By John J. Dunkley

Recent years have seen the increased use of hydrometallurgy in the smelting and refining of metals. However this is often used as a final refining step, following an initial pyrometallurgical smelting process. Huge amounts of material are produced as melts which have to be cast, comminuted, and taken up into solution or leached. A common method is to granulate the melt and then grind it. In the case of metallic melts this can be difficult or unfeasible due to the ductility of the granulated particles. Water atomisation is capable of replacing the granulation and grinding stages with a single process step that can process in excess of 30tlhour of melt into particles as fine as 50 microns. Applications in operation in Co, Cu, Ni, Ag, Au, Pt and Rh refining are discussed together with potential applications in copper smelting.

Jan 1, 2003

By John J. Dunkley

Recent years have seen the increased use of hydrometallurgy in the smelting and refining of metals. However this is often used as a final refining step, following an initial pyrometallurgical smelting process. Huge amounts of material are produced as melts which have to be cast, comminuted, and taken up into solution or leached. A common method is to granulate the melt and then grind it. In the case of metallic melts this can be difficult or unfeasible due to the ductility of the granulated particles. Water atomisation is capable of replacing the granulation and grinding stages with a single process step that can process in excess of 30t/hour of melt into particles as fine as 50 microns. Applications in operation in Co, Cu, Ni, Ag, Au, Pt and Rh refining are discussed together with potential applications in copper smelting.

Jan 1, 2003

By Volovik A. V. Ivtan, Shelkov E. M. Ivtah

"One of the most power consumption Industrial process is production of Al from bauxites (about 45000KWt.hour electrical energy for production of 1 ton. of technical Al). This process is based at the low efficiency and productivity electrolysis technology.Last years IVTAN investigations give to .us information about possibility to use of high temperature shaft- furnaces for efficiency production of alumina (AL2O3 ) technical. aluminium and some all.oys on the base of the high temperature carbon- thermal reduction process. At this case power consumption for production of unit of last, product will be less at the 3-4 times.The carbon-thermal method is allow produce alumina (Al203 ), technical Al and its alloys not only from deficient bauxites, but practically inexhaustible reserve of other types of Al-contain row materials (cianite, sillimonite and so on/The thermal-chemical economical analises of fulfilled at the IVTAN, production of alumina. Base on facts of production and technical technology are especially for ones arguments at the high temperature shaft-furnace technical Al and its alloysIn the last decades of the 20-th century, the discharge into atmosphere of high temperature and. combustion gases places . problems before humanity more and more sharply and becomes of great importance task.But at the same time, as production of material values increases, intensity of pollution of environment increases all time. And the value of new processes and. technologies of material production, aimed at reducing the expenditure of power and pollution of· the environment, also increases."

Jan 1, 2000

By Nicola Baldo, Marco Pasetto

"Recycling of tyre rubber in the road pavement, may be one of the best way to reduce waste tires in large quantities and, at the same time, improve some engineering properties of asphalt mixtures. The paper discusses the results of an experimental study, developed in order to analyse the potentialities of crumb rubber from road tyres in bituminous mixtures, using the dry process. Two types of porous asphalt mixtures and reference mixes without rubber were formulated by the traditional Marshall methodology, and mechanically evaluated by means of the Indirect Tensile Stiffness Modulus test, the Creep test (with confinement), and the Indirect Tensile Fatigue Test. Results of this study indicate that the tyre rubber has a positive influence on the performance characteristics, depending also on the grading and volumetric properties of the mix being studied: an interesting increase of the fatigue life, a better stiffness behaviour at lower temperatures and a bigger permanent deformation resistance at high temperatures are guaranteed. Introduction Recycling the rubber from used tyres, in the construction of road pavement layers, is potentially one of the more interesting and advantageous solutions from both the technical and environmental points of view, in order to reduce the total amount of car and lorry tyres to dispose. In road-building techniques, a technology, termed “wet”, for modifying bituminous binders with crumb rubber has by now become well consolidated. There have been numerous scientific studies conducted on this technology and its applications, particularly in the United States, where it has been adopted and codified in specific technical regulations (ASTM D-6114). If the wet process can be considered amply tested, the same cannot be said for a second technology, termed “dry”, which deserves careful study to evaluate its suitability and advantages. In “dry” processes, the rubber is usually used as a partial substitute of aggregate of equivalent grading and mixed with bitumen after integrating the crumb rubber in the lithic skeleton."

