The restraining effects of war conditions on oil-field development are well illustrated by statistics on South Texas † fields for the year 1942. Statistics also show a decline in wildcatting, but this decrease is much smaller than that shown by field activity. In comparison with results in 1941, there was a reduction of about 44 per cent in the total number of wells drilled in the area (802 in 1942 against 1452 in 1941) This 44 per cent drop represents declines of 50.4 per cent in field wells and of 17.4 per cent in rank wildcats. Field wells (exclusive of 18 wildcats that discovered fields) totaled 598; also, 204 rank wildcats were drilled (see Tables 3 and 4). The corresponding figures for 1941 are 1205 field and extension wells and 247 rank wildcats. In this connection, it should be noted that whereas in 1941 the rank wildcats made up only 17 per cent of all wells drilled in the area, their percentage of the 1942 total was 25.4 per cent. In spite of the decrease of 43 in the number of rank wildcatst drilled, there were 18 new productive areas discavered, one more than the 17 new fields found in 1941. Thus the field-discovery rate for 1942, one new field for every 11.3 wildcats drilled, compares favorably with the I to 14.5 rate of 1941. Thirteen new producing levels were opened in fields; this includes the finding of 44' gravity crude on the west flank of the Sejita field in a 5700-ft. sand, which produccs distillate higher on the structure. Interesting, and showing the general scarcity of sand discoveries, is the fact that of the 13 new sands discovered, 7 were found in Jim Wells County. The year's sand-discovery rate of one new level for every 46 field wells compares very unfavorably with the I to 19.7 rate of 1941, during which 61 new producing horizons were found. Developmeilt of new fields was on a small scale. In several instances activity in these areas was not carried beyond the drilling of the discovery well. The field discoveries of 1942, together with the type of production obtained from the discovery wells and the total number of wells (productive and dry) drilled in them, are given below: Discovery Num- Field.I County Well her Produced Wells I. Cadena....... Duval Oil 2 a. Garza......... Duval Oil I 3. Dinn......... Duval Gas I 4. Keller......... Duval Gas I 5. East.......... Tim 0 11 I 6. Green Branch . McMullen Gas 3 7. Frost. .GreenBranch........ Starr Oil I 8. Garcia........ Starr Oil 6 9. Ulrich........ Starr Oil 4 10. Lykes......... Webb Oil 2 11. McLean....... Webb Oil 9 Iz. Alamo........ Hidalgo Distillate 2 and gas 13. Penitas....... Hidalgo Distillate 2 and gas 14. Xmpnan..... Jim wells i a 15. South Premont Jim Wells Distillate i and gas 16. Quinto Creek.. Jim Wells Gas 4 17. Roth.. . :..... Jim Wells Gas I I 18. South Sinton.. San Distillate I Patricio and gas . • See Table 2 for data on discovery wells and Table I for information on these fields. • See Table 4.

Jan 1, 1943

By J. P. Givry

The bath and the liquid metal in the aluw~inuw~ electrolytic cells are moving under the action of the Laplace forces. Consequently there are differences in level at the interface of the liquid. This phenomena is studied by means of a computer; the characteristics of the mathematical model used are presented with the results corresponding to two typical cases. This study gives a new and origi~zal interpretation of magnetic ej-jects; their action depends very closely on the hydraulic phenomenon which explain the sensibility of the cells to the slope and thickness of solid bath frozen around the pot. MAGNETIC effects produced in the electrolytic cells used for the production of aluminum are known to exist, a factor whose importance is well-known by producers through its influence on cell operation and output. In particular, these effects bring about movements in both the bath and metal as well as interface variations in level that are detrimental to sound electrolysis . A direct study of these effects by means of an experimental device would raise a number of problems particularly difficult not to say impossible to solve in the present state of techniques. It is for this reason that we had recourse to an electronic computer for working out the speed and pressure distribution within the liquid in the cells. We have assumed that all other possible causes for movement, such as thermal convection and evolution of gas at the anode, are acting without any connection with magnetic effects, and that consequently we may study each of these causes separately. A basic cause for magnetic effects lies in the presence of Laplace forces within the bath and metal. Electric current and magnetic field distribution have been calculated with the help of an electronic computer, and two communications about it have already been made to AIME.* 1) PRESENTATION OF THE MATHEMATICAL PATTERN In order to solve this problem, it was essential to assume a number of simplifying hypotheses with regard to both the geometry of the actual cells and the phenomena themselves. A first simplification consisted in assuming that the movements of the conducting liquid modify neither the electric currents nor the magnetic fields. In consideration of the magnitude of the values involved this assumption seemed accep-tible. 1.1) Finding the Equation of the Problem. The problem raised consisted in determining the flow of two viscous immiscible liquids with different densities subjected in a complex environment to gravity and Laplace forces. As a matter of fact, the sum of the external forces acting on the liquids is: F = JAB +pg where F = volume energy, B = magnetic field, J = current density, p = specific gravity, g = gravity. In the case of a laminar flow and assuming that the liquids are Newtonian and incompressible liquids, the equations governing movements are the following: 1) Navier Stokes' equation written in vectorial form: In fact one tries to find a steady-state solution, so aVx/at = 0; besides, one assumes that the movements are slow enough for quadratic terms such as Vy(a Vx/ay) (of round about the square of speed) to be neglected in front of the viscosity term: pAV, so

Jan 1, 1968

By J. Gurland

The wmk is concerned with the estimate of the degee of continuity of a particulate phase dispersed in a matrix. The first section is a verieu: of the parameters nzeasurable by quantitative rnetallogvaphy, namely the contact area and, under certain conditions, the number of contacts between particles of one phase. In the second section, the frequency of particle contacts is related to the degee of continuity of a randomly embedded phase orz the basis of the lattice-percolation model of Hamrnersley and others. THE extent of continuity of the constituent phases may greatly influence the structure-sensitive properties of phase mixtures, particularly if the phase properties differ significantly. An example from the literature1 is shown in Fig. 1. The marked decrease of the electrical resistivity of sintered silver-alumina bodies near 25 pct by volume of silver presumably occurs because the more conductive phase changes from a discontinuous to a continuous structure. Other example of electrical- and thermal-conductivity transitions are cited by kingery In view of these observations, a knowledge and understanding of the connectivity of the microstructure may be of considerable practical importance. This study is concerned with one aspect of the genera1 problem, namely the estimate of the degree of continuity of a particulate phase dispersed in an opaque matrix. The first section reviews the parameters measurable on a polished cross section by auantitative metallography, such as the contact area and under certain conditions, the number of contacts between particles of one phase. In the second section, an attempt is made to relate the frequency of particle contacts to the degree of continuity of a randomly embedded phase. For the purpose of this discussion, the aggregate has two constituents: the particulate phase and the matrix. The latter is considered to be homogeneous. The term "particle" is used with the meaning of "grain", i.e., a minute unit of matter which is usually a single crystal of a readily distinguishable substance within the confines of a simply connected boundary. While many of the concepts which are used here to describe the structural variables characterizing the microstructure of phase mixtures are qualitative and ill-defined, they are presented with the intent of stimulating further work of a more general and rigorous nature. I) PARTICLE CONTACT, CONTIGUITY, AND MEAN FREE PATH 1) Measurement of Contiguity. The fraction of the total internal surface of a phase a shared with particles of that same phase in a two-phase mixture of and $ is indicated by the contiguity ratio:3 whereis the area of the interface between o particles, and Sap is the area of the interface between a particles and matrix P, per unit volume of mixture. The contiguity ratio ranges from 0 to 1 as the distribution of the a phase changes from a completely dispersed to a completely agglomerated structure. The interfacial areas may be obtained from simple intercept measurements on a random plane, after Smith and Guttman where and N are the numbers of intercepts between a random line of unit length on a plane of polish and the interparticle and interphase interfaces, respectively. The equations are valid for any distribution of particle sizes and shapes.

