By Satu Jyrkönen

A single-particle laminar-flow technique was used to study reactions of sulfidic nickel particles. The studied materials were three natural nickel concentrates and four synthesised nickel mattes. The variables of the experiments were the gas preheating temperature (500 - 1300°C), the composition of the reaction gas (N2 + 0 - 75 vol-% 02) and the ,particle size of the feed. Chemical analysis of the particles was used to determine the oxidation degree of the materials, and optical and scanning electron microscopy were used to detect alteration in their morphology, internal composition and structure. General reactivity of the materials was monitored by the extent of sulfur removal. The reaction mechanism of the studied materials was found to depend primarily on the materials composition as well as oxygen content of the reaction gas.

Jan 1, 1998

By Minji Jun

Leaching of the surface-coated metals from waste acrylonitrile butadiene styrene plastics (WABSP) has been investigated in the ammoniacal solution. The ammoniacal leaching of WABSP (typically containing 4.1 wt% Cu, 1.3 wt% Ni, 0.03 wt% Cr) efficiently dissolved copper and nickel, leaving unleached chromium as fine particles. The results indicate that the anions of different buffer media for metals leaching follow the order: CO3 2− > Cl− > SO4 2−. A declined leaching with high NH4OH–(NH4)2CO3 ratio (8:1) and a steep rise in extraction with high pulp in solution revealed the influence of anion (CO3 2−) and cation (Cu2+) present in the system. The leaching performed in carbonate solution by maintaining 5.0 M total NH3 concentration as NH4OH–(NH4)2CO3 ratio, 4:1; pulp density, 200 g/L; agitation speed, 400 rpm; temperature, 20 °C and time, 120 min yielded the maximum extraction (>99%) of copper and nickel. The study reveals a plausible recovery of the surface-coated metals from the WABSP without altering the properties of polymer material that can be recycled separatel

By Ragnhild E. Aune, Mark William Kennedy, Shahid Akhtar, Jon Arne Bakken

"To determine the heating rate of billets using ‘short coils’, an appropriate correction factor must be applied to the theoretical relationship. In 1945, Vaughan and Williamson published a semi-empirically modified Nagaoka coefficient applicable for moderate frequency induction heating processes (10 kHz). Recently it was demonstrated that the method of Vaughan and Williamson gives <10% error in the estimated power when heating aluminum billets at 50 Hz.In the present study, experiments have been conducted on aluminum billets in order to verify an empirical frequency corrected ‘short coil’ equation. Measurements of electrical conductivity (<± 0.5%), current (± 1%), heat (± 1-3%), and magnetic flux density (± 1-2%) have been performed. The results are compared with 1D analytical calculations, and 2D axial symmetric FEM modeling using COMSOL 4.2®. The frequency corrected equation has proven to provide accurate predictions of power (<4% error) within the frequency range 50 Hz to 500 kHz.IntroductionInduction heating is commonly applied to the re-heating of billets before forging or extrusion processes. The resistive heating produced by eddy currents in the solid or semi-solid work piece during this procedure, is driven by the time varying magnetic flux density in the air-gap between the work piece and the coil. The flux in the air-gap is created by the current flowing in the induction coil, i.e. the magneto-motive force. In Figure 1 it can be seen that the currents present in the work piece are concentrated in the outer ‘shell’, or the first electromagnetic penetration depth (dw), and flow in a direction which opposes the magnetic field produced by the induction coil."

Jan 1, 2012

By R. Altman

A Brookfield viscometer fitted with a stainless steel bob was used to measure the viscosity of industrial lead blast furnace slags between 1126 and 1298°c. Slag oxidation state was characterized by first annealing the? slag samples at 750°c in sealed copper tubes in order to precipitate magnetite crystals. The magnetite concentration was then measured on an Outokumpu Saturated Magnetic Analyzer. Using an Arrhenius-type equation, a viscosity model was developed by regression. The equation below accounted for 75% of the variability in the data used to generate the regression coefficients and, on average, could predict viscosity within ± 12% of the measured value. The greatest difficulty encountered in measuring viscosity was due to the occasional presence of solids in the slag which caused, at times, erroneously high viscosity measurements. Precautions to minimize this problem are outlined in the text.

