By Wei Yu, Tiejun Chun, Jian Pan, Deqing Zhu

In this paper, improving the pelletization of Brazilian hematite by adding a boron bearing additive was carried out, and the pelletization parameters were also optimized. The mechanism of boron bearing additive was revealed in the kinetics of crystal grain growth by using LEICA microscopy and its software to measure hematite grain growth. Good qualities of green balls are manufactured with drop numbers above 5.7 times/0.5m, compressive strength higher than 13 N/pellet and thermal shock temperature over 620? under the following conditions: 1.2wt% bentonite, 0.4wt% boron bearing additive, 7wt% moisture and pelletizing in disc for 15 min. When the green balls were preheated at 1000? for 8 min and fired at 1280? for 15 min, the compressive strength of the fired pellets containing boron bearing additive is about 3096 N/pellet, which is far beyond the standard requirement for good quality pellets. Compared to the fired pellets without adding any boron bearing additives, the compressive strength of fired pellets containing boron bearing additive is increased by 1225 N/pellet. It is revealed that adding boron additive into the hematite pellets help to form more liquid phases, lower the activation energy of the hematite grain growth by 135.2 kJ/mol and increase grain growth rate by 33.6%, leading to higher strength of fired pellets due to forming more coarse and dense recrystallized hematite and energy saving by firing at lower temperatures for shorten time.

Jan 1, 2011

By Alicia E. Ares

316 L Stainless Steel samples were solidified directionally under conditions which produced the columnar to equiaxed transition. The position of the transition was located in each sample and the distance from the bottom of the ingot was measured. During solidification the distribution of temperatures were measured by means of thermocouples located strategically. From the measured temperatures the following parameters were derived; the local temperature gradient, the cooling rate and the velocities of the liquid and solidus fronts. Comparing the location of the transition and the values of these parameters it was found that the temperature gradient reaches negative values of as low as -13.44 "C/cm, and velocities of the fronts of around 0.1 cm/s. Also, a supercooling of 5.81°C were measured which was associated with the supercooling for the nucleation and growth of the equiaxed grains ahead of the columnar front. In addition the primary and secondary dendritic spacing was measured in both regions. The spacing was compared with the predictions from available models. The results are presented and discussed in the frame of the results obtained for other alloys

Jan 1, 2002

By Shilai Yuan, Huimin Lu, Liyuan Zhao, Zhijiang Gao

"A purification process was developed to removal impurity element boron from metallurgical grade silicon by electromagnetic induction slag melting. Vacuum melting furnace was used to purify boron in both Al2O3-MgO-CaO-SiO2 slag system and Al2O3-CaO-SiO2 slag system. The relationship between different slag chemistry and the removal of boron in silicon were studied using Back Propagation (BP) Neural Network model. The best slag chemistry for the removal of boron was predicted by Genetic Algorithm (GA) contributed by the use of Matlab. The results show that the mass fraction of Boron in silicon is reduced from 11.7496×10-6 to 2.3259×10-6 after slag melting in 28.96%Al2O3-3.43%MgO-36.24%CaO-31.37%SiO2 slag system. The relative error obtained with GA-BP Neural Network model was below 0.35%.IntroductionSolar energy, due to its low green house gas emissions, has been paid great attention. Accordingly, the demand for solar grade silicon (SoG-Si) has been growing rapidly. The quest for developing a low-cost method of producing SoG-Si has been moving forward in the last decade. Refining of metallurgical-grade silicon (MG-Si) attracts research interest due to its low material and energy costs, and more environmentally friendly technology in comparison to the traditional Simens process. As such, impurity elements in MG-Si must be removed to low levels for the photovoltaics (PV) cell to operate at optimum efficiency. Most impurities in metallurgical-grade silicon (MG-Si), especially metal elements, can be separated by directional solidification and the zone refining plasma-arc method [1, 2]. The main focus in refining MG-Si to SoG-Si is on the impurities which are the most difficult to remove. Boron has relatively high segregation coefficients (KB=0.8, concentration of Boron in solid silicon divided by its concentration in liquid silicon) [3] and higher vapor tension (the saturated vapor pressure of boron and silicon are 6.78×10-7 Pa and 0.4 Pa, respectively). The vacuum melting and directional solidification methods hence have no effects on boron removal.Slag refining involves melting MG-Si in the presence of a flux to produce a slag phase that can take up the impurity elements. The mechanism of slag refining is considered to include two main steps: the oxidation of boron and the absorption of boron oxide by slag materials. The oxidation of boron, described by the oxygen potential (PO2), resulting from the equilibrium Si and SiO2. The absorption of boron oxide, described as the slag basicity, is interpreted as expected to facilitate their extraction to alkali and alkali-earth oxides in the slag phase. Thus, effective removal may be obtained for a certain slag composition. Researchers [4-5] examined the effect of boron removal in CaO-SiO2 based ternary systems and showed that the addition of excess CaO can decrease the activity of SiO2. Researchers [6-8] studied the boron behaviors in CaO-SiO2-Al2O3, CaO-SiO2-Na2O, Al2O3-BaO-SiO2, CaO-SiO2-Li2O and Al2O3-CaO-MgO-SiO2 slag systems by adding boron in the silicon to a degree. Li2O, Na2O, MgO and BaO are thought to be associated with B2O3."

