Search Documents

By T. P. Floridis

It was deemed desirable to obtain an understanding of the vacuum desulfurization process. McKechnie1 has reported that the sulfur content of nickel- and cobalt-base alloys is reduced in vacuo. Keverian and Taylor2 have observed that vacuum melting causes desulfurization of iron-carbon-silicon alloys. Garnyk and samarin3 have desulfurized transformer steel by vacuum treatment. Experiments were conducted in order to investigate the desulfurization of liquid iron under reduced pressures, and to establish the effect of some alloying elements, and various crucible materials. A vacuum-induction furnace of 50-lb capacity was used. The charge was Armco iron. Silicon was added as 90 pct ferrosilicon, carbon as electrode graphite, and aluminum as high-purity aluminum metal. Magnesia and silica crucibles were used, their inside diameters were 5 1/2 and 5 3/8 in., respectively. The temperature was measured with an optical pyrometer and it was held at 1600 1 15°C. Samples were withdrawn with quartz tubes of 6 mm ID, without disturbing the furnace atmosphere. Pressures were measured with an alphatron gage. The experimental results are shown in Fig. 1. They indicate that: 1) Sulfur can be removed from liquid iron alloys by vacuum treatment; 2) The desulfurization is enhanced by the presence of silicon, carbon, and aluminum, all these elements increase the activity of sulfur dissolved in liquid iron;4 3) The pronounced effect of silicon indicates that probably a volatile silicon sulfide is formed, Alcock and Richardson5 have observed a similar phenomenon; 4) The same rate of desulfurization was obtained when the metal was contained in either magnesia or silica crucibles. Dr. J. Keverian has contributed many discussions and recommendations. M. S. Sutliff has helped in conducting the heats. The permission of General Electric Co. for this publication is gratefully acknowledged.

Jan 1, 1960

By Ivan E. Goodner, Charles H. Fulton

THE subject of the constitution of copper-iron mattes has received considerable attention in recent years by Keller,1 Bolles,2 Hofman,3 and Gibb and Philp.4 Still more recently Friedrich, Röntgen, Wiedmann, Heyn and Bauer, and Leroux have published, in some instances, elaborate researches on the various systems of the sulphides, and the sulphides and their respective metals, which enter into the constitution of mattes, and have added very greatly to the knowledge of the subject. The work of Friedrich has been especially fruitful. But to date no effort has been made to correlate the data obtained in the latter researches and apply then to the study of the product called " matte," which is made in such large quantities by copper and lead-smelters. In this paper we propose to determine, by metallographic and chemical means, the constitution of copper-iron and copper-lead mattes in the light of the recent data above mentioned. We do not discuss copper-nickel mattes or speisses (artificial arsenides). The paper is divided into three sections I. A review and discussion of the various binary systems of the metallic, sulphides, and the binary systems of various metals and their respective sulphides entering into the constitution of mattes; also a discussion of the physical and chemical properties of these sulphides. II. A description of the results obtained from the chemical and metallographic examinations of the samples of copper-iron and copper-lead-iron matte obtained from various plants.

Nov 1, 1908

By Roland Kammel

For electrolytic recovery of silver from dilute aqueous solutions improved mass transfer is necessary to achieve favourable current efficiencies and high space-time yields. The many cell designs proposed for this application can be divided into two different groups: cells from which the silver must be redissolved and cells from which the deposit can be reclaimed as a metal. Introduction Electrolytic silver recovery methods have proven advantageous under technical and economic aspects for the treatment of rinse water, still rinses and spent silver solutions in the electroplating and surface finishing industry, of exhausted fixing baths from photographic processing, bleed electrolytes from silver refining processes and leach liquors. Examples of the compositions of typical dilute silver solutions are listed in Table I.

Jan 1, 1984

By A. A. Steel

(Spokane Meeting, September, 1909.) DURING. the summer of 1905 I was employed by the U. S. Geological Survey to investigate the geology, Mining, and preparation of barite in most. of the fields of the United States. The Eastern districts have been more or less completely described ; the Virginia field in detail by Thomas L. Watson, in his paper, Geology of the Virginia Barite-Deposits,' and other fields in abstract., including statistics of production and references to current literature, by various authors .2 There have also been published a few details of the occurrence of barite in the lead-mines of Washington county, Mo.3 The other accounts of this district are erroneous and meager, and since this field is the most important one in the United States at the present time, a detailed description of the local geology seems doubly desirable. Barite-deposits are scattered over nearly the whole of Washington and adjoining counties, but. the product, is all mined from the areas indicated upon the sketch-map, Fig. 1, and is shipped from the stations of the St. Louis, Iron Mountain &. Southern railway, between Blackwell and Potosi, from 45 to 60 miles SW. of St.. Louis. The topography is for the most part gently rolling, with slightly graded streams, usually less than 200 ft. below the higher hill-tops. Along Mineral fork and Indian creek are :some steep bluffs and cliffs, affording good exposures of the

