By Moto Goto

Onahama Smelter of Onahama Smelting & Refining Co., Ltd. has two green- charge reverberatory furnaces; the old furnace was constructed in 1965 and the new one in 1973. This paper discusses the use of oxygen-oil burners in a green-charge reverberatory furnace and also compares the copper loss in slag between the two furnaces at Onahama Smelter. During the past ten years of operation, no shutdowns of the old furnace were necessary and the smelting capacity was increased by 25% by the use of two oxygen-oil burners. These burners are suitable for a green-charge reverberatory furnace to in- crease the smelting capacity without causing an increase of the exhaust gas volume and refractory erosion. After two years of operation of the old furnace, a bottom build-up in the charging zone of approximately 50 centimeters was experienced, and this build-up has stayed at this level since then. In 1973, a new additional reverberatory furnace was put into operation. Copper content in slag of the new furnace was lower by approximately 0.15% than that of the old one during the first several months after the start-up. Investigations were then made on the effect of the bottom conditions in the charging zone on the copper content in slag.

Jan 1, 1976

By D. H. Magoon

The zinc smelter of Cominco Ltd. at Trail, B.C. Is the largest In the western world. A total of 550.000 tonnes of concentrate are proceed at the smelter annually. Approximately 80% of the zinc concentrate is roasted and the remainder Is treated by aqueous oxidation preaaure leaching. The zinc concentrate roasting and sulphur dioxide gas processing plants have undergone many changes over the years. This paper describes the processes and equipment currently used for concentrate roasting, S02 gas cooling and cleaning, mercury removal, sulphuric acid production liquid S02 production, and tall gas S02 scrubbing. The recent Installation of an advanced process control system for the operation of these Integrated processes Is also described.

Jan 1, 1990

By N. M. Komkov

The main operation of obtaining zinc from sulfide raw materials by hydrometallurgical technologies is the oxidation roasting of zinc concentrates in fluidized bed furnaces. The technical-economic parameters are determined by the parameters of the roasting process, which depend on the composition of the initial raw materials, the temperature of the bed and on other factors. The predetermined roasting temperature is maintained due to the change of specific efficiency as well as to the quantity of the heat removed from the bed. The efficiency of caissons depends at a high degree on the composition and the thickness of the accretion formed on the surface of the caissons. Forecasting the roasting results is impossible unless we know the mechanism of the accretion formation. The aim of the present paper is the thermodynamic analyses of the behavior of the charge compositions under roasting and the determination of the potential mechanism of the accretion formation. The thermodynamic analyses show that under conditions of the oxidation roasting the thermodynamic probability of the formation of zinc sulfate is higher than the probability of the oxide formation until a temperature of 873°K is reached. The thermodynamic probability of the formation of the lead sulfate is higher than the probability of oxide formation in the entire temperature range of roasting. The probability of formation of ferrites and silicates of zinc decreases only insignificantly the sulfate stability. The results of the investigation of the accretions composition formed under roasting of concentrates with particle sizes less than 0.02 um (60%), containing 65% of sphalerite (ZnS), 12% of pyrite and chalcopyrite (FeS2 and CuFeSz2 each, 3% of galenite (PbS), 7% of silica and other non-ore minerals, have shown that the composition of accretion varies depending on the depth of the accretion layer. The accretions on the caissons and the thermo-siphons consist mostly of zinc sulfate (more than 50%). The accretions of forchamber consist mostly of zinc oxide. They also contain ferrites and silicates. The formation of the sulfate zinc accretion in the cold parts of the fluidized bed furnace (the caissons and thermo-siphons) may be explained by a lower temperature on the surface and probably by a catalytic influence of the present oxides in the formation of S02 and sulfates. The nature of the structure of the accretion in the hotter parts of the furnace may supposedly be explained by the formation of elemental vaporous zinc during roasting.