Jan 1, 2014

By Brian P. Atkin

The NISOMI-81 opaque mineral searcil and identification system uses quantitative color values (Pe, dA, y) and VHN as its determinative para-meters. The system is designed to operate on a Radio-Shack TRS-80 micro-computer which is interfaced to a motorised diffraction grating mono-chromator (WILSCAN). Using an interfaced monochromator/photometer combination a typical identification including the measurement of the photometer data on both specimen and standard, calculation of color values and a computer search takes about 6 minutes. The data file contains 240 minerals at present but can easily be expanded as reliable new data become available.

Jan 1, 1982

By Jan Pan, Deqing Zhu, Xianlin Zhou, Yanhong Luo, Zixing Xue

"Magnetic roasting process, aiming at obtaining magnetite concentrate, is the principle method of exploiting siderite as a raw material in iron and steel industry. Study on preparing DRI from siderite through coal based reduction technology is sporadic. To make the process of how siderite is reduced to iron clear, roasted ore reduced from siderite by lignite under different time periods were analyzed. The results indicated that: at the temperature of 1050°C, siderite was rapidly decomposed into magnetite, and further reduced as Fe30r?FeO?Fe, the later step was slower than the previous one. A fracture of particles was found during the process of thermal decomposition and the reduction of newly formed magnetite. As the reduction proceeded, metallization rate of products increased, and the iron grain grew along with time.IntroductionWith the rapid development of economy, China demands more and more iron ores for the iron and steel industry. China has rich iron ore resources, but 97% of them are below 30% in iron grade, many are refractory and unutilized [1], therefore large quantities of imported iron ores are in a desperate need. China imported 686 million tons of iron ore in 2011 (data from the China Customs), accounting for nearly 60% of the total consumption. To guarantee the healthy development of iron and steel industry, domestic refractory iron ores have to be utilized both economically and environmentally."

Jan 1, 2013

By M. J. Adam

The U.S. Bureau of Mines has investigated the partitioning of complex minerals to simpler phases using sulfidation reactions for selective extraction of mineral values. This report describes research in which thermal processing of the complex Ti-bearing mineral ilmenite (FeTi03) resulted in partitioning of the valuable Ti metal to the simpler compound rutile (TiO2). Samples of ilmenite were blended with elemental S for thermal treatment at various temperatures under controlled atmospheres in an effort to dissociate the Fe from the ilmenite complex. Product characterization revealed that the Fe was partitioned 'from the ilmenite, forming a rim of pyrrhotite/pyrite (FeS/FeS2) on a rut il e core. The products were agate milled and then subjected to cursory magnetic and flotation techniques in an attempt to physically separate the partitioned phases. Partitioning results and phase concentration data are reported relative to thermal treatment variables and physical separation techniques.

Jan 1, 1991

By C. S. Ek

As a continuation of previous work, further tests have been carried out to recover silver from the residues obtained in a zinc jarosite process. Selective flotation has been performed with different reagents, and ?cleaning steps have been introduced to upgrade the silver concentrate. Leaching of crude residues, as well as flotation tailings, has been carried out with cyanide and thiourea. Finally, the different beneficiation methods are compared, and the industrial aspects? of their application are reviewed.

