By Kazutoshi Haga, Batnasan Altansukh, Atsushi Shibayama

In this study, the dissolution behavior of copper and arsenic from five different copper concentrates containing 21-34.7 %wt. of Cu, 1.3-7.3 %wt. of As and 15.6-27.5 %wt. of Fe were investigated under high pressure oxidative leaching conditions. Leaching experiments were conducted using different leaching reagents such as ferric sulfate, sodium chloride, deionized water, sulfuric acid and ferric sulfate-sodium chloride mixture in order to compare the effectiveness of each on the dissolution of copper and arsenic from copper concentrates. The effects of ferric sulfate (0.1-1 mol/L), sodium chloride (0.1-0.5 mol/L) and leaching temperature (100-180C) were investigated under 1 MPa autoclave pressure , particle size >45 m, pulp density of 100 g/L, stirring speed of 750 rpm and leaching time of 60 min. Results showed that the most effective leaching reagents for the dissolution of copper are 0.34 M NaCl and a mixture of 0.1 M Fe2(SO4)3 - 0.34 M NaCl, in which As extraction did not exceed 7%. The copper concentration in the pregnant leach solution obtained after leaching using 0.1 M Fe2(SO4)3 - 0.34 M NaCl was 13-30 g/L, while the concentration of As and Fe were in a range between 0.3-1 g/L and 0.2-10 g/L at 160C. INTRODUCTION Copper sulfide minerals, such as chalcopyrite (CuFeS2), chalcocite (Cu2S) and covellite (CuS) are used for the production of copper in mining and metallurgical industries worldwide. The conventional pyrometallurgical processing followed by electrorefining is a common process for the production of high purity copper (Moskalyk, & Alfantazi, 2003; Padilla, Aracena, & Ruiz, 2012). However, the degradation of copper content and an increase in the amount of metal impurities, especially arsenic (As), antimony (Sb) and bismuth (Bi) in copper concentrates cause serious problems to the production of copper and environmental pollution (Basha, Selvi, Ramasamy, & Chellammal, 2008; Long, Peng, & Bradshaw, 2012). Hydrometallurgical processes are used to recover metals from refractory ores, concentrates and tailings by leaching (Long, Peng, & Bradshaw, 2012; Masloboev, Seleznev, Svetlov, & Makarov, 2018). During the last decades, hydrometallurgical processing for the recovery of copper from enargite-bearing copper ores and concentrates has been extensively investigated due to its relatively more environmentally benign and less capital costs than the conventional pyrometallurgical processes (Long, Peng, & Bradshaw, 2012; Masloboev, Seleznev, Svetlov, & Makarov, 2018; Choubey, Lee, Kim, & Kim 2018). However, several issues facing the hydrometallurgical processing are incomplete extraction of copper associated with the coprecipitation of iron compounds, difficult stabilization of toxic impurities and production of a contaminated copper product (Dreisinger, 2003; Safarzadeh, Moats, & Miller, 2014). Hence, a number of studies have been conducted on the selective dissolution of copper from copper ores and concentrates or selective removal of arsenic leaving a clean copper residue using various leaching reagents or lixiviants (Safarzadeh, Moats, & Miller, 2014; Mihajlovic, Strbac, Zivkovic, Kovacevic, & Stehernic, 2007; Tongamp, Takasaki, & Shibayama, 2009). More extensive studies on the selective extraction of copper from enargite- bearing copper ores and concentrates are much needed to improve copper recovery.