Jan 1, 2003

By M. Omneya El-Hussaini, M. Galal Abdel Wahab, A. Mohamed Mahdy, M. Fathi El Shahat

"Um-Gheig Pb-Zn representative sample was collected from the main adite of Um-Gheig mine along Red Sea coast in Egypt. Its chemical analysis shows that, it contains 16% Zn, 2.3% Pb, 0.1% Cd and 0.1% B as elements of interest. After H2SO4 agitation leaching, the chemical composition of Um- Gheig Pb-Zn deposit ore residue assayed 2.26% Pb, 1.5% Zn, 0.085 % B and 0.01% Cd. This residue was leached with 20% HCl at S/L ratio 1/3 for 2 hours at 80o C. The chloride leach liquor was found to contain 18 g/l Pb, 13 g/l Zn, 0.1 g/l Cd and 0.75 g/l B with the corresponding leaching efficiencies 79%, 86%, 100% and 88% respectively. Lead was precipitated from the chloride leach liquor using concentrated H2SO4 to obtain PbSO4 with precipitation efficiency 96%. While boron was extracted by the selective resin Amberlite IRA743 with loading efficiency of 80%. On the other hand, Zn and Cd were precipitated using Na2S solution with 86.7% and 100% recovery efficiencies respectively.IntroductionLead-zinc ores occur in Egypt in a few localities distributed along the Red Sea coast between El Qusier and Ras Banas.. The reserve of the ore deposits has been estimated by Soviet and German Experts to be about 900,000 Ton, [1]. Onal et al., [2] recovered Pb from Pb–Zn sample containing 10.17 % Pb and 10.98 % Zn from Aladag in Turkey. El-Sherif, [3] used concentrated HCl to leach lead-zinc ore sample of Um-Sammuki area in Egypt. As had been published by Marchioretto et al. [4], the precipitation of heavy metals with lime, sulfide and caustic soda are the most commonly used economical methods for metal removal. Lead was completely removed from the anaerobically digested sludge by precipitation with NaOH and Na2S at waste water treatment plants. Mahdy et al., [5] had successfully extracted boron from the bittern solution of Qaron Lake by ion exchange resin (Amberlite IRA 743). The extraction of boron was mainly depending upon the pH value. They extracted 80% of boron at pH 5.5, while at pH 3.9 about 74% boron was extracted. Kabay et al. [6] used the column-mode to remove 1g/l of boron from geothermal waste water of the Kizildere-Geothermal Power Station by using Diaion CRB 02 Nglucamine- type chelating resins. In this regard, the removal of lead, cadmium and boron allow the residue to be reclassified as non hazardous material."

Jan 1, 2008

By Taiping Lou

The effects of slag composition, additive agents, and heat treatment conditions on the perovskite (CaO ? TiO2) crystal morphology, the precipitation behavior, the crystal growth and the volume fraction (VF) in the Ti-bearing blast furnace slags were investigated. The morphology of perovskite is dispersed dendriform in molten slags. The crystal growth mechanism of the remelting of fine dendrites and the coarsening of larger grains exists throughout the solidification of molten slags. With the temperature decrease, the VF was increased and Perovskite transformed from fine dendrites to coarsening ones or equiaxed grains. The lower cooling rate can increase the VF and coarsen the grain obviously, while higher cooling rate will decrease the VF and reduce the average equivalent diameter (AED) of Perovskite. When .increasing the content of CaO and Fe20}, the VF can increase obviosly. However, high basicity will give rise to the increasing of viscosity of slag, which result in the reducing of the AED. The experimental results showed that additive CaF2 and MnO can efficiently decreased the viscosity of the slags, and obviously improved the morphology of perovskite and promote growth.

Jan 1, 2000

By J. Y. Hwang

The relationship between coal characterization and physical cleaning has not been well understood due to the complex nature of coal. Therefore, it is difficult to apply the results of coal characterization to predict and evaluate the performance of a physical separation (e.g. flotation). Eight U.S. bituminous coals were analyzed and studied petrographically in conjunction with washability and flotation tests. The results show that grindability correlates to ash and fixed carbon contents; liberation determined directly by petrographic techniques is close to liberation determined indirectly by washability; and an ideal separation efficiency can be determined by measuring the inertinite content and the washability separation efficiency using a heavy liquid with a density of 1.4. The ideal separation efficiency was attained for most coals by packed column flotation. The ideal separation efficiency can be used for comparing process technologies and process parameters.