Jan 1, 1967

By John F. Elliott, John R. Rawling

The rate of reduction of silica to silicon by carbon at 1550° to 1700°C in iron blast-furnace type slag-metal systems has been investigated. In the tower portion of the temperature range oxygen transport in the metal boundary layer at the slag-tal interface is probably rate limiting. A second step, which apparently involves a chemical process in the slag at the slag-metal interface, appears to be rate limiting when the oxygen-transport limitation is avoided. Above 1650°C rate control of the reduction by carbon probably is mixed between the two steps. INVESTIGATIONS1.2 into the equilibrium distribution of silicon between graphite-saturated slags and metals typical of iron blast-furnace practice show that, under the experimental conditions specified, the reduction of silica to silicon is relatively slow compared with the rates of other slag-metal reactions under similar conditions. For this reason, the reduction of silica in blast-furnace slag-metal systems was considered to be an interesting subject for further study. Investigations of the kinetics of the reaction3-5 suggest that several possible steps may be rate controlling, and that the rate-controlling step depends not only on the physical state of the systems but also on the configuration of the apparatus. The main objects of the investigation reported here were to sug- gest plausible reaction paths for the reduction of silica under the experimental conditions chosen and to determine the step or steps which control the rate of reduction of silica. EXPERIMENTAL Two types of experiments involving the reduction of silica from the slag were carried out. In the first, the only reducing agent present was carbon (graphite), for which the over-all reaction is (SiO2) +2C(gr) —Si + 2Co(g) [l] The second type was a graphite-saturated ferro-silicon-iron concentration cell. In it silica in the slag could be reduced either by carbon according to Eq. [I], or by a reaction of electrochemical nature in which silicon was oxidized at the ferrosilicon-slag interface and silica was reduced at the slag-iron interface without the formation of CO. The two types of experiment are described below. Reduction of Silica with Carbon as the Only Available Reducing Agent. The reduction of silica was accomplished by allowing a liquid lime-alumina-silica slag and graphite-saturated iron to react in an induction-heated graphite crucible. The crucible was 2.25 in. diameter and 5 in. deep; it was fitted with a graphite stirrer which penetrated through the slag and into the metal, Fig. 1. The slag and metal charges weighed 350 g each. Pure carbon monoxide at a pressure of 1 atm was maintained above the melt by passing the purified gas through the crucible at a rate of 0.5 liter per min. The gas did not stir either the slag or metal. Temperature measurements were made by sighting an optical pyrometer down the hollow stirrer rod into a 1/4-in. hole drilled in the stirrer blade. The crucible temperature was maintained within *15"C of the required value by manual control of the power supply to the

Jan 1, 1965

By F. N. Ward, E. H. Bailey

Camp and sample-site methods useful for determining about 0.5 to 16 ppm of mercury in soils and rocks have been devised to complement the analytical methods already widely used in geochemical prospecting. In the camp-site procedure the sample solution is obtained by digesting the finely powdered sample with hot nine-molar sulfuric acid and bromine, the latter generated in place. The solution is buffered at a pH of 4 and the mercury is extracted into a relatively small volume of an organic solvent. Estimations are made by comparing the color of the mercuric dithizonate extracted from the sample with that extracted from a standard. In the sample-site method the mercury is volatilized as the iodide and the latter is dissolved in a buffer solution from which the mercury dithizonate is extracted as in the camp-site method. The estimation is made by a similar comparison with standards or by comparing the color of the mercuric dithizonate with artificial standards prepared from Orange II, an azo dye. Except for the establishment of standards, the time required by an experienced analyst seldom exceeds 10 min for a camp-site determination and 5 min for a sample-site determination. Camp-site determinations are useful for commodity studies and intensive exploration programs; sample-site determinations are applicable to extensive and reconnaissance-type geochemical prospecting programs. The results obtained on samples taken along traverses above known mercury ore deposits in the California Coast Range and western Nevada demonstrate the usefulness of both methods in geochemical prospecting. The increasing use of the mercury content of soils, rocks, plants, or water in geochemical prospecting emphasizes the need for analytical methods which are sensitive and at the same time require a minimum of readily available equipment. Sensitive methods based on the absorption of ultraviolet light by mercury vapor are common in the literature31 12. Although none of these methods have been used to analyze the large number of samples required in geochemical prospecting, they could be extremely useful except for the expensive instrumentation usually required to make the methods quantitative Also, such methods are perhaps too sensitive for field use, especially around areas of possible contamination. Other methods involve the distillation of mercury from a relatively large sample and subsequent collection of the vapors in nitric acid6. The mercury is then estimated by titration with a suitable reagent such as thiocyanate. These methods are not trace methods because the actual amount of mercury measured is often as great as 50 to 100 milligrams. Also, such methods are unsuitable for geochemical prospecting because of the amount of equipment necessary and the time required. Still other methods involve colorimetry, and the sensitive reaction between dithizone and mercury (11).. is the basis for a number of reports on the determination of mercury in biological materials 5,7. Moreover, by the judicious use of solvent extraction and suitable complexing agents, the dithiaone method can be made almost specific for mercury. However, none of the dithizone methods have yet been applied to the determination of mercury in soils and rocks. In most colorimetric methods he sample solution