Jan 1, 2008

By Florian Kongoli

Slags and fluxes are important interchangeable dimensions of pyrometallurgical processes. They can increase the efficiency of the smelting, converting and refining processes and improve the quality of the final products. A good slag should have appropriate physicochemical properties such as low liquidus temperature, optimal viscosity, maximum ability to attract undesirable elements, minimum potential of attracting valuable elements, etc .. A good flux, on the other hand, when properly used, can considerably improve the physicochemical properties of the slag since by modifying its chemical composition it could decrease the liquidus temperature, improve viscosity etc.. Consequently, the choice of a good slag and the corresponding fluxing strategies has become indispensable in most of industrial processes. However, the properties of multicomponent slags as well as the effect of several fluxes are known only empirically and confusion exists in the literature and in the industrial practice. In today's reality of frequent changes in the composition of raw materials and that of the fluxes themselves, in the existing or new developing technologies, the quantification of the thermophysicochemical properties of multicomponent slags and the effect of fluxes becomes indispensable. This paper reviews some of the work carried out by the author's group during the last ten years on the quantification of the thermophysicochemical properties of multicomponent slags and on the effect of fluxes in several smelting and converting processes in close relation to their individual characteristics. Several examples have been given in order to demonstrate the fact that when taken outside the context some fluxes can become in fact anti-fluxes.

Jan 1, 2003

By Florian Kongoli

Slags and fluxes are important interchangeable dimensions of pyrometallurgical processes. They can increase the efficiency of the smelting, converting and refining processes and improve the quality of the final products. A good slag should have appropriate physicochemical properties such as low liquidus temperature, optimal viscosity, maximum ability to attract undesirable elements, minimum potential of attracting valuable elements, etc .. A good flux, on the other hand, when properly used, can considerably improve the physicochemical properties of the slag since by modifYing its chemical composition it could decrease the liquidus temperature, improve viscosity etc.. Consequently, the choice of a good slag and the corresponding fluxing strategies has become indispensable in most of industrial processes. However, the properties of multi component slags as well as the effect of several fluxes are known only empirically and confusion exists in the literature and in the industrial practice. In today's reality of frequent changes in the composition of raw materials and that of the fluxes themselves, in the existing or new developing technologies, the quantification of the thermophysicochemical properties of multicomponent slags and the effect of fluxes becomes indispensable. This paper reviews some of the work carried out by the author's group during the last ten years on the quantification of the thermophysicochemical properties of multicomponent slags and on the effect of fluxes in several smelting and converting processes in close relation to their individual characteristics. Several examples have been given in order to demonstrate the fact that when taken outside the context some fluxes can become in fact anti-fluxes.

Jan 1, 2003

By M. J. Collins

Direct pressure leaching of zinc sulphide concentrates was started? commercially in October 1980. Continuing research and development studies at Sherritt and feasibility studies for a number of clients have defined various pressure leach configurations for integrattons with existing roast- 1 each operations and for grass roots plants. Existing and potential applications of zinc pressure leaching are discussed.

Jan 1, 1990

By J. Szekely, S. Rhee

"A mathematical formulation has been presented to describe heat and fluid flow phenomena in CVD operations. In the statement of the problem, which included consideration of plasma enhanced CVD systems, emphasis was placed on identifying the parameters which play a key role in determining the rate and the spatial uniformity of the deposition process. This was done both through the appropriate dimensionless groups and by presenting an extensive set of computed results. The main conclusions that may be drawn from this work are that the deposition rate will be inherently non-uniform for atmospheric CVD systems; this may be somewhat ameliorated by inclining the susceptor or changing the vessel contours. Operation at greatly redeced pressures and for PECVD systems will give a much more spatially uniform deposition rate.1. INTRODUCTIONIn recent years, there has been a growing interest in chemical vapor deposition techniques for the preparation of thin films for semiconductor, photovoltaic applications and for coatings in general, as evidenced by numerous journal articles and symposium proceedings devoted to this topic (1-6). An interesting variant of this technique is to perform the deposition in a plasma or glow discharge at low pressures because this technology obviates the need for the thermal decomposition of the precursor at the substrate surface and permits operation at greatly reduced temperatures (7-10).By far, the largest portion of the reported work dealing with both these aspects of the technology has been concerned with the characterization of the deposit, quite properly so. However, in more recent times it has been realized that the transport aspects of these processes are also deserving of attention because the understanding of heat flow, fluid flow and diffusional phenomena may provide the key to the solution of problems associated with obtaining uniform deposits and the proper scaling of laboratory measurements in order to design industrial CVD systems."