Feb 1, 1910

By Edward W. Parker

I. INTRODUCTION. AT the Seventy-sixth meeting of the Institute, held in New York, N. Y., February, 1899, I presented a, paper on this subject entitled, Coal-Cutting Machinery,' which has become somewhat out of date, in view of the decade's development in this feature of the coal-minim industry. It should be explained that the present paper is limited to the use of mining-machines in bituminous mines. Practically all of the anthracite mined is ?shot from the solid," no undercutting being done. Anthracite-mining is therefore not considered in the statistics or other references. The statistical record as compiled by the United States Geological Survey shows that in 1898, the year preceding the presentation of my former paper, there were 32,413,144 short tons of coal undercut by the use of machines. In 1907 the machine-mined coal-product amounted to 138,547,823 short tons. In sympathy with the general decrease in coal-production during 1908, the output of machine-mined coal decreased to 123,183,334 short tons, but the proportion of machine-mined coal to the total output, nevertheless, showed an increase, from 35.1 per cent in 1907 to 37 per cent in 1908. In 1898 only 19.5 per cent. of the total product was undercut by the use of machines. The number of undercutting-machines in use in the bituminous mines of the United States has increased from 2,622 in 1898 to 11,144 in 1907, and to 11,569 in 1908. The total production of bituminous coal in the United States in 1908 was almost exactly double that of 1898, while the machine- * Published by permission of the Director of the U. S. Geological Survey. 1 Trans.. xxix.. 400 to 4,59 (1899).

Sep 1, 1910

By O. Jay Myers

THE war effort has furnished the necessary impetus for better magnesium foundry practice. Four or five years ago, there were but a few formulas in general use for cores and mixtures for magnesium castings. Certain sands, binders, and inhibitors were specified and the proportions of these materials in each mixture were maintained between very narrow limits. As more and more war industries entered the field, much research was carried out and methods and practices were improved. Magnesium founding is still in a state of flux; therefore it is not uncommon to find one foundry spraying inhibitors on its cores, and another foundry using sand mixtures with incorporated protective agents. The basic core or dry-sand mold mixture for magnesium in use today is compounded with sand, core oil or resin binder, cereal, and moisture. Core oil or resin binder are added for baked strength while the cereal binder and moisture are for green strength. The normal mixtures (based on the weight of the sand) contain from 0.5 to 1.5 per cent of both cereal binder and core oil, and the moisture content varies between 1.5 and 5 per cent. The ratio of core oil to cereal binder varies from 60:40 to 40:60, while the correct amount of moisture depends upon the method of coremaking. PROTECTIVE AGENTS In all magnesium practice, protective agents are used in conjunction with the core and molding sands to prevent oxidation of the metal. The use of these inhibitors is not novel, but publications covering this field are not entirely adequate. Beck1 says Magnesium alloys decompose water to form magnesium oxide, hydrogen being liberated in the process (Mg + H20 -+ H21 + MgO). This reaction results in the blackening of the skin and the appearance of areas of porosity on the casting surface, the cavities of which are filled with a grey oxide powder (these are termed `burns'). Although sand cores for magnesium castings are thoroughly dried during the baking cycle, burning will take place on the castings unless the metal is protected properly. This type of burning is more difficult to define than the "water-magnesium" reaction cited by Beck. A possible explanation may lie in the following equation: 2Mg + 02 -s 2MgO Here, the source of the oxygen is not water, but the air in the mold cavity, together with the chemically combined oxygen in the core-binding media. Generally, two methods are used to prevent this reaction from taking place.

Jan 1, 1945

By Pei-Yung Huang, C. R. Hayward

In order to understand more fully the actual state of copper lost in copper reverberatory slags, a systematic study on the various reactions between certain metallurgically important copper compounds and synthetic copper reverberatory slags was undertaken by the authors in the Massachusetts Institute of Technology from 1942 to 1945.1 This paper, being only a part of the work completed, is published first because it furnishes the first experimental evidence of the formation of copper ferrite from reactions between cuprous oxide and copper reverberatory slags. Choice of Slag Composition The choice of the composition of the synthetic reverberatory slags to be used was much deliberated. Commercial copper reverberatory slags, neglecting minor constituents, avcrage :2,3 45 to 47 pct FeO; 38 to 42 pct SiO2; 5 to 6 pct CaO; 5 to 6 pct A12O3. Since the ternary system CaO-FeO-SiO2 has been much more thoroughly studied4 and is much simpler than the quaternary system CaO-FeO-SiO2-Al2O3, it was decided to use calcium oxide only instead of calcium oxide and alumina in the synthesis of the slags. Fortunately the composition of the average copper reverberatory slag with calcium oxide substituted for alumina lies in the region of the phase diagram clarified by the investigators. A survey of the phase diagram (Fig I) suggested two compositions: (I) the composition near the invariant point S, which is made up of 46 pct ferrous oxide, 37 pct silica and 17 pct calcium oxide; (2) the composition near the invariant point K with 45.5 pct ferrous oxide, 43 pct silica and 11.5 pct calcium oxide. Composition S has the advantage that the percentages of ferrous oxide and of silica almost exactly coincide with those of the average reverberatory slags, and that of the lowest melting point (1093º ± 3ºC) in the whole ternary system. The calcium oxide content, however, obviously is high. Since we have already substituted calcium oxide for alumina, and since calcium oxide is more basic than alumina, the fulfil- slag is decidedly too basic. Composition K has a slightly higher melting point (1150O + 3OC) and a higher silica content, but this is preferred because the slag is saturated with respect to tri-dymite and thus should not corrode siliceous refractories. Besides, it is less basic than composition S. The filial slag composition, therefore, was chosen to

