Search Documents

By E. R. Morgan

A series of manganese-rich ferromagnetic alloys has been studied. The alloys are based upon an interstitial solution of carbon in manganese. In each of the systems investigated, the ferromagnetic phase was found to be face-centered-cubic in structure. This magnetic phase is based upon the composition (Mn, X)4C; where X is a metallic element which has both a positive size factor with respect to manganese and a high positive valence. Typical elements of this type are aluminum, indium, and tin. Preliminary magnetic measurements indicate that the effective magnetic moment of manganese in the alloys is at least 1.0 Bohr magneton per atom. It is emphasized that the critical atomic separation beyond which ferromagnetism can occur will be governed by the electronic configuration of the manganese atoms. Lattice parameter measurements show that the ferromagnetic condition in the present alloys is associated with an increased atomic separation of only 3 to 6 pct compared with a hypothetical face-centered-cubic lattice of pure manganese. MANGANESE which is paramagnetic and not ferromagnetic in the pure state can become ferromagnetic if suitably alloyed. Under favorable conditions manganese can have an effective ferromagnetic moment of the order of 3.41,2 or even 4.0 compared with a moment of 2.2 Bohr magnetons for iron. The incidence of ferromagnetism is believed to be controlled by the degree of atomic separation.4,5 This is consistent with the fact that the atomic separation, when considered in terms of the ratio of the atomic diameter R to the diameter r of the 3d-shell, is larger in the ferromagnetic metals. The values of R/r calculated by Slater,' for metals of the iron group are given in Table I, and Slater has suggested that the critical ratio of R/r is 1.5. Consideration of the criterion of atomic separation alone would suggest that there are three classes of possible ferromagnetic manganese alloys: 1— Ordered structures, of either solution or compound types, such that manganese atoms are not near neighbors; 2—Structures in which the separation of near-neighbor manganese atoms is sufficiently increased by the presence of suitable solute atoms; and 3—Dilute solutions of manganese. Typical ferro- magnetic alloys of types 1 and 2 are the Heusler alloys and Mn4N, respectively. There are no recognized ferromagnetic alloys of type 3. In view of the proximity of the ratio R/r for manganese to the critical ratio of 1.5, the present work was concentrated on manganese-rich alloys rather than on ferromagnetic alloys of low manganese content, several examples of which are already known. Calculation of the distance of closest approach of manganese atoms in each of its allotropic forms, Table 11, indicates that the high temperature ? phase provides the most suitable basis for ferromagnetic alloys of high manganese content. However the high temperature forms of pure manganese cannot be retained on quenching, although a face-centered-tetragonal form apparently can be produced by electrodeposition. Since the critical separation which must be exceeded in order to obtain ferromagnetism is dependent upon the number of electrons in the d-shell, no exact critical value of R/r can be assumed. Not only will this separation vary from one pure metal to another, but it will also vary with the valency of the given type of atom when it is in an alloy. Raynor8 has shown that metals of the iron group probably

Jan 1, 1955

By P. Chiotti, E. R. Stevens

The electromotive force between pure magnesium and Mg-Zn alloys in a fused KC1-LiCl-MgC12 cell was measured over the temperature range 360° to 730°C and for alloy compositions of 0.052 to 0.635 atom fraction magnesium. The calculated activity coefficients of magnesium in the liquid alloys may he represented by the relation These data and the phase diagram were employed in calculating the standard free energy of formation for the compounds MgZn, MgZn2, and MgZn2, In the temperature range from 25° to 590°C the relation ZINC-rich magnesium alloys have been shown to be very effective in reducing various solute chlorides or oxides from fused salts such as KC1-LiC1 eutectic. Such reactions are of interest in the developinent of pyrometallurgical methods for reprocessing nuclear reactor fuels.' As the conceniration of the magnesium is increased beyond 5 to 10 wt pct the extent to which solutes, such as yttrium, lanthanum, cerium, and other rare earths, can be reduced or removed from the salt decreases. This effect is due to the resulting change in the activity of the solutes in the Zn-Mg alloy as well as the change in the activity of both the zinc and mag- nesium. The purpose of the present investigation was to determine the thermodynamic properties of the Zn-Mg system which, in addition to yielding information on the alloying behavior of these two elements, would permit a more quantitative understanding of the above reactions. Since this investigation was initiated several publications have appeared in the literature giving results on the thermodynamic properties for the liquid alloys of this system. 2-4 Kozuka, Moriyama, and Kushima3 measured the vapor pressure of zinc over four different alloy compositions by a carrier-gas technique. Eremenko and Tukashenko2 and Terpilowski4 measured the electromotive force between pure magnesium and various alloys in a fused salt cell. Earlier work has been summarized by Hultgren, Orr, Anderson, and Kelley.5 In the present investigation electromotive-force measurements were made on a cell of the type The temperature range covered for the lower-melting alloys was roughly 375° to 730°C. These data were employed in calculating the thermodynamic properties for the liquid alloys and in conjunction with the phase diagram,' reproduced in Fig. 1, were used in calculating the standard free energy of formation of the compounds MgZn, MgZn2, and Mg2 Zn11. The results obtained are compared with available data from the literature. MATERIALS AND EXPERIMENTAL PROCEDURES Materials employed were: Bunker Hill slab zinc, 99.99 pct pure; Ames Laboratory magnesium containing 13 ppm N, 195 ppm C, and trace amounts of calcium, copper, nickel, and silicon; reagent grade KC1, LiC1; and high-purity MgC12 obtained from Dow Chemical Co. The electrolyte consisting of KC1-LiCl eutectic (44.4 wt pct LiC1) to which was added 15 wt pct MgCl2, was dried in a quartz tube by heating to 340° C under vacuum for a period of 4 to 5 hr, and then passing HC1 through the salt as the temperature was slowly raised to above the melting point of the salt. After about 3 hr the HC1 was shut off and the system flushed with argon and then vacuum applied for 1 hr. The salt was finally siphoned through a sintered glass filter and cast into a Pyrex container which was sealed and