Jan 1, 1986

By Animesh Jha, Chris Dometakis

"Without the use of a flux, only a poor dispersion of ceramic phase can be achieved. A molten-flux-assisted ceramic phase dispersion technique for producing aluminium alloy metalmatrix composites has been developed. In this paper, we report the physical chemistry for the dispersion of TiB2 in molten aluminium. In particular, aspects of the interfacial energy and the thermodynamics of the dispersion reactions are briefly discussed for enhancing the volume of dispersion phase in the molten metal and for controlling their morphology. This investigation also addresses the role of molten flux in the fabrication of AI-alloy mmc using a casting technique. The morphological aspects of the dispersion are explained on the basis of the classical theory· of nucleation.IntroductionMetal matrix composites (MMCs), have long been recognised as an important class of material due to their greater wear resistance, specific stiffness and temperature capability when compared to conventional monolithic alloys. Particulate reinforced composites produced by melt casting techniques have been amongst the first MMCs to achieve commercial market viability. The advent of melt mixing techniques such as the Duralcan™ process have enabled low cost, easily fabricated composites based on the AI-SiC and AIAlz0 3 systems to be produced. In this process, uncoated ceramic particles with diameters 10ltm and larger, are incorporated into conventional monolithic alloys with reinforcement levels up to 25 volume percent. The AI-7Si-SiC metal-matrix composites have good wear resistance, high strength, low density and high thermal conductivity. The combination of these physical and mechanical properties has become a major attraction for the fabrication of light-alloy composite disc rotor brakes for the automotive sector2. However, in silicon-free alloys, SiC is thermodynamically unstable above the composite melting point and is extensively attacked by the melt to form aluminium carbide3 :"

Jan 1, 1996

By José Carlos Abreu

This work presents a kinetics study covering the effects of temperature over the reduction rates of a carbon composite briquette, aiming its use as burden in some of the new alternate ironmaking technologies, such as the Tecnored process. It is reported that increases in the temperature increases the reaction rate. Additionally, the morphology of the iron phase generated during the reduction of these briquettes is presented. It was possible to verify that three types of iron morphology occurred during the process: an external, dense and continuous iron layer, the presence of iron globules at the center of the briquettes and whiskers at the briquette's core. The measurement of the carbon content on the globules and the external iron layer is also presented.

Jan 1, 2003

By V. Jiricny

There is a growing need to process galvanized steel scrap from automobiles, etc., in order to remove the zinc coating that otherwise causes problems in remelting of the scrap in electric arc furnaces. One approach that has moved to the pilot plant stage is that of Metal Recovery Technologies, Inc., of East Chicago (MRI). That company leaches the zinc fiom the scrap with a sodium hydroxide solution. The leached and washed scrap can then be returned to the steel industry. What is left is a sodium hydroxidelzincate solution which must be processed to recover the zinc and the NaOH. Presently, this is done by MRI using electrodeposition on planar electrodes at moderate current density and the resulting zinc is in the form of fine powder which is hard to process into, say, zinc for galvanizing. MRI has supported an investigation of a novel electrode, the spouted bed electrode (SBE), for zinc electrodeposition. In laboratory cells, zinc particles with low porosity have been grown up to 3mm in size. Microanalysis of the deposited zinc showed low level of impurities. DC energy consumption values were usually in the range of 2-2.5 kWg which is well below the energy consumption of the existing cells (and of present-day cells for electrowinning from acid sulfate electrolytes). These results were achieved at current densities (few thousand A/m2) that are much higher than possible with conventional electrodes. Discussion is provided of the scale-up of the cell to a commercial scale.