Jan 1, 1949

By S. R. B. Cooke, S. W. Clark

Adsorption of calcium and magnesium by quartz was determined over a wide pH range using flame photometry for solution analysis. A parallelism was noted between calcium adsorption at alkaline pH and flotation of activated quartz by means of various fatty acid collectors. Abstraction of calcium from 100 ppm solutions increased above pH 10.5 until all of the calcium was removed at pH values between 12 and 12.5. Calcium was desorbed from the quartz over the pH range 12.5 to 13.0 and returned to the solution. Precipitation of magnesium hydroxide prevented measurement of magnesium adsorption above a pH of 9.9. A calcium adsorption isotherm determined at pH 9 matched measurements of barium adsorption by other investigators over the range where adsorption corresponded to the equation of a Freundlich adsorption isotherm. In accordance with the Gouy-Chapman theory for adsorption in the diffuse layer, adsorption of the divalent cations under these conditions was four times the adsorption of monovalent sodium. Activation of quartz by multivalent metal cations in flotation using anionic collectors has been studied by many investigators. The occurrence of activator cations in the water of flotation mills makes depression of silaceous gangue very difficult. Alternatively, in some flotation systems it is practical to cause activation of quartz so that it is floated from the desirable mineral values. The present study was initiated to investigate the activation of quartz by measuring adsorption of calcium and magnesium ions as a function of solution pH. Early empirical tests showed that quartz would be activated to flotation using anionic collectors if any of a number of divalent or trivalent metallic cations were present in the pulp.1*2 Subsequent studies by Clemmer,3 Cooke and Digre,4 Cooke,5 Schuhmann and Prakash,6 and Cooke, Iwasaki, and Choi,7-8 showed that flotation depended strongly upon the alkalinity of the flotation pulp, the concentration of the activating cations, and the chain length and structure of the organic collectors used. The concept of the electrical double layer has been applied to the case of the quartz-aqueous solution interface by Gaudin and Fuerstenau,9-10 and by de Bruyn 11 to explain the activation of quartz by multivalent metal cations. Studies of the surface of quartz by Gaudin and Fuerstenau9,10,12 and by Li " using the streaming potential technique contributed much information on the electro kinetic condition of the surface of quartz in the presence of various organic and inorganic ions. Measurement of adsorption of ac-

Jan 1, 1969

By F. A. Olson, J. S. Cho, M. E. Wadworth

An infrared study of the states of hydration of MgSO4 revealed a hitherto unreported metustable dehydration state in the temperature range just below that of the stable anhydrous salt. Infrared, thermogvavimetric, and X-ray studies indicated that the state had bisulfate and hydroxide characteristics. A formula fitting all of the experimental evidence is hydrogen-bonded Mg(OH)HSO4, or possibly the chemically equivalent 1/2 Mg(HSO4)2. Mg(OH)2 Infrared spectra of the 7, 6, 1, and OH2O states of hydration are given as well as the spectra of the newly found state which is called the bisulfate state in this paper. Thermogvavimetric studies as a function of water-vapor pressure gave an enthalpy value of 16 cal per mole, and 25 eu for the conversion of the bisulfate state to that of the anhydrous salt. The free energies of the transition varied from 1.76 to 0.18 kcal per mole as the transition temperature varied from 279° to 336°C. The bisulfate state is believed to be of importance in catalytic dehydration phenomena using MgSO4 and may be of interest because of properties in sulfating reactions differing from those of the monohydrate. Also, an analogous state may exist as a hydration state of other sulfates. ANHYDROUS magnesium sulfate is a catalyst with a high degree of specificity for the dehydration of secondary alcohols.1'2 The only product obtained at the usual operating temperature range of 360" to 400°C other than the corresponding olefin is water. Thus, the bonding of water to the anhydrous salt as well as an understanding of the hydration states of MgSO4 became of interest in attempting to understand the catalytic mechanism better. In the process of this study using infrared, X-ray, and thermogravimetric analyses a dehydration state not previously reported was found. Proof of its existence, the nature of the state, and its role, if any, in the catalytic mechanism then became of interest. This paper is concerned principally with the first two aspects of this problem. Magnesium sulfate forms many hydrates, of which the monohydrate and heptahydrate (Epsom salts)3 are most important. Other hydrates4 are known with 1-1/4,5 l-1/2, 5 2, 4, 5, 6, and 12 H2O's. The hydrates with 1-1/4, 1-1/2, 2, 4, and 5 HzO's are unstable. The anhydrous salt is very stable thermally and has a strong affinity for water. It can be heated without additional decomposition to about 800°C.' At 900°C noticeable decomposition takes