Jan 1, 1961

By R. Maddin, A. Lawley

Single crystal Mo-Re alloys (99.99+ purity), grown by electron bombardment floating zone heating, were deformed in tension at temperatures from -196° to +200°C. At -196oC, Mo-6 pet Re and Mo-20 pct Re alloys deform by slip on systems of the type (101) [1ll]. Above-78oC, the operative slip system is of the type (112) [111], (101) [1ll], or (211) [1ll], depending upon orientation. Mo-39 pct Re alloys deform by twinning and slip at all test temperatures with a (112) [111] type twinning system. Critical resolved shear stress for slip and twinning is calculated as a function of composition and temperature, and the mechanical properties compared with those of less Pure polycrystalline alloys. HEXAGONAL close-packed rhenium, c/a = 1.615, is highly soluble in molybdenum. The bee molybdenum-rich solid solution extends to approximately 42 at. pet Re* at 2500°C,' Fig. 1. Recent work on polycrystalline alloys has shown conclusively that the addition of rhenium to molybdenum improves both the fabricability and the low-temperature ductility.2"5 Similar behavior is observed for W-Re and Cr-Re alloys.5 Initially, Geach and Hughes2 found that the Mo-30 pct Re alloy could be cold rolled to approximately 90 pct reduction before the onset of cracking. The remarkable effect of the rhenium was later confirmed by Jaffee et al. 3-5 with an optimum condition of maximum strength combined with maximum ductility at the Mo-35 pet composition. At higher rhenium contents, the ductility was severely impaired due apparently to the presence of brittle tetragonal s phase, Fig. 1. In the Mo-35 pet Re alloy, at least 110 ppm (parts per million) oxygen could be tolerated before cold workability was reduced. By comparison, the corresponding tolerance figure in unalloyed molybdenum is ~ 10 ppm. The effect of rhenium was considered in terms of: 1) a reduction in oxygen solubility in the lattice; 2) a redistribution of intergranular oxide from grain boundary films to isolated spheres; and 3) the promotion of twinning as a further mode of plastic deformation. Paradoxically, twinning is often associated with brittle fracture in iron and the silicon irons.6'7 Work to date has been restricted to are-melted and powder metallurgy polycrystalline material of ~ 99.9 pet purity. The present investigation was initiated for the purpose of determining the mode and crystallography of plastic deformation of a series of bee Mo-Re alloy single crystals over a wide temperature range from -196o to +200°C. Using high-purity zone-melted material (~ 99.99 + pet purity), the specific role of rhenium in the molybdenum lattice may be understood more fully since effects due to grain boundaries and oxide redistribution will be absent. At the same time, the study provides a comparison of single and polycrystalline deformation behavior. EXPERIMENTAL TECHNIQUES A) Preparation and Purity of Single Crystals. Alloys in the form of either are-cast and swaged or sintered and ground bar, 0.120 in. diam, were obtained from the Chase Brass and Copper Co. Alloy single crystals ~ 8-in. long were grown from the

Jan 1, 1962

By B. L. Landrum, P. B. Crawford

Theoretical and potentiometric model studies have been made of the effect of non-uniform lateral permeabilities on pattern sweep efficiency and production capacity in waterflood and gas-cycling programs. It is shown that a diflerence in directional permeability by a factor of three may result in a sweep efficiency of only 43 per cent for a five-spot pattern or a sweep of either 79 or 38 per cent for a direct line-drive square pattern, depending on the direction of the line-drive flood. Changes in the pattern conductivity varied from about 0.8 to 1.34 over this same permeability variation, depending on the pattern used. It is suggested that measurements be made to determine the possible magnitude and extent of the directional permeability phenomenon early in the field developinent and certainly prior to the initiation of any fluid-injection progmm. INTRODUCTION Irregularities in reservoir sand properties long have been a major difficulty to anyone attempting to explicitly describe the field characteristics of oil production. In particular, it is well known that vertical and lateral permeabilities often differ appreciably; however, the existence of large regions with lateral permeabflity variation is not widely recognized. A number of years ago, extensive studies were conducted by the Secondary Recovery Research Labcratory of the Pennsylvania Grade Crude Oil Association, primarily on the Bradford field. Johnson and Hughes' reported a permeability trend in the northeast-southwest direction. They indicated that flow in the preferred direction may be 25 to 30 per cent greater in that direction than in the northwest-southeast direction. They also reported that similar effects may be found in other nearby fields. The origin of the permeability variation has been discussed by Griffith Hutchinson' described the results of labora- tory tests on limestone cores, pointing out that per-ferential directional permeabilities were significant in one-half of 10 formations studied and that the average permeability ratio was 16:1. Barfield, Jordan and Moore analyzed the fluid-injection displacement performance in the Spraberry and reported that the effective ratio of permeability parallel to the major axis to the permeability perpendicular to this axis was 144:l and that it inclined along an angle of about 30". To prevent the reduction of sweep efficiency which would normally result from flooding or cycling in such reservoirs, well spacing could be varied from the customary square to a diamond-shaped pattern. Johnson and Hughes' presented a method for determining the desired shape. Another method will be discussed in detail in the next section. It is the purpose of this paper to investigate quantitatively the effect of directional permeability upon the sweep efficiency and production capacity of the five-spot and line-drive well patterns. Information currently in the literature will be applied to this particular problem and augmented by a potentiometric model study. It is stressed that the effects herein discussed may or may not be of great importance because field data on this phenomenon are far too scant to form such an opinion. It is suggested that, if conditions similar to those found by Johnson and Hughes frequently exist (as may well be the case), more consideration cdrtainly should be given to this problem.