Jan 1, 1985

By V. I. Lakshmanan

The demand for elements such as nickel, cobalt, titanium and gold in various applications has increased significantly. Innovation to recover these elements now plays a major role in metallurgical processes as established technologies have challenges in treating the types of ores that are available while meeting the increasingly stricter environmental regulations. Alternative chloride based processes have been developed that can be used to recover the value elements from the available feed stocks with potentially lower environmental impact. Chloride-based hydrometallurgical processes have several advantages, including higher leachability of complex ores/tailings and relative stability of chloro-complexes of the metals. Process Research ORTECH Inc. (PRO) has developed mixed-chloride process flowsheets, where innovative solvent extraction process steps are used for the separation of nickel, cobalt, titanium and gold from their respective chloride solutions. This paper will discuss the potential aqueous chloro-chemistry of these metals and separation reaction mechanisms involved in the solvent extraction process.

By Dean Ilievski

Mathematical modelling of the precipitation process requires that the kinetics of crystal growth, nucleation and agglomeration be known: This paper reviews the current state of knowledge on these precipitation sub-processes (ie. growth, nucleation and agglomeration) and describes a number of experimental techniques for estimating their kinetics. The experimental methods used to generate the precipitation data and the data analysis techniques used to extract the kinetics information from the data are discussed separately. There is no universal "best" technique for determining the kinetics. However, studies on multi-crystal systems are more reliable for modelling purposes than are single crystal studies. The selection of a technique will depend on which sub-processes are present. A problem with all kinetics studies is that there is generally a large uncertainty in the estimated kinetic parameters. This stems from the scatter in the experimental data being further propagated by the mathematical techniques used to extract the kinetic parameters.

Jan 1, 1996

By C. S. Simons

This paper presents a review of the extractive processes used in the production of nickel, with emphasis on developments since the beginning of the Second World War. Attention is given to the factors, many outside the nickel industry itself, which determined the direction of process research and strongly influenced the ultimate commitments to industrialize the resulting developments. An example of such a factor is the sudden surge in demand, far exceeding the then available nickel production capacity, that was caused by the advent of World War II; the result was the first serious consideration ever given to low- grade laterites as a viable source of primary nickel. Other factors discussed include such items as process development in the extraction of other metals - particularly copper; the availability of increasingly sophisticated materials of const- ruction; the advent of the "environmentalist" and related political developments; the massive escalation in the price of energy - particularly oil. The paper concludes with an attempt to forecast the nature of the most effective nickel process of the future, based on extrapolation from the economic and political situation that exists today.

Jan 1, 1988

By J. M. Demarthe

MINEMET RECHERCHE (IMETAL Group, formerly Le Nickel-Penarroya-Mokta) has studied on a laboratory scale and patented a new process to recover metal values -copper- from sulphide ores and concentrates. It combines a cupric leaching, solvent extraction and copper sulphate electrowinning according to the main following steps - A direct and selective leaching of copper sulphide ores or concentrates at atmospheric pressure with cupric chloride to form cuprous and ferrous chlorides and elemental sulphur. Pyrite remains in the sulphur residue. - The leach solution is separated into two parts -In the first one, air is injected to precipitate iron as goethite. The oxidation step can be easily realized at atmospheric pressure by maintaining an excess of cuprous and-ferrous chlorides in the liquor. Copper is extracted from the second part as cupric ion by an LIX reagent. Direct injection or air in the mixing chamber maintains good extraction conditions, so that only one mixer settler is required. - Iron, in the form of ferrous ion, is not coextracted. - Copper is stripped from the organic phase, transferred into a sulfuric phase and sent to sulphate electrowinning cells, which are now conventional in copper metallurgy. - Only electricity and air are required. After a feasibility study, the next step will be to develop it on a pilot and commercial scale.

Jan 1, 1976

By T. K. Bundtzen

Placer gold in the Iditarod and Innoko mining camps of western Alaska is derived from a suite of comagmatic, Late Cretaceous to Early Tertiary, alkali-calcic, meta-aluminous. volcanic-plutonic complexes and peralumi-nous rhyolite sills that intrude Mesozoic flysch. Heavy-mineral concentrates from 42 mining operations and streams draining known mineralized areas in the igneous complexes contain placer gold and a variety of ore minerals derived from epithermal to hypothermal conditions of formation. The minerals include cassiterite, ilmenorutile, samarskite, cinnabar, scheelite, chromite, stibnite, silver sulfosalts, monazite, and zircon. Results of the study show that 1) cinnabar. stibnite, and quartz formed with the bulk of the placer gold in an epithermal lode environment, 2) chromite appears to have originated in mafic phases of monzonite plutons and alkalic basalts, and 3) niobium-tin-tungsten-uranium-silver values may have been derived from stockwork accumulations in cupolas of monzonite plutons.