Jan 1, 1964

By B. Post, F. W. Glaser

Three borides of zirconium have been reported: ZrB,l ZrB2,2,3 and ZrB12, 4 The phase relationships, ranges of stability, and some physical properties of these compounds are described. THE zirconium borides differ considerably from one another, particularly with respect to their relative stabilities at high temperatures in the presence of carbon.4,5 ZrB2 is extremelv stable at all temperatures (to the melting point) in contact with carbon. Both ZrB and ZrB12 tend to decompose at elevated temperatures when carbon is present in excess of about 0.5 pct. ZrB forms ZrB2 and ZrC, and ZrB12 decomposes to form ZrB2 and a boron-carbide phase. In the ZrB12 preparation, boron present in excess of that needed to form ZrB2 reacts with carbon, if present, to form carbides, in preference to forming the higher boride. Similar instability of borides, other than diborides of the transition metals of the 4th and 5th groups of the periodic table, has been reported.5,6 special precautions had, therefore, to be taken to minimize carbon contamination in the preparation of ZrB and ZrB12. Reactions below 1400°C were carried out by heating powdered mixtures of zirconium hydride and boron in quartz tubes in a hydrogen atmosphere. For temperatures above 1400°C, reactions were carried out in graphite molds. Carbon contamination from the molds was minimized by employing extremely rapid heating rates to reduce carbon diffusion into the body of the specimen, and by subsequent "shaving" of sample surfaces that had been in contact with the graphite dies. A heating rate of about 2000°C per min was obtained by heating the dies (by direct conduction), using a current of 40,000 amp. Although this type of heating cycle apparently allowed little time for "homogenization," close approximations to equilibrium conditions were usually obtained as a result of the very strongly exothermic reactions between zirconium hydride and boron at elevated temperatures. Reproducibility of results in repeated runs under varying conditions was taken as a reasonable indication that equilibrium conditions had been effectively achieved. Quenching was accomplished by rapidly immersing the entire die, containing the reaction products, in water. Specimens could also be cooled at controlled rates by adjustment of the rate of flow of water through the water-cooled copper electrodes in contact with the graphite dies.

Jan 1, 1954

By D. R. Miller

Internal friction and elastic modulus variations in electrorefined titanium, iodide refined titanium, and alloys of the latter material with oxygen, nitrogen, aluminum, and zirconium were investigated. No oxygen peak was detected with electrorefined titanium but, provided precautions were taken to prevent increases in background damping, an oxygen peak at about 410°C could be resolved with each of the other materials. An additional partially resolved peak was observed at 500°C in a Ti-N alloy. An anomaly in the variation of rigidity modulus with temperature was observed. Possible mechanisms for the formation of any oxygen peak have been discussed. PRATT, Bratina, and Chalmersl investigated the internal friction of commercial purity titanium and alloys of this material containing 1.5, 3.5, and 4.5 at. pct O. With commercial titanium the internal friction curve consisted of two components, a background which increased steadily with temperature and a peak at about 600" C which was due to grain boundary relaxation. In the Ti-O alloys, however, an additional internal friction peak was observed at 430" to 450°C and, since this peak increased in height as the oxygen content was increased, it was thought to be associated with the presence of oxygen. The diffusion of oxygen in titanium at temperatures between 300" and 500° C is believed to have marked effects in its tensile properties2'3 and the present internal friction measurements were undertaken to obtain further information on this diffusion, using material of higher purity than that of Pratt et d. and an apparatus of very much greater sensitivity. In the course of the investigation a number of important limitations on the work of Pratt et al. were revealed and results have been obtained which emphasize the need for ensuring that in this type of experiment, internal friction is independent of strain amplitude and that the values obtained are reproducible. 1) MATERIALS AND APPARATUS The basis material from which the majority of the specimens was prepared was iodide-refined titanium, the major impurities in which were oxygen and nitrogen—the metallic impurities being present at concentrations less than 0.001 at. pct. The hardness of this material after arc melting, forging, and swaging to rods 1/4 in. diameter was Dph = 110. Specimens 10 in. long and 0.020 in. (0.51 mm) diameter were prepared from these rods by further swaging and wire drawing and were finally annealed in vacuo (5 x 10-6 mmHg) for 24 hr at 800°C. The oxygen alloys were prepared from iodide-