By J. Serra, M. Turpin, R. Alberny

A new method is proposed to obtain automatically an unbiased estimate of the interdendritic spacing A. It is shown that the structure can be built by a random distribution of a rectangular basic unit. The usual definition of the interdendritic spacing yields a value 1 which, coupled with A, gives the shape of the basic rectangular unit. A study of the relationship between dendrite arm spacing and solidification rate was conducted as a part of a research program on dendritic solidification. For any comparison between theory and experiments to be meaningful, it is necessary to measure reproducible and clearly defined spacings. Fig. 1 shows clearly that even in a fairly simple structure such measurements are difficult. if we compare photos (a) and (b), we can hardly assess which one shows the larger spacing. Moreover, the quantity to be measured can be defined in several ways. On a small scale, dendrites seem to be distributed in a very regular and ordered way. However, on a larger scale, this regularity no longer exists. The usual way to measure spacings is to pick up some rows of dendrite stalks; such measurements are obviously biased since less orderly regions are not taken into account. A more objective method is to section the picture with randomly oriented straight lines and average the measured interdendritic spacings. The purpose of this paper is to show that such measurements, which can be conducted automatically, yield objective and reproducible results which are directly related to characteristic features of the dendritic structure. I) THEORETICAL ANALYSIS 1-1) Mathematical Morphology and Function of Co-variance. Matheronl and Serra2 enlarced- the definition and geometrical meaning of the notion of covariance to encompass problems in mathematical morphology. A brief review of part of their theory can be stated as follows. Let A' be an isolated particle, and let us consider a group of two scanning points h is the vector joinlng these points, h its modulus, and a its direction. Let us also define a boolean function, k(x), whose value is 1 if x lies inside the particle and 0 if it 1s outside. The total number of events in which both points are inside A' IS the covariance Ii',(h): is the measure of the intersection of A' with the particle ALh obtained by translating A' of -h Obviously K,(O) is the volume of the particle A', or its area if A' is a two-dimensional body. The average value of K,(h), when the direction of a vector h of constant modulus is rotated, is: An important property of the covariance is illustrated on Fig. 2: if the shape of a particle shows some regularity along a direction a, K,(h) generally presents a maximum. We now consider a group A, made of many particles A' distributed in space; then k(x) is taken as the realization of a stationary random f~nction.~ The volume fraction (or fraction of area if the problem is two-dimensional) occupied by A equals the average value q of k(x): meaning "average value of"). We also replace

Jan 1, 1970

By C. D. Rubert, W. J. Parton

A flotation plant was placed in operation in 1945 at the Tamaqua colliery of the Lehigh Navigation Coal Co. Inc., to recover fine anthracite which is discharged from the cleaning plant with the washery water.‡ In addition to the recovery plant, facilities were provided for the complete clarification of the washery water, recirculation of this clarified water for breaker use, and disposal of the refuse solids in a waste impounding dam. Fig I shows a view of the settling tanks and the flotation plant. Flow Diagram The flow diagram for the complete recovery project is given in Fig 2. All the waste water from the cleaning plant is collected in a sump A outside the breaker structure, from which a 7000 gpm pump B delivers it through a 16 in. line to a 75-ft diam hydroseparator C. The hydroseparator, acting as a classifier, is set to give a separation at approximately 200-mesh. The minus 200-mesh overflow is discharged by gravity into the 180-ft thickener D for final settling of the solids. The classifier underflow sludge is pumped to the flotation plant by a 6-in. quadruplex diaphragm pump E. A 10-ft diam hydroseparator F is used to make a second classification on the sludge solids at approximately 28-mesh. The underflow from this classifier containing the coarse particles is elevated by a 6-in. diaphragm pump G and is discharged on two 4- by 6-ft vibrating screens II. These screens are dressed with approximately 28-mesh cloth. Screen oversize product flows directly to the centrifuge that dewaters the cleaned froth. The screen underflow and the overflow from the 10-ft classifier flow to the flotation circuit. The flotation feed is conditioned in a 12 by 12-ft agitator tank J at a pulp density of I:2.33 (30 pct solids). Reagents are fed to the circuit by reagent feeder I. The conditioned pulp is then diluted to a pulp density of approximately I: 5 (18 pct solids) and is fed to two banks of four 100-cu ft froth flotation cells K for primary coal recovery and cleaning. Additional reagents from reagent distributor L are added to the feed weir-box of Nos. 2, 3, and 4 cells of each bank of flotation machines. Clean coal removed from these cells flows directly to the clean-coal sump. Dilute tailings from the primary cells is re-thickened in a 30-ft diam thickener M and is then retreated in a scavenger circuit for final recovery of coal. The scavenger circuit consists of a 6- by 6-ft agitator tank N and two banks of four 24-cu ft froth flotation cells 0. Coal froth from these cells flows to the dewatering equipment and the tailings flows to a vertical refuse pump which delivers it to the 180-ft diam waste thickener D. Dewatering of the coal products is accomplished in a 54- by 72-in Bird centrifugal filter P. The cake product is dropped onto a conveyor and is loaded

Jan 1, 1949

By Aloys H. Wohlrab

THE conditions that govern the selection of a suitable type of detachable bit for the small, isolated mine, for rock work and tunnel contracting and for the large mine are quite dissimilar, therefore intelligent recommendation of a particular make of detachable bit must involve consideration of many factors. Small, isolated mines may find advantageous a detachable bit that a larger mine cannot afford to use, because of more efficient conventional steel sharpening and steel-distribution practice, but a small mine may not be able to adopt the practice of large mines because of necessary capital expenditures for equipment for detachable-bit sharpening and shanking. The perfect detachable bit, suitable for all conditions, has not yet been developed. CONVENTIONAL DRILL BIT IN USE That drilling speed increases as the bit gauge decreases is well known, but since small-hole drilling is the exception rather than the rule the rate of such increase is probably not so generally recognized. Tests carried out by Holman Brothers Limited1 with 7/8 -in. steel show that when bit sizes are reduced from I ½ in., I 3/8 in., and I 3/16 in., to I 3/8 in., I ¼ in., and I 1/8 in., respectively, the volume of the hole is 15 per cent less and the drilling speed 49 per cent higher. Recent tests by the United States Bureau of Mines2,3 in hard, uniform basalt showed that a reduction in average gauge from 2.077 to I.826 in., a difference of 0. 2,5I in., gave an increased drilling speed of 65 per cent. The limits to which a drill hole may be extended depend upon the loss in gauge. Since the conventional bit with 5° and I4° clearances did not possess sufficient reaming edge to permit the smaller gauge changes that were required for small-hole drilling, experiments were made in bit construction with a view to correcting this deficiency. This resulted in the adoption of the full reaming cross bit (having full Carr characteristics) by some mines.4 In order to drill holes having a minimum taper from the collar to the bottom of the hole, full reaming center-hole cross bits with 90° cutting angles, 5° and 14° wing tapers, forged on 7/8-in. quarter-octagon drill rods, are used in the conventional drill-steel practice at Hollinger. In the steel shop close attention is given to the condition of the dies and dollies, which, combined with a rigid inspection of the finished bit, ensures as nearly a perfect bit as can be forged economically. Shop practices and costs have been discussed in earlier papers.5.6 The method by which the radii for the special dies used for forging bits of different gauge diameter are obtained so that the points and reaming edges cut circles of the same diameter has been discussed by Hibbert.7 REQUIREMENTS FOR DETACHABLE BIT FOR HOLLINGER Under these circumstances, it was apparent that it would be difficult to introduce a detachable bit that could successfully compete with the conventional bit already in