Jan 1, 1965

By V. Koump, T. F. Perzak, R. G. Olsson

The vate of dissolutioz of carbon in molten Fe-C alloys urns studied by votating- cylindrical g-vaphite sairlples in a stationary crucible containing the melt. The rate of dissolltion was determdined from the change in the bnth co)npositiorz. Alccss-tvansfev coeffi'cients, calcilated with the assurlption that the inte)yacial liquid ulas saturated with carbon, were found to be in agreement with an existing Correlation fov mass transfer jroni votating cylinders. It is corzcllrded tlat, itz the wnge of- Reynolds' numbers itzvestigated (790 to 18,000), the vate of dissolutio of carborz in Fe-C alloys is controlled by tile rate of carbon difirsion from the interface. The dissolution of carbon in molten Fe-C alloys has been the subject of a number of investigations. Most of these investigations have been inconclusive because of poorly defined experimental variables. Two of the more sophisticated studies are summarized below. Dahlke and Knacke' studied the phenomenon by, in part, immersing graphite rods into 0.5 pct carbon-steel for different lengths of time. Since the experiments were conducted in air or in CO atmospheres, the melt was strongly agitated by gas evolution. It was concluded that the change in bath composition as a function of immersion time was in agreement with the assumption that the dissolution process was transport-controlled. The hydrodynamic conditions in these experiments, however, were not well-defined and gave no indication of the nature of the dissolution process at higher fluid velocities. In a recent study Shurygin and ruk investigated the dissolution of carbon in molten Fe-C, Fe-Si, Fe-P, and Fe-Ni alloys. Small graphite disks were rotated in a crucible containing molten alloys under such conditions that only the lower face of the disk was exposed to the melt. The results of this investigation indicate that, over the range of velocities (100 to 1000 rpm) and bulk liquid concentrations (0.7 to 4.5 wt pct C) considered, the dissolution of carbon in the iron alloys is limited by the diffusion of carbon from the interface to the bulk liquid (a transport mechanism). For the particular geometry used by these authors, exact analytical solutions of hydrodynamic and diffusion problems are aailable. Hence the experimental results obtained by Shurygin and Kryuk permit the evaluation of diffusion coefficients of carbon in the four systems investigated. In the present investigation a series of experiments were conducted in which the rate of dissolution of carbon in Fe-C alloys was measured under conditions which permitted wide variation of the fluid velocity and the carbon concentration of the bulk liquid. Graphite cylinders were rotated at different speeds in a stationary concentric crucible containing various molten Fe-C alloys. THEORETICAL DEVELOPMENT In general, the resistance to mass transfer from a solid interface to a turbulent liquid is assumed to reside in a laminar boundary layer adjacent to the interface. If it is also assumed that the diffusion coefficient is independent of concentration, the steady-state rate of dissolution for the case of arbitrary liquid and solid densities can be obtained from the integration of the equations of continuity. The derivation is similar to that used by Lommel and chalmers4 for the case of pl = ps. The solution, expressed in terms where N = rate of diffusion of the solute from the interface. Exact analytical solutions of the hydrodynamic equation for the boundary layer thickness are available for only a limited number of geometries. Consequently, a mass-transfer coefficient, k, is usually

Jan 1, 1967

By J. D. Price, W. M. Bertholf

Making maximum possible use of available equipment and material, CF&I placed a high-efficiency, high-capacity washery unit in the existing buildings to gain simplified operation, reduced manpower requirements, raised efficiency, and boosted production. THE central washing plant of the Colorado Fuel & Iron Corp. was first operated in 1918 to furnish coal for two 60-oven batteries of Koppers design. Prior to that time the coke for the blast furnaces had been secured from a number of beehive operations, some with their own washeries. The original washery had four Elmore jigs, which did not do as well as had been expected. In 1923 the jigs were taken out and replaced by Deister Plat-O tables, with various changes in auxiliary equipment. In 1936 the throughput of the plant was considerably increased by the installation of vibrating filters for recovery and drying of fine coal, thereby reducing a large recirculating load of fine coal which passed through the screens of the Carpenter driers. In the late 1940's it became evident that something would have to be done to keep the washery abreast of progress at Pueblo and other washeries. Coal requirements were nearly two and one-half times the original requirements of the 120 small ovens, as additional ovens had been built in 1930, 1938, and 1945, whereas no additional coal washing capacity had been added since the 1936 modifications. Much of the equipment, moreover, had seen better days. One answer to the problem was to build a new and completely up-to-the-minute plant, with sep- arate sections for coarse, medium fine, fine, and very fine coal. On the other hand, it might be financially more profitable to place a high-efficiency, high-capacity unit in the existing buildings. The washing problem at Pueblo is not unique, but it is approached differently. There are no established specifications for coke ash and sulphur. The plant is operated on the principle that if it is more economical to wash it out than to slag it out, wash it out; otherwise, send it on to the blast furnaces. With coals at the Pueblo plant costing what they do, the benefits of washing at a low gravity are questionable. Hence the primary problem is to eliminate the high-ash components and retain all the low and medium-ash components. Sulphur is no problem at all, averaging 0.6 pct in the coke. Since a good proportion of the free impurity in the coals is as large as the coal or bone or larger, it appeared that it would be safe to go to jig washing and discontinue crushing the coal before washing, as had been the practice with the tables. This would boost the throughput. It might also decrease manpower requirements and washing costs considerably. It was assumed at the start and has been demonstrated in the first year of operation that a jig will do as well on the fines as the tables had been doing. It would not be necessary to discount any gains due to increased efficiency in washing the coarse material because of incapacity to wash the fines. By washing at —2+0 mesh it would be possible to dewater, by screening, a considerable tonnage satisfactorily, for example, at —2 + % or —2 + l/4, and then crush it in a hammer mill. The —?+20 could be dewatered in centrifugal driers and the remain-

Jan 1, 1955

By D. G. Westlake

NUMEROUS hydride habit planes in zirconium, Zircaloy-2, and Zircaloy-4 have been observed by various researchers and have been compiled by Louthan and Angerman.1 While only partial agreement exists on the identification of these habit planes, there is a growing consensus that a tensile stress applied on a polycrystalline rod during slow cooling will cause the hydride platelets to lie perpendicular to the tensile axis. walters2 agrees with Louthan and Angerman who reason that "The particular plane on which precipitation will occur is the plane that will result in the maximum relief of stress by precipitation of the low-density hydride." The experiment described below was initiated to test this hypothesis on a single crystal of zirconium. A single-crystalline tensile specimen of zone-refined zirconium, designated number 13 in a previous study,3 had a square cross section with one pair of parallel faces only 4 deg from the basal plane of the hcp structure. The tensile axis was about 86 deg from the (0001) pole, 14 deg from the (1010) pole, and 16 deg from the (1150) pole. The specimen was charged to 50 ppm H by allowing reaction with the correct amount of hydrogen at 1073°K, homogenizing at this temperature for 2 hr, and cooling in the furnace. Two- surface analysis revealed that hydride platelets had precipitated parallel to the three {1010} prism planes. The specimen was heated to 673°K, in air, for 16 hr to bring the hydrogen back into solid solution, and furnace-cooled to 573°K.* It was then stressed in ten- sion at 1.2 kg per sq mm. (This produced a resolved shear stress of 0.6 kg per sq mm for glide on the prism plane with the highest Schmid factor. A higher stress would have produced significant strain at this temperature because the critical resolved shear stress for prism-plane glide in this crystal was only 1.0 kg per sq mm at ambient temperature.) The poles of the three prism planes were at angles of 14, 46, and 74 deg to the tensile axis so that an applied stress would exert normal stresses on the three planes in the approximate ratios 10:5:1, respectively. As soon as the stress was applied, the sample was furnace-cooled to room temperature. It was ground on wet Sic paper and chemically polished in 50 parts HNO3, 50 parts water, and 7 parts HF before examination. The result of the experiment was negative; i.e., the three (1010) planes were of equal importance as hydride habit planes.* It must be admitted that the ex- periment is not entirely comparable to those performed by walters,2 Louthan,5 and Louthan and Marshall6 on polycrystalline materials. They have found that some critical stress (below the macroscopic yield stress) is required for stress-orienting the hydrides. The applied stress in the present experiment was, by necessity, smaller by an order of magnitude than the critical stresses they report for the various materials. If the critical stress was related to the microstructure, one might postulate that it should be decreased by increasing the degree of perfection of the metal lattice and by increasing the grain size. But the experiment above suggests that, for the extreme case of a zone-refined single crystal of zirconium, the critical stress lies above that which one can apply without introducing gross plastic strain as another variable.