Jan 1, 1962

By W. H. HOWARD

Discussion of the paper of W. H. HOWARD, presented at the Salt Lake meeting, August, 1914, and printed in Bulletin No. 92, August, 1914, pp. 2029 to 2046. EDGAR M. DUNN, Anaconda, Mont.-Mr. Howard's contribution to the literature on the Cottrell, method. of electrostatic precipitation of flue dust and fume at Garfield has been read by us with peculiar interest for the reason that we have been experimenting with the same process at Anaconda for the past eight or nine months, with a view to adapting it, under the direction of Dr. Cottrell and the supervision of J. 0. Elton. and D. R. Kellogg, representing the Anaconda Smelter Commission, to the treatment of very large volumes of gases, using large pipe treaters and various forms of electrodes, with about 150,000 volts rectified current. For the amount of gas to be treated here the 5-in. pipe means a cost for installation that is practically prohibitive, clue to the tremendous number of pipes required, and we have been trying to cut installation costs by increasing the size of the pipes. All of our work is still in the experimental stage, but we have obtained good clearance on our mixed roaster and converter gases with a 3-ft. pipe treater 20 ft. long, and with 5 ft. velocity therein; and with a discharge electrode of a single No. 29 nichrome wire set in the middle of the 3-ft. pipe, with. a consequent electrode spacing of 18 in. The current used has been 150,000 to -160,000 volts, .and of course there have been troubles galore, relating particularly to insulation and rectifying. Blast-furnace gases did not give so good clearance, probably due to relative poverty in moisture and S03 content of blast gases to roaster-converter gases; making the blast gases the poorer in conductivity. Our experience has been so satisfactory that in our next experimental plant-built on a somewhat larger scale-we shall attempt a 4-ft. treater with greater electrode spacing, and a somewhat higher voltage-up to 220,000. As to fractional precipitation, mentioned by Mr. Howard, this idea was tried out at Anaconda last year (1913). Formerly our furnaces (Bruntons) roasting flue dust for the recovery of white arsenic, passed so great an, amount of dust to the settling kitchens that refining of this arsenical product was necessary to eliminate the 5 to 20 per cent. dust contained therein. Consequently the manufacture of As203 was effected in two stages, with a reverberatory roast of the first .product to obtain the final 99.5 per cent. As203. -

Jan 11, 1914

By J. A. Lund, A. M. Lawson

THE structures of quenched eutectoid and hypereu-tectoid Fe-Cu alloys have been examined by X-ray diffraction and by optical and electron microscopy. The relevant portion of the Fe-Cu phase diagram is given in Fig. 1. Several values have been reported for the solubility of copper in a Fe at the eutectoid temperature, including 1.4 wt pct by orton' and 2.13 wt pct by Wreidt and Darken.2 Alloys containing 4.8 and 7.5 wt pct Cu have been prepared from two batches of Ferrovac E iron (0.005C and 0.013C) and electrolytic tough pitch copper (99.90 Cu). Specimens of dimensions 0.8 by 0.8 by 0.1 in. were cut from hot-rolled material, austenitized, and quenched into brine at 25°C. Similar specimens were also cooled in the furnace, after a short soaking treatment at 1100°C, at a rate estimated to be 10°C per min in the temperature range of 900" to 500°C. X-ray diffractometry was performed on quenched and on furnace-cooled bulk specimens using iron radiation. Only a bcc phase could be detected in all samples. Lattice parameters were calculated from measurements on four lines, made up of two resolved high-angle doublets. Comparisons were made against a silicon standard. Results are shown in Table I. Based on X-ray diffraction studies of a series of alloys of lower copper concentrations, orton' estimated that the tattice constant of a Fe at 25°C increases 0.0014A per wt pct Cu in solution. Extrapolating Norton's data, it may be concluded that all copper was retained in solution in the brine-quenched 4.8 pct Cu alloy, and that approximately 5 pct Cu was also held in solution on quenching the 7.5 pct Cu alloy. Typical microstructures of brine-quenched specimens, as observed by optical microscopy, are shown in Figs. 2 and 3. Precipitation of the E phase (copper-rich) occurred along the y grain boundaries on quenching the 7.5 pct Cu alloy, rendering them readily detectable in the microstructure, Fig. 3. The original boundaries in the 4.8 pct Cu specimens were gener- ally not discernible, however. This indicates that the z phase which was seen in the higher-copper alloy was probably of proeutectoid origin. Thin foils for transmission electron microscopy were obtained from bulk specimens by spark machining to 0.006 in. thickness, followed by electrolytic polishing. Typical transmission electron micrographs