Jan 1, 1987

By Gabriel Zarate

Mantoverde is a heap leach-SX-EW plant that was commissioned in December 1995 at a production rate of 42,130 tonnes of copper per year and 5.4 million tonnes of ore per year. Copper production was steadily increased reaching a maximum of 62,239 tonnes in 2012 for an ore throughput of 10,5 million tonnes. In order to get these production and throughput rates, a number of changes have been made in the metallurgical parameters of the plant operation since the start up, among them particle size, heap height, acid addition distribution in curing and leaching solution, leach cycles and pad type. Most of the modifications have been implemented after carrying out extensive column test work programs. The modifications implemented and the results obtained, as well as the test work programs carried out, are discussed in this paper.

By Terence Makanyire, Animesh Jha

The dissolution and chemical properties of vanadium, zirconium, and niobium in rutile lattice are analyzed by comparing the octahedral site preference energies, with respect to Ti4+ ion in the solvent phase. The oxides are often present in rutile lattice and interfere in achieving the quality of pigment grade TiO2 due to favourable Gibbs energy for dissolution in the solvent rutile matrix. Binary mixtures of V2O5 { TiO2; Nb2O5 { TiO2 and ZrO2 { TiO2 with compositions of 80, 85, 90, 95 and 97 wt% TiO2 were made, pelletized and sintered at 1100 °C for 24 hours. The solidsolution mixtures were then cooled and leached in 2M NaOH for 3 hours at 60 °C. Phase and lattice parameter characterizations, and microstructural and compositional analyses were then carried out using X-ray diraction and SEM/EDX, respectively. The leachates were analysed by Atomic Absorption Spectroscopy (AAS), using which the solute dissolution model for oxides were investigated.

Jan 1, 2014

By D. F. Suarez

Spontaneous nodulation leading to growth of well developed glossy spheroids (generally hemispheres) of up to 0.06 cm width in 120 min has been observed during copper electrodeposition with certain levels of glue, thiourea and C1-. Thiourea alone can produce spontaneous nodulation but addition of glue and/or Cl- is required for rapid and sustained growth. In most cases once the glossy nodules develop they consume the majority of the copper deposited; thus, the specific current densities (and hence copper electrodeposition rates) on the glossy nodules are about an order of magnitude or, more greater than on the adjacent planar surfaces. The texture of the adjaoent planar surfaces is not glossy in appearance but is well faceted showing the usual deposition grain structure for such additives. Cathode potentials when spontaneous nodulation occurs are about TOO my more negative than with usual copper electroplating. This fact associated with evidence of extremely high levels of cathode surface passivation based on cyclic voltammograms indicates that the conditions which lead to spontaneous nodulation result from a very tightly adsorbed additive surface film. This film breaks down in specific points initiating the glossy nodules which then grow at extremely rapid rates. Current density is also important in spontaneous nodulation. At equal deposition times a current density of 21.5 mA/cm produced much larger glossy nodules than at 48 mA/cm2. The surface concentration of the glossy nodules was much greater in the latter case, however. The role of current density is still not well understood. The role of it as well as the relative roles of the three additives, thiourea, glue and Cl- in spontaneous nodulation is presented. Preliminary results and some possible correlations of these to help explain spontaneous nodulation are presented. It is believed that tankhouse upsets where cathode nodulation occurs may be related to this phenomenon.

Jan 1, 1987

By C. S. Griffith

Lithium Australia NL (ASX:LIT) and ANSTO Minerals have been working together since 2015 on the development of halide accelerated leaching for the extraction of lithium from lithium-bearing micas, spodumene and clays. This technology has been termed SiLeach® process. The driving force behind development of the SiLeach® process, initially, was to develop a hydrometallurgical process to extract lithium from micas and spodumene without the need for the energy intensive, high temperature processing conventionally applied to lithium extraction. This driving force remains today and continues to hold promise in realising the value of previously under-utilised lithium resources. A comprehensive understanding of the technology and its applicability to the processing of micas and spodumene currently exists, and the flowsheet has been rigorously piloted. Production of battery grade lithium carbonate has been demonstrate