Jan 1, 1967

By E. S. Bumps

A series of macrographs are presented for the purpose of graphically recording the strain phenomenon that accompanies the energy transition in the Charpy impact testing of a mild steel that is susceptible to strain aging. STRAIN patterns in mild steel Charpy impact specimens were obtained in order to determine whether, on the first appearance of plastic strain during deformation, the initial fracture cracks appear in the region of plastic strain or in the elasti-cally deformed regions between. Although this attempt to locate the initiation of cleavage was not successful, the observed strain patterns illustrating various stress conditions in partially deformed Charpy specimens are presented along with a discussion of the possible dependence of transition energy on the yield phenomenon. Earlier work on the development of strain patterns in mild steel have been reported by Fry1 and later by Jevon.2 Harris, Rinebolt, and Raring3 observed characteristic strain markings on the surface of Charpy V-notch impact specimens fractured above and below the transition temperature which they presented schematically. It is intended that the strain figures presented here will add to the literature a graphic correlation of strain with transition energy in impact specimens. Samples of % in. round hot rolled, 0.20 pct C steel were machined to standard 0.394 in. sq, V-notch Charpy impact specimens. Preliminary testing involved determination of transition temperature, Fig. 1, using a Sontagg impact tester. These data were subsequently used to select temperatures above, within, and below the transition range at which specimens were partially deformed. Partial deformation was obtained by either varying the energy or the testing temperature, see Table I. Macroscopic strain figures shown in Figs. 2 to 19 were produced by several metallographic repolish-ing and etching steps. The macroetchant used was as follows:4 120 g HCl, concentrated; 100 ml water; and 90 g cupric chloride. Strain figures were obtained on the outer surface and on sections through the central portion of the impact specimens in order to determine an approximation of the volumetric strain pattern. In the tensile strain figures reported by Jevon, it was found that strain etching would not work immediately following strain unless the material was heated to 200°C. The impact strain patterns presented here were obtained without this heating, but the specimens were not etched until ten months after straining. This confirms a discussion of Jevon's paper, in which it was pointed out that strain figures can also be developed after aging for long periods of time at room temperature. Hardness of the strained and unstrained portions, revealed by the etched pattern, was explored using R, impressions converted to R, hardness values. Discussion of Results In the impact test, as in the tensile test, some parts of the specimen yield and deform plastically, while other regions are deformed only elastically. The plastic deformation bears a relation to the imposed stress pattern. In the strain figures presented here, the plastically deformed regions are the dark etching ones. The strain figures are always symmetrical because the stress state in the Charpy-type specimen under impact loading is symmetrical. The difficulties encountered to produce initial cracks are intimated in Figs. 2 and 4. At a temperature of —75ºF, the stress was not sufficient to pro-

Jan 1, 1953

By E. P. Miesch, P. B. Crawford

A study was made of the effect of permeable and impermeable lenses in a reservoir on the production capacity of a well. Both steady-state and unsteady-state data were obtained. An electrical resistivity model was used to obtain the steady-state data and thermal models. were constructed to obtain the unsteady-state data. The productivity of a well is affected very greatly only when the lenses are close to the well. The effect of circular lenses on the productivity ratio can be correlated with the distance from the center of the lens to the center of the well divided by the radius of the lens. When this dimensionless distance is equal to six or greater, the effect of the lenses on production capacity will be negligible. The pseudo steady-state productivity of a heterogeneous reservoir can be predicted using steady-state data. INTRODUCTION Many analytical solutions of reservoir behavior assume that reservoir rock is uniform and homogeneous. Although this assumption is used, all of the data from core analyses and well logging indicate that the reservoirs are heterogeneous. Very little work has been done on the performance of heterogeneous reservoirs. The work of Landrum,l et al. showed that transient phenomena in oil reservoirs could be studied with thermal models. Pickering and Cotman2 used thermal models to study flow in stratified reservoirs and investigated the effect of inhomo-geneities in oil reservoirs on transient flow performance. Loucks3 made a mathematical study of the pressure build-up in a system composed of two concentric regions of different permeability. Root, Silberberg and Pirson4 studied the effect of the growth of the flooded region on water influx predictions using a thermal model consisting of three concentric cylindrical regions of different thermal properties which simulated the aquifer, the flooded region and the unflooded portion of the original hydrocarbon region. Tomme, et a1.5 made a mathematical study of vertical fractures. The object of this investigation was to study the effect of highly permeable and impermeable lenses in the vicinity of the wellbore on the pressure depletion history of the well. Steady-state data were obtained for both conductive and nonconductive lenses that completely penetrated the formation. The lenses were symmetrically located at various distances from the wellbore. The unsteady-state data were obtained on seven thermal models. EXPERIMENTAL EQUIPMENT AND PROCEDURE STEADY-STATE DATA The steady-state data were obtained from an electrical resistivity model 30 in. in diameter and approximately 11/2 in. deep. The outside of the model was lined with a 30-in. diameter copper strip, which served as the outer boundary of the reservoir. The bottom was covered with a sheet of plexiglass so that it would be nonconductive. The model was filled with a slightly saline solution. The well size was varied from an 0.064-in. diameter copper wire to a 10-in. diameter copper cylinder. Readings were taken with an impedance bridge using AC current to prevent polarization at the contacts. Copper and wax lenses were used to represent infinitely conductive and nonconductive lenses, respectively. The resistance was first measured for each well diameter with no lenses in the reservoir. Then the conductive and nonconductive lenses were spaced symmetrically at various distances from the well and the resistance read from each lens location. The diameters of the conductive lenses were 3, 1.022 and 0.624 in., and those of the nonconductive lenses were 3, 2.25 and 1.563 in. The ratio of each resistance reading to the resistance reading with no lenses in the reservoir