Jan 1, 1967

By G. A. Parks, C. Kovacs

The xanthate flotation of chrysocolla can be improved by preheating the ore to 500° to 600°C. Addition of water vapor reduces the preheating temperature required. The temperature range of flotation improvement correlates well with the range over which dehydroxylation occurs. This observation is consistent with changes in the structure and properties of the mineral as detected by measurement of solubility, D.T.A., T.G.A., X-ray diffraction, and infrared absorption and with recently proposed explanations of chrysocolla flotation. A brief experiment by one of the authors several years ago showed that exposure of chrysocolla to high temperature water vapor resulted in increased recovery by subsequent xanthate flotation. Recently renewed interest in flotation and thermal properties of chrysocolla1-5 prompted further study of this effect and more detailed reporting.6 This paper explores the response of pure chrysocolla recovery in Hallimond tube flotation tests to the time and temperature of exposure and to changes in the water vapor pressure. Brief attention is paid to the effects of such treatment on accessory minerals. A single experiment with flotation of chrysocolla from an ore is reported. MATERIALS Chysocolla from Inspiration, Gila County, Ariz. was crushed in a porcelain mortar, cleaned of visible and magnetic impurities, and screened to obtain -48 +65 mesh (Tyler) material for flotation test work. The clean material contained 28.5% Cu and was identified as chrysocolla by comparison of X-ray diffraction, D.T.A., and infrared absorption data with that reported for similar materials by others.4,5,7 Samples of malachite and chalcopyrite, prepared in a similar way, were also identified by X-ray diffraction. The sources of these materials are unknown. A sample of chysocolla-bearing oxidized copper ore from Pima, Ariz. was crushed and dry ground for thermal activation and subsequent flotation. PROCEDURES Activation: The apparatus used for exposure of materials to high temperature water vapor is illustrated in Fig. 1. The furnace temperature was controlled to ±5°C Water vapor pressure was controlled by pre-saturating a nitrogen carrier stream with water in an adjustable thermostatted saturator (multiple bubbler). A water manometer and capillary orifice flow meter were used to measure nitrogen flow rates for activation and for subsequent Hallimond tube tests. Gas flow rate and temperature were adjusted prior to introduction of samples. Exposure time was measured from the moment of introduction of the sample to the furnace, hence includes an initial drop below the control temperature. After heating, the samples were removed from the furnace and stored at room temperature in air. Representative samples of activated materials were examined by X-ray diffraction and infrared absorption.

Jan 1, 1967

Not many accounts of mining methods or labor conditions in the mines in early days can be found; all that have seemed to be authentic have been included in the preceding chapters. In practically every field opened before 18.10 the first coal was recovered by quarrying, or strip mining, the operations, of course, being by hand and on a very small scale; new places were opened as soon as mining became difficult or expensive. Where it became necessary to drift into the hillsides, the first coal was taken out by sleds, and later by small wagons, the power being supplied by the miner, often assisted by dogs. Wooden rails then came into use with small cars running on them. These cars were very small, usually holding only a few bushels; in the Belleville, Illinois field as late as 1863 cars having capacities of 10, 12, 14 and some as large as 30 bushels were in use. It was not until late in the 1830's that horses or mules came into use for haulage purposes in the Pittsburgh region, although some had been used in the Richmond, Virginia field at an earlier date. Coal was usually undercut by hand and wedged down, until explosives came into general use, and in nearly every field the coal was forked into the cars, the fine coal, or slack, being left in the mine. Hours worked were very long, but few records remain to show what they were at different places and times; there was undoubtedly a great variation between districts and mines. Roy stated a miner could often produce 5 or 6 tons in a day of 8 or 9 hours in a 5 or 6 foot seam, but in another seam possibly could mine only 3 1/2 to 4 tons. He estimated an average day's work in a four foot seam at about 3 1/2 tons.1 In a strike in the Belleville field in 1863 it was found that an average skilled miner in the field could probably produce 4 to 5 tons a day.2 This was only the coarse coal loaded and did not include slack. In 1873, a coal undercutting machine was tried at a mine about two miles from Brazil, Indiana, said to be the first coal machine ever invented in the United States. It was run by a 5 H.P. steam engine (later to be changed to compressed air), and consisted of an iron rim, four feet in diameter with movable steel teeth placed about one foot apart. The rim

Jan 1, 1942

By J. A. Clum, R. W. Heins, T. D. Tiemann

The use of Na-montmorillonite clay hinders (Western Bentonite) in the pelletizing of iron ore concentrates is well established as is the idea that alternative binders must be found. 1-6 This note summarizes work done7 in evaluating a Wisconsin montmorillonite clay binder. The clay occurs in irregualr beds overlying the Prairie du Chien Dolomite and the St. Peters Sandstone near Hersey, St. Croix County. The raw Wisconsin clay contained 65% quartz and 35% clay minerals. The Na20to CaO ratio was 0.234. Suspension viscosity tests of the raw clay gave results only slightly better than water alone, even after treatment with activator materials. Sedimentation treatment reduced the quartz in the decantate to 5% after 240 min (four hours). Twenty minutes of sedimentation produced a decantate with 27.5% quartz which was found as effective as the 5% quartz decantate in pelletizing behavior. The 20 min decantate was used in subsequent tests. The decantate was filtered and dried at 110°(230°F). The minus 200 mesh portion of this was added directly to the magnetite concentrate. Pellets were made in a laboratory sized disc pelletizer from pastes consisting of ore concentrate, balling water (9%) and binder (clay, or clay + resins, or resins). The pastes were premixed in a Waring blender. The binders were: (1) 1% of a commercially used Western Bentonite; (2) 1 % or 3% of the Wisconsin clay (raw, or 20 min decantate); (3) 20 min decantate washed with activator solutions, (to exchange Na for Ca in the clay); (4) decantate with activator added in the balling water; (5) decantate with organic resins; (6) organic resins. Measurements of the 0.46 m (18 in.) Green Drop Number, the Dry Strength and the Fired Strength (fired at 1260°C (2300°F) for 30 min) were made. The dry and fired compressive strengths were determined on an Instron testing machine using a C-load cell and a F-load cell, respectively. The cross-head speed was 0.004 m/sec (0.1 in./min) for both. The results of each measurement were averaged for 15 pellets. A summary of those results is presented in [Table 1]. More detailed results and procedures are presented in another report.7 In addition to the effects on pellet strength due to various binders the effect of varying magnetite concentrate characteristics is noted in [Table l]. There, a few comparative data are shown for Cornwall, PA Magnetite, which has a generally liner particle size than the Black River Falls magnetite which was used for most of the tests.