Jan 1, 2019

By D. Harrington

Every few weeks United States newspapers of 25 or 30 years age ran scare-heads telling of some mine disaster, which was a first-page attraction for a day or two and then was forgotton until another disaster occurred a few weeks later. Interspersed with these disasters were the so-called sniping mine accidents, causing the death of one or two mine workers. The summation of all types of mine fatalities usually exceeded 3,000 a year. In the period 1906-10, inclusive, there wore 84 major explosion disasters (or about 17 per year) in united States coal mines; the fatalities resulting from those disasters numbered 2,388 for the 5-year period. These frightful catastrophies helped to cause the total number of fatalities in our coal mines for the 5 years (including the fatalities from major explosions) to reach the enormous total of 13,288, an average of 2,658 per year. In addition, some hundreds of other typos of mining accidents swelled the annual fatality list to upwards of 3,000. This admittedly deplorable condition created so much Nation-wide comment that Congress was impressed with the necessity of having something done by the Federal Government with a view to trying to halt at least sonic of the excessive loss of life in our mines; in consequence, the Bureau of Mines was created and began to function in July 1910.

Jan 1, 1935

By Perry D. Teitelbaum

In two earlier studies the Federal Bureau of Mines undertook to explore comprehensively the dimensions of the Nation's energy balance. The first of these studies, published in 1950 as Bureau of Mines Information Circular 7582, by Harold J, Barnett, was primarily concerned with projections of future domestic energy requirements and supplies, because these related to projected growth in major fuel-consuming sectors of the economy, changing rates of energy-use efficiency, and interfuel substitution patterns. But, to provide the essential background for these projections, it was first necessary to assemble and examine in some detail the quantitative information on the size and shape of the current United States fuel economy. Among other things, Barnett's path-breaking study indicated the need to consider energy as an entity, particularly for public and private policy makers, industry and commodity analysts, economists, and others concerned with long range questions of domestic and international energy supply and demand. The study also spotlighted a gap in the fabric of current economic intelligence; no comprehensive collation and reconcilation in any single report of available published statistical information covering the origin -a disposition of all energy materials existed. In response to this latter need, the Bureau of Mines prepared the second of the two studies referred t3 above. This was published in 1951 as Report of Investigations 4805, by W, H, Lyon and D, S. Colby, and it consisted of statistical information on the production and use of each of the various fuels and electric energy in the United States for 1929, 1939, and 1947; all were presented in tabular form and on a uniform basis. The three years selected were chosen largely on the basis of data availability.

Jan 1, 1961

By M. Abdellatif

Keywords: Pyrometallurgy, furnace, DC arc furnace, smelting, silicon The technical feasibility of silicon smelting in a DC arc furnace was investigated. A graphite-lined furnace was operated at power levels of 150 to 160 kW, and 40 to 60 V. The average feed rate during the silicon production period was about 30 kg/h. The recipe consisted of pre-mixed batches of 28% petroleum coke and 72% lumpy silica. The target furnace operating temperature was set at 1600°C and then raised to 1700°C. In total, about 1.6 tons of premixed feed materials was processed over 16 feeding?tapping operations. The feed was manually charged into the furnace in sub-batches of 10 to 40 kg at a time. The total batch mass was set at 90 kg during the initial part of the testwork, and increased to about 120 kg for the rest of the campaign.

Jan 1, 2011

By Nikhil Dhawan, Ashwini Kumar, Yogendra Pratap, Himanshu Tanvar

India does not possess any soluble potash reserves and depends completely on imports. In this study, an attempt has been made to recover potash (K) values from the mica sample employing thermal and mechanical routes followed by leaching. Direct leaching of mica in different lixiviants is found to be ineffective with very low K-dissolution (1–5%). Heat treatment with different fluxes, such as NaCl, NaOH, and CaCl2, is carried out and almost 85% K-values are recovered. Mechanical activation of mica and with different calcium additives is carried out to recover potash values. K is recovered in leach solution in the form of soluble salts, such as K2CO3, K2SO4, and KOH, and leach residue consists mainly of calcium-alumino-silicates. Using mechanical activation with flux, it is possible to recover >95% K-values from mica sample. Mechanical activation with calcium-based flux is found sustainable in the recovery of K-values from mica.