Jan 1, 1998

By Dong Joon Min, Joo Hyun Park, Mi Sun Choi, Jae Hong Shin

Sublimation of ZrCl4 is important for the production of nuclear grade metallic Zr in Kroll’s process. The sublimation kinetics of ZrCl4 was investigated by TGA under both isothermal and non-isothermal conditions. The sublimation rate of ZrCl4 increased with increasing temperature under isothermal conditions. ZrCl4 sublimation was confirmed to be a zero-order process under isothermal conditions, whereas it was first-order kinetics under non-isothermal conditions. The activation energy of ZrCl4 sublimation under isothermal conditions was 21.7 kJ/mol. The activation energy for non-isothermal sublimation was 101.4 kJ/mol and 108.1 kJ/mol with the Kissinger method and Flynn- Wall-Ozawa method, respectively. These non-isothermal activation energies were very close to the heat of sublimation (103.3 kJ/mol). Sublimation occurs by two elementary steps: surface reaction and desorption. Therefore, the overall activation energy of ZrCl4 sublimation is 104.8(±3.4) kJ/mol. The activation energy of the surface reaction and desorption steps are proposed to be 83.1 kJ/mol and 21.7 kJ/mol, respectively.

Jan 1, 2014

By S. M. Copley, M. Yankova, E. Y. Yankov, J. A. Todd

"Nanophased coupled growth structures, with spacings of -10 nm, have been observed in banded microstructures produced by laser melting hypoeutectic Ag-Cu alloys. These coupled growth structures comprised a Cu-rich phase of width - 1 nm and a Ag-rich phase of width - 9 nm. In this paper, microstructural observations of nanophased coupled growth structures in hypo eutectic AgCu alloys are presented. Laser beam velocities for the transition from banded to microsegregation free microstructures are modelled and compared with experimental values. Models are presented to show that, at a critical undercooling, initial growth of a Ag-rich, metastable, extended solid solution is rapid but slows to a halt as copper is partitioned into the liquid at the solid/liquid interface. Following nucleation, the coupled growth structure then grows until the partitioned copper is consumed, at which point growth of the Ag-rich solid solution is again accelerated. This cycle then repeats resulting in banded microstructures comprised of 750 nm of the Ag-rich extended, metastable solid solution, followed by 250 nm of the coupled growth structure.1. Structural Studies of Laser Melted and Resolidified TrailsPresented here are observations of laser melted and resolidified trails in Ag-Cu alloys obtained at beam velocities ranging from 0.7 to 34 cm S·I. When the laser beam is scanned along the surface (positive x-direction) with a velocity Vb a melt pool with the shape given in Fig. 1a moves with the beam. The isotherms move with the velocity, Vi,. = Vb cos.p. Calculations employing the thermal analysis of Kou, Hsu and Mehrabian [1] for the beam velocities of this investigation and for the thermal properties of AgCu alloys, indicated that, .p, the angle between the isotherm velocity and beam velocity should be small at the surface where microstructural studies were made. This prediction was supported by observations of trail cross-sections. Based on these observations, and the calculations which include latent heat effects, the isotherm velocity for observations near the surface in our investigation was taken to be 27 cm S-I."

Jan 1, 1994

By Thomas J. Keefe, O&apos

Results of metal electrodeposition experiments conducted at the University of Brussels and University of Missouri-Rolla over the past few years are reviewed in terms of the relationship and impact on industrial processes. Examples are cited from common electrowinning, electrorefining, or electroplating operations for copper, zinc, nickel, cobalt and silver. The following topics are considered : metallographic structure, crystallographic texture, surface morphology, nucleation and growth, additive monitoring and effects, high current density, substrate related properties including adhesion. The studies were conducted on a variety of scales from laboratory beaker tests to full sized pilot and industrial operating plants.