Jan 1, 1990

By Shu-cai Zhou

"To understand the solidification behavior of austenitic heat-resistant stainless steel (TP34 7) in rotary electromagnetic-field, the influence of electromagnetic stirring in mold (M-EMS) on solidification structure of TP34 7 heat resistant steel in a round billet continuous casting was investigated based on industrial experiments. The results indicate that the excellent billet solidification structure of TP34 7 heat resistant steel can be obtained with appropriate electromagnetic stirring parameters. The solidification structure of TP34 7 heat resistant steel can be remarkably refmed, central porosity and shrinkage cavity can be remarkably decreased and equiaxed grains zone widens was enlarged. The industrial trials verify that the stirring intensity of TP34 7 heat resistant austenitic stainless steel should be higher comparing with plain carbon steel. Due to a higher viscosity, rotating speed of molten stainless steel was 20-30% lower than that of molten carbon steel in the same magnetic flux density.IntroductionIn recent years, the development of ultra super critical (USC) plants is accelerated by the demands of environment protection and energy saving, and USC plants with steam temperature and pressure conditions in excess of 593°C and 24.lMPa respectively were constructed. To achieve the goal, it is important to develop new materials with excellent high temperature strength, superior resistance to oxidation and corrosion at high temperature. Besides, their cost must be low enough to meet the requirement of plants [ 1]. TP34 7H steel is promising austenitic heat-resistant steel, which is used as superheater/reheater tube material and is extensively used for high temperature components and fossil-fired power plants, and suitable to be used in USC boilers plant. This kind steel contains with about 0. 7%Nb and it keeps higher allowable stress and creep rupture strength than TP304 and TP321H [1-2]. TP347H has conventionally been produced by ingot casting followed by forging and rolling. Recently, in order to decrease the production cost, challenging trials to produce these types of alloys by a continuous casting (CC) process have been attempted. However, the solidification structure of austenitic stainless steel is one of the key issues that attract more attention. Due to the low thermal conductivity of TP347H heat resistant stainless steel (much smaller than that of plain carbon steel), pronounced defects during continuous casting of austenitic heat-resistant steel such as coarse columnar, center porosity and coarse bridging, greatly influence mechanical properties of fmished products.A widely used technique in metallurgy is the inductive drive of molten metals using rotational or traveling magnetic fields. Recently, rotary electromagnetic stirring (EMS) has been applied to reducing various defects and improving increase the solidification structure of the metals in the continuous casting of steel, Al-based alloys and Mg-based alloys [3-8]. Electromagnetic stirring of plain carbon and low alloy steel in the continuous casting bloom and slab is well established for improving the quality of cast products [9-11] and is widely used in industry. However, very few literatures on electromagnetic casting of heat resistant stainless steel have reported. In this work, an industrial plant trial was performed to clarify the effect ofM-EMS on the macroscopic quality ofTP347heat resistant steel billet, in which the regularity and mechanism of the influence of EMS on solidification casting billet were discussed."

Jan 1, 2014

By Lin Li, Wen Shi, Hua Wang

"Specimens of the ultra-low carbon bake hardening steel were soaked for 1 min to 5 min, and then cooled by water quenching. The internal friction experiments were carried out to detect the spectra of the specimens. Results show that Snoek peaks are present in all the specimens, however, an obvious Snoek-Koster peak is found only in the 5 min-annealed specimen. Besides, tensile results indicate that the bake hardening values increase with the annealing time prolonging from 1 min to 3 min, but decrease as the annealing time prolongs further to 5 min. The solute distributions in the specimens were characterized by three dimensional atom probe. Some segregated C and V are found in the 1 min-annealed specimen, and the C and V contents decrease as annealing time prolongs to 5 min.1. IntroductionAs an excellent member of automotive body panel materials, various types of bake hardening (BH) steels have been developed since 1980s. Bake hardening property, as one of the most important mechanical properties, has been studied by many researchers [ 1-5]. As is known, BH phenomenon is generally controlled by the interaction between solute C and dislocations. The Snoek peak of internal friction (IF) is very popular in the investigation of solute C [6-9]. However, result of internal friction cannot suggest the distribution pattern of solute C as well as its influence on BH phenomenon.Three dimensional atom probe (3DAP) can diagnose solute element atoms as well as nano-sized precipitates, and it is the only instrument that currently can identify the identities of individual atoms in a material and measure their spatial coordinates with the resolution close to 0.3 nm [10]. There have been a number of studies about using 3DAP to detect solute elements as well as nanometer sized precipitates [11-19]. For example, Hono et al. [16] used 3DAP to determine the solute elements in an age-hardened Mg-Ca-Zn alloy, and they also obtained the distribution patterns of the observed elements."