By Raymond A. Mazzoni

Over the last twenty years, roof support technology has made numerous advances since the original wedge and slotted bolts of the 1950's. By comparison, the roof supports used today are more complex and specialized than the supports used in the past, providing mines with a varied selection of supports from which to choose. As a result, when problems with supports are encountered, it is more difficult to determine whether it is the result of geological changes, poor installation practices, or malfunctioning supports. Recognizing this problem, MSHA's Roof Control Division of the Pittsburgh Safety and Health Technology Center, has undertaken the task of publishing a guide for trouble¬shooting problems encountered with roof support systems. The purpose of this guide is to provide a logical sequence to resolving the most common problems encountered with roof supports. The objective of this paper is to introduce this guide to the mining industry as well as provide insight into the evolution of the guide from its beginnings as rudimentary charts to its more comprehensive present format as a practical guide for use by the mining commu¬nity.

Jan 1, 1997

By Nelver Benavides

"Actualmente en la industria minera, las técnicas de control avanzado, la integración de procesos y tecnologías ya no son consideradas como conceptos exóticos y de dudoso impacto productivo, sino solo como un eslabón más en el proceso de mejora continua. En ese sentido, el presente texto señala la integración de estas tecnologías en la Concentradora Cuajone – Southern Perú, considerando las operaciones de chancado, molienda, sistemas de recuperación de agua y proyectando expectativas a mediano plazo para las operaciones de flotación, extracción y voladura. "

Sep 12, 2011

Base metal sulphide mineralisation on the northern end of Great Barrier Island is spatially associated with hypabyssal intermediate to acidic intrusives, in transgressive structures in indurated, complexly deformed greywackes and argillites. Copper predominates in the mineralisation, with minor accompanying lead and zinc and also some gold and silver. However, in some cases lead or zinc may be the dominant constituent. The mineralisation is generally characterised by only narrow envelopes of weak alteration (propyliticassemblages dominated by chlorite and epidote) and with only minor amounts of quartz accompanying the sulphides, which form a cement in zones of hydraulic fracturing. There are two distinct structural settings to the mineralisation: at MinerÆs Head, in a structurally complex situation in a shell-like zone of crackling in hornfelsed greywacke, in association with both north- and east-striking fractures and rubble breccias associated with the apical part of a large intrusive; and in very narrow, but very strike-persistent, 1inear steeply-dipping fracture zones, exposed on the north coast and inland areas near Tataweka.

Jan 1, 1984

Urban development to the south of Sydney is approaching areas of current and proposed coal mining. Already some structures and residential areas are affected by mining subsidence.Subsidence resulting from either conventional pillar extraction methods or longwall mining has been monitored for 15 years to enable the characteristics of the surface deformation to be determined.The vertical and horizontal displacements of survey stations on the surface are monitored and the results arc used to calculate subsidence, changes in slope of the surface, curvatures along the subsidence profile, and the ensile and compressive strains. These features are in turn related to the underground extraction to give a description of surface subsidence and the development of subsidence with time.Subsidence investigations have been carried out over all or part of the workings of six collieries in the Southern Coalfield.Two case histories illustrate the procedure in the investigation of subsidence phenomena. The first example is the study of the subsidence over a series of longwall panels in one seam and the second is a study of subsidence over pillar extraction in two seams one above the other. From the results of the investigations the effects of panel widths on subsidence are determined.This and other information assists mine planning in areas where surface movement and deformation are important considerations.

Jan 1, 1980

By K. Saikiran, A. R. Nalla

Longwall management, regular shield maintenance, and evaluation of ground control problems can be performed using real-time shield monitoring program. Based on real-time shield pressure data, evaluation of intensity and interval of periodic weighting, estimation of time-dependent pressure increase and the effects of geologic anomalies can be obtained. In this study, full-face shield pressure data of over 457 m (1,500 feet) of face advancement is analyzed to evaluate shield response in the presence of surface lineaments, floor undulations, and multiple main roofs. Shield pressure increase due to web cutting is also correlated with setting pressure during periodic weighting and normal time. In addition, time-dependent pressure increase rate on Sundays and holidays is also correlated with time average pressure and the location of previous periodic weighting.