Jan 1, 1988

By James C. Barker

Recent investigations of a 55-km long trend of intrusive complexes on southern Prince of Wales Island have identified significant resources of Nb, Y, REE. U, Zr, and a host of potential by-product metals. The northwesterly trend comprises multi-phased sodic alkaline and peralkaline diorite, monzonite, syenite, and riebeckite granite. There are at least three significant deposit types recognized, two of which, 1) pegmatite dikes/vein-dikes that zone laterally from the intrusions and 2) concentrically zoned pegmatites, contain most of the lithophile metals. A third, epigenetic replacement-type mineralization, contains much of the U resource. Other deposit types with minor or unknown resource potential include diatremes, carbonatite, and placers. This report summarizes the deposit evaluations, characterizes the mineralization, and estimates the resources. To date a total of 40.7 million tons of mineralized material is estimated as indicated or inferred. Most of the Y203 plus REO is at a grade exceeding 0.5% and half of the Nb20S exceeds 0.125%. Tonnage estimates would likely be substantially lncreased with additional exploration. Mineralogy is generally fine-grained and complex, and consists of more than a dozen principal REE-Y-Nb-U-Th-Zr phases, the sum of which may compose up to half of the rock. Approximately half of the REE-Y content comprises the heavy yttrium subgroup which is uncommon compared to deposits elsewhere. Although the Alaskan deposits are likely subeconomic at today's metal prices and consumption levels. recent technological advances suggest future demand may increase.

Jan 1, 1988

By Carlos Mauricio Fontes Vieira, Sergio Neves Monteiro, Thiago Samarão Motta

This work has as its objective to characterize ceramic bodies formulated with ornamental rock waste and two different clays to produce ceramic paver. Specimens were made by uniaxial press-molding at 20 MPa and then fired at 950 and 1050oC respectively. The determined technological properties were: plasticity, dry bulk density, linear shrinkage, water absorption and flexural rupture strength. The results showed that the type of the clay has strong influence on the properties of interest for heavy clay ceramics. The investigated waste must be incorporated in small amounts to avoid increasing in the porosity of the ceramics.

Jan 1, 2015

By Jong-Ren Tarng, Gin-Hwa Chen, Wen-ku Chang, Ke-Ming Lin, Yuan-Haun Lee

"The majority of early studies used X-ray diffraction, but this requires a model to interpret the diffraction processes. A turbostratic model has been applied by Warren, Franklin and Bacon to a wide range of materials including both soft and hard carbons. Maire and Mering applied the same methods to the interpretation of the (001) lines of a series of graphitic carbons. In our case, graphitic carbons undergone high temperature and high pressure graphitization processes have been evaluated by the same methods. It were found that most technological XRD data were obtained by a Rietveld method with the least-squares refinements could be in the simplest way since the full correction technique is very laborious. The behavior of carbon materials as it proceeds through the graphitization process is characterized by changes in the measured interlayer spacings (d) a~ a function of temperature. A series of graphitic carbons including the transformation of diamond to graphite through the process under high temperature and high pressure have been evaluated. A simple calibration equation has been established. IntroductionRecently, in battery industry, carbon materials are used as cathode in lithium ion batteries. However, graphitization of those carbon materials is concerned as if lithium ion intercalated into those carbon cathode. Both high-graphitization and low-graphitization carbon materials are suitable for this kind of application.As for graphitization, the starling materials from which carbons may be prepared vary extensively from pure chemical compounds, to mixtures containing II wide range of molecular weights, such as pitches. So its graphitizing, perhaps the most notable feature of the process, is the very wide range of temperature over which the perfection increase, unlike the more common transformations of solid state materials which occur in a narrow temperature range. The variables involved in the conversion of the initial hydrocarbon to a carbon residue, which may vary widely in final perfection, are time, temperature, stress and impurity content"

Jan 1, 1996

By Dong Hoon Han

The sulfation rates of magnesium oxide and calcium oxide (molar ratio 7:3) contained in calcined CMA ( calcium magnesium acetate) by SO2 were measured. The experiments were carried out in the temperature range 700 to 1100 °C and under the SO2 concentrations of 0.3 to I mol % (5 % 02). In the low-temperature range below 830 °C the reaction produced CaSO4.3MgSO4 and unreacted MgO, but no MgSO4 phase. The formation of CaSO4.3MgSO4 phase has a significant implication in that it allows the utilization of MgO for SO2 removal whereas the sulfation of MgO from conventional sources is so slow that it is of no practical interest. Thus, the calcined CMA can remove SO2 at lower temperatures than conventional SO2 absorbents and at a greater capacity. Above 950 °C only CaO reacts with SO2, but at a much greater rate than the calcined Ca(OH)2, which is one of the most reactive SO2 absorbents.