By K. Murayama, M. Kawakami, T. Takenaka, S. Yokoyama

"Cokes play an important role of spacer in blast furnace. However, they degenerate during Boudouard reaction. Blast furnace cokes are reacted with pure C02 at I 072 to 1673 K. Reaction rate was obtained by the weight change of spherical specimen. The specimen after reaction was examined by microscopic observation. The reaction rate increased with temperature and was expressed by two Arrhenius type lines. The activation energy was 126 KJ/mol at higher temperature than 13 73 K and 202 KJ/mol at lower temperature range. At the higher temperature range, the reaction proceeded from the surface leaving unreacted core, whereas homogeneously whole inside at lower temperature. The porosity increased from the center to surface at higher temperature, whereas it was almost constant at lower temperature.IntroductionThe cokes have the function of fuel, reductant and spacer to keep gas and liquid flow in the blast furnace. Thus, the reaction mechanism of coke with several gas and the strength after the reaction should be important factor to control the blast furnace operation. The reaction mechanism of coke with C02 has been studied extensively. The rate equations were derived by Gadsby[ I], Ergun[2] and Turkdogan and Vinters[3]. They were compared and discussed by Kobayashi and Omori [ 4]. Effect of crystallization degree on the reaction rate was examined by Kashiwaya and Ishii[5]. Catalytic enhancement effect of ash componets have been clarified by Kashiwaya et. al. [6]. Although degradation of coke in blast furnace has been examined recently[7], however, the degradation of coke after the reaction with C02 has not been well clarified yet. In the present work, the metallurgical coke specimen was heated in N2 and C02 and the reaction mechanism and degradation behavior after the reaction was investigated."

Jan 1, 2000

By J. K. Brimacombe

Plant trials have been conducted at the Tacoma Smelter of ASARCO to assess the effect on tuyere blockage and refractory erosion at the tuyere line, of increasing the injection pressure of air into a Peirce-Smith con¬verter. Four tuyeres each having an ID of 19.1 mm (3/4 in) were installed toward one end of the tuyere line of the No. 4 Converter. Air and oxygen-enriched air were injected at 414 kPag (60 psig) through these tuyeres and at the usual 83 kPag (12 psig) through the remainder of the tuyeres in an otherwise normal converter campaign. The test campaign consisted of 88 charges and lasted for 89 days. During this period, punching of the high-pressure tuyeres was found to-be unnecessary; and when, as a precaution, the tuyeres were cleaned by hand at the end of a charge, they were always open. Also it was observed that the flow of high-pressure air remained constant. Accretion formation around the tip of the high-pressure tuyeres varied from charge to charge and was influenced by the matte grade and the level of oxygen enrichment.

Jan 1, 1983

By Kimio Itagaki

The distribution behaviours of the VA elements between the gas, slag and matte phases in copper smelting were evaluated on the basis of the thermodynamic data, most of which were determined by the authors. The distribution is basically dependent on the process factors such as temperature, the content of the element in charge, the amount of the waste gas and degree of vapour saturation with the elements. The thermodynamic quantities such as the activity coefficients of the VA elements in matte, the activities of iron and copper, SO2 or 02 potential and the distribution ratio of the elements between the slag and matte phases seriously affect the distribution, and the behaviours in various smelters could be explained systematically and reasonably by considering the changes in these quantities, In oxidation smelting at PSO2= 0.1 to 1 atm, the proportion of arsenic and bismuth in gas is predomi22t for the arsenic and bismuth distributions in both smelting and converting stages. The degree of vapour saturation has serious effect on the distribution, and sufficient contact between gas and matte phases is desirable for transferring arsenic and bismuth into gas phase.The elimination of antimony by means of vaporization is not significant. In reduction smelting at po2 = 10-11 atm, the proportions of arsenic and antimony in the gas phase are quite small, but the proportion of bismuth does not change significantly.

Jan 1, 1983

By Joseph Gambogi

In 1998, approximately 57,000 tons of titanium metal was consumed in the form of mill products (1). Only about 5% of the 4 million tons of titanium minerals consumed each year is used to produce titanium metal, with the remainder primarily used to produce titanium dioxide pigment. Titanium metal production is primarily based on the direct chlorination of futile to produce titanium tetrachloride, which is then reduced to metal using the Kroll magnesium reduction process. The use of titanium is tied to its high strength-to-weight ratio and corrosion resistance. Aerospace is the largest application for titanium. In this paper, we discuss all aspects of the titanium industry from ore deposits through extraction to present and future applications. The methods of both primary (mining of ore, extraction, and purification) and secondary (forming and machining) operations will be analyzed. The chemical and physical properties of titanium metal will be briefly examined. Present and future applications for titanium will be discussed. Finally, the economics of titanium metal production also are analyzed as well as the advantages and disadvantages of various alternative extraction methods.