Jan 1, 2000

By F. J. Sotillo

The reduction in energy consumption has been always important for beneficiation plants. Also gravity separation processes have gained lately great importance due to environmental concerns, especially in the gold and silver Industries. In this sense, the paper point out how to reduce the energy consumption in grinding, and increase efficiency in both grinding and gravity separation are of utmost importance to optimize the use of the country’s resources. For these purposes, chemical additives, such as rheology modifiers have shown great potential, and deserved careful consideration.

Sep 9, 2007

By R. M. Becker

THIS IS a progress report on a study of the application of statistical practice to mine and mineral sampling undertaken by the Federal Bureau of Mines to provide sound theoretical and practical data for use of the mineral engineering professions. One of the problems in mine sampling is determining the reliability of the results. For certain types of sampling data (random data) the reliability of the results can be stated mathematically. For other types of data there is no known means of quantitatively expressing reliability. In applying measures of reliability to a set of random data, some knowledge or assumption of the characteristics of the particular data is necessary. In many fields these characteristics are well known. However, in mining, where the data are in assays, these characteristics are not well known.

Jan 1, 1961

By R. Ressel

Keywords: ferrovanadium, thermodynamics, phosphorus Recyclable material is rapidly gaining in importance as a source of raw materials in industrialized countries. This is also the case in the production of ferrovanadium, where, increasingly, materials such as discarded capacitors, spent catalysts, slag, dust and sludge are used. As the V-content in the raw material varies greatly, the demands on process technology are very high. The share of perturbing elements depends very much on the source of the raw materials, which, in turn, makes a corresponding optimization of the various refining steps necessary. The raw materials are mostly available as oxides, which means that carbon, silicon or aluminium are used as reducing agents. Thermodynamic calculations were used to show especially the behavior of vanadium and phosphorus at different process conditions.

Jan 1, 2005

Resonance re-emission from nickel vapour affords a convenient method for isolating the resonance lines at 3415A, 3515A, and 3524A. The vapour is generated by cathodic sputtering and is illuminated by light from a nickel atomic spectral lamp. The resonance lines thus isolated can be usefully employed for absorption measurements on mineral samples where the nickel concentration is too high for measurements with the more sensitive line at 2320A. A spectrophotometer employing a resonance lamp as monochromator possesses several advantages where a great number of determinations are made under routine conditions. The wavelength setting is stable under even the most rigorous conditions and with the provision for automatic setting of full scale deflection the instrument requires virtually no adjustment. The instrument has been used under routine conditions for the determination of nickel (in the range O· 05-2 per cent) in mineral samples.

Jan 1, 1968

By Hasan Nizamoğlu, Z. Abidin Sarı, Aslıhan Demiraslan, M. Deniz Turan, Tolga Depci

In this study, recovery of copper from solid material (obtained by leaching of chalcopyrite with oxalic acid in the presence of hydrogen peroxide) with a copper oxalate structure was carried out selectively using HCl. The chemical composition of the solid was as 29.3%, 9.7%, and 13.3% for Cu, Fe, and S, respectively. Selective recovery of copper by degrading the copper oxalate structure with a low-solubility product (Ksp = 4.43 × 10−10) was performed by conventional leaching in the presence of HCl. The optimum leaching conditions were determined as 5 M of HCl concentration, 318 K of leaching temperature, 120 min of leaching time, 25 ml/g of liquid–solid ratio and 400 rpm of stirring speed. Under these conditions, approximately 77% of copper and 3% of iron were taken into the solution. According to the characterization of the leach residue that was obtained, the oxalate structure was degraded. Moreover, the results of XRD analysis showed that the sulfur (S) and cubanite (CuFe2S3) phases were mostly observed in leaching residues, and this was supported by the SEM-EDX data. Based on the results, it may be stated that selective copper extraction can be obtained from a chalcopyrite concentrate by a two-step leaching method using a conventional hydrometallurgical technique.