Jan 1, 1998

By Cynthia Belt

"Before energy can be saved in the materials industry, the process must be understood. At the same time, baby boomers are starting to retire. New people are entering the field without experience and training especially in methods to save energy. Various classroom courses, seminars, books, software, and websites are available for the professional to better understand the industry with the ultimate goal to reduce energy use. This paper is a review of what is currently available with some comments on potential needs.IntroductionEnergy use is high within the materials industry. For the United States, the primary metal industry uses 8% of all energy used in manufacturing (Figure 1 )1 or 1, 736 trillion BTUs per year. Sadly, while energy use is high, energy management is not universal within the industry. Counting both internal programs and external such as the utility supplier, equipment manufacturers, federal and state programs, only 66% of primary metals companies participate in an energy management activity1.For the materials field, process heating is the majority of the energy use in a plant2. Understanding and optimizing process heating is a critical need for materials energy professionals. Surprisingly, process heating is not necessarily the work addressed within an energy program. The U.S. 2006 Manufacturing Energy Consumption Survey (see Table 1) found more primary metal companies addressing lighting with 31 % participation versus 15% with process heating work even though energy used in lighting tends to be a minor (in the range ofl-3% ofa typical plant's energy use)."

Jan 1, 2013

By Xiang-dong XING, Zhen-yang wang, Xing-le LIU, Jian-Liang Zhang

Experiments were carried out by adding CaF2 as catalyst in a Ar atmosphere to study the isothermal reduction kinetics of vanadium titano-magnetite carbon composite pellets under high temperature in the range from1473 to 1673K. By analyzing reduction mechanism, it was found that the rate controlling step was gas diffusion, and the activation energy was 178.39kJ•mol-1 without adding any catalysts. Adding CaF2 of 3% to vanadium titano-magnetite carbon composite pellets can decrease the apparent activation energy of reduction, and the decrease extent was 14.95kJ•mol-1. In addition, temperature is an important factor influencing on reaction rate.

Jan 1, 2015

By Y. Pokhvisnev, S. Vandariev, A. Yatshenko-Juk, V. Valavin, V. Romenets

The technology of the liquid-phase reduction process known as Romelt was developed in the Moscow Institute of Steel and Alloys in 1979. The pilot plant was constructed at the Novolipetsky Steel Works (Russia) in 1984. Investigations into processing zinc-containing blast oxygen furnace dust and slag from the Lead and Zinc Works at the pilot Romelt plant proved the perspective of using this technology for processing zinc and lead-containing materials. In this article, the description of Romelt technology, basic technological information of trials at the Romelt plant using zinc-containing materials, compositions of charging materials, metal, slag, gas and dust are presented. The influence of flue gas composition on the composition of zinccontaining dust is shown.

Jan 1, 2000

By C. Dupuis

Thiourea is a promising reagent for gold extraction especially from refractory ores that cannot be treated by traditional cyanidation route. In this study recovery of gold from thiourea leaching solutions was investigated by direct electrowinning. The electrolysis cell consisted of a carbon flow-through cathode and a lead anode. The anodic and cathodic compartments were separated by a membrane. Galvanostatic mode was chosen for operation of the cell. Factors affecting recovery efficiency such as cathode thickness, linear flowrate, current intensity, thiourea and gold concentrations were investigated. The influence of some species in solution on efficiency and selectivity of recovery was investigated. Gold recovery reached 99% but current efficiency was lower than 10%. The complex formed with ferric ion and formamidine disulfide are reduced before gold-thiourea complex. Thiourea consumption occurred during leaching mainly by oxidation and reaction with dissolved copper.

Jan 1, 1989

By Kazuteru Tozawa

Surface tension, density and viscosity coefficient of acidic copper sulfate solutions simulating electrolyte solution for electrolytic production of copper have been measured and are summarized as a function of the solution composition and temperature. Nickel sulfatc is taken to be a representative coexisting sulfate that affects the physical properties of the copper sulfate electrolyte solution. The sulfates in the solutions, including sulfuric acid, increase the physical properties under consideration. Gelatin, representing organic additives for electrolyte solution, was found to sensitively affect the surface tension of the solution at low concentration of up to 200mgIL. The surface tension was markedly lowered by the addition of gelatin and the increasing concentration of gelatin led to a more pronounced decrease in the observed values. The surface tension gradually increases with time after addition of gelatin and the increase is enhanced by higher acid concentration and higher temperature. The observed change in the surface tension is considered to reflect the preferential adsorption of gelatin to the bubble-solution interface and the decomposition of gelatin due to hydrolysis to form various molecules having smaller molecular weights.