Jan 1, 1942

By F. E. Rizzo, L. R. Bidwell, D. F. Frank

THE poor high-temperature oxidation resistance of the refractory metals becomes an important problem as higher operating temperatures are sought. A meaningful analysis of their oxidation behavior requires a knowledge of the phases that can appear during oxidation as well as their relative stability. Although several extensive investigations have been carried out to obtain this information for the W-0 system,1-10 serious inconsistencies still remain. First, the standard free energies of formation (AG°) determined in recent studies which used the solid electrolyte galvanic cell technique6,7,9 differ significantly from those obtained primarily from gas equilibration measurements.1,3,4,10 The disagreement is especially large for the highest oxides. These data have been used to predict the decomposition temperatures of WO2. 72 and WO2.90.1 A considerable extrapolation is required, resulting in a large uncertainty in the decomposition temperatures. Second, Bousquet and perachon3 have presented convincing evidence, ob- tained by gas equilibration measurements, in support of the long-contested existence of W30. Phillips and chang,ll on the other hand, were not able to observe this phase under similar experimental conditions. The purposes of this work, which is part of a continuing investigation of the W-Mo system, were to resolve the discrepancies between the AGO measured by gas equilibration and solid electrolyte galvanic cell techniques, to extend the latter measurements to lower temperatures, to redetermine the WO2.72 and WO2.90 decomposition temperatures, and to apply the more sensitive electromotive-force method to the question of the existence of W3O. I) EXPERIMENTAL PROCEDURE The measurement of ?G° of reaction by the use of calcia-stabilized zirconia solid electrolyte galvanic cells has been described previously.12 The method is based on the measurement of the difference in chemical potential of oxygen between an electrode containing the two oxides of interest and a reference electrode of known oxygen activity. Two different types of cell holders were used in this study. The first type of apparatus has been described earlier." It consisted of two solid electrodes separated by a disc of electrolyte. Both electrodes were exposed to the same stream of purified helium. With this design a gaseous transport of oxygen between the two electrodes is possible. The second type of apparatus, which has also been described earlier,14 effectively separated the two electrode atmospheres. It utilized a closed-end impervious, calcia-stabilized zirconia tube that was open to the atmosphere. The tube served as an electrolyte for the cell and provided a means for separating the anode compartment, which was held under a static vacuum, from an air reference cathode. The cells and reactions of interest are described in Table I. High-purity tungsten metal was obtained from the Fansteel Metallurgical Corp. and the Allied Chemical Corp. Table II contains an analysis of each material. WO3 was prepared by oxidizing the metal in air at approximately 600°C in high-purity recrystallized alumina boats and by the dehydration of reagent-grade tungstic acid in alundum boats. The two methods of preparing WO3 resulted in slightly different purities.

Jan 1, 1968

By P. F. Gnirk, J. B. Cheatham

An experimental investigation has been made to study the effects of tooth angle and confining pressure on the force required for indentation of dry rock samples under confining pressure. In these experiments static single-tooth indentations were made on two standstones, a limestone, a schist and a slate under confining pressures of 5,000 to 15,000 psi. Sharp wedge-shaped teeth with included angles ranging from 30°to 105°were used. In all cases the force-displarenzent curves are approxinlately linear for rocks tested under confining pressure, as contrmted with the discontinuous curves obtained for silnilar rocks at atmospheric conditions. Photonzicrographs of thin sections through the craters indicate very little evidence of chip formation during indentation. In general the experimental data lie between calculated values for perfectly rough and perfectly smooth tooth-rock interfaces. INTRODUCTION The variables associated with ctrilling at depth are numerous and, in many instances, are not easity isolated and controlled. Also, many of these variables are interdependent; however, if the variables which are sufficiently independent of each other are held constant and are appropriately introduced, the dependent variables can be more easily studied and evaluated. It is the purpose of the present investigation to study experimentally the simplest case of bit tooth-rock interaction. In essence, the experiments have involved the static loading of sharp wedge-shaped tools on the surfaces of effectively semi-infinite dry rock samples subjected to confining pressures. During this investigation the following quantities have been maintained constant: 1. Pore pressure: atmospheric (i.e., the rock is dry). 2. permeability: although the rocks may be permeable, they are "jacketed" in such a manner that the fluid is not permitted to flow through them. 3. Temperature: 75F. 4. Rate of loading: essentially static (approximately 0.002 in./second). 5. Bit tooth: a sharp wedge-shaped tooth loaded normal to the rock surface. 6. Rock surface: smooth and flat. 7. Drilling fluid: hydraulic oil. In addition to the above conditions, the rock surface was free of a layer of cuttings. There was no indexing to previously indented surfaces, and the influence of corners of the borehole was neglected because the rock samples were effectively semi-infinite. The following quantities have been varied, and the resulting effects have been studied: 1. Rock a) Type (e.g., limestone, sandstone, etc.). b) Mechanical properties ) Necessarily dependent c) Porosity on type of rock. 2. Bit tooth (included angle of wedge-shaped tooth). 3. Depth of penetration. 4. cobfining pressure. On the basis of laboratory experiments which have shown that many rocks exhibit ductile behavior at confining pressures corresponding to depths usually reached during drilling,'.' a theory has previously been advanced which predicts the force required for penetration by a single sharp wedge tooth into a ductile* material.' The material is assumed to be isotropic, homogeneous and rigidly plastic (no elastic deformation) and to obey the Coubomb yield criterion (Figs. 1 and 2). Equations governing the force required for penelration are given for two extreme cases:** 1. A smooth, perfectly lubricated tooth-rock interface (fridionless boundary), in which the solution gives a minimum value for the penetrating force: in which F = force of the tooth, b = length of tooth edge,