Jan 1, 2011

By Yuanbo Zhang, Zhixiong You, Daoxian Duan, Guanghui Li, Tao Jiang

"Manganese is mainly consumed by steel and battery industries. In recent years, it is essential to utilize the low-grade manganese oxide ores with total manganese grade below 25%, as the high quality manganese ore resources are becoming scarce with the rapid development of the steel industry. Conventional pyro-metallurgical processes for utilizing manganese oxide ores are characterized by high production cost and energy consumption, low productivity, serious environmental pollution, etc. In this study, reduction thermodynamic of MnO2 reduced by sulfur was firstly carried out. Then, a novel process of reduction roasting with sulfur followed by acid leaching was developed to recover manganese from the very low-grade manganese oxide ores. Effects of main factors, including temperature, reduction time and S/Mn mole ratio, were investigated, and a high leaching efficiency of Mn above 95% was obtained under optimal conditions.IntroductionHigh/middle-grade manganese oxide ores are generally used in the metallurgical industries, particularly in steel plants and ferro-alloy units. The consumption of metal manganese in the ferro-alloy industry accounts for 85- 90% of the total Mn demanded [1]. Therefore, high quality manganese ore resources are becoming scarce with the rapid development of steel industry. It is essential to make good use of large quantity of low-grade manganese ores (TMn < 25%) presently available."

Jan 1, 2012

By Yan Zeng

Lithium metal silicates (Li2MSiO4, M = Fe or Mn) composed of abundant and non-toxic elements are important cathode materials for Li-ion batteries (LIB). In contrast to solid-state or sol-gel methods, hydrothermal synthesis conducted in pressure reactors is a favorable processing route as it provides the potential for scalable production and is environmentally benign. However, the key is to control the precipitation reaction to obtain powders with desired properties to meet battery specifications. Through a systematic study, we have found that Li2MSiO4 with tunable size from 300 nm to 1.5 μm can be produced by adjusting precursor concentrations, temperature, and reaction time. Under optimum conditions, high purity Li2MSiO4 with minimum defects were successfully produced and examined as an LIB cathode. The use of complexing agents promoted the formation of unique hollow particles via the self-assembling of elongated crystals. A four-step formation mechanism is proposed based on extensive characterizations with XRD, HR-TEM, SEM, and Mössbauer spectroscopy.

By Zhen Zhang, Jiang Diao, Tao Zhang, Yi Ren, Lu Jiang, Xiao-Man Yan, Bing Xie

The precipitation behavior of phosphorus enrichment phase was investigated by slag modification with Al2O3. The mineral phase of the original slag and modified slags were measured by mineral phase microscope, SEM+EDS and XRD. The mechanism of Al2O3 modification was discussed according to the thermodynamic theory analysis software (Factsage version 6.3). The results show that the high phosphorus solid solution (nˊ2CaO·SiO2-3CaO·P2O5) was generated by the continuous reaction of nC2S-C3P (nˊ＜n) solid solution and Al2O3 under 1350℃. The amount of initially precipitated solid solution (nC2S-C3P) was reduced and even disappeared with the increasing of Al2O3. If the addition of Al2O3 is enough in the slag, the high phosphorus solid solution (nˊC2S-C3P) that generated by the above mentioned reaction will continue to react with Al2O3 to produce Ca2Al2SiO7 and even C3P, which was demonstrated that the addition of Al2O3 has a positive influence on the precipitation of phosphorus enrichment phase.

Jan 1, 2015

By J. Fogarty, J. Sofra

The mobile telecommunications sector is one of the fastest growing industries worldwide. However, increasingly stringent environmental regulations are placing pressure on manufacturers to accept responsibility for end of life products. The companies are therefore exploring avenues to recover the valuable components contained within the mobile telecommunications devices thus reducing the quantities of toxic components going to landfill. Batteries used to power the devices, are typically based on either nickel-cadmium, nickel metal hydride, or lithium ion cells. They contain toxic metals including nickel, cadmium, lithium, potassium, lead, and cobalt in a complicated arrangement of battery cells surrounded by a metals then plastic casing. The Ausmelt Catalytic Waste Converter (CWC) for waste treatment and recycling is well suited to processing all three mobile phone battery types for the recovery of valuable metals in marketable products that can be recycled to industry without turning out harmful levels of toxic emissions. Ausmelt recently demonstrated the capabilities of its CWC by continuously processing 4.5 tonnes of nickel-cadmium batteries. Using Ausmelt's pilot plant facility in Australia, the nickel-cadmium batteries were processed to produce a nickel iron sulphide (matte), a cadmium fume and a final slag which satisfied CS toxicity leach test criteria and was safe f<~r disposal to landfill. This paper explores the commercial development of the Ausmelt CWC for treating each of the three battery types in light of (a) the outcomes of the recent demonstration, and (b) the current and expected future availability of batteries for processing.