Jan 1, 2003

By R. Hurman Eric

Within the Ag-Pb-S ternary system, the boundaries of the immiscibility region together with the tie-line distributions were re-established at 925°C by the equilibrium-quenching technique where samples were kept in evacuated and sealed silica capsules. Activities of Pb were measured by the dew-point method along the Ag-Pb binary at 925°C, 1100° and l200°C, positive deviations were observed and the results were modeled by the Krupkowski formalism. Activities of Ag, Pb, and S, along the ternary miscibility gap were calculated at 925°C by utilizing the boundaries binary thermodynamics, phase equilibria and tie-lines. Activities of PbS within the pseudobinary Ag2S-PbS mattes were also measured by the dew-point technique and the results were again modeled by the Krupkowski formation where negative deviations were observed.

Jan 1, 2003

By R. Hurman Eric

Within the Ag-Pb-S ternary system, the boundaries of the immiscibility region together with the tie-line distributions were re-established at 925°C by the equilibrium-quenching technique where samples were kept in evacuated and sealed silica capsules. Activities of Pb were measured by the dew-point method along the Ag-Pb binary at 925°C, 1100° and 1200°C. positive deviations were observed and the results were modeled by the Krupkowski formalism. Activities of Ag, Pb, and S, along the ternary miscibility gap were calculated at 925°C by utilizing the boundaries binary thermodynamics, phase equilibria and tie-lines. Activities of PbS within the pseudobinary Ag2S-PbS mattes were also measured by the dew-point technique and the results were again modeled by the Krupkowski formation Where negative deviations were observed.

Jan 1, 2003

By Takahiro Miki

In order to use metallurgical grade silicon (MG-Si) as a starting material for solar cell, phosphorus has to be removed from silicon because phosphorus is a n-type dopant. On the other hand, silicon, ferrosilicon, and silicomanganese are widely used as deoxidizers in steel refining processes. Since most of the phosphorus introduced during the deoxidation process is brought into final products, it is important -to lower the phosphorus content of these alloys. Hence, thermodynamics of phosphorus in such metals is important for the evaluation of dephosphorization processes. In the present study, thermodynamic properties of phosphorus in molten Si-P alloys at 1723- 1848K and those of Si-Fe-P and Si-Mn-P alloys at 1723K have been determined by equilibrating respective metals in a controlled phosphorus partial pressure. The results are expressed as follows.

Jan 1, 1998

By I. Barin

The thermodynamics of cyclone smelting of sulphidic copper ores is described using as example the production of copper matte with 75 wt % Cu. Equilibrium calcualtions and material and energy balances show that an increase in process temperature from 1600 K to 1900 K results in the extensive transfer of minor elements such as As, Sb, Bi, Pb, Zn,.... to the gas phase. A pilot plant for carrying out the cyclone smelting process is described. Calculations of material and heat transfer for the reaction of ZnS show that the smelting reactions of sulphides in the cyclone take place very rapidly at high temperatures. The dissociation of the sulphides with subsequent oxidation reactions in the gas phase plays an important part in. the process and is mainly controlled by heat transfer.

Jan 1, 1983

By D. F. Suarez

Spontaneous nodulation leading to growth of well developed glossy spheroids (generally hemispheres) of up to 0.06 cm width in 120 min has been observed during copper electrodeposition with certain levels of glue, thiourea and C1-. Thiourea alone can produce spontaneous nodulation but addition of glue and/or Cl- is required for rapid and sustained growth. In most cases once the glossy nodules develop they consume the majority of the copper deposited; thus, the specific current densities (and hence copper electrodeposition rates) on the glossy nodules are about an order of magnitude or, more greater than on the adjacent planar surfaces. The texture of the adjaoent planar surfaces is not glossy in appearance but is well faceted showing the usual deposition grain structure for such additives. Cathode potentials when spontaneous nodulation occurs are about TOO my more negative than with usual copper electroplating. This fact associated with evidence of extremely high levels of cathode surface passivation based on cyclic voltammograms indicates that the conditions which lead to spontaneous nodulation result from a very tightly adsorbed additive surface film. This film breaks down in specific points initiating the glossy nodules which then grow at extremely rapid rates. Current density is also important in spontaneous nodulation. At equal deposition times a current density of 21.5 mA/cm produced much larger glossy nodules than at 48 mA/cm2. The surface concentration of the glossy nodules was much greater in the latter case, however. The role of current density is still not well understood. The role of it as well as the relative roles of the three additives, thiourea, glue and Cl- in spontaneous nodulation is presented. Preliminary results and some possible correlations of these to help explain spontaneous nodulation are presented. It is believed that tankhouse upsets where cathode nodulation occurs may be related to this phenomenon.

Jan 1, 1987