By K. A. Johnson, F. H. Ellinger, C. C. Land

The Pu-In phase diagram has been determined by thevmal, filtvation, micrographic, and X-ray diffraction methods. This alloy system is characterized by 1) limited solubility of indium (-2 at. pet) in 6 and e plutonium, 2) one eutectic, and 3) fizte intermediate phases. Of the latter, PuIn and PuIn3 melt con-gruently, and Pu31n, Pu31n5, and the high-temperatuve 7 solid solution are formed peritectically. The n phase decomposes eutectoidally into Pu3In and PuIn at 865°C. Although the 6 phase can readily be retained to room temperature, it is not thermo-dynamically stable below 300°C. The Pu-In system has been investigated at Los Alamos as part of a study of the alloys of plutonium with the group 111-B elements. Constitutional studies of the Pu-A1 and Pu-Ga systems have been reported earlier.'9' To date, published information on the constitution of Pu-In alloys covers only the identification of the intermediate phases Pu3In and PuIn3.3,4 EXPERIMENTAL The alloys were prepared from five different lots of plutonium and three different lots of indium. The principal impurities in the plutonium differed from lot to lot within the following limits (in ppm): iron, 30 to 80; nickel, 30 to 60; aluminum, 15 to 30; silicon, 20 to 145: thorium, 50 to 300; carbon, 75 to 335; and oxygen, 20 to 135. Spectroanalysis of the indium showed that two of the lots were 99.9 wt pct pure, and the third was 99.98 wt pct pure. The alloys, in the form of about 5-g buttons, were prepared by arc melting in conventional equipment. The components for each alloy were weighed to the nearest 0.1 mg. In most instances the weight losses during melting were negligible; therefore confirmatory chemical analyses were usually not made. A few results are given in Table I. Density measurements of the arc-cast buttons were made by the liquid displacement of bromoben-zene. Heat treating was done in muffle furnaces controlled to +2°C. The alloy buttons were wrapped in tantalum foil before being enclosed in evacuated clear silica capsules. As a precaution against breakage, each capsule was in turn placed in a silica tube closed with a refractory wool plug prior to being charged into the furnace. For a moderately fast quench of the alloys, the outer protection tubes containing the capsules were plunged into cold water. Differential thermal analyses (DTA) in racuo were performed at heating and cooling rates of about 1.5°C per min. Tantalum crucibles having inverted thermocouple wells were used for most of the analyses. It was found micrographically, however, that the liquid alloys containing more than about 35 at. pct In reacted with the tantalum, resulting in contamination of the surface of the alloy. A search for a more satisfactory crucible material was not successful: tungsten and yttria behaved comparably to tantalum; thoria, vitrified magnesia, and vitrified alumina severely contaminated the alloys. So as to minimize the contamination by the crucible mater-

Jan 1, 1965

By K. A. Semlak, F. N. Rhines

NFILTRATION is a term used to designate that i- process by which the pores of a metal powder are filled with a relatively low-melting liquid metal through the action of capillary forces. This is accomplished in practice either by heating the porous body in contact with the solid infiltrant metal above the melting point of the latter, or by preheating the porous body separately and then dipping it into the liquid metal. The liquid, as it sweeps through the porous body, replaces the gases progressively, thus yielding a relatively dense product in a short time.' Liquid-phase sintering, which is related to infiltration, is a process by which a mixture of two or more metal powders is sintered at a temperature between the liquidus and solidus of the ultimate alloy.' According to Cannon" liquid-phase sintering can be divided into three stages which he calls liquid flow, accommodation, and solid sintering. The largest density increase occurs during the first stage, where the lower melting component melts and, driven by capillary forces, flows among the particles of the higher melting component, where, after dissolution of the bonds between the solid particles, it moves them into close packing. This happens so quickly that little has yet been learned of its mechanism. A study of the rate of capillary rise of a liquid metal in a higher melting metal-powder compact may be expected, therefore, to contribute not only to a firmer understanding of the process of infiltration as such but also to a more extensive knowledge of what occurs during the initial stage of liquid-phase sintering. Theoretical Basis In order to derive a mathematical expression of the rate of infiltration, it has been assumed that a powder compact consists of a great many parallel capillary tubes and that the rate of rise of a liquid in an average capillary channel represents the rise in the entire compact. For a straight capillary, assuming that Poiseuille's law obtains for the non-stationary state and that wetting is very rapid, Ligenza and Bernstein' have derived the following differential eauation of motion where h is the height of rise of the column of liquid at time t, R, is the radius and 1 the length of the capillary, t) and 7, the viscosities of liquid and air, respectively, p and p, the density of the liquid and air, respectively, y the liquid-gas surface tension, 0 the liquid-solid contact angle, and g the acceleration due to gravity. The term on the left of Equation [I] represents the rate of change of momentum of the contents of the capillary tube. On the right the terms represent, respectively, the forces due to a) surface tension, b) viscous resistance, c) gravity, and d) end-drag effect. Equation [I] is not amenable to explicit solution, but for a tube of sufficiently small radius, the rate of rise may be slow enough so that the rate of change of momentum and end-drag terms may be neglected. The validity of this simplification was established by Ligenza and Bernstein' by graphical differentiation of observed data obtained from organic liquids rising in glass tubes. The solution of this simplified case is:

Jan 1, 1959

By Mark D. Tabak

Measurments of the transient photoconductivity in fillns of amorphous selenium with blocking- contacts haue been used in studying the transport properties. The results shozu that the transport of free carviers cannot be explained in terms of a model using bulk trapping. Measurments of the photocurrent-applied field characteristic as a unction of sample thickness do not pvoduce the scaling lau,s approps-iate lo a range-limited model. THE investigation described here was undertaken to explore the mechanisms of transport in amorphous selenium films. These films are used in xerography, where a photoconductor is charged electrostatically and then exposed to light to form a latent image. The sensitivity that one can expect when operating in this mode is directly related to the transport properties of the photoconductor material. The study of photoconductivity at high fields in insulating materials is often complicated by contact effects. Injection from the contacts can easily mask the fundamental transport processes that are being studied. A technique is described in this paper that allows a study of photoconductivity and transport processes in amorphous selenium films without the complicating effects introduced by contacts. Accordingly, the samples are prepared using insulating films between the sample and the metal electrodes, where the electrodes are capacitively coupled to the surfaces of the sample under study. A transient measurement is performed with pulsed light, and the photocurrent measured near the beginning of the pulse before the field is distorted by polarization at the blocking elec- trodes. A similar method has been described by Manyl using pulsed electric fields in studying the high field transport in insulating cadmium sulfide. EXPERIMENTAL It is possible to eliminate undesirable contact effects and maintain uniform high fields across the sample by using blocking electrodes and measuring the current-field characteristic under transient conditions. The sample configuration is shown schematically in Fig. 1. Each of the gold electrodes is separated from the amorphous selenium film by a layer of insulating plastic (Formvar) approximately 2000~ thick. The electrode on the front surface is semi-transparent to allow illumination of the sample. The whole configuration is mounted on a KEL-F substrate, which is a transparent insulating plastic having a thermal expansion coefficient that allows low-temperature measurements without cracking the selenium film. Fig. 2 shows a block diagram of the measurement apparatus. Light was obtained from a 450-w Xenon arc lamp, the intensity of which was controlled by stainless-steel screen filters and monitored by a pho-tomultiplier which was calibrated periodically against a thermopile. A camera shutter operated at 1/200 sec provided the light pulse and a synchronized signal to the oscilloscope. The photocurrent transient is ob-served with a high-speed picoammeter (response time of 1 msec) the output of which is displayed on an oscilloscope. The applied voltage is constant throughout the transient measurement. The selenium films were prepared by evaporation of four 9's pure selenium shot supplied by Canadian Copper Refiners. Spectrographic analysis showed about 1 ppm of Te and Fe, 5 ppm of C1, and 0.05 ppm