Jan 1, 1965

By J. Chipman, N. J. Grant, R. Rocca

Desulphurization of liquid iron by reducing slags of the electric-furnace type was studied from 65 heats. Variations were made in basicity over a wide range and in FeO up to about 5 pct for their effects on desulphurization. The role of FeO in desulphurization from the blast furnace, to the electric furnace, to the oxidizing conditions of the open hearth is shown to fit a relatively simple pattern of behavior. THE mechanism which controls the desulphurization of molten iron by basic slags has been the object of several investigations. In particular, equilibrium determinations have been made both in the field of basic open-hearth slags, which have a high iron-oxide concentration, and in the field of blast-furnace slags which have a very low iron-oxide concentration. In both cases the desulphurization ratio has been found to increase with increasing basicity of the slags; however, the mechanism of desulphurization differs in the two cases. In basic open-hearth slags desulphurization occurs mainly as a partition of iron sulphide:&apos; FeS * (FeS) and the desulphurization ratio is approximately independent of iron-oxide concentration in the slag. In blast-furnace slags the concentration of iron oxide is very low as a result of the highly reducing conditions in which they are formed. The controlling reaction for desulphurization is then:2,3 FeS + (CaO) <=* (CaS) + (FeO) The slags of the reducing stage in the electric furnace have an iron-oxide concentration which is intermediate between blast-furnace and open-hearth slags. The study of the mechanism of desulphurization for these slags has been the object of this investigation. The importance of low (FeO) in the slag for desulphurization was first verified by Bardenheuer and Geller,& who found that high desulphurization ratios were obtained in highly reduced slags. It was recognized" hat iron oxide in the slag becomes a controlling factor in desulphurization only at FeO concentrations approximately under 5 pct. A recent investigation conducted by Buehl,7 upon the suggestion of one of the authors, confirmed this opinion from the results obtained from a heat conducted in a small arc furnace. In the present investigation, slags of very high basicity, such as often are encountered in the basic electric furnace, could not be studied, but equilibrium data have been obtained for slags in a wide basicity range. The iron-oxide concentration in these slags ranged from 0.08 to 15 pct and was controlled by the addition of silicon to the metal. Other constituents of the slags were mainly CaO, MgO, SiO2, A120,, and CaF,. The experimental technique was essentially the same as that of previous investigations.1 8-lo In an open magnesia-lined induction furnace, 65 lb of Armco ingot iron was melted. An atmosphere of hydrogen was maintained over the melt for 1 hr to bring the carbon content down to approximately 0.010 pct maximum. The bath then was exposed to air for 25 min to remove hydrogen. The electrodes were put in place, and the furnace was operated from this point on in an atmosphere of nitrogen. A synthetic slag was added to which additions of silicon and iron sulphide were made. A rate study conducted at the beginning of this investigation had

Jan 1, 1952

By R. F. Domagala, M. Hansen, D. J. McPherson

On the basis of metallographic analysis, incipient melting data, thermal analysis work, and X-ray diffraction, phase relationships in the 0 to 50 atomic pct Cr region were carefully resolved. Phase relationships in the 50 to 100 atomic pct region were outlined. A single intermediate phase, ZrCr,, was established in the system. A eutectic and a eutectoid were found in the zirconium-rich region of the system, while a eutectic was located in the chromium-rich region. Limited solubility of chromium in both a and a zirconium was observed. THIS is another in a series of papers on zirconium-base binary phase diagrams based on a program sponsored by the Atomic Energy Commission. The Zr-Sn,&apos; Zr-Si,&apos; and Zr-Mo and Zr-W" systems have already been published. Previous work on the Zr-Cr system includes a partial diagram by Hayes, Roberson, and Davies&apos; and a complete diagram by McQuillan." The phase relationships reported by these authors were determined with magnesium-reduced zirconium, whereas those reported herein are based on iodide metal. Some X-ray work on the intermediate phase in this system was also reported by Hayes et al., as well as by Wallbaum.&apos; Comparisons with these data are made in the appropriate sections. Thermal analysis, metallographic and incipient melting techniques were employed to accurately resolve phase relationships in the 0 to 50 atomic pct Cr region, while the remainder of the diagram is outlined on a basis of cast structures and thermal analysis. A description and analyses of the metals used in the preparation of alloys for this study are included in Table I. A "low-hafnium" zirconium crystal bar (Westinghouse "Grade 3") was used. This material was produced by the decomposition of a volatile iodide onto a hot zirconium filament. The as-received crystal bar was coated with corrosion product from a standard autoclave test by which its grade designation is determined. A sand-blasting and subsequent HF-HNO, pickling treatment was employed to remove this contamination. The bars were cold-rolled to approximately 1/32-in. sheet, pickled again, sheared to 1/4-in. squares, washed with acetone, and stored for use. Ingot chromium metal from National Research Corp. and electrolytic chromium flakes from Johnson, Matthey and Co., Ltd., were available as alloy additions. The ingot chromium was received in granular form. The large granules were sized by crushing, treated for iron removal, rinsed with acetone, and stored. The flakes were broken to approximately 1/8 in. with mortar and pestle, cleaned with acetone, and stored for charging. Experimental Procedure A nonconsumable electrode arc furnace identical to that described by Hansen, Kessler, and McPher-son,&apos; was used in this work. A 400 amp dc welding generator was the source of power. To insure homogeneity, ingots were melted in a water-cooled spun copper crucible, a total of four times without opening the furnace. No difficulties were encountered in the preparation of these binary alloys. Analyzed chromium contents were found to agree very well with the intended content. Melts of pure zirconium were interspersed in the course of preparing the alloys and their hardness was measured to keep a constant check on the melting technique. Vycor and quartz bulbs were used to contain the samples for isothermal annealing treatments. Vycor bulbs were employed for temperatures up to 110O°C, while quartz was used above this temperature. For treatments up to 950°C the bulbs were evacuated before sealing, but for higher temperatures a partial pressure of argon was admitted to the

Jan 1, 1954

By C. L. T. Edwards

IN the preparation of this paper, the author has drawn upon experience with the operation of a blast furnace on 100 per cent scrap burden, which he believes was the first operation of its kind in the country. It is the writer&apos;s further belief that much of the controversy attending discussions of this subject may be obviated by the presentation of a group of facts that should be known by blast-furnace men and open-hearth men alike. The following question has been raised: "Is iron made with scrap in the blast-furnace charge as good iron as that made without scrap-made with straight ore?" This question may be answered in part by the fact that the open-hearth men of the Bethlehem Steel Co. who used pig iron from a blast furnace that operated on 100 per cent steel scrap found no difficulty in the processing of such iron other than that to be expected from the known analysis. OPERATION WITH 100 PER CENT STEEL SCRAP During World War I, there was accumulated at the Bethlehem plant of the Bethlehem Steel Co. some 22,000 tons of alloy-steel turnings and borings. This scrap material was highly corroded and, like alloy-steel turnings of that period, were as a drug on the market. There was also a small tonnage of scale, rich in valuable metal. If this scrap could be worked up into pig iron, it would become readily available for use in the open hearth. In order that the pig iron should contain the maximum percentage of nickel, permission was obtained from the Management to try a 100 per cent scrap operation. Accordingly, a blast furnace was swung over on July 25, 1919; the percentage of steel scrap increased more or less irregularly until July 29, when l00 per cent steel turnings were charged. Except for occasional charges of nickel scale as an "extra," the operation continued uninterruptedly until Aug. 27, when the furnace was swung back to the regular ore-ore and scrap-operation. During this period, the furnace production ranged from a low of 568.60 tons to a maximum of 766.07 tons. At the swing-over from i00 per cent scrap to the regular burden, the charge hung up rather severely. While the latter condition has nothing to do with the object of the paper, a brief discussion of the experience will appear later because of the interest it may have for blast-furnace operators. In Table I, results of the first and last days of the ore charge are shown, July 25 and July 29. The last column shows a summary for the period of maximum scrap charge. The furnace employed had a hearth 16 ft. 0 in., bosh 22 ft. 0 in., stock line 15 ft. 6 in., bell 11 ft. 6 in., batter ¾ in., bosh angle 73° 27&apos; and a Baker-Neuman top, with gas-engine blowers. Analyses Range of Material Charged Gravel: Si02, 64.40 to .7o.54 per cent; A1203,3-52 to 4.58; CaO, 7.27 to 9.49; M90, 5.09 to 6.14; FeO, 1.67 to 3.34, ignition loss, 9.50 to 13.83.