Jan 1, 1979

By Nathaniel Herz

The use of zinc dust for precipitating the pecious metals from cyanide solutions is well established now in many places, and has many advantages over the shavings method of precipitation. Although much work has been done o,n methods of testing zinc dust, as yet. no absolutely positive test has been devised to determine the value of the material. Certain facts are known, but often it happens that results on a working scale are not as expected from the laboratory tests. The purpose of this paper is to record some obscrvations made while testing a large variety of zinc-dust samples in the laboratory. W. J. Sharwoodl has described standard analytical methods, which have been followed, with the changes noted. The regular determinations include zinc oxide, by solution in ammonia and ammonium chloride, lead, and precipitating efficiency. In some cases cadmium was determined by a method similar to that described by J E Clennell.2 I will discuss the precipitating-efficiency test in detail. The procedure is as follows: "A solution of potassium silver cyanide is prepared by dissolving 10 grams of silver cyanide (AgCN) and 5 grams of 99 %' potassium cyanide in a little water and diluting up to 1000 cc. It is then adjusted by addition of a little more XCN or AgCN until the solution indicates from 0.12% to 0.15% free KCN by titration with standard silver nitrate. The titration is best made by using a 10-cc. or 20-cc. sample, adding 1 CC. of 2 % potassium iodide, and a slight excess of ammonia, as the end point is then sharper. Or 15 grams of pure crystallized XAg(CN)2 may be dissolved in a liter of water and 1.5 grams XCN added. " Weigh out 0.5 gram zinc dust into a 300-cc. beaker. Add a few cubic centimeters of watcr and stir until zinc is well mixed, then pour in 250 cc. of the prepared solution, stirring vigorously. See that all lumps are broken up, and continue stirring for fully five minutes. Stir occasionally (at least every 10 minutes) until the end of two hours from the addition of the solution. Then filter upon an 11-cm. filter, wash precipitate thoroughly, sprinkle with test lead, wrap it carefully in the paper, place in a scarifier with about 20 grams test lead, burn paper cautiously in muffle, scorify five minutes, cupel at low temperature and weigh silver. Milligrams silver obtained from 0.5 gram zinc X 0.0606 = percentage precipitating efflciency."³

Jan 1, 1916

By Nathaniel Herz

(San Francisco Meeting, September, 1915) THE use of zinc dust for precipitating the precious metals from cyanide solutions is well established now in many places, and has many advantages over the shavings method of precipitation. Although much work has been clone on methods of testing zinc dust, as yet no absolutely positive test has been devised to determine the value of the material. Certain facts are known, but often it happens that results on a working scale are not as expected from the laboratory tests. The purpose of this paper is to record some observations made while testing. a large variety of zinc-dust samples in the laboratory. W. J. Sharwood1 has described standard analytical methods, which have been followed, with the changes noted. The regular determinations include zinc oxide, by solution in ammonia and ammonium chloride, lead, and precipitating efficiency. In some cases cadmium was determined by a method similar to that described by J. E. Clennell.2 I will discuss the precipitating-efficiency test in detail. The procedure is as follows: "A solution of potassium silver cyanide is prepared by dissolving 10 grams of silver cyanide (AgCN) and 5 grams of `99 0' potassium cyanide in a little water and diluting up to 1000 cc. It is then adjusted by addition of a little more KCN or AgCN until the solution indicates from 0.12% to 0.15% free KCN by titration with standard silver nitrate. The titration is best made by using a 10-cc. or 20-cc. sample, adding 1 cc. of 2 % potassium iodide, and a slight excess of ammonia, as the end point is then sharper. Or 15 grains of pure crystallized KAg(CN)2 may he dissolved in a liter of water and 1.5 grams KCN added. "Weigh out 0.5 grain zinc dust into a 300-cc. beaker. Add a few cubic centimeters of water and stir until, zinc is well mixed, then pour in 250 cc. of the prepared solution, stirring vigorously. See that all lumps are broken up, and continue stirring for fully five minutes. Stir occasionally (at least every 10 minutes) until the end of two hours from the addition of the solution. Then filter upon an 11-cm. filter, wash precipitate thoroughly, sprinkle with test lead, wrap it carefully in the paper, plaice in a scorifier with about 20 grams test lead, burn paper cautiously in muffle, scorify five minutes, cupel at low temperature and weigh silver. Milligrams silver obtained from 0.5 gram zinc X 0.0606 = percentage precipitating efficiency."'