By Tony Mazzo

It has often been said by consulting engineers that foundation contractors are in the business of taking risks. One would agree that the mere fact a foundation project can be budgeted, planned, engineered and executed solely on the reliability of eight test borings made at a proposed site having an area of approximately 19,000 square feet, is a risky proposition, in and of itself. Now imagine that this site is actually one half of a city block located in an urban setting in an old, congested, historical neighborhood, surrounded by narrow city streets and historic landmark buildings. And suppose that the required depth of excavation for the construction of the new building on this site is approximately 35 feet and the natural groundwater table is at a depth below existing grade of only 25 feet. Given the difficult site conditions outlined above, one could certainly add the words "challenging" and "complicated" to the inherent word "risky" when describing the construction techniques involved to undertake a foundation project of this magnitude. This case study will discuss in detail how the excavation, sheeting, dewatering and underpinning work was accomplished as well as the problems overcome along the way.

Jan 1, 2003

By Dyson N. F

Mixed cobalt-nickel sulphides precipitated from ammoniacal process liquors derived from nickel sulphide concentrates, mattes, and reduced nickeliferous laterites have been characterized.The mixed sulphides are prone to oxidation on standing and are rapidly leached under relatively mild conditions. The kinetics of the leaching reactions are controlled principally by temperature and oxygen partial pressure. Although the samples have different CO:Ni ratios and have undergone varying degrees of oxidation, there is little difference in their leaching behaviour. The results suggest that a single plant would be able to process mixed sulphides of varying composition. Any copper and zinc present in the mixed sulphides as impurities also go into solution and must be removed prior to recovery of the cobalt and nickel in metallic form.

Jan 1, 1981

By Cesar Sáenz Acosta

El presente texto señala las mediciones de impactos que se han realizado a los programas de responsabilidad social de una empresa minera. Esta medición se realizó a través del cálculo del indicador “Retorno social de la inversión”, aplicando el modelo SROIM o Gestión del Retorno Social de la Inversión. Los proyectos de RS medidos permiten actuar a las empresas de manera responsable con su comunidad y comprenden: salud y nutrición, educación y desarrollo económico. Asimismo, esta medición contribuye a mejorar la comunicación de los impactos generados y desarrolla una gestión adecuada de estos.

Sep 12, 2011

By T. E. Bernard

Occupying a refuge alternative (RA) is an accepted practice in mine fires and explosions when escape is not feasible. MSHA has promulgated a final rule on refuge alternatives that includes a recognition that thermal environment is an important consideration. To this end, an environmental index was specified. The question remains about how to test a refuge shelter to demonstrate that it meets the final rule. The analysis followed five activities: A. Provide an estimate of heat generated by an individual refuge alternative occupant; B. Evaluate the Steadman Apparent Temperature criterion of 95°F; C. Discuss simulations based on body temperature or skin temperature limits; D. Suggest method of simulating human heat generation during refuge occupancy; and E. Suggest alternative methodologies/criteria for evaluating heat and humidity survivability inside a refuge alternative.

Feb 27, 2013

By John Wise

Significant movement to an existing slurry wall which serves as a retaining wall on 'O' Street in Southeast Washington, D.C. initiated the Department of Public Works for the District of Columbia to invite specialty contractors to propose a rehabilitation and stabilization for the failed slurry wall. Nicholson Construction Company proposed and was awarded a contract for the construction of an anchored precast lagging and soldier pile wall to be located approximately 4 feet in front of the existing structure with granular fill placed between the new and existing walls. Stabilization of the existing slurry wall also included drilling horizontal weep holes and demolishing the failed panels down to the existing ground surface. A new and improved drainage system was also constructed to increase the amount of water directed toward the existing storm sewer system running along 'O' Street. This paper provides a detailed account of these construction activities.

Jan 1, 2003