Jan 1, 1941

By H. R. Stahi

THE ore of the Southeast Missouri lead district consists essentially of galena in dolomitic limestone. The galena usually is in a very finely disseminated condition. The experience of recent years in the concentrating plants of the St. Joseph Lead Co. has shown that dry crushing carried to a point where about 90 per cent of the ore passes a 14-mesh screen liberates the larger portion of the galena, and minimizes further necessary reduction in rod or ball mills. Concentration practice has attempted to carry size reduction to a point where economic unlocking of the galena is obtained, without causing undue sliming of the very friable galena. While 60 per cent of the tonnage of the district is treated by the flotation process, only 40 per cent of the total concentrates is produced by that means, as efforts have always been made to keep the grade and tonnage of flotation feed as low as possible. The milling practice of the district for some years has recognized the generally accepted idea of better selective grinding in rod mills as compared with ball mills, with the attendant decrease in production of fines. The function of rod and ball mills in the various concentrating plants is the grinding of table middlings and coarse tailings that carry lead values too high to be discarded. The simplified flowsheet in Fig. I illustrates the place of grinding mills in the circuit. The arrangement of classifiers, tables and mills constitutes a closed circuit within somewhat flexible limits. In 1937 experiments were conducted in replacing the ball charge in a 6 by 4-ft. ball mill with rods 2 in. in diameter and 51 in. long. This step was taken with some hesitancy, as it was easy to picture a mass of tangled and crossed rods. However, no difficulties developed, and after a short trial period, six more ball mills were converted to rod mills. These mills are of the spur gear and pinion, belt-driven type, using in most cases a 75-hp. motor and having a 9 1/2 -in. open trunnion discharge. As ball mills, they carried a charge of 16,000 to 20,000 lb. of balls, 2 in. in original size. The feed to the mills was dewatered by dewatering wheels and introduced at 70 to 75 per cent solids, with a single scoop feeder. One change in mill design was found advisable when rods were introduced. The existing end liners had an outward flare of 3 ½ in. in 12 in. These were replaced by linings having vertical interior faces, in order to prevent undue end travel of the rods. This change gave an effective working length of 5 2 ¾ in. inside the mill. No alterations were made in the shell liners, which are of the smooth type, made of manganese steel 2 in. in original thickness. The rods at present in use are 51 in. long and 1 3/4in. in diameter. The composition has been varied at times; at present they contain 0.70 per cent carbon and 0.70 per cent manganese. Some breakage and etching occurs as the rods become small, but this is considered preferable to using softer rods, which may kink and cause tangling of the charge. The mill charges are renovated occasionally, broken pieces being removed and the charge brought up

Jan 1, 1945

By Charles L. Guettel

The temperature coefficients of electrical resistance of 31 alloys in the nickel-rich corner of the Ni-Cr-Fe system were determined. The results indicate that a range of binary Ni-Cr alloys has lower temperature coefficients than a specific region of Ni-Cr-Fe alloys which has been reported and quoted by others as providing the lowest coefficients in the ternary system. DESIRABLE properties of resistivity and temperature coefficients of resistance have been the basis for the successful commercial application of various Ni-Cr and Ni-Cr-Fe alloys. In particular, low or negligible temperature coefficients of resistance are necessary for wire used in precision wire wound resistors and potentiometers involved in closely controlled electrical and electronic circuitry. Alloys most successfully applied to this purpose basically have not been ternary Ni-Cr-Fe alloys but rather heat-treated Ni-Cr alloys in the region of approximately 73 to 79 pct Ni and 20 pct Cr with significant additions of other elements such as aluminum, silicon, iron, copper, manganese, and cobalt. While the addition elements play a vital role in the nature and control of the temperature-resistance curve of any one of these alloys, the inherent relatively low temperature coefficient of the binary Ni-Cr base composition itself in the approximate region of 80 pct Ni and 20 pct Cr contributes fundamentally to the eventual negligible temperature coefficient obtained with the applied alloys. W. A. Dean 1 has reported mean temperature coefficients (20&apos; to 100oC) of as-cast samples for the Ni-Cr-Fe system, the nickel corner of which is given in Fig. 1. Dean had to use as-cast samples because alloys from a considerable region of the system were unworkable. Dean refers to the work of Hunter and sebast2 who used annealed wire samples to show that, for chromium contents of 10 to 25 pct, the temperature coefficient increases as the iron content is increased at the expense of nickel. Although the data of Hunter and Sebast were limited in the nickel-rich areas to eight samples of 60 to 91 pct Ni with only four samples containing iron, the possibility that no Ni-Cr-Fe alloy has a lower temperature coefficient than certain binary Ni-Cr alloys should have been given serious consideration. However, Dean&apos;s work has been referred to by J. S. Marsh,3 who, quoting Dean, states that for the temperature coefficients "the smallest values-about 0.0001 per oC (100 ppm)—were found for alloys containing about 55 pct Ni and 20 pct Cr" (balance iron). A region such as that reported by Dean would be significant to those trying to develop alloys for the applications described. Therefore, a series of three-pound laboratory open-air induction melts of Ni-Cr and Ni-Cr-Fe alloys were melted, conventionally processed to 0.005 in. diam wire, and continuously strand annealed at 1900° F. The basic Ni-Cr compositions, with balances essentially iron other than usual minor impurities, and the corresponding temperature coefficients of resistance and resistivities are given in Table I. The resistivities are approximate and are not to be considered as a basis for relating them to their position of composition in the ternary system. The wire diameters were determined with a micrometer, and not by weight and density measurements which would be required for accurate resistivity values. However,

Jan 1, 1963

By O. N. Carlson, D. G. Alexander

THE hardness anisotropy of metals and alloys has been of increasing interest in recent years but silicon ferrite,1 niobium,2 and tungsten3,4 are the only bcc metals about which this type of information has been reported. This investigation was carried out on vanadium and chromium single crystals in an effort to determine to what degree the hardness variations observed in these metals are due to orientation effects and to compare their behavior with other bcc metals. In earlier work the authors had observed a small angular dependence in the Diamond Pyramid Hardness of single crystalline vanadium on the (100) plane but no anisotropic effects were noted on either the (110) or (111) planes. At the suggestion of R. G. wheeler5 it was decided to investigate this effect in greater detail using the more asymmetric Knoop indentor. The vanadium metal used in the study was prepared by the aluminothermic reduction of V2O5 followed by electron beam melting.6 The principal analyzed impurities were 230 ppm C, 230 ppm O, 65 ppm N, 90 pprn Al, Cr not detected, 50 ppm Fe, 60 ppm Ni, and 200 ppm Si. The chromium was an iodide-refined product obtained from the Chromalloy Corporation. Analysis of this material showed the following amounts of impurities present: 10 ppm C, 9 ppm O, 2 ppm N, 0.4 ppm H, 3 ppm Al, 2 ppm Ca, 2 ppm Cu, 20 ppm Fe, 1 ppm Mg, 0.3 ppm Mn, 1 ppm Mo, 3 ppm Ni, 10 ppm Si, and 1 ppm V. Single crystals of both metals about 1 cm in diam and 10 cm in length were grown by an arc-zone melt- ing technique.7 The chromium crystal was annealed at 1600°C for 6 hr in a purified argon atmosphere to remove any strains or inhomogeneities, but the vanadium was tested in the as-grown condition. The crystals were oriented by the Laue back-reflection method and then sectioned with a spark cutter into individual specimens with a (loo), (110), or (111) plane parallel to the crystal surface. They were mounted in Lucite and carefully ground to a flat surface. The vanadium specimens were then electropolished in a 6 pct perchloric acid-methanol mixture while the chromium specimens were mechanically polished on a Syntron vibratory polisher using an alumina abrasive. The orientation of each crystal was then rechecked by the back-reflection X-ray method. All of them were found to lie within 2 deg of the desired orientation with the exception of the (110)-Oriented chromium crystal which was within 4 deg. Microhardness impressions were taken at 10 deg intervals from the common (110) direction by rotating the crystal in the plane of the crystal surface. A Knoop indentor was used with a 400-g load on the vanadium crystals and an 800-g load on the chromium. The hardness values are averages of 6 impressions and standard deviations were calculated for each set of data. The values reported for the (111) plane of vanadium are based on from 10 to 15 measurements for each point. The microhardness results for vanadium and chromium are plotted as a function of the angular rotation of the long axis of a Knoop indentor from the (110)