Jan 1, 1993

By Stephen Chryssoulis, Stamen Dimov

Detection and quantification of precious metals (Au, Pd, Pt, and Rh) in spinels and silicate minerals is important for establishing the maximum attainable recovery by sulphide flotation. To achieve this goal subpart per billion (ppb) detection limits are required plus the ability to quantify results. Existing quantitative microbeam techniques (EPMA, PIXE, SIMS, TOFLIMS) have limits of detection in the O. l-200ppm range. Time-of-flight resonance ionization mass spectrometry (TOF-RIMS) is a microbeam analytical technique that allows for the identification and quantification of atomic species in very small quantities. It utilizes a tunable laser source for resonant excitation and ionization of a particular element of interest and has some unique features: elemental selectivity, linear response over a large dynamic range and very high sensitivity. The analysis consist of three steps: (i) the solid sample is vaporized by laser ablation to form a plume containing neutral atoms, (ii) the neutral atoms of a specific atomic element in the plume are resonantly excited and ionized by another tunable laser, and finally (iii) the ions created are mass analyzed in a time-of-flight mass spectrometer. A TOF-RIMS mass spectrometer was developed at AMTEL for trace element analysis of Au, Pd, and Rh in minerals. The spectrometer was calibrated using homogeneous CANMET and NIST reference samples covering three orders of magnitude in concentration. Attained minimum detection limits (MDL=2cr of the background) are in the low ppb range.

Jan 1, 1999

By Chuanfu Zhang, Liwei Liang, Yanxin Wu, Jinliang Wang

"According to the reaction shaft operation characteristics during the flash smelting process, 15 groups of slag samples containing high Fe3O4 were prepared by some chemical reagents, and then the slag viscosities were measured using a RTW-10 type synthetic test instrument for melt physical property by the rotating cylinder method. The effects of Fe/SiO2 ratio (mFe/mSiO2), Fe3O4 content (wFe3O4), Cu2o), MgO content (WMgO) and Cao content (wCaO) on the slag viscosity were also studied. Results show that slag viscosity is decreased with the increase of temperature, mFe/mSiO2, wCu2o, wMgO and wCao, and with the decrease of wFe3O4, under the range of slag contents: mFe/mSiO2 1.36~1.78, wFe3O4 17.83%~21.18%, wCu2o 3.51%~8.34%m wNgI 2.21%~6.57%m w/caI 6.22%~9.387% and temperature range if 1250 o/c~1450 oC. Only wFe3O4m and w/caO have great influence on the slag viscosity when temperatures as high as 1400 oC. Only wFe3O4 and wCaO have great influence on the slag viscosity when temperatures as high as 1400 oC or so. To form a freeze slag with higher viscosity inside the reaction shaft, wFe3O4 should be more than 20% and wCaO should be less then 6%.IntroductionSince its appearance in 1949, Outokumpu flash smelting technology has making continuous innovation and has become the most competitive intensified smelting technology [1], widely considered to be the standard clean smelting process [2]. At present, flash smelting technology is adopted to newly build or reconstruct most of the world's copper or nickel smelting enterprise [3]. Reaction shaft is the most important part of the flash smelting furnace. During the flash smelting process, reaction shaft must be able to withstand the following harsh conditions at the same time: 1) high temperature varying from 1400 °C to 1500 °C. 2) strong oxidative atmosphere containing 50% - 80% oxygen. 3) solid particles and melt with speed up to l00 m/s. 4) high acidic or basic slag with strong chemical corrosiveness. 5) smelting gas containing 50% - 80% SO2. 6) matte with strong dissolution."

Jan 1, 2012

By H. Matsuda, T. Iwashita, H. Awata, H. Liwei, D. Hirabayashi, Y. Saito, S. Ozawa, Y. Goto

"The present study is concerned with investigating the effect of chemical treatment on enhancing the HCl absorption capacities of coal burnt ash and slag. It was found that the HCl absorption capacity of coal burnt ash discharged from fluidized bed combustor was improved by hydration with water and 5% polyethylene glycol solution. This phenomenon was based on an increase of the specific surface area of treated coal burnt ash. The HCl absorption capacity of hydrated ash with polyethylene glycol solution was almost equivalent to that of standard CaO and Ca(OH)2. In particular, the specific surface area of hydrated ash with polyethylene glycol solution was found to be 19 m2/g, which was more than over eight times larger than that of raw sample. Hydrated slag treated with lON sodium hydroxide solution also showed high HCl absorption capacity, with highly improved surface area. It was found that the absorption capacity of slag for HCl depended on the treatment time, showing the maximum absorption capacity for 12 hours of hydration treatment.IntroductionA large amount of coal burnt ash, slag and dust are discharged from such industrial processes as coal combustion and metal refinery etc., and it becomes an serious problem to recover and diminish these solid wastes because of the shortage of dump sites and subsequent metal elution to the environment. Figure 1 shows the present situation of reutilization of coal burnt ash and slag in Japan [1,2]. It is shown in this figure that these solid wastes are recycled as materials in the fields of earthwork, agriculture and forestry etc. A part of these solid wastes, however, is still dumped to landfill. To decrease this dumped amount, the development of environmentally friendly reutilization technique for these solid wastes is of great importance."