Jan 1, 2000

By Atinuke Oladoye, David Esezobor

"Particulate Copper Silicon carbide (Cu-SiCp) composites find application as wear and heat resistant materials in electrical sliding contacts such as in homopolar machines, railway overhead current collector systems where high electrical/thermal conductivity combined with good wear properties is required. However, challenges occur during machining due to the presence of hard reinforcement in the matrix. This may lead to high turnover of tool wear and poor surface finish. The adoption of near-net shape technology to produce such hard-to-machine metal matrix composites and subsequent finish machining with its attendant cost has reported limited success. This paper critically appraises the challenges and opportunities in the improvement of tribological characteristics of particulate Cu-SiC composites and identifies low cost reinforcement material that could be used to improve its tribological characteristics.IntroductionTribology consideration is increasingly becoming a decisive factor in the design and selection of materials for applications involving interacting surfaces in relative motion. The consideration is mainly on the combined effects of friction and lubrication on material's wear integrity and performance amongst other. Annual losses due to tribology in the US industries are estimated at between 1-2% of the Gross National Income [1], in Russia it is about 1-4% of the GDP [2]. Thus, the attributes of tribology has become imperative in modem machinery especially those applications involving sliding and rolling surfaces, and electrical contacts [3- 8].These are readily found in homopolar machines, internal combustion engines, aircraft engines, gears, cams, seals and railway overhead current collector systems [9-12]. In these systems, the dissipation of frictional heat arising from the interacting surfaces as quickly as possible imposes constraints on the choice of materials for such application to prevent softening, plastic and shear flow and the transfer of metal as wear debris onto the interacting surfaces. If these possibilities occur, system performance is compromised and premature failure may result. Materials for these systems are expected to possess high electrical and thermal conductivities, low coefficient of thermal expansion, good corrosion resistance and high melting point [3-8, 13]."

Jan 1, 2011

By S. Viswanathan, Q. Han, A. S. Sabau

"In spite of recent advances in the mathematical modeling of fluid dynamics for materials processing applications, no significant advances have been made in the numerical discretization of these equations. In this work, the application of two-step projection methods for the numerical simulation of interdendritic flows is discussed. Unlike previous methods, the methods presented here are constructed for the exact equations which are characterized by variable density and volumetric fraction of the liquid. The drag terms, which describe the momentum loss due to the flow around and through the dendrite structures, are treated implicitly. Numerical examples for shrinkage-induced flow during solidification of an Al-4.5% Cu alloy bar is used to illustrate the effectiveness of the proposed algorithm.IntroductionLiquid contraction during solidification plays an important role in the formation of casting defects such as shrinkage voids, microporosity, and macrosegregation. Owing to their importance, the study of transport processes during solidification have received considerable attention during the past years [1, 2]. By the use of volume-averaging techniques, the mass and momentum equations for flow through a stationary dendritic structure were derived [3]. By using the volume-averaging techniques for multi-phase systems, two-phase transport equations for solidification problems were derived [4]."

Jan 1, 1999

By Ángel Ruiz-Sánchez

Ethylene glycol additions to aqueous acid solutions for leaching copper sulfides increase both copper and iron extractions compared to a conventional sulfuric acid leach with hydrogen peroxide (H2O2). The role of ethylene glycol is to prevent peroxide destruction, which normally occurs in solutions that contain both cupric and ferric ions. However, despite this improvement, ethylene glycol and sulfuric acid concentrations must be high (3.5 M and 0.7 M, respectively) to obtain satisfactory conversion levels at room temperature. In the present investigation, EDTA was used as an additive to complex the cupric and ferrous ions, lowering the requirements of ethylene glycol and H2SO4 to 0.11 M and 0.007 M, respectively, while minimizing oxidant decomposition. The experimental results for a mainly chalcopyrite, copper concentrate showed complete copper extraction in 24 h at room temperature, with the stoichiometric quantity of EDTA for the copper and iron dissolved. Tests using seawater were equally as successful.