Jan 1, 1970

By D. H. Gray, G. Bergamini, I. Fatt

A method developed by soil scientists for measuring permeability anisotropy of soils has been adapted for use in studies of sandstone permeability aniso-tmpy. Studies on Berea and Bandera sandstone show that permeability of these materials decreases upon application of simulated overburden pressure. Permeability reduction of Berea and Grubb sandstone cores subjected to simulated overburden pressure is shown to be a function of the ratio of radial to axial stress. INTRODUCTION The effects of mechanical stress on reservoir rock parameters are now generally accepted as being important in reservoir engineering calculations. In several oil fields the unique behavior of the reservoir has been attributed to the influence of overburden pressure or internal fluid pressure on rock permeability or fluid content. l Although the gross effects of overburden pressure on permeability, porosity, waterflood efficiency, electrical resistance and sonic velocity have now been established,3-9 there are some very interesting, and perhaps important, details of rock behavior under stress that have not heretofore been studied. In this paper we will show that permeability anistropy of several sandstones is a function of overburden pressure. We will also show that permeability reduction of cylindrical samples of two sandstones, when subjected to mechanical stress, is a function of the ratio of radial to axial stress. Most studies of overburden pressure effects made in the past have attempted to duplicate reservoir conditions by applying hydrostatic external pressure on all surfaces of the sample. Assuming perfect elasticity, that is, no viscoelastic flow during geological time, reservoir rock in situ cannot be under hydrostatic stress as is apparent from the value of 0.25 for Poisson&apos;s ratio for most rock. In the absence of tectonic forces the horizontal stress component If there are directional permeability effects, as has been reported from field and laboratory studies, l0,11 then one would expect hydrostatic stress as used in the laboratory to give a different permeability reduction from that occurring under reservoir stress conditions. The influence of stress on directional permeability was measured by a modification of the method first described by Maasland and Kirkham for use on soil samples.12 Their method permits calculation of the permeabilities along each of the three mutually perpendicular axes of a cubic sample. The modification reported in this paper extends the method to observing these permeabilities when the sample is under hydrostatic stress. The Hassler sleeve type of core holder is satisfactory for studying overburden pressure effects on permeability if a known force is applied to the end plugs. Wyble6 used a sleeve core holder but did not load the end plugs. In this paper we combine sleeve pressure and axial force to give permeability changes which we believe are close to those occurring in reservoirs when reservoir pressure changes. The combination of sleeve pressure and axial force assumes, however, that the sleeve pressure simulates both vertical stress and horizontal stress in one direction. METHOD PERMEABILITY ANISOTROPY The Maasland and Kirkhaml2 method of measuring permeability anisotropy uses a cube of porous material which is Open On three faces and has discs with a Center hole for an air inlet cemented to the other three mutually perpendicular faces (Fig. 1). The rate at which air pressure falls in a bottle of known volume, and pressure slightly above atmospheric, when the bottle discharges through each disc, is

By D. N. Seidman

In the course of a study of the electronic and thermodynamic properties of Pb-Se alloys it was found necessary to have an accurate knowledge of the phase diagram. However, the literature is in disagreement as to whether or not a monotectic reaction occurs in the lead rich portion of the phase diagram. Pelabonl reported only a two-phase region consisting of lead-rich liquid and solid PbSe extending from almost pure lead to the compound PbSe, and gave the melting point of PbSe as 1065°C. The data of Friedrich and Leroux2 are in general agreement with this type of diagram, with the melting point of the compound being 1088°C. However, Nozato and Igaki by inverse rate thermal analysis observed a monotectic reaction isotherm exlacing at 860°C with a monotectic composition of 20.5 at. pct Se. The miscibility gap in the liquid state extends from 7.5 to 20.5 at. pct Se. Hansen and Anderko4 accepted Nozato and Igaki&apos;s phase diagram in the region of the lead-rich monotectic. To reinvestigate this portion of the phase diagram, both thermal analysis and metallographic examination of various compositions were performed. The thermal analysis apparatus was constructed according to the specifications of the National Bureau of Standards. A t/t-l pct Rh thermocouple was calibrated against the melting point of copper (NBS), zinc (NBS), and antimony (A. D. Mackay), the emf being measured with a Rubicon Type B potentiometer sensitive to lpv. The absolute accuracy of the thermal analysis obtainable with this system is ± 0.5oC. Starting materials were semiconductor grade lead and selenium purchased from the American Smelting and Refining Co. Both elements were 99.999 pct pure with only trace impurities detected upon spectroscopic examination. One hundred galloys were sealed in quartz crucibles with a central thermocouple well under a vacuum of less than 1 p. This procedure prevented any composition change due to vaporization during the run. Cooling curves were obtained on the alloys listed in Table I. Data was taken by the direct method at cooling rates ranging between 1/2 to 2°C per min. The alloys were heated well above the liquidus and shaken vigorously to insure homogeneity. No evidence of an arrest indicative of the monotectic reaction was observed, and the two-phase region reported by Pelabonl and Friedrich and Leroux? was confirmed in general, although our data give higher liquidus temperatures than Friedrich and Leroux. The melting point of stoichiomet-ric PbSe determined for two different samples was 1080.7 0.5oC. The results of this investigation are compared with Nozato and Igaki&apos;s data in Fig. 1. To Complement the thermal analysis data, an 86 at. pct Pb specimen was examined microscopically. This composition was in the center of the miscibility gap reported by Nozato and Igaki.3 The alloy was heated to 1000°C, held for 1/2 hr, and water quenched. The specimen was polished using standard metallographic techniques for lead. The alloy was etched with an acetic-nitric acid etchant for 10 min at 45°C. Microscopic examination did not indicate the existence of two separate layers or solidified droplets imbedded in a matrix, as would be expected if a miscibility gap were present. The mi-crostructure shown in Fig. 2 consists of uniformly dispersed, dendritic PbSe in a lead-rich matrix.

