the center

Jan 1, 1967