Jan 1, 1968

By B. L. Averbach, Morris Cohen, L. L. Seigle

Free energies, enthalpies, and entropies of mixing of Ni-Au solid solutions containing 5 to 95 atomic pct Ni have been determined by the electromotive force method at 700° to 900°C. The thermodynamic activities exhibit large positive deviations from Raoult's law, and the entropies of mixing are almost twice those of ideal solutions. The enthalpies of mixing are positive (heat is absorbed) and are attributable to the lattice distortional energy resulting from the size difference between the nickel and gold atoms. This factor appears to be responsible for the miscibility gap at lower temperatures. IN the thermodynamic study of metallic solid solutions, most interest has been directed toward systems with negative deviation from Raoult's law, namely, those exhibiting superlattice or compound formation. The results of previous investigations are summarized in recent publications.'-' Relatively little experimental work has been carried out on solid solutions which manifest a positive deviation, possibly because the range of solubility in such cases is usually quite limited. Nevertheless, the relationship of the thermodynamic properties of these solutions to diffusion, nucleation, and precipitation in the solid state are of considerable importance. The binary Ni-Au alloys are particularly suited to an investigation of these relationships. Despite the presence of a miscibility gap at lower temperatures, Fig. 1, indicating a large positive deviation from Raoult's law, complete solid solubility is found above 840°C. Moreover, the difference in the atomic scattering powers of nickel and gold is sufficiently great to permit X-ray diffraction studies of atomic arrangements and pre-precipitation phenomena. Radioisotopes of both nickel and gold are available for diffusion work, and finally, a large difference in nobility between the two elements facilitates measurement of the thermodynamic properties. The present paper describes the experimental determination of the free energies, enthalpies, and entropies of mixing of solid Ni-Au alloys. Table I gives a list of the symbols used in the paper. Experimental Method The stability of nickel chloride relative to gold chloride" indicated that the galvanic cell method could be used for determining the thermodynamic properties of Ni-Au alloys. An electrolytic cell (Fig. 2) was constructed, similar to that of Weibke and Matthes,7 in which the electrodes were solid nickel and Ni-Au alloys, and the electrolyte was a fused mixture of alkali chlorides containing NiCl,. The cell electrodes were made from fine gold granules and carbonyl nickel shot melted together under argon, chill cast, swaged to 1/16 in. diam rod, and annealed for one week at 850°C. Commercial reagent and chemically pure grade salts, purified by dehydration, were used for the electrolyte. The cell, operating in an atmosphere of purified argon, was heated in a resistance-wound cylindrical furnace whose temperature was controlled to within ±0.5ºC. The potential developed between the pure nickel and the alloy electrodes, which is related to the thermodynamic properties of the alloys by standard equations to be presented later, was measured with a potentiometer and a mirror galvanometer sensitive to 10-7 v. Dehydration of the electrolyte was carried out in the assembled cell by evacuating at 100°C for about

Jan 1, 1953

By George C. Fryburg

The oxidation of platinum at high temperatures (above 800°C) is controlled by boundary-layer diffusion, except at the lowest pressures. The rate of oxidation is determined by the rate of diffusion of oxide through the boundary layer away from the platinum. This is in contrast to the situation in tungsten and molybdenum oxidation, where the rate is controlled largely by the diffusion of oxygen through the boundary layer towards the metal. The difference in mechanism is a consequence of the much lower rate of oxidation of platinum. Evidence is presented that supports this mechanism for the oxidation of platinum. SOME years ago we reported1 a study of the oxidation of platinum in ordinary oxygen in the temperature region above 800°C, where the oxide is volatile. All the data available up to that time had been obtained with platinum crucibles or plates heated in tube furnaces. The results were widely variant and highly dependent on the flow rate of gas through the furnace: the faster the gas flow rate, the higher the measured oxidation rate. These results indicated to us2 that reaction equilibrium was being approached in the furnace and that the rate was diffusion limited. To minimize these effects, we employed1 electrically heated ribbons placed in a cooled bulb. We were primarily interested in the low-pressure region, but some experiments were performed at pressures up to 1 atm. We found a peculiar pressure dependency which was explained on the basis that the rate of oxidation was proportional to the pressure at all pressures, but that with increasing pressure an increasing fraction of the volatilizing oxide was back-reflected to the ribbon by the surrounding gas molecules. The oxide molecules are not stable at the temperature of the platinum and are decomposed on impact, the platinum being re-deposited on the specimen. Because of the limitations of space, this explanation was offered summarily without detailed support. Recently, Jaffee and associates3, 4 have suggested that the pressure dependency of our data up to 0.5 torr could be explained on the basis of a Langmuir-type adsorption of molecular oxygen followed by dissociation. Since the correct explanation of the effect of pressure on the oxidation rate is a necessary requirement to the development of the basic mechanism of the oxidation reaction, we felt that the back-reflection theory should be presented in more detail. This is the object of the present paper. RESULTS AND DISCUSSION A typical set of results showing the pressure dependency of the oxidation reaction is presented in Fig. 1, where we have plotted, on logarithmic scales, the rate of oxidation, R, vs the pressure, p. For comparison some results of Krier and Jaffee4 and of Raub and plate5 are also shown. These data were taken at atmospheric pressure using furnaces. The effect of reaction equilibrium within the furnace is apparent from the much smaller values that these observers obtained: Raub and Plate In O2 found a rate of 3.1 µg cm-2 hr-1 compared to our value of