Jan 1, 1962

By S. C. Sun

Most previous work on sedimentation of coal 1 and mineral 2-3 suspensions has been conducted in graduated 1-liter glass cylinders of 6-cm diam. With this type of large container it is often difficult to see through the suspension and tedious to perform a large number of tests. Furthermore, the heavy glass walls and the graduation lines of glass cylinders cause internal and stray reflections, respectively. To obviate these difficulties, an Atlab Emulsion Viewer from Arthur H. Thomas Co. was adopted as an alternative apparatus. Equipment: The viewer," shown in Fig. 1, consists of: 1) a stainless steel frame rack holding 21 flat-bottom Nessler tubes or an ungraduated replica 1.64 cm ID and 1.80 cm OD, 2) a movable masked 150-w lumaline lamp behind the tubes, and 3) a scaled glass panel with 100 vertical divisions in front of the tubes. The tubes are snugly held by springs in slots formed by spacer bars, which also serve as shields to eliminate stray light. The lumaline lamp is mounted behind a slit in a movable housing so that it can be positioned behind the suspension to be examined. The lowest or 100-divi-sion line on the front glass plate is leveled with the upper side of the bottom of all tubes. The scaled portion of each tube, roughly 19 cm high and 40 ml in volume, is used to study coal and mineral suspensions. Procedure: The following procedure was used in many tests. A 1.6-gm sample of dry coal was mixed with 16 ml of distilled water in an ordinary test tube and allowed to stand for three days, with occasional shaking to insure thorough wetting of all particles. The slurry was transferred to a Nessler tube and diluted to 32 ml. The pH regulator and flocculating reagent were added, and the slurry was diluted to reach the uppermost or zero-division line. The tube was immediately stoppered and inverted downward and up again ten times during a period of 35 to 40 sec. The lumaline lamp was turned on during the inversion period. After inversion the tube was quickly returned to the viewer rack. The time elapsed for each 10-division drop of the demarcation line between solid and liquid was recorded by stopwatch until the 80-division line was reached in the zone of compression. Additional readings were taken at 15, 30, and 60 min after settling began. The clarity of the supernatent liquid was observed also. As the settling rate became considerably slower at the 75-division line, it was convenient at this time to start the next test in a separate Nessler tube. This was continued until the suspensions in any number of the 21 tubes were tested. An attempt was made to correlate the experimental results between the Nessler tube and a 1-liter glass cylinder. Table I shows that coal particles settle much faster in the cylinder than in the tube, which has a large wall effect.&apos; The correction factor for the tube impedance is 1.662 2 0.145 at the 40-division line in the hindered settling zone, and 1.614 & 0.139 at the 75-division line in the compression zone. This rough correlation was established by dividing the pulp height of each container into 100 divisions and comparing the settling rates of the two containers at the same divisions. Tests were also performed to determine the accuracy of the viewer. The results, not presented, showed that error was within 10 pct.

Jan 1, 1960

By N. H. MacMillan, W. M. Mularie, R. E. Jackson, A. R. C. Westwood

The initial results of a study of the environment-sensitive microhardness and diamond rotary drilling behavior of granite and its constituent minerals quartz and feldspar (microcline)1 have established that many similarities exist between the environment-sensitive mechanical (chemomechanical) behavior of these materials and that of the simpler solids such as periclase, soda-lime glass, and alumina4 studied previously, at least as far as n-alcohol (straight-chain alcohol) environments are concerned. The results of this study (hereafter designated study I) also suggested that the rate of drilling of granite in these environments is controlled by the chemomechanical behavior of its quartz constituent, and is greatest in those environments which impart a zero l-potential to this phase, thereby maximizing its hardness. Now, cationic surface-active species strongly influence the l-potentials of silicate minerals. For this reason they are widely used in mineral separation operations. In particular, dodecyl trimethyl ammonium bromide (DTAB) was found in study I to produce f 0 for quartz at a concentration in water of 107 to 10-4 moles per 1. Accordingly, the influence of dilute aqueous solutions of this surfactant on the drilling behavior of granite also was examined in study I. This revealed that granite could be drilled three to four times faster in 10-° molar aqueous DTAB than in water, and confirmed by experiment the suggestion that granite is most effectively drilled with a diamond core bit in environments which impart a zero l-potential to quartz. According to O&apos;Connor and Buchanan&apos; however, the isoelectric point for quartz in aqueous DTAB solutions occurs at a concentration of .•.•2 x 10-° moles per 1, rather than [101 to 10-1] moles per 1. To confirm the results of study I, therefore, a more comprehensive investigation of the [ ]-potentials of quartz, microcline, and Westerly granite in aqueous DTAB environments has now been undertaken. At the same time an examination has been made of one of the basic assumptions of the current conceptual understanding of chemomechanical effects. In this view, although hardness changes occur essentially instantaneously following wetting of the solid, they are confined to a surface layer at most a few micrometers (µm) deep. Hence, to maximize the influence of chemomechanical effects on bit penetration rate only shallow cuts should be taken. Practical penetration rates are then obtained by increasing bit rotation speed. Experimental l-potentials were determined by the streaming potential technique using an automated rapid-cycling apparatus recently developed by Martin Marietta Laboratory from a design by Somasundaran and Kulkarni. The drilling studies employed 3.2-mm-OD 120-grit diamond-loaded core bits with a wall thickness of ~0.7 mm, and bit rotation speeds of 2200 and 25,000 rpm. The load applied to the bit was independent of the depth drilled in both cases. The 2200 rpm measurements employed the same drill press and puddle drilling technique as used in study I. The higher rotation speed was obtained using a water-driven dental turbine drill. In the case, the surface active fluid was pumped down the axis of the bit to ensure efficient wetting and flushing of the drilling debris from the hole. In both cases drilling rate was measured by the parameter D(200), defined as the average rate of bit penetration during the interval from 150 to 250 sec after drilling commenced.