By Xiao-hui Fan, Li-shun Yuan, Xu-ling Chen, Wei Lv, Min Gan, Yi Wang

"As the amount of ferrous scrap increases every year, it becomes more and more urgent to deal with this iron-bearing resource properly. This paper puts forward a method on resource-oriented utilization of ferrous scrap (cold-bonded pelletizing), and these cold-bonded pellets can be used as coolant in a converter. The influence on the pellets qualities by using different kinds of chloride as rust agents is studied, and results show that the strength of cold-bonded pellets increases significantly by using a combination of the three kinds of chloride -NaCl,MgClz,FeCh, their best dosages are 1.2%, 0.2%, 0.1% respectively. Other iron-bearing materials also have an effect upon the pellets strength, by adding 5% iron powder and maintaining for 48h, the compressive strength of the clumps surpass 2500N/A, dropping strength surpass 4 times/ A, and 10% iron slag or 20% steel slag can replace 5% iron powder while obtaining the comparative quality. The influence of different ratios of three ferrous scrap (converter mud, iron scale and dust) is further studied, and results show that when the ratio is 30% : 30% : 40%, the pellet strength reaches the maximum. After maintaining for 24~48h, the clumps can meet the mechanical as well as the physical-chemical requirements as BOF steelmaking refrigerant.IntroductionGreat amounts of converter mud, dust and iron scale are produced in steel production process. These materials are of great values, and their accumulation not only leads to environmental pollution, but also wastes the precious resources, which restricts the sustainable development of the steel industry [1,2] The main approach at present to dealing with the ferrous scrap is to add them into sintering. But in this way, the utilization factor of sintering and the quality of sinter decline while the energy consumption increases [3].Therefore, more advanced and efficient technology is needed to make the best of these iron resources. Cold consolidation of ferrous scrap is a simple process that has many advantages such as less investment, quicker effect, lower energy and lower cost [4-5] But the conventional maintaining period is too long, usually up to four-six weeks, and the pellet strength is low. Therefore, the key points of the cold-bonded pelletizing are to develop a new adhesive [4,5] to shorten the natural maintenance cycle and to improve the strength of the pellets. A method on resource-oriented utilization of ferrous scrap (cold-bonded pelletizing) is brought forward, and these cold-bonded pellets can be used as coolant in converter. After maintaining for 48h, these cold-bonded pellets can satisfy the mechanical requirements to replace the converter coolant [6]."

Jan 1, 2013

By Y. Z. Zhang

Electrochemical oxidation of arsenopyrite in ferric sulphate media in the absence and presence of bacteria T jerrooxidans has been investigated for the purpose of understanding the dissolution chemistry of arsenopyrite and the bacteria attack mechanism. Mixed potential, polarization resistance measurements, polarization curve, cyclic voltammetry experiments were conducted in a ferric sulphate medium of 10g/L FeH, temp.25-35°C, pH 1.5-2.5 in the absence and presence of bacteria Tjerrooxidans, respectively. For the anodic process, a two-step reaction sequence is suggested by the electrochemical measurements. The initial step at a low potential is described by:

Jan 1, 1996

By Hong Yong Sohn

A novel flash ironmaking technology is under development at the University of Utah under the support of U.S. Department of Energy (DOE) and American Iron and Steel Institute (AISI). The history of the development from the conception of the idea to the current status will be discussed. The flash ironmaking process produces iron directly from fine iron ore concentrates without requiring cokemaking and pelletization/sintering, which will enable the technology to significantly reduce energy consumption and carbon dioxide emissions compared with blast furnace ironmaking. Unlike other gas-based ironmaking processes, this technology will not suffer from the problems of solid sticking and fusion. Current work is focused on the method of supplying the energy required to maintain the necessary temperature, as an intermediate step to determine the scalability for larger, industrial-scale pilot trials.

Jan 1, 2014

By Sang-Beom Lee

For thermodynamic prediction, the deoxidation equilibrium of aluminum in Fe-36%Ni alloy was studied with a cold crucible under Ar gas atmosphere at 1773K. For the deoxidation reaction in liquid Fe-36%Ni base, i.e.: A12O3(s) = 2A1 + 3O The interaction parameters and the equilibrium constant between aluminum and oxygen in liquid Fe-36%Ni alloy are given in the following: eo Al = -3.8, roA1=0.9, eAl° = -6.4, rAl° = 700, rAIAIo = 3.1, roA1o = 833 within the composition range of [Al] < 1 mass%. The temperature dependence of the equilibrium constant was obtained in the range of 1773K < T < 1973K by using reported data and present results as follows: log KAo= 0.58-24463.7 / T The deoxidation equilibrium with aluminum in Fe-36%Ni could be thermodynamically well described in the range up [Al] < 1 mass% with first and second order interaction parameters as well as the equilibrium constant determined in this study.

Jan 1, 2002