Jan 1, 1965

By N. Albon, J. F. Miller, R. W. Coutant

The deposition of nickel from nickel carbonyl onto amorphous substrates has been studied, with attention being paid to the specific effects of the physical and chemical nature of the substrate and to the effect of oxygen on the crystal morphology. With substrates having microscratches or etch lines, nu-cleation was observed to occur preferentially at these surface features. Flame polishing of the substrate surfaces was found to remove any regularity in preferred nucleation sites. Nucleation was observed to occur less readily on substrates having relatively low surface energies, e.g., Teflon and carbon, than on materials having relatively high surface energies such as fused silica. At low oxygen concentrations [Ni(CO)4/O2 > 54 x 1031, apparently pure and well-formed nickel crystals were observed to nucleate and grow irrespective of the presence of oxygen. At higher concentrations of oxygen, a secondary growth process, dependent upon oxygen concentration and resulting in a gradual change in crystal morphology, was observed. It is concluded that the influence of oxygen on the nucleation and growth of nickel is determined by the relative kinetics of the various possible reactions, and that under the experimental conditions employed the 0-Ni interaction occurs at some nucleation or prenuclea-tion stage. THE purpose of the research on crystal nucleation in chemical vapor deposition as described in this paper has been twofold: 1) to examine some effects arising from the use of amorphous substrates, and 2) to study the specific effects of oxygen on the nucleation and growth of nickel in a nickel carbonyl-carbon monoxide system. The nickel-nickel carbonyl system was chosen for study for several reasons: 1) nickel films are of potential interest in electronic technology, and 2) the deposition can be carried out at moderate temperatures, thus making possible detailed study of the processes occurring and the use of a variety of substrate materials (including some which melt at relatively low temperatures). Fairly well-characterized chemical kinetics and a broad background of information are available on the py-rolysis reactions and on the mechanisms of Ni-O interactions. NUCLEATION AND GROWTH THEORY The theoretical background for the analysis of nucleation and growth by vapor deposition for a one-component system (physical vapor deposition) and the problems encountered therein have been reviewed by Hirth and pound.' More recently Mande12 has indicated the difficulties of applying such theory to chemical systems. One of the major problems involved is the possible multiplicity of chemical reactions and deposition routes. For example, those reactions which are probably of significance in a discussion of the pyrolytic deposition of nickel from nickel carbonyl under the conditions of the present experimental work are illustrated in Fig. 1. As is true with most cases of chemical deposition, many of the quantitative data necessary for a complete analysis of the system are either not available or not directly measurable. However, with the present system, sufficient data are available for a discussion of nucleation and growth on a qualitative basis. Classically, the rate of nucleation of a monatomic species being deposited from a vapor phase is given by

Jan 1, 1965

By C. R. Johnson, R. A. Greenkorn, E. G. Woods

A new method of reservoir evaluation called pulse-testins has been developed for describing formation properties between wells. Pulse-testing utilizes a sensitive differential-pressure gauge at a responding well to measure and record the response generated by a series of flow rate changes (pulses) at an adjacent or pulsing well. Since the pulse-test instruments have a sensitivity of about 0.001 psi, pulses of several hours or less in duration will generate a measurable response in most reservoirs. For this reason, many well pairs can be tested in a short period of time with little interference in field operations. Comparison of pulse-test results to conventional testing methods shows that the pulses obey unsteady-state, compressible-flow theory and thus provide a measure of both transmissibility (kh/µ) and storage (Fch). In additian, the method can be used qualitatively to describe communication across faults and between zones, and direction and tnagnitude of fracture trends. INTRODUCTION To obtain maximum usefulness of new reservoir analysis methods as well as to aid the field engineer in understanding local reservoir anomalies, improved methods are needed to describe heterogeneities in specific reservoirs. Optimum well spacing, equipment specifications, well completion design and especially the economics of pressure maintenance and secondary recovery programs depend on the extent and location of the heterogeneities that affect flow behavior in the field. One method for obtaining a measure of areal reservoir heterogeneity is an interference test. In the simplest interference test. constant-rate production or injection is initiated at one well and the effect of this flow is measured as pressure vs time at another well. Thus, during interference tests the flow characteristics of the formation are determined in situ. Despite their obvious usefulness in reservoir delineation. interference tests have not enjoyed frequent usage. Reasons for this have been the weeks or months required in many fields to obtain a pressure response measurable with conventional gauges, and the interruption of routine field operation during the field-wide shut-in normally required during these long times. Also, only average properties of the relatively large volume of the reservoir disturbed during these long times can normally be obtained — variations in properties between individual wells cannot be delineated. To eliminate these drawbacks of conventional tests, a special reservoir description technique called pulse testing' has been developed. Pulse-testing has several advantages that make it more convenient and practical for field use than interference tests. Valid tests are more certain because use of a series of flow disturbances gives rise to a diagnostic pressure response that can more readily be distinguished from unknown trends in reservoir pressure and other "noise." The time required is only a fraction of that for an interference test because a special, high-sensitivity differential pressure gauge can detect a much smaller pressure change. Variations in properties between individual wells can be delineated because of the relatively small volume of the reservoir disturbed during these short times. Finally, wells other than the pulsing and responding wells do not have to be shut in or carefully regulated.

Jan 1, 1967

By H. O. Jahns, R. A. Greenkorn, R. E. Haring, L. K. Shallenbarger

This paper is a study of the effects of heterogeneity on flow in an analog of porous media, the Hele-Shaw model. l-3 A set of experiments in heterogeneous Hele-Shaw models showed streamlines through and around heterogeneities of various sizes, shapes and levels. (A level, we define as the ratio between the transmissibility of the heterogeneity and that of the rest of the model.) The heterogeneities were restrictions or expansions of the flow stream analogous to variations in the transmissibility of porous media. The experimental data agreed well with numerical results and with an analytical solution, which we derived for a circular heterogeneity in an infinite field. This study considers the flow-stream distortion due to the shape, size and level of heterogeneities. Size and level are much more important than shape provided the heterogeneity is not long and narrow. Our analytical solution shows that a circular heterogeneity in a large field can be replaced by an equivalent circle of either zero or infinite permeability. The radius of the. equivalent circle is a simple function of size and level of the actual circle. INTRODUCTION With the availability of high-speed computers and numerical procedures to predict reservoir behavior, we are faced with an important question. How much information about the reservoir do we need to justify the cost of the computer in any given case? To answer this question, we have to know how various reservoir parameters affect flow behavior. Reservoir heterogeneity is one of these parameters. In this study, we used a simple, two-dimensional model of porous media, the hele-shaw model, to investigate the effect of heterogeneity on flow behavior. We restricted ourselves to linear, single-phase, steady-state flow in a rectangular field with a single heterogeneity at its center. The analogy between flow in Hele-Shaw models and in porous media is easily verified. Let us first consider a homogeneous Hele-Shaw model with constant plate separation h. (The Hele-Shaw model is constructed by placing two plates, usually glass, very close together and allowing liquid to flow between them. Streamlines are made visible by introducing colored fluid into the space between the plates at a number of points across the model.) We assume a cartesian coordinate system with its origin in the middle between the plates and the z axis directed perpendicular to the glass plates (Fig. 1). The fluid flow is always in a direction parallel to the glass plates and varies from a maximum value to zero in the very small distance from the middle (z = 0) to either plate (z = h/2). For slow motion of an incompressible fluid, neglecting inertia and body forces, we have the viscous flow equation: where p is the fluid pressure, p the viscosity, and v the velocity vector with components u, v and w in the x, y and z directions, respectively. In our rase. and the derivatives of 3 with respect to x and y are small as compared with the derivative in the z direction. Therefore, approximately, with Vp and v being two-dimensional vectors in the x-y plane. Two integrations with respect to z give

Jan 1, 1965