Jan 1, 1976

By B. Lustman

IT has been known for a number of years that the addition of certain alkaline-earth and rare-earth metals to nickel-chromium base electric resistance alloys causes marked increase in their oxidation resistance as measured in an intermittent oxidation test similar to the ASTM—B 76-39 test. However, the mechanism whereby such additions confer protection is still unknown. On the basis of the experimental observation that the increase in life in intermittent tests of nickel-base alloys is proportional to the atomic radius of the added element, Hessen-bruchl has proposed that the added metal ions occupy holes in the oxide lattice which prevent diffusion of nickel ions in the oxide. Horn2 has postulated that the effect of such additions is to accelerate the rate of diffusion of chromium atoms in the metal and thus to favor the formation of Cr2O3 scales. Hickman and Gulbransen3 concluded from electron diffraction observation that the addition of the elements in question results in the formation of a barrier to the diffusion of nickel ions to the surface. In connection with some experiments conducted to develop a test for the resistance to oxidation of alloys in massive form under conditions of intermittent heating and cooling, some features of the oxidation of nickel-chromium base alloys were revealed which may serve to elucidate the mechanism of protection conferred by rare-earth and alkaline-earth elements. Specimens of cylindrical shape 0.360 in. diam x 0.37 in. long were placed in alumina thimbles and inserted into and withdrawn from a Globar-heated furnace operating at 2150°F at 7.5-min intervals. The weight of oxygen absorbed as well as the weight of oxide spalled were measured at intervals. With the particular experimental conditions used, the specimens in a 7.5-min cycle were at temperature for 2 min which corresponds to the heating time of the ASTM test. The weight changes of similar specimens under conditions of continuous heating in air at 2150°F were also measured. The specimens after oxidation were examined metal- lographically and samples of the spalled oxide collected for X-ray diffraction identification of the phases. The specimens used were from the same lot of material used by Hickman and Gulbransen3 and had the compositions shown in table 1. Included in table I are results of ASTM life tests on the materials in the form of wires. These materials, their composition and the ASTM life test data thereon were all supplied by F. E. Bash of the Driver-Harris Co. It may be noted that alloy 13246 of 80 pct nickel, 20 pct chromium nominal composition showed the shortest life in the ASTM test; alloy 12246 with the addition of small amounts of the elements zirconium, calcium, and aluminum, intermediate life; and alloy 12046 with the further addition of silicon, the longest life. In fig. 1 are shown the results of intermittent oxidation tests made on bulk specimens at 2150°F as well as continuous tests conducted at the same temperature. Duplicate tests were made on each specimen. The ordinate scale, inches of metal oxidized, was derived from the experimentally observed weight gain of oxygen by assuming the scale to be entirely Cr2O3. It may be noted that the metal-loss curves during intermittent oxidation show a constant or continuously increasing rate of weight

Jan 1, 1951

By E. C. W. Perryman

On electropolishing, high-purity Cu-Sn and Cu-Sn-P alloys with more than 5 to 9 pct Sn were found to contain many grain boundaries with a ridge-and-furrow profile. The effect was not eliminated by solution treatment and was present at the new boundaries in recrystallized material. It could be produced by diffusing tin into the 3 pct Sn alloy and it is concluded that the effect is due to enrichment of certain boundaries in tin, or possibly in an impurity present in the tin, in solid solution. IN the hot working of tin bronzes, especially those with moderately high tin contents, considerable difficulty is frequently encountered from intercrystal-line weakness, which results in cracking at the edges in sheet on strip rolling and in the unsupported regions of the rod in rod rolling.&apos; These difficulties are not at all pronounced with up to 3 pct Sn, but at 5 pct Sn impose serious limitations and at higher tin contents, especially if the phosphorus content is also high, they may become very severe. In some work carried out at the laboratories of The British Non-Ferrous Metals Research Association it was found that a notable lack of ductility in tension at elevated temperatures, associated with intercrystal-line failure, was characteristic of tin bronzes even of relatively high purity. That the intercrystalline fracture is not due to a brittle or molten impurity phase at the grain boundaries was shown by the fact that the temperature at which intercrystalline fracture first occurred decreased with decrease of rate of straining. Tensile tests on some commercial tin bronzes, reported by Goetzel,² show a similar fall in ductility with increasing temperature. As no visual evidence had been obtained showing that the grain boundaries of the tin bronzes were different from those in copper, a more detailed microscopical examination was carried out, and the results of this are given in the present report. Several workers"&apos; have observed that electrolytic polishing is a powerful tool for detecting small amounts of a second phase and in particular for detecting high solute concentrations, "equilibrium segregation," at grain boundaries. Since it had been found that the suggested solutions for electropolishing bronze and the standard solutions for brass and copper did not give satisfactory results it was first necessary to find a suitable electropolishing solution.&apos; Experimental Procedure Materials Used: The cast and wrought materials used for this work were the same as those used for the mechanical tests referred to above. They comprised 3, 6, and 9 pct Sn alloys without phosphorus and the same three basic alloys with 0.03 and 0.4 pct P. A 5 pct Sn alloy without phosphorus, of similar purity, was also examined. The basis materials were Chempur tin, high purity 15 pct phosphor-copper and cathode copper, and spectrographic analyses are given in Table I. Treatment: The cathode copper was first melted under charcoal, degassed by plunging marble chips beneath the surface, and cast through a coal gas flame into sand molds to produce a number of small ingots which after machining were of a suitable size for subsequent vacuum melting. Chill cast bars of the alloys, approximately 1¼ in. in diameter, were then made by melting and casting in vacuo, the tern-

Jan 1, 1954

By H. J. Beach

This paper describes the properties and uses of cementitious mixtures containing 10 to 20 per cent bentonite and 2 per cent or more sodium chloride. Salt additions improve bentonite cement by increasing early strength and stabilizing viscosity without changing thickening time. The volume yield of cement is increased 20 per cent or more without lowered early strength. The unique properties of salt in this type of system make savings of more than 10 per cent possible where light-weight, low-strength cementitious material is adequate to fill behind pipe. The density range of these mixtures is 12 to 13 1b/gal and the filtration rates are medium-low, aiding the placement of long columns in primary cementing. Where available, sea water is an ideal salt source in preparing these slurries. INTRODUCTION Accelerators increase the rate of cement hydration. In speeding reaction with water, they can affect cement performance by reducing thickening time and increasing early strength after set. Accelerators that cause both effects can be considered "total", and those which produce only one effect can be called "partial". Materials that act conversely to accelerators are retarders. and they also can be total or partial. Partial retarders. make high-temperature cementing possible by prolonging thickening time while impairing early strength only slightly. Most known accelerators are total. A useful partial accelerator would increase strength without altering thickening time. This report concerns material combinations in which a normally total accelerator exerts unique partial properties. Utilizing these limited effects improves bentonite cement. SEPARATE EFFECTS OF SODIUM CHLORIDE AND BENTONITE ON CEMENT Sodium chloride and calcium chloride are commonly used in cement, and at low concentrations their effects are similar. Ludwig1 studied sodium chloride in API Class A and Class E cements.&apos; Figs. 1 and 2 sum- marize his data taken at 140°F on slurry pumpability and early strength. Normal water-to-cement ratios are 0.46 and 0.40, respectively, for Class A and Class E cements. At saturation the salt content is 12 to 14 per cent of the weight of cement solids. The illustrations, therefore, cover the range of salt solubility in the mixing water. The data show that sodium chloride is a total accelerator of the Class E cement studied over the range of solubility. It is total in Class A cement to 6 per cent. Above this concentration salt becomes a retarder— partial from 6 to 10 per cent and total above. These results are general for different brands of Class A cement, although the shift from acceleration to retardation may occur at different salt concentrations for different temperatures. The results are specific for the Class E brand studied. In discussing his data, the investigator emphasized that different Class E cements might respond erratically to salt, depending on the brand chosen. Morgan and Dumbauld3 escribe the properties of bentonite cement in a paper that is a standard reference in using these systems. Bentonite functions in cement as an enabling agent; each bentonite addition equal to 1 per cent of the weight of dry cement makes possible the further addition of 4.5 per cent water.&apos; Thus, 10 per cent bentonite in Class A cement, normally slurried neat with 46 per cent water, enables the slurry to contain another 45 per cent before settling. Water is one of the lightest and cheapest cement extenders; it reduces density and cost. Bentonite cements produce uniform slurries having low susceptibility to solids separation. After set, they offer low resistance to perforation.