Jan 8, 1915

By Joseph M. Jacisin

Fatigue tests were conducted on 2017-T4 alumium in alloy in an u1lrcthig.h vacuum of 2 x 10-lo Torr and in air. The vatio of vacuum-to-air faligue life for this ~malerial varied Jrom 3.5:1 at a strain of 2.5 X 1O-3 ill. pegr in. to 8:l at a strum of 3.3 x X ill. per 171. Sotlze pvelivtlinary data were also obtained on the faligue life of the alumirnum alloy in a dvy-nitrogen atmosphere. A dark deposit observed on the fracture surfaces of the aiv-tested specimens was identified as oxides of tr~angarzese and magnesium This observalion, and the close correlalion betaveen results obtained in vaCuum and dry-nitrogen environtments, tend to confirm that air stvongly influences the fatigue mechanism by a covrosion process. THE fatigue life of certain metals is known to increase when the atmospheric pressure is reduced. Gough and Sopwith1-2 postulated that this is due to a joint chemical and mechanical process operating in air at the surface of the metal with oxygen and water vapor playing significant roles. Wadsworth and Hutchings3 observed that aluminum is mainly affected by the presence of water vapor. Very little information is available on the fatigue properties of structural aluminum alloys in a vacuum environment. This report describes work performed on 2017-T4 aluminum alloy in an ultrahigh vacuum (2 x 10-loTorr) and in air. Some preliminary data are also presented on the fatigue life of the alloy in a dry-nitrogen environment. 1) EXPERIMENT 1.1) Test Material. The material tested was commerciaT 2017-T4 aluminum alloy which, in addition to aluminum, has an approximate composition of 4 pct Cu, 1 pct Fe, 0.8 pct Si, 0.5 pct Mg, 0.5 pct Mn, plus smaller amounts of other elements.* Some typical naturally age to a substantially stable condition. Specimens were then machined from these rods and ground to a No. 8 microfinish. In order to minimize variation in material characteristics, specimens were made from rods procured from the same lot. 1.2) Apparatus. The apparatus and test specimen used in the fatigue tests are shown in Fig. 1. The device utilized a single-cantilever beam with rotating-bending loading. Bending stress was applied to the fatigue test specimen by placing a spacer beneath the bearing support, thereby providing a constant deflec-

Jan 1, 1968

By K. G. Davis

Dilute alloys of silzer in tilz haz been solidzjzed a1 controlled rules, in lzorizontal tubes 2 mrz and 0.5 rn in diam. Radioactive; tracer techniques we?-e used to study solute distvihutions along llze specimens and irmpurity substructures, as functions of the conditions growth. The results have heen mzalyzed using Burton, Prim, and Slichter's tnodel for the solute disty-ihution in the liquid ahead of an advancing solid-liquid interface. DECANTING techniques have been used to establish criteria for the formation of impurity substructure during solidification in several alloy systems An analysis equating the appearance of impurity substructure with the incidence of constitutional supercooling was developed,= in which diffusion was assumed to be the predominant mode of solute mixing in the liquid. Substitution of experimental data into the equations derived from the diffusion analysis gave reasonable values for solute diffusivity in the liquid. However, in these investigations solidification rates of 10 cm per hr and over were used, to minimize the effect of natural conection, whereas for crystals of high perfection lower solidification rates are needed, usually between 1 and 5 cm per hr. A knowledge of the conditions under which impurity substructures will be formed at low growth rates, and the degree of segregation to be expected, is therefore of interest. In the present investigation, radioactive-tracer techniques have been used to study the effect of growth rate, initial solute concentration, and size of specimen on the formation of substructure in uni- directionally solidified rods of dilute silver in tin alloys, over a range of growth rate between 0.5 and 10 cm per hr. Criteria for the formation of substructure were established by auto radiography. This was believed preferable to the decanting technique, for the relationship of the structure on a decanted interface with that of the freezing interface is not clear, since a layer of liquid is left on the surface following decanting.' The effect of substructure on the distribution of solute along the rods was also investigated. EXPERIMENTAL The procedure for sample preparation has been described in detail by einber. Alloys were prepared from tin of 99.999 pct purity and silver of 99.99 pct purity. A"', an emitter of both y and 0 radiation, was used as tracer. Samples of the alloys were drawn up into silica tubes with inside diameters 0.5 or 2 mm, remelted in a horizontal furnace, and solidified at controlled rates. A few centimeters of the samples were left unmelted for a measure of the initial concentration. Total sample length was approximately 20 cm. The temperature gradient in the furnace was kept constant at 36°C per cm in the region corresponding to the melting point for tin. To find how well this corresponded to the actual temperature gradient in the melt, a thermocouple of 38-gage wire was electrically insulated with a thin layer of Sauereisen cement and placed within one of the 2-mm-diam tubes, which was then filled with tin. The maximum diameter of the coated wire was 0.5 mm, the bead of the thermocouple junction being no larger than the diameter of the wire. A plot of temperature vs distance traveled by the furnace is given in Fig. 1 for a rate of furnace travel of 1 cm per hr. The temperature gradient in the liquid

Jan 1, 1967