Nov 26, 1999

By Dominik Hofer

A broad spectrum of tantalum containing input materials can be processed for the production of synthetic tantalum concentrate (“SynCon”). The use of these low grade substances offers a secure alternative to mining of coltan in Central Africa. SynCon is produced in a multi-stage pyrometallurgical process, wherefore the melting behaviour of slags presents an important factor especially regarding the energy consumption and its optimisation. The characteristics of a slag comprising mostly Al2O3, CaO, SiO2 and MgO are influenced by the amount of other oxidic constituents which enfolds the main focus of this study. A hot stage microscope serves for the investigation of the slag behaviour in a temperature range from 1000 to 1600 °C under reducing atmosphere (CO/CO2 gas). The experimental results are compared with thermodynamic calculations (FactSage) to get a better understanding of the process.

By N. M. Komkov

The main operation of obtaining zinc from sulfide raw materials by hydrometallurgical technologies is the oxidation roasting of zinc concentrates in fluidized bed furnaces. The technical-economic parameters are determined by the parameters of the roasting process, which depend on the composition of the initial raw materials, the temperature of the bed and on other factors. The predetermined roasting temperature is maintained due to the change of specific efficiency as well as to the quantity of the heat removed from the bed. The efficiency of caissons depends at a high degree on the composition and the thickness of the accretion formed on the surface of the caissons. Forecasting the roasting results is impossible unless we know the mechanism of the accretion formation. The aim of the present paper is the thermodynamic analyses of the behavior of the charge compositions under roasting and the determination of the potential mechanism of the accretion formation. The thermodynamic analyses show that under conditions of the oxidation roasting the thermodynamic probability of the formation of zinc sulfate is higher than the probability of the oxide formation until a temperature of873 OK is reached. The thermodynamic probability of the formation of the lead sulfate is higher than the probability of oxide formation in the entire temperature range of roasting. The probability of formation of ferrites and silicates of zinc decreases only insignificantly the sulfate stability. The results of the investigation of the accretions composItion formed under roasting of concentrates with particle sizes less than 0.02 J..lm (60%), containing 65% of sphalerite (ZnS), 12% of pyrite and chalcopyrite (FeS2 and CufeSz) each, 3% of galenite (PbS), 7% of silica and other non-ore minerals, have shown that the composition of accretion varies depending on the depth of the accretion layer. The accretions on the caissons and the thermo-siphons consist mostly of zinc sulfate (more than 50%). The accretions of forehamber consist mostly of zinc oxide. They also contain ferrites and silicates. The formation of the sulfate zinc accretion in the cold parts of the fluidized bed furnace (the caissons and thermo-siphons) may be explained by a lower temperature on the surface and probably by a catalytic influence of the present oxides in the formation of S02 and sulfates. The nature of the structure of the accretion in the hotter parts of the furnace may supposedly be explained by the formation of elemental vaporous zinc during roasting.

Jan 1, 2003

By S. N. Monteiro, C. M. F. Vieira, A. P. N. M. de Sa, J. P. D. Vitorino

"This work has as its objective to characterize an ash waste and to evaluate its incorporation into a clay to produce bricks and roofing tiles. The waste is a type of fly-ash resulting from the incineration of a selected part of urban garbage, which is basically constituted of organic matter and plastics. The waste was submitted to mineralogical and chemical characterization. Compositions were prepared with incorporation of the waste in amounts of up to 20wt.% into athe clay. Rectangular specimens were prepared by extrusion and fired in a laboratory furnace at 900°C. The physical and mechanical properties evaluated were: linear shrinkage, water absorption and flexural rupture strength. The results showed that the waste is predominantly composed of quartz and calcium compounds. The incorporation of the ash was deleterious to the evaluated properties of the clay. It is suggested that the incorporation should be made in amounts below 5wt. % to avoid deleterious effect in the mechanical strength and water absorption of the clayey ceramic.IntroductionThe world attention has turned to a subject of great concern today, the production and disposal of large amounts of industrial wastes as well as wastes of various sources. When deposed in an unsuitable place, these wastes can cause considerable harm to human health and to the environment. Our planet suffers with air pollution, groundwater and soil contamination as well as silting of rivers and lakes with the growing amounts of our society wastes.The recycling of waste materials is of great interest to the industries, mainly due to the environmental agencies legislation. One of the practices for correct disposal of these wastes being investigated is to incorporate into red ceramics, such as bricks and roofing tiles. The natural variability of the characteristics of the clays associated with the relatively simple processing techniques and also the low performance required for the products allow the presence of relatively high levels of impurities in clayey ceramics."

Jan 1, 2011