Jan 1, 2000

By Yanhui Liu, Xuewei Lv, Chenguang Bai

A thermodynamic model for determining the surface tension of molten slag by considering the surface tension and molar volume of the pure oxide component, and their ionic radii was extended to the slag bearing high TiO2 (varying from 80 to 67%) at 1973 K. The iso-surface tension curves for the FeO-TiO2-Ti2O3 ternary system at 1973 K are almost parallel to the FeOTi2O3 line. TiO2 plays a role of surface-active solute, and its surface-active effect is attenuating with increasing the TiO2 content. The iso-surface tension curve shifts away from the TiO2 corner, indicating that the surface tension of the ternary slag decreases along with the addition of SiO2. The reasons include the addition of SiO2 with lower surface tension and the decrease of the total ion moment at the surface. Both CaO and MgO can bring about that the iso-surface tension curve shifts towards the TiO2 corner, indicating that the surface tension of the ternary slag increases along with the addition of CaO or MgO. CaO has a more pronounced effect on increasing the surface tension of the ternary slag than MgO at an equimolar amount addition. The increase of the surface tension results from both the compositional change and the variation of the slag structure.

Jan 1, 2015

By Suresh Sundarraj

A diffusion mass transport model for predicting the microsegregation in a solidifying and coarsening dendritic mushy region of a binary alloy is presented. Two versions of this model are tested; one based on expressing the solute concentration in terms of mole fraction and the other on expressing the solute concentration in terms of mass fraction. On comparing previous model data sets and conditions, used in the analysis of Aluminum-Copper systems, a number of inconsistencies emerge. These inconsistencies are resolved on identifying a single set of data and conditions which take account of compositional density changes, "non-linear" thermodynamics and dynamic coarsening. An additional investigation is carried out to study the effect of assumed cooling mechanisms.

Jan 1, 1992

By Boyd Davis, Vladimiros Papangelakis, Joshua LaMarre, Jan de Bakker

"HCl leaching using molten salt hydrates has the potential to improve the extraction of nickel from laterite ores. However, as in other HCl leaching applications, recovery of HCl is key to process economics. Spray pyrohydrolysis, which is used in current chloride-based flowsheets, is associated with a high energy cost. The authors have developed a proposed laterite leach circuit using an alternative HCl recovery route. The leach circuit envisions a leach by concentrated (33%) HCl in an MgCl2 molten salt hydrate (MSH) or brine medium, followed by Ni/Co recovery and iron precipitation. Magnesium and chloride are precipitated from solution as magnesium hydroxychloride; this hydroxychloride is thermally decomposed to produce HCl gas. The proposed flowsheet employs a chloride leach circuit with simpler equipment and lower energy cost than in the conventional practice of pyrohydrolysis. Laboratory work investigated key aspects of the flowsheet, including precipitation of magnesium hydroxychlorides and their composition; magnesium hydroxychloride thermal decomposition; and iron control.Introduction As sulphide nickel ores become harder to mine and more complex to process, laterite ores will increase in importance. Laterite ore deposits can be divided into two main mineralogies. Limonite ores consist mostly of hydrated iron oxide, FeOOH, with 1-3% nickel substituting for the iron. Saprolite ores consist of iron-magnesium silicates, (Fe, Mg)2Si04, again with some nickel substituting for the metal ions. Limonite ores can be treated using the HP AL (High Pressure Acid Leach) process, in which the ore is reacted with sulphuric acid at high temperature in an autoclave. HP AL, however, cannot in general be used to treat saprolite ores because the magnesium enters solution and consumes sulphuric acid, which results in excessive spending on lixiviant. It is therefore desirable to find a hydrometallurgical process specifically for saprolite ores that can provide better results than the treatment options currently available."

Jan 1, 2011